Abstrak :
Preparasi tekstil termodifikasi TiO2 dengan mengikuti prosedur sol gel dan pad-dry curetelah berhasil dilakukan.Kinerja katalis diuji dengan eliminasi metilen blue dan desinfeksi E.Coli. Sifat mekanik dipelajari dengan uji tarik, uji elongasi dan uji kerontokan. Sementara studi katalis pada substrat dipelajari dari karakterisasi SEM, EDS, FTIR DRS dan XRD.Post-treatment hidrotermal menghasilkan katalis yang tersebar merata pada tekstil namun lebih rentan terlepas, sementara post-treatment furnace katalisnya terpusat di beberapa titik namun katalis yang lebih sulit terlepas. Kekuatan mekanik tensil dan elongasi terbaik dicapai oleh TiO2-5-F-Si dengan kekuatan tensil 67,10 ± 0,21 MPa dan elongasi 111,0 ± 29,7 %. Uji eliminasi metilen blue menunjukkan TiO2-12-H-Si setelah 5 jam adalah 79,8% dibandingkan dengan TiO2-25-H-Si yang dapat mengeliminasi 1,05 kali lipat namun dengan bahan baku 2 kalinya. Pada desinfeksi E.Coli,TiO2-12-H-Si mendesinfeksi E.Coli sebesar 67,4% setelah 30 menit dibandingkan dengan TiO2-25-H-Si yang mendesinfeksi 1,14 kali lipat namun dengan bahan baku 2 kalinya. ......Preparation using sol gel and pad dry cure method had been done. Mechanical study observed are tensile test, elongation test and disattachement test. While catalyst on substrate observed using SEM, EDS, FTIR, DRS and XRD characterization. Hydrothermal post treatment results a diverge catalyst distribution but with tendency to be disattached from substrate, while furnace post treatment results a converge catalyst distribution but with low tendency to be disattached from substrate. Best tensile and elongation result achieved by TiO2-5-F-Si with tensile strength 67,10 ± 0,21 MPa and elongation 111,0 ± 29,7 %. From methylene blue elimination, TiO2-12-H-Si showed 79,8% elimination, compared to TiO2-25-H-Si which is 1,05 times better than TiO2-12-H-Si but using twice the material used. On E.Coli desinfection, TiO2-12-H-Si able to desinfect 67,4% E.Coli after 30 minutes, compared to TiO2-25-H-Si which is 1,14 times better than TiO2-12-H-Si but using twice the material used.

Abstrak :
ABSTRAK Demam chikungunya adalah penyakit yang disebabkan oleh virus chikungunya (CHIKV) yang dapat menginfeksi manusia melalui gigitan nyamuk. CHIKV ditularkan melalui nyamuk Aedes aegypti dan Aedes albopictus. CHIKV juga merupakan penyakit arbovirus yang penting karena morbiditas yang tinggi. Kejadian Luar Biasa (KLB) infeksi CHIKV pertama kali dilaporkan pada tahun 1973 di Kalimantan Timur dan DKI Jakarta. Dengan besarnya frekuensi KLB dan tingginya prevalensi infeksi CHIKV di Indonesia maka diperlukan studi genotipe CHIKV. Faktor virus seperti variasi genotipe diyakini berperan dalam menentukan derajat keparahan penyakit. Pada penelitian ini menggunakan sampel yang tersimpan di Badan Litbangkes Jakarta sebagai Pusat Rujukan pemeriksaan infeksi CHIKV. Variasi genetik CHIKV dari 19 sampel dari 8 Propinsi di Indonesia tahun 2012?2014 dikerjakan dengan melakukan amplifikasi dan sekuensing gen E1 dan Capsid. Analisis filogenetik menunjukkan bahwa semua sampel pada penelitian adalah genotipe Asian. Homologi nukleotida dan asam amino gen E1 ditemukan berkisar 97,8%-100% dan 95,6%-100% untuk asam aminonya. Analisis epitop sel B dan sel T pada gen capsid memperlihatkan tidak adanya perbedaan antara CH12_069 dengan genotipe CHIKV di dunia. Epitop sel B di gen E1 ada beberapa perbedaan antara CH12_069 dengan genotipe Asian yaitu K196R dan L203I, sedangkan epitop sel T pada gen E1 tidak ditemukan perubahan asam amino.

