Abstrak :
Clay-epoxy nanocomposites were synthesized from DGEBA resin and montmorillonite clay with an in-situ polymerization. One type of untreated clay and two types of organo clay were used to produce the nanocompsoites. The aims of this study were to examine the nanocomposite structure using different tools and to compare the results between the unmodified clay and modified clays as nanofillers. Although diffractogram in reflection mode did not show any apparent peak of both types of materials, the transmitted XRD (X-Ray Difraction) graphs, DSC (Differential Scanning Calorimeter) analysis and TEM (Transmission Electron Microscope) images revealed that the modified clay-epoxy and unmodified clay-epoxy provides different results. Interestingly, the micrographs showed that some of the modified clay layers possessed non-exfoliated layers in the modified clay-epoxy nanocomposites. Clay aggregates and a hackle pattern were found from E-SEM images for both types of nanocomposite materials. It is shown that different tools should be used to determine the nanocomposite structure.

Abstrak :
ABSTRAK
A natural-based nanocomposite film consisting of chitosan, montmorillonite (MMT) and cashew nut shell liquid (CNSL) was synthesized. The nanocomposite was prepared by mixing a suspension of clay particles (filler, MMT) with a solution containing chitosan as the macroscopic polymer matrix. In this study, it was proposed that non-ionic long-chain alkyl molecules with possible interact ions with the amine group of chitosan could be used as a plasticizer. As a natu-ral source for these compounds, an extract of CNSL was used. A series of chitosan/MMT com-posite samples containing two different clay contents and a sample with an additional CNSL were prepared. FTIR spectroscopy of the nanocomposite films indicated that, by addition of CNSL, amide groups of the chitosan are probably less attached and have more space for vibration. CNSL seems to provide in termolecular spaces between the chitosan molecules. Atomic force microscopy (AFM) analysis showed that the composite contained particles measuring 100 nm or less, which confirmed that the nanocomposite had been successfully produced by this method. Addition of CNSL as plasticizer improved the tensile strength by 10% and the elastic modulus by almost 18%. Cell growth was observed on all the nanocomposite samples studied.

Abstrak :
Montmorillonite berpilar aluminium (MBA) dan modifikasinya oleh surfaktan kationik dihasilkan dengan mereaksikan montmorillonite terhadap larutan aluminium chlorohydrate atau dengan penambahan larutan cetyl trimethyl ammonium bromide (CTABr). Kondisi untuk menghasilkan montmorillonite berpilar aluminium dan modifikasinya oleh CTABr adalah sebagai berikut: perbandingan OH / Al sebesar 2,2; rasio Al / montmorillonite divariasikan pada 5, 10, 20 mmol / gr dan perbandingan CTABr / montmorillonite 2 (w/w). Montmorillonite berpilar aluminum mempunyai basal spacing sekitar 17,5? dan 2 luas permukaannya di atas 200 m / gr. Montmorillonite berpilar aluminum yang dimodifikasi oleh CTABr (MBAc) menunjukkan lebar basal spacing yang lebih rendah menjadi 13,3?. Luas permukaan spesifik dari MBAc menjadi lebih rendah daripada MBA ataupun montmorillonite (M) awal. Ukuran diameter pori rata-rata yang didapat lebih besar dari 20? akibat hilangya spesi organik oleh kalsinasi. Sifat adsorpsi surfaktan kationik pada struktur multilayer montmorillonite ataupun interlamellar space juga dipelajari melalui spektra IR.

Abstrak :
Tesis ini meneliti sintesa organoclay dengan menggunakan berbagai surfaktan,Alkyl Benzyl Dimethyl Ammonium Chloride, Ammonium Lauryl Sulfate, Sodium Dodecyl Sulfate. Clay atau yang lebih dikenal dengan lempung yang berasal dari Garut, Tasikmalaya, Cibadak, Jawa Timur, Kalimantan dan Cina. Sifatnya yang khas seperti mampu mengembang diantara ruang galerinya, mampu mengalami pertukaran kation dan bersifat hydrophilic sangat menarik untuk diteliti. Perubahan dari hydrophilic menjadi hydrophobic akan sangat berguna didalam penelitian bahan - bahan baru pada jenis bahan - bahan masa depan. ......This thesis studies organoclay synthesized using various surfactant, Alkyl Benzyl Dimethyl Ammonium Chloride, Ammonium Lauryl Sulfate, Sodium Dodecyl Sulfate. Clay which is being known as "lempung" from Garut, Tasikmalaya, Cibadak, Jawa Timur, Kalimantan and China. Clay has swelling capability at inter gallery space, cation exchange ability and hydrophilic properties is very interesting to observe. Clay modification from hydrophilic into hydrophobic is very useful for materials research to discover future materials.

