Abstrak :
Pada penelitian ini berhasil disintesis natrium alginat tercangkok poli akrilat-co-akrilamida yang dikompositkan dengan montmorillonite MMT , dan dengan penambahan mikronutrien berupa asam borat dan boraks ke dalam superabsorben nanokomposit dengan metode in situ dan eksitu. Kapasitas swelling optimum superabsorben nanokomposit pupuk lepas lambat asam borat dan boraks dengan metode in situ berturut ndash; turut adalah 247,030 g/g dan 515,093 g/g, sedangkan dengan metode eksitu adalah 305,421 g/g dan 455,514 g/g. Kapasitas release optimum superabsorben nanokomposit pupuk lepas lambat asam borat dan boraks dengan metode in situ berturut ndash; turut adalah 68,59 dan 72,76 , sedangkan pada metode eksitu 61,66 dan 78,08. Digunakan FTIR, SEM, TEM, XRD dan UV-Vis untuk mengkaraterisasi. Di dapatkan kapasitas release optimum mikronutrien dari superabsorben nanokomposit pupuk lepas lambat in situ pada pengujian UV-Vis untuk asam borat sebesar 2,328 ppm, sedangkan boraks sebesar 1,587 ppm. Untuk parameter laju swelling didapatkan dengan parameter laju optimum untuk superabsorben nanokomposit terhadap air, larutan asam borat, dan larutan boraks berturut-turut adalah 256,0177; 227;9296; 173;7719. Untuk parameter laju swelling didapatkan dengan parameter laju optimum untuk superabsorben nanokomposit insitu asam borat dan boraks berturut-turut adalah 241,4187; 203,9398. Orde yang didapatkan pada superabsorben nanokomposit yaitu orde-pseudo 1. ...... In this study succeeded in synthesized sodium alginate poly acrylate co acrylamide with montmorillonite MMT , and by addition of micronutrients in the form of boric acid and borax into nanocomposite superabsorbents by in situ and ex situ method. The optimum swelling capacity of superabsorbent nanocomposite of slow release of boric acid and borax by in situ method were 247.030 g g and 515,093 g g, respectively, with ex situ is 305,421 g g and 455,514 g g. The optimum release capacity of superabsorbent nanocomposite of slow release of boric acid and borax by in situ method was 68.59 and 72.76, respectively, while in the ex situ method 61.66 and 78.08. Used FTIR, SEM, TEM, XRD and UV Vis for electartizing. In obtaining the optimum release capacity of micronutrients from superabsorbent nanocomposite loose in situ fertilizers in UV Vis testing for boric acid was 2,328 ppm, while borax was 1,587 ppm. For swelling rate parameters with optimum rate parameters for superabsorbent nanocomposite to air, boric acid solution, and borax solution were 256,0177 227 9296 173 7719. For swelling rate parameters with optimum rate parameters for superabsorbent nanocomposites in situ boric acid and borax are 241,4187 203.9398. The order

Abstrak :
In order to develop the applications of radiations for biomaterial preparation, a non - toxic superabsorbent has been sinthesized. A series of superbaorbent hydrogel were prepared from aqueous solution containing 5% polyethylene oxide (PEO) with different concertration of alginate (0,5-2.0%) were irradiated at the doses of 20,30 and 40 kGy by gamma radiation. The gel fraction, swelling kinetics and the equilibrium degree of swelling (EDS) of the hydrogels were studied. It was found that the incorporation of even 2 % alginate (sodium salt) increased the EDS of the hydrogels from 20 g to 320 g/g. At a dose of 20 kGy, PEO - alginat hydrogels with high gel fraction (-80%) and very high EDS (-30 g/g) were obtained. The hydrogels were also found to be sensitive to the ionic solution of NaCL. The PEO - alginate hydrogels could be considered as candidate biomaterials in health care.

