"ABSTRAKSubstitusi atom Zinc pada site-Fe material LaFeO3 (LaFe1-xZnxO3 dengan x= 0.0, 0.03, 0.05, dan 0.07) telah dilakukan dengan metode sintesis sol-gel. Sifat struktur material perovskite LaFe1-xZnxO3 dikarakterisasi menggunakan XRD, XRF, SEM dan EDS. Hasil analisis dari XRD untuk material LaFe1-xZnxO3 menunjukkan material memiliki struktur Orthorhombic dengan space group Pbnm. Dari hasil rietveld bahwa parameter kisi, volum, densitas serta parameter geometrikal material mengalami perubahan setelah subtitusi Zinc. Hasil SEM menunjukkan bahwa ukuran grain terlihat semakin menurun dan terjadi aglomerasi. XRF dan EDS mengkonfirmasi adanya unsur La, Zn, Fe dan O pada material perovskite LaFe1-xZnxO3. Sifat optik dikarakterisasi dengan menggunakan FTIR, Raman spectroscopy dan UV-Vis. FTIR mengkonfirmasi adanya stretching vibration La-O, Fe/Zn-O dan bending vibration Fe/Zn-O-Fe/Zn sedangkan pada hasil Raman spectroscopy diperoleh pembentukan material LaFeO3 serta energi aktivasi pada material dilihat dari modes yang terbentuk. Hasil karakterisasi UV-Vis menunjukkan penurunan nilai energi band gap dengan rentang 2.14-2.05 eV. Sifat listrik material diuji menggunakan RLC-meter dengan metode Impedance Spectroscopy (IS) pada rentang temperatur 30°C-200°C, dimana, diperoleh peningkatan konduktivitas akibat terjadinya penurunan resistivitas pada sampel bulk.

---

ABSTRACTZinc substitution at Fe-site on LaFeO3 material (LaFe1-xZnxO3 with x = 0.03, 0.05, and 0.07) has been carried out by sol-gel synthesis method. The structural properties of LaFe1-xZnxO3 perovskite material were characterized using XRD, XRF, SEM, and EDS. The analysis results from XRD for LaFe1-xZnxO3 material showed that the material has an Orthorhombic structure with Pbnm space group. From the Rietveld result that lattice parameters, volume, density and also geometrical parameters happened to be distorted or changed the result of properties. SEM result shows a decreasing in grain size and with a homogenous form of spherical in each sample. XRF and EDS confirmed the presence of La, Zn, Fe and O elements in the LaFe1-xZnxO3 perovskite material. Optical properties were characterized using FTIR, Raman spectroscopy and UV-Vis. FTIR confirmed that there were stretching vibrations of Fe/Zn-O and bending vibration Fe/Zn-O-Fe/Zn while the results of Raman spectroscopy were obtained by LaFeO3 material formation and activation energy in the material seen from the formed modes. The results of UV-Vis characterization showed a decrease in the value of the bandgap energy with a range of 2.104-2.004 eV. The electrical properties of the material were tested using the RLC-meter with the Complex Impedance Spectroscopy (CIS) method with range of temperatures 30°C-200°C, where the result of increasing in conductivity and decreasing in activation energy."

"ABSTRAKLanthanum Orthoferrite (LaFeO3) adalah salah satu material perovskite oxide ABO3 yang memiliki struktur ortorombik. Pada penelitian ini telah disintesis LaFeO3 yang disubstitusi dengan Zr pada situs Fe (LaFe1-xZrxO3 dengan x=0.01, 0.03 dan 0.05) yang dipreparasi menggunakan metode sol-gel. Penelitian ini bertujuan untuk mengetahui sifat struktur kristal, listrik dan optik material sebagai kandidat SOFC. Sampel yang telah dipreparasi diuji menggunakan XRD menunjukkan sampel yang single phase, struktur Orthorhombic dan space group Pbnm. Terjadi perubahan nilai bond-length dan bond-angle sebagai akibat dari substitusi Zr di situs Fe. Hal tersebut sesuai dengan hasil uji FTIR dan pergeseran mode pada Raman shift. Uji XRF menunjukkan stoichiometry pada material yang memiliki sedikit perbedaan dengan perhitungan. Selain itu, diperoleh komposisi stoikiometri yang lebih presisi dengan menggunakan uji EDX. Hasil uji SEM menunjukkan bahwa penambahan jumlah Zr menyebabkan rata-rata ukuran grain menurun yang konsisten dengan hasil dari XRD. Hasil uji UV-Vis menunjukkan data nilai band gap energy yang menurun seiring dengan peningkatan doping Zr sesuai dengan perubahan nilai bond-length pada XRD. Uji listrik pada material dilakukan dengan menggunakan metode impedance spectroscopy sebagai fungsi frekuensi (100Hz-1 MHz) dengan menggunakan RLC meter. Data IS disajikan dalam bentuk Nyquist Plot dan Bode Plot, yang digunakan untuk mengindentifikasi parameter rangkaian yang ekuivalen beserta nilainya. Hasil uji dengan RLC meter menunjukkan diameter semi-sirkular menurun seiring peningkatan temperatur, mengindikasikan material ini bersifat semikonduktor serta adanya peningkatan konduktivitas pada sampel dan penurunan nilai resistansi.

