Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Kekerasan nanokomposit nc-TiN/a-Si3N4 yang diperoleh dengan dengan dua metode pengukuran yaitu pengukuran kedalaman indentor dan pengukuran luas bekas indentasi yang diperbesar dengan SEM (Scanning Electron Microscope) memberikan hasil yang sama. Nilai kekerasan yang diperoleh tidak dipengaruhi oleh biaksial dan residual kompresif stress. Pengukuran biaksial stress pada substrat menghasilkan nilai yang sangat kecil dan perlakuan termal menunjukkan kekerasan yang tetap dengan ukuran butir yang tetap. Kekerasan yang diperoleh diyakini sebagai nilai kekerasan yang intrinsik yang tergantung pada sifat mikrostrukturnya.

---

Hardness of nc-TiN/a-Si3N4 nanocomposites which was determined by using two methods of measurements i. e. depth sensing method and remaining plastic indentation area that were magnified by using SEM (Scanning Electron Microscope) lie in the good agreement. The hardness value is not influenced by the biaxial and residual compressive stress. The measurement of the biaxial stress on the substrate shows a very small value of biaxial stress as well as the constant hardness and crystallite size against annealing temperature. Therefore, the reported hardness value here is the intrinsic value that depend on its microstructure properties.

Abstrak :
Telah dilakukan degradasi senyawa 4,4?-dikloro bifenil dengan kombinasi proses fotokatalis dan radiasi gamma menggunakan nanokomposit karbon aktif-zeolit alam dan TiO2 (KAZA-TiO2). Nanotitania pada komposit KAZA-TiO2 disintesis melalui metode sol gel menggunakan titanium tetraisopropoxide sebagai precursor. Karakterisasi nanokomposit dilakukan dengan BET, XRD, FT-IR dan SEM-EDX. Hasil karakterisasi menunjukkan nanokomposit KAZA-TiO2 memiliki ukuran pori 5 - 7 A dengan volum 0,15-0,21 cm3/g dan luas permukaan 79-107 m2/g. Kristal TiO2 yang terbentuk terdiri dari anatase dan rutile, dengan ukuran kristal berturut-turut 15-22 nm dan 37-52 nm, yang terdistribusi secara merata pada adsorben. Degradasi 4,4?-dikloro bifenil dalam air dengan konsentrasi awal 10 ppm sebesar 88% dapat dicapai menggunakan nanokomposit KAZA-TiO2 dengan perbandingan awal 2:1:7 dan waktu reaksi 270 menit. ......Degradation of 4,4?-dichloro biphenyl (4,4?-DCB) had been done by combination process of photocatalyst and gamma radiation using activated carbon, natural zeolite and TiO2 (KAZA-TiO2). The nanotitania on KAZA-TiO2 composite was synthesized by sol gel method using titanium tetraisopropoxide as precursor. Characterisation of nanocomposite was conducted by using BET, XRD, FT-IR dan SEM-EDX. Result showed that KAZA-TiO2 composite had mesopore with size range between 50 - 70 A and volume 0,15-0,21 cm3/g with surface area 79-107 m2/g. TiO2 crystalite on KAZA-TiO2 nanocomposite consist of anatase and rutile type with crystal size range 14-22 nm for anatase and 37-52 nm for rutile, which was distribute uniformly on support. Degradation of 4,4?-DCB in water, with initial concentration of 10 ppm, achived as much as 88% using KAZA-TiO2 with initial ratio 2:1:7 and reaction time 270 minute.

Abstrak :
Tesis ini merupakan bahasan hasil penelitian fabrikasi material nanokomposit dengan perbaikan pada proses fabrikasi. Penelitian ini bertujuan untuk meningkatkan sifat mekanik dan termal dari material nanokomposit nanoclay- polipropilena melalui peningkatan panjang screw dalam mesin twin screw extruder (TSE). Screw pendek yang digunakan memiliki panjang 300 mm, sedangkan screw panjang ukurannya 600 mm. Formulasi dari nanokomposit adalah 3,5 % nanoclay dalam matrik polipropilena dengan aditif kompatibiliser 5 % PP-g-MA. Hasil pengamatan struktur mikro nanokomposit menggunakan scanning electron microscope

