"Phase transformation studies have been carried out for pure iron and iron-carbon compounds of composition 0.1wt%C (low carbon), 0.4wt%C (hypo-eutectoid), and 0.8wt%C (nominal eutectoid) respectively. The samples were produced by powder metallurgy method. In this case Fe-C alloys were prepared by mixing both Fe and C powder prior to loading into a cylinder die and subsequently pressed using uniaxial force of 5 tons. The pressed samples (grain compact) were inserted into the quartz tube and air was evacuated by vacum to the level of 1.5x1 ff2mbar and then heated to 1100°C for 6 hours toward fully dense samples. Sintered samples were cooled in the furnace to room temperature. Results of OTA experiment indicated that ferromagnetic transition of pure iron taking place at temperature of 774°C and phase transformation of ferrite-austenite at temperature of 929°C. For 0.1wt%C alloy was occured pearlite-austenite transition at temperature of - 723°C with entalphy of formation of 17. 14J/g, and pro-eutectoid ferriteaustenite transition at temperature of 930°C. For 0.4wt%C alloy was occured entalphy of formation increasing of pearlite-austenite to 41.1 SJ/g. For nominal composition of 0.8wt%C was occured entalphy of formation increasing of pearlite-austenite to 72.0SJ/g at temperature of -723°C. From this study, it is found that the microstructure of pearlite consisted of ferrite and cementite in the lamelar structure. The volume fraction of pearlite consistently increased to -100% as the carbon content increased to the eutectoid composition."

"ABSTRAKPenelitian ini membahas kinetika pertumbuhan kristal dan karakterisasimaterial penyerap gelombang mikro berbahan dasar LSMO di substitusi Fe-Tidengan formula La0.5Sr0.5Mn0.8Fe0.1Ti0.1O3. Preparasi material menggunakanmetode paduan mekanik selama 10 jam, kemudian diberikan variasi waktu 0, 1, 5dan 24 jam pada temperatur 1000 C, 1100 C dan 1300 C. Pengujian XRDsebelum proses sintering dan sesudah sintering yang menunjukan hasil bahwasintesa bahan atau paduan La0.5Sr0.5Mn0.8Fe0.1Ti0.1O3 memiliki fasa tunggal (singlephase) dengan struktur kristal orthorombik dengan parameter kisi a=7.7 Å ; b=5.5Å ; c=5.4 Å. Berdasarkan hasil pengukuran ukuran kristal rata-rata melaluimetode Debye-Scherrer, kinetika pertumbuhan kristal rata-rata mengikutipersamaan Avrami dengan nilai energi aktivasi sebesar Q=21.29 kJ/mol.K.Karakteristik nilai serapan gelombang mikro pada frekuensi 8?15 GHz dianalisamenggunakan Vector Network Analyzer (VNA). Karakterisasi kurva reflektansiloss sampel material T1300-24jam memberikan nilai intensitas yang palingoptimal yaitu sebesar -3.58 dB atau 34% frekuensi serapan pada frekuensi optimal12.5 GHz, dan lebar pita penyerapan sebesar 3 GHz.

---

ABSTRACTThe kinetics of crystallite growth and microwave characteristics for Fe-Ti

substituted LSMO with La0.5Sr0.5Mn0.8Fe0.1 Ti0.1O3 composition was investigated.

Material preparation was carried out by means of mechanical alloying process for

10 hours milling times. The powders which prepared from mechanically milled

material were sintered at temperatures 1000 C, 1100 C dan 1300 C respectively

for 0, 1, 5 and 24 hours time sintering time. The XRD traces for sintered materials

confirmed that the La0.5Sr0.5Mn0.8Fe0.1 Ti0.1O3 is a single phase material with a

orthomobic crystal structure a=7.7 Å ; b=5.5 Å ; c=5.4 Å. Refering to mean

crystallite size evaluation which employing Debye Scherrer method. It was found

that the kinetics of mean crystallite growth followed the Avrami equation with an

activation energy for crystallite growth Q=21.29 kJ/mol.K. In addition to

crystallite growth kinetics the absorbtion characteristics of material was evaluated

by a Vector Network Analyzer (VNA) in the electromagnetic frequency range 8-

15GHz. The best absorbtion characteristics was found in the sample code T1300-

24h. This follows that the reflection loss of -3.58 dB or 34% was absorb occurred

at frequency 12.5 GHz was the bandwith 3GHz."

