Abstrak :
Studi Pengaruh Temperatur Sinterisasi Terhadap Kandungan Oksigen .Superkonduktor YBa 2cu 3ox Dengan Memakai Cara Titras i Yodometri xi + 68f~ halarnan tabel , gambar , lampiran Senyawa keramik YBa2cu3ox dibuat dengan mencampur - kan r 2o3 , Baco3 ,dan CuO dal am perbandingan mol ~ ·~ 2. : 3 , melalui berbagai t ahapan kerja yaitu kal s inasi, sinterisasi, dan anea isasi. Se:riyawa i ni dapat bertindak sebagai superkonduktor pada temper atur kritis yang sangat rendah ( 93 K ). Mutu superkonduktor YBa2cu3ox ditentukan oleh tinggi- rendahnya temperatur saat munculnya gejala superkon - duktivi tas, yang berkai tan dengan kandungan oksigen su perkonduktor YBa2cu 3ox tersebut. Penelitian ini menyelidiki pengaruh tinggi-renda~- nya temperatur proses sinterisasi terhadap kandungan oksigen superkonduktor YBa2cu3ox. Kte-beradaan gejala superkonduktivitas pada c.uplikan dibuktika:n melalui cara - cara uji efek Meissner - Ochsenfeld dan perbandingan pola difraksi sinar X, sementara untuk menentukan kandungan oksigennya dipakai cara t.i trasi yodometri. Hasil P,eneli tian menunjukkan bahwa semakin tinggi temperat.ur sinteri sasi. superkondukt.or YBa2cu,ox,. kandungan oksigennya semakin rendah

Abstrak :
Penelitian ini bertujuan untuk memperoleh kandungan Superkonduktor (Bi-Pb)-2223 setinggi mungkin dengan cara variasi doping Pb dengan proses sintesis dua tahap, juga untuk memahami mekanisme pembentukan Superkonduktor yang bersangkutan khususnya peranan Pb di dalam proses tersebut. Metode 'basah' gunakan dalam pembentukan Superkonduktor (Bi-Pb)-2223 yang dibuat melalui prekursor (Bi-Pb)-22I2 dengan ditambah bahan pelengkap Ca2CuO^ dan CuO. Perhitungan fraksi volume fase 2223 dan kurva p-T untuk sampel Bi] 8PbxSr2CaCuiO8 (x=0,4) menunjukkan basil yang terbaik. Doping Pb sebesar 0,4 merupakan harga paling optimal. Fraksi volume fase 2223 yang dicapai sebesar 92,34%, sedangkan Tc tertinggi yang dicapai adalah 110 K.

---

The goal of this experiment is to obtain the highest contents of high Tc superconductor (Bi - Pb) -2223 with variation of Pb dopant, in a two step synthesized process, to understand the formation of phase and the role of Pb. Superconductor (Bi - Pb) - 2223 was formed from the precursor (Bi-Pb)-2212 with addition of Ca2CuO3 and CuO, all the process is done in "wet" method. From the volume fraction of XRD spectra and p-Tcurves, in found that sample Bi] sPbxSr2CaCu2 ( x - 0.4 ) is the best. The optimum Pb dopant is 0.4 and the highest Tc is 11 OK.

Abstrak :
INTISARI Telah dibuat superkonduktor komposit YBa2Cu307.x +X dengan X adalah Ag203 dan PVA (polyvinil alcohol) dan diukur suseptibilitasnya. Massa bahan komposit tambahan Ag203 sekitar 13 %, sedangkan massa PVA adalah 10 %. Superkonduktor komposit disiapkan dengan reaksi padatan. Selanjutnya cuplikan disiapkan dalam bentuk silinder tipis berdiameter 10 mm dan tebal sekitar 2 mm. Cuplikan superkonduktor diuji dengan melihat levitasinya di dalam medan magnet. Pengukuran suseptibilitas dilakukan dengan mengukur suseptibilitas ACnya Hasil pengukuran menunjukkan bahwa penambahan Ag203 ke dalam cuplikan akan mengurangi kekuatan gandengan butiran superkonduktor dan mempengaruhi suhu kritis dari bahan superkonduktor beberapa kelvin. Hasil yang serupa diperoleh pada superkonduktor komposit dengan PVA. Kekuatan gandengan antar butir pada superkonduktor komposit Ag lebih besar dibandingkan dengan kekuatan gandengan antar butir pada superkonduktor komposit PVA.

