Abstrak :
Studi numerik yang dihasilkan oleh perangkat lunak SAP2000 untuk mengamati perilaku sambungan spun pile ke pile cap sesuai dengan praktik umum standar Indonesia dengan penguatan selubung baja tambahan. Analisis push over dilakukan dalam penelitian dengan pendekatan pemuatan monotonik. Parameter dalam pengujian adalah ketebalan jaket baja dan adanya perekat antara baja dan permukaan beton. Jaket baja yang dibangun mengikuti metode baru menunjukkan hasil yang baik untuk meningkatkan kekuatan tekan dan daktilitas tiang berselimut baja sehubungan dengan tiang pancang. Selubung baja yang lebih tebal menunjukkan peningkatan kekuatan tekan, dan perekat antara baja dan permukaan beton mengurangi efek pengekangan dari selubung baja. ......Numerical study was generated by SAP2000 software to observe the behaviour of spun pile to pile cap connection according to the common practice of Indonesia standard with additional steel jacketing strengthening. Push over analysis were conducted in the research with monotonic loading approach. The parameters in the test were the steel jacket's thickness and the existence of adhesive between steel and concrete surface. The steel jacket built following the new method showed good results of increasing the compressive strength and ductility of the jacketed pile with respect to the plain pile. The thicker steel jackets showed that the increased compressive strength, and the adhesive between steel and concrete surface reduced the confining effect of the steel jackets.

Abstrak :
Pada penelitian ini pengaruh defonnasi regangan terhadap anil rekristalisasi diteliti melalui percobaan eksperimental laboratorium, Pada percobaan, bahan SPCC dideformasi 17 % sampai 35 % kemudian dilakukan proses anil dengan temperatur SOO °C, 550 °C, 600 "C, dan 650 °C. Waktu tahan pemanasan dibuat konstan selama 1 jam. Pengujian kekerasan dan metalografi dilakukan untuk mengetahui rentang temperatur yang sesuai terjadinya rekristalisasi. Untuk deformasi regangan yang besar (dalam penelitian ini 51% sampai 85 %) memeiliki rentang temperatur rekristalisasi 550 “C sampai 600 °C, sedangkan untuk deformasi regangan yang kecil (dalam penelitian ini 17 % sampai 34 %) memiliki temperatur rekristalisasi lebih tinggi dari 600 °C. Dimana kekerasan pada deformasi regangan 85 % penurunannya sangat drastis yakni dari 129,29 Hv menjadi 79,52 Hv dan pada deformasi regangan 17 % perbedaanya tidak besar yakni dari 95,13 Hv menjadi 90,50 Hv. Hasil menunjukkan pengaruh temperatur anil tekristalisasi terhadap baja SPCC akan menurunkan kekerasan untuk semua deformasi. Sedangkan temperatur untuk terjadinya rekristalisasi berbeda, dimana untuk defomasi yang kecil temperatur rekristalisasi semakin besar tetapi untuk deformasi yang besar temperatur rekristaiisasi semakin kecil. Hal ini dibuktikan dengan ukuran butir yang semakin besar atau bilangan besar butir (G) semakin kecil disamping kekerasannya menurun. Oleh karena itu dapat disimpulkan dengan meningkatnya parameter deformasi akan menurunkan temperatur rekristalisasi.

