Zandini Nurichi
Studi fabrikasi anodic aluminium oxide (AAO) sebagai cetakan untuk elektrodeposisi logam = Study fabrication of anodic aluminium oxide (AAO)as a templet for metal electrochemical deposition
"Fabricate through-hole porous anodic aluminum oxide (AAO) template were made by a two-step anodization method of an aluminum with purity 99,98% in 0,3 M oxalic acid at 45 V with 360 minutes of second anodization time. The effect of duration time on the second anodizing step, voltage and solution of the electrolyte on the porous oxide layer and influence of the pore opening on the structural as a template were studied in detail. Then, the prepared template was used as a template for fabricated of dense array of Cu by using electrochemical deposition process performed by direct current (DC). The composition of AAO was confirmed by x-ray diffraction (XRD) analyses and for the deposition of Cu were performed by energy dispersive x-ray spectroscopy (EDS). The structural features of nanowire were calculated by scanning electron microscopy (SEM) images and compared with the imaging of AAO template as parameter.
Fabrikasi templet Anodic aluminium Oxide (AAO) sebagai nanopori dilakukan dengan proses anodisasi dengan metode two-step anodization menggunakan alumunium dengan kemurnian 99,98 % pada larutan asam oksalat dengan konsentrasi 0,3 M pada voltase 45 V dan waktu anodisasi kedua sebesar 360 menit. Waktu anodisasi kedua dan voltase serta arus yang digunakan menjadi faktor utama dalam pembentukan ketebalan lapisan oksida dan diameter pori yang dihasilkan. Selain itu, pengaruh konsentrasi sangat berpengaruh dalam ketebalan templet AAO. Aplikasi templet AAO ini digunakan sebagai templet deposisi logam Cu, yaitu dengan cara elektrodeposisi dengan pada arus searah (DC). Digunakan pula X-ray diffraction (XRD) untuk melihat templet AAO dan komposisi Cu pada templet dikarakterisasi dengan energy dispersive x-ray spectroscopy. Untuk melihat morfologi nanopori pada cetakan AAO, dikarakterisasi dengan scanning electron microscopy (SEM)."
Depok: Universitas Indonesia, 2016
S64000
UI - Skripsi Membership  Universitas Indonesia Library
cover
Nadya Aryani Putri
Pengaruh tegangan dan konsentrasi elektrolit H3PO4 pada proses anodisasi terhadap lapisan warna, kekasaran permukaan dan biokompatibilitas material implan Ti-6Al-4V = Effect of voltage and H3PO4 electrolyte concentration during anodizing on the resulting coloured oxide film, surface roughness and biocompatibility of Ti-6Al-4V as an implant material
"Titanium adalah salah satu material yang paling populer untuk digunakan sebagai material implan karena memiliki sifat biokompatibilitas yang baik karena adanya lapisan oksida tipis di permukaannya yang secara spontan terbentuk, dimana lapisan oksida ini menyebabkan Titanium menjadi pasif sehingga tidak mengalami korosi saat diaplikasikan menjadi material implan. Namun material Titanium ini tergolong sebagai material bio-inert, sehingga masih kurang mendukung dalam pertumbuhan dan perkembangan tulang (osseointegrasi) jika dibandingkan dengan material yang tergolong sebagai bio-active. Salah satu cara untuk meningkatkan biokompatibilitas dari Titanium adalah dengan mengasarkan permukaan, karena berdasarkan studi yang telah dilakukan sel cenderung lebih dapat menempel dan berkembang pada material dengan topografi permukaan yang lebih kasar. Anodisasi adalah salah satu cara yang efektif dan mudah untuk meningkatkan kekasaran permukaan Titanium, sekaligus memproduksi lapisan warna yang dapat digunakan untuk identifikasi material implan. Sehingga pada penelitian ini akan dilakukan anodisasi pada Ti-6Al-4V untuk menghasilkan lapisan warna sekaligus mengevaluasi pengaruh parameter yang diaplikasikan terhadap kekasaran permukaan serta biokompatibilitasnya. Anodisasi dilakukan dalam elektrolit H3PO4 dengan konsentrasi 0.5 M dan 1 M menggunakan tegangan 30, 70, dan 120 V untuk mengevaluasi kekasaran permukaan serta efeknya dalam meningkatkan biokompatibilitas Ti-6Al-4V. Selain itu juga dihasilkan Ti-6Al-4V hasil anodisasi pada tegangan 10 hingga 90 V untuk mengetahui pengaruh tegangan terhadap warna yang dihasilkan. Hasil dari anodisasi ini dievaluasi secara makro, mikro menggunakan SEM, komposisi lapisan oksida yang dihasilkan menggunakan EDS, kekasaran permukaannya menggunakan Accretech Surfcom 2900SD3, dan ketahanan goresnya menggunakan scriber yang kemudian diamati dengan mikroskop optik. Hasil yang didapatkan menunjukan kenaikan kekasaran permukaan pada Ti-6Al-4V yang telah dianodisasi, dimana dengan meningkatnya tegangan dan konsentrasi elektrolit yang diaplikasikan maka kekasarannya juga meningkat.. Lalu hasil EDS juga menunjukan adanya inkorporasi ion Fosfor dalam lapisan oksida. Mekanisme terkait hasil yang didapatkan dan pengaruhnya terhadap biokompatibilitas akan lebih lanjut dijelaskan dalam hasil penelitian ini.