Abstrak :
Nanopartikel oksida seng (ZnO) yang diberi dopan kromium (Cr) dan penambahan 10 % montmorillonite (MMT) disintesis dengan metode kopresipitasi untuk empat variasi persen atom Cr. Nanopartikel dikarakterisasi menggunakan X-Ray Diffraction (XRD), Energy Dispersive X-Ray (EDX), Fourier Transform Infrared (FTIR), UV-Visible Diffuse Reflectance (UV-Vis) dan Electronic Spin Resonance (ESR). Pengujian aktivitas fotokatalitik dilakukan menggunakan model polutan methylene blue dengan paparan sinar UV. Penambahan montmorillonite dan dopan Cr pada ZnO dapat meningkatkan degradasi methylene blue dengan Cr doped ZnO/MMT 10 at.% menunjukkan degradasi maksimum dengan kondisi optimum dosis fotokatalis 0.7 g/L dan konsenstrasi larutan 20 mg/L. Spesies dominan pada aktivitas fotokatalitik adalah hole dan OH● berturut-turut. ......Chromium (Cr) doped zinc oxide (ZnO) nanoparticles with 10% montmorillonite (MMT) addition were synthesized by co-precipitation method for four chrome atomic percentage variations. Samples were characterized by X-Ray Diffraction (XRD), Energy Dispersive X-Ray (EDX), Fourier Transform Infrared (FTIR), UV-Visible Diffuse Reflectance (UV-Vis) and Electronic Spin Resonance (ESR). Photocatalytic were evaluated using methylene blue under UV light irradiation. MMT addition and Cr dopant to ZnO nanoparticles enhance methylene blue degradation with the optimum conditions are 0.7 g/L of nanoparticle and 20 mg/L of methylene blue initial concentration. Hole and OH● were identified as dominant species of photocatalytic activity.

Abstrak :
Low linear density polyethylene/organo-montmorillonite (LLDPE/OMMT) nanocomposites at 1–5 wt% OMMT loading were prepared by the melt intercalation technique. The OMMT was synthesized via an ion exchange reaction by replacing the interlayer of sodium ions (Na+ ) in the repeating unit of silicate layers of montmorillonite (MMT) with the cationic surfactant in the form of trihexyltetradecylphosphonium (THTDP) ions. The obtained OMMT and its nanocomposites were characterized by X-ray diffraction, Fourier transform infrared spectroscopy, and elemental and thermogravimetric analyses. The interlayer spacing of MMT expanded from 1.41 to 2.29 nm due to the accommodation of THTDP ions in the intergallery of OMMT. The introduction of THTDP in the interlayer of OMMT rendered better dispersion of OMMT layers in the LLDPE/OMMT nanocomposites and significantly improved the thermal degradation properties of nanocomposites as compared to the pristine LLDPE.

