Hasil Pencarian  ::  Simpan CSV :: Kembali

"Element impurity determination in U3 Si2 powder by using ICPS equipment, the analysis of trace elements in U3 Si2 powder (Al, B,Cd,Co,Cu,Fe,NI,Li,Zn) has been done by using ICPS. The aim of this activity is to get the data support or comparator in verification between work is to verity the trace elements content quantitatively in U3 Si2 powder and to verity its specification toward the required standard specified by IAEA. Sample preparation is carried out by dissolving of 1 g U3 Si2 powder, in HNO3 6M, then filtered and extracted with TBP / Hexane (7:3). Result of analysis, indicate that all metal element (Al,B,Cd,Co,Cu,Fe,Ni,Zn,Li) which is required in nuclear fuel element specification, can be detected quality...."

"The behavior of UO2 powder from ADU, AUC,IDR AND modified adu processes during sintering using dilatometer. Research on the bahavior of UO2 powder during sintering has been performed. Observation of the powder bahavior is conducted on four types of UO2 powder prepared from ADU,AUC,IDR and modified ADU routes. The purpose is to determine UO2 powder that has good sinterability without pre-conditioning treatment on the powder...."

"This study was focused on production and utilisation of loccase in pulp bleaching process. Loccase was produced by white-rot fungi of Marasmius sp which was immobilised in luffa sponge in a modified immersion bioreactor...."

"Bantalan (bearing) merupakan salah satu komponen penting pada industry otomotif yang membutuhkan material dengan properties yang baik. Peningkatan properties dari suatu komponen dapat dilakukan dengan pemilihan material yang tepat. Komposit merupakan material alternatif yang dapat digunakan, dengan menggabungkan sifat-sifat unggul dari suatu material yang dapat menghasilkan material baru dengan properties yang lebih baik. Komposit alumunium grafit yang digolongkan dalam Metal Matrix Composite dapat digunakan sebagai pilihan yang potensial untuk menghasilkan bearing dengan kualitas yang lebih baik karena memiliki sifat mekanis dan fisik yang sesuai untuk kebutuhan industri otomotif. Keunggulan utama dari komposit ini adalah memiliki densitas yang rendah sehingga berat komponen akan semakin ringan, disamping itu juga memiliki ketahanan aus yang baik, kekuatan dan kekerasan yang tinggi. Pada penelitian ini, komposit alumunium grafit dihasilkan dengan metode metalurgi serbuk dengan tahapan proses dari karakterisasi serbuk hingga sintering. Digunakan pula serbuk Cu (tembaga) sebagai wetting agent. Dengan variable yang digunakan adalah %Vf grafit maka akan diketahui pengaruhnya terhadap sifat mekanis, yaitu kekerasan, densitas/porositas, laju aus, dan kuat tekan serta struktur mikro material komposit alumunium grafit ini. Kadar grafit yang digunakan adalah 0,5%, 1%, 3%, 5%, dan 7%. Dalam penelitian ini disimpulkan bahwa penambahan kadar grafit akan menaikkan properties diantaranya kekerasan, kuat tekan, dan densitas serta menurunkan porositas dan laju aus. Namun, peningkatan properties ini hanya akan tercapai apabila wetting agent yang digunakan mencukupi untuk membasahi grafit. Kadar optimum penambahan grafit adalah 1%Vf dimana nilai kekerasan dan densitas mencapai nilai tertinggi dan laju aus serta porositas pada nilai terendah. Dari hasil pengujian, nilai densitas optimum yaitu sebesar 2,30 gr/cm3 diperoleh pada sampel sinter maupun non-sinter dengan 1%Vf Grafit. Nilai kekerasan optimum diperoleh pada sampel hasil sinter dengan kadar grafit sebesar 1%Vf sebesar 65 BHN, sedangkan kuat tekan optimum pada kadar grafit 7% yaitu 549 MPa. Nilai porositas minimum diperoleh pada sampel sinter dengan variable %Vf Grafit 0,5% yaitu sebesar 11,23%. Nilai laju aus minimum diperoleh pada sampel hasil sinter dengan %Vf Grafit 1% yaitu sebesar 4 x 10-5 mm3/mm. Pada pengamatan struktur mikro terlihat bahwa penambahan grafit akan meningkatkan porositas. Hasil SEM dan EDS menunjukkan adanya 3 fasa yaitu, fasa matriks, Al2O3 dan terbentuknya fasa intermetalik AlCu2.