Abstrak :
Perovskit LaFeO3 menunjukan sifat konduktivitas gabungan ionik dan elektronik yang dapat diaplikasikan sebagai solid oxide fuel cell. Untuk meningkatan efisiensi katoda solid oxide fuel cell digunakan berbagai macam cara salah satunya adalah merubah ukuran grain. Ukuran grain sangat penting untuk meningkatkan efisiensi dari katoda SOFC. Salah satu cara untuk merekayasa ukuran dari grain adalah menambahkan material komposit pada basis LaFeO3. Pada penelitian ini Fe3O4 ditambahkan pada LaFeO3 merupakan senyawa untuk menghambat pertumbuhan grain dari LaFeO3. Nanokomposit LaFeO3.0,1Fe3O4 dibentuk dari LaFeO3 yang disintesis dengan metode sol-gel. LaFeO3 dicampurkan dengan Fe3O4 dan disintering pada temperatur 1300°C selama 1 jam. Setelah proses sintering nanokomposit LaFeO3.0,1Fe3O4 di annealing dengan variasi temperatur 1000°C, 1100°C, 1200°C selama 12 jam. Struktur dan morfologi sampel dipelajari menggunakan metode karakterisasi XRD and SEM. Pola dari XRD menunjukan bahwa adanya double fasa LaFeO3 dan Fe3O4. Ukuran kristalit dari sampel berada di antara rentang 30-60 nm yang dihitung dari pola XRD menggunakan Schrerrer?s formula. Sifat listrik diukur sebagai fungsi frekuensi dan temperatur menggunakan metode spektroskopi impedansi pada frekuensi (1kHz ? 1MHz) dan temperatur (RT - 373 K). Sifat listrik direpresentasikan dengan plot Nyquist, plot Bode dan konstanta dielektrik (ɛ?) sebagai fungsi frekuensi. Fenomena relaksasi dielektrik pada plot Bode Zim vs f menunjukan pergeseran puncak ke frekuensi yang lebih besar. Dari kurva log f sebagai fungsi temperatur, nilai energi aktivasi terlihat memiliki ketergantungan terhadap ukuran grain. ......Perovskite LaFeO3 show the mixed electronic and ionic conductivity has enabled their use in applications such as solid oxide fuel cell cathodes . For increasing the eficiency of SOFC used some method as change the grain size. Grain size is very important to improve the efficiency of the SOFC cathode. One way to manipulate the size of the grain is to provide a composite material based to the LaFeO3. In this research, Fe3O4 is used as the compound to inhibit grain growth of LaFeO3. LaFeO3.0,1Fe3O4 nanocompsite made of LaFeO3 synthesized by the method solgel and mixed with Fe3O4 then sintered at 1300°C for 1h. LaFeO3.0,1Fe3O4 nano-composite was annealed at temperature of 1000°C, 1100°C, 1200°C for 12 h. Structural studies was carried out using X-ray diffraction (XRD) and SEM. XRD pattern confirmed the double phase LaFeO3 and Fe3O4. The crystallite size of the synthesized material lie in the range 30-60 nm as calculated from X-ray diffraction pattern using Schrerrer?s formula. Electrical properties evaluated as a function of frequency, temperature using an impedance spectroscopy in frequency range (1kHz - 1MHz) and temperature ( RT-373 K) . Electrical properties represented in Nyquist plot, bode plot and dielectrict constant (ɛ?) as a fuction of frequency. The phenomena can be explained on the basis of Maxwell-Wagner type of interfacial polarization and hopping mechanism. The dielectric relaxation in the bode plot Z?? vs f shown the relaxation peak shift to the higher frequency. From vs log f as a function of a temperature, the activation energy was calculated and its value depend on the grain size.

Abstrak :
Data XRD dari nanokomposit Ti-Si-N telah dianalisis menggunakan program GSAS berbasis metode Rietveld untuk mengidentifikasa fasa-fasa pembentuk serta komposisinya dan mencari pengaruhnya terhadap kekerasan material tersebut. Telah ditemukan fasa-fasa baru dalam sampel tersebut, disamping fasa-fasa nanokomposit nc-TiN/a-Si3N4 & a-/nc-TiSi2 yang telah banyak dikenal. Dari fasa-fasa kristal yang diperoleh, setelah dilakukan perhitungan fraksi fasa amorf Si3N4 dan TiSi2 maka diperoleh bahwa kekerasan optimal terjadi pada kandungan a-Si3N4 8 wt.%.

---

Phase composition analysis using rietveld methode and it?s influence to the hardness of Ti-Si-N nanocomposites. XRD data of nanocomposites Ti-Si-N have been analysed using GSAS based on Rietveld Method in order to identify phases and their composition as well as its influence on the hardness of these nanocomposites. Several new phases have been found in the sample beside the nc-TiN/a-Si3N4& a-/nc-TiSi2 that have been known widely. From the obtained crystalline phase, after the calculation of amorf Si3N4 and TiSi2 phase fraction, it is found that the optimum hardness can be reached when the fraction of a-Si3N4 phase around 8 wt.%.

