cover
Epson Ray Kinko
"Konsumsi polimer dalam jumlah besar, menekan industri polimer untuk menghemat bahan baku material dan mempercepat laju produksi. MFC berbasis serat alam telah dipelajari mampu memperbaiki sifat dan kecepatan laju proses dari polimer. Indonesia sebagai negara agraris memiliki banyak sumber serat alam, salah satunya serat ijuk. Melalui proses perlakuan, serat alam diproses hingga didapatkan MFC yang akan dipelajari sifatnya sebagai agen penukleasi didalam polimer polipropilena jenis kopolimer impak. Dengan penambahan MFC, dapat meningkatkan 2% kristalinitas dan kecepatan kristalinitas hingga 12 detik. Penelitian ini menitik beratkan pada kemampuan kristalinitas dari PP setelah ditambahakan MFC.

Polymer comsumption in large scale, pushing polymer industry to reduce consumption of base material and increasing production time. ?Ijuk? based MFC has been studied can improve quality and accelerate process on PP. Indonesia as a maritime nation had many kind land riches, the one is ?ijuk? fiber. By conditioning process, ?ijuk? fiber made into MFC than have good bonding and will be studied his properties as nucleating agent on polymer polypropylene copolymer impact. With addiction of
"
Depok: Fakultas Teknik Universitas Indonesia, 2016
S36319
UI - Skripsi Membership  Universitas Indonesia Library
cover
Satrio Wibowo
"Saat ini penggunaan material berbasis polimer semakin meningkat seiring dengan pertumbuhan populasi manusia. Kebutuhan akan material berbasis polimer tersebut didasari oleh harga yang relatif murah dan fungsinya serba guna. Polimer berbasis pada minyak bumi merupakan jenis polimer yang sulit untuk diuraikan oleh mikroorganisme sehingga dibutuhkan material polimer alternative yang berasal dari alam untuk mengatasi isu lingkungan tersebut. Poly Lactic Acid (PLA) merupakan salah satu polimer alam yang cukup banyak digunakan. Namun PLA memiliki sifat mekanik dan ketahanan termal yang kurang baik, sehingga dibutuhkan pengisi dari bahan alam seperti serat ijuk untuk meningkatkan sifat mekanik.
Pada penelitian ini dilakukan percobaan untuk mengetahui kompatibilitas pengisi dan matriks, konsentrasi optimal pemutihan serat, waktu optimal pemutihan serat dan komposisi optimal antara pengisi dan matriks. Pengamatan dilakukan terhadap morfologi permukaan serat ijuk dan fraktografi material komposit menggunakan FE-SEM, mengetahui perubahan kristalinitas serat ijuk menggunakan X-RD, mengetahui gugus fungsi dari serat ijuk untuk melihat kandungan lignin dan hemiselulosa menggunakan FTIR serta kekuatan tarik material komposit menggunakan micro-tensile.
Hasil dari penelitian ini yaitu pemutihan dapat meningkatkan kompatibilitas pengisi dan matriks, konsentrasi optimal pemutihan adalah 7,5% NaClO selama 2 jam dan waktu optimal pemutihan adalah 1 jam dengan 10% NaClO. Dengan penambahan komposisi ijuk 10%, 20%, 30% ke dalam matriks PLA maka kekuatan tarik material komposit semakin meningkat.

Nowadays, The necessity of polymer-based material is getting higher because of its versatile utilization and relatively low cost. Petroleum polymer is difficult to be processed by micro-organism so that the alternative natural polymer is required to tackel this issue. Poly Lactic Acid (PLA) is one of the polymer used in many industries but PLA has the poorness on its mechanical properties and thermal resistance. Therefore, the addition of reinforcement such as ijuk fiber can be used to optimize its properties.
In this research, the compability of reinforcement and matrix, the optimum concentration of bleaching, the time of bleaching and the composition of reinforcement and matrix are studied. Visual observation on the morfology and fractography of ijuk fiber surface was performed using FE-SEM, the crystallinity of ijuk fiber was conducted using XRD, the functional group of ijuk fiber was carried out using FTIR to examine lignin and hemi-cellulose content and the tensile test of this composite material was performed using micro-tensile test.
