Abstrak :
Telah dilakukan preparasi alloy magnet FeSi dengan variasi Si = 1, 2, 3 dan 4 at % menggunakan metode arc melting. Alloy tersebut kemudian di anil pada temperatur 800 C selama 1 jam. XRD dan fotomikro digunakan untuk meneliti struktur mikro seperti fase, parameter kisi, ukuran, distribusi dan batas butir. Analisis struktur mikro menunjukkan terjadinya fase tunggal a-Fe baik pada kondisi As cast maupun kondisi annealed. Proses anil menyebabkan pertumbuhan ukuran butir dan kristalisasi serta difusi atom-atom Si pada kristal a-Fe. Karekterisasi listrik menggunakan RLC meter menunjukkan bahwa rangkaian ekivalen alloy FeSi adalah rangkaian RL yang tersusun secara seri. Bertambahnya %Si dalam alloy FeSi baik dalam kondisi As cast dan kondisi annealed cenderung meningkatkan nilai resistivitas dan induktansi listrik. Proses anil juga menyebabkan nilai resistivitas dan induktansi listrik meningkat.

---

Preparation of FeSi magnetic alloy with composition of Si = 1, 2, 3 and 4 at% has been done using arc melting technique under Ar atmosphere. These alloy was annelead at 800 C for 1 hour. XRD and metallography was used to investigate the existance of phase, lattice parameter, size, boundary and distribution of grains. Microstructural analysis of as-cast and annealed samples show that these alloys consist of single phase a-Fe. Heat treatment of these alloys cause grain growth, crystalization and diffusion of Si atoms in a-Fe crystals. Electrical characterization by RLC meter indicates RL series circuit as equivalent circuit. Increasing %Si in FeSi alloy both in as-cast and annealed state tend to increase the values of electrical resistivity and inductance. These values also increase due to annealing process.

Abstrak :
Untuk meningkatkan kemampuan baterai sekunder, pemahaman mengenai bahan elektroda dan elektrolit harus ditingkatkan. Bahan elektroda negatif yang banyak digunakan adalah grafit, sedangkan elektroda positif yang banyak digunakan adalah LiCoO2. Pada penelitian ini dilakukan pengamatan mikrostruktur LiCoO2 komersial. Pada LiCoO2 diberikan pembebanan( 5, 10 dan 15 GPa), pemanasan (60°C, 150°C, dan 200°C) dan pemanasan secara in situ (25, 60, 70, 75, 80, 90, 100 dan 115°C) yang selanjutnya dilakukan pengujian kristalografi menggunakan teknik difraksi sinar-x. Selanjutnya dilakukan refinement terhadap data hasil difraksi sinar-x menggunakan GSAS-EXPGUI. Dari hasil refinement diperoleh data perubahan parameter kisi, occupancy, dan density. Nilai occupancy, dan density semakin menurun dengan meningkatnya nilai pembebanan dan meningkatnya suhu pemanasan. Pada penelitian ini juga teramati adanya prefered orientation pada bidang (003) dan delithiasi yang ditandai dengan penurunan nilai occupancy Li akibat pembebanan dan pemanasan. ...... In order to increase the secondary battery's ability, the understanding of electrode and electrolit has to be improved. The negative electrode material which is commonly used is grafit, as for the positive electrode, it is LiCoO2. In this research, microstructure LiCoO2 commercial observation will be done. On LiCoO2, imposition ( 5,10 and 15 GPa), heating (60°C, 150°C, and 200°C), and heating with in situ (25, 60, 70, 75, 80, 90, 100 and 115°C) are given, and then crystallography using x-ray diffraction technique is tested. Next, refinement to the data of x-ray diffraction result is done by using GSAS-EXPGUI. The data of grid parameter, occupancy, and density are obtained from the result of refinement. The rate of occupancy and density become lower as the imposition's rate and the heating temperature increase. In this research, there are also prefered orientation on field (003) and delithiasi which are marked with the decreasing of occupancy Li rate due to the imposition and heating.