Titanium is one of the most popular materials to be used as implant material because it has good biocompatibility due to the presence of a thin oxide layer that spontaneously forms on its surface, this oxide layer causes Titanium to become passive so it does not corrode when being applied as implant material. But Titanium is only classified as a bio-inert material and still less capable in supporting bone growth and its development (osseointegration) when compared to bio-active material. One way to improve the biocompatibility of Titanium is to roughen its surface, because based on studies that have been carried out cells tend to be more adhere and develop in materials with a more rough surface topography. Anodization is one of the effective and easy ways to increase surface roughness of Titanium, while producing a colour oxide film that can be used to identify implant material. Thus, this study will carried out anodization of Ti-6Al-4V to produce a color oxide film while evaluating the effect of parameters applied to its surface roughness and biocompatibility. Anodization was carried out in H3PO4 electrolytes with concentrations of 0.5 M and 1 M using voltages of 30, 70 and 120 V to evaluate surface roughness and its effect in increasing Ti-6Al-4V biocompatibility. Besides that, this study also anodized Ti-6Al-4V at 10 to 90 V to find out the effect of voltage on the color produced. The results of this investigation were evaluated by macro-image, SEM, EDS, Accretech Surfcom 2900SD3, and its scratch resistance using scriber made out of carbide. The results obtained show an increase in surface roughness in anodised Ti-6Al-4V, where as the voltage and electrolyte concentration increase, the surface roughness also increases. Then, the EDS results also show the presence of incorporation of Phosphorus ions in the oxide layer produced by anodization. The mechanism related to the results obtained and its effect on biocompatibility will be further explained in the results of this study."
Depok: Fakultas Teknik Universitas Indonesia, 2019
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Nabila Ramadhanti
Pengaruh tegangan dan konsentrasi elektrolit H2SO4 pada proses anodisasi terhadap lapisan warna, sifat biokompatibilitas, dan kekasaran permukaan material implan Ti-6Al-4V = Effect of voltage and concentration of H2SO4 electrolyte during anodizing on colored oxide film, biocompatibility, and surface roughness of implant Ti-6Al-4V
"ABSTRAK
Kelemahan material implan Ti-6Al-4V adalah bersifat ­bio-inert, sehingga tidak mendukung reaksi jaringan/sel tubuh dengan implan. Penelitian ini bertujuan meningkatkan tendensi pelekatan sel osteoblas pada permukaan implan Ti-6Al-4V melalui modifikasi biokompatibilitas dengan meningkatkan kekasaran permukaan sehingga sel di sekitar implan berkembang. Menggunakan metode anodisasi maka dapat mendukung pula tujuan coloring implan guna memudahkan identifikasi implan ketika pemasangan. Sebelum anodisasi, sampel dipreparasi hingga permukaanya mirror like dan bersih dari kotoran lemak. Anodisasi menggunakan elektrolit H2SO4 0.5 M dan 1 M, pada variasi tegangan 30 V, 50 V, dan 70 V selama 5 menit. Pengaruh tegangan dan konsentrasi elektrolit terhadap kekasaran permukaan diidentifikasi melalui pengujian Surfcom, pengamatan morfologi dan karakterisasi unsur di permukaan dan cross section lapisan TiO2 dengan SEM-EDS, dan kekuatan penempelan lapisan oksida diuji dengan uji ketahanan gores dan diamati dengan OM. Hasil penelitian menunjukkan bahwa semakin tinggi tegangan maka lapisan oksida warna semakin tebal dengan kekasaran permukaan dan ketahanan gores yang lebih tinggi, sehingga hasilnya menunjukkan bahwa kekerasan lapisan oksida meningkat. Fitur kekasaran permukaan didapatkan dari tekstur berupa lembah dan puncak dengan adanya mikropori TiO2 yang terbentuk karena reaksi evolusi oksigen dan inkorporasi ion sulfat dari elektrolit, sehingga biokompatibilitas implan meningkat dengan mekanisme mechanical interlocking antara implan dengan jaringan/sel osteoblas.
