Abstrak :
Penelitian ini bertujuan memperoleh informasi karakteristik thin film GaSb dengan sistem penumbuhan evaporasi thermal. Bahan yang digunakan adalah ingot GaSb dengan sistem penumbuhan pemanasan vertikal pada bagian ujungnya. Penumbuhan thin film GaSb secara evaporasi thermal menggunakan evaporator Univex 450 pada Laboratorium Fisika Universitas Indonesia. Karakterisasi thin film GaSb menggunakan difraksi sinar-X (dirraktometer Cu-Ka dan Co-Ka) dan four point probe (Veeco EPP-lOO) dilakukan pada Laboratorium Fisika Universitas Indonesia dan Lembaga Sumber Daya dan Energi, pada bulan Agustus I996 - Maret I997. Hasil analisis thin film GaSb substrat kronig pada temperatur pemanasan substrat 200 °C menunjukkan karakteristik yang sama dengan referensi dengan konstanta kisi (a) 6,24 A, volume 197,79 A3, sistem kristal kubik dengan struktur kubik pusat muka pada orientasi bidang (111, 220, 333).

---

This research is intended to obtain information regarding characteristic of GaSb thin film from thermally evaporated growth system. The material use consist of GaSb ingot growth vertically by thermally evaporated. The evaporator used is univer 450, and the characterization is carried out using X - ray difractometer and veeco four points probe. The thin film analysis indicated that GaSb at temperature of 200°C have similar characteristics with the reference, having lattice constant of 6.24 A and volume 197.79 A and have a structure of FCC oriented at (III), (220) and (333) crystal planes.

Abstrak :
ABSTRAK
Etanol dapat dipisahkan dengan proses pervaporasi menggunakan membran-PV (pervaporasi). Material membran TFC (thin film composite) yang digunakan sebagai metode pemisahan campuran etanol-air dengan proses pervaporasi yang lebih khusus dengan mempertimbangkan nilai keekonomisannya. Penelitian dibagi menjadi dua tahap penelitian, yaitu penelitian pendahuluan dan penelitian utama. Penelitian pendahuluan dilakukan dengan memvariasikan kondisi operasi pada 35, 39 dan 44oC dan tekanan pada sisi permeat sebesar 660, 510, dan 260 mmHga. Metode pervaporasi diaplikasikan pada campuran etanol-air dengan menggunakan kondisi optimum pada suhu 39oC dan tekanan 510 mmHga. Sedangkan untuk variasi konsentrasi etanol yang digunakan pada penelitian utama senilai 10, 30, 50, 70 %. Dari hasil penelitian yang dilakukan, diperoleh pada kondisi operasi optimum didapatkan penurunan konsentrasi permeat paling besar senilai 14,4% pada konsentrasi etanol awal 70%, dengan nilai selektifitas 1,575 dan nilai fluks permeat sebesar 0,0160 kg/m2.min. Hasil penelitian tersebut menunjukan bahwa dengan menggunakan membran Thin Film Composite (TFC) untuk proses pemurnian campuran etanol-air dengan metode pervaporasi perlu dilakukan modifikasi lebih lanjut.

---

ABSTRACT
Ethanol can be separated by pervaporation process using a membrane-PV (pervaporation). TFC membrane material (thin film composite) was used as a method of separation of ethanol-water mixture by pervaporation process more specifically taking into account the economic value. The study was divided into two phases of research, the preliminary research and primary research. Preliminary research carried out by varying the operating conditions at 35, 39 and 44oC and pressure on the permeate side at 660, 510, and 260 mmHga. The method was applied to the pervaporation of ethanol-water mixture by using the optimum conditions at a temperature of 39oC and a pressure of 510 mmHga. As for the variation of the concentration of ethanol used in the main study worth 10, 30, 50, 70%. From the results of research conducted, obtained at the optimum operating conditions found in decreased concentrations of the permeate most worth 14.4% in the initial ethanol concentration of 70%, with selectivity value of 1.575 and permeate flux values 0.0160 kg/m2.min. The results showed that by using a membrane Thin Film Composite (TFC) for the purification of ethanol-water mixtures by pervaporation method needs to be done further modifications.

Abstrak :
Sintesis semikonduktor Cu2ZnSnS4 (CZTS) sebagai absorber sel surya lapis tipis telah dilakukan dengan metode ekonomis dan ramah terhadap lingkungan dengan pelarut etanol. Prekursor CZTS diperoleh dari melarutkan garam logam berupa CuCl2, ZnCl2, dan SnCl4 dengan etanol, kemudian larutan tersebut ditambahkan 2-mercaptopropionic acid sebagai stabilizer. Penambahan thiourea dengan konsentrasi 4,4M, 5,4M, dan 6,4M dilakukan setelah memasukkan 2-mercaptopropionic acid yang dilanjutkan dengan deposisi larutan di atas kaca menggunakan metode spin coating. Sifat optik, morfologi, dan komposisi semikonduktor CZTS dibahas secara detil. Dengan konsentrasi sulfur yang bertambah akan memberikan hasil deposisi lapisan yang mengalami penurunan sifat optik. Nilai energi celah pita yang dihasilkan sebesar 1,4eV, 1,5eV, dan 1,52eV untuk konsentrasi 4,4M, 5,4M, dan 6,4M secara berurutan.

---

Synthesis Cu2ZnSnS4 (CZTS) thin film absorber layer semiconductor has been made by cost-effective and environmentally friendly method using ethanol solvent. The precursor of CZTS was obtained from dissolving metal salts of CuCl2, ZnCl2, and SnCl4 with ethanol, then the solution was added 2-mercaptopropionic acid as stabilizer. The addition of thiourea with concentration 4,4M, 5,4M, and 6,4M was performed after adding 2-mercaptopropionic acid followed by deposition of the solution on the glass using spin coating method. The characteristic of optic, morphology, and composition of CZTS semiconductor are to be described in-depth. With increasing the sulfur concentration will decreased optical properties of deposition coating result. The constants of band gap that are produced are 1,4eV, 1,5eV, and 1,52eV for 4,4M, 5,4M, and 6,4M respectively.