"ABSTRAKProses reduksi selektif bijih nikel laterit dengan penambahan aditif NaCl dan gas pereduksi CO, diikuti dengan proses separasi magnetik telah dipelajari dalam penelitian ini. Karakterisasi bijih menunjukan kandungan nikel sebesar 1,4% dan besi sebesar 50,5% dengan fasa-fasa dalam bijih yaitu gutit (FeOOH), lizardit (Mg3(Si2O5)(OH)4), olivin ((Fe,Mg)2SiO4), dan kuarsa (SiO2). Proses reduksi dilakukan dengan variasi temperatur 900, 1000, dan 1100 °C, waktu tahan 30-180 menit, dan dengan penambahan 10% aditif NaCl. Proses separasi magnetik yang dilakukan menggunakan metode basah dan kekuatan magnet sebesar 500 gauss untuk memisahkan produk konsentrat dan tailing. Bijih hasil reduksi dikarakterisasi dengan menggunakan pengujian metalisasi, X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM) yang dilengkapi dengan Energy Dispersive X-Ray Spectroscopy (EDS) serta konsentrat dan tailing diidentifikasi dengan alat uji X-Ray Flourescence (XRF). Fasa yang terdapat dalam bijih hasil reduksi yaitu kamasit (FeNi), magnetit (Fe3O4), wustit (FeO), natrium klorida (NaCl) dan fayalit (Fe2SiO4). Hasil percobaan menunjukkan derajat metalisasi nikel dan besi meningkat seiring dengan meningkatnya temperatur dari 900-1100 °C dan waktu tahan reduksi dari 30-180 menit oleh karena semakin intensnya proses kloridasi, segregasi, dan reduksi pada bijih. Hal ini berdampak pada meningkatnya kadar nikel dan besi pada konsentrat hasil proses separasi magnetik. Perolehan nikel meningkat seiring dengan meningkatnya temperatur dan waktu tahan reduksi oleh karena semakin banyaknya nikel yang terbebas dari fasa pengandungnya, sementara fayalit semakin banyak terbentuk sehingga perolehan besi menurun. Kadar dan perolehan optimum yang didapat yaitu berturut-turut 2,8% dan 59,2% untuk nikel, dan 58,16% dan 34,27% untuk besi. Derajat metalisasi digunakan sebagai parameter kinetika reduksi dan didapatkan model Avrami-Erofeyev sebagai model yang merepresentasikan mekanisme nukleasi pada proses reduksi. Energi aktivasi yang didapat yaitu sebesar 38,1622 kJ/mol atau 9,12 kkal/mol dengan tahapan pengendali laju reaksi yaitu gabungan antara difusi gas dan reaksi kimia antarmuka.

---

ABSTRACTKSelective reduction process of lateritic nickel ore using CO and NaCl additive were studied in this work. Ore characterization result shows the nickel grade of 1.4% and iron grade of 50,5% with phases contained in the ores were goethite (FeOOH), lizardite (Mg3(Si2O5)(OH)4), olivine ((Fe,Mg)2SiO4) and quartz (SiO2). The temperature of reduction process varied from 900, 1000, and 1100 °C with reduction time of 30-180 min and 10% NaCl additives. Magnetic separation process were done using wet methode and magnetic intensity of 500 gauss to separate concentrate and tailing. The reduced ore were characterisized using metallization test, X-Ray Diffraction (XRD), Scanning Electron Microscope (SEM) with Energy Dispersive X-Ray Spectroscopy (EDS) while the concentrate and tailing were identified using X-Ray Flourescence (XRF). Kamacite (FeNi), magnetite (Fe3O4), wustite (FeO), natrium chloride (NaCl) dan fayalite (Fe2SiO4) were the phases present in the reduced ore. The result shows that the degree of metallization of nickel and iron increases with the increasing temperature from 900 to 1100 °C and holding time from 30 to 180 minutes because of the increasing intensity of the chloridization, segregation and reduction process. This has an impact on increasing the grade of nickel and iron on the concentrate. The recovery of nickel was increased along with the increasing temperature and holding time because of the increasing amount of nickel liberated from its bearing phase, while fayalite were increasingly formed so that the recovery of iron was decreased. The optimum grade and recovery resulted from the experiment was 2.8% and 59.2% for nickel respcetively, and 58.16% and 34.27% for iron. The degree of metallization was used as reduction kinetics paramter and the model representing the reduction proces was Avrami-Erofeyef with its nucleation mechanism. The resulting activation energy of 38.1622 kJ/mol or 9,12 kkal/mol with combined gas diffusion and interfacial chemical reaction as the rate-controlling step."