Abstrak :
ABSTRACT
Peneliti melakukan proses sintesis dari material superkonduktor La2-xSrxCuO4 LSCO, dengan x = 0,16; 0,22 dan 0,25, dengan metode sol-gel. Prekursor yang peneliti gunakan dalam metode ini berbasis nitrat. Bahan dikalsinasi untuk menghilangkan komponen organik dan disintering dengan suhu 600 C selama 6 jam. Analisis pengukuran difraksi sinar-X XRD dengan Rietvield Refinement menunjukkan bahwa struktur stabil pada fase tetragonal I4/mmm dengan ukuran kristal cenderung semakin mengecil seiring dengan bertambahnya doping Sr. Scanning Electron Microscopy SEM digunakan untuk mengamati morfologi material dan mengkonfirmasi parameter sel dari analisis pengukuran XRD. Penggunaan SEM juga untuk mengkonfirmasi kehomogenan dari material LSCO. Dengan Electron Dispersive Spectroscopy hasilnya mengkonfirmasi komposisi material yang sudah mendekati nilai perhitungan. Untuk melihat adanya perubahan fasa superkonduktor, cryogenic magnetometer digunakan untuk mengukur resistivitas pada material LSCO.

---

ABSTRACT
We performed a synthesis process of the La2 xSrxCuO4 LSCO, with x 0,16 0,22 and 0,25, superconducting material by sol gel method. Precursors that we use in this method are nitrate based. The material was calcined to remove the organic component and sintered at 600 C for 6 hours. Analysis of X ray diffraction measurements XRD with Rietvield Refinement showed that the structure stabilized to the tetragonal phase I4 mmm with the crystallite size tends to decrease as doping increases Sr. Scanning Electron Microscopy SEM is used to observe the morphology of the material and confirm the cell parameters of the XRD measurement analysis. The use of SEM is also to confirm the homogeneity of LSCO material. With Electron Dispersive Spectroscopy the results confirm the composition of the material that is close to the calculation value. To see a superconducting phase change, cryogenic magnetometers are used to measure resistivity in LSCO materials.

Abstrak :
Bahan superkonduktor BPSCCO-2212 dengan kadar CaCO3 1,0 dan 1,10 fraksi mol telah disintesis dengan metode reaksi padatan (solid state reaction method). Sintesis dilakukan selama 10 jam pada suhu kalsinasi (Tk) 800oC dan sintering selama 20 jam dengan suhu (Ts) 830oC. Tujuan penelitian untuk mengetahui pengaruh variasi doping Pb dan Ca terhadap tingkat kemurnian fase superkonduktor Bi-2212 yang terbentuk (fraksi volume (Fv), derajat orientasi (P), dan impuritas (I)). Hasil sintesis dikarakterisasi menggunakan XRD (X-Ray Diffraction) dan SEM (Scanning Electron Microscopy). Hasil analisis profil XRD oleh sofware Celref menunjukkan variasi doping Pb cenderung meningkatkan fraksi volume (Fv) BSCCO-2212. Fraksi volume (Fv) pada kadar Ca = 1,0 dan Pb = 0 diperoleh 72,60%, Pb = 0,2, diperoleh 74,10%, Pb = 0,4 diperoleh 60,48 %, dan Pb = 0,6 diperoleh 61,90 %. Sedangkan derajat orientasi (P) tertinggi diperoleh dengan doping Pb = 0,6 sebesar 30,62%. Untuk Fraksi volume (Fv) pada kadar Ca = 1,10 dan doping Pb = 0, diperoleh 65,17 %, Pb = 0,2, diperoleh 78,81%, Pb = 0,4 diperoleh 63,29%, dan Pb = 0,6, diperoleh 87,31%. Fraksi volume relatif baik pada sampel kadar Ca = 1,10 dengan doping Pb = 0,6, yaitu 87,31%. Sedangkan derajat orientasi (P) relatif baik pada sampel Ca = 1,10 tanpa doping Pb yaitu 32,76 %.