---

ABSTRACTLanthanum Orthoferrite (LaFeO3) is one of ABO3 perovskite oxide material which has orthorhombic structure. In this study, LaFeO3 substituted Zr at the Fe site (LaFe1-xZrxO3 with x = 0.01, 0.03 and 0.05) prepared using the sol-gel method. This study aims to determine the crystal structure, electrical properties and optical properties of materials. Sample was characterized with XRD showed single phase samples, Orthorhombic structures and Pbnm space groups. Changes in bond-length and bond-angle values occur as a result of Zr substitution at the Fe site. This is consistent with the results of FTIR and the shift mode on the Raman shift. XRF characterization shows stoichiometry on material that has a slight difference with the calculation. In addition, a more precise stoichiometric composition was obtained using EDX. SEM results show that increasing of Zr causes the average grain size decrease which is consistent with the results of XRD. UV-Vis results show that the band gap energy value decreases with the increase in Zr doping according to changes in the bond-length value in XRD. RLC meters show the semi-circular diameter decreases with increasing temperature, indicating this material is semiconductor as well as an increase in conductivity in the sample and a decrease in the resistance value corresponding to the activation energy in the grain and grain size SEM results. Electrical tests on the material are carried out using the impedance spectroscopy method as a function of frequency (100Hz-1 MHz) using the RLC meter. IS data are presented in the form of Nyquist Plots and Bode Plots, which are used to identify equivalent circuit parameters and their values."

"Perovskite tipe oksida jenis lanthanum orthoferrite (LaFeO3) telah menjadi salah satu kandidat jenis terbaru untuk material elektroda dikarenakan memiliki good activation property dan high electrochemical capacity. Beberapa penelitian sistematis tentang modifikasi LaFeO3 dengan melakukan substitusi menggunakan kation valensi yang lebih rendah seperti Zn2+ dan Ca2+ telah dilaporkan dan menunjukkan dampak yang baik pada physicochemical properties yang potensial untuk dapat diaplikasikan di bidang fotokatalitik. Pada penelitian ini, material perovskite LaFe1-xMgxO3 dengan x = 0.0, 0.1, 0.2 dan 0.3 telah berhasil disintesis menggunakan metode sol-gel. Proses sintesis material menghasilkan sampel dalam bentuk powder (bubuk) dan bulk (pellet). Uji karakterisasi yang telah dilakukan adalah XRD, XRF, FTIR, Raman, UV-VIS, SEM-EDX, BET, PSA, dan RLC Meter. Hasil uji karakterisasi XRD menunjukkan sampel yang single phase, struktur Orthorhombic dan space group Pnma. Terjadi peningkatan nilai bond-length dan bond-angle sebagai akibat dari substitusi Mg di situs Fe yang dikonfirmasi juga oleh hasil uji FTIR dan pergeseran mode pada Raman shift. Hasil uji XRF menunjukkan stoikiometri pada material yang sedikit berbeda dengan perhitungan, hal ini dikarenakan karena keterbatasan XRF untuk mendeteksi light element. Namun diperoleh komposisi stoikiometri yang lebih presisi dengan menggunakan uji EDX. Hasil uji SEM menunjukkan bahwa penambahan jumlah Mg menyebabkan rata-rata ukuran grain menurun, data ini konsisten dengan hasil yang diperoleh XRD. Hasil uji PSA menunjukkan nilai particle size rata-rata yang tidak beraturan, distribusi nilai particle size merata dan terdistribusi normal, sedangkan uji BET menunjukkan keberagaman nilai surface area yang dikonfirmasi juga karena adanya perbedaan komposisi elemen pada sampel powder yang dikonfirmasi dengan hasil uji XRF. Hasil uji UV-Vis menunjukkan data nilai band gap energy yang menurun seiring dengan peningkatan doping magnesium berkorelasi dengan peningkatan nilai bond-length pada XRD. Hasil uji dengan RLC meter menunjukkan diameter semi-sirkular menurun seiring peningkatan temperatur, mengindikasikan material ini bersifat semikonduktor serta adanya peningkatan konduktivitas pada sampel dan penurunan nilai resistansi berkorespondensi dengan energy aktivasi pada grain dan grain size hasil uji SEM.

