Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Konsentrasi CO2 di dalam atmosfer yang terus meningkat menjadi perhatian bagi peneliti untuk mengkonversi CO2 menjadi senyawa yang lebih ramah lingkungan serta bermanfaat. Dalam penelitian ini, dilakukan studi adsorpsi dan reaksi karboksilasi untuk mengkonversi CO2 menggunakan substrat fenilasetilena, katalis heterogen Cu/MC, dan basa Cs2CO3 pada suhu 75˚C. Hasil sintesis karbon mesopori (MC) dikarakterisasi dengan FTIR dan SEMEDX- Mapping. Hasil FTIR MC memperlihatkan proses karbonisasi yang belum sempurna, ditandai dengan adanya peak C-O dan O-H. Namun hasil SEM-EDX-Mapping memperlihat struktur pori yang cukup seragam dengan komposisi unsur C mencapai 86.01% dan unsur O mencapai 13.99%. Hasil sintesis Cu/MC dikarakterisasi dengan FTIR dan SEM-EDX yang menunjukkan bertambahnya gugus C=C terkonjugasi sehingga komposisi C meningkat menjadi 82,34%, sementara komposisi O sekitar 15,34%, dan komposisi Cu sekitar 02,32%. Hasil karboksilasi fenilasetilena dengan CO2 menunjukan terbentuknya produk asam-3-fenil propiolat namun dalam jumlah yang sangat sedikit. Dalam penelitian ini juga diuji sifat adsorpsi fenilasetilena pada Cu/MC dan adsorpsi fenilasetilena pada MC dengan adanya penambahan basa Cs2CO3. Berdasarkan hasil HPLC uji adsorpsi fenilasetilena, diketahui bahwa adsorpsi fenilasetilena pada Cu/MC lebih baik daripada adsorpsi fenilasetilena pada MC. ......Concentration of CO2 in the atmosphere that continues to increase is a concern for researchers to convert CO2 into compounds that are more environmentally friendly and useful. In this research, study of phenylethethylene adsorption and carboxylation reaction were carried out. The carboxylation reaction to convert CO2 required phenylacetylene as substrate, Cu/MC as heterogeneous catalyst, and Cs2CO3 as base (source of nucleophile). The carboxylation reactions were carried out at 75˚C. The results of mesoporous carbon synthesis (MC) were characterized by FTIR and SEM-EDX-Mapping. The FTIR MC results show that the carbonization process is not perfect, characterized by the peak C-O and O-H. But the SEM-EDX-Mapping results show a fairly uniform pore structure with the composition of element C reaching 86.01% and element O reaching 13.99%. The results of Cu/MC synthesis were characterized by FTIR and SEM-EDX which showed an increase in the conjugated C = C group so that the composition of C increased to 82.34%, while the composition of O was around 15.34%, and the composition of Cu was around 02.32%. The carboxylation of phenylacetylene with CO2 showed the formation of acid-3-phenyl propiolic products but in very small amounts. In this study also tested the properties of phenylacetylene adsorption on Cu/MC and phenylacetylene adsorption on MC with the addition of Cs2CO3 base. Based on the results of HPLC phenylacetylene adsorption test, it is known that the adsorption of phenylacetylene in Cu/MC is better than phenylacetylene adsorption on MC.

Abstrak :
ABSTRAK
Karbon dioksida (CO2) merupakan senyawa yang potensial digunakan sebagai sumber karbon dalam sintesis fine chemicals karena keberadaannya melimpah di alam, bersifat non toksik, ekonomis, dan termasuk ke dalam sumber yang dapat diperbaharui. Namun pemanfaatan CO2 secara luas masih terkendala karena sifatnya yang inert dan stabil. Oleh karena itu, keberadaan katalis sangat diperlukan dalam proses konversi CO2. Penelitian ini bertujuan untuk mensintesis Cu terimpregnasi pada karbon mesopori sebagai katalis karboksilasi fenilasetilena dengan CO2 menjadi asam karboksilat. Pembuatan karbon mesopori dilakukan dengan metode soft template menggunakan Pluronik F-127 sebagai pembentuk pori, formaldehida dan floroglusinol sebagai sumber karbon, dan HCl sebagai katalis asam. Material Cu/MC yang dihasilkan dikarakterisasi dengan FTIR, XRD, SAA, dan SEM-EDX. Analisis BET terhadap karbon mesopori menunjukkan bahwa material tersebut memiliki luas permukaan sebesar 405,8 m2/g dengan rata-rata pori sebesar 7,2 nm. Hasil analisa dengan XRD memperlihatkan puncak pada 2θ 36,62°; 43,47°; 50,63°; dan 74,19° yang mengindikasikan bahwa Cu telah berhasil terimpregnasi yang mewakili spesi Cu(0) dan Cu(I). Reaksi karboksilasi fenilasetilena dengan CO2 dilakukan dengan variasi suhu (25°C; 50°C; dan 75°C), variasi jumlah katalis (28,6; 57,2; dan 85,8 mg) dan variasi basa (Cs2CO3; K2CO3; dan Na2CO3). Hasil reaksi dianalisa dengan HPLC dan memperlihatkan %konversi terbaik terjadi pada suhu 75°C yaitu 41,32% dengan menggunakan Cs2CO3 sebagai basa, dan produk yang terbentuk diidentifikasi dengan FTIR dan LC-MS.