Abstrak :
uperabsorbent polymers (SAP) dapat dihimbau mendapatkan minat yang meningkat dari berbagai industry yang berbeda dalam beberapa tahun terakhir. Namun, mayoritas dari SAP diproduksi menggunakan petroleum sebagai bahan baku yang merupakan sebuah ancaman bagi lingkungan dikarenakan masa degradasi yang panjang. Polimer yang diproduksi dari selulosa merupakan sebuah alternatif yang menjanjikan dikarenakan properti biodegradasi. Efek dari crosslinking untuk biodegradasi SAP diuji terhadap beberapa properti yang berbeda. Literatur yang telah tercetak menunjukkan bahwa dengan crosslinking yang lebih kuat, maka daya tahan biodegradasi akan menjadi lebih tinggi. Namun, eksperimen pendahuluan yang telah dilakukan menunjukkan hasil yang berbeda. Selulase dari Trichoderma reesei di-analisa menggunakan beberapa teknik yang berbeda. Hasil analisis menunjukkan sebuah kecenderungan dimana biodegradasi terjadi lebih cepat di sampel yang telah di-crosslink. Alasan untuk hal tersebut, namun, tidak dapat ditentukan dikarenakan diluar cakupan riset. ......Superabsorbent polymers (SAPs) have seen an increase in interest from various different industries within the past few years. However, a majority of SAPs are produced using petroleum-based polymer which poses as a major environmental threat due to its long degradation period. SAPs produced from cellulose is a promising alternative due to its sustainable characteristics as well as its ease of biodegradation. The effect of crosslinking on the biodegradation of SAPs was tested. Current literature has shown that crosslinking increases stability and resistance to biodegradation. Nanocellulose foams, synthesized through a TEMPO-mediated oxidation process, were crosslinked using Hexamethylenediamine (HMDA) and tested through different analysis methods. UV-Vis spectrophotometry was used to analyse enzymatic activity, gas chromatography was used to test microbial activity, and high-performance liquid chromatography (HPLC) was used to analyse biodegradation testing. Cellulose from Trichoderma reesei was used as the enzyme for an enzymatic biodegradation process. The experimental results showed a trend which sees a higher rate of biodegradation in chemically crosslinked samples. This result may prove to be significant as it contradicts established literature. Experimental results, however, was unable to prove a possible reason relating to enzymatic activity due to unreproducible results. Other possible reasons were explored which includes HMDA crosslinking affecting the crystallinity and hydrophobicity of nanocellulose foam. These reasons have yet to be tested as it is outside the scope of research, however further research might prove beneficial as it may bring significant insight regarding crosslinking.

Abstrak :
Hidrogel superabsorben dapat menyerap dan menahan sejumlah besar larutan. Polimer superabsorben berdasarkan hidrogel kitosan disintesis dengan mengikatsilang kitosan dengan agen pengikat silang yang berbeda, yaitu Formaldehid, Asetaldehid, dan Glutaraldehid. Kemampuan swelling hidrogel kitosan terikat silang dilakukan dengan merendam gel dalam media cair dan pengaruh agen pengikat silang terhadap daya absorbsi air telah diamati. Hidrogel kitosan terikat silang dengan asetaldehid memperlihatkan rasio swelling paling tinggi hingga 350%. Pengaruh luar yang mempengaruhi seperti pH dan suhu media swelling diamati. Hidrogel memperlihatkan perilaku yang khas terhadap pH dan suhu media seperti pada media pH rendah (pH 4) dan suhu tinggi (55oC) swelling maksimal sedangkan pada pH tinggi (pH 10) dan suhu rendah (35oC) memperlihatkan swelling minimal. Film hidrogel kitosan terikat silang dikarakterisasi menggunakan Fourier Transform Infrared Spectroscopy (FTIR). ......Superabsorbent hydrogels are able to absorb and retain large amounts of aqueous fluids. Superabsorbent polymer based crosslinked chitosan hydrogels were synthesized by crosslinking chitosan with different crosslinking agents, i.e. formaldehyde, acetaldehyde and glutaraldehyde. The Swelling behavior of the crosslinked chitosan hydrogels was measured by immerse the gels and the effect of crosslinking agent on water absorbency has been investigated. The crosslinked chitosan hydrogel by acetaldehyde exhibited a higher swelling ratio up to 350%. The influence of external stimuli such as pH and temperature of the swelling media has been observed. Hydrogels showed a typical pH and temperature responsive behaviour such as low pH (pH 4) and high temperature (55oC) has maximum swelling while high pH (pH 10) and low temperature (35oC) show minimum swelling. The film of crosslinked chitosan hydrogels were characterized by Fourier Transform Infrared Spectroscopy (FTIR).