Abstrak :
Baja meupakan material yang penting yang digunakan dalam berbagai sektor kebutuhan. Rekayasa struktur baja merupakan salah satu langkah yang dapat dilakukan agar mendapatkan sifat baja yang sesuai. Perlakuan panas dan pendinginan cepat menggunakan nanofluida merupakan salah satu metode rekayasa struktur yang dapat dilakukan untuk mengeraskan baja. Pada penlitian ini membahas penggunaan nano fluida sebagai media pendingin pada perlakuan baja S45C. Fluida yang digunakan disintesis dengan mendispersikan surfaktan polyethylene glycol dengan variabel konsentrasi 0; 3; 5; dan 7% v/v dan partikel hasil daur ulang limbah PCB dengan variabel konsentrasi 0; 0,1; 0,3; 0,5% w/v didalam air distilasi,. Proses sintesis partikel PCB meliputi crushing, leaching dengan HCL 1M, pirolisis pada suhu 500oC, dan ball milling dengan total durasi 20 jam. Hasil pengujian Particle Size Analyzer (PSA) pada partikel menunjukkan adanya peningkatan ukuran partikel dari 268 nm menjadi 1035 nm saat di milling selama 10 jam kemudian turun menjadi 572 nm saat di milling selama 20 jam. Ukuran yang diperoleh tidak mencapai ukuran nano (1-100 nm) sehingga partikel tergolong kedalam partikel mikron. Untuk mengevaluasi pengaruh konsentrasi surfaktan polyethylene glycol dan partikel PCB pada fluida, dilakukan pemanasan Baja S45C pada suhu 900oC yang kemudian didinginkan cepat menggunakan fluida partikel mikron. Hasil yang diperoleh dari perlakuan pada baja meliputi kurva pendinginan, nilai kekerasan HRC dan foto mikrostruktur. Kurva pendinginan yang diperoleh memperkirakan fasa akhir yang didapatkan baja adalah ferrite, pearlite, bainite dan martensite. Adapun struktur mikro yang dihasilkan oleh baja menunjukan fasa pearlite, bainite, martensite dengan nilai kekerasan diatas 50 HRC serta kekerasan tertinggi mencapai 56,3 HRC ......Steel is classified as an important materials that used in various sector of applications. Engineering the microstructure of steels is an important step that can be used to obtain the desired properties of steel. Quenching, especially with nanofluids is one of the great options to alter the microstructure of steel, specifically through steel hardening treatments. In this study, the use of nanofluid as steel quenchant id discussed. Synthesized fluid obtained by dispersing polyethylene glycol as a surfactant with 4 variation of concentration (0; 3; 5; 7% v/v) and PCB recycled particle with also 4 concentration variation (0; 0.1; 0.3; 0.5% w/v) to the distilled water. Recycling / synthesis process of PCB particle include crushing, leaching with 1 Molar Hydrochloric Acid, pyrolysis at 500oC, and ball milling for up to 20 hours. Results obtained from the particle size analyser (PSA) indicate an increase in particle size from 268 nm to 1035 nm within 10 hours milling and reduced to 572 nm when milled for 20 hours. Particle retrieved after the recycling process classified as micron sized particle because the final size doesn’t meet the criteria of nanoparticles (1-100 nm). To evaluate the effects of polyethylene glycol and PCB based particle concentration on the dispersed fluids, a hardening treatment is conducted by heating S45C steels to 900oC for 1 hour then quenched with the dispersed fluid. Information that can be obtained from the process are the cooling curves, rockwell hardness, and microstructure of steels. Obtained cooling curves predict the final phase that may be present at steels are ferrite, pearlite, bainite, martensite. The microstructure of steels after quenching in general consist of pearlite, bainite, martensite. Meanwhile, overall steels rockwell hardness obtained after quenching is above 50 HRC with maximum value of 56,3 HRC.

Abstrak :
Peningkatan sifat mekanis baja perkakas untuk pengerjaan panas telah menjadi perhatian dunia industri sebagai prioritas untuk menghasilkan produk dengan kualitas dan efektifitas produksi terbaik. Penelitian ini dilakukan dengan membandingkan sifat mekanis dari proses High Impact Treatment (HIT) yang mengalami pendinginan dengan media oli pada temperatur 180oC dan pendinginan oleh angin dan sifat mekanis yang diperoleh dengan menggunakan proses High speed quenching. Hasil penelitian ini digambarkan dalam grafik laju pendinginan, harga impak dan nilai kekerasan yang menjadi parameter dalam menentukan hasil yang dianggap lebih baik. Sampel dengan penggunaan metode HIT dengan media quenching oli memiliki nilai harga impak yang paling tinggi yaitu 25 J pada permukaan dan 28 J di bagian tengah sampel. Sementara proses high speed quenching memiliki nilai kekerasan paling tinggi dengan nilai 47 HRC di permukaan dan 45 di bagian tengah. Dengan tujuan meningkatkan ketangguhan baja perkakas, metode HIT dengan media quenching oli pada temperature 180oC dianggap mampu menjadi alternatif pengganti metode High speed quenching.

---

Improving the mechanical properties of hot work tool steel has become one of industry’s the biggest concern to get a better product by its quality and effectiveness of production. The research was conducted by comparing the mechanical properties of the High Impact Treatment (HIT) which is quenched by oil at temperatures of 180oC and gas quenching, and the mechanical properties which is obtained by using High speed quenching process. The results of this study were illustrated in the cooling rate graph, the impact values and hardness as the parameters that are considered in determining the better process. Samples of HIT process with oil quenching have the best impact value with 25 J on the surface and 28 J on its core. On the other hand, sample of high speed quenching claims the biggest value of 47 HRC for hardness on the surface and 45 HRC in the core. For improving the toughness of tool steel, HIT process with oil quenching medium at temperatures of 180oC is considered to be an alternative High speed quenching process.

