"Corrosion is a degradation process of metal quality due to chemical reaction between metal and their environment. One of the methods widely used to control corrosion is using corrosion inhibitor. Imidazoline is used as an organic corrosion inhibitor because it has good adsorption characteristic, can make a protector film on carbon steel surface, and has hydrophobic sites. In this research, imidazoline derivatives from triethylenetetramine (TETA) were successfully synthesized with various fatty acid i.e. stearic (SA), oleic (OA), and linoleic acid (LNA), yielded TETA-SA, TETA-OA, TETA-LNA, respectively, using MAOS (Microwave Assisted Organic Synthesis) method with variation of reaction times. The optimum yield of TETA-SA was obtained at 9 minutes reaction time (89.12%), TETA-OA at 13 minutes (98.79%), and the optimum mass for TETA-LNA was obtained at 9 minutes (1.7023 g).The as-synthesis of TETA-SA from MAOS method had been compared with reflux and Dean Stark methods with xylene as solvent and it was obtained that the highest percentage yield came at 13 hours reaction time for both reflux (96.83%) and Dean-Stark (97.27%) methods. The as-synthesis imidazolines then were identified using thin layer chromatography (TLC), melting point test, and further characterized using UV-Vis, FTIR, ¹H-NMR, and LC-MS/MS instruments. Corrosion inhibition activity was measured by varying the concentration of all as-synthesis compounds (100, 200, 300, 400, and 500 ppm) in various concentration of NaCl (1%, 3%, and 5%) by cyclic voltammetry method using potentiostat then processed using Tafel polarization method to obtain percentage of inhibition efficiency (%IE).The results from corrosion inhibition activities, showed the highest %IE were obtained at 500 ppm of TETA-SA, TETA-OA, and TETA-LNA with %IE of 84.54%, 85.63%, and 89.26% (1% NaCl); 66.82%, 70.98%, and 75.23% (3% NaCl); and 52.30%, 54.18%, and 60.19% (5% NaCl), respectively. These results revealed that the more double bonds in hydrocarbon chain of imidazoline, the higher %IE will be produced. In line with increasing NaCl concentration in the environment, %IE will be decreased; but imidazoline derivatives still had their activities as corrosion inhibitor towards carbon steel.  Therefor, it can be suggested that imidazoline derivatives can be used as corrosion inhibitor on carbon steel in high salinity of sea water.

---

Korosi adalah suatu proses penurunan kualitas logam karena adanya reaksi kimia antara logam dengan lingkungannya. Salah satu metode untuk mengendalikan korosi yaitu dengan menggunakan inhibitor korosi. Imidazolin digunakan sebagai inhibitor korosi organik karena memiliki karakter adsorpsi yang baik, dapat membentuk lapisan pelindung pada permukaan logam, dan memiliki lapisan hidrofobik. Pada penelitian ini telah berhasil disintesis tiga senyawa turunan imidazolin dari reaksi antara TETA (trietilentetramina) dengan variasi asam lemak, yaitu asam stearat (AS), oleat (AO), dan linoleat (ALN), berturut-turut yaitu TETA-AS, TETA-AO, dan TETA-ALN menggunakan metode MAOS (Microwave Assisted Organic Synthesis) dengan variasi waktu reaksi. Persen yield optimum dari senyawa TETA-AS didapatkan pada waktu reaksi 9 menit (89,12%), TETA-AO 13 menit (98,79%), dan massa opimum untuk TETA-ALN diperoleh pada menit ke 9 (1,7023 g).Hasil sintesis senyawa TETA-AS dengan metode MAOS telah dibandingkan dengan metode refluks dan Dean Stark dalam pelarut xylena dan diperoleh % yield tertinggi pada waktu reaksi 13 jam untuk refluks (96,83%) dan Dean-Stark (97,27%). Terhadap hasil reaksi dilakukan identifikasi dengan menggunakan kromatografi lapis tipis (KLT) dan uji titik leleh, selanjutnya dilakukan karakterisasi menggunakan instrumen UV-Vis, FTIR, 1H-NMR, dan LC-MS/MS. Uji aktivitas inhibisi korosi dilakukan dengan memvariasikan konsentrasi seluruh senyawa hasil sintesis (100, 200, 300, 400, dan 500 ppm) serta variasi konsentrasi NaCl (1%, 3%, dan 5%) dengan metode siklik voltametri menggunakan potensiostat yang kemudian diolah menggunakan metode polarisasi Tafel untuk memperoleh nilai persen efisiensi inhibisi (%EI).Dari hasil pengukuran, diperoleh bahwa nilai %EI tertinggi berada pada konsentrasi 500 ppm dari senyawa TETA-AS, TETA-AO, dan TETA-ALN dengan nilai %EI berturut-turut 84,54%; 85,63%; dan 89,26% (NaCl 1%); 66,82%; 70,98%; dan 75,23% (NaCl 3%); serta 52,30%; 54,18%; dan 60,19% (NaCl 5%). Hasil uji aktivitas dalam menginhibisi korosi menunjukkan bahwa semakin banyak jumlah ikatan rangkap pada rantai hidrokarbon senyawa turunan imidazolin, semakin tinggi pula nilai %EI yang dihasilkan. Seiring dengan bertambahnya konsentrasi larutan NaCl dalam lingkungan akan menurunkan nilai %EI, namun senyawa turunan imidazolin masih memiliki aktivitas sebagai inhibitor korosi pada baja karbon. Sehingga diharapkan senyawa turunan imidazolin dapat digunakan sebagai inhibitor korosi pada baja karbon dalam perairan laut dengan kadar garam yang tinggi."