From the data, it was acquired that bleaching enhance the compability between filler and matrix, the optimum concentration of bleaching is 7,5% NaClO for 2 hours and the optimum time of bleaching is 1 hour with 10% NaClO. In the mechanical properties aspect, it is obtained that as the higher ijuk addition, from 10% to 30%, into the PLA matrix, the tensile strength of the composite is improve.
"
Depok: Fakultas Teknik Universitas Indonesia, 2015
S60812
UI - Skripsi Membership  Universitas Indonesia Library
cover
Muhammad Taufiq
"ABSTRAK
Penelitian ini fokus pada peningkatan sifat mekanis Polipropilena impak kopolimer (PP) dengan menggunakan serat ijuk yang telah dimodifikasi. Modifikasi serat ijuk dilakukan dengan menggunakan proses alkalinisasi dan pemutihan. Proses tersebut bertujuan untuk meningkatkan kristalinitas dan kompatibilitas serat ijuk terhadap matriks PP. Pembuatan komposit PP-ijuk dilakukan menggunakan metode pencampuran lelehan panas untuk selanjutnya di cetak sesuai spesifikasi sampel uji sifat mekanis. Proses pencampuran dilakukan selama 15 menit dan dipelajari dua variabel utama, yakni variasi kadar serat ijuk (1%, 3%, 5%) dan variasi temperatur pencampuran (160⁰C dan 165⁰C). Komposit yang terbentuk selanjutnya dilakukan pengujian STA dan UTM. Dari hasil percobaan dapat disimpulkan bahwa peningkatan sifat mekanis yang optimal didapatkan pada percobaan menggunakan serat ijuk 1% dan suhu pencampuran 160⁰C. pada sampel tersebut teramati penambahan nilai kuat tarik hampir mencapai 1 Mpa. Hasil percobaan mengindikasikan bahwa serat ijuk hasil modifikasi dapat digunakan sebagai filler untuk meningkatkan sifat mekanis PP. Kondisi utama yang paling mempengaruhi peran positif serat ijuk adalah distribusi dan dispersi.

ABSTRACT
This research focused on the employment of modificated ?ijuk? fibers as fillers to improve the mechanical properties of polypropylene impact copolymer (PP). Ijuk fibers are processed through alkali treatment and bleaching. Those processes are intended to improve the crystalinity and compatibility of ?ijuk? fibers to matrix PP. Afterwards, PP-ijuk composite is made by using rheomixing and subsequently casted in satisfactory to meet the requirements as standard sample for tensile strength testing. Rheomixing was conducted for 15 minutes in different concentration of ?ijuk? fibers (1%, 3%, 5%) and temperature (160⁰C dan 165⁰C). STA and UTM were used to observe the properties of the composite. From the results, can be concluded that the optimal condition to improve the mechanical properties of PP is obtained in the condition of 1% ?ijuk? fibers and 160⁰C mixing temperature. These condition were successfully improved the tensile strength of PP by 1 Mpa. The experiments indicated that modificated ?ijuk? fibers can be used as filler to increase the mechanical properties of PP. Distribution and dispertion were attributed as the main factors which influenced the processes."
Depok: Fakultas Teknik Universitas Indonesia, 2016
S66420
UI - Skripsi Membership  Universitas Indonesia Library
cover
Juniko Nur Pratama
"Saat ini, plastik menjadi perhatian terkait dengan degradasi dan isu-isu lingkungan. Hal ini menyebabkan penelitian untuk mengembangkan bahan ramah lingkungan. Untuk meminimalkan dampak dari masalah tersebut, baru-baru ini penggunaan serat alam sebagai pengisi diperkenalkan karena biodegradabilitas dan ketersediaan. Serat alami yang menjanjikan adalah serat ijuk dari Arenga pinnata tanaman sebagai pengisi dan polypropylene polimer (PP) sebagai matriks. Sayangnya, serat alam dan polimer memiliki sifat yang berbeda, polimer memiliki sifat polar sedangkan serat alam bersifat non-polar sehingga mengurangi kompatibilitas dan dihasilkan kristalinitas yang sangat rendah. Untuk meningkatkan kompatibilitas dan kristalinitas, serat ijuk diberikan perlakuan dengan beberapa tahapan termasuk alkalinization dengan 5% dan 10% natrium hidroksida (NaOH), oksidasi dengan 3% dan 6% sodium hypochlorite (NaClO) dan hidrolisis dengan asam sulfat 20% (H2SO4) di urutan.
