Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Telah dilakukan penelitian pembuatan sediaan tablet parasetamol cara cetak langsung dengan bahan penolong kombinasi antara pati singkong terpregelatinasi dan pati singkong dibandingkan dengan Starch 1500 dan pati singkong dengan beberapa perbandingan yaitu 75 : 25, 50: 50 dan 25 : 75. Pati singkong terpregelatinasi yang digunakan dibuat dengan double drum dryer pada suhu ±80°C dan kadar air ±44 %b/b dari berat kering pati singkong. Ukuran pati singkong terpregelatinasi yang digunakan yaitu 60/100 mesh. Hasil penelitian yang diperoleh menunjukkan bahwa kombinasi antara pati singkong terpregelatinasi dan pati singkong yang memberikan keseragaman bobot terbaik, kekerasan tertinggi dan keregasan terendah yaitu formula 1 (75 : 25); formula 11(50 : 50) memberikan disolusi terbaik dan formula III (25 : 75) memberjkan waktu hancur tercepat. Kombinasj antara pati singkong terpregelatinasi dan pati singkong juga memberikan kekerasan yang lebih tinggi, keregasan yang lebih rendah, waktu hancur yang lebih lama dan disolusi yang lebih rendah dibandingkan dengan kombinasj antara Starch 1500 dan pati singkong. Semakin banyak jumlah pati singkong terpregelatjnasj yang digunakan semakin kuat tablet yang dihasilkan. ...... It has been done research on preparation of paracetamol tablet by direct compressed using additional material from the combination of pregelatinized amylum manihot and amylum manihot compared with the combination of Starch 1500 and amylum manihot in several proportions as 75 25, 50: 50 and 25 : 75. Pregelatinized aniylum manihot was made by double drum dryer with the temperature of ±80°C and ±44% 1'/b of water content calculated from the amylum manihot dry weight. Particle size of pregelatinized amylum manihot used in this research is 60/100 mesh. This research obtained result shows that combination of pregelatinized amylum manihot and amylum manihot which gives the best uniformity in weight, the highesthardness and the lowest friability is formula I (75 25); formula 11(50 : 50) gives the best dissolution rate and formula III (25 75) gives the shortest disintegration time . The combination of pregelatinized amylum manihot and amylum manihot also gives higher hardness, lower friability, longer disintegration time and lower dissolution rate compared with the combination of Starch 1500 and amylum manihot. The bigger amount of pregelatinized amylum manihot used could increase the strength of tablets produced.

Abstrak :
Manihot esculenta Crant atau Manihot utilissima Pohl merupakan tanaman yang mudah tumbuh hampir di seluruh dataran di Indonesia dan waktu panen relatif singkat, sehingga efektif untuk digunakan sebagai penghasil bahan baku, seperti pati singkong atau tapioka. Dalam industri Farmasi, pati singkong digunakan sebagian besar sebagai bahan penolong tablet secara granulasi basah. Namun demikian, sampai saat mi produksi pati singkong yang digunakan untuk industri Farmasi mi sangat terbatas. Dalam formula tablet cetak langsung pati singkong belum banyak dipakai, karena tidak memiliki sifat alir dan kompresibilitas yang baik. Sehingga perlu adanya usaha untuk memodifikasi pati singkong. Tujuan penelitian mi adalah untuk mengetahui karakteristik pati singkong dan pati singkong terpregelatinasi, yang meliputi karakteristik fisik, kimia dan fungsional serta dibandingkan dengan Starch 1500 sebagai bahan penolong tablet cetak langsung. Dalam penelitian mi, pati singkong terpregelatinasi dibuat dari pati singkong ditambah dengan air suling 44% dari berat bahan, kemudian pasta yang terbentuk dialirkan ke double drum drier yang sudah diatur suhunya 80°C. Selanjutnya lapisan atau serpihan-serpihan tipis yang dihasilkan digiling menggunakan Hammer mill, maka serbuk yang terbentuk selanjutnya dianalisis. Pregelatinasi pati tidak merubah komposisi kimia produknya. Akan tetapi merubah karakteristik fisik seperti bentuk dan ukuran granula, pola diffraksi sinar-X, derajat putih, sifat birefringence, densitas kamba dan viskositas, serta karakteristik fungsionalnya seperti waktu alir, laju alir, sudut diam dan kompresibilitas. Waktu alir pati singkong terpregelatinasi dan Starch 1500 tidak memiliki perbedaan yang bermakna. Sedangkan kompresibilitas Starch 1500 lebih besar daripada pati