---

Perovskite type-oxide lanthanum orthoferrite (LaFeO3) has become a new type of electrode material because has good activation property and high electrochemical capacity. A few systematic works about modifying LaFeO3 by substitute with lower valent-cation such as Zn2+ and Mg2+ has been reported before and showed a great impact on the physicochemical properties which potential to be applied as photocatalytic application. In this research, LaFe1-xMgxO3 (x = 0.0, 0.1, 0.2, 0.3) material has been synthesized using sol-gel method. The synthesis process resulting in two forms of the sample; powder and bulk. The characterization tests have done with XRD, XRF, FTIR, UV-Vis, SEM-EDX, BET, PSA and RLC meter. XRD characterization test was confirmed single phase with the orthorhombic crystal structure and Pnma space group for all samples. The increament of bond-length and bond-angle as a result of Mg-substitution in Fe-site confirmed by FTIR test and shift mode in Raman. XRF characterization test was displayed the stoichiometry a little bit different from the calculation, it can be happened because of the limitation of XRF to detecting the light element. But, the precise composition was getting from EDX characterization test. SEM characterization test shows that Mg-substitution resulting in the decreament of average grain size, this data was consistent with the XRD result. PSA characterization test observed inhomogenous of average particle size value, the particle size distribution normally, the BET characterization test shows the various value of surface area which confirmed by XRF results. UV-Vis characterization test displays band gap energy decrease with the increasing number of Magnesium correlating with increasing value of bond-length confirmed by XRD. RLC meter characterization test perform the decrement of semicircle diameter with increasing of temperature which indicating this material was a semiconductor and there is an enhancement of conductivity and the decrement of resistance value corresponding with activation energy on grain and grain size SEM result tests.

"

"ABSTRAKPerovskite lanthanum bismuth orthoferrite (La_1-xBi_xFeO₃ dengan x=0.1, 0.2, 0.3, 0.4 dan 0.5) telah disintesis menggunakan metode sol-gel. Hasil pola XRD yang telah dianalisa menggunakan program Highscore Plus menunjukkan bahwa material memiliki struktur orthorhombic serta semua sampel berfase tunggal dengan Pnma space group. Nilai parameter kisi meningkat dengan meningkatnya konsentrasi doping yang sebanding dengan meningkatnya jarak ikatan dari La-O dan Fe-O. Hal tersebut dipengaruhi oleh perbedaan jari-jari atom (ionic radii) antara Bi³⁺ dan La³⁺. Hasil pengukuran XRF menunjukkan terdapat perbedaan hasil antara hasil pengukuran dan eksperimental, hal ini dapat disebabkan oleh eror pengukuran dan proses sintesis (kehilangan massa pada saat proses sintesis). Hasil pengukuran SEM menunjukkan bahwa semua sampel memiliki ukuran dan bentuk grain tidak homogen dan juga terdapat porositas pada semua sampel. Pengujian sifat listrik dilakukan dengan menggunakan metode spektroskopi impedansi dengan rentang frekuensi 1 kHz sampai 1 MHz. Temperatur yang digunakan dalam pengujian ini yaitu dari rentang 75^oC - 200^oC. Analisis impedansi menunjukkan sifat semikonduktor untuk semua sampel. Terlihat jelas adanya kontribusi grain dan grain boundary pada nyquist plot dan juga terjadi penurunan grafik semisirkular dengan menurunnya temperatur. Bode plot menunjukkan fenomenana relaksasi, waktu relaksasi bergantung pada aktivitas termal. Analisis dielektrik menunjukkan semua sampel memiliki konstanta dielektrik menurun dengan menurunnya konsentrasi doping serta nilai konstanta dielektrik memiliki orde yang besar. Sifat konduktivitas listrik memenuhi Jonshers power law. Energi bandgap menurun dengan meningkatnya konsentrasi doping.

