Hasil Pencarian  ::  Simpan CSV :: Kembali

"Nanofluida adalah fluida penghantar panas yang mengandung partikel berukuran nano ( 1 – 100 nm). Penelitian yang dilakukan membahas karakterisasi nanofluida berbahan dasar fraksi non-logam dari limbah elektronik Printed Circuit Board (PCB) yang didominasi kandungan SiO2. Karakterisasi berfokus pada pengaruh konsentrasi partikel (0; 0,1; 0,3; dan 0,5%) dan surfaktan Cetyltrimethylammonium bromida (CTAB) (0; 3; 5; dan 7%) terhadap kondktivitas termal, viskositas, dan zeta potensial nanofluida. Hasil pengujian Particle Size Analyzer (PSA) pada partikel menunjukkan terjadinya peningkatan ukuran partikel dari 268,7 d.nm menjadi 1035,6 d.nm (milling 10 jam) dan 572,6 d.nm (milling 20 jam), sehingga partikel tidak mencapai ukuran nano dan tergolong kedalam micro-dispersed thermal fluid. Nilai konduktivitas termal mengalami penurunan seiring meningkatnya konsentrasi partikel dan surfaktan dengan nilai tertinggi pada sampel 0,5% partikel dan 0% CTAB sebesar 0,764 W/mK. Nilai viskositas mengalami peningkatan linear seiring dengan penambahan konsentrasi partikel dan surfaktan dengan nilai tertinggi pada sampel 0,5% partikel dan 7% CTAB sebesar 2,658 mPa.s. Nilai zeta potensial mengalami peningkatan seiring penambahan konsentrasi partikel dan surfaktan hingga titik optimumnya pada sampel 5% CTAB dengan hasil zeta potensial 43 mV.

---

Nanofluids are heat transfer fluids that contain nano-sized particles (1-100 nm). The conducted research discusses the characterization of nanofluids based on the non-metallic fraction of Printed Circuit Board (PCB) electronic waste, predominantly containing SiO2. The characterization focuses on the influence of particle concentration (0, 0.1, 0.3, and 0.5%) and Cetyltrimethylammonium bromide (CTAB) surfactant (0, 3, 5, and 7%) on the thermal conductivity, viscosity, and zeta potential of the nanofluids. Particle Size Analyzer (PSA) testing results on the particles indicate an increase in particle size from 268.7 d.nm to 1035.6 d.nm (after 10 hours of milling) and 572.6 d.nm (after 20 hours of milling), indicating that the particles do not reach the nano size and belong to the category of micro-dispersed thermal fluid. The thermal conductivity value decreases with increasing particle and surfactant concentrations, with the highest value observed in the sample with 0.5% particles and 0% CTAB, amounting to 0.764 W/mK. The viscosity value shows a linear increase with the addition of particle and surfactant concentrations, reaching the highest value in the sample with 0.5% particles and 7% CTAB, at 2.658 mPa.s. The zeta potential value increases with increasing particle and surfactant concentrations until reaching the optimum point in the sample with 5% CTAB, resulting in a zeta potential of 43 mV."

"Perkembangan teknologi pendinginan sangat berpengaruh terhadap hasil dari perlakuan panas yang dilakukan pada sebuah material. Media pendingin yang efektif dinilai mampu menghasilkan kecepatan pendinginan yang cepat sehingga dapat menghasilkan baja dengan kekerasan yang tinggi. Penelitian ini bertujuan untuk memanfaatkan grafit dan oli 5W-40 untuk membuat nanofluida sebagai media pendingin. Grafit yang digunakan terlebih dahulu digerus sebelum dicampurkan dengan oli 5W-40. Pada penelitian ini juga dilihat pengaruh dari penambahan surfaktan berupa sodium dodecylbenzenesulfonate (SDBS), cetyltrimethylammonium-bromide (CTAB), dan polyethylene glycol (PEG) untuk membandingkan efektivitas nanofluidanya. Konsentrasi grafit yang digunakan juga beragam, yaitu 0.1%w/v, 0.3%w/v, dan 0.5%w/v sehingga dapat dilihat pengaruh yang dihasilkan dari perubahan konsentrasi tersebut. Berdasarkan hasil penelitian, didapatkan bahwa penambahan surfaktan dapat meningkatkan nilai konduktivitas termal dari nanofluidanya. Diketahui bahwa penambahan CTAB dengan konsentrasi partikel 0.1%w/v menghasilkan nanofluida dengan nilai konduktivitas tertinggi, yaitu 0.173 W/mK. Sementara itu, kekerasan baja tertinggi dihasilkan oleh nanofluida dengan penambahan PEG dan konsentrasi partikel 0.1%w/v, yaitu sebesar 38 HRC dan diikuti oleh nanofluida dengan penambahan CTAB dan konsentrasi partikel 0.1%w/v, yaitu sebesar 36 HRC. Hal ini disebabkan karena adanya mekanisme penyerapan yang berbeda-beda dari surfaktan pada lingkungan yang berbeda.