singkong terpregelatinasi. Pati singkong terpregelatinasi seperti Starch 1500 dapat digunakan sebagai bahan penolong tablet cetak langsung. ...... Manihot esculenta Crant or Manihot utilissima Pohl is one easy-to-grow crop in Indonesia. It can be found in most every part of the country that it is of such great potential for effective production of cassava starch or tapioca. In Pharmaceutical industry, cassava starch is mostly used as excipient in wetgranulation process. The production of the starch used in the industry, however, is still limited. The starch is not used in direct compression formulation due to its flow characteristic and compressibility that does not meet the desired specification. Therefore, it is of great importance and necessity to conduct intensive research and study to modify the characteristics of the starch to meet such requirements. One of such modification is the pregelatination. In the experiment pregelatinized starch is made from cassava added with distilled water 44% of the material dry weight. The suspension-like mixture is then flowed through double drum dryer previously set up at a temperature of 80°C. After drying process, the flakes are then ground on a Hammer mill. The product is then ready to be analyzed. The pregelatination process does not alter chemical composition of the starch, but changes the physical properties of the starch such as the shape of granules, X-ray diffraction pattern, degree of whiteness, birefringence, bulk density and viscosity, as well as its functional characteristics such as flow properties, angle of repose, and compressibility Flow time of the pregelatinized starch is not significantly different from that of Starch 1500, whereas Starch 1500 compressibility is greater than that of the starch. Like Starch 1500, pregelatinized cassava starch can be used as an excipient in direct compression tablet formulation.

Abstrak :
Penelitian mengenai kanji berlambang orang ini bertujuan untuk meneliti makna kanji. Kanji adalah huruf yang asal_nya dari Cina, sama sekali tidak dapat dilepaskan dari bahasa Jepang, khususnya yang berkaitan dengan sistem penulisan bahasa Jepang, meskipun bahasa Jepang mempunyai aksara-aksara yang diciptakan sendiri, yakni hiragana dan katakana. Hal ini disebabkan karena kanji memiliki fungsi sebagai pembeda arti kata dalam bahasa Jepang, di samping ada juga fungsinya yang lain, yaitu sebagai pelambang ucapan untuk ungkapan yang me_nyatakan nama orang, tempat, kota, dan lain-lain. Huruf-huruf kanji kebanyakan terdiri lebih dari satu komponen pembentuk, hanya sedikit sekali kanji yang terdiri dart satu komponen pembentuk. Pada golongan kanji yang diben_tuk oleh lebih dari satu komponen pembentuk, kanji itu memi_liki komponen utama atau disebut juga lambang kanji. Lambang kanji ini dipakai untuk mengolong-golongkan kanji dan memudah_ken pencarian kanji di dalam suatu kamus kanji. Skripsi ini hanya membatasi pada kanji-kanji yang berlambang orang, yang ada di dalam buku teks Nihongo I dan II yang digunakan di lingkungan Fakultas Sastra Universitas Indonesia Jurusan Jepang. Pengumpulan data skripsi dilakukan melalui penelitian buku-buku yang sebagian besar adalah kamus-kamus kanji. Pene litian ini didahului dengan melihat sejarah masuknya kanji ke dalam bahasa Jepang, dan hal-hal yang berkaitan dengan kanji itu sendiri, yaitu fungsi kanji dalam bahasa Jepang, kanji bahasa Jepang, dan hal-hal yang berhubungan dengan pembentuk_an kanji. Hasil dari penelitian ini menunjukkan bahwa kanji khu_susnya dalam lingkup kanji berlambang orang pada buku ajar Nihongo I dan II sebagian besar maknanya berkaitan dengan lambang kanji (komponen utama kanji) tersebut. Tetapi ada ju_ga kanji yang dibentuk dari gabungan komponen-komponeh.oem_bentuk kanji yang menghasilkan makna baru dari kanji tersebut. Meskipun demikian makna itu sedikit banyak masih mengandung makna komponen-komponen pembentuknya, baik itu komponen uta_ma, komponen lainnya (komponen pendukung) atau bahkan kedua jenis komponen tersebut. Secara rinci hal itu dapat dilihat dalam skripsi ini. Untuk lebih memperjelas keterangan-keterangan di dalam skripsi ini, pada akhir skripsi disertakan. sebuah tabel yang memuat mengenai daftar kanji yang diteliti, daftar komponen pembentuk utamanya, beserta keterangan-keterangannya.