---

ABSTRACTPerovskite lanthanum bismuth orthoferrite (La_1-xBi_xFeO₃ with x = 0.1, 0.2, 0.3, 0.4 and 0.5) has been synthesized using the sol-gel method. The results of the XRD pattern analyzed using the Highscore Plus program indicate that the material has an orthorhombic structure and all single-phase samples with the Pnma space group. The lattice parameter value increases with increasing doping concentration which is proportional to the increasing bond distance of La - O and Fe - O. It is influenced by the difference in atomic radius (ionic radii) between Bi³⁺ and La³⁺. XRF measurement results show there are differences in results between measurement and experimental results, it can be caused by measurement error and synthesis process (mass loss during the synthesis process). The results of SEM measurement indicate that all samples have a size and shape not homogeneous and also have porosity in all samples. Measurement of electrical properties is carried out using impedance spectroscopic methods with a frequency range of 1 kHz to 1 MHz. The temperature used in this test is from the range 75^oC - 200^oC. Impedance analysis shows the semiconductor properties for all samples. It is clear that there is a contribution of grain and grain boundary on nyquist plots and also a decrease in semicircular graphs with decreasing temperature value. The bode plot shows the relaxation phenomena, which is the relaxation time itself depends on thermal activity. Dielectric analysis shows that all samples have a dielectric constant decreases with decreasing doping concentration and the dielectric constant value has large order. The conductivity of electricity analyze with Jonshers power law. The band gap energy decreases with increasing doping concentration.

"

"Seng merupakan mikronutrien yang penting dalam masa pertumbuhan anak dan untuk menjaga daya tahan tubuh pada masa pandemi ini. Seng tidak memiliki cadangan yang besar yang dapat menyimpan atau mengeluarkan seng sesuai dengan kebutuhan, sehingga seng menjadi penting untuk diperhatikan kecukupannya. Kekurangan seng lebih mungkin terjadi selama masa kanak-kanak, ketika kebutuhan harian seng lebih tinggi. Defisiensi seng dapat menyebabkan hilangnya nafsu makan, sehingga dapat berdampak pada status gizi dan pertumbuhan. Kadar seng rambut dapat menggambarkan status seng secara kronis, lebih stabil, dan lebih sesuai digunakan pada anak karena kurang invasive. Tujuan penelitian ini adalah untuk mengetahui korelasi asupan seng dengan kadar seng rambut anak usia 2-3 tahun. Penelitian ini menggunakan desain cross-sectional. Pengambilan data subjek dilakukan di Kelurahan Kampung Melayu (n=70) dan dilakukan pemeriksaan kadar seng rambut. Dari penelitian ini didapatkan median asupan seng adalah 6 (1,2-22,5) mg/hari dan sebanyak 20% anak memiliki asupan seng yang kurang. sedangkan nilai median kadar seng rambut adalah 132 (30-451) μg/g dan sebanyak 17,1% anak memiliki kadar seng rambut dibawah nilai normal. Hasil analisis menunjukkan korelasi negatif sangat lemah antara asupan seng dengan kadar seng rambut, namun secara statistik tidak bermakna (r=-0,077, p=0,528). Sedangkan untuk faktor faktor yang berhubungan, didapatkan hasil korelasi positif lemah bermakna antara nilai VAS nafsu makan dan kadar seng rambut (r=0,247, p=0,039). Sebagai kesimpulan, asupan seng pada anak usia 2-3 tahun tidak berkorelasi dengan kadar seng rambut, dan faktor yang berhubungan dengan kadar seng rambut adalah nilai VAS nafsu makan