---

ABSTRACT Chikungunya fever is a disease caused by the chikungunya virus (CHIKV) that can infect humans through mosquito bites. CHIKV is transmitted by Aedes aegypti and Aedes albopictus mosquitos. CHIKV is also an important arbovirus disease because of the high morbidity. The outbreaks of CHIKV infection was first reported in 1973 in East Kalimantan and Jakarta. With the magnitude of the frequency of outbreaks and the high prevalence of CHIKV infection in Indonesia, CHIKV genotype study is needed. Viral factor such as genotype variation is suggested play a role in determining the degree of severity of the disease. In this study, we used the stored samples in National Institute of Health Research and Development Jakarta as a Reference Laboratory Center of CHIKV infection. Genetic variation CHIKV of 19 samples from 8 provinces in Indonesia in 2012? 2014 done by performing amplification and sequencing of genes E1 and capsids. Phylogenetic analysis showed that all samples in this study were Asian genotype. E1 gene nucleotide homology was found ranging from 97.8%-100% and 95.6%- 100% for the amino acid. Analysis of B cell epitops and T cells epitop in the capsid gene showed no differences between CH12_069 with CHIKV genotype in the world. B cells epitops in E1 gene were showed no specific distinction between CH12_069 among CHIKV strains all over the world. B cell epitops in E1 gene there were some differences between CH12_069 with the Asian genotype such as K196R and L203I, whereas T cell epitops in E1 gene not found amino acid changes.

Abstrak :
Sintesa dan karakteristisasi Rasio magneto-resistansi bahan LaMnO3 telah berhasil dilakukan. Bahan LaMnO3 yang dihasilkan memiliki fasa tunggal dengan struktur kristal orthorhombic, space group Pnma (I-62) dan parameter kisi a =5,44145 ± 0.00093 A, b = 7,70625 ± 0.00074 A dan c = 5.53700 ± 0,00098 A, dengan sudut pembentuk kristal α=β=γ=90°, volume satu unit sel V = 232,184 ± 0,069 A3, kerapatan satu unit sel ρ = 6,005833 g/cm3. Kualitas fasa yang dihasilkan cukup baik dengan komposisi unsur La:Mn:O = 22,40% : 19,73% : 59,80%. Dari pengamatan SEM, morfologi permukaan bahan menunjukkan partikelnya berbentuk buat-bulat hampir homogen, dengan distribusi ukuran partikel sebesar 1000 - 3000 nm. Rasio magneto-resistansi terbaik yang dihasilkan adalah 33,30% pada arus 10 mA. Faktor-faktor yang memberi kontribusi keberhasilan penelitian ini antara lain proses milling, kompaksi dan pemanasan ulang, sehingga diperoleh homogenitas campuran, porositas yang minimal dalam pembentukan fasa, pengikatan oksigen, sehingga diperoleh fasa LaMnO3 yang lebih sempurna. Dalam penelitian ini variasi kompaksi dan pemanasan ulang merupakan faktor ekstrinsik yang mempermudah orientasi untuk memperbesar domain magnetik.

---

The synthesis and characterization of magnetoresistance ratio on the material compound of LaMnO3 was successfully carried out. It yielded single phase with orthorombic crystal structure, space group Pnma (I-62) and grid parameter of a = 5.44145 ± 0.00093A, b = 7.70625 ± 0.00074 A and c = 5.53700 ± 0.00098 A, in the angle of crystal shaper α=β=γ= 90°, one unit cell volume V = 232.184± 0,09A3, one unit cell density ρ = 6.005833 g/cm3 The phase quality yielded is sufficiently good in the element composition La : Mn: O = 22.40%: 19.73% : 59.80% respectively. Based on the observation of SEM that the morphologically material indicated a round particles are almost homogeneous, in the distribution of particle size is 1000 - 3000 nm. The best magneto-resistance to be yielded is 33,30% with current I = 10 mA. The factors contributing to successful of this research among other milling process, compact and re-heating, so that it was obtained a compound was homogeneous, a minimal porosities, phase forming, oxygen binding, and thus it was obtained phase of LaMnO3 is more perfected. In this research, that compact variation and reheat are extrinsic factor that is may easily orientation to enlarge magnetic domain.