Abstrak :
ABSTRAK
Perkembangan nanoteknologi khususnya nanokomposit berbasis biopolimer dari limbah industri telah banyak diteliti. Biopolimer selulosa yang diisolasi dari limbah serbuk gergaji kayu sengon dianggap sebagai nanomaterial yang berkelanjutan. Rendemen hasil isolasi selulosa diperoleh sebesar 63,40% dengan bentuk permukaan, seperti serat yang halus dan pendek. Nanopartikel TiO2 dan ZrO2 berhasil disintesis dengan ukuran partikel masing-masing 25 nm dan 15 nm, serta oksida biner TiO2-ZrO2 dengan ukuran partikel sekitar 20 nm. Selulosa sebagai bahan pendukung katalis yang digabungkan dengan nanopartikel anorganik dalam bentuk oksida biner TiO2-ZrO2 dapat membentuk material nanokomposit dengan keunggulan sifat yang sinergis dari nanomaterial penyusunnya. Ukuran nanokomposit selulosa/TiO2-ZrO2 yang diperoleh berkisar 50 nm. Uji aktivitas katalitik dilakukan dengan mengkonversi glukosa menjadi 5-EMF. Hasil produk 5-EMF terbaik sebesar 45,47% dengan kondisi rasio TiO2-ZrO2 dalam katalis (1:1), waktu reaksi selama 4 jam, dan suhu reaksi 160°C. Pemanfaatan biopolimer selulosa dari limbah serbuk gergaji kayu sengon menjanjikan sebagai alternatif katalis yang ramah lingkungan dan juga 5-EMF menjadi alternatif bahan baku biofuel yang bermanfaat dalam pengembangan energi alternatif terbarukan.

---

ABSTRACT
The development of nanotechnology, especially biopolymer based nanocomposite from industrial waste has been widely studied. Cellulose biopolymer isolated from sengon sawdust waste is considered a sustainable nanomaterial. The yield of cellulose isolation was 63,40% with surface morphology, such as smooth and short fibers. TiO2 and ZrO2 nanoparticles were successfully synthesized with particle sizes of 25 nm and 15 nm respectively, and binary oxide TiO2-ZrO2 with a particle size about 20 nm. Cellulose as a catalyst support material combined with inorganic nanoparticles in the form of TiO2-ZrO2 binary oxide can form a nanocomposite material with superior synergistic properties of the constituent nanomaterials. The size of the cellulose/TiO2-ZrO2 nanocomposites obtained was around 50 nm. The catalytic activity test was carried out by converting glucose to 5-EMF. The best 5-EMF product yield was 45.47% under the conditions of the TiO2-ZrO2 ratio in the catalyst (1:1), the reaction time was 4 hours, and the reaction temperature was 160°C. Utilization of cellulose biopolymer from sengon sawdust waste is promising as an alternative to environmentally friendly catalysts and 5-EMF as an alternative raw material for biofuels which is useful in developing alternative renewable energy.

