Hasil Pencarian  ::  Simpan CSV :: Kembali

"Katalis CuO dengan struktur nanoleaf berhasil dikomposit pada penyangga γ-Al2O3 yang disintesis dengan metode wet chemical dengan etilen glikol sebagai bahan penstabil nanostruktur. Komposit CuO-nanoleaf/γ-Al2O3 memiliki aktivitas katalitik yang menjanjikan untuk reaksi sintesis senyawa p-Aminofenol (PAF) dari p-Nitrofenol (PNF). Komposit CuO-nanoleaf/γ-Al2O3 telah dikarakterisasi menggunakan Field Emission Scanning Electron Microscopy-Energy Dispersive Spectroscopy (FESEM-EDS), X-Ray Diffraction (XRD), Transmission Electron Microscopy (TEM), dan N2 adsorpsi-desorpsi.  Hasil karakterisasi FESEM-EDS dan TEM menunjukkan bahwa morfologi CuO adalah berbentuk nanoleaf yang menempel diatas permukaan penyangga γ-Al2O3 serta kom-posisi unsur Cu, Al dan O pada komposit. Pola puncak difraktogram XRD menunjukkan adanya fasa kristal CuO monoklinik dan fasa Al2O3 dalam komposit. Disisi lain, hasil karakterisasi N2 adsorpsi-desorpsi menunjukkan bahwa komposit CuO-nanoleaf/γ-Al2O3 memiliki luas permukaan spesifik yang tinggi yakni 140,19 m2/g. Berdasarkan hasil uji sintesis PAF dari PNF, komposisi CuO dalam katalis yang optimal adalah 5% dengan kondisi operasi yang optimum adalah dengan loading katalis 5 g/L, suhu reaksi 30 oC dan konsentrasi reaktan kurang dari 3.000 ppm dengan waktu reaksi 12 menit. Suhu optimum saat proses kristalisasi PAF adalah suhu 8 oC dengan yield 85,65% dan kemurnian 78,36%. Selain itu, kristal PAF telah dikarakterisasi menggunakan Fourier Transform Infra-Red (FT-IR) dan Ultra Performance Liquid Chromatography-Mass Spectrometer (UPLC-MS). Hasil karakterisasi menunjukkan bahwa sampel PAF memiliki spektra FT-IR yang serupa dengan spektra FT-IR PAF standar dan berat molekul 109,12 g/mol.

---

The CuO catalyst with nanoleaf structure was successfully composited on γ-Al2O3 surface which was synthesized by wet chemical and ethylene glycol as a nanostructure stabilizer. The CuO-nanoleaf/γ-Al2O3 composite has promising catalytic activity in the synthesis of p-Aminophenol (PAF) from p-Nitrophenol (PNF). The CuO-nanoleaf/γ-Al2O3 was characterized using Field Emission Scanning Electron Microscopy-Energy Dispersive Spectroscopy (FESEM-EDS), X-Ray Diffraction (XRD), Transmission Electron Micros-copy (TEM), and N2 adsorption-desorption. The results of FESEM-EDS and TEM characterization results showed the morphology of CuO with nanoleaf structure attached into the surface of the γ-Al2O3 and the elemental composition of Cu, Al and O was identified in the composite. The XRD pattern shows the crystalline of monoclinic CuO phase and Al2O3 phase in the composite. The N2 adsorption-desorption characterization showed that CuO-nanoleaf/γ-Al2O3 had a high specific surface area of 140.19 m2/g. Based on the results of the synthesis of PAF from PNF, the optimal composition of CuO in the catalyst was 5% under optimum operating conditions with a catalyst loading of 5 g/L, a reaction temperature of 30oC and a reactant concentration of less than 3000 ppm with a reaction time of 12 minutes. In the PAF crystallization process, the crystallization temperature of 8oC could produce PAF crystals with a yield of 85.65% and a purity of 78.36%. In addition, PAF crystal was characterized using Fourier Transform Infra-Red (FT-IR) and Ultra Performance Liquid Chromatography-Mass Spectrometer (UPLC-MS). The characterization results showed that PAF sample had a FT-IR chromatogram similar to the PAF standard and the PAF synthesized was identified as having a molecular weight of 109.12 g/mol."

