Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
ABSTRAK
The present works investigates the leaching of tin slag by using hydrochloric and citric acid. In the preliminary stages, the research begins with a thorough literature review, followed by the development of the methods and apparatus determination. It was found that these methods were able to extract tin from tin slag and produced comparable results with the previously published researches for hydrochloric and citric acid leaching. Regarding the rare metals extraction (Nb and Ta), it was found to be unreactive with the solution, hence making indications that their presence mostly remains in leaching residue.

---

ABSTRACT
Studi ini menyelidiki pelindian terak timah dengan menggunakan klorida dan asam sitrat. Pada tahap awal, penelitian ini dimulai dengan tinjauan literatur secara menyeluruh dan diikuti dengan pengembangan metode dan penentuan alatalat eksperimen. Penelitian ini menemukan bahwa metode pelindian dengan asam hydrochloric dan asam citric mampu mengekstrak timah dari terak timah dan menghasilkan hasil yang sebanding dengan penelitian-penelitian sebelumnya yang diterbitkan. Mengenai ekstraksi logam tanah jarang, ditemukan bahwa logam tanah jarang (Nb dan Ta) tidak reaktif dengan larutan asam hydrochloric dan asam citric. Hal ini membuat indikasi bahwa kehadiran mereka sebagian besar masih tersimpan di residu pelindian.

Abstrak :
Sejak lama, mayoritas logam nikel diproduksi melalui bijih sulfide. Namun, Namun, dengan semakin menurunnya cadangan nikel sulfida dan di sisi lain permintaan terhadap logam nikel semakin tinggi, maka pemurnian nikel dari bijih laterit semakin menjanjikan karena berlimpahnya cadangan bijih laterit dan biaya penambangannya relatif lebih rendah. Oleh sebab itu, bijih laterit berpotensi menjadi sumber bahan baku utama untuk memperoleh logam nikel di masa yang akan mendatang. Penelitian ini menggunakan bijih laterite kadar rendah atau limonite, dengan tujuan untuk mengetahui fasa yang terdapat pada bijih pada keadaan awal dan pada keadaan setelah proses reduksi roasting dengan suhu 600°C dan komposisi serbuk batu bara 20% wt selama 30 menit dengan menggunakan XRD. Selain itu, pengaruh reduksi roasting terhadap proses recovery logam nikel juga dilakukan dengan melakukan leaching menggunakan pelarut asam sulfat (H2SO4) selama 60 menit dan suhu kamar (±25°C) dengan konsentrasi bervariasi dari 0.1 sampai 0.4 M. Hasil penelitian ini menunjukkan bahwa proses reduksi roasting dan peningkatan konsentrasi H2SO4 pada leaching mempunyai pengaruh positif terhadap % recovery nikel. Pada bijih limonit yang tidak direduksi, leaching dengan konsentrasi 0.4 M mempunyai %recovery 10.13%. Sedangkan pada bijih yang tereduksi, leaching dengan konsentrasi 0.4 M menghasilkan %recovery sebesar 12.71%. ......The majority of nickel metals are produced through sulfide ore. However, with the decreasing of nickel sulfide ore deposite and on the other hand, the demand of nickel metal is getting higher, then the extraction process using laterite ore is more promising since the abundance of the ore and the low cost of its mining process. Hence, laterite ore will potentially be the main source to obtain nickel in the near future. This experiment is using low grade laterite ore, namely limonite, in purpose to recognize the phases which are exist in the raw ore and in the roasted ore at temperature 600°C and pulverized coal composition 20%wt in 30 minutes using XRD. Moreover, the effect of reduction roasting on recovery of nickel is done with sulphuric acid (H2SO4) leaching in 60 minutes and room temperature (±25°C) with various concentration from 0.1 to 0.4 M. The result shows that the reduction roasting and the increasing of the concentration of H2SO4 in leaching have the positive impact on %recovery nickel. In unreduced limonite ore, leaching using 0.4 M concentration has 10.13% of %recovery, whereas in reduced ore, leaching using 0.4 M concentration has 12.71% of %recovery.

Abstrak :
Building on previous editions described as "a useful contribution to the current literature on corrosion science, engineering, and technology" by Corrosion Review, this third installment offers real-world applications and problem-solving techniques to reduce the occurrence of pits, cracks, and deterioration in industrial, automotive, marine, and electronic structures. It also details the electrochemical and chemical properties, adsorption mechanisms, environmental parameters, and microstructural factors that influence corrosion formation. Including contributions from authors around the world, this reorganized third edition covers the most recent advances in the field, adding three new chapters on Fundamentals of Corrosion from a Surface Science and Electrochemical Basis, High-Temperature Oxidation, and Atomistic Modeling of Corrosion.