Abstrak :
ABSTRAK
Lumpur Bledug Kuwu mengandung 0,0029 Li dalam bentuk fasa Li-Montmorillonit sehingga berpotensi sebagai deposit litium di Indonesia. Li-Montmorillonit dilindih menggunakan media akuades pada variasi rasio padatan/cairan 1/2, 1/5, 1/10 , temperatur 25oC, 30 oC, 35 oC, dan 45 oC , selama 2,3,4,dan 5 jam. Kondisi optimal adalah kondisi dengan kadar Li tertinggi dan rasio impuritas paling rendah, yaitu pada temperatur ruang selama 3 jam , rasio S/L = . Brine mengandung 15,11 ppm Li dengan rasio kadar Na/Li = 80,74 ; K/Li = 11,91 ; Ca/Li = 4,77 ; Mg/Li = 1,97. Semakin kecil rasio S/L maka perolehan kadar litium semakin kecil hingga 3,09 ppm dengan persen perolehan 92,71 . Semakin tinggi temperatur hingga 45oC maka perolehan litium semakin kecil hingga 9,29 ppm dengan persen perolehan 46,75 . Perolehan kadar litium meningkat seiring waktu pelindian namun mencapai maksimum setelah 3 jam dan kemudian menurun hingga 12,47 ppm dengan persen perolehan sebesar 69,67 . Hasil Uji XRD dan SEM mengonfirmasi bahwa Li-Montmorillonit telah berhasil dilarutkan dengan akuades pada semua kondisi pelindian. Selanjutnya, brine digunakan sebagai bahan baku pada tahap penguarangan kadar Mg dengan reagen batu kapur CaO . Penghilangan ion Mg dan Ca pada konsentrat menggunakan prinsip presipitasi kimia berdasarkan nilai kelarutan senyawa. Tahapan ini menghilangkan Mg hingga kadar akhir 0,02 ndash; 0,1 ppm. Semakin banyak jumlah CaO yang ditambahkan, semakin kecil kadar Mg dan B, namun kadar Li, Ca, dan K cenderung meningkat. Endapan dikonfirmasi oleh SEM-EDX dan XRD sebagai MgO. Kondisi optimal pada penambahan CaO sebesar 0,1875 gram ke dalam 100 ml brine. Reagen asam oksalat digunakan untuk membentuk presipitat Ca-Oksalat dengan adanya ion C2O42-. Namun, adanya ion HC2O4- dan H dapat meningkatkan kelarutan Ca-oksalat dalam larutan, sehingga kadar Ca semakin meningkat seiring penambahan asam oksalat. Reagen oksalat tidak stabil terhadap Li. Semakin banyak massa oksalat, litium mulai mengendap sebagai litium hidrogen oksalat hingga kadar Li berkurang menjadi 3,7119 ppm. Konsentrat 2 selanjutnya sebagai inluen pada proses pertukaran kation. Resin Lewatit S-108 dengan gugus aktif sulfonat hanya mampu mengadsorpsi fisika ion Li dan K, serta adsorpsi elektrostatik ion exchange ion Ca dalam kandungan inluen yang divariasikan pH 4, 6, dan 12 dan laju alir 50ml/0,5jam ; 50ml/1jam ;dan 50ml/2jam . Jumlah adsorpsi ion Li sebesar 0,0030 ndash; 0,0032 mmol/g, adsorpsi ion K sebesar 0,0027 ndash; 0,0028 mmol/g, adsorpsi ion Ca2 sebesar 0,0001 ndash; 0,0002 mmol/g, dan adsorpsi Na bernilai negatif. Semakin cepat laju alir, semakin tinggi juga efisiensi perolehan Li, Ca, dan K. Semakin tinggi pH mendekati basa , jumlah dan kapasitas maksimum adsorpsi Li, Ca, dan K.

---

ABSTRACT
The Bledug Kuwu rsquo s Mud contained 0,0029 Li in Li Montmorillonite phase form so that it could potentially be a lithium deposit in Indonesia. Li Montmorillonite was leached using water with variation of solid liquid ratio 1 2, 1 5, 1 10 , temperature 25oC, 30 oC, 35 oC, dan 45 oC , for 2, 3, 4, and 5 hour. The optimum leaching process was the condition that yield the highest Li content with the lowest impurity ratio. Water leaching at ambient temperature for 3 hours with the S L ratio of is the best condition. Brine contained 15,1086 ppm Li with content ratio of Na Li 80,74 K Li 11,91 Ca Li 4,77 Mg Li 1,97. The smaller the ratio of S L, the acquisition rate of lithium was the smaller until 3,0902 ppm with 92,71 of recovery. The increasing of temperature up to 45oC, the yield of litium was decreased until 9,29 ppm with 46,75 of recovery. The XRD and SEM results confirmed that Li Montmorillonite has been succesfully dissolved with aquadest under all condition of leaching process. Furthermore, Brine was used as a Raw Material at the removal stage of Mg content with a reagent of limestone solid CaO . The removal of Mg and Ca for concentrate used the principle of chemical precipitation based on the solubility of the compound. This reagent could remove Mg with an initial content of 29,76 ppm to concentrate with a final content of 0,02 ndash 0,1 ppm. The more CaO levels were added, the more Mg and B levels would decrease. While, the levels of Li, Ca, and K tend to increase. The phase of precipitate was confirmed by SEM EDX test as a cubic shaped MgO. The optimum condition concentrate 1 was obtained by adding CaO of 0,1875 gram into 100 ml Brine, so that final composition of lithium was 14,73 ppm. Oxalic acid reagents were used to form precipitates of Ca oxalate in the presence of C2O42 ions during ionization. However, the presence of HC2O4 and H ions could increase the solubility of Ca oxalate in solution, so that Ca content increased with the addition of oxalic acid. The oxalate reagent was unstable against the Li content, the more oxalate mass 4,7 grams added , the lithium began to settle as lithium hydrogen oxalate until the concentration of Li at Concentrate 2 decreases to 3,71 ppm. Concentrate 2 as an inluent in cation exchange process. Lewatit S 108 resin with sulfonate active group was only capable of adsorbing the physics of Li and K ions, as well as electrostatic adsorption ion exchange Ca ions in inluent content that varied on pH 4, 6, and 12 and flow rate 50ml 0,5hour 50ml 1hour and 50ml 2hour . The amount of Li ion adsorption is 0,003 0,0032 mmol g, adsorption of K ion 0,00274 ndash 0,00284 mmol g, Ca2 ion adsorption 0,0001 ndash 0,00022 mmol g, and Na adsorption is negative. The faster the flow rate, the higher the percentage recovery of Li, Ca, and K. While, the higher the pH near base , the maximum amount and the adsorption capacity of Li, Ca, and K.