"Pemanfaatan aplikasi dengan katalisis menggunakan nanopartikel merupakan salah satu hal yang banyak dilakukan dalam bidang nanosains. Struktur nanopartikel terus dikembangkan untuk meningkatkan kinerja dalam berbagai aplikasi. TiO₂sebagai katalis dilakukan dengan pembentukan TiO₂nanopartikel. Metode molten saltmerupakan salah satu metode yang dapat digunakan untuk mensintesis TiO₂nanowiresdengan menumbuhkan kristal tunggal dalam jumlah banyak melalui media lelehan garam. Pada penelitian ini dilakukan sintesis TiO₂nanowiresmelalui metode molten saltserta modifikasi penambahan logam perak melalui metode presipitasi, impregnasi, dan molten saltsehingga mempengaruhi sifat katalitiknya. Pencampuran dilakukan pada TiO₂anatase, NaCl, dan Na₂HPO₄yang dikalsinasi pada suhu 825°C selama 8 jam dan kemudian didinginkan hingga suhu ruang. Modifikasi penambahan logam perak dilakukan pada metode molten saltdengan perlakuan yang sama. Modifikasi juga dilakukan pada metode presipitasi dengan penambahan larutan NaOH serta pada metode impregnasi dengan perlakuan kalsinasi pada suhu 400°C. TiO₂nanowires dan Ag₂O/ TiO₂ yang telah disintesis dikarakterisasi dengan menggunakan XRD, FTIR, SEM, TEM, UV-Vis DRS, dan amonia TPD. Dengan adanya penambahan logam perak dapat mempengaruhi penurunan nilai energi celah pita namun tidak mempengaruhi struktur morfologinya. Masing-masing katalis yang telah disintesis digunakan dalam reaksi reduksi 4-nitrophenoldengan bantuan NaBH₄. Reduksi 4-nitrophenoldapat ditandai dengan adanya perubahan warna karena adanya katalis yang digunakan dapat mempercepat proses reduksi tersebut. Kecepatan reaksi tertinggi terjadi pada reduksi 4-nitrophenol dengan katalis Ag₂O/TiO₂nanowiresmelalui metode impregnasi dengan waktu reaksi 30 detik. Uji reusabilitas dilakukan terhadap katalis Ag₂O/TiO₂nanowires impregnasi sebanyak 4 kali dan menghasilkan penurunan kecepatan reaksi sebesar 180 kali.

---

Utilizing the application with catalysis using nanoparticle is one of many substances conducted in the field of nanoscience. To form TiO₂as a catalyst is by forming TiO₂ nanoparticle. The structure of nanoparticle is keep on being developed to increase its productivity on various applications. The molten salt method is one of the methods that can be used to synthesize TiO2 nanowires by growing up a tremendous amount of single crystals with the medium of molten salt. In this research, there will be conducted the synthesis of TiO₂nanowires using molten salt method with modification by adding silver nitrate metals with precipitation method, impregnation method, and molten salt method so that it will influence its catalytic nature. The mixing is carried out on TiO₂anatase, NaCl, and Na₂HPO₄that are calcined at 825 degrees celsius for 8 hours and then chilled until room temperature is reached. The modification by adding molten salt is carried out on molten salt method with the same treatment. The modification is also carried out on precipitation method by adding NaOH solution, also on impregnation method with calcination at 400 degrees celsius. TiO₂nanowires and Ag₂O/ TiO₂that has been synthesized is characterized by using XRD, FTIR, SEM, TEM, and also UV-Vis DRS. Adding silver metal can influence its band gap devaluation but can not influence its morphological structure. Each synthesized catalysts are being used in the reaction of the reduction of 4-nitrophenol with the help of NaBH₄. The 4-nitrophenol reduction can be marked by the change of color because of the catalysts existence can accelerate the reduction process. The reaction’s highest speed occurs at the reduction of 4-nitrophenol with the catalyst of Ag₂O/TiO₂nanowires with impregnation method with the reaction speed of 30 seconds. The reusability test is conducted to the catalyst of Ag₂O/TiO₂nanowires impregnation for 4 times and resulted in the decrease of reaction speed by 180 times."