Tujuan dari perlakuan bertahap adalah untuk menghapus komponen seperti lignin, lilin, hemiselulosa, memfragmentasi lignin yang tersisa secara oksidatif dan menghilangkan bagian amorf masing-masing. Fourier-Transform Infrared (FT-IR) mengidentifikasi tingkat kompatibilitas sementara itu Differential Scanning Calorimetry (DSC) menunjukan kristalinitas dan Scanning Electron Microscope (SEM) menampilkan permukaan morfologi polypropylene.
Percobaan mengungkapkan bahwa efek dari serat ijuk dengan perlakuan bertahap dari 5% NaOH dan 10% NaOH menghasilkan kristalinitas polypropylene sekitar 31,2% dan 27,64% masing-masing dibandingkan dengan kristalinitas sebelum menambahkan "ijuk" serat untuk 16,8%. Hal ini menunjukkan bahwa seluruh perlakuan meningkatkan kompatibilitas dan kristalinitas polypropylene. Selain itu, penggunaan 5% NaOH menawarkan kristalinitas lebih baik dari polypropylene non-diobati. Percobaan menyimpulkan bahwa dengan menambahkan alkalinized serat ijuk perlakuan bertahap dapat meningkatkan kompatibilitas dan kristalinitas dari polypropylene.

Nowadays, plastics becomes concern associated with its degradation and environmental issues. It has led studies to develop an environmental-friendly material. To minimize the impact of those problems, recently the usage of natural fibers as a filler are introduced because of biodegradability and availability. The promising natural fiber is ijuk fiber from Arenga pinnata plant as a filler and polypropylene (PP) polymer as a matrix. Unfortunately, the natural fibers and polymers have the different properties on which polymers are polar while natural fibers are non-polar so that reducing the compatibility and resulting the poor crystallinity. To enhance the compatibility and crystallinity, ijuk fibers were prepared by multistage treatments including alkalinization with 5% and 10% sodium hydroxide (NaOH), oxidation with 3% and 6% sodium hypochlorite (NaClO) and hydrolysis with 20% sulphuric acid (H2SO4) in sequences.
The purposes of multistage treatments are to remove the components such as lignin, wax, hemicellulose, to cause an oxidative fragmentation of remaining lignin and to annihilate the amorphous parts respectively. Fourier-Transform Infrared (FTIR) confirms the compatibility meanwhile Differential Scanning Calorimetry (DSC) reveals the crystallinity and Scanning Electron Microscope (SEM) displays surface morphology of polypropylene.
The experiments were revealing that the effects of ijuk fibers by the multistage treatments of 5% NaOH and 10% NaOH resulting the crystallinity of polypropylene around 31,2% and 27,64% respectively compared to the crystallinity before adding the ijuk fibers for 16,8%. It indicates that the entire treatments increasing the compatibility and crystallinity of polypropylene. In addition, the use of 5% NaOH offers the better crystallinity than non-treated polypropylene. The experiments conclude that by adding alkalinized ijuk fibers of multistage treatments can increase the compatibility and crystallinity of polypropylene.
"
Depok: Fakultas Teknik Universitas Indonesia, 2015
T47073
UI - Tesis Membership  Universitas Indonesia Library
cover
Rangga Agung Pribadi Heriawan
"Serat ijuk semakin menarik untuk diteliti sebagai bahan pengisi polimer. Dengan memodifikasi permukaan serat ijuk, didapatkan selulosa mikrofibril (MFC) yang berbasis ijuk untuk kemudian dicampurkan dengan polimer membentuk produk berbasis MFC ijuk. Namun morfologi, kompatibilitas, stabilitas termal MFC berbasis ijuk terhadap sifat produk polimer perlu dilakukan penelitian lebih lanjut dan dibandingkan karakteristiknya dengan produk berbasis bubble glass.
Dalam penelitian ini telah dilakukan proses pencampuran lelehan panas dengan menggunakan mesin rheomix yaitu antara MFC berbasis ijuk dan bubble glass dengan polipropilena jenis homopolimer. Kandungan MFC berbasis ijuk dan bubble glass dalam campuran adalah 0,3; 0,6; dan 1 wt% dalam tiap 50 gram homopolimer polipropilena dengan variasi temperatur 160, 175, dan 190°C selama 15 menit.