"ABSTRACTDewasa ini, kebutuhan inhibitor korosi di Indonesia semakin meningkat seiring dengan banyaknya industri minyak dan gas bumi. Oleh karena itu, diperlukan suatu penelitian mengenai sintesis inhibitor korosi khususnya yang berbasis senyawa organik untuk menangani permasalahan tersebut. Senyawa turunan imidazolin merupakan salah satu senyawa organik yang sering digunakan sebagai inhibitor korosi pada baja karbon. Pada penelitian ini, telah berhasil disintesis senyawa turunan imidazolin yaitu EDA-AS, DETA-AS, TETA-AS, dan AEEA-AS dengan mereaksikan asam stearat (AS) dan variasi poliamina dengan menggunakan metode MAOS (Microwave Assisted Organic Synthesis). Persen yield optimum senyawa EDA-AS diperoleh pada waktu sintesis 5 menit (94,28%), DETA-AS 7 menit (89,81%), TETA-AS 9 menit (89,18%), dan AEEA-AS 3 menit (96,21%). Sintesis senyawa TETA-AS menggunakan metode Dean Stark dan refluks juga dilakukan sebagai pembanding untuk mengetahui metode yang lebih efektif dan efisien, dimana diperoleh % yield tertinggi yaitu menggunakan metode Dean Stark (97,27%), diikuti oleh metode refluks (96,83%) dan MAOS (89,81%). Seluruh senyawa hasil sintesis telah dikonfirmasi strukturnya menggunakan instrumen UV-Vis, FT-IR, 1H-NMR, dan LC-MS/MS dimana terlebih dahulu diuji kemurniannya menggunakan kromatografi lapis tipis (KLT) dan alat pengukur titik leleh. Hasil sintesis kemudian diuji aktivitasnya sebagai inhibitor korosi terhadap baja karbon dalam larutan 1% NaCl dengan memvariasikan konsentrasi imidazolin (100, 200, 300, 400, dan 500 ppm) yang kemudian diolah dengan menggunakan metode polarisasi Tafel. Nilai %EI tertinggi diperoleh pada penambahan 500 ppm senyawa EDA-AS, DETA-AS, TETA-AS, dan AEEA-AS berturut-turut sebesar 74,21%; 75,90%; 85,52%; dan 89,70%. Penelitian ini telah membuktikan bahwa dengan memvariasikan poliamina akan sangat mempengaruhi aktivitas inhibisi dimana pada senyawa AEEA-AS memiliki aktivitas inhibisi paling besar karena memiliki kelektronegatifan yang lebih besar dibandingkan senyawa lainnya. Berdasarkan data yang diperoleh pada penelitian ini, dapat disimpulkan bahwa senyawa turunan imidazolin dapat memiliki kemampuan sebagai inhibitor korosi pada baja karbon.