"Pengaruh doping potassium (K) pada lanthanum manganite La1-xKxMnO3 (x= 0; 0,1; 0,2; 0,3) terhadap sifat penyerapan gelombang mikro telah selesai dipelajari. Sampel disintesis menggunakan metode Sol-Gel dengan suhu kalsinasi 600˚C selama 6 jam dan suhu sintering 750˚C selama 24 jam. Hasil analisis XRD menunjukkan bahwa seluruh sampel memiliki struktur kristal rhombohedral dengan space group R-3c. Ukuran kristalit sampel berdasarkan uji SEM-EDS berkisar antara 80 – 400 nm. Hasil karakterisasi EDS menunjukkan sinar-x karakteristik masing-masing komponen timbul pada hasil EDS. Karakterisasi sifat magnetik menggunakan VSM menunjukkan bahwa sifat magnetik sampel mengalami transisi dari paramagnetik pada sampel menjadi ferromagnetik seiring dengan bertambahnya komposisi potassium. Uji VNA dilakukan pada frekuensi x-band, yakni pada rentang frekuensi 8 – 12.5 GHz. Nilai reflection loss masing-masing sampel adalah -4,58 dB untuk sampel LKMO-0; -5,47 dB untuk LKMO-1; -4,65 dB untuk LKMO-2, dan -5,19 dB untuk LKMO-3. Puncak reflection loss seluruh sampel rata-rata berada pada frekuensi 9 GHz. Pada frekuensi tersebut juga sampel LKMO-1 memiliki nilai permeabilitas real dan imajiner yang paling tinggi daripada sampel lainnya.

---

The effect of potassium (K) doping on lanthanum manganite La1-xKxMnO3 (x= 0; 0.1; 0.2; 0.3) on the microwave absorption properties has been studied. The samples were synthesized using Sol-Gel method with a calcination temperature 600˚ for 6 hours and sintering temperature 750˚ for 24 hours. The XRD result showed that all of the samples are rhombohedral with space group R-3c. The crystallite size of the samples based on the SEM-EDS test ranges from 80-400 nm and characteristic x-rays of each component appear in the EDS results. Magnetic characterization using VSM revealed that the magnetic properties of the samples changed from paramagnetic to ferromagnetic as the potassium composition increased. VNA characterization was conducted at the x-band frequency with range 8-12.5 GHz. The reflection loss values of each sample were -4.58 dB for LKMO-0 sample; -5.47 dB for LKMO-1; -4.65 dB for LKMO-2, and -5.19 dB for LKMO-3. The peak of reflection loss curve of all samples was averagely at 9 GHz frequencies. At this frequency, the LKMO-1 sample has the highest real and imaginary permeability values compared to the others."

"Material La0,8K0,2MnO3 memiliki kemampuan penyerapan gelombang mikro yang cukup baik dan bandwith yang lebar. Pada penelitian lain, beberapa material yang diberikan doping Zn di site B mampu meningkatkan kemampuan penyerapan gelombang mikro dan juga lebar bandwithnya. Namun, belum ada penelitian doping Zn pada material La0,8K0,2MnO3. Penelitian ini membahas pengaruh doping Zn pada material La0,8K0,2MnO3 yang disintesis dengan variasi x = 0,1; 0,3 dan 0,5. Material La0,8K0,2Mn(1-x)ZnxO3 disentesis menggunakan metode sol-gel, setelah sampel disintesis dilanjutkan dengan melakukan proses dehidrasi, kalsinasi, kompaksi dan sintering sebelum melakukan karakterisasi. Karakterisasi sampel menggunakan XRD, Permagraf dan VNA. Karakterisasi XRD menunjukkan bahwa material La0,8K0,2Mn(1-x)ZnxO3 memiliki fasa tunggal dengan struktur kristal rhombohedral. Pengujian menggunakan permagraf menunjukan bahwa doping Zn meningkatkan nilai dieletrik dari material La0,8K0,2MnO3. Hasil karakterisasi VNA menunjukkan doping Zn dapat meningkatkan kemampuan penyerapan gelombang mikro dari material La0,8K0,2MnO3. Nilai reflection loss terbesar yaitu -26,456 dB pada frekuensi 9,644 GHz untuk x = 0,5.