Dari hasil penelitian diketahui bahwa dengan penambahan MFC berbasis ijuk dan bubble glass dapat menurunkan temperatur leleh (Tm) dan menaikan temperatur dekomposisi (Td), kecuali Td produk berbasis bubble glass akibat karakteristik bubble glass yang amorf. Tm maksimum produk berbasis MFC ijuk dan bubble glass didapatkan pada komposisi yang sama yaitu 0,3 wt% masing-masing sebesar 160,68°C dan 161,29°C. Sedangkan pada Tm maksimum produk berbasis MFC ijuk dan bubble glass masing-masing didapatkan pada temperatur pencampuran 190°C sebesar 160,66°C dan 175°C sebesar 162,52°C. Untuk Td maksimum produk berbasis MFC ijuk dan bubble glass didapatkan pada komposisi 1 wt% sebesar 256,08°C dan 0,3 wt% sebesar 296,07°C. Sedangkan pada Td maksimum produk berbasis MFC ijuk dan bubble glass masing-masing didapatkan pada temperatur pencampuran 175°C sebesar 270,72°C dan 160°C sebesar 290,12°C.

Ijuk fiber more interesting to study as a filler material for polymer. By modyfiying the surface fibers, microfibrilscellulose (MFC) ijuk-based obtained and then mixed it with polymer to form MFC ijuk-based products. However morphology, compatibility, thermal stability of MFC ijuk-based towards polymer product need further research and compared its characteristic with glass bubblebased products.
In this research has been carried out the process of hot-melt mixing using a rheomix machine that is between MFC ijuk-based and glass bubble with homopolymer type of polypropylene. The content of MFC ijuk-based and glass bubble in the mixture is 0.3; 0.6; and 1%wt in each 50 grams of homopolymer polypropylene with a temperature variation of 160, 175, and 190°C for 15 minutes.
The result showed that with the addition of MFC ijuk-based and glass bubblebased can lower the melting temperature (Tm) and raise the decomposition temperature (Td), except Td of glass bubble-based products due to the amorphous characteristics of glass bubble. The maximum Tm of MFC ijuk-based and glass bubble products obtained in the same composition that is 0,3%wt at 160.68°C and 161.29°C, respectively. In other side, the maximum Tm MFC ijuk-based and glass bubble-based obtained at mixing temperature of 190°C at 160.66°C and 175°C at 162.52°C, respectively. For maximum Td of MFC ijuk-based and glass bubble-based products obtained on the composition of 1%wt at 256.08°C and 0.3%wt at 296.07°C. In other side, the maximum Td of MFC ijuk-based and glass bubble product obtained at mixing temperature of 175°C at 270.72°C and 160°C at 290.12°C, respectively.
"
Depok: Fakultas Teknik Universitas Indonesia, 2016
T45868
UI - Tesis Membership  Universitas Indonesia Library
cover
Rachmat Ferdian
"Kelangkaan minyak bumi yang tidak terbarukan terus mendorong kenaikan produk-produk turunannya, salah satunya adalah plastik. Untuk mencari alternatif dari hal tersebut, dikembangkanlah plastik komposit yang terbuat dari Polylactic Acid (PLA) dengan penambahan serat ijuk diharapkan mempunyai sifat mekanis yang cukup tinggi dan ramah lingkungan. Kompatibilitas dari kedua bahan tersebut menjadi perhatian utama untuk menciptakan material komposit dengan sifat mekanis yang baik. Penelitian ini menggunakan matriks PLA dengan serat ijuk yang dicampur dengan metode pelarutan menggunakan Dichloromethane dan kemudian dicetak menjadi sampel uji tarik dengan metode cetak panas. Variabel yang digunakan adalah fraksi volum penguat 0%; 10%; 20%; 30%; 40% dan 50%, serta modifikasi permukaan serat dengan perlakuan alkali (NaOH) 0,25 M selama 30 menit untuk meningkatkan kompatibilitas serat terhadap matriks. Hasil pengujian menunjukkan penurunan sifat kekuatan tarik dan Modulus Young terhadap fraksi volum penguat dari 0% hingga 50%, yang tidak menunjukkan efek penguatan serat terhadap matriks untuk sampel tanpa modifikasi perrmukaan, sementara nilai elongasi menunjukkan tren peningkatan. Hal ini diakibatkan kompatibilitas yang buruk antara matriks dan serat. Setelah dilakukan modifikasi permukaan serat, terjadi peningkatan dari sifat mekanis komposit tersebut. Hasil pengujian FTIR menunjukkan terjadinya pengurangan lignin dan hemiselulosa yang dapat meningkatkan kompatibilitas matriks dan serat.

