Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Microstructural identification of synthesized steel with significant local content has been carried out. Alloy ingot was prepared using a casting technique. The samples were then formed into bulk steel by a machining process. A high resolution powder neutron diffractometer (HRPD) was used as an equipment for characterization. By applying neutron diffraction techniques, a ferritic steel profile can be resulted in as well as ‘minor peaks’ belong to impurities formed in the sample. These impurities can be identified as small amounts of Al2O3 54SiO2, Al4C3, SiC and Cr23C6. Scanning transmission electron microscopy (STEM) combined with energy dispersive X-ray spectroscopy (EDX) confirmed and revealed neutron identified phase distributions. Joint Committee on Powder Diffraction Standards (JCPDS) least square curves calibration can precisely calculate the dhkl parameters of each reflection plane. As a comparison, another sample of alloy ingot was also investigated using neutron diffraction. The pattern was free from crystal impurities. Rietveld refinements provide satisfactory goodness of fits Rwp = 10.42% and reliability factor S = 1.7. This was so-called a ‘real bulky’ sample of a 73Fe24Cr2Si0.8Mn0.1Ni ferritic steel alloy.

Abstrak :
Dissimilar metal adalah gabungan dari dua jenis logam berbeda yang dapat diperoleh dengan menggunakan proses pengelasan. Pada penelitian ini, pengelasan dilakukan dengan metode GTAW. Dalam proses pengelasan, panas yang diberikan pada logam menyebabkan distribusi suhu yang tidak seragam yang nantinya akan menyebabkan terjadinya tegangan sisa dan distorsi. Distribusi tegangan sisa hasil pengelasan dari SUS304 dan baja karbon SS400 mengalami perbedaan yang signifikan karena adanya perbedaan koefisien ekspansi termal dan konduktifitas termal antara kedua logam induk. Ada tiga buah pelat dengan ketebalan berbeda yang digunakan, yaitu 8 mm, 10 mm, dan 12 mm. Besarnya nilai tegangan sisa diukur menggunakan instrument difraksi neutron, dan besarnya nilai distorsi angular diukur menggunakan dial gauge. Dari hasil penelitian, didapatkan nilai distorsi angular sebesar 1,07o untuk pelat 8 mm, 2,14o untuk pelat 10 mm, dan 3,21o untuk pelat 12 mm. Nilai tegangan sisa untuk pelat 12 mm yaitu -15,650 MPa pada arah transversal, -2,716 MPa pada arah normal, dan -16,462 MPa pada arah axial, dan besar tegangan sisa untuk pelat 10 mm, dan 8 mm berturut - turut sebagai berikut, -46,146 MPa dan -63,658 MPa untuk arah transversal, -94,302 MPa dan -99,718 MPa untuk arah normal, dan -28,162 MPa dan -99,118 MPa untuk arah axial.

---

Dissimilar metal is a combination of two different types of metals that can be obtained by using welding process. This research uses Gas Tungsten Arc Welding method. Heat input in the process of welding on the metal causes non-uniform temperature distribution that would lead to the occurrence of residual stress and distortion. Distribution of welding residual stress of SUS304 and SS400 carbon steel having a significant difference due to different coefficients of thermal expansion and thermal conductivity between the base metal. There are three plates with different thicknesses are used, namely 8 mm, 10 mm and 12 mm. From the results of the research, obtained the value of the angular distortion of 1.07° to plate 8 mm, 2.14° for plate 10 mm, and 3.21° for 12 mm plate. Residual stress values for plates of 12 mm is -15.650 Mpa in the transverse direction, -2.716Mpa in the normal direction, and -16.462 Mpa in the axial direction, and the value of residual stress for 10 mm, and 8 mm plates respectively as follows, -46.146 Mpa and -63.658 Mpa for the transverse direction, and -94.302 Mpa and -99.718 Mpa for the normal direction, and -28.162 MPa and -99.118Mpa for the axial direction.

Abstrak :
Penyambungan dua jenis material merupakan salah satu tantangan dalam industri manufaktur. Salah satu aplikasinya dilakukan pada penyambungan antara pipa baja tahan karat Dupleks 2205 disambungkan dengan pelat baja HY80 yang banyak dipakai bahan bakar kapal selam. Pengelasan menggunakan SMAW (Shielded Metal Arc Welding) dilakukan karena merupakan pengelasan yang paling efisien dan baik bagi baja paduan. Setelah proses pengelasan dilakukan pengujian radiografi menggunakan sinar X, pengukuran tegangan sisa dengan hamburan neutron untuk mengukur ketahanan sisa di dalam serta menggunakan hamburan sinar X untuk pengukuran tegangan sisa di permukaan, selanjutnya untuk melengkapi data dilakukan juga pengujian kekerasan material dan pengambilan gambar struktur mikro atau metalografi, serta uji tekuk untuk mengetahui kekuatan hasil lasan. Hasil pengujian menunjukkan bahwa masukan panas yang lebih tinggi selain menghasilkan ukuran butir yang lebih besar, ternyata juga menghasilkan karbida yang lebih banyak sehingga kekerasannya lebih tinggi. Tingginya nilai kekerasan akan memberikan efek terhadap nilai tegangan sisa, kekerasan yang tinggi dihasilkan dari tegangan yang bersifat kompresi, sementara tegangan sisa bersifat tarik akan menghasilkan kekerasan yang rendah.

 

---

Joining two types of material is one of the challenges in the manufacturing industry. One application is carried out on the connection between HY80 steel plates connected with Duplex 2205 stainless steel pipes which are widely used as submarine fuel. Welding using SMAW (Shielded Metal Arc Welding) is done because it is the most efficient and good welding for alloy steel. After the welding process, radiographic testing using X-rays is carried out, the residual stress measured at the surface (using X ray diffraction) and in the middle of the metal (using neutron diffraction), hardness checked, metallography, and buckling test are also done to determine the strength of weld results. The test results show that higher heat input in addition to producing larger grain sizes, it also produces more carbides so that the hardness is higher. The high value of hardness will have an effect on the value of residual stress, high hardness is produced from compressive stress, while the tensile residual stress will produce low hardness.