Abstrak :
Nanokomposit berbasis biopolimer yang didukung dengan bimetal semikonduktor, menarik untuk dikembangkan sebagai katalis degradasi zat warna. Pada penelitian ini, nanokomposit selulosa/γ-Fe2O3/ZrO2 telah berhasil disintesis yang didukung dengan karakterisasi menggunakan FTIR, XRD, UV-DRS, dan SEM-EDS. Selulosa merupakan biopolimer sebagai support katalis dan dapat membentuk komposit dengan sifat yang baik jika digabungkan dengan γ-Fe2O3/ZrO2. Zirkonium oksida (m-ZrO2) disintesis melalui metode kopresipitasi dan maghemit (γ-Fe2O3) disintesis melalui metode sol gel, dengan γ-Fe2O3 yang bersifat magnetik. Karakterisasi UV-DRS menunjukkan bahwa penambahan γ-Fe2O3 efektif menurunkan enegi band gap ZrO2 dari 4,99 eV menjadi 2,05 eV. Nanokomposit selulosa/γ-Fe2O3/ZrO2 memiliki ukuran partikel rata-rata sebesar 21,46 nm menggunakan karakterisaasi XRD, dan diperoleh energi band gap 2,08 eV yang dapat digunakan sebagai katalis degradasi congo red. Kondisi optimum diperoleh dengan jumlah katalis 40 mg, pH larutan pada pH 3, rasio γ-Fe2O3 dan ZrO2 (1:2), rasio selulosa dan γ-Fe2O3/ZrO2 (2:1), lama reaksi 30 menit dengan menggunakan sinar matahari diperoleh persen degradasi maksimal sebesar 98%. Pada proses fotokatalisis, telah dipelajari studi kinetika dan diperoleh reaksi fotokatalisis yang mengikuti kinetika orde satu dan proses adsorpsi mengikuti model isoterm adsorpsi Langmuir. Nanokomposit yang diperoleh dapat menjadi solusi untuk mengurangi limbah zat warna yang bersifat biodegradable sehingga ramah terhadap lingkungan. ......Nanocomposites of semiconductor bimetal supported by biopolymer are interesting to be developed as catalysts for dye degradation. In this study, cellulose/γ-Fe2O3/ZrO2 nanocomposites were successfully synthesized and supported by characterization using FTIR, XRD, UV-DRS, and SEM-EDS. Cellulose is a biopolymer as a catalyst support and able to form composites with good poperties when combined by γ-Fe2O3/ZrO2 semiconductor. Zirconium oxide (m-ZrO2) was synthesized via coprecipitation method and maghemite (γ-Fe2O3) was synthesized via sol gel method, with γ-Fe2O3 is magnetic. UV-DRS characterization showed that the addition of γ-Fe2O3 effectively reduced the band gap energy ZrO2 from 4.99 eV to 2.05 eV. Cellulose/γ-Fe2O3/ZrO2 nanocomposite with average particle size of 21.46 nm and band gap energy of 2.08 eV was used as a catalyst for congo red degradation. The optimum conditions were obtained by amount of catalyst 40 mg, pH of the solution at pH 3, γ-Fe2O3 and ZrO2 ratio (1: 2), cellulose and γ-Fe2O3/ZrO2 ratio (2: 1), reaction time of 30 minutes using sunlight and obtained percent degradation of 98%. In the photocatalytic process, kinetics studies have been conducted in which the photocatalytic reactions that follows the first order kinetics and the adsorption process follows the Langmuir adsorption isotherm model. Nanocomposites can reduce dye waste and be biodegradable so that it is environmentally friendly.

Abstrak :
Nanokomposit selulosa asetat telah disintesis dengan menggunakan nanofiller organoclayyang dimodifikasi dengan TiO2. Bentonit Tapanuli yang sebelumnyadikenai proses purifikasi dan penyeragaman kation dimodifikasi dengan ditambahkan TiO2 dengan persen berat yakni 0%, 1%, 3%, 5%, 10% dan 7% organoclay terhadap total komposit.. Analisis BET mengindikasikan adanya penambahan luas permukaan bentonit pada penambahan surfaktan dan TiO2 sebesar 16,41 m2/g, 29,49 m2/g, 27,57 m2/g, dan 36,74 m2/g. Analisis FTIR menunjukkan interkalasi surfaktan telah berhasil dilakukan dengan adanya pita serapan baru dari HDTMABr pada 2636 cm- 1 dan 2569 cm-1. Analisis Raman menunjukkan TiO2 telah berhasil diinterkalasi ke dalam organoclay ditunjukkan dengan pita serapan baru khas TiO2 pada panjang gelombang 637cm-1, 516 cm-1, 395 cm-1 dan 147 cm-1. Difraktogram XRD menunjukkan kenaikan basal spasing pada modifikasi bentonit yakni dari 15.7 Å pada bentonit alam menjadi 19,7 Å. Pembuatan nanokomposit dilakukan dengan menggunakan aseton sebagai pelarut dan metode solvent castingsebagai teknik untuk pembuatan film nanokomposit. Aplikasi nanokomposit berupa uji fotodegradasi pada penyinaran sinar matahari langsung, lampu UV, dan tanpa penyinaran selama enam hari. Diketahui, semakin banyak TiO2 semakin besar komposit yang terdegradasi. Persen penurunan berat hasil uji aplikasi pada penyinaran lampu UV sebesar 1,11%, 2,15%, 2,73%, 3,18%, 3,96%, pada penyinaran langsung sebesar 1,03%, 3,03%, 3,88%, 4,53%, 5,57%.Modifikasi nanokomposit dengan penambahan TiO2.

