Proses Micro Friction Stir Spot Welding (mFSSW) merupakan teknik pengelasan pelat logam yang memiliki ketebalan pelat yang relatif tipis. mFSSW memiliki keunggulan dalam proses pengelasan dibandingkan dengan pengelasan konvensional, seperti Arc Welding. Keunggulannya adalah dari segi kualitas pengelasan yang lebih baik dan distorsi yang relatif rendah. Tujuan dari penelitian ini adalah untuk mengetahui pengaruh bentuk pahat dan kedalaman pahat terhadap sifat mekanik dan geometri hasil lasan pada teknik pengelasan Micro Friction Stir Spot Welding (mFSSW) menggunakan pelat tipis aluminium A1100. Pada penelitian ini parameter yang divariasikan adalah geometri pahat dan kedalaman pahat. Parameter geometri pahat divariasikan dalam penelitian ini menjadi 7 jenis geometri pahat. Parameter kedalaman puncture divariasikan dalam penelitian ini menjadi 3 macam kedalaman (200 mikron, 400 mikron, dan 600 mikron). Uji makro dilakukan untuk mengetahui geometri las, yaitu profil kontur, diameter, dan kedalaman sambungan. Hasil uji makro dilakukan untuk memprediksi hasil dan kekuatan patah. Untuk mengetahui sifat mekanik dilakukan dua pengujian yaitu uji tarik dan uji tarik silang. Hasil uji tarik akan dianalisa untuk menentukan jenis patahan dan kekuatannya. Dari hasil percobaan dan analisis diketahui bahwa geometri pahat dan kedalaman tusukan akan menghasilkan karakteristik tersendiri untuk geometri las dan kekuatan las. Geometri las yang akan terlihat pada profil adalah shoulder, pin, TMAZ, dan kedalaman aktual yang dihasilkan. Kekuatan las atau sifat mekanik yang akan diketahui adalah tegangan

---

ABSTRACT
The Micro Friction Stir Spot Welding (mFSSW) process is a metal plate welding technique that has a relatively thin plate thickness. mFSSW has advantages in the welding process compared to conventional welding, such as Arc Welding. The advantages are in terms of better welding quality and relatively low distortion. The purpose of this study was to determine the effect of chisel shape and chisel depth on the mechanical properties and geometry of the welds in the Micro Friction Stir Spot Welding (mFSSW) welding technique using A1100 aluminum thin plates. In this study, the parameters that were varied were tool geometry and tool depth. The tool geometry parameters were varied in this study into 7 types of tool geometry. The parameters of the puncture depth were varied in this study into 3 different depths (200 microns, 400 microns, and 600 microns). The macro test was carried out to determine the weld geometry, namely the contour profile, diameter, and joint depth. Macro test results were performed to predict yield and fracture strength. To determine the mechanical properties, two tests were carried out, namely tensile test and cross-tensile test. Tensile test results will be analyzed to determine the type of fracture and its strength. From the experimental results and analysis, it is known that the tool geometry and the depth of the puncture will produce its own characteristics for the weld geometry and weld strength. The weld geometry that will be seen in the profile is the shoulder, pin, TMAZ, and the actual resulting depth. Weld strength or mechanical properties that will be known is the stress

Abstrak :
Indoaustralia, dan Pasifik. Hal tersebut membuat Indonesia memiliki potensi terjadi gempa bumi yang tinggi. Dilansir dari (BBC News, 2018), wilayah Indonesia berpotensi mengalami gempa kuat terimplikasi dari adanya sekitar enam tumbukan lempeng aktif. Bencana alam selalu menyisakan puing-puing bangunan yang telah hancur dan rusak. Peneliti Pusat Litbang Perumahan dan Permukiman, Badan Penelitian dan Pengembangan, Kementerian Pekerjaan Umum dan Perumahan Rakyat (PUPR), M. Edi Nur, mengatakan bahwa puing bangunan sisa bencana bisa saja menjadi sampah, tetapi ada juga yang masih dapat dimanfaatkan. Menurut (Haryanti, 2018), dalam satu rumah bertembok sederhana terdapat unsur beton sebanyak 22%, lalu unsur tembok, lantai, serta genteng sebesar 60%, dan masih ada unsur kayu atau bambu sekitar 18%. Limbah beton tersebut dapat dimanfaatkan kembali menjadi agregat daur ulang penyusun beton. Penulis melakukan penelitian mengenai karakteristik beton dengan material subtitusi agregat kasar daur ulang mengenai kuat tekan dan homogenitasnya pada umur muda hingga optimum. Terdapat dua metode pengujian yang dilakukan terhadap beton daur ulang ini, yaitu metode destruktif dan non-destruktif. Dimana pengujian destruktif yang dilakukan ialah crushing test untuk mendapatkan nilai kuat tekan dan pengujian non-destruktif yang dilakukan ialah Ultrasonic Pulse Velocity (UPV) test untuk mendapatkan nilai kecepatan rambat gelombang ultrasonik pada beton daur ulang. Selain menganalisis karakteristik beton daur ulang dari nilai kuat tekan dan nilai kecepatan rambat gelombangnya, dilakukan pengolahan untuk mengetahui hubungan dari kedua variabel tersebut. Penelitian ini mendapatkan persamaan hubungan kuat tekan dengan kecepatan rambat gelombang yaitu 𝑓𝑐= 0,0381827741𝑒1,5376800300𝑉𝑐 [𝑘𝑚 𝑠⁄ ] dengan koefisien determinasi sebesar R2 = 0,6985272443. Selanjutnya karakteristik homogenitas beton daur ulang akan dilihat tingkat homogenitasnya melalui nilai kecepatan rambat gelombang dimulai dari empat atau lima jam setelah proses pengadukan.