---

Zinc is an important micronutrient in the growth period of children and to maintain the immune system during this pandemic. Zinc does not have a large reserve that can store or release zinc as needed, so it is important to pay attention to its adequacy. Zinc deficiency is more likely during childhood, when daily zinc requirements are higher. Zinc deficiency can cause loss of appetite, which can have an impact on nutritional status and growth. Hair zinc levels can describe chronic zinc status, are more stable, and are more suitable for use in children because they are less invasive. The purpose of this study was to determine the correlation of zinc intake with hair zinc levels of children aged 2-3 years. This study used a cross-sectional design. Subject data collection was carried out in Kampung Melayu Sub-district (n=70) and hair zinc levels were examined. From this study, it was found that the median intake of zinc was 6 (1.2-22.5) mg/day and as many as 20% of children had insufficient zinc intake. while the median hair zinc level was 132 (30-451) g/g and 17.1% of children had hair zinc levels below the normal value. The results of the analysis showed a very weak negative correlation between zinc intake and hair zinc levels, but not statistically significant (r=-0.077, p=0.528). For the associated factors, there was a significant weak positive correlation between VAS appetite value and hair zinc levels (r=0.247, p=0.039). In conclusion, zinc intake in children aged 2-3 years did not have a correlation with hair zinc levels, and factor associated to hair zinc levels was VAS appetite value."

"ABSTRACTSilika mesopori SBA-15 telah disintesis menggunakan tetraorthosilicate sebagai prekursor dan kopolimer triblok P123 sebagai template melalui proses sol-gel dan diteruskan melalui proses hidrotermal dan kalsinasi. Kemudian, SBA-15 di modifikasi menggunakan agen fungsionalisasi CPTMS 3-chloropropyl trimethoxysilane . Dalam penelitian ini, dibandingkan nilai penghilangan Zn menggunakan adsorban SBA-15 dan SBA-15-CPTMS. Keduanya digunakan sebagai adsorban untuk Zn dari air limbah industri menggunakan sampel air laboratorium. Adsorban tersebut juga di karakterisasi menggunakan SAXRD, FTIR untuk mengetahui gugus organik dan AAS untuk pengukuran konsentrasi ion dalam lautan setelah proses adsorpsi. Berdasarkan hasil katakterisasi BET, SBA-15 memiliki luas permukaan 831,996 m2/g, nilai tersebut lebih tinggi dibandingkan luas permukaan SBA-15-CPTMS sebesar 711,061 m2/g. Dari hasil AAS, SBA-15-CPTMS memiliki efektivitas dalam adsorpsi logam Zn lebih rendah daripada SBA-15 murni. "hr>""b>ABSTRACT"Mesoporous silica SBA 15 has been synthesized using Tetraorthosilicate as precursor and Pluronic 123 triblock copolymers as template through the sol gel method then continue with hydrothermal and calcination process. The surface of SBA 15 was modified using functionalization agent CPTMS 3 chloropropyl trimethoxy silane . In this study, we compared the percentage of Zn removal using CPTMS SBA 15 and SBA 15 systems. These SBA 15 CPTMS and SBA 15 were used as adsorbent of Zn from industrial waste water using laboratory water samples. The materials were characterized by SAXRD, the presence of organic group was demonstrated by FTIR, and the ions concentration in solution after adsorption process was determined by AAS. SBA 15 was found to have surface area of 831.996 m2 g higher than SBA 15 CPTMS which has surface area at 711.061 m2 g. CPTMS SBA 15 showed lower effectiveness in adsorption of those metals than pure SBA 15. "

