ABSTRAK Baja tahan karat dua fasa SAF 2205 memiliki ketahanan korosi menyeluruh dan korosi terlokalisasi di berbagai lingkungan. Akan tetapi, baja tahan karat dua fasa SAF 2205 rentan terserang korosi sumuran pada lingkungan klorida. Perlakuan panas dilakukan untuk meningkatkan ketangguhan baja tahan karat SAF 2205. Pada penelitian ini dilakukan investigasi pengaruh perlakuan panas baja tahan karat SAF 2205 terhadap korosi sumuran dengan melihat temperatur kritis terjadinya korosi sumuran (critical pitting temperature). Nilai temperatur kritis korosi sumuran diinvestigasi menggunakan polarisasi potentiodynamic dan Electrochemical Impedance Spectroscopy (EIS) di larutan NaCl 1M. Hasil pengujian menunjukkan nilai temperatur kritis korosi sumuran baja tahan karat dua fasa SAF 2205 adalah 650C dan perlakuan panas tidak mempengaruhi nilai tersebut. Selain itu, hasil penelitian juga menunjukkan bahwa fasa yang rentan terserang korosi sumuran adalah fasa austenit.

---

ABSTRACT Duplex stainless steel SAF 2205 has good corrosion reistance of uniform and localized corrosion in various environments. However, duplex stainless steel SAF 2205 is susceptible to pitting corrosion in chloride environment. Heat treatment was done to improve the toughness of duplex stainless steel SAF 2205. This research was investigated influence of heat treatment on pitting corrosion resistance of duplex stainless steel SAF 2205 by looking at the Critical Pitting Temperature (CPT). The value of critical pitting temperature was investigated by using potentiodynamic polarization and Electrochemical Impedance Spectroscopy (EIS) methods in 1 M NaCl solution. The results showed that the critical pitting temperature of duplex stainless steel SAF 2205 is 650C and heat treatment didn?t affect the critical pitting temperature. Moreover, the result showed that the austenite phase is susceptible to pitting corrosion.

Abstrak :
Ekstrak biji keluak dan ubi ungu merupakan ekstrak inhibitor dari tumbuhan yang potensial dapat dijadikan bahan inhibitor alternatif ramah lingkungan untuk diaplikasikan pada pipa baja API 5L. Kemampuan inhibisi korosi dari kedua inhibitor ini diinvestigasi dengan menggunakan pengujian Polarisasi Potensiodinamik dan 'Electrochemical Impedance Spectroscopy<' (EIS). Sedangkan senyawa kimia yang terkandung didalam inhibitor diinvestigasi dengan pengujian FTIR. Dari hasil karakterisasi yang dilakukan terhadap kedua ekstrak inhibitor tersebut dengan pengujian FTIR menunjukkan bahwa senyawa yang terdapat pada kedua inhibitor tersebut adalah senyawa golongan 'flavonoid<' dari group fungsi polar seperti hidroksil dan karbonil. Sedangkan dari hasil pengujian elektrokimia didapatkan efisiensi inhibisi terbaik terjadi pada konsentrasi inhibitor yang secara berturut- turut adalah 4000 ppm pada ekstrak biji keluak dengan efisiensi 61.28%, 3000 ppm pada ekstrak ubi ungu dengan efisiensi 65.31% dan 4000 ppm : 4000 ppm pada kombinasi ekstrak biji keluak & ubi ungu dengan efisiensi sebesar 26.93%. Hasil pengujian EIS menunjukkan bahwa kedua inhibitor ini dapat melindungi logam dengan membentuk sebuah lapisan film yang melapisi permukaan logam. Mekanisme adsorpsi inhibitor menunjukkan sebagai mekanisme adsorpsi secara fisik serta sesuai dengan model dari Langmuir dan Tempkin. ...... Keluak seed extract and purple sweet potato are inhibitor extracts from plants that have the potential to be made as an environmental friendly inhibitors to apply for API 5L steel pipes. Corrosion inhibition ability of these two inhibitors were investigated by using Potentiodynamic Polarization and Electrochemical Impedance Spectroscopy (EIS) tests. While the chemical compounds contained in inhibitor were investigated by FTIR testing. From the results of the characterization performed on the two inhibitor extracts by FTIR testing showed that the compounds contained in the two inhibitors were flavonoid compounds from polar function groups such as hydroxyl and carbonyl. Meanwhile, the results of the electrochemical test showed that the best inhibition efficiency occurred on inhibitor concentration of 4000 ppm in the extract of keluak seed with efficiency of 61.28%, 3000 ppm in the purple sweet potato extract with efficiency of 65.31% and 4000 ppm : 4000 ppm in a combination of keluak seed extract & purple sweet potatoes with efficiency of 26.93%, respectively. The EIS test results showed that these two inhibitors can protect the metal by forming a film layer that inhibited the metal surface. The adsorption mechanism of the inhibitor shows as a physical adsorption mechanism and in accordance with the models from Langmuir and Tempkin.

