Hasil Pencarian  ::  Simpan CSV :: Kembali

"Mengikuti studi literatur, ekstraksi mangan dan litium dari larutan asam dapat dicapai dengan menggunakan natrium karbonat, menghasilkan presipitat karbonat mangan dan litium. Setelah reaksi, padatan disaring menggunakan filter pelat dari larutan asam. Subsistem filter reaktor kedua kemudian dipasang sebagai sejumlah besar litium yang tidak bereaksi dan litium karbonat terlarut yang tersisa. Dengan cara ini, produk padat mangan dan litium karbonat diperoleh pada 99,5% berat. Aliran daur ulang awalnya direncanakan. Namun, setelah pertimbangan dan penyelidikan lebih dalam dalam neraca massa dan spesifikasi peralatan, hal itu dipertimbangkan. Dengan demikian, aliran daur ulang dapat dianggap dilewati. Area pabrik ini mahal, memiliki total biaya tetap berdasarkan lokasi US$164.864.820 di Jakarta, Indonesia. Artinya, rencana proses ini masih memerlukan optimasi dan pertimbangan ulang. Pabrik ini juga mengeluarkan emisi karbon sebesar 80.910,20 kg CO2 per tahun. Dengan optimasi peralatan lebih lanjut, hal ini dapat dikurangi. Analisis bahaya awal menunjukkan bahwa bahaya yang ditimbulkan dalam proses ini agak minimal dan terkait dengan aliran dan bahan peralatan. Tumpahan, korosi, dan erosi adalah bahaya utama yang dapat dicegah dan dikurangi dengan perawatan dan pemeriksaan rutin.

---

Following a literature study, the extraction of manganese and lithium from an acidic solution can be achieved using sodium carbonate, producing carbonate precipitates of manganese and lithium. Following reaction, solids are filtered out using a plate filter from the acidic solution. A second reactor-filter subsystem is then set in place as a sizeable amount of unreacted lithium and dissolved lithium carbonate remain. In this way, a solid product of manganese and lithium carbonates are obtained at 99.5% by weight. A recycle stream was initially planned. However, after deeper consideration and investigation in mass balances and equipment specifications, it was considered. Thus, the recycle stream can be considered by-passed. This plant area is costly, having a locationfactored total fixed cost US$164,864,820 in Jakarta, Indonesia. This means that this process plan still requires optimisation and reconsiderations. This plant also gives off a carbon emission of 80,910.20 kg CO2 annually. With further equipment optimisation, this can be reduced. Preliminary hazard analysis shows that the hazards posed in this process are rather minimal and are related with flowrates and equipment materials. Spillage, corrosion, and erosion are the major hazards which can be prevented and mitigated by routine maintenance and check-up."

"Dengan pertumbuhan pesat baterai Lithium-ion (LIB) di seluruh dunia dan di Australia untuk berbagai tujuan, LIB menghadirkan beberapa tantangan baru seperti sumber daya mineral kritis (misalnya, litium, kobalt, nikel, mangan) dan pengelolaan limbah baterai di akhir masa pakainya. Tujuan dari laporan ini adalah untuk merancang dan mengembangkan proses yang mampu memulihkan litium dari baterai LIB yang sudah habis masa pakainya. Pabrik pemrosesan yang diusulkan akan berlokasi di Townsville, Queensland. Umpan yang dimasukkan ke pabrik pemrosesan ini adalah 3000 ton/tahun material katoda. Tujuan dari pabrik pemrosesan ini adalah untuk mendaur ulang litium dalam bentuk lithium phosphate (Li3PO4) dan pabrik ini ditargetkan untuk memproduksi 76,06 kg/jam Li3PO4. Produk ini ditargetkan memiliki kandungan litium sebesar 99,9%. Bagian presipitasi yang mengikuti proses pencucian melalui hidrometalurgi memiliki tujuan utama untuk memulihkan litium dalam bentuk Li3PO4. 81,22 kg/jam Li2SO4 dari bagian pemurnian dan 54,09 kg/jam Na3PO4.12H2O dari tangki penyimpanan masuk ke dalam proses presipitasi. Produk dari bagian presipitasi terdiri dari 78,5 kg/jam Li3PO4 yang kemudian masuk ke bagian pencucian dan 52,3 kg/jam Na2SO4 yang keluar dari proses. Unit utama dalam proses ini adalah unit presipitasi, yang digunakan untuk memulihkan litium dengan cara mengendapkan Li2SO4 dengan Na3PO4.12H2O. Unit lain dalam proses ini terdiri dari pompa umpan/produk untuk mengangkut cairan ke/dari unit presipitasi dan tangki penyimpanan untuk menyimpan umpan/produk. Perkiraan biaya untuk bagian pabrik ini adalah 331.917,70 AUD dengan penggunaan listrik tahunan sebesar 16.704 kW/tahun.