"Tingginya temperatur dalam proses peleburan/smelting bijih nikel laterit menyebabkan tingginya biaya/konsumsi energi. Penggunaan sulfur/sulfat mampu mengoptimalkan proses reduksi pada temperatur rendah melalui pembentukan senyawa FeS. Limbah biomass, yaitu arang cangkang sawit (ACS) memiliki potensi sebagai reduktor dalam proses reduksi bijih nikel laterit dikarenakan memiliki nilai fixed carbon dan nilai kalor yang cukup tinggi di bandingkan biomass yang lain, selain itu limbah ACS semakin melimpah seiring dengan makin tumbuh berkembangnya industri perkebunan sawit Indonesia. Oleh karena itu, dalam penelitian ini akan dipelajari proses selektif reduksi bijih nikel laterit menjadi konsentrat logam ferronikel pada temperatur rendah menggunakan reduktor biomass ACS dengan aditif elemental sulfur dan sodium sulfate.Bijih nikel laterit kadar rendah (laterit jenis limonit), reduktor ACS, dan aditif sulfur-sodium sulfate digerus hingga berukuran kurang dari 100 mesh, kemudian diaduk secara merata dan di-aglomerasi dalam bentuk pellet berukuran 10-15 mm. Variasi penambahan elemental sulfur dilakukan sebanyak 0-5%S. Variasi jumlah ACS dilakukan berdasarkan stoikiometri sebesar 0,5-1,5% dengan penambahan aditif 10% Na2SO4. Proses reduksi terhadap pellet bijih nikel laterit dilakukan dengan menggunakan muffle furnace pada temperatur 950, 1050, 1150ºC selama 60 menit. Selanjutnya dilakukan proses pemisahan magnet (500 gauss) terhadap pellet hasil reduksi untuk memisahkan konsentrat-ferronikel (magnetik) dengan tailing-pengotor (non-magnetik). Bahan baku, pellet hasil reduksi, produk konsentrat dan tailing akan dikarakterisasi/dilakukan pengujian menggunakan XRF, XRD dan SEM-EDS.Hasil yang diperoleh yaitu semakin tinggi temperatur reduksi maka terjadi kenaikan kadar dan perolehan nikel dalam konsentrat. Pada penelitian kali ini didapatkan kondisi optimum pada proses reduksi yaitu dengan temperatur 1150 ºC serta penggunaan 0,5% stoikiometri reduktor arang cangkang sawit (ACS) dan aditif 10% Na2SO4 tanpa penambahan sulfur (0%S), dimana kadar nikel yang diperoleh didalam konsentrat yaitu 2,852% dengan perolehan 73,51%. Saat penambahan 2,68% sulfur, kadar nikel yang didapatkan lebih tinggi yaitu 3% namun perolehan yang didapat yaitu hanya 64,84%. Maka dari itu, penambahan arang cangkang sawit (ACS) dan sulfur harus dilakukan dalam jumlah yang optimum."

