Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Pada penelitian ini dilakukan sintesis senyawa analog kalkon (1,5-Difenil-2,4-pentadien-1-on) dari sinamaldehida (0,01 mol) dan asetofenon (0.01 mol) melalui reaksi kondensasi aldol silang menggunakan katalis CaO dan uji sitotoksik sel murin leukemia P-388 serta dilanjutkan dengan sintesis senyawa pirazol (3-fenil-5-styril-1H-pirazol) melalui reaksi senyawa analog kalkon dengan hidrazin hidrat. Preparasi katalis CaO dilakukan dari cangkang telur bebek melalui metode kopresipitasi dan dihasilkan distribusi ukuran partikel CaO 57-94 nm dalam medium polietilen glikol. Reaksi optimasi pada penambahan jumlah katalis (0,2 g) menghasilkan persen konversi senyawa analog kalkon sebesar 99,2 % dan lama reaksi pemanasan selama 8 jam dengan komposisi hidrazin hidrat 55%-60% (0,02 mol) diperoleh persen konversi senyawa pirazol sebesar 83,71 %. Karakterisasi menggunakan spektrofotometri UV-Visible menunjukkan adanya pergeseran batokromik pada senyawa analog kalkon sebesar 59 nm. Spektrofotometri infra merah menunjukkan pada senyawa analog kalkon terdapat ikatan C=O pada bilangan gelombang 1654,03 cm-1 dan pada senyawa pirazol menunjukkan adanya ikatan C=N pada bilangan gelombang 1679,11 cm-1. Hasil kromatografi gas dan spektroskopi massa diperoleh senyawa analog kalkon muncul pada waktu retensi 16,64 menit dengan nilai m/z sebesar 234,2 dan senyawa pirazol diperoleh pada waktu retensi 22,74 menit dengan nilai m/z sebesar 246,1. Senyawa analog kalkon sangat aktif sebagai senyawa antikanker dengan nilai IC50 = 1,503 µg/mL pada hasil uji sel murin leukemia P-388. ...... This research was conducted a synthesis of chalcone analog compound (1,5-Diphenyl-2,4-pentadien-1-on) of cinnamaldehide (0.01 mol) and acetophenone (0,01 mol) by a cross aldol condensation reaction using CaO catalysts and cytotoxic test cell murine leukemia P-388 and proceeded with the synthesis of pyrazole compound (3-phenyl-5-styril-1H-pyrazole). The CaO catalyst preparation from duck egg shell through coprecipitation method resulted CaO particle size distribution 57-94 nm in medium of polyethylene glycol. Optimization result by adding catalyst (0.2 g) produced the highest percent conversion of chalcone analog compound by 99.2% and heating reaction for 8 hours with the hydrazine hydrate (0.02 mol) obtained 83.71% conversion of pyrazole compound. The characterization using UV-Visible spectrophotometry showed a bathochromic shift in chalcone analog compound by 59 nm. Infrared spectrophotometry showed C=O vibration of the chalcone analog compound at 1654.03 cm-1 and C=N vibration of pyrazole compound at 1679.11 cm-1. Gas chromatography and mass spectroscopy analysis gave chalcone analog compound a retention time of 16.64 minutes with m/z values ​​of 234.2 and pyrazole compound a retention time of 22.74 minutes with m/z value of 246.1. This chalcone analog compound is very active as an anticancer compound with IC50 value of 1.503 µg/mL in murine leukemia cells P-388 assay.

Abstrak :

Transesterifikasi adalah reaksi kimia yang digunakan untuk mengubah minyak hewani menjadi biodiesel yang dapat digunakan. Pada penelitian ini, bahan bakar biodiesel disintesis dari lemak sapi dalam reaktor menggunakan katalis CaO yang disintesis dari cangkang telur bebek. Katalis CaO berbasis limbah disintesis dari cangkang telur bebek melalui proses kalsinasi pada suhu 900 ^OC selama 2 jam. Transesterifikasi dilakukan pada suhu 55 ^OC pada 6 sampel dengan variasi penggunaan jumlah katalis (1.5 wt%, 6.5 wt%, dan 10 wt%) serta variasi katalis CaO komersial dan limbah. Katalis yang disintesis dari cangkang telur itik menghasilkan kadar Kalsium Oksida (CaO) sebesar 93.2%. Hasil pengujian sampel terbaik diperoleh untuk biodiesel dengan katalis 6.5% berbahan dasar limbah dan 10% katalis komersial. Untuk biodiesel dengan katalis berbasis limbah 6.5%, rendemen 90.75%, densitas 855.1 kg/m3, viskositas 5.73 mm2/cst, keasaman 1.69 mg-KOH/g, dan bilangan yodium 30.87 g-I2/100g. Untuk biodiesel dengan katalis berbasis limbah 10%, rendemen 90.81%, densitas 860.5 kg/m3, viskositas 6.52 mm2/cst, keasaman 2.03 mg-KOH/g, dan bilangan yodium 27.51 g-I2/100g. Angka keasaman standar tidak tercapai dimana maksimumnya adalah 0.5 mg-KOH/g.