"

Studi mengenai katalisis dengan menggunakan nanopartikel merupakan salah satu hal yang banyak dipelajari dalam bidang nanosains modern. Aplikasi TiO₂ dalam bidang katalisis dikembangkan melalui pembentukan TiO₂ nanopartikel. Sintesis one-dimensional material untuk menghasilkan yield yang cukup banyak masih terus dikembangkan. Metode molten-salt digunakan untuk mensintesis single-crystalline TiO₂ nanowires dalam jumlah banyak dan dimensi yang terkontrol. Pada penelitian ini dilakukan sintesis TiO₂ nanowires dengan menggunakan metode molten-salt serta modifikasinya dengan penambahan logam transisi sehingga terjadi perubahan karakteristik. TiO₂ anatase berbentuk bubuk, NaCl, dan Na₂HPO₄ dicampurkan kemudian dikalsinasi menggunakan furnace pada suhu 825 °C selama 8 jam dan didinginkan perlahan hingga mencapai suhu ruang. Penambahan logam dilakukan untuk melihat pengaruhnya terhadap kemampuan katalisis. Sintesis dilakukan dengan cara yang sama dengan penambahan logam pada saat pencampuran dengan mortar. TiO₂ nanowires dan M-O/ TiO₂ nanowires yang telah disintesis dikarakterisasi dengan menggunakan XRD, SEM, TEM, serta UV-Vis DRS. Adanya penambahan logam transisi tidak mempengaruhi struktur dan morfologi dari TiO₂ nanowires, namun terdapat perubahan pada ukuran kristal dan nilai ban gapnya. Katalis yang telah dipreparasi digunakan pada reaksi reduksi 4-nitrophenol dengan adanya NaBH₄. Adanya katalis pada reaksi tersebut mempercepat proses reduksi 4-nitrophenol menjadi 4-aminophenol yang ditandai dengan adanya perubahan warna. Penurunan kecepatan reaksi secara signifikan ditunjukkan pada penggunaan katalis Ag₂O/TiO₂ nanowires dengan waktu reaksi 18 detik untuk penggunaan katalis sebanyak 0,1 gram. Uji reusabilitas juga dilakukan terhadap katalis Ag₂O/TiO₂ nanowires.

---

The study of catalysis using nanoparticles is one of the things that widely studied in the field of modern nanoscience. The application of TiO₂ in the field of catalysis was developed through the formation of TiO₂ nanoparticles. The synthesis of one-dimensional material to produce sufficient yields is still being developed. The molten-salt method was used to synthesize large quantities of single-crystalline TiO₂ nanowires and controlled dimensions. In this study, the synthesis of TiO₂ nanowires was carried out using the molten-salt method and its modification with the addition of transition metals so that changes in characteristics occurred. Anatase TiO₂ in the form of powder, NaCl, and Na₂HPO₄ mixed and then calcined using furnaces at 825 ° C for 8 hours and cooled slowly to reach room temperature. Metal addition was added to see the effect on the ability of catalysis. Synthesis was done in the same way as adding metal during mixing with mortar. The synthesized TiO₂ nanowires and M-O/TiO₂ nanowires were characterized using XRD, SEM, TEM, and UV-Vis DRS. The addition of transition metals does not affect the structure and morphology of TiO₂ nanowires, but there are changes in the size of the crystal and the value of the band gap. The prepared catalyst was used in the 4-nitrophenol reduction reaction in the presence of NaBH₄. The presence of a catalyst in the reaction accelerates the process of reducing 4-nitrophenol to 4-aminophenol which is characterized by a change in color. A significant decrease in reaction speed was shown in the use of Ag₂O/TiO₂ nanowires catalysts with a reaction time of 18 seconds for catalyst use of 0.1 gram. Reusability tests were also carried out on Ag₂O/TiO₂ nanowires catalysts.

"