"Reduksi selektif merupakan chemical treatment yang mereduksi nikel secara selektif dan mencegah konversi material penganggu. Banyak indikator yang mempengaruhi efektivitas reduksi, salah satunya adalah basisitas. Penelitian ini bertujuan untuk mengetahui dosis reduktor yang tepat berdasarkan stoikiometri dan pengaruh basisitas dengan penambahan CaO berdasarkan basisitas ternary. Bijih nikel laterit jenis limonit, aditif Na2SO4, dan reduktor batu bara bituminous 0,71%S dengan variasi stoikiometri 0,1-0,5 digerus dan dibentuk menjadi pellet berukuran 10-15mm. Proses reduksi dilakukan pada suhu 1150℃ dengan waktu tahan 60 menit di muffle furnace. Selanjutnya dilakukan pemisahan magnetik dan karakterisasi dengan XRF, XRD, OM. Dilakukan pencampuran bahan baku dengan CaO berdasarkan basisitas ternary B 0,1-1,0. Metode dan karakterisasi yang diterapkan sama dengan uji stoikiometri reduktor. Hasil pengujian menunjukkan stoikiometri 0,1 merupakan stoikiometri optimal. Reduktor stoikiometri 0,1 menghasilkan nikel dengan kadar 5,88% dan recovery 88,71% sedangkan besi memiliki kadar 77,06% dan recovery 33,45%. Recovery besi yang rendah mengindikasikan selektifitas reduksi terhadap nikel. Seiring meningkatnya stoikiometri reduktor kadar nikel cenderung mengalami penurunan dan terbentuk senyawa fayalit. Basisitas 0,1 adalah basisitas optimal yang menghasilkan kadar nikel 6,082% dan recovery 88,83%, besi kadar 83,779% dan recovery 40,76%. Penambahan CaO yang berlebih mengakibatkan terbentuknya senyawa kalsium silikat.

---

Selective reduction is a chemical treatment that reduces nickel selectively and prevents transformation of confounding material. Many indicators affect the effectiveness of reduction, one of which is basicity. This study aims to decide the correct reducing agent dosage based on stoichiometry and the effect of basicity with the addition of CaO based on ternary basicity. Limonite nickel laterite ore, Na2SO4, and 0.71% S bituminous coal with stoichiometric variations of 0.1-0.5 are crushed and formed into 10-15mm pellets. The reduction process is carried out at a temperature of 1150 ℃ with a holding time of 60 minutes in the muffle furnace. Then the magnetic separation and characterization with XRF, XRD, OM were carried out. The raw material is mixed with CaO based on ternary basicity B 0.1-1.0. The method and characterization applied are the same as the reductor stoichiometry test. The results show that stoichiometry 0.1 is optimal stoichiometry and produces nickel with a grade of 5.88% and recovery of 88.71% while iron grade is 77.06% and recovery of 33.45% . Low iron recovery indicates nickel selective reduction, as stoichiometry increases the nickel grade tends to decrease and fayalite compounds are formed. Basicity 0.1 is the optimal basicity produces 6.082% nickel grade and 88.83% recovery, 83.777% iron grade and 40.76% recovery. Excessive addition of CaO results in the formation of calcium silicate compounds."

"Penelitian ini menggunakan sampel bijih nikel laterit yang telah dilindi dengan metode pelindian atmosferik di lab Badan Pengkajian dan Penerapan Teknologi (BPPT). Penelitian ini berfokus untuk mengendapkan pengotor pada PLS, terutama pengotor besi, yang bertujuan untuk menghasilkan mixed hydroxide precipitate pada produk akhirnya. Untuk mengendapkan pengotor tersebut, dilakukan proses yang disebut iron removal sebanyak tiga tahap, yaitu dengan secara berurutan dilakukan titrasi reagen kalsium karbonat (CaCO3) dengan kandungan 25%w/w, 15%w/w, dan 12,5%w/w kedalam PLS hingga mencapai pH 2, 3, dan 3,5. Selanjutnya sampel tersebut dipanaskan dengan temperatur 90oC selama 2, 1,5, dan 1 jam. Pada penelitian diakhiri dengan proses titrasi MHP dengan dilakukan titrasi reagen magnesia (MgO) dengan kandungan 20%w/w kedalam PLS hingga mencapai pH 7. Selanjutnya sampel tersebut dipanaskan dengan temperatur 50oC selama 0,5 jam. Secara keseluruhan hasil penelitian, ditemukan bahwa proses iron removal sebanyak 3 tahap mampu mengurangi kadar pengotor, terutama besi, secara signifikan. Kadar besi mampu berkurang dengan %recovery total mencapai 7,46%. Berbeda dengan kadar nikel dan kobalt yang banyak terbuang pada proses iron removal dengan %recovery nikel sebesar 66,63% dan kobalt sebesar 12,51%. Pada hasil proses titrasi MHP menunjukkan hasil yang belum optimal, hal tersebut diindikasikan oleh kadar nikel dan kobal yang tidak bertambah secara signifikan dan kadar pengotor yang masih ada pada MHP. Kadar nikel pada endapan hanya sebesar 19,3%.

