Hasil Pencarian  ::  Simpan CSV :: Kembali

"Dalam penelitian ini dilakukan absorpsi gas CO2 dari campuran gas CO2/CH4 melalui kontaktor membran Spiral Wound Berpori Nano dengan menggunakan pelarut Dietanol Amine. Penelitian ini difokuskan pada pengaruh dari variasi laju alir pelarut DEA serta pengaruh dari laju alir gas terhadap efektivitas absorpsi gas CO2 melalui kontaktor membran berpori nano. Pengaruh dari variasi laju alir pelarut DEA dilakukan dengan memvariasikan laju alir DEA dari 100-600 mL/menit sementara pengaruh dari variasi laju alir gas dilakukan dengan memvariasikan laju alir gas dari 0,3-0,8 L/menit. Dari hasil penelitian ini didapatkan bahwa variasi laju alir gas memberikan hasil yang lebih signifikan dibandingkan variasi laju alir pelarut DEA terhadap efektivitas absorpsi gas CO2 melalui kontaktor membran berpori nano. Jumlah mol CO2 terserap optimum didapat sebesar 0,014 mol pada laju alir DEA sebesar 400 ml/menit dan laju alir gas sebesar 0,8 L/menit. Persentase penyerapan CO2 optimum didapat sebesar 81,51% pada laju alir DEA sebesar 400 ml/menit dan laju alir gas sebesar 0,8 L/menit.

---

This research is focused on effects of DEA flow rate and gas flow rate variations towards effectivity of absorption of CO2 gas through nano porous membrane contactor. Effects of DEA flow rate variation is done by varying DEA flow rate from 100-600 mL/minute while effects of gas flow rate variation is done by varying gas flow rate from 0,3-0,8 L/minute.

This research shows that gas flow rate variation gives more significant result than DEA flow rate variation towards effectivity of absorption of CO2 gas through nano porous membrane contactor. The optimum amount of absorbed CO2 is 0,014 mol at DEA flow rate of 400 mL/minute and gas flow rate of 0,8 L/minute. The optimum CO2 absorbed percentage is 81,51% at DEA flow rate of 400 mL/minute and gas flow rate of 0,8 L/minute."

"Saat ini nanoteknologi berkembang dengan sangat pesat karena menghasilkan sifat yang menarik dan berbeda dengan teknologi yang dihasilkan dalam ukuran makroskopis. Produk-produk nanoteknologi berbasis nanostructure materials telah banyak dikaji dan dikembangkan, beberapa diantaranya adalah carbon nanotube, quantum dots, dan nano porous membrane. Sintesis nanostructure materials tersebut dapat dilakukan dengan template nano porous aluminum oxide hasil proses anodisasi. Sifat dan struktur nanoporous aluminum oxide tersebut sangat dipengaruhi oleh beberapa variabel proses anodisasi seperti waktu anodisasi, jenis dan konsentrasi larutan elektrolit, tegangan dan rapat arus, dan juga temperatur.Pembuatan nano porous aluminum oxide dari aluminium foil untuk aplikasi nanostructure materials telah dilakukan dengan metoda anodisasi. Proses anodisasi dilakukan dengan kenaikan temperatur 10 °C, 20 °C, dan 30 °C dalam campuran larutan asam sulfat 3 M dan asam oksalat 0,5 M, pada kondisi tegangan 15 volt, dan waktu anodisasi 30 menit. Pengamatan diameter pori dilakukan dengan alat FESEM sedangkan pengukuran ketebalan dilakukan dengan alat SEM. Hasil pengamatan menunjukkan bahwa pada kondisi temperatur 10 °C dan 20 °C tidak terbentuk lapisan nano porous alumina sedangkan pada temperatur 30 °C terbentuk nano porous dengan keteraturan near-ordered dengan diameter ratarata 25 nm. Pengujian ketebalan oksida menunjukkan bahwa semakin tinggi temperatur menyebabkan kenaikan ketebalan rata-rata oksida. Ketebalan lapisan oksida mengalami kenaikan berturut-turut 351 nm, 652 nm, dan 770 nm pada temperatur 10 °C, 20 °C, dan 30 °C.

---

Recently, nanotechnology grows fast because it develops interesting features and different from technology produced on macroscopic scale. Nanotechnology products like nanostructure materials have been studied and developed. Some of them are carbon nanotube, quantum dots, and nano porous membrane. Fabrication of nanostructure materials can be done by template of nano porous aluminum oxide from anodizing process. Properties and structure of the nano porous aluminum oxide was influenced by several variables from anodizing process like time, type and concentration of solution, voltage and current density, and temperature.

Fabrication of nano porous aluminum oxide from aluminum foil for nanostructure materials application have been done from anodizing process in this research. Anodizing process was done on different temperature 10 °C, 20 °C, and 30 °C in mixing solution of sulfuric acid 3 M and oxalic acid 0.5 M, voltage 15 volt, anodizing time 30 minute. Observation of pores diameter was done by FESEM and measurement of oxide thickness was done by SEM. The result shows that there is no formation of porous alumina on temperature 10 °C and 20 °C. In other hand, there is formation of near-ordered nano porous aluminum oxide on temperature 30 °C with 25 nm average diameters. Measurement of thickness show that oxide thickness increases when temperature is raised. Oxide film thickness increases 351 nm, 652 nm, and 770 nm on temperature 10 °C, 20 °C, and 30 °C, respectively."

"Gas CO2 dalam gas alam yang bersifat asam merugikan karena korosif sehingga dapat menyebabkan kerusakan pada sistem perpipaan dan utilitas di industri serta mengurangi kalor pembakaran proses jika bercampur dengan air. Penelitian ini dilakukan untuk pemurnian dan pengolahan gas alam dengan absorpsi menggunakan kontaktor membran. Kontaktor membran berpori nano bersifat lebih ekonomis dan dapat menutupi kekurangan pada kolom absorpsi konvesional dalam proses absorpsi CO2. Pelarut amina lazim digunakan dalam proses absorpsi CO2 karena ekonomis juga memiliki kecepatan reaksi yang tinggi untuk mengabsorp CO2. Dalam penelitian ini, pelarut campuran amina TEA/DEA digunakan untuk mengabsorpsi CO2 melalui kontaktor membran berpori nano spiral wound berbahan dasar poliamida dengan luas 0,5 m2. Pelarut campuran amina TEA 5% wt + DEA 3% wt menunjukkan hasil terbaik dalam penelitian ini dengan koefisien perpindahan massa 0,0012 cm/s dan dapat menyerap 0,021 mol/L. Secara hidrodinamika, penurunan tekanan cairan pada membran mencapai 0,69 psi pada laju alir 500 mL/menit.

---

Gas CO2 is one of acid gas in natural gas and considered to be harmful since it is corrosive and can cause damage in piping system and utilities in the industry as well as reduce the value of heating calor when mixed with water. In this research, there will be acid gas removal and purification processes by absorption using membranes. Nano porous membrane contactor is economical and can cover the disadvantages of conventional coloumn to absorp CO2. Amine solvent is widely used in CO2 absorption because it is economical and reactive with CO2.

In this research, mixture of amine solvent of TEA/DEA is used to absorp CO2 with nano-porous spiral wound membrane made from poly-amide having area of 0.5 m2. The mixture of amine solvent by TEA 5% wt + DEA 3% wt shows the best result in this research with mass transfer coefficient 0.0012 cm/s and can absorp 0.021 mol/L. Based on hydrodynamic test, the pressure drop of liquid has approached 0.69 psi by the flow rate 500 mL/minutes."