"Material perovskite LaFe_1-xMn_xO₃ (x = 0,05, 0,10, 0,15, 0,20) telah disintesis dengan menggunakan metode sol-gel. Hasil karakterisasi menggunakan X-Ray Diffraction (XRD) menunjukan struktur kristal orthohombic dengan fase tunggal untuk semua sampel. Nilai crystallite size menurun seiring dengan meningkatnya substitusi Mn, dari 79,5 nm – 58,7 nm.  Karakterisasi FTIR menunjukan adanya vibrasi bending Fe/Mn – O – Fe/Mn dan stretching Fe/Mn – O pada sampel. Hasil X-Ray Fluorescence (XRF) komposisi unsur sampel LaFe_1-xMn_xO₃ telah sesuai dengan komposisi unsur hasil perhitungan. Sifat mikrostruktur hasil karakterisasi Scanning Electron Microscopy (SEM) menunjukan permukaan sampel dengan bentuk grain homogen bulat dengan adanya porositas. Nilai grain meningkat seiring meningkatnya subtitusi Mn dan menyebabkan porositas berkurang. Karakteriasi sifat listrik material LaFe_1-xMn_xO₃ dilakukan dengan menggunakan metode spektroskopi impedansi pada rentang frekuensi 100 Hz – 1 MHz. Karakterisasi dilakukan pada temperatur kamar dan  temperatur tinggi (100^oC – 275^oC). Data hasil karakterisasi disajikan dalam grafik nyquist plot dan bode plot. Pada temperatur kamar nyquist plot menunjukan penurunan ukuran semisirkular seiring bertambahnya konsentrasi substitusi Mn. Nilai konstanta dielektrik pada suhu kamar menunjukan typical colossal dielectric constant. Nyquits plot pada temperatur tinggi menunjukan sifat negative temperatur coefficient of resistance (NTCR). Hasil fitting energi aktivasi dari slope log ( ) versus 10³/T plots menunjukan bahwa nilai energi aktivasi (Ea) grain menurun dengan meningkatnya konsentrasi subtitusi Mn. Bode plot menunjukan fenomena relaksasi yang bergantung pada temperatur. Nilai waktu relaksasi menurun seiring dengan meningkatnya temperatur menunjukan typical semiconductor behavior. Energi aktivasi (Ea) yang dihitung dari waktu relaksasi menunjukan kecenderungan yang sama dengan energi aktivasi (Ea) grain. Nilai band gap energy meningkat seiring meningkatnya konsentrasi substitusi Mn.

---

Perovskite material LaFe_1-xMn_xO₃ (x = 0.05, 0.10, 0.15, 0.20) has been synthesized using the sol-gel method. The results of characterization using X-Ray Diffraction (XRD) show a single phase orthohombic crystal structure for all samples. The crystallite size value decreases with increasing Mn substitution, from 79.5 nm - 58.7 nm. FTIR characterization shows the presence of vibrations bending Fe/Mn – O – Fe/Mn and stretching Fe/Mn – O in the sample. The results of X-Ray Fluorescence (XRF) composition of LaFe_1-xMn_xO₃ sample elements are in accordance with the composition of the calculated elements. The microstructure of the the characterization results by Scanning Electron Microscopy (SEM) shows the surface of the sample in the form of a round homogeneous grain in the presence of porosity. Grain value increases with increasing Mn substitution cause decreasing porosity. The electrical properties of LaFe_1-xMn_xO₃ material is carried out using impedance spectroscopic methods in the frequency range of 100 Hz - 1 MHz. Characterization are carried out at room temperature and high temperature (100^oC – 275^oC). Data from characterization results are presented in nyquist plot and bode plot charts. The nyquist plot at room temperature shows decreasing impedance semicircle with increasing Mn substitution. The dielectric constant at room temperature shows colossal dielectric constant behavior. The nyquist plot at high temperature shows a negative temperature coefficient of resistance (NTCR). The result of energy fitting activation of the slope log ( ) versus 10³/T plots shows that the activation energy value (Ea) grain decreases with increasing Mn substitution concentration. Bode plots show the phenomenon of relaxation which depends on temperature. The value of relaxation time decreases with increasing temperature indicating typical semiconductor behavior. The activation energy (Ea) calculated from the relaxation time shows a tendency similar to the activation energy (Ea) grain. The band gap energy value increases with increasing concentration of Mn substitution."

"[ABSTRAKTelah dilakukan penelitian sifat listrik bahan perovskit SrFeO3 dan LaFeO3 padatemperatur tinggi pada kisaran temperatur ruang hingga 250 0C. Sampel disinter950 0C selama 6 jam. Hasil karakterisasi XRD menunjukkan SrFeO3 memilik fasetunggal dan memiliki struktur kristal kubik dengan space grup pm3m dangrainsize 20 nm, dan LaFeO3 memiliki struktur kristal orthorombik dengan spacegrup Pbnm dan grainsize 22 nm. Data impedansi disajikan dalam bentuk nyquistplot dan bode plot yang digunakan untuk mengidentifikasi parameter rangkaianekivalen. Sifat listrik bahan SrFeO3 dan LaFeO3 dapat dideskripsikan denganrangkaian R, RC paralel maupun kombinasi dari keduanya yang menunjukanadanya kontribusi grain dan grain boundary. Energi aktivasi diperoleh darihubungan konduktivitas dc sebagai fungsi temperatur. Energi aktivasi sampelSrFeO3 dan LaFeO3 adalah 0,1817 eV dan 0,0158 eV.