Abstrak :
Penelitian ini bertujuan untuk membuat pupuk slow-release nanokomposit superabsorben. Sintesis pupuk slow-release nanokomposit superabsorben dilakukan dalam 4 tahap. Tahap pertama, isolasi natrium alginat dari ganggang coklat diperoleh rendemen natrium alginat sebesar 44,32% dengan berat molekul 10163,819 g/mol. Keberhasilan isolasi didukung dengan karakterisasi menggunakan FTIR, XRD, SEM dan DSC. Tahap kedua, sintesis superabsorben nanokomposit menggunakan natrium alginat sebagai backbone, asam akrilat dan akrilamida sebagai monomer, kalium persulfat sebagai inisiator dan N,N-metilena bisakrilamida (MBA) sebagai pengikat silang serta zat anorganik bentonit sebagai filler. Kapasitas swelling superabsorben nanokomposit terbaik sebesar 576 g/g dan kapasitas swelling dan release terhadap larutan urea sebesar 629 g/g, dan 15 %. Hasil ini didukung dengan karakterisasi menggunakan FTIR, SEM dan DSC. Komposisi terbaik ini digunakan untuk sintesis pupuk slow release dengan metode polimerisasi insitu diperoleh kapasitas swelling air sebesar 638 g/g dan kapasitas release sebesar 72,76 %. Pupuk slow release dikarakterisaasi dengan FTIR dan SEM. ...... Superabsorbent nanocomposite fertilizer was synthezised in four steps. Initially, isolation alginate sodium from brown algae by extraction method. Sodium alginate obtained from extraction of brown algae used as the backbone for the synthesis of superabsorbent nanocomposite copolymerization.. The rendement of sodium alginate obtained was 44.32% with molecular weight of 10163,819 g/mol from measurement the intrinsic viscosity. The product isolation was characterized by FTIR, XRD, SEM, and DSC. The next step was synthesis of nanocomposite superabsorbent by acrylic acid and acrylamide as monomer, sodium alginate as backbone, potassium persulfate as inisiator, MBA as crosslinker and bentonite as filler by radical polimeryzation method. Optimazation of composition nanocomposite superabsorbent was done by swelling capacity. The results of swelling capacity in water gave 576 g/g for SA3 while swelling and release in urea solutions gave respectively 629 g/g and 15%. SA3 was characterized by FTIR, SEM, and DSC. The composition in synthesis of SA3 was used to synthesized slow release fertilizer and characterized by FTIR and SEM. Swelling and release capacity of fertilizer was 638 g/g and 72,76 % respectively

Abstrak :
Superabsorbent polymers SAP adalah material yang dapat menyerap cairan dalam jumlah yang sangat besar. Pada penelitian ini dilakukan sintesis material SAP dengan bahan baku natrium karboksimetil selulosa NaCMC yang berasal dari selulosa eceng gondok. Salah satu karakteristik NaCMC yang sangat berpengaruh adalah derajat substitusi DS . Semakin tinggi nilai DS dari NaCMC, semakin baik kemampuan SAP yang dihasilkan dalam menyerap cairan yang dinyatakan dengan swelling ratio SR . Jenis media yang digunakan dalam sintesis NaCMC sangat berpengaruh terhadap nilai DS. Semakin rendah polaritas media, semakin tinggi nilai DS yang dihasilkan. Penelitian ini bertujuan untuk menghasilkan NaCMC berbahan dasar eceng gondok dengan nilai DS yang tinggi dan menghasilkan material SAP dengan kemampuan mengabsorbsi air yang tinggi.Penelitian ini terdiri dari tiga tahap, yaitu isolasi selulosa, sintesis NaCMC, dan sintesis SAP. Isolasi selulosa dilakukan dengan menggunakan larutan NaClO2 dan NaOH untuk menghilangkan lignin dan hemiselulosa. Kemudian sintesis NaCMC dilakukan dengan menggunakan campuran dua larutan sebagai media reaksi agar diperoleh polaritas yang lebih rendah. Ada lima kombinasi campuran media reaksi yang digunakan, yaitu campuran isopropil alkohol-etanol IPE , 2-butanol-etanol BE , isobutil alkohol-etanol IBE , isopropil alkohol-2-butanol IPB , dan isopropil alkohol-isobutil alkohol IPIB dengan komposisi 20:80, 50:50, dan 80:20. Untuk masing-masing komposisi media, dilakukan variasi larutan NaOH 5-35 . NaCMC yang diperoleh dengan menggunakan media reaksi IPB, digunakan sebagai bahan baku pada sintesis SAP dengan menggunakan asam sitrat sebagai agen pengikat silang. Analisis dilakukan terhadap kadar selulosa di dalam eceng gondok dan selulosa hasil isolasi, nilai DS NaCMC, analisis menggunakan SEM, FTIR dan XRD terhadap selulosa dan NaCMC, serta pengukuran kadar Na di dalam alkali selulosa menggunakan AAS, sedangkan produk SAP dikarakterisasi menggunakan FTIR, SEM dan analisa SR.Hasil dari penelitian ini menunjukkan bahwa kadar selulosa dari produk selulosa sebesar 95,04 dan produk NaCMC eceng gondok memiliki nilai DS di atas 0,72. Nilai DS tertinggi dari NaCMC eceng gondok adalah 2,34 yang dicapai dengan menggunakan media campuran isopropil alkohol dan isobutil alkohol dengan komposisi 20:80 pada konsentrasi NaOH 35 . Produk material SAP yang dihasilkan dapat mencapai nilai SR sebesar 12,99.