Abstrak :
Material Bi1-xGdxFeO3 dengan nilai x=0, 0.06, 0.1, 0.2 dibuat melalui metode solgel autocombustion. Material dibuat denganprekursorFe(NO3)3.9H2O powder, Bi(NO3).6H2O powder, Gd(NO3)3.6H2O powder, H2O, dan citric acid (C6H8O7). Material ini di-sintering pada temperatur 750oC selama 3 jam setelah diperoleh gel. Pengaruh dari variasi doping Gd pada material BFO ini menjadi fokus yang akan dipelajari. Kemudian material ini akan dikarakterisasi dengan menggunakan X-Ray Diffraction (XRD), Permagraph, dan SEM Edax. Hasil karakterisasi XRD menunjukkan bahwa terjadi pembentukan dua fasa yang berbeda. Secara umum hasil pengujian Permagrapf pada suhu ruang menunjukkan bahwa material tersebut bersifat diamagnetik yang dikarenakan tingginya intensitas bismuth pada material. ...... Bi1-xGdxFeO3material which is x = 0, 0.06, 0.1, 0.2 is made by the sol-gel method autocombustion. The material is made with the precursors of Fe(NO3)3.9H2O powder, Bi(NO3).6H2O powder, Gd(NO3)3.6H2O powder, H2O, andcitric acid (C6H8O7). Then the material will be sintered in 750° for three hours after the gel has been obtained. Effect of Gd doped BFO with variations of x is the main focus that will be learned. After that, this material will be characterized with X-Ray Diffraction (XRD), Permagraph, and SEM Edax.Result of XRD shows that there?re two differen phase. In general, the result of permagraf testing on room temperature shows that the material is kind of diamagnetic because of the high bismuth intensity on material.

Abstrak :
Telah dilakukan sintesis bahan magnetik La0.67Ca0.33MnO3 (LCMO) serta La0,7(Ba1-xCax)0,3MnO3 x = 0,01; 0.03; 0.05 (LBCMO) dengan metode reaksi padatan untuk kemudian dilihat pengaruhnya terhadap parameter kisi, sifat magnetoresistansi, serta efek magnetokalorik. Karakterisasi XRD menunjukkan bahwa seluruh sampel memiliki fasa tunggal dan pergeseran puncak terdeteksi akibat penambahan doping kalsium. Pengujian resistivitas di bawah medan magnet menunjukkan bahwa resistivitas meningkat dengan bertambahnya doping kalsium. Selain itu penambahan doping kalsium mengakibatkan pergeseran temperatur transisi metal-insulator (Tp) menuju region temperatur yang lebih rendah. Selain itu, penambahan doping kalsium mengakibatkan bervariasinya nilai rasio magnetoresistansi. Studi magnetokalorik dilakukan dengan menggunakan metode Xiong[6]. Kurva magnetokalorik dari sampel tidak menunjukkan trend yang tepat, karena perbedaan jenis bahan yang digunakan pada penelitian ini (polikristal) dengan penelitian referensi (epitaxial thin film). ......Magnetic materials La0.7(Ba1-xCax)0.3MnO3 x = 0.01 - 0.05 (LBCMO) has been syntesized using solid state reaction method in order to find the relations between doping agent Calcium and the perovskite's lattice, magnetoresistance and magnetocaloric effect. A characterization using X-Ray Diffractometer shows that all of the samples have single phase pattern with several peak shifts detected as the influence of increasing the doping content. A resistivity measurement under influence of magnetic field shows that the resistivity increases and the metal - insulator transition temperatur (Tp) shifted into lower temperatur region. In other case, introducing calcium dopant into the main compound LBMO also give the effect of variation in magnetoresistance ratio. Magnetocaloric study was carried by using Xiong's method[6]. Magnetocaloric's curve of the samples shows its inacuraccy in its trend because the sample for this research (polycrystalline) and reference's sample (epitaxial thin film) was different.

Abstrak :
Telah dilakukan penelitian sifat resistansi dan hubungannya dengan efek magnetoresistanpada bahan perovskit La0,67Ba0,33MnO3 (LBMO) dan La0,7(Ba1-xCax)0,3Mn0,975Ni0,025O3 (x=0,01;0,03;0,05). Bahan uji disintesis dengan menggunakan solid state reaction. Variasi temperatur sintering pada LBMO tidak merubah parameter kisi. Sedangkan variasi dopan pada LBCMNiO dapat mengubah parameter kisi. Pengukuran sifat resistivitas dan sifat magnetoresistan bahan menunjukkan hasil yang berbeda. Karakterisasi menggunakan X-ray diffraction menunjukkan bahwa bahan uji memiliki fasa tunggal pada setiap variasi. Dari pengujian resistivitas di bawah pengaruh medan magnet menunjukkan bahwa variasi suhu sinter dan dopan menghasilkan perbedaan sifat resistivitas yang sangat signifikan. Variasi sinter yng lebih besar dan penambahan dopan kalsium dan nikel dengan komposisi lebih banyak dapat menurnkan resistivitas dan menggeser puncak resistiitas ke arah temperatur ruang serta menaikkan rasio magnetoresistansi mencapai -10% di bawah medan magnet 20.000 gauss. Pendekatan magnetokalorik menghasilkan nilai perubahan entropi yang bervariasi pada tiap sampel uji baik LBMO maupun LBCMNiO.