Abstrak :
Mikroalga Spirulina platensis rnerupakan salah satu sumber asam lemak tidakjenuh majemuk atau Poly Unsaturated Fatty Acid (PUFA), yaitu asam linoleat dan asam y-linolenat. Produksi PUFA ini berkaitan dengan aktivitas enzim desaturase yang terdapat di dalam sel S. platensis. Desaturase merupakan enzim yang dapat mengkatalisis reaksi pembentukan ikatan rangkap pada rantai karbon asam lemak. Enzim ini dapat dimanfaatkan pada biokonversi secara in vitro untuk meningkatkan ketidakjenuhan asam lemak. Penelitian ini bertujuan untuk mengisolasi dan " menentukan aktivitas dan sifat enzim tersebut sebagai biokatalisator pada reaksi pembentukan ikatan rangkap asam lemak minyak sawit. Hasil penelitian menunjukkan bahwa desaturase dapat diisolasi dari S. platensis dan mampu meningkatkan ketidakjenuhan asam lernak minyak sawit. Pengujian karakteristik desaturase menunjukkan bahwa desaturase memiliki aktivitas optimum pada perbandingan substrat-enzim (1 :1), pH 7,5 dan suhu 25°C. logam kofaktor yang bersifat aktifator untuk desaturase adalah Ca2 +, Mn2 +, Cu2: dan Mg2 +, sedangkan sebagai inhibitor adalah Mg2 + (pada konsentrasi diatas 0,5 mM) dan EDTA. Desaturase S. platensis memiliki I periode stabilitas yang singkat, yaitu tiga jam. Analisis kromatografi gas terhadap perubahan komposisi asam lemak minyak sawit sebelum dan setelah desaturasi menunjukkan adanya aktivitas delta-12 desaturase.

Abstrak :
ABSTRAK
Kitinase merupakan enzim yang berguna dalam degradasi kitin dan dapat dimanfaatkan dalam pengolahan limbah perikanan, biokontrol terhadap jamur fitopatogen, biopestisida, dan produksi protein sel tunggal. Penelitian mengenai karakterisasi kitinase kasar dari Trichoderma amazonicum LP3 dilakukan menggunakan substrat koloidal kitin. Penelitian bertujuan untuk mengetahui produksi dan karakterisasi kitinase kasar yang dihasilkan oleh T. amazonicum LP3. Penentuan aktivitas kitinase dilakukan dengan metode kolorimetri dan produk akhir hasil hidrolisis dianalisis berdasarkan metode Reissig. Hasil penelitian menunjukkan aktivitas kitinase dari T. amazonicum LP3 tertinggi pada inkubasi hari kedua sebesar 8,22 U/mL. Karakterisasi kitinase kasar menunjukkan aktivitas optimum pada pH 5, suhu 50°C, dan stabil selama 3 jam kondisi pH 5 dan selama 1 jam kondisi suhu 50°C. Ion logam Ca2+, Co2+, Fe2+, Mg2+, Zn2+, dan EDTA 1 mM bersifat sebagai aktivator, sedangkan ion logam Hg2+ dan Cu2+ bersifat sebagai inhibitor.

---

ABSTRACT
Chitinase enzyme is an effective tool for chitin degradation and can be used in fishery waste management, biocontrol of phytopathogenic fungi, biopesticide, and single cell protein production. A research on the characterization of crude chitinase from Trichoderma amazonicum LP3 has been investigated using colloidal chitin as substrate. This research aims to investigate the production and characterization of crude chitinase from T. amazonicum LP3. Chitinase activity was assayed using the colorimetric method and the end products of the reaction were analyzed by the Reissig method. The highest activity of chitinase (8,22 U/mL) was observed after 2 days incubation. Characterization of crude chitinase showed optimum activity at pH 5, temperature 50°C, stable for 3 hours at pH 5 and 1 hour at 50°C. The activities were increased when treated by Ca2+, Co2+, Fe2+, Mg2+, Zn2+, and EDTA 1 mM, whereas activities were inhibited when treated by Hg2+ dan Cu2+.