---

Superabsorbent polymers SAP is a material which is able to absorb a considerable amount of liquid. In the present study, synthesis of SAP material using Sodium Carboxymethyl Cellulose NaCMC from water hyacinth cellulose as raw material was conducted. One of the most important characteristic of NaCMC is degree of Subtitution DS . Higher DS of NaCMC will improve the ability of produced SAP to absorb liquid, as measured by swelling ratio SR . Type of medium used in NaCMC synthesis also plays a significant role in DS value. Medium with low polarity will result in higher DS value. The aim of this study is to produce NaCMC from water hyacinth with high DS value, thus SAP material with high absorption ability can be obtained.This research consists of three main steps cellulose isolation, synthesis of NaCMC and synthesis of SAP. Isolation of cellulose was performed using NaClO2 and NaOH to remove lignin and hemicellulose content. Synthesis of NaCMC was then carried out using a mixture of two solutions as reaction medium in order to obtain low polarity medium. Five different combinations of reaction medium mixtures were used, i.e. isopropyl alcohol ethanol IPE , 2 butanol ethanol BE , isobuthyl alcohol ethanol IBE , isopropyl alcohol 2 butanol IPB , and isopropyl alcohol isobutyl alcohol IPIB with different ratios 20 80, 50 50 and 80 20 , followed by variation of NaOH 5 35 solution for each ratio. NaCMC obtained using reaction medium IPB was further utilized as raw material in synthesis SAP with citric acid as crosslinker agent. Cellulose content in water hyacinth and cellulose from isolation step and DS of NaCMC were measured. Cellulose and NaCMC were analyzed by SEM, FTIR and XRD. Measurement of Na content in alkali cellulose were performed using AAS, and SAP product was characterized by FTIR, SEM and SR analysis.The results obtained show that cellulose content of cellulose product is 95.04 and degree of subtitusion of NaCMC product from water hyacinth is above 0.72. Highest DS value of NaCMC from water hyacinth is 2.34, which was achieved using a mixture medium of isopropyl alcohol and isobutyl alcohol 20 80 at NaOH 35 . SR value of produced SAP material was 12.99.