---

ABSTRACTThe electrical properties of SrFeO3 and LaFeO3 perovskite materials areinvestigated at high temperatures from room temperature to 250 0C. Samples aresintered at 950 0C for 6 hours. XRD characterization show SrFeO3 has a singlephase and having cubic structure with pm3m space group and grainzise 20 nm.LaFeO3 having orthorombic structure with Pbnm space group and grainsize 22 nm.Impedance data are presented in the nyquist plot and bode plot which is used toidentify an equivalent circuit. The electrical properties of SrFeO3 and LaFeO3perovskite materials can described by R, RC parallel or both combination thatseem a grain and grain boundary. The value of the activation energy which isevaluated from dc conductivity as a function of temperature. The activationenergy of SrFeO3 and LaFeO3 is 0.1817 eV and 0.0158 eV., The electrical properties of SrFeO3 and LaFeO3 perovskite materials areinvestigated at high temperatures from room temperature to 250 0C. Samples aresintered at 950 0C for 6 hours. XRD characterization show SrFeO3 has a singlephase and having cubic structure with pm3m space group and grainzise 20 nm.LaFeO3 having orthorombic structure with Pbnm space group and grainsize 22 nm.Impedance data are presented in the nyquist plot and bode plot which is used toidentify an equivalent circuit. The electrical properties of SrFeO3 and LaFeO3perovskite materials can described by R, RC parallel or both combination thatseem a grain and grain boundary. The value of the activation energy which isevaluated from dc conductivity as a function of temperature. The activationenergy of SrFeO3 and LaFeO3 is 0.1817 eV and 0.0158 eV.]"

"ABSTRACTTelah dilakukan penelitian mengenai struktur,sifat listrik, dan sifat magnet material perovskite manganites La0,7Sr0,2Ba0,1Mn1-xNixO3 x = 0; 0,02; 0,05; 0,1 yang disintesis dengan metode sol gel. Hasil karakterisasi XRD menunjukkan bahwa sampel memiliki fase tunggal dengan struktur rhombohedral dan space group R-3c. Pemberian sedikit doping nickel tidak mengubah struktur kristal, tetapi merubah nilai parameter kisi kristal. Karakterisasi SEM-EDS menunjukkan perubahan ukuran grain dan mengkonfirmasi unsur nickel berhasil tersubstitusi. Ukuran grain size semakin kecil seiring dengan penambahan konsentrasi nickel. Kurva histerisis yang dihasilkan menunjukkan bahwa pemberian doping nickel menurunkan sifat kemagnetan bahan yang ditunjukkan oleh penurunan nilai saturasi magnetisasi. Kurva resistivitas sebagai fungsi temperatur menunjukkan bahwa doping nickel meningkatkan besar resistivitas material. Hasil fitting dengan menggunakan model percolation menunjukkan penambahan konsentrasi nickel menurunkan nilai temperatur curie Tc dan temperatur transisi metal-isolator TM-I ke temperatur yang lebih rendah.

---

ABSTRACTThe structure, electrical properties, and magnetic properties of perovskite manganite La0.7Sr0.2Ba0.1Mn1 xNixO3 x 0 0.02 0.05 0.1 material were synthesized by the sol gel method have been studied. The result of XRD characterization showed that sample has a single phase with rhombohedral structure and R 3c space group. Nickel doped on site Mn does not change the crystal structure but changes the lattice parameter. The SEM EDS characterization shows changes in grain size and confirms that site Mn succeeds substituted with nickel ion. Grain size decreased with the addition of nickel concentration. The hysteresis curve showed that nickel doped decreased magnetic properties of the material as indicated by the decrease in magnetization saturation value. Characterization of SEM EDX shows changes in grain size and confirms the nickel element successfully substituted. Resistivity curve as a function of temperature indicates that nickel doped increased resistivity. The result of fitting by using percolation model showed that the addition of nickel concentration decreased temperature curie Tc and metal isolator transition temperature TM I to lower temperature."

