Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
ABSTRAK
Penghubung geser spiral adalah salah satu jenis penghubung geser yang digunakan pada struktur komposit. Pengujian terhadap besarnya kekuatan penghubung geser spiral dilakukan dengan pengujian push out. Dari pengujian tersebut diperoleh grafik hubungan beban-slip yang kemudian dipergunakan sebagai input karakteristik link.. Link adalah elemen konektor dalam SAP2000 yang dipergunakan sebagai konektor pada balok komposit baja-beton. Permodelan dilakukan pada 4 spesimen yang memiliki properti material dan karakteristik link yang berbeda satu sama lain. Hasil menunjukkan bahwa link pada program SAP2000 mampu mengidealisasikan perilaku dari penghubung geser spiral dengan kontrol validasi berupa lendutan hasil pengujian eksperimental yang dilakukan oleh Council of Scientific and Industrial Research Govt. of India New Delhi (1969).

---

ABSTRACT
Spiral shear connector is one of shear connector types used in composite structure. Shear connector capacity tests could be done by push out test. Those test results is a load-slip relationship curve that will be used as an input for link characteristic. Link is a connector element in SAP2000 used as a connector for steel-concrete composite beam. Modelling of steel-concrete composite beam will be done for 4 specimens which has different material properties and link characteristics one anothers. Results show that link connector in SAP2000 could idealize the behaviour of spiral shear connector with validation control model using deflection from experimental test by Council of Scientific and Industrial Research Govt. of India New Delhi (1969).

Abstrak :
[Permintaan terhadap munisi kaliber besar untuk kebutuhan bidang HanKam di dalam negeri sangat tinggi. Oleh karena itu, produsen harus mengimpor bahan baku Cu-Zn 70/30 dari luar negeri dengan harga yang tinggi. Hal ini yang menyebabkan produsen di dalam negeri berlomba untuk menguasai teknologi pembuatan selongsong peluru kaliber besar agar dapat meningkatkan kemandirian di bidang HanKam supaya biaya produksi menjadi lebih rendah. Salah satunya adalah menggunakan proses thixocasting untuk menghasilkan preform/mangkuk Cu-Zn 70/30 dari billet yang dilanjutkan dengan ironing. Keberhasilan proses ironing tergantung dari mampu bentuk dingin material Cu-Zn 70/30 yang digunakan. Oleh karena itu, pada penelitian ini dipelajari bagaimana meningkatkan mampu bentuk dingin dengan metode thermomechanical controlled processed menggunakan teknologi canai hangat. Teknologi canai hangat dilakukan dengan metode double pass reversible sebanyak 25% x 2, 30% x 2, dan 35% x 2 dengan variabel temperatur 300oC, 400oC, dan 500oC. Dengan melakukan pengamatan metalografi baik menggunakan optical microscope maupun FE-SEM, pengujian mekanik baik uji tarik maupun uji keras mikro vickers, dan pengujian mampu bentuk dengan swift test menghasilkan kesimpulan yaitu derajat deformasi aktual canai hangat yang dilakukan tidak sesuai dengan teoritis, namun dari variabel canai hangat yang dilakukan masih bisa dihasilkan sifat mampu bentuk terbaik yaitu pada benda uji yang dideformasi canai hangat di temperatur 500oC dengan derajat deformasi aktual sebesar 38.7%. Sifat mampu bentuk yang tinggi berhubungan dengan sifat mekanik dan struktur mikro yang dihasilkan yaitu ukuran butir halus mencapai 29 μm, berbentuk equiaxed dengan nilai GAR mencapai 1.2, dan nilai kekerasan mikro yang tinggi mencapai 155 HV. Selain itu, kekuatan UTS dan YS tertinggi masing-masing sebesar 533 MPa dan 435 MPa juga didapatkan dari benda uji yang dilakukan parameter deformasi canai hangat di temperatur 500oC dengan derajat deformasi aktual 38.7%. Sedangkan apabila dilihat dari sifat mampu bentuknya maka benda uji yang dideformasi canai hangat pada kondisi parameter ini memiliki nilai koefisien pengerasan regang yang tinggi sebesar 0.00228, nilai anisotropi normal rata-rata yang tinggi sebesar 0.5452, nilai anisotropi planar (Δr) yang rendah yaitu Δr<1 sebesar -0.42, LDR tinggi sebesar 2.625, dan tinggi mangkuk terbesar yaitu 10.31 mm.;The needs of high calibre munition for Indonesian army is very high. To fulfill this strategic requirement, the government has to import this munition even the price is very high. This condition stimulates local industry to obtain the latest technology to produce high calibre munition, especially on casing. It is expected that the price will be lower by producing high calibre munition in Indonesia. On of technology which is used to produce high calibre casing munition is thixocasting to produce pre-formed cup of Cu-Zn from billet then followed by ironing process. The quality result of ironoing process is mostly dependent on cold formability of Cu-Zn 70/30 material used. Therefore, this research focuses to study how to improve cold formability by implemented thermo mechanical controlled processed with warm rolling. Warm rolling is conducted on double pass reversible method with deformation 25% x 2, 30% x 2, and 35% x 2 at various temperatur 300oC, 400oC, and 500oC. The specimens are then examined and tested by several method such as metallography using optical microscopy and FE SEM, tensile test, vickers hardness test and swift test to observed cold formability. The result indicate that the aktual degree of deformasi of warm rolling can not be achieved as planned due to some problems with the equipment. However, the best formability can be measured, where the best formability is obtained for specimens which were warm rolled at temperatur 500oC with aktual deformation 38.7%. Formability is strongly related to the mechanical properties and its microstructure where the best formability obtained for the specimens which has 29 μm grain size in equiaxed form and has GAR value of 1.2, and maximmum hardness value is 155 HV. This specimen has UTS and YS maximum are 533 MPa and 435 MPa, maximum strain hardening coefficient 0.00228, average anisotropic 0.5452, anisotropic planar Δr<1 at -0.42, LDR maximum 2.625, and the height of cup is 10.31 mm., The needs of high calibre munition for Indonesian army is very high. To fulfill this strategic requirement, the government has to import this munition even the price is very high. This condition stimulates local industry to obtain the latest technology to produce high calibre munition, especially on casing. It is expected that the price will be lower by producing high calibre munition in Indonesia. On of technology which is used to produce high calibre casing munition is thixocasting to produce pre-formed cup of Cu-Zn from billet then followed by ironing process. The quality result of ironoing process is mostly dependent on cold formability of Cu-Zn 70/30 material used. Therefore, this research focuses to study how to improve cold formability by implemented thermo mechanical controlled processed with warm rolling. Warm rolling is conducted on double pass reversible method with deformation 25% x 2, 30% x 2, and 35% x 2 at various temperatur 300oC, 400oC, and 500oC. The specimens are then examined and tested by several method such as metallography using optical microscopy and FE SEM, tensile test, vickers hardness test and swift test to observed cold formability. The result indicate that the aktual degree of deformasi of warm rolling can not be achieved as planned due to some problems with the equipment. However, the best formability can be measured, where the best formability is obtained for specimens which were warm rolled at temperatur 500oC with aktual deformation 38.7%. Formability is strongly related to the mechanical properties and its microstructure where the best formability obtained for the specimens which has 29 μm grain size in equiaxed form and has GAR value of 1.2, and maximmum hardness value is 155 HV. This specimen has UTS and YS maximum are 533 MPa and 435 MPa, maximum strain hardening coefficient 0.00228, average anisotropic 0.5452, anisotropic planar Δr<1 at -0.42, LDR maximum 2.625, and the height of cup is 10.31 mm.]