Abstrak :
ABSTRAK
Pada penelitian ini, komposit superabsorben berbasis selulosa jerami padi dan bentonit telah berhasil disintesis. Selulosa jerami padi berhasil diisolasi dengan rendemen rata-rata sebesar 30,332%. Selanjutnya, selulosa hasil isolasi dipolimerisasi masing-masing menggunakan monomer asam akrilat dan akrilamida serta kalium persulfat digunakan sebagai inisiator dan N-N? dimetil bisakrilamida sebagai agen pengikat silang. Pada uji kapasitas swelling didapatkan bahwa superabsorben selulosa isolasi memiliki kapasitas swelling maksimum untuk air sebesar 189,894 g/g untuk monomer asam akrilat dan 149,77 g/g untuk monomer akrilamida. Kapasitas swelling maksimum untuk urea didapatkan nilai sebesar 604,543 g/g untuk monomer asam akrilat dan 137,308 g/g untuk monomer akrilamida. Kapasitas release superasorben selulosa jerami padi untuk air didapatkan nilai sebesar 77,508% untuk monomer asam akrilat dan 69,106% untuk monomer akrilamida. Kapasitas swelling untuk larutan urea diperoleh nilai 47,034% untuk monomer asam akrilat dan 18,835% untuk monomer akrilamida. Kinetika swelling dari superasorben didapatkan mengikuti kinetika pseudo orde satu untuk masing-masing superabsoben dengan hukum laju v=k[absorbat]. Dengan menggunakan metode kecepatan, didapat orde terhadap aborbat untuk swelling superabsorben monomer asam akrilat adalah 1,440 dan monomer akrilamida memiliki orde 1,476. Orde terhadap superabsorben didapatkan sebesar -0,777 pada monomer asam akrilat dan -0,065 pada monomer akrilamida. Superabsorben yang disentesis diuji menggunakan FTIR untuk mengetahui gugus fungsi, XRD untuk mengetahui derajat krstalinitas, SEM untuk mengetahui morfologi permukaan dan DSC untuk mengetahui fenomena dari pemanasan.

---

ABSTRAK
In this research, composite superabsorbent cellulose-based rice straw and bentonite have been successfully synthesized. Rice straw cellulose was isolated obtained an average yield 30.332%. After that, cellulose is polymerized using acrylic acid and acrylamide as monomer ,potassium persulfate as initiator and N-N 'dimethyl bisacrylamide as crosslinking agent. Through swelling capacity test,it was known that maximum swelling capacity of the rice straw cellulose superabsorbent grafted acrylic acid for water was about 189.894 g / g and by superabsorbent grafted acrylamide was about 149.77 g, while the maximum swelling capacity of urea by superabsorbent grafted acrylate acid was about 604,543 g/g and by superabsorbent grafted acrylamide was about 137,308 g/g. Then, the release capacity of water by superabsorbent grafted acrylic acid was about 77.508% and superabsorben grafted acrylamide was about 69.106%. The release capacity of urea by superabsorbent grafted acrylic acid was about 47.034% and superabsorbent grafted acrylamide was about 18.835%. The swelling kinetic from superabsorbent was obtained following the kinetic of pseudo first-order for each superabsorbent using rate law v=k[absorbat]. By using initial velocitiy method is obtained the order for the swelling superabsorbent grafted acrylic acid and acrylamide is 1,440 and 1,476 of the order for absorbate. Order of the superabsorbent obtained by -0.777 for superabsorbent grafted acrylic acid and superabsorbent grafted acrylamide is -0.065. Superabsorbent was tested using FTIR to determine the functional groups, XRD for knowing the degree of cristalinity, SEM to determine the surface morphology and DSC for knowing the the heat phenomenon

Abstrak :
ABSTRAK
Selulosa telah diisolasi dari jerami padi dengan proses penghilangan lignin, hemiselulosa dan bleaching dalam satu tahapan reaksi. Pada penelitian ini, rendemen selulosa hasil isolasi yang diperoleh 36,95 %. Kemudian selulosa hasil isolasi dari jerami padi dilakukan kopolimerisasi dengan asam akrilat dan akrilamida sebagai monomer, kalium persufat sebagai inisiator dan N,N‟ dimetil-bis-akrilamida sebagai pengikat silang. Kemudian, campuran tersebut dicampurkan bentonit sebagai bahan komposit dan kopolimerisasi dilakukan selama 2 jam pada suhu 70oC. Kapasitas swelling terbaik, baik dalam air maupun urea dengan konsentrasi 200 ppm adalah pada selulosa hasil isolasi dengan kapasitas swelling berturut-turut sebesar 427,94 g/g dan 410,07 g/g. Kapasitas release air dan urea dari superabsorben yang paling baik adalah pada selulosa murni dengan kapasitas release berturut-turut yaitu 67,452% dan 41,140%. Kinetika swelling dan release superabsorben selulosa jerami padi tercangkok poli(Asam akrilat-ko-akrilamida)/Bentonit mengikuti orde reaksi pseudo kedua dan memiliki persamaan laju reaksi v = k[Absorbat]2. Karakterisasi selulosa dan superabsorben dilakukan dengan spektroskopi FTIR untuk analisis gugus fungsi, XRD untuk analisis pola difraksi, SEM untuk melihat morfologi permukaan superabsorben, dan DSC untuk analisis ketahanan termal. Karakterisasi selulosa dan superabsorben dilakukan dengan spektroskopi FTIR untuk analisis gugus fungsi, XRD untuk analisis pola difraksi, SEM untuk melihat morfologi permukaan hidrogel, dan DSC untuk analisis ketahanan termal. Proses absorpsi mengikuti model isoterm adsorpsi Freundlich. Studi termodinamika proses absorpsi urea oleh superabsorben komposit selulosa jerami tercangkok poli (asam akrilat-ko-akrilamida)/bentonit berlangsung spontan dengan nilai ΔG˚ negatif, ΔH˚ sebesar 4,996 kJ/mol dan ΔS˚ sebesar 268,79 J/mol.