---

La0.8K0.2MnO3 material has a fairly good microwave absorption capability and wide bandwidth. In another study, some of the materials provided by Zn doping at site B were able to increase the absorption ability of microwaves and also the width of the bandwidth. However, there have been no Zn doping studies on La0.8K0.2MnO3 material. This study discussed the effect of Zn doping on La0.8K0.2MnO3 material synthesized with variations x = 0.1; 0.3 and 0,5. La0.8K0.2Mn(1-x)ZnxO3 material is synthesized using the sol-gel method, after the sample is synthesized it is continued by carrying out the process of dehydration, calcination, compaction and sintering before characterization. Sample characterization using XRD, Permagraph and VNA. XRD characterization shows that the material La0.8K0.2Mn(1-x)ZnxO3 has a single phase with a rhombohedral crystal structure. Tests using permagraphs showed that Zn doping increased the dieletric value of the La0.8K0.2MnO3 material. The results of VNA characterization show that Zn doping can increase the microwave absorption ability of La0.8K0.2MnO3 material. The largest reflection loss value is -26.456 dB at a frequency of 9.644 GHz for x = 0,5."

"Diabetes menjadi salah satu penyakit yang diderita sebagian besar manusia pada masa kini. Mahalnya alat deteksi insulin, hormon yang sangat penting dalam menjaga gula darah, menjadi masalah dalam pendeteksian kadar insulin. Sehingga dibutuhkan sensor yang murah, cepat dan sensitif terhadap insulin. Salah satunya sensor berbasis elektrokimia dari karbon. Dalam penelitian ini telah dibuat sensor screen printed carbon electrode (SPCE) termodifikasi multiwalled carbon nanotube (SPCE/MWCNT) dan termodifikasi nanopartikel emas (AuNP) ukuran 42,2 ± 8,7 nm (SPCE/MWCNT/Au 1- 20) dan 56,9 ± 6,3 nm (SPCE/MWCNT/Au 1-60) yang telah disintesis menggunakan metode Turkevich. Uji morfologi dengan SEM menunjukkan nanopartikel emas telah terdeposisi dengan adanya aglomerasi. Terjadi peningkatan luas permukaan aktif sensor menjadi 0,250 ± 0,007 cm2, 0,127 ± 0,001 cm2, 0,136 ± 0,002 cm2 dari sensor SPCE/MWCNT/Au 1-20, SPCE/MWCNT/Au 1-60 dan SPCE/MWCNT dari sensor SPCE yang hanya sebesar 0,108 ± 0,001 cm2. Karakterisasi impedansi dengan EIS menunjukkan SPCE/MWCNT/Au 1-20 memiliki nilai hambatan transfer muatan (Rct) terkecil, sebesar 124,62 Ω, sementara sensor SPCE/MWCNT/Au 1-60 dan SPCE/MWCNT masing-masing sebesar 240,03 Ω dan 230,50 Ω. Pengujian dengan insulin lispro komersial pada rentang konsentrasi 0,15 μM hingga 10,0 μM dalam larutan penyangga fosfat 0,1 M pH 7 menunjukkan adanya puncak oksidasi pada ketiga sensor, pada SPCE/MWCNT puncak oksidasi terlihat pada 0,5 V sementara pada sensor SPCE/MWCNT/Au 1-20 dan Au 1-60 masing-masing pada 0,42 V dan 0,44 V. Pada pengujian insulin dengan metode cyclic voltammetry (CV) sensor SPCE/MWCNT/Au 1- 60 menunjukkan performa terbaik dengan sensitivitas sebesar 16,25 μA/μM/cm2 (R2 0,98072), 25,67% lebih besar dibanding SPCE/MWCNT dengan limit deteksi (LOD) dan limit kuantifikasi (LOQ) sebesar 1,55 μM dan 5,18 μM. Sementara pengujian insulin dengan metode kronoamperometri, sensor SPCE/MWCNT/Au 1-60 juga menunjukkan sensitivitas terbaik, sebesar 2,17 μA/μM/cm2 (R2 0,99758), tidak terlalu signifikan berbeda dengan sensor SPCE/MWCNT yang memiliki sensitivitas sebesar 2,12 μA/μM/cm2 (R2 0,9904). Sensor SPCE/MWCNT/Au 1-60 dengan metode kronoamperometri ini memiliki limit deteksi (LOD) dan limit kuantifikasi (LOQ) sebesar 2,99 μM dan 9,96 μM.