---

Indonesia is located at the confluence of three major plates of the world, the Eurasia Plates, Indo-Australia, and the Pacific. This makes Indonesia has the highest potential for earthquakes to happen. Reported by (BBC News, 2018), Indonesias region has the potential to encounter a strong earthquake implicated by, at least six active plates collision. Natural disaster always left ruins of buildings which have been ruined. Researcher at the Research and Development Agency, Ministry of Public Works and Public Housing, M. Edi Nur, conveyed that ruins of buildings remained from natural disaster could become trash, but some could also be used as something useful. According to (Haryanti, 2018), in a simple walled house usually has as many as 22% of concrete elements, wall elements, floor, and roof as many as 60%, and the other 18% are wood or bamboo elements. The concrete waste can be reused into recycled concrete complier aggregates. The writer did research about concrete characteristics with coarse recycled aggregate substitution material regarding the compressive strength and its homogeneity at early age to optimum age. There are two testing methods done for this recycled concrete, destructive methode and non-destructive methode. The destructive methode is done by crushing test to achieve the compressive strength value and the non-destructive method is done by Ultrasonic Pulse Velocity (UPV) test to gain ultrasonic pulse velocity value of the recycled concrete. Aside from analizing the characteristics of the recycled concrete from compressive strength value and the ultrasonic pulse velocity value, a process is done to knowledge the relation between the two variables. This research gained the equation of the relation between compressive strength and ultrasonic pulse velocity, which is 𝑓𝑐= 0,0381827741𝑒1,5376800300𝑉𝑐 [𝑘𝑚 𝑠⁄ ] with coefficient of determination in the amount of R2 = 0,6985272443. Hereafter, the characteristics of recycled concrete homogeneity will be seen from the level of its homogeneity through the amount of ultrasonic pulse velocity starting from four or five hours after casting process.

Abstrak :
Pertambahan penduduk merupakan fenomena yang tidak dapat dihindarkan. Di Indonesia sendiri terdapat kurang lebih 271 juta jiwa dan 56% diantaranya tinggal di pulau Jawa (Badan Pusat Statistik, 2014). Hal ini menyebabkan intensitas aktivitas antropogenik meningkat, sehingga mengakibatkan limpasan limbah yang besar yang dibuang ke sistem sungai. Pencemaran ini dapat ditemukan baik di kolom air maupun di sedimen yang telah terakumulasi dalam jangka waktu yang lama. Penelitian ini bertujuan untuk mengidentifikasi polutan di sungai-sungai perkotaan yang berada di wilayah Jabodetabek, menganalisis hubungan antara penggunaan lahan dan kualitas sungai dan memberikan rekomendasi mengenai opsi remediasi yang akan dilaksanakan. Pengambilan data dilakukan dengan mengambil sampel yang berada di hulu Sungai Ciliwung dan beberapa titik yang tersebar di wilayah Jabodetabek. Pengujian yang dilakukan meliputi parameter organik dan unsur logam berat. Parameter organik berupa DO, TN, TP, TOC, pH, suhu dan TSS. Hasil analisis tata guna lahan dan jarak garis lurus setiap pengambilan sampel ke bagian hilir Sungai Ciliwung dikaitkan dengan data yang telah diperoleh dari pengujian sampel. Analisis logam berat dilakukan dengan menghitung nilai indeks geoakumulasi, dimana komposisi logam berat pada setiap titik pengambilan sampel dibandingkan dengan nilai latar belakang atau hulu Sungai Ciliwung. Ditemukan adanya unsur-unsur seperti Mn, Cr, Ni, Eu, Mo, Yb dan Re yang menjadi beban pencemaran terbesar di lokasi tersebut. Setelah melalui perhitungan indeks geoakumulasi, ditemukan bahwa Sungai Mookervart tergolong pencemaran ekstrim. Sehingga Sungai Mookervart menjadi pilihan utama dalam melakukan pemulihan melalui metode remediasi. Metode remediasi yang disarankan adalah pengerukan atau dredging karena geometri Sungai Mookervart cenderung kecil. Secara teknis, pengerukan Sungai Mookervart sepanjang 2,16 km akan menelan biaya sekitar 8 miliar rupiah dan membutuhkan waktu 10 hari untuk menyelesaikan perbaikan.

---

Population growth is an unavoidable phenomenon. In Indonesia alone there are approximately 271 million people and 56% of them live on the island of Java (Central Bureau of Statistics, 2014). This causes the intensity of anthropogenic activity to increase, resulting in large waste runoff being discharged into the river system. This pollution can be found both in the water column and in sediments that have accumulated over a long period of time. This study aims to identify pollutants in urban rivers located in the Greater Jakarta area, analyze the relationship between land use and river quality and provide recommendations on remediation options to be implemented. Data collection was carried out by taking samples in the upper reaches of the Ciliwung River and several points scattered in the Greater Jakarta area. The tests carried out include organic parameters and heavy metal elements. Organic parameters in the form of DO, TN, TP, TOC, pH, temperature and TSS. The results of the land use analysis and the straight line distance of each sampling to the lower reaches of the Ciliwung River are associated with the data that has been obtained from sample testing. Heavy metal analysis was carried out by calculating the geoaccumulation index value, where the composition of heavy metals at each sampling point was compared with the background value or the upstream of the Ciliwung River. It was found that the presence of elements such as Mn, Cr, Ni, Eu, Mo, Yb and Re which became the biggest pollution burden at that location. After going through the calculation of the geoaccumulation index, it was found that the Mookervart River is classified as extreme pollution. So that the Mookervart River becomes the main choice in carrying out recovery through the remediation method. The recommended remediation method is dredging or dredging because the geometry of the Mookervart River tends to be small. Technically, dredging the 2.16 km Mookervart River would cost around IDR 8 billion and take 10 days to complete the repairs.