Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Penelitian ini bertujuan untuk mengetahui pengaruh ketebalan resin terhadap depth of cure resin komposit serat sebagai substruktur. Lima belas spesimen dibagi menjadi 3 kelompok ketebalan berbeda: 3, 4, dan 5 mm n=5 . Masing-masing spesimen disinari dengan iradiansi 800 mW/cm selama 20 detik. Hasil penelitian menunjukkan depth of cure kelompok 1 adalah 81 , kelompok 2 adalah 78 dan kelompok 3 adalah 34. Nilai tersebut berbeda bermakna secara statistik melalui uji One-way ANOVA dan Post-hoc. Games-Howell. Disimpulkan bahwa ketebalan mempengaruhi depth of cure resin komposit serat sebagai substruktur.

---

The aim of this study is to know the effect of resin thickness on the depth of cure of fiber reinforced resin composite as substructure. Fifteen specimens are divided into 3 different thickness groups 3, 4, and 5 mm n 5 . Each specimen was cured with irradiation of 800 mW cm for 20 seconds. The result showed the depth of cure of group 1 was 81 , group 2 78 and group 3 34. The result was significantly different using One way ANOVA and Games Howell Post hoc test. It was concluded that resin thickness has effect on the depth of cure of fiber reinforced resin composit as substructure.

Abstrak :
Penelitian ini bertujuan untuk mengetahui pengaruh post-cure terhadap depth of cure DOC resin komposit serat dan membandingkan metode pengukuran DOC. Sembilan spesimen EverX Posterior warna A3 yang disinar dengan irradiansi 800-1000 mW/cm2 20 detik dibagi menjadi 3 kelompok: diukur setelah penyinaran dan setelah 24 jam post-cure dengan profil kekerasan Vickers; serta metode ISO 4049. DOC yang diukur setelah penyinaran dan setelah 24 jam post-cure 3,02 0,02 mm dan 3,93 0,03 mm; serta metode pengukuran ISO 4049 4,88 0,13 mm. Disimpulkan terdapat peningkatan bermakna DOC yang diukur setelah 24 jam post-cure, dan metode ISO 4049 menghasilkan DOC bermakna lebih tinggi dari profil kekerasan Vickers.

---

This study aims to identify the effect of post cure towards depth of cure DOC fiber reinforced composite and compare DOC measuring methods. Nine speciments of EverX Posterior shade A3 cured with light irradiation 800 1000 mW cm2 20s divided into 3 groups measured after curing and after 24 hours post cure with Vickers microhardness profile and ISO 4049 method. DOC that measured after curing and after 24 hours post cure are 3,02 0,02 mm and 3,93 0,03 mm and with ISO 4049 method 4,88 0,13 mm. It was concluded thatDOC measured after 24 hours post cure is significantly higher than immediately after curing, and ISO 4049 method produce significantly higher DOC than Vickers microhardness profile.

Abstrak :
Penelitian ini bertujuan untuk menganalisis pengaruh jarak penyinaran terhadap depth of cure DOC resin komposit serat sebagai substruktur. Delapan belas spesimen EverX Posterior warna A3 berbentuk silinder diameter 6 mm dan tebal 4 mm dibagi menjadi 3 kelompok jarak penyinaran 0, 2, dan 4 mm yang dipolimerisasi dengan LED Litex 695, irradiansi 800 mW/cm2, selama 20 detik. Pengukuran DOC dilakukan melalui rasio kekerasan Vickers. Analisis data dilakukan menggunakan uji ANOVA satu arah. Hasil penelitian menunjukkan DOC pada jarak penyinaran 0, 2, dan 4 mm sebesar 79 0,7, 77 0,6, dan 75 0,8. Disimpulkan terdapat perbedaan bermakna pada nilai DOC pada seluruh jarak penyinaran.

---

This study aims to analyze the effect of light curing distance on the depth of cure DOC of fiber reinforced composite as substructure. Eighteen specimens consist of EverX Posterior shade A3, formed into a cylindrical shape 6 mm in diameter and 4 mm thickness divided into 3 groups according to light curing distance 0, 2, and 4 mm which were polymerized with LED Litex 695, irradiance 800 mW cm2, for 20s. Meansurement of DOC was carried out by Vickers hardness ratio of specimens. Data were analyzed statistically by one way ANOVA test. The result showed the DOC at a light curing distances of 0, 2, and 4 mm was 79 0,7, 77 0,6, and 75 0,8. It was concluded that there is a significant difference in DOC among the light curing distance.