---

This research used samples of lateritic nickel ore that had been leached using the atmospheric leaching method at Badan Pengkajian dan Penerapan Teknologi (BPPT) lab. This research focuses on precipitating impurities in PLS, especially iron impurities, which aims to produce mixed hydroxide precipitate in the final product. To precipitate these impurities, a process called iron removal was carried out in three stages, iron removal is carried out in series by titrating calcium carbonate reagent (CaCO3) with a content of 25%w/w, 15%w/w, and 12,5%w/w into PLS until it reaches a pH of 2, 3, and 3,5. Furthermore, the sample was heated to a temperature of 90oC for 2, 1,5, and 1 hours. The research ended with the MHP titration process by titrating magnesia reagent (MgO) with a content of 20% w/w into PLS until it reached pH 7. Then the sample was heated to a temperature of 50oC for 0,5 hour. Overall, the results of the study found that the 3-stage iron removal process was able to significantly reduce the levels of impurities, especially iron. Iron content can be reduced with total % recovery reaching 7,46%. In contrast to the nickel and cobalt content, which was mostly precipitate in the iron removal process, with % nickel recovery of 66.63% and cobalt of 12,51%. The results of the MHP titration process showed results that were not optimal, this was indicated by the levels of nickel and cobalt which did not increase significantly and the levels of impurities that were still present in the MHP. The nickel content in the precipitate is only 19,3%."

"Indonesia merupakan salah satu dari 3 negara yang memiliki deposit bijih nikel laterit terbesar di dunia. Dengan meningkatnya kepentingan nikel pada trend dunia saat ini, Indonesia saat ini direncanakan akan membangun 30 smelter nikel baru hingga tahun 2024. Rencana ini memiliki potensial ekonomi yang tinggi tetapi terdapat satu faktor yang harus diantisipasi, yaitu terak yang akan dihasilkan oleh smelter-smelter nikel yang baru dibuat. Berdasarkan kementerian ESDM pada tahun 2019, tercatat sudah ada 17 juta ton terak yang dapat ditemukan pada kegiatan pengolahan dan pemurnian komoditas nikel. Penelitian ini menjelaskan tentang utilisasi kembali terak feronikel dengan mengekstraksi Fe dan Mg dari terak feronikel menggunakan pelindian asam klorida (HCl) dengan variasi konsentrasi zat pelindi 0,75, 1,125, 1,5, 1,875, dan 2,5 M, variasi temperatur pelindian 32 (temperature ruang), 50, dan 90 oC, serta variasi waktu pelindian 10, 20, 30, 60, dan 90 menit untuk mendapatkan hasil ekstraksi paling efisien. Karakterisasi yang digunakan pada penelitian kali ini adalah ICP-OES untuk sampel filtrat, XRD dan XRF untuk sampel terak feronikel awal dan residu hasil pelindian. Hasil Karakterisasi ICP-OES menunjukkan bahwa hasil ekstraksi Fe dan Mg terbesar berada pada variabel konsentrasi HCl 2,5 M, temperatur pelindian 90 oC, dan waktu pelindian 90 menit dengan hasil sebesar 92,61% untuk Mg dan 89,41% untuk Fe.