---

ABSTRACTNowadays, the need of corrosion inhibitors in Indonesia is increasing because many oil and gas industries use equipment and instruments made of metal on their operational activities. Therefore, a study is needed on corrosion inhibitor synthesis, especially those derived from organic coumpunds to solve these problem. Imidazoline derivatives are one of the organic compounds that are often used as corrosion inhibitors in carbon steel. In this study, four imidazoline derivatives, i.e. (EDA-SA), (DETA-SA), (TETA-SA), dan (AEEA-SA) had been successfully synthesized by reacting Stearic Acid (SA) and various polyamine with variation of reaction time by using MAOS (Microwave Assisted Organic Synthesis) method. The optimum yield of imidazoline derivative compounds were obtained from EDA-SA at 5` (94,28%), DETA-SA at 7` (89,81%), TETA-SA at 9` (89,18%) and AEEA-SA at 3` (96,21%). The synthesis of TETA-SA compounds using the Dean Stark method and reflux was also carried out as a comparison to find out more effective and efficient methods, which obtained the highest% yield using Dean Stark method (97,27%), followed by the reflux method (96,83%) and MAOS (89,81%)). All of the synthesized compounds were identified by using thin layer chromatography (TLC) and examined their melting point. The structure of all synthesized compounds had been confirmed by using UV-Vis, FT-IR, 1H-NMR, and Liquid Chromatography-Mass Spectrometer (LC-MS). All of synthesized was tested for its activity as a corrosion inhibitor of carbon steel in 1% NaCl solution with variation of the imidazoline concentration (100, 200, 300, 400 and 500) ppm which is then processed using the Tafel polarization method. The highest %EI was obtained at 500 ppm of EDA-SA, DETA-SA, TETA-SA, and AEEA-SA with 74,21%; 75,90%; 85,52%; and 89,70%. This study has proven that varying polyamines will greatly influence inhibitory activity where the AEEA-SA compounds have the greatest inhibitory activity due to this compound having greater electronegativity than other compounds. Based on the data obtained in this study, it can be concluded that imidazoline derivative compounds can have the ability as corrosion inhibitors on carbon steel."

"Korosi yang disebabkan oleh karbondioksida (CO2) pada pipa baja karbon dan peralatan di pengolahan minyak dan gas sangat umum terjadi. CO2 larut dalam air menghasilkan asam karbonat (H2CO3) yang mempunyai sifat yang lebih korosif dibanding asam klorida (HCL) pada pH yang sama. Electrochemical impedance spectroscopy dan linear polarization resistance digunakan untuk mengetahui fenomena proses yang terjadi selama proses adsorbsi inhibitor di permukaan logam. Variasi temperature dan konsentrasi dari inhibitor dilakukan untuk mengetahui kemampuan inhibisi inhibitor dan mekanisme inhibisi. Penelitian ini dilakukan pada baja karbon A106 grB di dalam lingkungan 3% NaCl. Konsentrasi inhibitor bervariasi dari 0,5,15, dan 40 ppm dan dengan variasi temperature di 40 0C dan 90 0C. Pada temperature 40 0C laju korosi menunjukan 213,9 MPY pada lingkungan tanpa penambahan inhibitor , dan akan turun drastis ke 22,4 MPY ketika 5 ppm inhibitor ditambahkan ke lingkungan, dengan effisiensi inhibisi 90%. Penambahan konsentrasi inhibitor sampai 40 ppm meningkatkan effisiensi inhibisi sampai 98%. Penambahan konsentrasi inhibitor berbasis Imidazoline dari dari 0 ppm sampai 5 ppm pada temperature 90 0C dapat menghasilkan penurunan laju korosi yang signifikan yaitu dari 173,3 MPY menjadi 31,67 MPY, dengan effisiensi inhibisi 82%. Dengan penambahan konsentrasi inhibitor sebanyak 40 ppm akan menaikan effisiensi inhibisi sampai 99,99 %. Mekanisme penghambatan laju korosi terjadi sebagai akibat terbentuknya ikatan polar (O-H dan N-H) yang berikatan dengan permukaan logam melalui proses chemisorption.

---

Corrosion caused by carbon dioxide (CO2) in carbon steel pipes and equipment in oil and gas processing is very common. Water soluble CO2 produces carbonic acid (H2CO3) which has more corrosive properties than hydrochloric acid (HCL) at the same pH. Electrochemical impedance spectroscopy and linear polarization resistance are used to determine the processes that occur during the adsorbs inhibitor process on the metal surface. Variation of concentration of the inhibitor is conducted to determine the ability of inhibitor inhibition and inhibition mechanism. This research was conducted on A106 gr. B carbon steel in an environment of 3% NaCl. The inhibitor concentration varies from 0,5,15, and 40 ppm at 40 0C. At temperatures of 400C the corrosion rate shows 213.9 MPY in the environment without the addition of inhibitors, and will drop dramatically to 22.4 MPY when 5 ppm inhibitors are added to the environment. Electrochemical Impedance Spectroscopy is used to study inhibition mechanism. Increasing the concentration of Imidazoline based inhibitors from 0 ppm to 5 ppm at 90 0C can produce a significant decrease in corrosion rate from 173.3 MPY to 31.67 MPY, with 82% inhibition efficiency. With the addition of inhibitor concentrations up to 40 ppm will increase inhibition efficiency to 99,99 %. The mechanism of inhibition of corrosion rate occurs as a result of the formation of polar bonds (O-H and N-H) that bind to the metal surface through a chemisorption process."