ABSTRACT
Ti-6Al-4V implants are bio-inert, it doesnt support tissues or cells reaction with implants. This study was aimed to increase the tendency of attaching osteoblasts to the surface of implants through biocompatibility modification by increased surface roughness, also to get colored implants to facilitate identification of implants when the implants going to be installed, by anodization method. The sample was prepared until had mirror-like surfaces and cleaned from dirt. Anodization used 0.5 M and 1 M H2SO4 electrolytes, 30 V, 50 V, and 70 V for 5 minutes. The effect of voltage and electrolyte concentration on surface roughness was identified through Surfcom, morphological and elemental characterization with SEM-EDS, and the attachment strength of the oxide layer tested by scratch resistance test and observed with OM. The results indicated that the higher the voltage, the color oxide layer gets thicker with higher surface roughness and scratch resistance, so those results indicated that the oxide layers hardness increased. Surface roughness features was obtained by texture of valleys and peaks with TiO2 micropores caused by oxygen evolution reactions and incorporation of sulfate ions from electrolytes, so that implants biocompatibility can be increased by mechanical interlocking mechanism between implants and osteoblast bone cells / tissue."
2019
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Sipayung, Sandhy Putra Pangidoan
Pengaruh penambahan konsentrasi asam sulfat pada larutan elektrolit asam oksalat 0,5 m terhadap ketebalan lapisan oksida hasil anodisasi aluminium foil = Effect of sulfuric acid addition on 0.5 m oxalic acid to the thickness of oxide layer produced by anodization of aluminium foil
"Aluminium merupakan salah satu material logam yang banyak digunakan serta dikembangkan pada berbagai macam aplikasi. Untuk meningkatkan kualitas aluminium, baik sifat fisik maupun mekanisnya, dilakukan beberapa perlakuan terhadap aluminium tersebut. Salah satu proses yang dilakukan adalah dengan rekayasa permukaan melalui proses anodisasi. Dalam proses anodisasi, pada permukaan aluminium akan terbentuk lapisan aluminium oksida yang amat keras dan tahan terhadap korosi.
Saat ini pengembangan proses anodisasi dikembangkan dalam pengetahuan tentang nanoteknologi. Melalui proses anodisasi yang dilakukan diharapkan lapisan yang dihasilkan memiliki kebaikan sifat-sifat mekanis seperti ketebalan, kekerasan, dan karakteristik diameter pori yang sesuai agar nantinya dapat digunakan pada aplikasi nanoteknologi seperti pembuatan carbon nanotube, nanoporous membrane, ataupun quantum dots. Salah satu parameter yang terpenting dan menentukan karakteristik permukaan hasil anodisasi adalah konsentrasi dan jenis elektrolit yang digunakan.
Penelitian kemudian dilakukan untuk memahami pengaruh dari besarnya penambahan konsentrasi elektrolit terhadap karakteristik dari lapisan oksida yang dihasilkan pada permukaan aluminium foil. Pada penelitian ini digunakan elektrolit tetap asam oksalat 0,5 M, serta variabel bebas penambahan asam sulfat 0,12 M, 0,24 M, 0,36 M, dan 0,48 M.
Hasil penelitian kemudian menunjukkan bahwa lapisan oksida yang dihasilkan benar merupakan lapisan Al2O3 dan dengan meningkatnya konsentrasi asam sulfat lapisan oksida yang dihasilkan akan memiliki permukaan yang semakin pekat warna kelabu-nya serta meningkat ketebalannya, hingga mencapai ketebalan tertinggi sekitar 14,51 µm pada konsentrasi 0,36 M namun menurun hingga ketebalan 9,95 µm pada konsentrasi 0,48 M. Kekerasan lapisan yang dihasilkan tidak valid karena alat pengujian yang digunakan kurang mendukung untuk jenis sampel yang digunakan.