Abstrak :
Film bionanokomposit kitosan/Na-MMT/glutaraldehid (GLA) telah berhasil disintesis dengan metode solvent casting. Selain itu, uji aktivitas antimikroba dengan bakteri S. aureus dan Salmonella juga telah dilakukan. Terdapat tiga tahapan dalam melakukan sintesis. Tahapan pertama adalah Sintesis serbuk Bionanokompoit dengan metode presipitasi lalu tahapan selanjutnya serbuk bionanokomposit digunakan untuk pembuatan Film berbasis kitosan sehingga terbentuk Film Bionanokomposit Na-MMT/Kitosan/GLA. Selain itu juga dilakukan variasi penambahan material pada permbuatan serbuk bionanokomposit yaitu penambahan kitosan (0,5; 1; 2; 3 ;4 gram), variasi penambahan Na-MMT (0,5; 1; 2; 3 ;4 gram) terhadap 10 mL GLA dan variasi Na-MMT berbanding kitosan terhadap GLA masing-masing yaitu; (0,5:2,5); (1:2); (1,5:1,5); (2:1); (2,5:0,5) gram. Karakterisasi yang dilakukan berupa FTIR, XRD, TEM, uji kelarutan dalam air dan uji aktivitas antibakteri. Karakterisasi FTIR memberikan indikasi interaksi GLA dengan kitosan ditunjukkan adanya puncak pada bilangan gelombang 1613 cm-1 dan interaksi Kitosan dengan Na-MMT oleh munculnya regangan (C=N) pada bilang gelombang 1613 cm-1. Selain itu, karakterisasi XRD pada serbuk bionanokomposit menunjukkan pergeseran nilai basal spacing pada Na-MMT. Hal ini mengindikasikan bahwa GLA telah berhasil melakukan interkalasi terhadap Na-MMT dan menjadikan sifat hidrofilik dari Na-MMT menjadi organofilik. Sebagai pendukung data pada karakterisasi XRD, karakterisasi TEM memperlihatkan layer Na-MMT yang telah terinterkalasi. Uji kelarutan dalam air yang telah dilakukan memperlihatkan penyusutan bionanokomposit terkecil sebesar 9,19 % dari berat semula yaitu kitosan film dengan persen kelarutan dalam air yaitu sebesar 23,44%. Selain itu, uji aktivitas antibakteri memberikan nilai zona hambat paling besar yaitu 15,5 mm pada bakteri Salmonellla sp dan 8,5 mm pada bakteri S aureus setelah inkubasi 48 jam. ......In this study, the solvent casting method was used to successfully produce a chitosan/Na-MMT/glutaraldehyde (GLA) bionanocomposite film. Antimicrobial activity studies also performed. The microorganisms Staphylococcus aureus and Salmonella were also tested. In the synthesis, there are three steps. The initial stage is to make bionanocomposite powder using the precipitation method, followed by bionanocomposite preparation. Then the next step is the bionanocomposite powder used to manufacture chitosan-based films to form a Na-MMT/chitosan/GLA bionanocomposite film. In addition, variations in the addition of materials to the manufacture of bionanocomposite powders were carried out, namely the addition of chitosan (0.5; 1; 2; 3 ;4 grams), variations in the addition of Na-MMT (0.5; 1; 2; 3 ;4 grams) to 10 mL of GLA and variation of Na-MMT versus chitosan to GLA, respectively; (0,5:2,5); (1:2); (1,5:1,5); (2:1); (2.5:0.5) grams. Characterization carried out in the form of FTIR, XRD, TEM, water solubility test and antibacterial activity test. The FTIR characterization gave an indication of the interaction of GLA with chitosan indicated by the peak at wave number 1613 cm-1 and the interaction of Chitosan with Na-MMT by the appearance of streching (C=N) at wave number 1613 cm-1. In addition, the XRD characterization of the bionanocomposite powder showed a shift in the basal spacing value of Na-MMT. This indicates that GLA has successfully intercalated Na-MMT and made the hydrophilic nature of Na-MMT organophilic. To support the data on XRD characterization, TEM characterization shows the intercalated Na-MMT layer. The water solubility test that has been carried out shows the smallest shrinkage of the bionanocomposite of 9.19% from its initial weight, namely chitosan film with a percent solubility in water of 23.44%. In addition, the antibacterial activity test gave the greatest inhibition zone value, namely 15.5 mm for Salmonella sp and 8.5 mm for S aureus after 48 hours of incubation.