"Oleic imidozaline is one of the nitrogen containing heterocyclic compounds that has been widely used as commercial corrosion inhibitor, especially in minizing the carbon dioxcide induced corrosion process in oilfield mining....."

"Dengan perkembangan industri yang cukup cepat diperlukan perlindungan untuk alat-alat proses yang merupakan suatu komponen penting dalam proses produksi. Perlindungan ini dapat berupa inhibitor korosi yang menjaga peralatan dari korosi terutama industry minyak dan gas bumi yang bersentungan langusng dengan fluida yang memiliki kecepatan dan tekanan tinggi, serta keadaan fluida yang asam sehingga dapat menyebabkan korosi pada peralatan produksi seperti sistem perpipaan. Proposal ini akan membahas mengenai produksi dari turunan imidazolin yang terbentuk dari asam oleat dan trietiltertamina yang dapat digunakan sebagai inhibitor korosi dengan melakukan simulasi proses serta pada proposal ini akan dilakukan perhitungan keekonomian untuk mengetahui seberapa mungkin perusahaan ini untuk dibangun di Indonesia.

---

With the rapid development of the industry, protection is needed for process equipment, which is an important component in the production process. This protection can take the form of corrosion inhibitors that protect equipment from corrosion, especially in the oil and gas industry, where they come into direct contact with fluids that have high velocity and pressure, as well as acidic conditions that can cause corrosion in production equipment such as pipeline systems. This proposal will discuss the production of turunan imidazoline, which is formed from oleic acid and triethylamine and can be used as a corrosion inhibitor. It will simulate the process and also include an economic calculation to determine the feasibility of establishing this company in Indonesia."

"Kemampuan inhibitor Imidazoline dalam menginhibisi baja karbon API 5L Grade B dalam lingkungan NaCl 3.5 % diinvestigasi dengan menggunakan metode Polarisasi Tahanan Linier atau Linier Polarization Resistance (LPR) dalam berbagai variasi konsentrasi. Konsentrasi yang digunakan pada penelitian kali ini adalah 0 ppm, 50 ppm, 10 ppm, 150 ppm, 200 ppm, dan 250 ppm. Hasil pengujian menunjukkan bahwa konsentrasi optimum dalam menurunkan laju korosi terdapat pada 200 ppm dengan laju korosi sebesar 0,0005 mm/year, sedangkan nilai Rp terus meningkat dan optimum pada konsentrasi 250 ppm dengan nilai sebesar 579,042 Ohm. Kurva laju korosi vs konsentrasi inhibitor menunjukkan bahwa konsentrasi optimum inhibitor imidazoline dalam menurunkan laju korosi terdapat pada konsentrasi 200 ppm.

---

The performance of Imidazoline based commercial corrosion inhibitor on carbon stel API 5L Grade B on NaCl 3.5 % solution was investigated using Linear Polarization Resistance Method or LPR. The Inhibitor concentration that used in this experiment were 0 ppm, 50 ppm, 100 ppm, 150 ppm, 200 ppm, and 250 ppm. Experimental results showed that the optimum concentration to decrease the corrosion rate is 200 ppm with the corrosion rate is 0,0005 mm/year , while the optimum polarization resistance is 579,042 Ohm at 250 ppm. The plot of corrosion rate vs inhibitor concentration show the optimum imidazoline inhibitor concentration for decreasing corrosion rate is 200 ppm."