Petroleum as a non-renewable resources shows price increment for its derivative products, which one of those is plastics. The development for an alternative solution are developed, that is composite material from Polylactic Acid (PLA) which combined with Ijuk (Arenga pinnata) with the main focus in their compatibility to meet the demand for high specific strength and environmetalfriendly material. This research use PLA as a matrices dan Ijuk as a reinforcement, which is solution mixed using Dicholoromethane and then pressed by hot pressing method to formed tensile test specimens. The variations are volume fraction and fiber surface modification. Volume fraction used are 0%; 10%; 20%; 30%; 40% and 50%, while alkali treatment with NaOH 0,25M for 30 minutes is used for surface modification. Tensile test results show the decreament in tensile strength and Young’s Modulus versus fiber addition from 0-50%, while the elongation shows the conversely results, is showing no strengthening effect of fiber to the matrices for untreated composites. This is due to poor compatibility between matrices and fibers. After surface modification, tensile test results show the improvement in the mechanical properties due to elimination of lignin and hemicellulose which increases its compatibility, supported by the FTIR test results.
"
Depok: Fakultas Teknik Universitas Indonesia, 2013
T34974
UI - Tesis Membership  Universitas Indonesia Library
cover
Enrico Susanto
"[Pada penelitian ini, serat ijuk dihancurkan dan diayak ukuran 40 # setelah itu serat ijuk diberi perlakuan kimia dengan NaOH 2 % selama 1 jam, KMnO4 0,1 N selama 15 menit, dan NaClO 5 % selama 5 jam dengan tujuan mendapatkan selulosa kristalin. Setelah itu dilakukan proses pencampuran kering (hotmelt mixing) antara polipropilen dengan serat ijuk hasil perlakuan kimia dengan 7,5 % volum serat ijuk terhadap polipropilen dengan variabel temperatur 160°C, 165°C, dan 170°C dan variabel waktu pencampuran 15 menit dan 20 menit. Setelah itu dilakukan pengujian uji FTIR buat serat, sedangan buat komposit adalah uji tarik, uji STA, uji XRD, dan uji FE-SEM hal ini dilakukan untuk mendapatkan sifat kristalinitas dan mekanik dari komposit polipropilen ini. Hasil penelitian menunjukkan bahwa serat ijuk hasil perlakuaan lebih kristalin dari pada serat ijuk tanpa perlakukan, polipropilen dengan serat ijuk hasil perlakuaan kimia cukup kompatibel terhadap polipropilen, dari penelitian didapatkan sifat kristalinitas terbaik pada variabel 165°C selama 20 menit. Dan yang memiliki sifat kekuatan tarik paling baik adalah variabel 170°C selama 20 menit, sedangkan yang memiliki % elongasi paling baik adalah dengan variabel 160°C 20 menit.

In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes.;In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes.;In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes.;In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes.;In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes., In this work, palm fiber crushed and sieved size 40 # after the palm fiber chemically treated with 2% NaOH for 1 hour, 0.1 N KMnO4 for 15 minutes, and 5% NaClO for 5 hours in order to obtain crystalline cellulose. Once that is done the dry mixing (hotmelt mixing) between polypropylene and palm fiber chemical treatment results with 7.5% volume of the palm fiber and polypropylene with a variable temperature of 160°C, 165°C and 170°C and a variable time mixing 15 minutes and 20 minutes. After it was examined FTIR test for fiber, while the composite is made tensile test, STA test, XRD test and FE-SEM test this is done to obtain crystallinity and mechanical properties of polypropylene composites this. The results show that fiber perlakuaan results more crystalline fibers than untreated palm fiber, polypropylene and palm fiber chemistry results treatment compatible enough to polypropylene, crystallinity of the research showed the best properties on the variable 165 ° C for 20 minutes. And who has the most excellent tensile strength properties are variable 170 ° C for 20 minutes, while the best of % elongation is at a variable 160 ° C 20 minutes.]"
Depok: Fakultas Teknik Universitas Indonesia, 2015
S1575