---

Transesterification is a chemical reaction used to convert animal oils into usable biodiesel. In this study, biodiesel fuel was synthesized from beef tallow in a reactor using a CaO catalyst which also synthesized from duck eggshells. Waste-based CaO catalyst synthesized from duck eggshells through a calcination process at 900 ^OC for 2 hours. Transesterification carried out at a temperature of 55 ^OC on 6 samples with variations in the use of the amount of catalyst (1.5 wt%, 6.5 wt%, and 10 wt%) as well as variations of commercial and waste based CaO catalysts. The catalyst synthesized from duck eggshells obtained a yield of 93.2% amount of Calcium Oxide (CaO). The synthesized biodiesel also tested for its chemical and physical properties to fulfill the Indonesian National Standard (SNI). The best sample test results were obtained for biodiesel with 6.5% catalyst from waste-based and 10% catalyst from commercial. For biodiesel with 6.5% waste-based catalyst, 90.75% yield, 855.1 kg/m3 density, 5.73 mm2/cst viscosity, 1.69 mg-KOH/g acidity, and 30.87 g-I2/100g iodine number. For biodiesel with 10% waste-based catalyst, 90.81% yield, 860.5 kg/m3 density, 6.52 mm2/cst viscosity, 2.03 mg-KOH/g acidity, and 27.51 g-I2/100g iodine number. The standard acidity number is not reached where the maximum is 0.5 mg-KOH/g.

Abstrak :
Transesterifikasi adalah reaksi kimia yang mengubah minyak hewani menjadi biodiesel yang berguna melalui proses kimia transesterifikasi. Pada penelitian ini, biodiesel diproduksi dengan cara mentransesterifikasi lemak sapi dalam reaktor dengan katalis CaO berbahan dasar cangkang telur puyuh. Enam sampel menjalani transesterifikasi pada suhu 55 ^OC dengan perbedaan jumlah katalis yang digunakan (1,5 wt%, 6,5 wt%, dan 10 wt%). Variasi jenis katalis, yang terdiri dari katalis komersial dan berbasis limbah, juga dipakai dalam penelitian ini. Katalis CaO berbasis limbah disintesis dari cangkang telur puyuh melalui proses kalsinasi pada suhu 900 ^OC dengan durasi 2 jam. Katalis berhasil disiapkan dengan persentase hasil 92,4% kalsium oksida. Hasil pengujian sampel terbaik ditunjukkan oleh biodiesel dengan penggunaan katalis berbasis limbah 6,5% dan katalis komersial 6,5%. Untuk biodiesel dengan katalis berbasis limbah 6,5%, diperoleh yield 91,747%, densitas 856 kg/m3, viskositas 5,2915 mm2/cst, angka keasaman 0,94 mg-KOH/g, dan angka iodin 33,96 g-I2/100g. Untuk biodiesel dengan katalis komersial 6,5% diperoleh yield 90,236%, densitas 861,1 kg/m3, viskositas 5,414 mm2/cst, angka keasaman 4,13 mg-KOH/g, dan angka iodin 29,37 g-I2/100g. Angka keasaman standar dengan maksimum 0,5 mg-KOH/g tidak dipenuhi oleh kedua sampel. ...... Transesterification is a chemical reaction that transforms animal oils into useful biodiesel by the chemical process of transesterification. In this study, the biodiesel is produced by transesterifying beef tallow in a reactor with a CaO catalyst made from quail eggshell. Six samples are subjected to transesterification at a temperature of of 55 ^OC with different amounts of catalyst being used (1.5 wt%, 6.5 wt%, and 10 wt%). A variation of catalyst type, that consists of the commercial and waste-based catalyst, is also integrated to this study. Waste-based CaO catalyst is synthesized from quail eggshells through a calcination process at 900 ^OC with the duration of 2 hours. The catalyst was successfully prepared with the yield percentage of 92.4% calcium oxide. The best sample test results were exhibited by the biodiesel with the usage of 6.5% waste-based catalyst and 6.5% commercial catalyst. For biodiesel with 6.5% waste-based catalyst, 91.747% yield, 856 kg/m³ density, 5.2915 mm²/cst viscosity, 0.94 mg-KOH/g acidity number, and 33.96 g-I₂/100g iodine number were obtained. For biodiesel with 6,5% commercial catalyst, 90.236% yield, 861.1 kg/m³ density, 5.414 mm²/cst viscosity, 4.13 mg-KOH/g acidity number, and 29.37 g-I₂/100g iodine number were obtained. The standard acidity number with the maximum of 0.5 mg-KOH/g is not satisfied by both samples.