"Imidazolin adalah senyawa heterosiklik yang mengandung nitrogen. Imidazolin dikenal di dunia industri, terutama di industri perminyakan sebagai inhibitor korosi pada kilang minyak baja dalam perairan laut. Dalam penelitian ini, telah berhasil disintesis empat senyawa turunan imidazolin, yaitu N1- 2- 2-undesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AL , N1- 2- 2-tridesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AM , N1- 2- 2-pentadesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AP , dan N1- 2- 2-heptadesil-4,5-dihidro-1H-imidazol-1il etil etana-1,2-diamina TETA-AS dengan mereaksikan TETA trietilentetramina dan variasi asam lemak jenuh berturut-turut asam laurat AL , miristat AM , palmitat AP , dan stearat AS tanpa pelarut dengan variasi waktu reaksi menggunakan metode MAOS Microwave Assisted Organic Synthesis . Yield optimum senyawa turunan imidazolin TETA-AL diperoleh pada waktu sintesis 7 menit 72,64 , TETA-AM 9 menit 81,13 , TETA-AP 11 menit 84,62 , dan TETA-AS 11 menit 87,49 . Metode refluks dan Dean Stark dengan pelarut xylena digunakan sebagai pembanding untuk memperoleh metode yang paling efektif dan efisien dalam sintesis senyawa imidazolin TETA-AP, dimana diperoleh yield tertinggi didapatkan pada metode Dean Stark 13 jam 95,89 , diikuti dengan metode refluks 13 jam 88,53 , dan MAOS 11 menit 84,62 . Seluruh senyawa hasil sintesis sudah dikonfirmasi strukturnya menggunakan instrumen spektrofotometer UV-Vis, spektrometer FTIR, spektroskopi 1H-NMR, dan spektrometer massa MS dengan terlebih dulu diidentifikasi dengan menggunakan kromatografi lapis tipis KLT dan uji penentuan titik leleh. Uji aktivitas sebagai inhibitor korosi terhadap baja karbon dalam larutan NaCl 1 dilakukan pada seluruh senyawa hasil sintesis dengan variasi konsentrasi imidazolin 100, 200, 300, 400, 500 ppm dengan mengukur arus korosi icorr menggunakan potensiostat eDAQ 450 dan Versasatat II . Hasil pengukuran arus menggunakan metode voltametri siklik ini kemudian diolah menggunakan metode Polarisasi Tafel untuk menentukan persen efisiensi inhibisi EI . Diperoleh EI tertinggi pada penambahan konsentrasi 500 ppm senyawa TETA-AL, TETA-AM, TETA-AP, dan TETA-AS berturut-turut adalah 74,44 ; 72,97 ; 78,55 ; dan 87,17 . Berdasarkan data tersebut, dapat disimpulkan bahwa keempat senyawa imidazolin TETA-AL, TETA-AM, TETA-AP, dan TETA-AS berpotensi sebagai inhibitor korosi pada baja karbon.

---

Imidazoline is a heterocyclic compound containing nitrogen atom. Imidazoline is well known in industry, especially in petroleum field as a corrosion inhibitor of oil refineries in sea environment. In this study, four imidazoline derivatives, i.e. N1 2 2 undecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA LA , N1 2 2 tridecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA MA , N1 2 2 pentadecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA PA , and N1 2 2 heptadecyl 4,5 dihydro 1H imidazol 1yl ethyl ethane 1,2 diamine TETA SA had been successfully synthesized by reacting TETA triethylenetetramine and various saturated fatty acid, such as lauric LA , miristic MA , palmitic PA , and stearic acid SA , respectively, with solvent free and variation of reaction time by using MAOS Microwave Assisted Organic Synthesis method. The optimum yield of imidazoline derivative compounds were obtained from TETA AL at 7 rsquo 72,64 , TETA AM at 9 rsquo 81,13 , TETA AP at 11 rsquo 84,62 , and TETA AS at 11 rsquo 87,49 . Reflux and Dean Stark methods in xylene were also conducted as a comparison to obtained the most effective and efficient methods in imidazoline TETA AP synthesis, which the highest yield was obtained from Dean Stark method at 13 h 95,89 , followed by reflux method at 13 h 88,53 , and MAOS method at 11 rsquo 84,62 . All of the synthesized compounds were identified by using thin layer chromatography TLC and examined their melting point. The structure of all synthesized compounds had been confirmed by using UV Vis spectrophotometer, FT IR spectrometer, 1H NMR spectroscopy, and mass spectrometer MS . Inhibition corrosion test of carbon steel in 1 NaCl solution was performed on all synthesized imidazoline derivatives compounds with variation of imidazoline concentration 100, 200, 300, 400, 500 ppm by measuring the corrosion current icorr using potensiostat eDAQ 450 and Versasatat II . Using cyclic voltammetry method, the measurement result were processed through Tafel Polarization to obtain the percentage of inhibition efficiency EI . The highest EI was obtained at 500 ppm of TETA AL, TETA AM, TETA AP, and TETA AS with 74,44 , 72,97 , 78,55 , and 87,17 , respectively. It can be concluded that all of the imidazoline compounds i.e. TETA AL, TETA AM, TETA AP, and TETA AS are potential organic compound as a corrosion inhibitor towards carbon steel."