Aluminium is one of the most common metal that has been used and developed in wide application. To enhance the quality of aluminium (physical and mechanical properties), some process have been done to the aluminium itself. One of the process is by changing its surface properties with anodizing process. In anodizing process, the aluminium oxide layer would be formed on the surface, and it has great hardness and good corrosion resistance.
At the present, the anodizing process has been developed for the knowledge of nanotechnology. By anodizing, it is hoped that the layer produced would have good mechanical properties like thickness, hardness, and good pore diameter characteristic. Then, with it good properties, it can be used in nanotechnology application like in the manufacturing of carbon nanotube, nanoporous membrane, and quantum dots. One of the most important parameter to the characteristic of the anodizing surface layer is the use of electrolyte.
This experiment was conducted to study the effect of increasing electolyte concentration to the characteristic of the oxide layer that produced at the surface of aluminium foil. The experiment used 0,5 M oxalic acid mixed with 0,12 M, 0,24 M, 0,36 M, and 0,48 M sulfuric acid.
The results showed that the oxide layer was Al2O3 layer. With the increase of sulfuric acid concentration, the oxide layer would be darker in the colour of gray and has some increasing in thickness. The highest thickness was about 14,51 µm in the addition of 0,36 M electrolytic concentration, but it is decreased to the 9,95 µm thickness when the concentration increased up to 0,48 M. The hardness of the layer could not be tested. The hardness testing machine used was not supported the kind of sample that were tested."
Depok: Fakultas Teknik Universitas Indonesia, 2008
S41736
UI - Skripsi Open  Universitas Indonesia Library
cover
Hutasoit, Martino R.
Pengaruh penambahan konsentrasi asam oksalat terhadap ketebalan lapisan oksida pada aluminium foil hasil proses anodisasi = Influence of oxalic acid concentration increment on thickness of oxide layer formed in anodized aluminium foil
"Modifikasi permukaan aluminium secara elektrokimia merupakan suatu proses yang tengah berkembang pesat saat ini. Modifikasi permukaan secara elektrokimia pada awalnya lebih diarahkan pada peningkatan nilai ketahanan korosi, peningkatan kekerasan, dan juga peningkatan nilai estetika. Namun pada perkembangannya, salah satu proses elektrokimia, yaitu anodisasi, telah berkembang menjadi suatu proses modifikasi permukaan yang bertujuan untuk diaplikasikan pada teknologi berbasis nanoteknologi. Pemanfaatan lapisan oksida pada permukaan aluminium hasil proses anodisasi dilakukan dengan memanfaatkan pori (porous anodic alumina) yang terbentuk sebagai template pada pembuatan material yang berbasis pada nano teknologi seperti quantum-dot arrays, photonic crystals, magnetic memory arrays, nanowire dan berbagai alat mikroelektronik lainnya.
Penelitian ini bertujuan untuk mengetahui pengaruh perubahan konsentrasi larutan elektrolit terhadap ketebalan lapisan oksida yang terbentuk pada permukaan aluminium. Penelitian dilakukan dengan menggunakan sampel logam berupa aluminium foil (pure aluminium, 96.49%Al) dengan permukaan anodisasi sebesar 2X2 cm. Larutan elektrolit yang digunakan adalah asam oksalat dengan variasi konsentrasi 0.4 M, 0.5 M, 0.6 M. Tegangan pada proses adalah 32.5 Volt, temperatur dijaga pada rentang 4°C - 16°C, dan diaduk dengan menggunakan magnetic stirrer 500 rpm.
Hasil yang diperoleh melalui penelitian ini adalah bahwa tidak terjadi perubahan warna yang signifikan pada proses anodisasi dengan larutan asam oksalat. Nilai ketebalan lapisan oksida yang terbentuk akan semakin meningkat pada peningkatan konsentrasi asam oksalat. Nilai kekerasan pada sampel aluminium foil tidak dapat dilakukan dengan menggunakan metode microhardness tester.
Modification of aluminum surface with electrochemistry methods are developing rapidly nowadays. This surface modification were initially intended to increase the corrosion resistance, hardness, properties and improving the aesthetic appearance of aluminum. Recently, one of these electrochemistry methods, anodizing, were developed into one of the surface modification that can be applied in nanotechnology. Oxide layer which formed by anodizing process in the aluminum surface could be used as template for microelectronic nanotechnology material such as quantum-dot arrays, photonic crystals, magnetic memory arrays, nanowire because of it porous anodic alumina texture.