---

Synthesis of BPSCCO-2212 superconducting materials with CaCO3 1,0 and 1,10 mole fraction has been done using solid reaction method. Synthesis conducted with calcination for 10 hours at temperature of 800oC and sintering for 20 hours with sintering temperature 830 0C. Variation Pb dopant was performed to determine the effect on the level of purity of the Bi-2212 superconducting phase is formed (volume fraction (Fv), the degree of orientation (P), and impurity (I)). The samples were characterized using XRD (X-Ray Diffraction) and SEM (Scanning Electron Microscopy). XRD analysis results showed variation tended to increase the value of the volume fraction (Fv). Value of the volume fraction (Fv) with Ca 1,0 and Pb = 0, obtained 72,60%, Pb = 0,2 obtained 74,10%, Pb = 0,4 obtained 60,48%, and Pb = 0,6, obtained 61.90%. While the value of highest degree of orientation (P) with Pb = 0,6 obtained 30,62%. Volume fraction (Fv) with Ca = 1,10, and dopant Pb = 0, obtained 56,17%, Pb = 0,2, obtained 78,81%, Pb = 0,4 obtained 63,29%, and Pb = 0,6, obtained 87,31%. Volume Fraction relatively well contained in Ca = 1,10 witg Pb dopant 0,6 is 87,31%. While the degree of orientation (P) is relatively well contained in the sample with Ca = 1,10 without Pb dopant is 32,76%.

Abstrak :
ABSTRACT
One of the attempts performed to improve advanced materials is the application of superconducting wires as base materials for medical application. Magnesium Diboride MgB2 is one of the most promising superconducting wires that can be used to replace superconducting wires Nb. MgB2 superconductor has relatively high critical temperature, however, the main problem in manufacturing MgB2 superconducting wires is the formation of crack at the surface. This crack formation should be avoided, because crack will weaken the superconductivity of a material. There are several ways to avoid the formation of crack, which include the usage of Fe tube. The critical temperature of pure MgB2 is higher than Nb group superconductor, and this critical temperature of MgB2 still can be enhanced by several methods such like doping. Recently, it was found that doping of SiC can make the critical temperature of MgB2 superconductor enhanced. In this research, Powder in Tube PIT were used. These powders were then poured into the Fe tubes with heat treatment under an argon environment. These samples were then characterized by using X Ray Diffraction XRD , Scanning Electron Microscopy SEM and resistivity testing under TC. The results show that nano SiC can be a very high potential doping agent for MgB2 superconducting wires, however, further sample preparation should be considered in manufacturing MgB2 wires. This is true since the unexpected phases such like MgO and Mg2Si exist in the phase. Applying heat treatment to MgB2 can causes instability in MgB2, and thus having all sample prepared under vacuum is recommended. There is also a chance for the boron inside the MgB2 can also doped inside the SiC, especially for nano SiC which have high surface area. Hence, liquid phase sintering would likely to be recommended, due to dissolving of boron into molten magnesium.

---

ABSTRACT
Salah satu upaya yang dapat dilakukan untuk mengembangan material maju adalah penggunaan kawat superkonduktor sebagai material dasar untuk banyak aplikasi di dunia kedokteran. Magnesium diborida MgB2 adalah salah satu kawat superkonduktor yang memiliki potensi besar untuk dipakai sebagai pengganti kawat superkonduktor tipe Nb. Superkonduktor MgB2 memiliki temperatur kritis yang relative tinggi high temperature superconductor, HTS . Masalah yang timbul dalam proses pembuatan kawat superkonduktor MgB2 adalah terbentuknya retak pada permukaan. Pembentukan retak permukaan ini harus dicegah karena akanmenggangu nilai superkonduktifitasnya. Beberapa upaya telah dilakukan untuk mencegah terbentuknya retak permukaan, antara lain penggunaan Fe tube. Meskipun temperatur kritis dari MgB2 sudah lebih tinggi dari superkonduktor tipe Nb, namun ternyata temperatur kritis dari MgB2 masih dapat ditingkatkan, diantara lain menggunakan dopan. Dalam penelitian ini, dopan nano-SiC digunakan untuk meningkatkan temperatur kritis dari MgB2. Dalam penelitian ini, metoda in-situ Powder in Tube PIT digunakan untuk membuat kawat superkonduktor. Proses ini dilanjutkan dengan proses perlakuan panas pada lingkungan gas Argon. Setelah kawat superkonduktor dibuat, akan dilakukan analisis karakterisasinya dengan memakai XRD, SEM dan pengukuran resistivity untuk mengetahui sifat superkonduktivitas kawat tersebut. Untuk hasilnya, ditemukan beberapa senyawa yang tidak diinginkan seperti MgO, Mg2Si dan Si whiskers. Ini disebabkan karena berbagai faktor seperti kurangnya panas ataupun keadaan lingkungan tidak vakum.