Abstrak :
Nanokomposit CeO2/SnO2 telah disintesis melalui proses hidrotermal dan pola difraksi XRD nanokomposit yang dihasilkan masih memuat impuritas selain SnO2 dan CeO2, dan belum menunjukkan terjadinya kristalisasi. Weight loss di 250oC dan 600 oC yang berhubungan dengan hilangnya molekul air dan terjadinya kristalisasi pada nanokomposit diketahui dari hasil pengukuran TGA (Thermal Gravimetric Analysis). Proses kalsinasi terhadap nanokomposit untuk tiga variasi suhu, yaitu 500 oC, 600 oC, dan 700 oC selama 2 jam, menghasilkan pola difrasi XRD (X-Ray Diffraction) dengan hilangnya impuritas dan kristalisasi yang baik. Indentifikasi nanokomposit menggunakan XRF (X-Ray Fluoroscene) menunjukkan elemen Sn dan Ce tetap hadir setelah proses kalsinasi. Kehadiran ikatan oksigen dengan Ce (~460 cm-1) dan Sn (~630 cm-1) diketahui dari pengukuran Raman. Perhitungan celah pita optik nanokomposit dari hasil reflektansi UV-VIS DRS (UV-Visible Diffuse Reflectance Spectroscopy) berada diantara CeO2 dan SnO2, dan tidak menunjukkan perubahan yang besar dengan perlakuan kalsinasi. Sifat permukaan nanokomposit CeO2/SnO2 dengan dan tanpa kalsinasi menunjukkan macropores yang berbentuk slit-shaped pores. Nanokomposit CeO2/SnO2 yang dikalsinasi pada suhu 600 oC menunjukkan kinerja fotokatalitik terbaik untuk cahaya tampak, dengan dosis 0.2 g/L, dan pH 13 dalam mendegradasi MB (Methylene Blue). Bertambahnya waktu rekombinasi elektron-hole dengan penggabungan CeO2 dan SnO2 yang berbeda celah pita optik, yang berkontribusi dalam degradasi maksimum MB, dengan hole sebagai species yang berperan aktif untuk paparan pada cahaya tampak. ......The CeO2/SnO2 nanocomposites have been synthesized through the hydrothermal process and the nanocomposites XRD diffraction pattern produced still contains impurity other than SnO2 and CeO2, and have not shown crystallization. Weight loss at 250 oC and 600 oC which is related to the loss of water molecules and the occurrence of crystallization in nanocomposites is known from the results of TGA (Thermal Gravimetric Analysis) measurements. The process of calcination of nanocomposites for three variations of temperature, namely 500 oC, 600 oC, and 700 oC for 2 hours, produces XRD (X-Ray Diffraction) diffraction patterns with impurity loss and good crystallization. Identification of nanocomposites using XRF (X-Ray Fluoroscene) shows the elements Sn and Ce remain present after the calcination process. The presence of oxygen bonds with Ce (~ 460 cm-1) and Sn (~ 630 cm-1) is known from Raman measurements. Calculation of nanocomposite optical band gap from the results of UV-VIS DRS (UV-Visible Diffuse Reflectance Spectroscopy) is between CeO2 and SnO2, and does not show a large change with calcination treatment. Surface properties of CeO2 / SnO2 nanocomposites with and without calcination showed macropores in the form of slit-shaped pores. CeO2 / SnO2 nanocomposites calcined at 600 oC showed the best photocatalytic performance for visible light, at a dose of 0.2 g / L, and pH 13 in degrading MB (Methylene Blue). Increased electron-hole recombination time by combining CeO2 and SnO2 with different optical band gaps, which contributes to the maximum degradation of MB, with holes as species that play an active role for exposure to visible light.

Abstrak :
Telah dilakukan sintesis dan karakterisasi dielektrik amorf terhadap bahan berbasis barium titanat dengan penambahan unsur Pb. Dalam penelitian ini cuplikan Ba(1_,¢Pb,Ti0, diperoleh melalui metalurgi serbuk dengan bahan dasar BaCO3, PbCO,, dan TiO2 yang merupakan grade reagen dari E-Merck dengan perbandingan stoikidmetri nominal masing-masing 0,1 : 0,9 : 1. Analisis tennal menunjukkan bahwa bahan memiliki titik leleh pada 1350°C dimana temperatur tersebut lebih rendah dari BaTiO, Fasa gelas diperoleh melaiui pemanasan bahan hingga meleleh pada temperatur 1350°C diikuti oleh pendinginan oepat dalam medium nitrogen cair hingga membentuk cairan super dingin_ Difraktogram sinar-X dengan cacah step dan panjang gelombang. A (Cu Ka.)=1,5405 A yang diperoleh pada temperatur kamar, menunjukkan hilangnya seluruh puncak Bragg dan terjadi penggeiembungan cacah latar pada bahan. Kurva distribusi radial hasil pengamatan tanpa melakukan reduksi data diperoieh dengan menggunakan paket program kristallografi GSAS, secara kualitatif menunjukkan keminpan dengan fungsi distribusi radial yang ditunjukkan oleh zat cair sederhana. Pengukuran terhadap besaran konstanta dielelctrik relatif menunjukkan kenaikan yang tinggi pada 12O°C hingga 360°C dan temperatur curie dicapai pada 140°C dimana nilai konstanta dielektdk relatifnya adalah 4,13x10°.' Jangkauan temperatur yang Iebar dengan konstanta dieiektrik tinggi yang diperoleh menunjukkan bahwa sampel cocnk untuk temperatur tinggi dan berfluktuasi pada daerah jangkauan tersebut.