---

The development of quenching technology will highly influence the results of materials’ heat treatment process. An effective quenchant obtained fast cooling rate during the quenching process so that the steel’s hardness increased. This study aims to utilize graphite as nanoparticles and 5W-40 engine oil as the base fluid to make a nanofluid quenchant. The graphite was being milled before mixed with the oil. This study also studied the effect of surfactants addition in the form of sodium dodecylbenzenesulfonate (SDBS), cetyltrimethylammonium-bromide (CTAB), and polyethylene glycol (PEG) to compare the effectiveness of the nanofluids. The graphite concentration varies as well, namely 0.1%w/v, 0.3%w/v, and 0.5%w/v to see the effect resulting from the change in concentration. Based on the results of the study, it was found that the addition of surfactants affects the nanofluids’ thermal conductivity sufficiently. It is known that the addition of CTAB with particle concentration of 0.1%w/v produces the highest conductivity value, which is 0.173 W/mK. Meanwhile, the highest steel hardness was produced by nanofluid with the addition of PEG with particle concentration of 0.1%w/v, which was 38 HRC and followed by nanofluid with the addition of CTAB with particle concentration of 0.1%w/v, which was 36 HRC. The discrepancy happened because of the surfactants’ different absorption mechanism in different environments."

"Papan PCB merupakan bahan penyusun utama dari perangkat elektronik. Seiring berjalannya waktu perkembangan perangkat listrik semakin tinggi dan meningkat hal ini juga berkaitan terhadap limbah yang dihasilkan terhadap lingkungan. Limbah papan PCB dapat dimanfaatkan salah satunya sebagai nanopartikel. Papan PCB disintesis menjadi nanopartikel dengan melakukan beberapa tahap diantaranya leaching menggunakan HCL 1 M selama 24 jam, Pirolisis dilakukan dengan gas flow 5L/menit pada suhu 500oC menggunakan gas argon, dan Dry milling selama 20 jam. Setelah disintesis dilakukan karakterisasi pada sebelum dan sesudah proses menggunakan pengujian XRF pada proses leaching, pengujian XRD pada proses pirolisis, dan pengujian PSA pada proses milling. Nanofluida disintesis dengan variabel kombinasi dari 0%, 0,1%, 0,3%, dan 0,5% nanopartikel dan 0%, 3%, 5%, dan 7% surfaktan. Hasil pendinginan cepat menggunakan nanofluida didapatkan dengan penambahan 0,3% nanopartikel tanpa surfaktan dimana mikrostruktur yang terbentuk didominasi oleh fasa martensite dengan beberapa fasa bainite. Sedangkan kekerasan yang didapat dengan nilai tertinggi yaitu 55 HRC pada penggunaan 0,5% nanopartikel tanpa surfaktan. Sedangkan nilai kekerasan terendah didapat dengan kombinasi 0,5% nanopartikel dan 5% surfaktan dengan nilai kekerasan 34 HRC. Penambahan surfaktan CTAB pada nanofluida sebagai aplikasi media pendinginan cepat kurang efektif dikarenakan karakteristik sifat CTAB yang sensitive terhadap panas menjadi gumpalan.

---

PCB board is the main constituent of electronic devices. As time goes by, the development of electrical devices is getting higher and increasing, this is also related to the waste they produce on the environment. PCB board waste can be used as nanoparticles. PCB boards were synthesized into nanoparticles by carrying out several steps including leaching using 1 M HCL for 24 hours, pyrolysis was carried out with a gas flow of 5L/minute at 500oC using argon gas, and dry milling for 20 hours. After being synthesized, characterization was carried out before and after the process using XRF testing in the leaching process, XRD testing in the pyrolysis process, and PSA testing in the milling process. The nanofluids were synthesized with variable combinations of 0%, 0.1%, 0.3%, and 0.5% nanoparticles and 0%, 3%, 5%, and 7% surfactants. Fast cooling results using a nanofluids were obtained by adding 0.3% nanoparticles without surfactants where the microstructure formed was dominated by the martensite phase with several bainite phases. While the hardness obtained with the highest value is 55 HRC using 0.5% nanoparticles without surfactants. While the lowest hardness value was obtained with a combination of 0.5% nanoparticles and 5% surfactants with a hardness value of 34 HRC. The addition of CTAB surfactants to nanofluids as fast cooling media applications is less effective due to the characteristics of CTAB which are sensitive to heat to form agglomerates."