This research is conducted to found the effect of electrolyte concentration changes on thickness of oxide layer formed in aluminum surface. This research is carried out with aluminum foil sample (pure aluminum, 96.49% Al) with anodizing surface measured 2X2 cm. Electrolyte which used in this research is oxalic acid with concentration variation 0.4 M, 0.5 M, 0.6 M. This process using 32.5 Volt potential, temperature were kept in range of 4°C - 16°C, and the electrolyte were stirred electromagnetically at 500 rpm.
The result from this research shows that the colour of oxide layer by anodizing of aluminum in oxalic acid solution was transparent. By anodizing in oxalic acid, the thickness of formed oxide layer was dependent with the increase of concentration. Hardness testing on aluminum foil or oxide layer could?nt use to obtain hardness number in this research."
Depok: Fakultas Teknik Universitas Indonesia, 2008
S41633
UI - Skripsi Open  Universitas Indonesia Library
cover
Muhamad Anton Eka Sakti
Studi pengaruh temperatur terhadap pembentukan nano porous aluminium oxide hasil anodisasi aluminium foil = Study of temperature influence on nano porous aluminium oxide formation from anodizing process of aluminum foil
"Saat ini nanoteknologi berkembang dengan sangat pesat karena menghasilkan sifat yang menarik dan berbeda dengan teknologi yang dihasilkan dalam ukuran makroskopis. Produk-produk nanoteknologi berbasis nanostructure materials telah banyak dikaji dan dikembangkan, beberapa diantaranya adalah carbon nanotube, quantum dots, dan nano porous membrane. Sintesis nanostructure materials tersebut dapat dilakukan dengan template nano porous aluminum oxide hasil proses anodisasi. Sifat dan struktur nanoporous aluminum oxide tersebut sangat dipengaruhi oleh beberapa variabel proses anodisasi seperti waktu anodisasi, jenis dan konsentrasi larutan elektrolit, tegangan dan rapat arus, dan juga temperatur.
Pembuatan nano porous aluminum oxide dari aluminium foil untuk aplikasi nanostructure materials telah dilakukan dengan metoda anodisasi. Proses anodisasi dilakukan dengan kenaikan temperatur 10 °C, 20 °C, dan 30 °C dalam campuran larutan asam sulfat 3 M dan asam oksalat 0,5 M, pada kondisi tegangan 15 volt, dan waktu anodisasi 30 menit. Pengamatan diameter pori dilakukan dengan alat FESEM sedangkan pengukuran ketebalan dilakukan dengan alat SEM. Hasil pengamatan menunjukkan bahwa pada kondisi temperatur 10 °C dan 20 °C tidak terbentuk lapisan nano porous alumina sedangkan pada temperatur 30 °C terbentuk nano porous dengan keteraturan near-ordered dengan diameter ratarata 25 nm. Pengujian ketebalan oksida menunjukkan bahwa semakin tinggi temperatur menyebabkan kenaikan ketebalan rata-rata oksida. Ketebalan lapisan oksida mengalami kenaikan berturut-turut 351 nm, 652 nm, dan 770 nm pada temperatur 10 °C, 20 °C, dan 30 °C.
Recently, nanotechnology grows fast because it develops interesting features and different from technology produced on macroscopic scale. Nanotechnology products like nanostructure materials have been studied and developed. Some of them are carbon nanotube, quantum dots, and nano porous membrane. Fabrication of nanostructure materials can be done by template of nano porous aluminum oxide from anodizing process. Properties and structure of the nano porous aluminum oxide was influenced by several variables from anodizing process like time, type and concentration of solution, voltage and current density, and temperature.
Fabrication of nano porous aluminum oxide from aluminum foil for nanostructure materials application have been done from anodizing process in this research. Anodizing process was done on different temperature 10 °C, 20 °C, and 30 °C in mixing solution of sulfuric acid 3 M and oxalic acid 0.5 M, voltage 15 volt, anodizing time 30 minute. Observation of pores diameter was done by FESEM and measurement of oxide thickness was done by SEM. The result shows that there is no formation of porous alumina on temperature 10 °C and 20 °C. In other hand, there is formation of near-ordered nano porous aluminum oxide on temperature 30 °C with 25 nm average diameters. Measurement of thickness show that oxide thickness increases when temperature is raised. Oxide film thickness increases 351 nm, 652 nm, and 770 nm on temperature 10 °C, 20 °C, and 30 °C, respectively."