---

Barium titanate based with amorphous dielectric materials with Pb as a substituent atom have been synthesized and characterized. ln this study, Ba(,_,,Pb,,TiO3 were synthesized by using powder metallurgy trom BaCO3, PbCO3 and Ti02, which were reagents from E-Merck with nominal stoichiometric ratio of 0.1 : 0.9 : 1 respectively. Themwal analysis showed that the sample melting point is of 1350°C which is lower than that of BaTiO3. The glassy states was obtained by heating at the melting point temperature of 1350°C followed by quenching in liquid nitrogen media rapidly when the supercooled conditions achieved. The X-ray diffractograms were obtained with step scan and 2. (Cu Ka) =1,5405 A at room temperature showed the Bragg peaks dissapeared completely and the fluctuation of background prohle was occurred. The observed radial distribution function without data reduction were obtained by using of GSAS crystallographic software package which qualitatively showed that the function resembles the radial distribution function belongs to simple fluids. The relative dielectric constant that was measured from room temperature showed that there is a signiticant increasing value starting at 120°C up to 36O°C and the Curie temperature was occurred at 140°C while the value of corresponding relative dielectric constant is of 4,13x105. Broad range of temperature in which high dielectric constant was obtained indicates that the sample is suitables for high and tluctuating temperature in the range.

Abstrak :
Film Ba0,5Sr0,5TiO3 doping Ga2O3 (BGST) telah berhasil dibuat di atas substrat Si(111) dengan proses penumbuhan larutan kimia 1 M larutan BGST [(BaxSr1-xTi1-yGay) O3-y/2] dan dilanjutkan dengan spin coating pada kecepatan putar 3000 rpm selama 30 detik. Karakterisasi yang dilakukan berupa struktur mikro menggunakan XRF, XRD dan SEM serta uji sifat ferroelektrik. Hasil XRF menunjukkan unsur-unsur pembentuk BST telah terdeposit. Sementara hasil XRD pada substrat Si(111) didapatkan nilai parameter kisi untuk BST, BGST (1%, 2% dan 4%) berturut-turut sebesar 3,9469Å, 3,9354Å, 3,8617Å dan 3,7550Å. Adapun bidang hkl yang muncul yaitu (100) untuk sampel BST dan BGST1M1%Si serta bidang (100) dan (110) untuk sampel BGST1M2%Si dan BGST1M4%Si. Hasil analisa SEM menunjukkan bahwa permukaan film BST maupun BGST dengan variasi doping masih heterogen. Hasil uji histerisis menunjukkan adanya hubungan yang linear antara nilai polarisasi dengan nilai medan listrik yang diberikan. Nilai polarisasi spontan memiliki hubungan yang berbanding terbalik dengan nilai parameter kisi suatu bahan. Polarisasi spontan hasil perhitungan berdasarkan posisi atom diperoleh untuk BGST1M1%Si, BGST1M2%Si dan BGST1M4%Si berturut-turut 51,6550(µC/ cm2 ) , (µC/ cm2 ) dan 56,7375 (µC/ cm2 ). A film of Ga2O3 doped Ba0.5Sr0.5TiO3 (BGST) is successfully make on silicon substrate (111) using chemical solution deposition process 1M BGST (BaxSr1-xTi1-yGay)O3-y/2 solution followed by spin coating process with spin velocity 3000 rpm for 30 second. Characterizations conducted are micro structure characterization using XRF, XRD and SEM and ferroelectric property. The result of XRF shows that the BST forming elements are already deposited. Where as the result of XRD on silicon substrate (111) shows the lattice parameter for BST, BGST (1%, 2% and 4%) are respectively as follow: 3.9469 Å , 3.9354 Å , 3.8617 Å and 3.7550 Å . In addition, the XRD result also show that the hkl plane observed is (100) plane for BST sample and BGST1M1%Si, and (100) and (110) planes for BGST1M2%Si and BGST1M4%Si. The result of SEM shows that the films surface of BST as well as BGST with various doping concentration are still heterogeneous. The result of hysterisis test shows the existence of directly proportional relationship between the polarization value and electric field value. The spontaneous polarization value is conversely proportional to the lattice parameter value of material. The spontaneous polarization value obtained from calculation based on atomic position for BGST1M1%Si, BGST1M2%Si and BGST1m4%Si are respectively as follow: 51.6550, 53.6454 and 56.7375 (µC/ cm2 ).