Abstrak :
Perkembangan industri kendaraan bermoror sekarang ini mengalami peningkatan, sejalan dengan itu keburuhan komponen-komponennya akan mengalami peningkatan. Komponen dengan syarat-syarat mekanis yang baik dan biaya produksi yang rendah akan menjanh produk yang kompetitif salah satu yang memenuhi persyaratan tersebut adalah besi tuang nodular (BTN). Ruang lingkup penelitian yang dilakukan adalah menggunakan BTN ripe FCD 50. Untuk mendapatkan peningkatan sifat mekanis yang lebih baik BTN melakukan proses dimenisasi dengan temperarur 950 °C sekema 30 menit dan dilanjutkan dengan proses austemper 275 “C 325 “CZ 375 °C dan -125 “C selama 30 menit. Untuk menganalis hasil proses diakses dilakukan pengrqian lcelmalarz rarilq kekerasan dan pengamatan strukrur mikro. Perlalruan pan-as yang dilakukan pada penelilicm ini diharapkan menghasilkarz ADI 04us!emperea'Ducri1e Iron) yang memilild kombinasi si/'ar me/aanis yang baik, cmtara lain : kekuaran Iarilq Icekerasrm dan keulelmzrgza. Dari hasil penelitian dfperoleh peningkaran sgfat mekanis yaitu kekualan tarik dan kekerasan. Perubahan SVG( mekanis ini fedadi karena admgya perubahan mikrostrukrur karena rerbentuknya .siruktur bainit.