Depok: Fakultas Teknik Universitas Indonesia, 2008
S41677
UI - Skripsi Open  Universitas Indonesia Library
cover
Annisa Dewi Pangestuti
Studi preparasi TiO2, nanotube yang didekorasi dengan Ag-Cu nanopartikel untuk mendapatkan aktivitas fotokatalitik pada daerah sinar tampak = Study on preparation TiO2 nanotube decorated with Ag-Cu nanopartcles to enhances photocatalytics activity in visible light
"TiO2 merupakan fotokatalis yang telah banyak digunakan sebagai pendegradasi bahan pencemar organik, seperti zat warna. Fotokatalis TiO2 mempunyai nilai energi celah yang sebanding dengan panjang gelombang sinar UV, sehingga fotokatalis ini hanya aktif bila disinari dengan sinar UV dan kurang responsif bila disinari pada panjang gelombang sinar tampak. Dekorasi logam secara fotodeposisi pada permukaan TiO2 dengan memanfaatkan peristiwa Surface Plasmon Resonance (SPR) akan mengaktifkan fotokatalis pada daerah sinar tampak. Absorbsi plasmon logam aktif pada daerah sinar tampak, sehingga bila dikombinasikan dengan TiO2 akan menghasilkan fotokatalis yang dapat digunakan pada daerah sinar tampak. Pada penelitian ini dilakukan preparasi TiO2 nanotube yang didekorasi dengan bimetalik Ag-Cu nanopartikel secara fotodeposisi menggunakan iradiasi sinar UV. TiO2 nanotube dipreparasi menggunakan metode anodisasi secara elektrokimia dilanjutkan dengan kalsinasi selama 3 jam pada suhu 500ºC. Dekorasi logam pada permukaan TiO2 nanotube secara fotodeposisi menggunakan iradiasi sinar UV dilakukan dengan variasi waktu deposisi untuk mendapatkan waktu deposisi terbaik ke permukaan fotokatalis. Ag-Cu/TiO2 yang terbentuk dikarakterisasi menggunakan DRS UV-VIS, FTIR, XRD, FESEM, EDS, dan LSV. Kemudian dilakukan uji fotokatalitik pada daerah sinar tampak dan UV, menunjukkan fotokatalis aktif pada kedua daerah tersebut. Uji fotokatalitik dilakukan dengan melihat penurunan konsentrasi larutan uji yaitu zat warna congo red.
TiO2 is a photocatalyst that has been used for degradation of organic pollutants such as dyes substance. TiO2 photocatalyst has a band gap energy value that equal to UV light`s wavelength. So this photocatalyst is only active in UV light region and less responsive in visible light region. Metal, as nano particle, decoration on TiO2 surface may induce a Surface Plasmon Resonace (SPR) phenomenon and activate the photocatalyst in visible light region. The SPR of metal may active in visible light region, so if we combined metal and TiO2, will eventually create photocatalyst that can be used in visible light region. In this research, TiO2 nanotube were prepared and decorated with bimetallic Ag-Cu nanoparticles, which was prepared by photodeposition method using UV light irradiation. TiO2 nanotube were prepared by anodization method using and followed by calcinations for 3 hours at 500ºC. Metal`s decoration with photodeposition method on TiO2 nanotube surface were prepared by using UV light irradiation at various deposition time to obtain the best deposition time on photocatalyst surface. Ag-Cu/TiO2 photocatalyst were characterized by using DRS UV-VIS, FTIR, XRD, FESEM, EDS, and LSV. Afterward, the prepared photocatalyts were tested under visible light region and UV light region, it showed that the photocatalyst are active in both region."
Depok: Fakultas Matematika Dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
S55168
UI - Skripsi Membership  Universitas Indonesia Library
cover
Adinda Rifany
Studi degradasi methylene blue pada zona katalisis quantum dot sensitized solar cell qdssc termodifikasi menggunakan elektroda counter tio2 nanotubes = Degradation of methylene blue studies on modified quantum dot sensitized solar cell s qdssc catalytic zone using tio2 nanotubes counter electrode
"Pengujian kinerja sistem Quantum Dot Sensitized Solar Cell (QDSSC) termodifikasi dengan menggunakan elektroda counter TiO2 nanotubes untuk mendegradasi Methylene Blue pada zona katalisis telah berhasil dilakukan. Metode Successive Ionic Layer Adsorption and Reaction (SILAR) dengan bantuan ultrasonikasi digunakan untuk melekatkan CdS nanopartikel pada permukaan TiO2 nanotubes yang disintesis dengan metode anodisasi. Karakterisasi dilakukan menggunakan Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), dan Fourier Transform Infra Red (FTIR).