---

Indonesia is one of three countries that has the largest lateritic nickel ore deposits in the world. With the increasing importance of nickel in today’s world trends. Indonesia currently planning to build 30 new nickel smelters till 2024. This plan has a vast economic potential but there are one factor that need to be anticipated, namely the slag that will be produced by the new nickel smelter. According to ministry of ESDM in 2019, there are already 17 million tons of slag that can be found in the processing and refining of nickel commodities. This study describes the utilisation of ferronickel slag by extracting Fe and Mg from ferronickel slag using hydrochloric acid (HCl) leaching with variations in the concentration of leachate 0,75, 1,125, 1,5, 1,875, and 2,5 M, variation of leaching temperature 32 (ambient temperature), 50, and 90 oC, as well as variations in leaching time of 10, 20, 30, 60, 90 minutes to get the most efficient extraction results. The characterizations used in this study were ICP-OES for the filtrat sample, XRD and XRF for the initial ferronickel slag sample and leaching residue. The results of the ICP-OES Characterization showed that the largest extraction yields of Fe and Mg were in the variable leachate concentration of 2,5 M, leaching temperature of 90 oC, and leaching time of 90 minutes with yields of 92,61% for Mg and 89,41% for Fe.

"

"Deposit laterite adalah salah satu jenis bijih nikel yang memiliki cadangan mineral nikel terbanyak dan berlimpah di alam. Bijih limonite merupakan salah satu mineral dalam tiga daerah pada deposit laterite dapat menjadi sumber mineral nikel masa depan yang menarik untuk diproduksi menjadi logam nikel, walaupun kadar nikel didalamnya relatif rendah.Pada penelitian ini dilakukan beberapa eksperimen meliputi karakterisasi awal bijih limonite, reduksi roasting dan agitasi leaching menggunakan amonium bikarbonat. Karakterisasi bijih limonite dilakukan menggunakan X-ray Diffraction (XRD) dan X-Ray Flourescence (XRF). Limonite direduksi menggunakan reduktor briket 20% wt pada temperatur 750°C selama 90 menit, hasilnya kemudian diuji menggunakan XRD. Dan yang terakhir proses agitasi leaching pada bijih limonite yang direduksi dan bijih yang tidak direduksi dengan menggunakan larutan amonium bikarbonat pada variasi konsentrasi yaitu 2 M, 1 M, 0.5 M, 0.2 M, 0.1 M, jumlah nikel yang larut kedalam larutan dianalisis menggunakan Atomic Absorbance Spectroscopy (AAS). Penelitian ini dilakukan untuk mengetahui transformasi fasa yang terjadi pada bijih limonite akibat reduksi roasting, recovery nikel pada bijih limonite oleh leaching amonium bikarbonat, dan pengaruh reduksi roasting dan variasi konsentrasi pelarut terhadap recovery nikel.Hasil dari penelitian ini yaitu terjadi transormasi fasa dari geothite menjadi magnetite (Fe3O4) dan FeNi akibat reduksi roasting. Pada proses leaching amonium bikarbonat dengan konsentrasi 1 M recovery nikel yang diperoleh adalah sebesar 1.55 %, sehingga untuk mendapatkan nikel melalui proses ini tidak efektif. Recovery nikel yang didapat pada bijih nikel yang direduksi lebih tinggi 2.7 kali daripada bijih nikel yang tidak direduksi, dan diketahui juga bahwa dengan semakin tinggi konsentrasi pelarut maka recovery nikel akan semakin tinggi dan mencapai nilai optimal pada konsentrasi 1 M.