---

With the rapid growing of Lithium-ion battery (LIB) across the world and in Australia for multiple purposes, LIB presents several emerging challenges such as sourcing the critical minerals (e.g., lithium, cobalt, nickel, manganese) and managing the end-of-life battery waste management. The purpose of this report is to design and develop a process that is able to recover lithium from end-of-life LIB. The proposed processing plant would be located at Townsville, Queensland. The feed that is introduced to the process plant would be 3000 t/y of cathode material. The objective of the process plant is to recycle lithium in the form of lithium phosphate (Li3PO4) and the plant is aim to produce 76.06 kg/hr of Li3PO4. The product is aim to have 99.9% of lithium. The precipitation section comes following washing through hydrometallurgy main process objective is to recover lithium in the form of Li3PO4. 81.22 kg/hr of Li2SO4 from the purification section and 54.09 kg/hr of Na3PO4.12H2O from the storage tank enters the precipitation process. The product of the precipitation section consists of 78.5 kg/hr of Li3PO4 which then enters the washing section and 52.3 kg/hr of Na2SO4 which exits the process. Main unit in the process is the precipitation unit, which is used to recover lithium by precipitating Li2SO4 with Na3PO4.12H2O. Other units in the process consists of feed/product pump to transport liquid to/from the precipitation unit and storage tank to store the feed/product. The estimated cost of this plant section is 331,917.70 AUD with annual electricity usage of 16,704 kW/year."

"With the rapid growing of Lithium-ion battery (LIB) across the world and in Australia for multiple purposes, LIB presents several emerging challenges such as sourcing the critical minerals (e.g., lithium, cobalt, nickel, manganese) and managing the end-of-life battery waste management. The purpose of this report is to design and develop a process that is able to recover lithium from end-of-life LIB. The proposed processing plant would be located at Townsville, Queensland. The feed that is introduced to the process plant would be 3000 t/y of cathode material. The objective of the process plant is to recycle lithium in the form of lithium phosphate (Li3PO4) and the plant is aim to produce 76.06 kg/hr of Li3PO4. The product is aim to have 99.9% of lithium. The main objective of purification process is to remove the remaining impurities from the previous units and increasing the concentration of the product before going into the next processing unit. After the crushed powder went through selective leaching, the leaching brine may still contain a small amount of impurities (e.g. iron, aluminum, etc.). The leaching brine then goes into a purification unit where the leaching brine is precipitated from all impurities. However, since NaOH is required to precipitate the impurities, other Sodium compounds (NaAl(OH)4, Na2SO4, Na3PO4, Na2O2) might be created and dissolved in the solution (containing water), making them hard to separate. Li2SO4 and other Sodium compounds then goes into an evaporation chamber to remove water before going into precipitation unit where the Sodium compounds will be removed.

---

Dengan pertumbuhan pesat baterai Lithium-ion (LIB) di seluruh dunia dan di Australia untuk berbagai keperluan, LIB menghadirkan beberapa tantangan baru seperti penyediaan mineral kritis (misalnya, litium, kobalt, nikel, mangan) dan pengelolaan limbah baterai di akhir masa pakainya. Tujuan dari laporan ini adalah merancang dan mengembangkan proses yang mampu memulihkan litium dari LIB di akhir masa pakainya. Pabrik pengolahan yang diusulkan akan berlokasi di Townsville, Queensland. Bahan baku yang dimasukkan ke dalam pabrik pengolahan adalah 3000 t/y bahan katoda. Tujuan dari pabrik pengolahan ini adalah mendaur ulang litium dalam bentuk litium fosfat (Li3PO4), dan pabrik ini ditargetkan menghasilkan 76,06 kg/jam Li3PO4. Produk ini ditargetkan memiliki kemurnian litium sebesar 99,9%. Tujuan utama dari proses pemurnian adalah menghilangkan kotoran yang tersisa dari unit sebelumnya dan meningkatkan konsentrasi produk sebelum masuk ke unit pengolahan berikutnya. Setelah bubuk yang dihancurkan melewati proses pelindian selektif, larutan pelindian mungkin masih mengandung sejumlah kecil kotoran (misalnya, besi, aluminium, dll.). Larutan pelindian kemudian masuk ke unit pemurnian di mana larutan pelindian diendapkan untuk menghilangkan semua kotoran. Namun, karena NaOH diperlukan untuk mengendapkan kotoran, senyawa Natrium lainnya (NaAl(OH)4, Na2SO4, Na3PO4, Na2O2) mungkin terbentuk dan larut dalam larutan (mengandung air), sehingga sulit dipisahkan. Li2SO4 dan senyawa Natrium lainnya kemudian masuk ke ruang penguapan untuk menghilangkan air sebelum masuk ke unit pengendapan di mana senyawa Natrium akan dihilangkan.

"