Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Engineering tribology, is an established introductory reference focusing on the key concepts and engineering implications of tribology. Taking an interdisciplinary view, the book brings together the relevant knowledge from different fields needed to achieve effective analysis and control of friction and wear. Updated to cover recent advances in tribology, this new edition includes new sections on ionic and mesogenic lubricants, surface texturing, and multiscale characterization of 3D surfaces and coatings. Current trends in nanotribology are discussed, such as those relating to lubricants, coatings and composites, and geotribology is introduced.

Abstrak :
Buku yang berjudul "Handbook of tribology : Materials, coatings, and surface treatments" ini ditulis oleh Bharat Bhushan dan B. K. Gupta. Buku ini merupakan sebuah buku panduan mengenai tribologi.

Abstrak :
Telah dilakukan kegiatan penelitian mengenai pembuatan dan analisis nanofluida bio berbasis serat bacterial cellulosa nata de coco dengan modifikasi 2,2,6,6- Tetramethylpiperidine-1-oxyl (TEMPO). Pertama, serat mentah yang berbentuk pelikel diproses hingga menjadi film. Proses penghancuran serat kemudian dilakukan dengan menggunakan grinder hingga bentuk serat menjadi bubuk. Kemudian, serat dicampur dengan TEMPO untuk melemahkan ikatan hidrogen pada serat. Serat yang sudah dimodifikasi kemudian dicampurkan ke dalam fluida dasar oli polyol ester (POE) beserta nonionic surfaktan Span 60. Surfaktan bertujuan untuk membentuk tolakan stearic antara partikel serat. Uji yang dilakukan adalah berupa karakterisasi, stabilitas, viskositas, konduktivitas thermal, dan tribologi. Analisa Life Cycle Assessment (LCA) juga dilakukan untuk mengetahui seberapa besar pengaruh penelitian ini terhadap lingkungan. Terdapat peningkatan viskositas dengan pemberian serat nata de coco. Koefisien friksi (COF) terendah diperoleh oleh sampel N2S4 dengan peningkatan sebesar 40% dibandingkan dengan POE. Dapat disimpulkan bahwa hasil ini dapat menjadikan serat nata de coco sebagai aditif pelumas yang mengurangi friksi dan meningkatkan viskositas

---

Research activities had been carried out on the synthesis and analysis of bio nanofluids based on bacterial cellulose nata de coco fibers with a modification of 2,2,6,6-Tetramethylpiperidine-1-oxyl (TEMPO). Firstly, the raw nata de coco in the form of pellicles are processed into films. The process of cellulose crushing was carried out using a grinder to form the cellulose into powder. Then, the dried cellulose was modified with TEMPO to weaken its hydrogen bonding. The modified cellulose was then mixed into the polyol ester (POE) base fluid along with the nonionic surfactant Span 60. The aim of the surfactant is to form a stearic repulsion between cellulose particles. Characterization, stability, viscosity, thermal conductivity, and tribology were successfully conducted. Life Cycle Assessment (LCA) analysis was also conducted. There was an increase in viscosity with the provision of nata de coco fiber. The lowest coefficient of friction (COF) was obtained by the N2S4 sample with 40% increament compared to POE. It can be concluded that nata de coco fiber has a potential as a lubricant additive that reduces friction and modifiy viscosity

Abstrak :
Written by leading experts in a range of related fields, this book covers biomimetics, environmentally friendly lubrication, tribology of wind turbines and renewable sources of energy, and ecological impact of new technologies of surface treatment.

Abstrak :
ABSTRAK
Proses semprot logam merupakan suatu proses perlakuan permukaan untuk memperoleh ketahanan aus yang lebih baik dari logam induknya dan bisa juga untuk memperbaiki dimensi material yang mengalami pengecilan. Pada penelitian iui digunrakan paduan babbitt sebagai umpan dalam bentuk umpan kawat yang dicairkan oleh nyala api dari gas oksigen-asetilen. Paduan babbit itu sering digunakan sebagai bantalan karena memiliki sifat tahan aus dan bersifat sebagai pelumas.

Dalam penelitian ini digunakan dua parameter proses semprot logam yaitu kecepatan umpan dan jarak semprot. Adapun kecepatan umpan yang dicimbil adalah 1/54 m/det dan 1/61 m/det, dengan jarak semprot 7,63, 12,70, 17,78 cm. Dari parameter tersebut dapat dipelajari karakteristlik hasil pelapisan dengan melakukan pengujian kekerasan, porositas dan keausan.

Dari hasil penelitian diketahui bahwa kekerasan terlinggi dan ketahanan aus tertinggi yang diperoleh dari deposit lapisan babbitt dicapai pada kondisi dengan kecepatan umpan 1/64 m/det dengan jarak penyemprotan 12, 70 cm.