Hasil pengukuran photocurrent menggunakan potensiostat menunjukkan bahwa TiO2 nanotubes aktif pada daerah UV sedangkan TiO2 nanotubes/CdS nanopartikel aktif pada daerah visible. Pada uji performa sistem QDSSC termodifikasi dengan menggunakan elektroda counter TiO2 nanotubes untuk mendegradasi Methylene Blue, diperoleh hasil degradasi optimum sebesar 42,67% pada kondisi zona solar cell disinari lampu visible dan elektroda counter TiO2 nanotubes disinari lampu UV.
A performance testing of modified Quantum Dot Sensitized Solar Cell (QDSSC) employing TiO2 nanotubes as a counter electrode to degrade the Methylene Blue at the catalytic zone has been successfully carried out. Successive Ionic Layer Adsorption and Reaction (SILAR) method with ultrasonication used to attach the CdS nanoparticles on the surface of TiO2 nanotubes were grown on titanium plate by anodization method. Characterization was performed using Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), and Fourier Transform Infra Red (FTIR).
The Results of photocurrent measurements using the potentiostat indicates that TiO2 nanotubes were active in the UV region while TiO2 nanotubes/CdS nanoparticles were active in the visible region. In the modified QDSSC system with employing TiO2 nanotubes as a counter electrode performance test to degrade the Methylene Blue, the results indicate an optimum degradation of 42.67% on the condition solar cell?s zone illuminated by visible light while TiO2 nanotubes counter electrode illuminated by UV light."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2016
S62393
UI - Skripsi Membership  Universitas Indonesia Library
cover
Annis Safitri Febrianti
Preparasi dan karakterisasi tio2 nanotube dengan metode free standing anodisasi serta pengujian self cleaning pada berbagai bahan = Preparation and characterization of tio2 nanotube with free standing anodization method and self cleaning testing on materials
"Pembuatan TiO2 nanotube telah berhasil dilakukan. TiO2 nanotube dihasilkan dari proses anodisasi plat Ti dalam larutan elektrolit garam flourida dalam etilen glikol. Proses anodisasi dilakukan dengan menggunakan potensial 40 V selama 1 jam. TiO2 nanotube yang terbentuk kemudian didispersikan dalam larutan hidrogen peroksida, sehingga membentuk koloid TiO2. Penggunaan koloid TiO2 salah satunya adalah untuk melapisi TiO2 pada permukaan bahan agar memiliki kemampuan self cleaning.
Pelapisan TiO2 pada kain dan kaca telah berhasil dilakukan. Pelapisan TiO2 pada kain diperlukan penambahan spacer kimia dan perendaman kain dalam koloid TiO2. Pada pelapisan permukaan kaca dengan TiO2 dilakukan dengan cara penetesan koloid TiO2 pada permukaan kaca. Permukaan bahan yang telah dilapisi TiO2 dikarakterisasi dengan menggunakan SEM, UV-Vis DRS, FTIR, dan Contact Angle Meter. Setelah terlapisi dengan TiO2 permukaan kain kaca diuji kemampuan self cleaning dengan menggunakan zat warna Rhodamin B.
Telah didapatkan hasil pengujian aktivitas fotokatalis dari kain dan kaca yang telah terlapisi TiO2 dengan menggunakan iluminasi sinar matahari dan sinar UV. Kain yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 60,67% dengan iluminasi sinar UV selama 100 menit dan sebesar 75,63 % dengan iluminasi sinar matahari selama 180 menit. Kaca yang telah terlapis TiO2 dapat mendegradasi zat warna sebesar 53,01% dengan iluminasi sinar UV selama 60 menit, tidak terdeteksi pada 80 dan 100 menit dan sebesar 39,65% dengan iluminasi sinar matahari selama 20 menit, tidak terdeteksi pada 40, 60, 80 dan 100 menit.