"Material Perovskite-like layered structrure (PLS) La2Ti2O7 merupakan material feroelektrik yang sangat aplikatif dengan didasarkan pada sifat piezoelektrik, piroelektrik, dan elektro optik yang dimilikinya. Feroelektrik dikatakan unggul ketika memiliki sifat dielektrik yang tinggi yang dapat diaplikasikan untuk DRAM (Dynamic Random Access Memory) pada kapasitornya. PLS La2Ti2O7 dengan substitusi Zn2+ di situs Ti (La2Ti2- xZnxO7) dengan x = 0.0, 0.1, 0.2 berhasil disintesis menggunakan metode sol-gel yang dilanjutkan dengan proses sintering. Karakterisasi sampel telah dilakukan untuk mempelajari sifat struktur dengan data hasil XRD, SEM-EDS, UV-Vis dan sifat listrik dengan metode sprektoskopi impedansi. Hasil uji XRD menunjukkan bahwa semua sampel La(Ti,Zn)O single phase dan memiliki struktur stabil monoklinik dengan space group P21. Jari-jari atom doping Zn2+ (0.74 Ǻ) yang lebih besar dari atom Ti4+(0.61 Ǻ) menyebabkan pergeseran sudut 2θ lebih rendah sehingga parameter kisi akan lebih besar dan sebanding dengan volumenya. Hasil uji SEM menunjukkan bahwa penambahan konsentrasi Zn2+ menyebabkan grain size menurun yang konsisten dengan hasil yang diperoleh XRD yang mengkonfirmasi terjadinya penurunan cristalllite size seiring dengan kenaikan konsentrasi doping. Hasil EDX menunjukkan pada sampel murni tidak terdapat Zn di dalamnya dengan nilai persen atomic dan persen berat unsur Ti4+ menurun dan menunjukkan kenaikan pada unsur Zn2+ seiring kenaikan konsentrasi x. Hasil uji UV- Vis dengan data absorbansi diplot menggunakan metode tauc dan menghasilkan nilai energy band gap yang meningkat seiring kenaikan konsentrasi x. Hasil ini dikonfirmasi dengan hasil uji listrik yang menunjukkan nilai konstanta dielektrik yang meningkat dan konduktivitas yang meningkat seiring peningkatan konsentrasi x dikarenakan ada banyak kekosongan oksigen yang berkorelasi dengan hasil SEM.

---

Perovskite-like layered structure (PLS) La2Ti2O7 is a highly applicable ferroelectric material based on its piezoelectric, pyroelectric, and electro-optic properties. Ferroelectric is said to be superior when it has high dielectric properties that can be applied to DRAM (Dynamic Random Access Memory) in the capacitor. PLS La2Ti2O7 with Zn2+ substitution at the B-site (La2Ti2-xZnxO7) with x = 0.0, 0.1, 0.2 was successfully synthesized using the sol-gel method followed by a sintering process. Sample characterization was carried out to study the structural properties using XRD, SEM-EDS, UV-Vis, and electrical properties using impedance spectroscopic methods. XRD test results showed that all samples of La(Ti,Zn)O were single phase and had a stable monoclinic structure with space group P21. The atomic radius of Zn2+ doped (0.74 ) which is larger than that of Ti4+ (0.61 ) causes a lower 2θ angular shift so that the lattice parameters (a, b, c) will be larger and proportional to the volume. The SEM test results show that the addition of Zn2+ concentration causes the grain size to decrease which is consistent with the results obtained by XRD which confirms a decrease in crystallite size along with the increase in doping concentration. The EDX results show that in the pure sample there is no Zn in it with the atomic percent and weight percent values of Ti4+ decreasing and showing an increase in Zn2+ as the concentration of x increases. The results of the UV-Vis test with absorbance data plotted using the tauc method and resulted in an energy band gap value that increased with the increase in x concentration. This result was confirmed by the electrical test results which showed an increasing dielectric constant value and an increasing conductivity with an increase in x concentration due to the presence of many oxygen vacancies which correlated with the SEM results."