Abstrak :
Baja ASTM A36 merupakan mild carbon steel yang banyak digunakan pada sektor infrastruktur, namun demikian baja karbon memiliki ketahanan korosi yang lebih rendah dibandingkan dengan jenis baja lainnya, yang menyebabkan material ini rentan terhadap korosi dalam lingkungan atmosferik. Oleh sebab itu, untuk meningkatkan ketahanan korosinya, baja ASTM A36 dapat dilapisi dengan glass flake epoxy. Penelitian ini bertujuan untuk mempelajari pengaruh perbedaan metode surface cleaning terhadap kekuatan adhesi glass flake epoxy yang diaplikasikan pada substrat baja tersebut dan ketahanan korosi yang dihasilkannya. Dalam penelitian ini diterapkan 5 (lima) jenis metode surface cleaning yaitu: (i) solvent cleaning, (ii) hand tool cleaning, (iii) power tool cleaning, (iv) power tool to bare metal cleaning, serta (v) abrasive blast cleaning. Selanjutnya, dilakukan proses pengukuran kekasaran permukaan dari masing-masing sampel baja ASTM A36 menggunakan metode field test, sebelum diaplikasikan cat dilakukan pengecekan kondisi lingkungan terlebih dahulu (dry and wet temperature, steel temperature, dew point temperature, serta relative humidity), kemudian glass-flake epoxy diaplikasikan pada permukaan substrat baja menggunakan roller paint brush. Setelah itu, dilakukan pengukuran wet dan dry film thickness. Metode analisis data dilakukan per lima sampel dari masing-masing pengujian yang dilakukan yakni pengujian salt spray, pengujian electrochemical impedance spectroscopy, serta dua pengujian adhesi yaitu pull off adhesion dan tape test test. Hasil penelitian menunjukkan bahwa kemampuan organic coating dipengaruhi oleh perbedaan metode surface cleaning yang diterapkan. Abrasive blast cleaning memiliki ketahanan korosi yang paling baik dengan rata-rata pelebaran (creepage) korosi paling rendah yakni 0.49 mm yang termasuk ke dalam rating number 9, dan kekuatan adhesi rata-rata tertinggi yaitu 3.16 MPa. Dengan demikian dapat disimpulkan bahwa, ketahanan korosi dipengaruhi oleh tingkat kebersihan, sementara kekuatan adhesi dipengaruhi oleh tingkat kekasaran. ...... ASTM A36 steel is a mild carbon steel that is widely used in the infrastructure sector; however, carbon steel has a lower corrosion resistance compared to other types of steel, which makes this material susceptible to corrosion in atmospheric environments. Therefore, to improve its corrosion resistance, ASTM A36 steel can be coated with glass flake epoxy. This research aims to study the effect of different surface cleaning methods on the adhesion strength of glass flake epoxy applied to the steel substrate and the resulting corrosion resistance. In this research, five types of surface cleaning methods were applied, namely: (i) solvent cleaning; (ii) hand tool cleaning; (iii) power tool cleaning; (iv) power tool to bare metal cleaning; and (v) abrasive blast cleaning. Subsequently, the surface roughness measurement process for each ASTM A36 steel sample was carried out using the field test method. Prior to applying the paint, environmental conditions were checked first (dry and wet temperature, steel temperature, dew point temperature, and relative humidity), and then glass-flake epoxy was applied to the surface of the steel substrate using a roller paint brush. Afterward, wet and dry film thickness measurements were taken. The data analysis method was carried out on five samples from each test carried out, namely salt spray testing, electrochemical impedance spectroscopy testing, and two adhesion tests, namely pull-off adhesion and tape test tests. The results show that the organic coating ability is influenced by the different surface cleaning methods applied. Abrasive blast cleaning has the finest corrosion resistance with the lowest average corrosion creepage of 0.49 mm, which is included in rating number 9. In addition, the resulting average adhesion strength is also high at 3.16 MPa. It can be concluded that corrosion resistance is influenced by the degree of cleanliness, while adhesion strength is influenced by the degree of roughness.