Abstrak :
Penelitian ini bertujuan untuk menganalisis pengaruh ketebalan komposit resin serat pendek KRSP dan waktu penyinaran terhadap kekerasan dan depth of cure DoC. Dua puluh empat spesimen KRSP EverX PosteriorTM berbentuk silinder berdiameter 6 mm, dibagi menjadi dua kelompok ketebalan: 4 dan 5 mm n=12. Setiap kelompok ketebalan disinar dengan jarak 2 mm, iradiansi 800 mW/cm2 selama 25 dan 30 detik n=6. Nilai kekerasan diukur dengan uji Vickers dan DoC didapatkan dengan menghitung rasio kekerasan permukaan atas dan bawah KRSP. Data dianalisis menggunakan uji One-way ANOVA. Disimpulkan ketebalan dan waktu penyinaran mempengaruhi kekerasan dan DoC KRSP sebagai substruktur. ......This study aims to analyze the effect of short fibre reinforced resin composite SFRC thickness and curing time on the hardness and depth of cure DoC. Twenty four specimens of SFRC EverX PosteriorTM were made and formed into cylindrical shapes with 6 mm in diameter, divided into two different thickness groups 4 and 5 mm n 12. Each thickness group were cured with 2 mm light curing distance, irradiance 800 mW cm2 for 25 and 30 seconds n 6. The hardness was measured by Vickers test and depth of cure was obtained by calculating the hardness ratio of the bottom to the top surface. Data were analyzed statistically by One Way ANOVA tests. It was concluded that thickness and curing time has significant effect on the hardness and DoC of SFRC as substructure.

Abstrak :
Resin komposit Bulk-Fill merupakan material yang dapat merestorasi kavitas dengan kedalaman 4-5 mm dalam satu kali penyinaran. Polimerisasi resin komposit dipengaruhi oleh durasi penyinaran dan metode penyinaran Light Curing Unit. Polimerisasi adekuat diperlukan untuk mendapatkan kekerasan permukaan dan Depth of Cure yang optimal. Penelitian ini dilakukan untuk mengetahui kekerasan permukaan dan Depth of Cure resin komposit Bulk-Fill yang disinar menggunakan Light Curing Unit penyinaran pulsa selama 5, 10, dan 20 detik. Spesimen berjumlah 30 buah dibagi berdasarkan kelompok perlakuan yaitu kelompok durasi penyinaran (5, 10, dan 20 detik) dan penyinaran (pulsa dan kontinu). Spesimen berdiameter 6 mm dan tebal 4 mm diuji menggunakan Knoop Microhardness Tester dengan beban indentasi 50 g selama 10 detik pada 5 titik berbeda. Hasil penelitian menunjukkan peningkatan kekerasan permukaan yang disinar dengan Light Curing Unit penyinaran pulsa dan kontinu seiring pemanjangan durasi penyinaran. Terdapat perbedaan bermakna (p<0,05) pada kekerasan permukaan di kelompok durasi penyinaran. Pada nilai depth of cure dengan kedua Light Curing Unit tidak terdapat perbedaan bermakna (p>0,05). Sehingga disimpulkan, penyinaran pulsa Light Curing Unit selama 5, 10, dan 20 detik pada resin komposit Bulk-Fill mengalami peningkatan kekerasan permukaan yang signifikan dan penggunaan dua metode penyinaran sama baik pada nilai depth of cure. ......Bulk-Fill composite resin have been introduced with the purpose of time savings. It can be placed in a 4-5 mm thickness bulks to be photo-cured in one step. Polymerization of composite resins affected by the irradiation time and mode. Adequate polymerization is needed to obtain optimal surface hardness and Depth of Cure. This study aimed to evaluate the influence of different exposure time with pulse-lighting mode on Bulk-Fill composite resin surface microhardness and Depth of Cure. Thirty specimens divided into 3 groups of exposure time (5, 10, and 20 sec) and 2 groups of irradiation mode (pulse and continuous), 6 mm in diameter and 4 mm in thick were prepared. Each specimen was measured using Knoop Microhardness Tester at each surface. The result showed that irradiation of Bulk-Fill composite resin with pulse-lighting mode curing unit for 5, 10, and 20 seconds experienced a significant increase in surface hardness. The depth of cure values shows no significant difference among different irradiation mode. It was concluded that that Bulk-Fill composite resin irradiated at longer exposure time exhibited significantly higher surface microhardness than those irradiated at shorter time. Meanwhile, there was no significant difference between two different irradiation mode for depth of cure.