Preparation of TiO2 nanotubes have been successfully carried out. The TiO2 nanotubes were produced by anodizing Ti plate in proper electrolyte solution. Anodizing process is performed by using a potential of 40 V for 1 hour. The formed TiO2 nanotubes were then dispersed in the water containing hydrogen peroxide, to obtain TiO2 colloidal. The water base colloidal of TiO2 then was applied to prepare a cloth/fabric and glass those have a self cleaning property. TiO2 coating on the fabric required the addition of a chemical spacer and soaking fabrics in TiO2 suspension.
While surface coating of the glass with TiO2 done by dripping of glass surface in the colloidal of TiO2. The materials those have been coated with TiO2 the were characterized by using SEM, UV-Vis DRS, FTIR, and Contact Angle Meter. In addition the TiO2 coated glass fabric was tested its self-cleaning ability by using Rhodamine B dyes, under illumination of sunlight and UV rays.
The test result of cloth/fabric which has been coated TiO2 showed that under UV light illumination for 100 minutes, it can degrade the dye by 60,67%, while under with sunlight illumination for 180 minutes can degrade up 75,63%. For the glass that has been coated with TiO2, the test showed that, under illumination of UV light for 60 minutes, it can degrade 53,01% of the dye, not detected for 80 and 100 minutes and under illumination of the sunlight for 20 minutes can degrade 39,65% of the dyes, not detected for 40,60,80 and 100 minutes."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2015
S61490
UI - Skripsi Membership  Universitas Indonesia Library
cover
Donnie Indrawan
Pengaruh variasi tegangan dan waktu anodisasi terhadap sifat korosi paduan aluminium 2xxx pada larutan natrium klorida nacl 3,5 = Effect of anodizing voltage and time variations on corrosion behaviour of aluminium alloys 2xxx in 3 5 sodium chloride (nacl) solution
"Aluminium 2024 (Al 2024) merupakan salah satu jenis paduan aluminium komersil dengan tembaga sebagai paduan utamanya. Jenis paduan ini sudah sejak lama digunakan dalam industri otomotif, penerbangan, dan militer. Keberadaan unsur Cu sebagai paduan utama memberikan efek penguatan pada segi mekanis tetapi melemahkan sifat korosinya. Anodisasi merupakan salah satu metode perlindungan aluminium paduan dari korosi menggunakan prinsip elektrokimia yang cepat, sederhana dan ekonomis. Variasi tegangan dan waktu dilakukan untuk melihat pengaruh parameter terhadap ketebalan serta ketahanan korosi Al 2024. Proses anodisasi dilakukan pada larutan H2SO4 30% pada temperatur ruang.
Hasil dari material anodisasi kemudian diuji pada medium korosif NaCl 3,5% selama 6 hari melalui proses immersion test. Ketebalan lapisan oksida paling efektif diperoleh pada anodisasi dengan parameter tegangan 15 V dan waktu 10 menit. Sebagian besar sampel uji menunjukkan trend yang sama dan indikasi terjadinya korosi sumuran (pitting corrosion) disertai munculnya endapan pada permukaan. Perlakuan anodisasi yang memberikan proteksi berupa lapisan oksida dibuktikan dengan kehadiran fasa α-Al2O3 and ɣ-Al2O3 dalam pengujian XRD. Pengamatan SEM dan mikroskop optik memperlihatkan penampakan permukaan Al 2024 setelah 6 hari immersion test pada larutan NaCl 3,5%.
Aluminium Alloy 2024 (Al 2024) is one of commercial alloy with copper as the main alloy. This alloy has been used in many industrial application such as automotive, aerospace, and military. Copper as a major alloying elements gives a mechanical strengthening effect but weaken the corrosion resistance. Anodizing is fast, simple, and economical method to protect aluminium from corrosion with the principal of electrochemical. The variations of anodizing voltage and time have been done with 30% H2SO4 electrolyte at room temperature to analyze its influence on thickness and corrosion behaviour of Al 2024.
Results of anodizing were then tested by immerse the samples in 3,5% NaCl solution for 6 days. The thickness of the oxide layer is most effective with the parameters obtained in anodizing voltage of 15 V and 10 minutes. Most of samples show the similar trend and indications of pitting corrosion along with the presence of deposition on its surface. Anodizing proccess gives the protection layer aluminium oxide which is proved by the presence of α-Al2O3 and ɣ-Al2O3 phase in XRD testing. SEM and optical microscope observation show the surface appearence of Al 2024 after immersion test for 6 days in 3,5% NaCl solution."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2016
S65455
UI - Skripsi Membership  Universitas Indonesia Library