---

ABSTRACT
Cellulose had been isolated from rice straw with removal hemicellulose and lignin process and bleaching. In this study, the average rendement of cellulose isolated from rice straw obtained 36,95%. Then cellulose isolated from rice straw was copolymerized using acid acrylate and acrylamide as a monomer, Pottasium persulfat as inisiator and N,N‟ dimethyl-bis-acrylamide as crosslinking. This mixture was mixed with bentonite as composite materials and copolymerization was further carried out for 2 hours at 70oC. Swelling capacity of superabsorbent for cellulose isolated was the best in water and urea solution (200 ppm), with the swelling capacity were 427,94 g/g and 410,07 g/g, respectively. Release capacity of superabsorbent for pure celullose was the best, and the release capacity were 67,452% and 41,140% for water and urea solution respectively. urea at 681,26 g/g, the water release at 69,716% and 12,318% release of urea. Kinetics of swelling and release produced by rice straw superabsorbent cellulose grafted poly(arylic acid-co-acrylamide)/bentonite is followed pseudo second-order reaction and has a rate equation v=k[Absorbate]2 . Characterization of cellulose and superabsorbent by FTIR for the analysis of functional groups, XRD diffraction pattern for analysis, SEM to look at the morphology of the superabsorbent‟s surface, and DSC for analysis of thermal resistance. Absorption process fitted well with Freundlich isoterm model. Thermodynamics studies showed that absorption process of urea by superabsorbent composite of cellulose form rice straw grafted poly(AA-ko-Aam)/bentonite was spontaneously with negative value of ΔG˚, ΔH˚ 4,996 kJ/mole and ΔS˚ 268,79 J/mole.