---

Cellulose acetate nanocomposite has been synthesized using organoclay nanofiller modified with TiO2. Bentonite Tapanuli were previously subjected to processes of purification and unification of cations modified with TiO2 that was added as much as 0%, 1%, 3%, 5%, 10% of the total composite. BET analysis indicated surface area of bentonite was increased with the addition of surfactant and TiO2 of 16.41 m2 / g, 29.49 m2 / g, 27.57 m2 / g, and 36.74 m2 / g. FTIR analysis showed intercalation with surfactant was successfully carried out in the presence of HDTMABr, indicated by new absorption band at 2636 cm-1 and 2569 cm-1. Raman analysis showed TiO2 has been successfully intercalated into the organoclay shown with Raman peaks typical of TiO2 at a wavelength of 637cm-1, 516 cm- 1, 395 cm-1 and 147 cm-1. XRD diffractogram shows the increase in basal spasing on the modification of bentonite, film from 15.7 Å to 19.7 Å, before and after modification. Fabrication of nanocomposite was carried out using acetone as solvent and through solvent casting method. Nanocomposite application in photodegradation test was carried out under direct sunlight radiation, UV light, and without irradiation for six days. It's found that, the greater presence amount of TiO2 in the composites, the more weight loss occured, due to photodegradation. Percent weight loss of UV light irradiation are 1.11%, 2.15%, 2.73%, 3.18%, and 3.96%, while under direct irradiation, the weight loss was 1.03%, 3.03%, 3.88%, 4.53%, and 5.57%. Modification of nanocomposite with the addition of photocatalytic TiO2 as photocatalytic agent has shown the ability of self-photodegradation of nanocomposite.

Abstrak :
Nanokomposit Perak, Titanium dioksida, dan Mangan (II,III) oksida (Ag/TiO2/Mn3O4) dengan berbagai rasio molar telah disintesis menggunakan metode hidrotermal. Pengukuran difraksi sinar-X (XRD) mengkonfirmasi struktur nanokomposit Ag/TiO2/Mn3O4 yang terdiri dari struktur kubik Ag, TiO2 anatase, dan Mn3O4 tetragonal. Rasio komposisi unsur nanokomposit Ag/TiO2/Mn3O4 diselidiki dengan fluoresensi sinar-X (XRF). Efek sinergis Ag, TiO2 dan Mn3O4 dapat meningkatkan efisiensi nanokomposit sebagai fotokatalis. Peningkatan efisiensi ditunjukkan dengan melebarnya rentang absorbansi pada hasil pengukuran UV-Vis Diffuse Reflectance. Pengukuran adsorpsi-desorpsi nitrogen menunjukkan bahwa penambahan geraham TiO2 mengakibatkan penurunan luas permukaan spesifik nanokomposit Ag/TiO2/Mn3O4, sedangkan hasil sebaliknya diberikan dengan penambahan geraham Mn3O4. Pada uji fotokatalitik, hasil terbaik ditunjukkan oleh nanokomposit Ag/TiO2/Mn3O4 dengan dominasi Mn3O4 untuk radiasi UV dan cahaya tampak. Pada kondisi optimum, nanokomposit Ag/TiO2/Mn3O4 mampu mendegradasi metilen biru hingga 91% dengan penyinaran selama 2 jam. Uji scavenger mengidentifikasi lubang sebagai spesies yang berkontribusi paling besar pada proses fotokatalitik ini. Uji reusabilitas dan stabilitas pada nanokomposit Ag/TiO2/Mn3O4 menunjukkan hasil positif. ......Silver, Titanium dioxide, and Manganese (II,III) oxide (Ag/TiO2/Mn3O4) nanocomposites with various molar ratios have been synthesized using the hydrothermal method. X-ray diffraction (XRD) measurements confirmed the structure of the Ag/TiO2/Mn3O4 nanocomposite consisting of a cubic structure of Ag, TiO2 anatase, and tetragonal Mn3O4. The elemental composition ratio of Ag/TiO2/Mn3O4 nanocomposite was investigated by X-ray fluorescence (XRF). The synergistic effect of Ag, TiO2 and Mn3O4 can increase the efficiency of nanocomposites as photocatalysts. The increase in efficiency is indicated by the widening of the absorbance range on the measurement results of UV-Vis Diffuse Reflectance. The nitrogen adsorption-desorption measurements showed that the addition of TiO2 molars resulted in a decrease in the specific surface area of ​​the Ag/TiO2/Mn3O4 nanocomposite, while the opposite result was given by the addition of Mn3O4 molars. In the photocatalytic test, the best results were shown by the Ag/TiO2/Mn3O4 nanocomposite with the dominance of Mn3O4 for UV radiation and visible light. Under optimum conditions, Ag/TiO2/Mn3O4 nanocomposite was able to degrade methylene blue up to 91% with irradiation for 2 hours. The scavenger test identified pits as the species that contributed most to this photocatalytic process. Reusability and stability tests on Ag/TiO2/Mn3O4 nanocomposites showed positive results.