---

Diabetes is one of many chronic diseases that most people suffer nowadays. Insulin is an important hormone that regulates blood sugar to prevent diabetes. Since the cost of insulin detection instrument, a cheap, fast, and sensitive sensor for insulin detection is needed. One of them is a carbon-based electrochemical sensor. In this study, screen printed carbon electrode (SPCE) with multiwalled carbon nanotube (SPCE/MWCNT) and gold nanoparticles (AuNPs) with sizes of 42,2 ± 8,7 nm (SPCE/MWCNT/Au 1-20) and 56,9 ± 6,3 nm (SPCE/MWCNT/Au 1-60) which have been synthesized by the Turkevich method were selected for insulin determination. Morphology characterization with SEM showed the gold nanoparticles had been deposited into the sensor and had agglomerated. Active surface area of the SPCE/MWCNT/Au 1-20, SPCE/MWCNT/Au 1-60 and SPCE/MWCNT sensors enhanced to 0,250 ± 0,007 cm2, 0,127 ± 0,001 cm2, 0,136 ± 0,002 cm2 from 0,108 ± 0,001 cm2 of bare SPCE. EIS result showed each charge transfer resistance (Rct) of SPCE/MWCNT/Au 1-20, SPCE/MWCNT/Au 1-60 and SPCE/MWCNT are 124,62 Ω, 240,03 Ω dan 230,50 Ω. The SPCE/MWCNT, SPCE/MWCNT/Au 1-20 and Au 1-60 were oxidized at 0,5 V, 0,42 V, and 0,44 V, respectively, when given 0,15 μM to 10,0 μM insulin lispro diluted in 0,1 M phosphate buffer solution (pH 7). The SPCE/MWCNT/Au 1-60 with sensitivity of 16,25 μA/μM/cm2 (R2 0,98072) displayed a significant increase of sensitivity on cyclic voltammetry measurement to SPCE/MWCNT by 25,67%. The limit of detection (LOD) and limit of quantification of the sensor are 1,55 μM and 5,18 μM. Chronoamperometry measurement showed SPCE/MWCNT/Au 1-60 good sensitivity of 2,17 μA/μM/cm2 (R2 0,99758), LOD of 2,99 μM and LOQ of 9,96 μM. The sensitivity of the sensor in chronoamperometry measurement has not improved significantly from SPCE/MWCNT sensor."

"Sistem evaporasi fototermal telah menjadi solusi yang menjanjikan dalam mengatasi krisis air bersih dalam beberapa tahun terakhir. Sistem ini menggunakan energi matahari untuk menguapkan air yang tercemar atau air laut, meninggalkan zat-zat berbahaya atau garam dan menghasilkan air bersih yang dapat digunakan kembali. Molibdenum disulfida (MoS2) merupakan salah satu material fototermal yang menarik karena memiliki karakteristik penyerapan sinar yang luas pada daerah cahaya tampak. Hal ini memungkinkan MoS2 untuk mengkonversikan sinar matahari menjadi panas dengan efisiensi yang tinggi. Penting untuk mempelajari morfologi, struktur mikro, dan sifat optik dari MoS2. Annealing adalah proses perlakuan panas yang dilakukan pada material untuk mengubah struktur kristal dan sifat-sifatnya. Dengan mengontrol parameter annealing seperti suhu dan waktu, kita dapat mengubah morfologi partikel MoS2 menjadi bentuk yang diinginkan. Perubahan ini dapat berdampak pada penyerapan sinar matahari dan efisiensi konversi energi fototermal. Disini, kami menganalisis pengaruh perlakuan annealing terhadap morfologi, mikro struktur MoS2. Hasil pengujian kinerja evaporasi fototermal menunjukkan bahwa sampel MoS2-400 memiliki laju evaporasi tertinggi, yaitu sebesar 1,65 kg/m2h. Berdasarkan hasil ini, dapat disimpulkan bahwa perlakuan annealing dapat berpengaruh dan meningkatkan kinerja laju evaporasi fototermal.

---

Photothermal evaporation systems have emerged as a promising solution to overcome the clean water crisis in recent years. This system utilizes solar energy to evaporate polluted air or seawater, leaving behind harmful substances or salts and producing clean water that can be reused. Molybdenum disulfide (MoS2) is an interesting photothermal material due to its wide absorption characteristic in the visible light region, allowing it to efficiently convert sunlight into heat. Therefore, it is essential to study the morphology, microstructure, and optical properties of MoS2. Annealing is a heat treatment process performed on a material to alter its crystal structure and properties. By controlling the annealing parameters such as temperature and time, we can change the morphology of the MoS2 particles to the desired shape. These changes can significantly impact the absorption of sunlight and the efficiency of photothermal energy conversion. In this study, we analyze the effect of the annealing treatment on the morphology and microstructure of MoS2. The results of the photothermal evaporation performance test revealed that the MoS2-400 sample exhibited the highest evaporation rate, reaching 1.65 kg/m2 h. Based on these findings, we can infer that the annealing settings can influence and enhance the performance of the photothermal evaporation rate."