Abstrak :
Tool Steel merupakan jenis baja paduan khusus yang digunakan sebagai perkakas dimana aplikasinya untuk memotong dan membentuk material lain menggunakan baja perkakas maka dibutuhkan sifat mekanik yang baik. Fasa austenit sisa memiliki sifat yang lunak dan tidak stabil yang dapat merubah sifat mekanik dari baja perkakas sehingga austenit sisa dalam jumlah yang banyak cenderung menurunkan sifat mekanik dari baja perkakas. Penelitian ini menggunakan AISI O1 tool steel yang merupakan salah satu jenis cold work tool steel dengan variasi temperatur austenisasi yaitu 750, 800, 850, 900, dan 950oC. Penelitian ini difokuskan untuk menentukan temperatur austenisasi yang paling optimal dimana jumlah austenit sisa paling ideal pada material baja AISI O1 dengan tetap mempertahankan kekerasan dari material baja AISI O1 sesuai aplikasi yang diinginkan. Metode karakterisasi yang digunakan dalam penelitian ini adalah Optical Microscope dengan software image-J, dan uji kekerasan Brinell dan Vickers. Fasa yang terkandung pada mikrostruktur secara umum adalah martensit berbentuk jarum, bainite island, austenit sisa, dan fasa karbida yang jumlahnya sangat sedikit. Meningkatnya temperatur austenisasi menyebabkan jumlah karbida yang terlarut semakin banyak, jumlah austenit sisa semakin banyak pada sampel As Quench (γr 1,57% - 7,46%) maupun sampel As Temper (γr 1,23% - 5,66%). dan fasa martensit menjadi lebih kasar. Meningkatnya temperatur austenisasi menyebabkan peningkatan nilai kekerasan sampel As Quench maupun sampel As Temper pada temperatur 750oC - 800oC dan menurunnya nilai kekerasan pada temperatur 800oC – 950oC yang disebabkan faktor kandungan karbon dan paduan pada matriks, jumlah austenit sisa, dan besar butir. Tidak ada pengaruh yang signifikan antara sampel As Quench dengan sampel As Temper terhadap mikrostruktur, jumlah austenit sisa, dan nilai kekerasan. Temperatur austenisasi paling ideal terdapat pada variabel 800oC dimana sampel as Quench dan As Temper berturut – turut memiliki nilai 4,62% dan 3,84% dengan nilai kekerasan sebesar 756,6 HB dan 685,52 HB. ......Tool Steel is a special type of alloy steel used as a tool where the application to cut and form other materials. Tool steel required good mechanical properties. Retained austenite has soft and unstable properties that can change the mechanical properties of tool steel so that a large amount of retained austenite tends to lower the mechanical properties of tool steel. This study uses AISI O1 tool steel which is a type of cold work tool steel with austenitizing temperature variations of 750, 800, 850, 900, and 950oC. This research is focused on determining the most optimal austenitizing temperature where the most ideal amount of retained austenite in AISI O1 while maintaining the hardness of the AISI O1 according to the desired application. The characterizations carried out in this study are Optical Microscope with software Image-J, Brinell hardness test, and Vickers hardness test. The phases contained in the microstructure, in general, are needle-shaped martensite, bainite island, retained austenite, and a very small carbide phase. Increased austenitizing temperatures cause the number of dissolved carbides to increase, the number of retained austenite is increasing in the As Quench sample (γr 1.57% - 7.46%) as well as the As Temper sample (γr 1.23% - 5.66%), and the martensite phase becomes coarser. Increased austenitizing temperatures led to an increase in the hardness value of As Quench and As Temper samples at 750oC - 800oC and decreased hardness values at 800oC – 950oC due to the effect of carbon and alloy content in the matrix, the amount of retained austenite, and grain size. There was no significant influence between the As Quench sample and the As Temper sample on the microstructure, the amount of retained austenite, and the hardness value. The most optimal austenitizing temperature is found in the variable 800oC where the sample as Quench and As Temper respectively have a value of 4,62% and 3,84% with a hardness value of 756,6 HB and 685,52 HB.

Abstrak :
In this study, H13 tool steel and Cr-Mo-V steel were treated by two different types of surface treatments, i.e. double shot peening with nitriding and single shot peening. Samples were dipped into the molten aluminum alloy ADC12 as a simulation of the die casting process and held there for 0.5, 5, and 30 minutes. Several characteristics were analyzed, including surface hardness, microstructure observation, and identification of elements on the intermetallic layer formed. The results of the research showed that H13 steel treated by double shot peening with nitriding had higher surface hardness (1402 VHN) than when treated by shot peening only (536 VHN). A similar tendency emerged with the Cr-Mo-V steel, which had 1402 VHN and 503 VHN after treatment with double shot peening with nitriding and the single shot peening process. In addition, with a dipping time of 30 minutes, the H13 steel treated by double shot peening with nitriding produced a lower average thickness of the compact intermetallic layer. Moreover, double shot peening did not form a broken intermetallic layer, while single shot peening formed one (91.66 µm). Likewise, the Cr-Mo-V steel treated by double shot peening with nitriding produced a thinner compact intermetallic layer than single shot peening, 22.2 µm vs. 27.77 µm, as well as a lower average thickness of the broken intermetallic layer, 40.2 µm vs. 113 µm. This indicates that material treated by double shot peening with nitriding could minimize the occurrence of die soldering.