Abstrak :
Ekstrak daun jati cina Cassia angustifolia sebagai inhibitor ramah lingkungan pada Baja API 5L di lingkungan HCl diinvestigasi. Pengujian yang dilakukan adalah polarisasi dan kehilangan berat. Senyawa yang terkandung pada ekstrak adalah senyawa flavonoid, xanthone, dan anthraquinone. Senyawa tersebut diinvestigasi melalui pengujian FTIR. Variabel pengujian merupakan konsentrasi inhibitor, meliputi 10 ml, 20 ml, 30 ml, 40 ml, dan 50 ml. Kemampuan inhibitor untuk menginhibisi optimum pada konsentrasi 40 ml. Ekstrak daun jati cina berperan sebagai inhibitor campuran dengan dominan katodik. Mekanisme adsorpsi pada ekstrak daun jati cina merupakan mekanisme adsorpsi isotherm Langmuir dengan tipe adsorpsi physisorption. ......Cassia angustifolia leaves extract as green inhibitor for API 5L steel pipe in HCl environment was investigated. This study was experimented by using different types of test, such as polarization and weight loss. The compound in cassia angustifolia are flavonoid, xanthone, and anthraquinone. These compound was investigated by using FTIR. This experiment was investigated with different number of concentrations as its variables, which are 10 ml, 20 ml, 30 ml, 40 ml, and 50 ml inhibitor extracts. The optimum capability of the inhibitor to inhibit the steel surface was in 40 ml concentrations. Cassia angustifolia leaves extract is found to be a mixed type inhibitor with predominant cathodic effectiveness. The adsorption mechanism of cassia angustifolia leaves extract was Langmuir with physisorption as the types of adsorption.

Abstrak :
Telah dilakukan penelitian untuk mengetahui pengaruh air formasi berinhibitor terhadap perilaku korosi dan laju korosi baja API 5L Grade B. Metode yang digunakan yaitu Weight loss dan Polarisasi Potensiodinamik. Uji celup dilakukan dengan variasi waktu 8, 11, dan 14 hari. Hasil penelitian menunjukkan bahwa kondisi baja API 5L dalam larutan air formasi berinhibitor mengalami pemasifan dan laju korosi semakin menurun seiring pertambahan waktu. Hasil pengujian XRD menunjukkan bahwa produk korosi yang dihasilkan adalah Fe3O4. ......A research has been conducted to know the influences formation water with presence of inhibitor to the corrosion behaviour and corrosion rate API 5L Grade B steel. Weight loss and Potentiodynamic Polarization methodology has been carried out. An immersion test with various time 8,11, and 14 days has been done. This research has show that passivity happened and the corrosion rate has decreased as the increased of time. The corrosion product of Fe3O4 has been known as the result of XRD test.

Abstrak :
Paduan titanium-besi (Ti-Fe) diharapkan dapat digunakan di bidang presisi tinggi karena kekuatannya yang tinggi dan ketahanan terhadap korosi dengan tetap mempertimbangkan efisiensi ekonomi. Metalurgi serbuk (PM) dan proses Hot Isostatic pressing (HIP) digunakan untuk memanfaatkan laju difusi besi (Fe) yang sangat tinggi dalam titanium (Ti) untuk menghindari segregasi selama pemadatan dan untuk mencoba membuat paduan Ti-Fe yang homogen. Sifat mekanik dan kinerja korosi paduan Ti-Fe yang terbuat dari HIP yang mengandung proporsi Fe berbeda dievaluasi secara komprehensif. Metode yang digunakan meliputi uji tarik, uji energi impak Charpy, cyclic potentiodynamic polarization (CPP) dan electrochemical impedance spectroscopy (EIS). Hasilnya menunjukkan bahwa dengan meningkatnya kandungan Fe, tegangan tahan 0,2%, kekuatan tarik ultimate (UTS), dan tegangan patah paduan meningkat, namun perpanjangan dan energi serap pada tumbukan menunjukkan tren menurun, menunjukkan bahwa kekuatan mekanik meningkat tetapi paduannya menjadi lebih rapuh. Misalnya, UTS Ti-5%Fe mencapai 732MPa, atau 1,9 kali lipat dibandingkan CP-Ti. Secara umum, paduan Ti xFe menunjukkan ketahanan korosi yang unggul dibandingkan CP-Ti karena penghalusan butiran dan kinetika pertumbuhan lapisan oksidasi. Misalnya, resistensi perpindahan muatan Ti-5%Fe paling tinggi yaitu 2,68E+05 Ω∙〖cm〗^2, atau 2,3 kali lipat CP-Ti, diikuti oleh Ti-2%Fe. Namun peningkatan ketahanan korosi ini tidak sebanding dengan kandungan Fe melainkan terdapat rasio Ti-Fe yang optimal. Kombinasi sifat mekanik dan kinerja korosi membuktikan potensi yang baik dari paduan Ti-Fe. ......Titanium-iron (Ti-Fe) alloys are expected to be used in high-precision fields because of their high strength and corrosion resistance while taking into account economic efficiency. Powder metallurgy (PM) and the hot isostatic pressing (HIP) process was used to utilize the very high diffusion rate of iron (Fe) in titanium (Ti) to avoid the segregation during solidification and to try to make homogeneous Ti-Fe alloys. The mechanical properties and corrosion performance of Ti-Fe alloys made from HIP containing different proportions of Fe were evaluated comprehensively. The used methods included tensile test, Charpy impact energy test, cyclic potentiodynamic polarization (CPP) and electrochemical impedance spectroscopy (EIS). The results indicate that with the increase of Fe content, the 0.2% proof stress, ultimate tensile strength (UTS) and fracture stress of the alloys increase, but the elongation and absorbed energy on impact show decreasing trends, indicating that the mechanical strength increases but the alloys become more brittle. For instance, the UTS of Ti-5%Fe is reached 732MPa, or 1.9 times over CP-Ti. In general, Ti xFe alloys exhibit superior corrosion resistance compared to CP-Ti due to the grain refinement and oxidation film growth kinetics. For example, the charge transfer resistance of Ti-5%Fe is highest which is 2.68E+05 Ω∙〖cm〗^2, or 2.3 times over CP-Ti, followed by Ti-2%Fe. However, this increase in corrosion resistance is not proportional to the Fe content but there is an optimal Ti-Fe ratio. The combination of mechanical properties and corrosion performance evidence the good potential of Ti-Fe alloys.