"Paduan aluminium banyak digunakan dalam berbagai aplikasi, terutama di bidang otomotif dan penerbangan karena keunggulannya. Aluminium bersifat ringan, kekuatan tinggi, serta densitas rendah. Namun, sifat mekanik dan ketahanan korosinya perlu ditingkatkan. Plasma Electrolytic Oxidation (PEO) adalah metode terbaru untuk melindungi aluminium dengan menumbuhkan lapisan keramik oksida pada permukaannya. Dalam penelitian ini, proses PEO dilakukan pada paduan aluminium seri 1100 dan 7075-T735 dengan elektrolit campuran 30 g/Na2SiO3, 30 g/l KOH, dan 20 g/l TEA dengan rapat arus 200 A/m2 selama 6 menit. Kedua jenis seri paduan tersebut digunakan sebagai pembanding dalam proses PEO dimana seri 1100 tergolong Al murni sedangkan seri 7075 memiliki banyak presipitat. Hasil uji korosi dengan menggunakan uji elektrokimia menunjukkan bahwa sampel AA7075-T735 berlapis PEO memiliki ketahanan korosi yang paling baik. Hal ini dibuktikan dengan nilai rapat arus korosi (icorr) terendah, yaitu mencapai 5,91x10-7 A.cm-2 dan loop kapasitif yang paling besar serta ketidakhadiran loop induktif pada kurva Nyquist. Dari uji hilang berat juga diperoleh hasil rata-rata hilang berat yang lebih rendah pada sampel AA7075-T735 dibandingkan dengan AA1100. Ketahanan korosi sampel berlapis PEO mengikuti perilaku substratnya. Sampel AA1100 mengalami degradasi coating yang lebih dominan daripada AA7075-T735. Hal ini berkaitan dengan porositas dan kepadatan lapisan PEO pada kedua sampel.

---

Aluminum alloys are widely used in various applications, especially in the automotive and aviation industries, due to their advantages. Aluminum is lightweight, has high strength, and low density. However, its mechanical properties and corrosion resistance need improvement. Plasma Electrolytic Oxidation (PEO) is the latest method used to protect aluminum by growing a ceramic oxide layer on its surface. In this study, the PEO process was applied to aluminum alloys of series 1100 and 7075-T735 using an electrolyte mixture of 30 g/L Na2SiO3, 30 g/L KOH, and 20 g/L TEA with a current density of 200 A/m2 for 6 minutes. Both alloy series were used as comparators in the PEO process, with series 1100 being classified as pure Al, while series 7075 has numerous precipitates. Corrosion tests using electrochemical analysis showed that the PEO-coated AA7075-T735 sample exhibited the best corrosion resistance. This was evident from its lowest corrosion current density (icorr) value, which reached 5.91x10-7 A.cm-2 , as well as the largest capacitive loop and the absence of an inductive loop in the Nyquist curve. Weight loss tests also indicated that the average weight loss was lower in the AA7075-T735 sample compared to AA1100. The corrosion resistance of the PEO-coated samples followed the behavior of their substrates. The AA1100 sample experienced more dominant coating degradation compared to AA7075-T735, which was related to the porosity and density of the PEO layer in both samples."