Abstrak :
Penggunaan elektrolit cair dalam baterai masih menyisakan masalah keamanan akibat kebocoran dan kebakaran. Karena itu, penelitian dan penemuan elektrolit padat dengan performa yang bagus menjadi hal yang sangat menarik dan penting dilakukan, untuk menggantikan elektrolit cair dalam baterai. Lithium Fosfat (Li₃PO₄) adalah elektrolit padat berbasis xLi₂O-yP₂O₅ (x=3, y=1) yang stabil, namun memiliki konduktivitas ionik yang kecil sekitar 10^-9~10^-8 S/cm, terlalu rendah untuk diaplikasikan menjadi elektrolit dalam baterai. Penelitian ini bertujuan untuk mengembangkan bahan elektrolit padat baru berbasiskan Li₂O-P₂O₅, dengan modifikasi komposisi paduannya, dan dikombinasikan dengan Montmorillonite (MMT) membentuk material komposit elektrolit padat.  Komposit elektrolit dipreparasi melalui teknik pencampuran metalurgi biasa dan disintesis memanfaatkan teknik reaksi padatan melt-quenching. Morfologi komposit hasil sintesis dikarakterisasi menggunakan Scanning Electron Microscopy (SEM), dipadukan dengan Energy Dispersive X-ray Spectroscopy (EDS) untuk analisis unsur, sedangkan X-ray Diffractometer (XRD) digunakan untuk analisis struktural. Pengujian performa elektrokimia yang meliputi konduktivitas, impedansi dan sifat dielektrik komposit dilakukan menggunakan Electrochemical Impedance Spectrometry (EIS). Pencampuran paduan Li₃PO₄ dengan MMT menggunakan pengikat PVDF, memberikan komposit yang menunjukkan konduktivitas sebesar 3.59x10^-7 S/cm. Modifikasi komposisi x dari 3 menjadi 1.5, memberikan peningkatan konduktivitas menjadi 3.98x10^-6 S/cm, 2-3 orde lebih tinggi dari konduktivitas Li₃PO₄. Penambahan konten MMT ke dalam paduan hasil modifikasi komposisi 1.5Li₂O-P₂O₅, menciptakan komposit elektrolit padat baru yang menunjukkan konduktivitas lebih baik pada orde 10^-4 S/cm. Peningkatan konduktivitas tersebut diyakini merupakan kontribusi fasa dominan Li₄P₂O₇. MMT berkontribusi meningkatkan sifat dielektrik komposit, dan mengakibatkan muatan dalam elektrolit menjadi lebih mudah bergerak, yang ditunjukkan dengan nilai energi aktivasi komposit dengan kandungan MMT sebesar 0,86 eV, lebih rendah dibandingkan dengan komposit tanpa MMT sebesar 1.50 eV. Komposit Li₂O-P₂O₅-MMT terbukti bisa berfungsi dengan baik sebagai elektrolit padat dalam sel baterai, dan menghantarkan muatan pada proses charge-discharge