Abstrak :
Gempa adalah satu fenomena alam yang dapat terjadi kapan saja. Untuk itu, struktur gedung harus direncanakan sedemikan rupa agar dapat memikul beban gempa rencana. Bahkan untuk gempa besar yang jarang terjadi, struktur gedung diharapkan dapat survive tanpa mengalami keruntuhan (collapse) secara tiba-tiba. Hal tersebut memerlukan sebuah desain struktur yang cermat yang dapat merekayasa pola kerusakan atau failure yang akan dialami struktur ketika dilanda gempa besar. Pola kerusakan yang baik agar struktur tidak runtuh tiba-tiba adalah terbentuknya sendi-sendi plastis (plastic hinges) pada elemen-elemen balok satu demi satu sebelum akhirnya sendi-sendi plastis terakhir terbentuk pada ujung kolom-kolom lantai pertama. Kriteria keruntuhan tersebut dikenal dengan istilah strong-column-weak-beam, yang dapat dipenuhi dengan melakukan desain kapasitas (capacity design). Untuk menghadapi gaya gempa yang bekerja pada arah lateral, suatu bangunan memerlukan elemen struktur yang berfimgsi memikul beban lateral tersebut. Salah satu altematifiiya adalah dengan menggunakan Moment Resisting Steel Frame yang ditempatkan pada sisi-sisi tertentu pada bangunan. Untuk mengetahui kinerja moment resisting steel frame terhadap beban gempa, dapat dilakukan analisa pushover dinamis maupun statis baik dengan model dua dimensi maupun tiga dimensi. Analisa dinamis dan model tiga dimensi memberikan hasil yang lebih akurat, namun memerlukan banyak waktu dan tenaga. Sebaliknya analisa statis ekivalen dan model dua dimensi memberikan hasil yang kurang akurat, namun prosesnya lebih sederhana. Analisa pushover dapat dilakukan dengan menggunakan program DRAIN2DX yang dapat mengindikasikan pola keruntuhan yang mungkin terjadi pada struktur yang dianalisa, yaitu urutan teriadinya sendi-sendi plastis.

Abstrak :
Kawat bendrat dibandingkan dengan serat baja yang pada umumnya digunakan untuk campuran beton memiliki kelebihan yakni harga yang lebih murah. Kawat bendrat digunakan sebagai pengganti serat baja dengan cara dipotong menjadi serat berukuran 30 mm. Penggunaan serat kawat bendrat di dalam campuran beton berguna untuk memperbaiki sifat mekanis beton, seperti kuat geser. Penelitian ini menggunakan sampel geser double-L berukuran 30 cm x 20 cm x 7.5 cm dan sampel geser kubus berukuran 30 cm x 15 cm x 10 cm. Sampel diuji dengan menggunakan alat tes tekan universal. Sampel dibuat dengan mutu beton fc? 25 MPa dengan variabel jumlah bendrat di dalam campuran beton sebanyak 0%, 4%, 6%, 8%, 10%, dan 12% terhadap jumlah semen. Hasil dari penelitian ini menunjukkan bahwa sampel yang menggunakan kawat bendrat sebanyak 8% terhadap jumlah semen dalam campuran beton memiliki kenaikan kekuatan geser langsung yang optimum. ......Annealed wire is less expensive compared to the steel fibre used for fibre reinforced concrete and it is used as replacement of steel fibre by cutting this wire into pieces by size of 30 mm. The use of annealed wire fibre (AW-fibre) in concrete mix is to strengthen the shear capacity of concrete. A research outcomes based on a set of laboratory experimental works done to numbers of double L concrete specimens size of 30 cm x 20 cm x 7.5 cm and cube concrete specimens size of 30 cm x 15 cm x 10 cm loaded under direct shear force by a universal compression machine. The specimens were constructed from 25 MPa AW-fiber concrete, using 0%, 4%, 6%, 8%, 10%, and 12% percentage of fibre content to the weight of cement proportion. The result from this research shows that by adding 8% of AW-fibre produced a maximum improvement of the direct shear strength capacity of this type of AW-fibre concrete.