"Material La0,8K0,2MnO3 telah berhasil disintesis menggunakan metode Sol-Gel pada variasi suhu sintering 750℃, 800℃, 900℃, dan 1000℃. Uji karakterisasi XRD menunjukkan bahwa sampel membentuk fasa tunggal tanpa unsur pengotor dengan struktur Rhombohedral space group R-3c. Variasi suhu sintering yang semakin tinggi mengindikasikan pertumbuhan grain pada sampel yang semakin cepat, oleh sebab itu grain pada sampel menunjukkan peningkatan ukuran rata-rata seiiring meningkatnya suhu sintering. Material La0,8K0,2MnO3 memiliki sifat ferromagnetik disebabkan doping ion monovalen K+ yang menyebabkan muncul valensi baru Mn4+. Ion Mn4+ ini akan bereaksi dengan ion Mn3+, di mana elektron pada Mn3+ akan berpindah ke ion Mn4+ melewati ion O2-, reaksi ini disebut reaksi double exchange. Reaksi ini bergantung dengan hubungan ikatan antar ion Mn dan O, di mana jika jarak jari-jari ikatan Mn-O semakin dekat dan sudut ikatan Mn-O-Mn semakin lebar akan mempermudah perpindahan elektron ini sehingga sifat magnetik pada material akan semakin baik. Dari data ikatan atom yang diperoleh dari hasil refinement pola XRD, variasi suhu sintering sebesar 900℃ menjadi kandidat sebagai material yang memiliki sifat magnetik paling baik. Hal ini dikonfirmasi dengan hasil uji karakterisasi VSM yang menunjukkan puncak saturasi magnetisasi terhadap medan magnet eksternal tertinggi adalah sampel dengan suhu sintering 900℃, diikuti 800℃, 1000℃, dan terendah 750℃. Dari uji VNA juga diketahui bahwa penyerapan gelombang mikro yang terbaik terjadi pada sampel dengan suhu sintering 750℃.

---

Material La0,8K0,2MnO3 has been successfully synthesized using the Sol-Gel method at various sintering temperatures of 750℃, 800℃, 900℃, and 1000℃. The XRD characterization test showed that the sample formed a single phase without any impurity elements with the Rhombohedral space group R-3c structure. The higher sintering temperature variation indicates faster grain growth in the sample, therefore the grains in the sample show an increase in average size as the sintering temperature increases. The material La0,8K0,2MnO3 has ferromagnetic properties due to the doping of monovalent K+ ions which causes a new valency of Mn4+ to appear. This Mn4+ ion will react with Mn3+ ions, where electrons in Mn3+ will hop to Mn4+ ions through O2- ions, this reaction is called a double exchange reaction. This reaction depends on the bond relationship between Mn and O, where if the Mn-O bond radius is closer and the Mn-O-Mn bond angle is wider it will make it easier to bind these electrons so that the magnetic properties of the material will be better. From the atomic bond data obtained from the refinement of the XRD pattern, the sintering temperature variation of 900℃ is a candidate as the material with the best magnetic properties. This was confirmed by the results of the VSM characterization test which showed that the highest peaks of magnetization saturation to external magnetic fields were samples with a sintering temperature of 900℃, followed by 800℃, 1000℃, and the lowest was 750℃. From the VNA test it is also known that the best absorption of microwaves occurs in samples with a sintering temperature of 750℃."

"Komposit sandwich merupakan komposit struktur yang diproduksi menjadi panel atau balok ringan yang memiliki sifat kekakuan dan kekuatan yang tinggi. Penelitian ini bertujuan untuk membandingkan sifat mekanik dan morfologi komposit sandwich kulit polyester berpenguat woven roving E glass dan inti honeycomb polypropylene yang difabrikasikan dengan teknik VARI dan adhesif cold-press. Pengujian mekanik yang dilakukan pada penelitian ini adalah uji lentur, uji tarik, dan uji tekan. Pengamatan morfologi pada sebelum dan sesudah pengujian dilakukan dengan menggunakan kamera. Hasil penelitian ini menunjukkan bahwa fabrikasi adhesif cold-press memiliki nilai kekuatan lentur, tarik, dan tekan yang lebih unggul dibandingkan dengan metode VARI yaitu masing-masing sebesar (24,93 ± 0,21) MPa, (0,52 ± 0,02) MPa, dan (1,95 ± 0,05) MPa. Setelah uji lentur, tarik, dan tekan, sampel mengalami kerusakan pada bagian inti.

---

Sandwich composites are structural composites that are manufactured into lightweight panels or beams with high stiffness and strength properties. This study aimed to compare the mechanical properties and morphological of polyester skin sandwich reinforced with woven roving E-glass reinforced polyester as skins and a polypropylene honeycomb core fabricated by the VARI and cold-press adhesive techniques. The mechanical tests which were flexural, tensile, and compressive tests were conducted. Morphological observations before and after testing were carried out using a camera. The results of this study indicated that the cold-press adhesive fabrication had superior flexural, tensile, and compressive strength values compared to the ones of VARI method, namely (24,93 ± 0,21) MPa, (0,52 ± 0,02) MPa, and (1,95 ± 0,05) MPa respectively. After bending, tensile, and compressive tests, all samples were failed in the core."