Abstrak :
Latar belakang: Light Curing Unit (LCU) LED metode pulsa iradiansi 900 mW/cm2 telah dikembangkan untuk menghasilkan suhu pada ruang pulpa lebih rendah dibandingkan metode kontinu akibat polimerisasi resin komposit Nanofill pada durasi penyinaran 20 detik. Tujuan: menganalisis pengaruh durasi dan metode penyinaran pulsa terhadap kekerasan permukaan dan Depth of Cure resin komposit Nanofill. Metode: Spesimen resin komposit Nanofill (diameter 6 mm dan tebal 2 mm) disinar dengan LCU LED metode pulsa beriradiansi 900 mW/cm2 selama 5, 10, dan 20 detik, lalu direndam di dalam 5 ml akuades (37˚C 24 jam). Setiap spesimen diuji dengan Knoop Microhardness Tester sebanyak 5 kali pada permukaan atas dan bawah dan dihitung depth of cure. Hasil: Terjadi peningkatan kekerasan permukaan yang disinar dengan LCU metode penyinaran pulsa dan kontinu selama 5 hingga 20 detik yaitu 45,9±1,6/26,4±1,6 KHN hingga 68,8±1,8/57,4±1,6 KHN, dan 46,8±1,6/28,2±1,5 KHN hingga 69,3±1,2/57,8±1,1 KHN. Terdapat perbedaan bermakna (p<0,05) pada kekerasan permukaan di kelompok durasi penyinaran dengan uji One-way Anova dan post hoc Tamhane. Pada nilai depth of cure resin komposit Nanofill yang disinar antara kedua metode penyinaran tidak terdapat perbedaan bermakna (p>0,05) secara statistik. Kesimpulan: Resin komposit Nanofill yang disinar pada durasi lebih lama menunjukkan kekerasaan permukaan atas maupun bawah lebih tinggi dibandingkan dengan durasi lebih pendek. Demikian pula, depth of cure pada durasi lebih lama menunjukkan nilai lebih tinggi. Penyinaran metode pulsa iradiansi 900 mW/cm2 dan kontinu iradiansi 900 mW/cm2 menunjukkan kekerasan permukaan dan depth of cure yang sama.