---

ABSTRACT
Carbon dioxide (CO2) is a compound that has the potential to be used as carbon source in the synthesis of fine chemicals because it is abundant in nature, non-toxic, inexpensive, and is included as a renewable source. However, utilization of CO2 is still constrained due to its inert and stable nature. Therefore, the presence of a catalyst is needed in CO2 conversion. This study aims to synthesize impregnated Cu on mesoporous carbon (Cu/MC) as a catalyst for phenylacetylene carboxylation reaction with CO2 into carboxylic acid. The synthesis of mesoporous carbon was performed via soft template method using Pluronic F-127 as a pore forming agen, formaldehyde and phloroglucinol as carbon sources, and HCl as an acid catalyst. The Cu/MC material produced was characterized by FTIR, SAA, XRD, and SEM-EDX. BET surface area analysis of mesoporous carbon showed that the material has a surface area of 405.8 m2/g with an average pore diameter of 7,2 nm. XRD pattern of Cu/MC showed some sharp peaks at 2θ of 36.62°; 43.47°; 50.63°; and 74.19° which indicates that Cu has been successfully impregnated in the form of Cu(0) and Cu(I). Phenylacetylene carboxylation reaction with CO2 was carried out by varying reaction temperatures (25, 50, and 75 °C), the amount of catalyst (28.6, 57.2, and 85.8 mg) and the type of base (Cs2CO3, K2CO3, and Na2CO3). The reaction mixtures were analyzed by HPLC and showed that highest phenylacetylene conversion of 41% was obtained for the reaction at 75°C using Cs2CO3 as a base. The product was further identified using FTIR and LCMS.

Abstrak :
Kenaikan sejumlah besar CO₂ mengakibatkan konsentrasi CO₂ semakin meningkat di atmosfer secara terus-menerus yang menyebabkan terjadinya perubahan iklim. Pengembangan reaksi katalitik terbarukan diperlukan untuk mentransformasi CO₂ menjadi produk yang lebih bermanfaat. Pada penelitian ini, telah dilakukan uji reaksi karboksilasi fenilasetilena dengan CO₂ menggunakan katalis Ni(acac)₂, NiCl₂ dan Ni(DBU)₂ yang terimpregnasi pada penyangga karbon mesopori. Material karbon mesopori, Ni(acac)₂/ MC, NiCl₂/ MC dan Ni(DBU)₂/ MC dikarakterisasi dengan FT-IR, XRD, SAA dan SEM-EDS. Karbon mesopori telah berhasil disintesis menggunakan metode soft template dibuktikan dengan hasil  analisa XRD yang menunjukkan pola difraksi secara khas pada material karbon pada 25,68^o dan 43,26^o dengan indeks Miller (002) dan (100). Proses impregnasi  pada Ni(acac)₂, NiCl₂ dan Ni(DBU)₂  pada penyangga karbon mesopori telah berhasil ditunjukkan dengan analisa FT-IR dimana pada spektrum Ni(acac)₂/ MC, NiCl₂/ MC dan Ni(DBU)₂/ MC menghasilkan spektrum yang sama dengan MC dikarenakan senyawa terimpregnasi telah masuk ke dalam pori sehingga mengakibatkan tidak terdeteksinya gugus fungsi yang ada pada senyawa-senyawa tersebut. Hasil karakterisasi SAA menunjukkan bahwa ketiga katalis heterogen termasuk ke dalam material mesopori. Radius pori yang diperoleh pada ketiga senyawa yaitu  Ni(acac)₂/ MC sebesar 3,288 nm, NiCl₂/ MC sebesar 4,799 nm, dan Ni(DBU)₂/ MC sebesar 4,763 nm. Uji daya adsorpsi dan uji reaksi karboksilasi fenilasetilena dengan CO₂ dengan katalis heterogen Ni(acac)₂/ MC, NiCl₂/ MC dan Ni(DBU)₂/ MC telah dilakukan dan membuktikan bahwa katalis Ni(acac)2/ MC memiliki daya adsorpsi lebih baik dan menghasilkan produk fenil maleat lebih banyak dibanding dengan katalis NiCl₂/ MC dan Ni(DBU)₂/ MC.

---

The continuous increase of CO₂ concentrations in the atmosphere for decades has influenced the global climate change. The development of renewable catalytic reactions is needed to transform CO₂ into more useful products. In this research, phenylacetylene carboxylation reaction with CO₂ was tested using catalysts Ni(acac)₂, NiCl₂ and Ni(DBU)₂ which were impregnated on the mesoporous carbon support. Mesoporous carbon materials, Ni(acac)₂ / MC, NiCl₂ / MC , and Ni(DBU)₂ / MC are characterized by FT-IR, XRD, SAA and SEM-EDS. Mesoporous carbon was successfully synthesized using soft template method which showed typical diffraction patterns of carbon materials which were 25.68^o and 43.26^o with the Miller index of (002) and (100), respectively. The impregnation process in Ni(acac)₂, NiCl₂ and Ni(DBU)₂ in mesoporous carbon support has been successfully proven by FT-IR analysis in which Ni(acac)₂ / MC, NiCl₂ / MC, and Ni(DBU)₂ / MC have similiar IR-spectrum to MC IR-spectrum because the compounds have been substituted into the pore so that no functional groups were detected in the samples. The results of the SAA characterization showed that the three heterogeneous catalysts belong to compounds that have meso-sized pores. The pore radius obtained in the three materials were 3,288 nm for Ni(acac)₂ / MC, 4,799 nm for NiCl₂ / MC, and 4,763 nm for Ni(DBU)₂ / MC. Adsorption test and phenylacetylene carboxylation reaction test with CO₂ with heterogeneous catalyst Ni(acac)₂ / MC, NiCl₂ / MC and Ni(DBU)₂ / MC have been carried out and proved the Ni(acac)₂ / MC catalyst had better adsorption performance and produced more phenyl maleate product compared to NiCl₂ / MC and Ni(DBU)₂ / MC catalysts.