---

A research has been conducted to investigate the resistivity behavior and it?s relation with magneto-resistance effect on perovskite materials which are La0.67Ba0.33MnO3 (LBMO) and La0.7(Ba1-xCax)0.3Mn0,975Ni0,025O3 (x=0.01;0.03;0.05). The samples were synthesized using solid state reaction. The sintering temperature variation on LBMO does not change its lattice parameter and doping variation on LBCMNiO has the lattice parameter. Different result was observed for resistivity and mangneto-resistancy properties of the materials. Characterization using x-ray diffraction showed that the samples have single phase on each variation. The resistivity measurement under the influence of magnetic field showed that the temperature variation of sintering and doping resulted in the significant differences of resistivity property. A higher sintering variation and the higher addition of Calcium & nickel as doping, decreased the resistivity and shifted the peak of resistivity to near room temperature and increased the ratio of magneto-resistance until -10% under magnetic field 20,000 gauss. A magnetocaloric approach resulted varied entropy change for each sample.

Abstrak :
Material Fe murni dengan tingkat kemurnian 99,9% memiliki fasa tunggal dan sistem kristal Body Centered Cubic (BCC) yang kemudian dilakukan penggerusan mekanik (Mechanical Alloying) dan penambahan serbuk SiC untuk membandingkan pengaruh ukuran kristal material dengan sifat magnetiknya. Serbuk SiC digunakan untuk membantu memperkecil ukuran kristal Fe karena nilai kekerasan yang dimiliki SiC dapat membantu menghaluskan atom-atom Fe. Karakterisasi yang dilakukan yaitu X-Ray Diffraction (XRD) dan Permagraf. XRD dilakukan untuk melihat ukuran dari partikel, densitas, dan parameter kisi pada material Fe yang sudah dilakukan penggerusan mekanik dan penambahan SiC sedangkan Permagraf dilakukan untuk melihat sifat magnetik dari ukuran kristal yang semakin kecil. Sifat magnetik suatu material menurun seiring dengan mengecilnya ukuran kristal partikel Fe. ...... Pure iron materials with 99,9% purity have a single phase and Body Centered Cubic (BCC) crystal system then performed mechanical alloying and addition SiC (silicon carbide) powder to compare the effect of crystallite size on magnetic properties of iron. SiC powder used to help reduce size of crystallite of iron because hardness values from SiC can help smooth atoms of iron. Identification study of x-rays and permagraph has been characterized. X-ray Diffraction used to found crystallite size, density, and lattice parameters in iron which performed mechanical alloying and addition SiC and then permagraph used to found magnetic properties from smaller crystallite size. Magnetic properties in material decrease with smaller crystallite size.

Abstrak :
Superkonduktivitas merupakan fenomenologika fisika yang terjadi di suatu material yang ditandai dengan hilangnya resistivitas elektrik seiring dengan suhu lingkungan di turunkan secara ekstrim. Material yang memiliki fase superkonduktor salah satunya ditunjukkan oleh material berbasis kuprat yang mayoritas memiliki suhu kritis fase superkonduktivitas lebih tinggi dibandingkan titik leleh nitrogen cair sebagai pendingin eksternal suhu lingkungan. Material berbasis kuprat dengan suhu kritis tertinggi salah satunya terdapat pada senyawa Bi-Sr-Ca-Cu-O, spesifik pada material Bi2Sr2Ca2Cu3O10 dengan suhu kritis di suhu 110 K. Pengaruh pendopingan terhadap material kuprat berbasis senyawa Bi-Sr-Ca-Cu-O di salah satu unsur terbukti dapat mempengaruhi suhu kritis fasa superkonduktivitasnya. Dengan melakukan doping unsur Cr terhadap Cu yang bertanggung jawab atas eksisnya fasa superkonduktivitas menjadikan material Bi2Sr2Ca2(Cu1-xCrx)3O10 mengalami transisi fasa dari superkonduktor menjadi semikonduktor. Diketahui bahwa suhu transisi setelah mengalami doping Cr ditemui pada material Bi2Sr2Ca2Cu2.4Cr0.6O10 di kisaran 76.03K. Keberadaan Bi8CrO15 terlacak oleh pemetaan XRD yang diduga menjadi alasan dibalik transisi fasa dari superkonduktor menuju semikonduktor dari material Bi2Sr2Ca2(Cu1-xCrx)3O10. Kemunculan dari fasa baru Bi8CrO15 meningkat seiring dengan bertambahnya doping Cr dari material Bi2Sr2Ca2(Cu1-xCrx)3O10. ......Superconductivity is a phenomenological physics phenomenon that occurs in a material characterized by the complete absence of electrical resistivity as the environmental temperature is lowered to an extreme level. Materials exhibiting superconducting phases include copper-based compounds that typically have higher critical temperatures for superconductivity compared to the boiling point of liquid nitrogen, which serves as an external coolant at ambient temperatures. One of the copper-based compound materials with the highest critical temperature is the Bi-Sr-Ca-Cu-O compound, specifically the Bi2Sr2Ca2Cu3O10 material with a critical temperature of 110 K. The doping effect on copper-based materials such as Bi-Sr-Ca-Cu-O has been proven to influence the critical temperature of the superconducting phase. By doping the copper element with chromium (Cr), which is responsible for the existence of the superconducting phase, the material Bi2Sr2Ca2(Cu1-xCrx)3O10 undergoes a phase transition from superconductor to semiconductor. It is known that the transition temperature after chromium doping is found in the range of 76.03 K for the material Bi2Sr2Ca2Cu2.4Cr0.6O10. The existence of Bi8CrO15 is traced by XRD mapping which is suspected to be the reason behind the phase transition from superconductor to semiconductor from Bi2Sr2Ca2(Cu1-xCrx)3O10 material. The appearance of the new phase Bi8CrO15 increases with increasing Cr doping of the Bi2Sr2Ca2(Cu1-xCrx)3O10 material.

