Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Material polikristalin La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05) telah berhasil disintesis menggunakan metode sol-gel. Analisis hasil karakterisasi X-Ray Diffractometer (XRD) menunjukkan bahwa material La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05) yang telah disintesis merupakan material fasa tunggal dengan struktur rhombohedral dan space group R-3c. Hasil karakterisasi XRD juga diperkuat oleh hasil karakterisasi Energy Dispersive X-ray (EDX) dan X-ray Photoelectron Spectroscopy (XPS) yang telah menunjukkan bahwa semua jenis senyawa kimia yang terdapat pada material La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05) merupakan senyawa yang diinginkan. Observasi morfologi menggunakan Scanning Electron Microscope (SEM) menujukkan bahwa substitusi ion potasium berdampak pada terjadinya perbesaran ukuran grain. Karakterisasi Magnetic Properties Measurement System (MPMS) menunjukkan bahwa substitusi ion potasium menyebabkan terjadinya peningkatan temperatur Curie dari 320 K, untuk nilai x = 0, menjadi 335 K, untuk nilai x = 0,05. Peningkatan ini disebabkan karena menguatnya interaksi double-exchange pada sampel dengan nilai x = 0,05. Substitusi ion potasium juga berdampak pada terjadinya peningkatan nilai perubahan entropi magnetik (A𝑆𝑀) dan nilai Low Field Magnetoresistance (LFMR). Nilai −Δ𝑆𝑀 material La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05) meningkat dari 4,21 J/kg K menjadi 4,98 J/kg K pada medan magnet eksternal lima Tesla. Sementara itu, nilai LFMR mengalami peningkatan dari 9% menjadi 14% pada medan magnet eksternal satu Tesla. Berdasarkan hasil analisis perilaku kritis dari material La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05) dapat disimpulkan bahwa substitusi ion potasium mempengaruhi perilaku kritis dari material La0.8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05). Hal ini dibuktikan dengan berubahnya nilai parameter kritis dari material tersebut. Nilai parameter kritis untuk x = 0 adalah 𝛽 = 0,248; 𝛾 = 1,048; dan 𝛿 = 3,342 sedangkan nilai parameter kritis untuk x = 0,05 adalah 𝛽 = 0,226; 𝛾 = 1,183; dan 𝛿 = 4,518. Karakterisasi ESR menunjukkan adanya fasa magnetik yang tidak homogen pada material La0,8-xKxBa0,05Sr0,15MnO3 (x = 0 dan 0,05). Keberadaan fasa magnetik yang tidak homogen ini merupakan bukti terjadinya fenomena phase separation yang berkorelasi kuat terhadap terjadinya peningkatan nilai A𝑆𝑀 dan nilai LFMR.

---

Exploration on the magnetic properties of polycrystalline La0.8-xKxBa0.05Sr0.15MnO3 (x = 0 and 0.05) manganite have been reported. The samples have been synthesized using sol-gel method. Powder diffraction analysis shows that both samples crystallized in rhombohedral structure with R-3c space group. Furthermore, rietveld refinement analysis proves that the obtained samples are single phase, without any detectable impurities. This argument is also supported by the characterization result from Energy Dispersive X-ray (EDX) and X-ray Photoelectron Spectroscopy (XPS). Morphological observation using Scanning Electron Microscope (SEM) shows that potassium substitution increases the average grain size of the studied samples. Magnetization measurement with respect to temperature shows that the curie temperature (𝑇𝐶) of sample with potassium ion is larger compared to the undoped sample. The reported 𝑇𝐶 was be 320 and 335 K for x = 0 and x = 0.05, respectively. Detailed inspection upon the magnetocaloric property of the samples shows that potassium substitution increases the magnetic entropy change (A𝑆𝑀) of the sample. The reported −Δ𝑆𝑀 value was 4.21 and 4.98 J/kg K for x = 0 and x = 0.05, respectively. It was found that both samples exhibit a Low Field Magnetoresistance (LFMR) phenomenon at low temperature and low external magnetic field (< 1T). Moreover, potassium substitution increases the estimated LFMR value from 9 to 14% for x = 0 and x = 0.05, respectively. The analysis on the critical behavior of both samples shows that potassium substitution affects the critical behavior of the studied samples. This is shown by the different critical parameters for each sample. The reported critical parameter for x = 0 are 𝛽 = 0.248; 𝛾 = 1.048; 𝛿 = 3.342 and the critical parameters for x = 0.05 are 𝛽 = 0.226; 𝛾 = 1.183; and 𝛿 = 4.518. Electron Spin Resonance (ESR) characterization reveals that there is a presence of magnetic inhomogeneity inside both samples. The presence of magnetic inhomogeneity suggests that both samples exhibit a phase separation phenomenon. This phenomenon is believed to greatly influence the increase of A𝑆𝑀 and LFMR value in the studied samples.

Abstrak :
Penelitian dilakukan dengan mensubstitusikan Ti kedalam bahan Mn pada paduan La0,67Ca0,33Mn1-xTixO3 (x = 0,04; 0,06; 0,08; 0,10; 0,12). Proses perlakuan terhadap sampel meliputi penggerusan atau milling selama 25 jam, pemanasan atau kalsinasi pada suhu 400°C selama 5 jam, pembuatan pelet atau kompaksi, pemanasan sampel melebihi titil leleh atau sintering pada suhu 1200°C selama 12 jam. Setiap milling dan kalsinasi dilakukan karakterisasi dengan menggunakan XRD. dan karakterisasi. Dan setelah sintering seluruh karakterisasi dilakukan. Karakterisasi yang dilakukan meliputi karakterisasi struktur atom dengan XRD, karakterisasi morfologi struktur mikro bahan dengan SEM, karakterisasi komposisi bahan dengan menggunakan EDAX, dan karakterisasi sifat kelistrikan dengan menggunakan LCR meter. Setelah seluruh rangakian proses dilakukan, hasilnya menunjukan bahwa terjadi fasa baru setelah dilakukan sintering, morfologi mikro permukaan menunjukan ukuran partikel terkecil pada x = 0,10 dengan pembesaran 2500x, komposisi sampel terkait penambahan Ti menunjukan kenaikan pada parameter kisi (a,b,c), dan volumenya. Karakterisasi sifat listrik menujukkan konduktivitas bahan tertinggi pada x =0,10. ......The study was conducted by substituting Ti into Mn material on la0 material, 67Ca0, 33Mn1 - xTixO3 ( x = 0.04 ; 0.06 ; 0.08 ; 0.10, 0.12 ). Treatment of samples includes milling for 25 hours, calcination at 400°C for 5 hours , pelletizing , sintering at a temperature of 1200°C for 12 hours. After milling and calcination, then performed using XRD characterization. and after sintering characterization SEM, EDS, EDAX, LCR, VNA. Characterization was conducted on the characterization of the atomic structure using XRD, morphological characterization of the microstructure of materials using SEM, characterization of material composition using EDAX, and electrical characterization using LCR meter. After the whole process is done, the results showed that there was a new phase after sintering, micro surface morphology showed the smallest particle size in the x = 0.10 with 2500x magnification . Ti substitution showed an increase in the lattice parameters ( a, b , c ), and volume. Characterization of the electrical properties of the material showed the highest conductivity at x = 0.10.