Abstrak :
ABSTRAK
Kebutuhan penghematan energi dunia menuntut untuk melakukan peminimalisasian energi tak terlepas di bidang pengecoran. Penggunaan TWADI (Thin Wall Austempered Ductile Iron) yang didapatkan dari heat treatment TWDI (Thin Wall Ductile Iron) menjadi kandidat yang paling menarik karena ketangguhannya yang sangat tinggi serta biaya lebih murah dan tentunya lebih hemat energi dibandingkan aluminium. Dalam Pemrosesan TWDI menemui masalah yaitu perubahan grafit nodul menjadi flakes atau yang dikenal sebagai skin effect dimana skin akan menurunkan sifat mekanis dari TWDI. Penelitian ini mempelajari pengaruh penambahan kadar nodulizer terhadap terbentuknya skin serta pengaruhnya terhadap sifat mekanis. Skin yang didapat pada penambahan 1,1 % nodulizer dengan tebal 40 µm lebih tipis dibandingkan 1 % nodulizer yang memiliki tebal skin 45 µm. Nilai UTS yang didapat oleh penambahan 1,1% nodulizer yaitu 416,5 MPa, lebih tinggi dibandingkan 1 % nodulizer sebesar 387,54 MPa, dimana hal tersebut sejalan dengan nodularitas yang lebih tinggi dengan penambahan 1,1 % nodulizer. Nilai elongasi kedua sampel tidak mencapai 10 % yang dikarenakan terbentuknya kolumnar karbida yang terbentuk dari berlebihnya kadar mangan pada kedua sampel.

---

ABSTRACT
Recent world energy condition obligates people to reduce quantity of energy useement especially ini casting process. Uses of Thin Wall Austempered Ductile Iron (TWADI), which is a heat treatment material from Thin Wall Ductile Iron (TWDI) , become a best candidate to replace aluminium in industry due to the fact of its high quality toughness and another mechanical properties, with low producing cost and also low energy production. One of the most issue that have been met in processing TWDI is a phenomenon that nodular graphites turn into flakes shape which will decrease large amount of mechanical properties. This research is studying about the enhacement of content nodulizer for reducing skin thickness and also to increase mechanical properties. The addition of 1,1 % nodulizer that obtained shown an effective result with reducing 11 % thickness of skin compared to the thickness of addition 1 % nodulizer. The thickness of skin with addition 1,1% nodulizer is 40 µm, while with addition 1 % nodulizer is 45 µm. The UTS number that has been reached by 1,1 % nodulizer is 416,5 % MPa, which is bigger than the UTS of 1 % nodulizer in the amount of 387,54 MPa which also as a result of grater nodularity of 1,1 % nodulizer. The elongation of both sample have elongation below 10 %, as result of carbides that have been formed in the microstructure, because of excessive number of manganese.

Abstrak :
ABSTRAK
Penambahan partikel nano SiC kedalam matriks Al6061 menghasilkan material komposit dengan kekuatan mekanis yang tinggi namun tetap mampu mempertahankan sifat ulet. Magnesium sebesar 10% Vf juga ditambahkan sebagai agen pembasah agar didapatkan ikatan yang kuat pada daerah antarmuka. Pada penelitian ini digunakan variasi penambahan partikel nano SiC sebesar 0,05%, 0,10%, 0,15%, 0,20% dan 0,30% untuk mengetahui titik optimal penambahan penguat. Hasil dari penelitian ini menunjukkan penambahan partikel nano SiC optimal di komposisi 0,15%, dengan kekuatan tarik 263,43 MPa, presentase elongasi 7,67%, kekerasan 56,5 HRB, dan harga impak sebesar 0,0550 J/mm2. Peningkatan kekuatan mekanis pada komposit dihasilkan dari kehadiran fasa penguat Mg2Si, distribusi partikel nano SiC yang merata, serta pembasahan yang baik antara matriks dan partikel penguat.

---

ABSTRACT
The addition of nano SiC particles to Al6061 matrix has enhancing the mechanical properties of metal matrix composite while the ductility properties still maintained. 10% Vf of magnesium were used as wetting agent to achieve strong interface bonding. In the present work, Al6061 reinforced with various amounts (0,05%, 0,10%, 0,15%, 0,20% and 0,30%) of nano SiC were prepared. Results of this study shows the optimum content of nano SiC in Al6061 matrix were 0,15% Vf, with UTS (Ultimate Tensile Strength) reached 263,43 MPa, 7,67% elongation, hardness up to 56,5 HRB, and 0,0550 J/mm2 impact value. The enhancement of mechanical properties of Al6061/SiC composite were influenced by the presence of Mg2Si phase, good distribution of nano SiC particles, and also good interface bonding between matrix and reinforce. ;