Abstrak :
Pengaruh variasi persen berat Bi di dalam sistem material Sn-Cu-Bi dan pemberian tekanan pada material solder SnCu terhadap parameter kisi dan ukuran kristal masing-masing sampel material telah diteliti dalam penelitian ini. Material Sn-Cu-Bi yang digunakan memiliki 5 komposisi berbeda dengan variasi persen berat Bi antara 1.2 % hingga 12%. Material SnCu yang digunakan memiliki komposisi 99.3Sn-0.7Cu kemudian diberikan variasi tekanan 5-15ton. Semua material yang digunakan dipreparasi dengan metode solid solution dengan teknik peleburan. Karakterisasi XRD digunakan untuk melihat sifat struktural, fasa yang terbentuk, ukuran kristal serta regangan mikro masing-masing sampel tiap material. Untuk material Sn-Cu-Bi, hasil refinement data XRD menggunakan metode Le Bail menunjukan bahwa pada komposisi Sn-Cu-Bi dengan persen berat Bi kurang dari 3% membentuk suatu paduan dengan satu fasa Sn. Untuk persen berat Bi lebih dari 6% campuran Sn-Cu-Bi membentuk campuran yang memiliki 2 fasa yaitu fasa Sn dan Bi. Parameter kisi dan ukuran kristal pada sistem material Sn-Cu-Bi berubah seiring dengan bertambahnya persen berat Bi dalam campuran. Untuk material paduan SnCu, pemberian tekanan pada material tersebut memberikan pengaruh pada hasil data XRD tiap-tiap material. Hasil XRD menunjukan penambahan tekanan memberikan pengaruh pada pergeseran puncak difraksi dan pelebaran puncak difraksi. Gambaran paling jelas terlihat pada puncak difraksi bidang 112. Pelebaran dan pergeseran puncak difraksi itu menunjukan pengaruh pada ukuran dan regangan mikro kristal. ......In this research, efffects of weight percent of Bi (Bismuth) variations and various pressure addition on the lattice parameter and crystallite size of Sn-Cu-Bi and Sn-Cu material system was investigated. Sn-Cu-Bi alloys and Sn-Cu alloys were manufactured using fusion solid solution method with five various composition SnCuBi and pressure addition about 5-15 ton on Sn-Cu alloy. XRD characterization was used to observe the structural properties, type of phase, crystallite size and microstrain. For material Sn-Cu-Bi, refinement XRD data pattern result using Le Bail method shown that material SnCuBi that consist weight percent Bi lower than 3%, formed an alloy with single phase, Sn. For material SnCuBi that consist weight percent Bi upper than 6.5%, mix material that has 2 phase, Sn and Bi phase was formed. Based on refinement XRD data pattern result, lattice parameter Changde along with the change of Bi concentration. The crystallite size and microstrain would change when the Bi composition increased. For SnCu alloys,the various pressure that was applied to materials could change the XRD pattern. The XRD?s result shown that diffraction?s peaks pattern become broader. The clearest figure about broadener peaks pattern was shown by diffraction?s peak plane 112 (Sn phase).