---

The use of liquid electrolytes in the battery still leaves safety problems due to leaks and fires. Therefore, research and discovery of solid electrolytes with good performance are very interesting and important to do, to replace liquid electrolytes in batteries. Lithium Phosphate (Li₃PO₄) is a solid electrolyte based on xLi₂O-yP₂O₅ (x = 3, y = 1) which is stable, but has a small ionic conductivity of about 10^-9 ~ 10^-8 S / cm, that still too low to be applied as solid electrolytes in a battery. This study aims to develop new solid electrolyte materials based on Li₂O-P₂O₅, with modified compositions, and combined with Montmorillonite (MMT) to form a solid electrolyte composite material. Electrolyte composites are prepared through ordinary metallurgical mixing and synthesized using melt-quenching solid reaction techniques. The morphology of the synthesized composite was characterized using Scanning Electron Microscopy (SEM), combined with the Energy Dispersive X-ray Spectroscopy (EDS) for elemental analysis, while the X-ray Diffractometer (XRD) was used for structural analysis. Electrochemical performance testing which includes conductivity, impedance, and composite dielectric properties were carried out using Electrochemical Impedance Spectrometry (EIS). Mixing Li₃PO₄ with MMT using PVDF binder, has provided a composite that shows conductivity value of 3.59x10^-7 S/cm. Modification of the composition of x value, from 3 to 1.5, gave an increase in conductivity to 3.98x10^-6 S / cm, higher by 2-3 order of magnitude than that of Li₃PO₄. Addition of MMT content to a composition modified system 1.5Li₂O-P₂O_5, has created a new solid electrolyte composite that shows better conductivity in the order of 10^-4 S / cm. The increase in conductivity is believed to be the contribution of the dominant phase of Li₄P₂O₇. MMT contributes to increasing composite dielectric properties and results in charge carriers becoming more easily polarized, which is indicated by the activation energy value of the composite with MMT content of 0.86 eV, lower than the composite without MMT of 1.50 eV. Li₂O-P₂O₅-MMT composites have proven to function as solid electrolytes in battery cells and conduct charge carriers in the charge-discharge process.:major-bidi'>dikarakterisasi menggunakan Scanning Electron Microscopy (SEM), dipadukan dengan Energy Dispersive X-ray Spectroscopy (EDS) untuk analisis unsur, sedangkan X-ray Diffractometer (XRD) digunakan untuk analisis struktural. Pengujian performa elektrokimia yang meliputi konduktivitas, impedansi dan sifat dielektrik komposit dilakukan menggunakan Electrochemical Impedance Spectrometry (EIS). Pencampuran paduan Li₃PO₄ dengan MMT menggunakan pengikat PVDF, memberikan komposit yang menunjukkan konduktivitas sebesar 3.59x10^-7 S/cm. Modifikasi komposisi x dari 3 menjadi 1.5, memberikan peningkatan konduktivitas menjadi 3.98x10^-6 S/cm, 2-3 orde lebih tinggi dari konduktivitas Li₃PO₄. Penambahan konten MMT ke dalam paduan hasil modifikasi komposisi 1.5Li₂O-P₂O₅, menciptakan komposit elektrolit padat baru yang menunjukkan konduktivitas lebih baik pada orde 10^-4 S/cm. Peningkatan konduktivitas tersebut diyakini merupakan kontribusi fasa dominan Li₄P₂O₇. MMT berkontribusi meningkatkan sifat dielektrik komposit, dan mengakibatkan muatan dalam elektrolit menjadi lebih mudah bergerak, yang ditunjukkan dengan nilai energi aktivasi komposit dengan kandungan MMT sebesar 0,86 eV, lebih rendah dibandingkan dengan komposit tanpa MMT sebesar 1.50 eV. Komposit Li₂O-P₂O₅-MMT terbukti bisa berfungsi dengan baik sebagai elektrolit padat dalam sel baterai, dan menghantarkan muatan pada proses charge-discharge.