Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Dimetil eter (DME) diproduksi secara langsung dari sintesis gas dalam reaktor fixed bed. Dalam penelitian ini, katalis Cu-Zn/Y-Al2O3 digunakan sebagai katalis bifungsi sintesis langsung dimetil eter dengan variasi pH dan komposisi serta dilakukan perbandingan antara metode kopresipitasi sedimentasi dengan sol-gel impregnasi. Katalis ini dikarakterisasi luas permukaan, XRF, dan XRD. Katalis ini direaksikan pada kondisi operasi tekanan 20 bar dan temperatur 220ºC. Hasil uji aktivitas katalis terbaik menunjukan konversi CO sebesar 70%, selektivitas dimetil eter sebesar 80%, dan yield dimetil eter sebesar 54%, yaitu pada katalis dengan metode sol-gel impregnasi. ......Dimethyl Ether (DME) was directly synthesized from synthesis gas (syngas) in fixed bed reactor. In this research, Cu-Zn/Y-Al2O3 used as bifunctional catalyst for synthesis of dimethyl ether and these catalysts was varied by pH, composition, and compared method between co-precipitation sedimentation and sol-gel impregnation method. These catalysts characterized by surface area, XRF, and XRD. These catalysts performance was tested at 20 bars, 220ºC. Activity result from the best catalyst in this research shown 70% conversion of CO, 80% selectivity and 54% yield of dimethyl ether, at catalyst with sol-gel impregnation method.

Abstrak :
ABSTRAK
Pada penelitian ini, katalis H2SO4/SiO2 dibuat dengan menggunakan metode immobilisasi sol-gel dan impregnasi pada silika gel. Katalis H2SO4/SiO2 dikarakterisasi dengan XRD, XRF, dan FTIR. Katalis yang dihasilkan diuji dengan metode leaching untuk mengetahui banyaknya asam sulfat yang terlepas dan digunakan pada reaksi esterifikasi. Persen leaching yang diperoleh dari impregnasi pada silika gel sebesar 4,78% per 0,1 g katalis dan untuk katalis solgel sebesar 7,1% per 0,1 g katalis. Berdasarkan hasil yang diperoleh, katalis solgel selanjutnya digunakan untuk reaksi esterifikasi asam-3,4,5-trihidroksibenzoat (asam galat) dan sukrosa dengan suhu 90 oC dan 110 oC, rasio mol asam galat dan sukrosa 2:3, 8:1, 9:1 dengan suhu optimum 110 oC, waktu reaksi 24 jam, 5% katalis dan pelarut DMSO. Sebelum reaksi esterifikasi, reaktan dicampur dan dipanaskan dalam oven microwave selama 4 menit dan dibandingkan dengan 10 menit. Hasil reaksi esterifikasi dianalisis menggunakan HPLC, FT-IR dan LCESI- MS dan menunjukkan sebagian besar asam galat telah bereaksi. Hasil LC-ESIMS menunjukkan hanya terbentuk monogalloyl glucose. Selanjutnya, produk ester diuji dengan metode DPPH radical scavenging dan menunjukkan bahwa ester yang dihasilkan memiliki IC50 34,68 ppm.

---

ABSTRACT In this research, the catalysts H2SO4/SiO2 were prepared by sol-gel and impregnation methods and were characterized with XRD, XRF and FT-IR. Both catalysts were tested by leaching method to determine the leaching of sulfuric acid and were used on the esterification reaction. Percent leaching of H2SO4 from the impregnated silica gel was 4.78% per 0.1 g catalyst and from the immobilized solgel was 7.1% per 0.1 g catalyst. Based on these results, sol-gel catalyst was used on the esterification reaction between 3,4,5-trihydroxyl benzoic acid (gallic acid) and sucrose at temperatures of 90oC and 110 oC, by varying the molar ratios of gallic acid/sucrose 2/3; 8/1 and 9/1 at optimum temperature of 110 oC, for 24 hours and 5% catalyst using DMSO as solvent. Prior to the esterification reaction, the reactants mixture was heated in a microvawe oven for 4 minutes compare to 10 minutes. The esterification reaction products were analyzed by HPLC, FT-IR and LC-ESI-MS and showed that almost all gallic acid was reacted. The LC-ESI-MS results indicated that only monogalloyl glucose was produced. Furthermore, the esterification product was determined by DPPH radical scavenging method and showed that IC50 from the ester was 34,68 ppm.

Abstrak :
Dimetil eter (DME) diproduksi dengan dua metode: (1) metode tidak langsung yang memiliki dua langkah prosedur, pembentukan metanol dari gas sintesis dilanjutkan dehidrasi metanol dan (2) metode langsung yang memiliki satu langkah prosedur yaitu proses pembentukan dimetil eter secara langsung dari gas sintesis. Sintesis langsung dimetil eter dari gas sintesis secara termodinamika lebih berprospek karena memiliki konversi yang lebih tinggi dan secara ekonomi memiliki biaya operasi yang rendah. Penelitian ini bertujuan membuat katalis bifungsi dengan karakteristik kristalinitas tinggi dan luas permukaan besar dengan aktivitas yang tinggi. Katalis yang digunakan adalah logam Cu-Zn sebagai katalis sintesis metanol dan Zeolit Alam Malang teraktivasi (HZAM). Metode preparasi katalis yang digunakan adalah kopresipitasi-sedimentasi dan sol gel-impregnasi. Dilakukan variasi temperatur kalsinasi pada 350, 500, dan 600°C. Pengujian terhadap zeolit alam teraktivasi yang dihasilkan adalah dengan menggunakan karakterisasi BET untuk mengetahui luas permukaan dan karakterisasi XRF untuk mengetahui rasio Si/Al di dalamnya. Pada katalis bifungsi dilakukan karakterisasi BET, XRD, dan XRF. Katalis bifungsi beroperasi pada kondisi tekanan 20 bar dan temperatur 220_C. Hasil uji aktivitas katalis terbaik yaitu pada katalis dengan metode kopresipitasi sedimentasi, menunjukan konversi CO sebesar 34% (% mol), selektivitas dimetil eter sebesar 55% (% mol), dan yield dimetil eter sebesar 19% (% mol). ......Dimethyl ether produced using methods (1) Indirect method, synthesis and dehidration of methanol (2) Direct method, synthesis dimethyl ether from syngas. It has higher conversion thermodynamically and lower operating cost. This research aims to make a bifunctional catalyst with some characteristic such as high crystalinity, high surface area, and high activities. Catalyst consists of Cu-Zn metal as synthesis methanol catalayst and activated natural zeolite as dehydration catalyst. Method using in preparation catalyst is coprecipitation sedimentation and sol gel impregnation. Variation is done in calcinations temperature, 350, 500, and 600°C. Activated natural zeolite characterized by BET to know surface area and XRF to know Si/Al ratio. Bifunctional catalyst characterized by BET surface area, XRD, and XRF. Operation condition of bifunctional catalyst is 20 bar and 220°C. Best catalyst activity, catalyst with coprecipitation sedimentation method show CO conversion 34% (% mole), dimethyl ether selectivity 55% (% mole), and yield dimethyl ether 19% (% mole).