Abstrak :
ABSTRAK Sintesis material Fe(Se,Te) dilakukan dengan metode reaksi padatan dengan berbagai variasi komposisi. Sampel yang mengandung serbuk dengan kemurnian tinggi, Fe 99,99%, Se 99,99%, Te 99,99% dipreparasi di dalam glove box dan dimasukkan ke dalam vial high energy milling dan di milling menggunakan shaker mill selama 2 jam dan disintering pada suhu 773 K selama 6 jam. Karakterisasi X-ray Diffractometer (XRD) dilakukan untuk mengetahui struktur kristal dan fasa yang terbentuk dan morfologi permukaan dari material di karakterisasi menggunakan Scanning Electron Microscope (SEM-EDX). Nilai resistansi dari sampel dikarakterisasi dengan menggunakan Cryogenic Oxford Instrument TeslatronTMCF dengan four point probe method. Hasil karakterisasi XRD didapatkan sampel A memiliki fasa FeSe dengan space group P4/nmm dan morfologi permukaan sampel serupa dengan literatur. Sampel B merupakan fasa FeTe dengan space group P4/nmm. Sampel C tidak terbentuk fasa superkonduktor. Sampel D memiliki fasa FeSe. Dari analisa kuantitatif dengan EDX sampel A mengandung Fe 34,27 at% dan Se 17,41 at%. Sampel B mengandung Fe 22,99 at% dan Te 19,18 at%. Sampel C mengandung Fe 13,29 at%, Se 24,33 at%, dan Te 3,87 at%. Sampel D mengandung Fe 40,87 at%, Se 21,21 at% dan Te 37,91 at%. Dari hasil uji resistansi diketahui bahwa sampel A dan B menunjukkan karakteristik dari superkonduktor apabila dilihat dari grafik dibandingkan dengan literatur. Sedangkan sampel C menunjukkan sifat semikonduktor. Untuk sampel D menunjukkan karakteristik superkonduktor dengan nilai Tc onset 13,5K, walaupun belum mencapai Tc zero.

---

ABSTRACT Synthesis material Fe (Se,Te) is performed by solid state reaction method with a variety of compositions. Samples containing powder with high purity, 99.99% Fe, 99.99% Se, Te 99.99% was prepared in the glove box and put in a vial of high energy milling and milled by a shaker mill for 2 hours and sintered at a temperature of 773 K for 6 hours. X-ray Diffractometer (XRD) Characterization was conducted to determine the crystal structure and phase are formed and the surface morphology of the material identified using the Scanning Electron Microscope (SEM-EDX). The resistance value of the samples were characterized using Oxford Instruments Cryogenic TeslatronTMCF with a four-point probe method. XRD characterization results obtained sample A has FeSe phase with space group P4/nmm and the surface morphology of the sample similar to the literature. The sample B is a FeTe phase with space group P4/nmm. Sample C did not form the superconducting phase and Sample D has FeSe phase. The quantitative analysis by EDX informed that sample A contains 34.27 at% Fe and 17.41 at% Se. Sample B contains 22.99 at% Fe and 19.18 at% Te. Sample C contains 13.29 at% Fe, 24.33 at% Se, and 3.87 at% Te. Sample D contains 40.87 at% Fe, 21.21 at% Se and 37.91 at% Te. From the test results is known that the resistance of the sample A and B showed the characteristics of superconductors when seen from the graph compared with the literature. While the sample C showed semiconducting properties. For sample D showed superconductor characteristics with values of Tc onset 13,5K, although not yet reached the Tc Zero.