Abstrak :
Superabsorben nanokomposit berbasis natrium alginat tercangkok poli akrilat-co-akrilamida yang dikompositkan dengan montmorillonite MMT , dan dengan penambahan pupuk NPK ke dalam superabsorben nanokomposit dengan metode polimerisasi in situ telah berhasil disintesis pada panelitian ini. Pada awal penelitian dilakukan isolasi natrium alginat dari ganggang coklat dengan persen rendemen rata-rata yang diperoleh sebesar 44,26 . Selanjutnya, natrium alginat hasil isolasi dikopolimerisasi dengan menggunakan asam akrilat dan akrilamida sebagai monomer, kalium persulfat sebagai inisiator, N,N '; metilen-bis-akrilamida MBA sebagai agen pengikat silang dan ditambahkan MMT untuk memperkuat sifat fisik dari superabsorben nanokomposit. Superabsorben nanokomposit dikarakterisasi dengan instrumen FTIR untuk analisis gugus fungsi, XRD untuk analisis indeks kristanilitas, dan SEM untuk melihat morfologi permukaan. Kapasitas swelling air, urea, KH2PO4, dan NH4 H2PO4 superabsorben nanokomposit natrium alginat menunjukkan nilai kapasitas terbaik, yaitu berturut-turut sebesar 475.8 g/g, 491.1 g/g, 122.9 g/g, dan 134.9 g/g. Kapasitas release air, urea, KH2PO4, dan NH4 H2PO4 superabsorben nanokomposit natrium alginat menunjukkan nilai kapasitas terbaik, yaitu berturut-turut sebesar 70.9 , 69.8 , 52.6 , dan 48.6 . Kapasitas swelling optimum superabsorben nanokomposit pupuk lepas lambat dengan in situ urea, KH2PO4, NH4 H2PO4, yaitu berturut - turut sebesar 423.3 g/g, 89.8 g/g, dan 138.1 g/g. Kapasitas release optimum superabsorben nanokomposit pupuk lepas lambat dengan in situ urea, KH2PO4, NH4 H2PO4, yaitu berturut - turut sebesar 55.0 , 35.3 , 28.2 . Kinetika orde swelling optimum SA9 FD terhadap larutan air, urea, KH2PO4, dan NH4 H2PO4 mengikuti hukum laju orde pseudo-pertama. Kinetika orde release optimum SA9 FD terhadap larutan KH2PO4, dan NH4 H2PO4 mengikuti hukum laju orde pseudo-pertama, sedangkan kinetika orde release optimum SA9 FD terhadap larutan air dan urea mengikuti hukum laju orde pseudo-kedua. Kinetika orde swelling optimum superabsorben nanokomposit pupuk lepas lambat in situ KH2PO4 SA17 FD terhadap air mengikuti hukum laju orde pseudo-pertama, sedangkan kinetika orde swelling optimum superabsorben nanokomposit pupuk lepas lambat in situ urea SA14 FD , dan in situ NH4 H2PO4 SA20 FD mengikuti hukum laju orde pseudo-kedua. Kinetika orde release optimum SA14 FD dan SA20 FD terhadap larutan NaCl 0.9 mengikuti hukum laju orde pseudo-pertama, sedangkan kinetika orde release optimum SA17 FD mengikuti hukum laju orde pseudo-kedua. Hukum laju reaksi orde pseudo-pertama mengikuti persamaan v=k[absorbat]^1, sedangkan hukum laju reaksi orde pseudo-kedua mengikuti persamaan v=k[absorbat]^2. ...... Superabsorbent nanocomposite based sodium alginate grafted poly acrylate co acrylamide composited with montmorillonite MMT , and with the addition of NPK fertilizers into superabsorbent nanocomposite by in situ polymerization methods have been successfully synthesized in this study. At the beginning of the study, the isolation of sodium alginate from brown algae with percentage of average yield was 44,26 . Furthermore, the isolated sodium alginate was copolymerized using acrylic acid and acrylamide as monomer, potassium persulfate as initiator, N, N 39 methylene bis acrylamide MBA as a crosslinking agent and MMT was added to enhance the physical properties of the superabsorbent nanocomposite. Superabsorbent nanocomposite were characterized by FTIR instruments for functional group analysis, XRD for christanility index analysis, and SEM for viewing surface morphology. The swelling capacity of water, urea, KH2PO4, and NH4 H2PO4 superabsorbent nanocomposite sodium alginate show the best capacity value, ie 475,8 g g, 491,1 g g, 122,9 g g, and 134,9 g g, respectively. The release capacity of water, urea, KH2PO4, and NH4 H2PO4 superabsorbent nanocomposite sodium alginate show the best capacity, ie 70,9 , 69,8 , 52,6 and 48,6 , respectively. The optimum swelling capacity of slow release fertilizer superabsorbent nanocomposites with in situ urea, KH2PO4, NH4 H2PO4, ie 423,3 g g, 89,8 g g, and 138,1 g g, respectively. The optimum release capacity of slow release fertilizer superabsorbent nanocomposites with in situ urea, KH2PO4, NH4 H2PO4, ie 55.0 g g, 35,3 g g, 28,2 g g, respectively. The optimum swelling order kinetics of SA9 FD against water, urea, KH2PO4, and NH4 H2PO4 solution follows the pseudo first order rate law. The optimum release order kinetics of SA9 FD against KH2PO4, and NH4 H2PO4 solution follows the pseudo first order rate law, whereas the optimum release order kinetics of SA9 FD against water and urea solution follows the pseudo second order rate law. The optimum swelling order kinetics superabsorbent nanocomposite fertilizer slow release in situ KH2PO4 SA17 FD against the water follows the pseudo first order rate law, while the optimum swelling order kinetics superabsorbent nanocomposite fertilizer slow release in situ urea SA14 FD , and in situ NH4 H2PO4 SA20 FD follows the pseudo second order rate law. The optimum release order kinetics SA14 FD and SA20 FD against 0.9 NaCl solution follows the pseudo first order rate law, while the optimum release order kinetics SA17 FD follows the pseudo second order rate law. The pseudo first order reaction rate law follows the equation v k absorbat 1, while the pseudo second order reaction rate law follows the equation v k absorbat 2.