---

Bearing is one of important components in automotive industry which is requiring good properties. By combining the best properties from each material and produce a new amterial with better properties, composite being an alternative materials. An aluminum MMC reinforced graphite posses a number of mechanical and physical properties that make them attractive for automotive applications, such as bearing to produce parts with better quality. Primary advantages of using this material are its low-density that will produce light weight component, with better wear resistance, higher strength and hardness.

In this reasearch, aluminum graphite composite was produced by powder metallurgy methode which started from powder characterization until sintering process. Copper powders were added as wetting agent. Graphite content from 0.5%, 1%, 3%, 5%, to 7%Vf were used as variable of this reasearch to observe the effect of graphite addition on mechanical properties, those are hardness, density/porosity, wear rate, compressive strength, and microstructure of aluminum graphite composite.

The result shows that graphite addition increased compressive strength, hardness, and the number of porosity but decrease density and wear rate. But it would be achieved if wetting agent is sufficient to wet graphite. The optimum properties achieved at addition of 1%Vf graphite which hardness and density are the highest meanwhile wear rate and porosity are the lowest.

The optimum density is 2.30 gr/cm3 which is reached at 1%Vf graphite content for both sintered and non-sintered samples. The highest hardness is 65 BHN from 1%Vf, sintered sample. The highest compressive strength is 549 MPa achieved at 7%Vf graphite content. Minimum porosity obtained at 0.5%Vf is 11.23%. And wear rate value is 4 x 10-5 mm3/mm reached at 1%Vf sintered sample. Microstructures observation shows that graphite addition increased the number of porosity. SEM and EDS data show that there are 3 phases on sintered sample, i.e matrix phase, Al2O3 phase and intermetallic AlCu2 phase."

"Telah dilakukan pembuatan paduan Al Cu dengan proses metalurgi serbuk (powder metallurgy). Bahan diperoleh dari Merck, kemurnian > 98,5 % untuk serbuk Al , sedang serbuk Cu, kemurnian > 99,7 %. Kedua serbuk tersebut dicampur dengan berbagai variasi komposisi persen berat, terdiri dari Al - 90,40% Cu, Al - 70, 19% Cu, Al - 33,33% Cu, Al - 0% Cu, Al - 3% Cu, Al - 5% Cu. Proses pembentukan dilakukan dengan menggerusnya selama 3 jam. Kemudian dilakukan proses pembentukan dengan cara cetak tekan menggunakan hidrolik press dengan tekanan 7 ton dan selanjutnya di Sinter/pembakaran pada temperatur 400°C, 500°C, 600°C. Heat treatment dilakukan selama 1 jam pada temperatur 540°C, quenching dalam media air. Karakterisasi meliputi analisis fasa dengan XRD, kekerasan, densitas serta kandungan unsur paduan dengan XRF. Hasil analisis fasa memperlihatkan adanya fasa Al2Cu yang ditunjukkan oleh puncak difraksi dengan orientasi (220), (310), (130). Fasa Al3Cu2 bidang orientasi (111), (205), (102) sedang fasa Al4Cu9, oleh puncak difraksi (330), (411 ), (600), (442) , pada temperatur sinter >- 500°C, densitas (appaerent density) meningkat dengan bertambahnya prosentase Cu,dan kenaikan temperatur sinter untuk komposisi Cu relatif kecil, nilai densitas :2,23gr/cm3 - 6,44gr/cm3 . Kekerasan cenderung meningkat tajam untuk temperatur sinter 600°C bisa mencapai 797 ,5 HV, khususnya untuk paduan komposisi (Al - 70, 19% Cu), hasil analisis kandungan unsur dengan XRF, semakin tinggi temperatur sinter ternyata prosentasi kandungan Al mengecil, kecuali untuk paduan Al - 0% Cu, kenaikan temperatur sinter menyebabkan kandungan Al justru naik, walaupun kenaikannya relatif kecil."