Abstrak :
Latar belakang : Resin komposit bulkfill merupakan resin terbaru yang dapat direstorasi dengan kedalaman 4-5 mm dalam sekali penyinaran. Polimerisasi dipengaruhi oleh durasi penyinaran dan besaran irradiansi lightcuring untuk mendapatkan kekerasan permukaan dan depth of cure yang optimal. Tujuan: Penelitian ini bertujuan untuk mengetahui perbedaan nilai kekerasan resin komposit dan depth of cure resin komposit Tetric® N- Ceram bulk-fill yang disinari lightcure dengan durasi 5 detik, 10 detik dan 15 detik. Metode Penelitian: Dalam penelitian ini digunakan 24 spesimen resin komposit Tetric® N-Ceram bulk-fill berbentuk silinder dengan ukuran diameter 6 mm dan tebal 4 mm. Selembar mylar strip diletakkan diatas permukaan resin komposit sebelum dilakukan proses curing. Polimerisasi dilakukan menggunakan Light Curing Unit (LED DBA iLed) selama 5 detik, 10 detik dan 15 detik dengan irradiansi 1100 mW/cm2. Setelah polimerisasi, spesimen direndam dalam akuades pada suhu 37oC selama 24 jam. Spesimen dibagi menjadi tiga kelompok (n=8) yaitu; kelompok resin komposit dengan penyinaran 5 detik, penyinaran 10 detik dan penyinaran 15 detik. Spesimen diuji menggunakan HMV-G Series Micro Vickers Hardness Tester (Shimadzu, Jepang) dengan beban 100 gram selama 10 detik untuk mendapatkan nilai kekerasan. Data dianalisis dengan uji statistik Kruskall Wallis dan Post-Hoc Mann Whitney. Hasil Penelitian: Hasil uji statistik menunjukkan kenaikan bermakna nilai kekerasan permukaan dan depth of cure pada resin komposit Tetric® N-Ceram bulk-fill. Nilai kekerasan dan depth of cure tertinggi terlihat pada resin komposit Tetric® N-Ceram bulk-fill pada kelompok penyinaran 15 detik, yaitu sebesar 41,61 ± 1,25 KHN dan 72,71 ± 1,88. Kesimpulan: Disimpulkan bahwa semakin bertambah durasi penyinaran lightcure yang disinari, semakin bertambah nilai kekerasan permukaan dan depth of cure resin komposit Tetric® N-Ceram bulk-fill. ......Background : Bulkfill composite resin is the newest resin that can be restored to a depth of 4-5 mm in one step. Polymerization is determined by the irradiation time and the amount of light curing irradiance to obtain optimal microhardness and depth of cure. Objective: The aim of this study was to determine the difference in the value of the microhardness of the composite resin and the depth of cure of the Tetric® N-Ceram bulk- fill composite resin irradiated by lightcure with a duration of 5 seconds, 10 seconds and 15 seconds. Method: Twenty four specimens of Tetric® N-Ceram bulk-fill Composite Resin were used in this study. All materials were prepared into disk-shaped specimens of 6 mm in diameter and 4 mm in thickness. A piece of mylar strip was placed on the top of the specimens just before the polymerization.. Polymerization was carried out using a Light Curing Unit (LED DBA iLed) for 5 seconds, 10 seconds and 15 seconds with an irradiance of 1100 mW/cm2. After polymerization, specimens were immersed in 37 aquadest solution for 24 hours. Specimens were divided into three groups (n=8) that is; composite resin group with 5 seconds of irradiation, 10 seconds of irradiation and 15 seconds of irradiation. Specimens were tested with HMV-G Series Micro Vickers Hardness Tester (Shimadzu, Jepang) with 100 gram indentation in 10 seconds. Data were analyzed using Kruskall Wallis and Post-Hoc Mann Whitney to assess the significant differences among groups Result: The results of statistical tests showed a significant increase in the value of microharhardness and depth of cure on Tetric® N-Ceram bulk- fill composite resin. The highest microhardness and depth of cure values were seen in the Tetric® N-Ceram bulk-fill composite resin in the 15 second irradiation group, namely 41.61 ± 1.25 KHN and 72.71 ± 1.88. Conclusion: It was concluded that the longer the duration of irradiation of the irradiated lightcure, the higher the microhardness value and depth of cure of the Tetric® N-Ceram bulk-fill composite resin.

Abstrak :
Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi. ......Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC.

Abstrak :
Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi. ......Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC.

Abstrak :
Penelitian ini bertujuan untuk menganalisis pengaruh ketebalan komposit resin serat pendek KRSP dan iradiansi terhadap kekerasan dan depth of cure DoC. Dua puluh empat spesimen KRSP berbentuk silinder berdiameter 6 mm dibagi menjadi 2 kelompok ketebalan; 4 dan 5 mm n=12. Masing-masing kelompok dibagi menjadi 2 kelompok yang dipolimerisasi dengan iradiansi berbeda; 1000 dan 1200 mW/cm2 n=6. Setiap spesimen dipolimerisasi selama 20 detik dengan jarak penyinaran 2 mm. Nilai kekerasan didapat melalui uji kekerasan Vickers dan DoC didapat dengan mengukur rasio kekerasan permukaan bawah terhadap permukaan atas. Data dianalisis menggunakan uji statistik One-Way ANOVA. Hasil penelitian menunjukkan adanya perbedaan signifikan. ......This study aims to analyze the effect of short fibre reinforced resin composite SFRC thickness and light curing irradiance on the hardness and depth of cure DoC . Twenty four specimens of SFRC were made into cylindrical shape with a diameter of 6 mm and divided into 2 different thickness groups 4 and 5 mm n 12. Each group was divided into another 2 different groups which was cured by different irradiance 1000 and 1200 mW cm2 n 6 . Each specimen was cured for 20s with 2 mm light curing distance. The hardness was measured by Vickers hardness test and DoC was measured by calculating a hardness ratio of the bottom to the top surface of specimens. Data were analyzed statistically by One Way ANOVA tests. The result showed significant differences.