---

Laterite deposit is a kind of nickel ores that has the greatest of nickel reserves in the world. Limonite ores, which constitutes one of three zones of type lateritic deposits, is attractive future sources of nickel ores for the production of refined nickel, even though their nickel grades are low.At this research, several experiments were conducted including characterization of limonite ore, reduction roasting and agitation leaching by ammonium bicarbonate. Characterization of limonite ore was done using X-ray Diffraction (XRD) and X-Ray Florescences (XRF). Limonite was reduced utilize 20 % wt briquette as a reductant at temperature up to 750oC for 90 minutes, and then the result is tested using XRD. And the last experiment is agitation leaching process of reduced limonite ore and unreduced ore utilize ammonium bicarbonate solution at various concentration which is 2 M, 1 M, 0.5 M, 0.2 M, 0.1 M, the number of nickel dissolution is measured using Atomic Absorbance Spectroscopy (AAS). This research is conducted to observe about the phase transformation of limonite ore as a result of reduction roasting, recovery nickel from limonite ore by ammonium bicarbonate leaching, and then the effects of reduction roasting and the effect of concentration of ammonium bicarbonate on the nickel recovery under atmospheric condition and room temperature.The results of this research show the phase transformation from goethite transformed to magnetite (Fe3O4) and Fe-Ni as a result of reduction roasting. Nickel recovery by leaching using 1 M ammonium bicarbonate is 1.55 % wt, so the nickel extraction using this process is not effective. Nickel recovery obtained from reduced nickel ore is 2.7 times greater than nickel recovery from unreduced ore. Nickel recovery will increase if the concentration of ammonium bicarbonate increases, and achieve optimal value at 1 M."

"Salah satu limbah elektronik dalam jumlah yang besar adalah printed circuit board (PCB). Daur ulang PCB dilakukan menggunakan metode pirolisis dengan tujuan mendekomposisi material organik yang dapat digunakan sebagai reduktor berbasis karbon. Penelitian ini bertujuan untuk mengetahui kemampureduksian dua jenis PCB dan batubara serta konsentrasi optimalnya sebagai agen pereduksi bijih nikel. Penelitian ini menggunakan serbuk PCB, arang PCB, batubara (pembanding) sebagai reduktor dengan variasi konsentrasi 5, 10, dan 15 wt%. Proses karbotermik dilakukan pada atmosfer nitrogen hingga temperatur 1100 °C dengan laju pemanasan 10 °C/menit. Karakterisasi produk karbotermik dilakukan menggunakan TG-DSC, XRD, dan SEM-EDS.Berdasarkan hasil pengujian, senyawa yang umumnya terdapat pada masing-masing sampel dengan reduktor PCB antara lain magnetite, wustite, fayalite, trevorite, ferro nickel, dan nickel oxide. Pada produk karbotermik dengan reduktor serbuk PCB ditemukan elemen tembaga dan timah. Tembaga berada dalam produk karena terbawa dari PCB melalui proses separasi yang tidak optimal. Adanya tembaga pada produk karbotermik dapat disebut juga sebagai pengotor. Untuk mengurangi pengotor pada produk karbotermik, digunakanlah reduktor arang PCB yang menunjukkan hasil separasi tembaga lebih optimal. Di samping itu, penambahan reduktor 5 wt.% arang PCB mengindikasikan hasil yang optimal karena kecenderungannya membuat proses reduksi menjadi lebih sempurna dibandingkan serbuk PCB.

---

One of the largest number of electronic waste is printed circuit boards (PCB). PCB recycling is carried out using the pyrolysis method with the aim of decomposing organic material that can be used as a carbon-based reducing agent. This research aims to determine the ability of two types of PCBs and coal also their optimal concentrations as agents for reducing nickel ore in Indonesia. This research uses PCB powder, PCB charcoal, coal (comparator) as a reducing agent with variations in the concentration of 5, 10, and 15 wt.%. The carbothermic process is carried out in a nitrogen atmosphere up to a temperature of 1100 ° C with a heating rate of 10 ° C / minute. The characterization of carbothermic products was carried out using TG-DSC, XRD, and SEM-EDS. Based on the test results, compounds that are generally present in each sample with a PCB reducing agent include magnetite, wustite, fayalite, trevorite, ferro nickel, and nickel oxide. In addition, found the presence of copper and tin elements in carbothermic products with a PCB powder reductor. The presence of copper in carbothermic products is caused by the carrying of copper from the PCB due to the suboptimal separation process. The presence of copper in carbothermic products can also be called impurity. To reduce impurities in the carbothermic product, a charcoal PCB reductor is used which shows more optimal copper separation results. In addition, the addition of a 5 wt.% PCB char reducing agent indicates optimal results because of its tendency to make the reduction process more perfect than PCB powder.

"