Abstrak :
Dalam tubuh manusia, bahan implan tidak hanya berinteraksi dengan ion anorganik, tetapi juga berinteraksi dengan senyawa organik, terutama protein. Variasi konsentrasi 0 g/L – 0,4 g/L Bovine Serum Albumin (BSA) sebagai protein yang disimulasikan ditambahkan pada larutan Phosphate Buffered Saline (PBS) untuk mengamati perilaku korosi niobium (Nb) melalui pengujian elektrokimia dan karakterisasi permukaan. Berdasarkan analisis kurva polarisasi potensiodinamik, didapatkan nilai potensial korosi yaitu -0,84 V; -0,86 V; -0,87 V; -0,87 V dan rapat arus korosi 4,4 μA cm-2; 2,9 μA cm-2; 1,9 μA cm-2; 1,9 μA cm-2. Nilai potensial dan rapat arus korosi menurun seiring penambahan konsentrasi BSA, menyebabkan laju korosi yang menurun juga. Analisis hasil karakterisasi XRD menunjukkan bahwa fasa oksida dari Nb tidak muncul, karena lapisan oksida yang terbentuk sangat tipis. Pengamatan morfologi permukaan menggunakan Scanning Electron Microscope (SEM) juga didapatkan jumlah kerusakan akibat serangan korosi semakin berkurang seiring penambahan konsentrasi BSA. ......In the human body, the material of the implant is not only interact with the inorganic ions, but also interact with organic compounds, especially proteins. Variation of the concentration of 0 g/L to 0.4 g/L Bovine Serum Albumin (BSA) as a protein that is simulated is added in a solution of Phosphate Buffered Saline (PBS) to observe the corrosion behavior of niobium (Nb), through testing and electrochemical characterization of the surface. Based on the analysis of the curves of potentiodynamic polarization, obtained the value of the corrosion potential that is -0.84 V; -0.86 V; -0.87 V; -0.87 V and current density of corrosion of 4.4 µA cm-2; a 2.9 µA cm-2; the 1.9 µA cm-2; A 1.9 µA cm-2. The value of the potential and current density of corrosion decreases as the addition of the concentration of BSA, causing the corrosion rate decreased as well. Analysis of the results of XRD characterization shows that the phase of the oxide of Nb does not appear, because the oxide layer formed is very thin. The observation of surface morphology using Scanning Electron Microscope (SEM) also showed the amount of damage due to corrosion attack on the wane as the addition of the concentration of BSA.

Abstrak :
Latar Belakang: Penatalaksanaan defek tulang dengan terapi regeneratif seperti penggunaan sekretom berpotensi mengatasi kekurangan, seperti morbiditas donor, dari pencangkokan tulang autologus. Namun hingga saat ini belum ada penelitian yang meneliti perbedaan kemampuan pertumbuhan tulang dari sekretom asal sel punca tali pusat, jaringan lemak, dan sumsum tulang. Metode: Penelitian ini adalah penelitian eksperimental hewan menggunakan 63 tikus, dibagi menjadi 5 kelompok besar, yaitu kelompok sekretom sel punca mesenkimal (SPM) asal tali pusat, jaringan lemak, sumsum tulang, kontrol tanpa tindakan, dan kontrol dengan hidroksiapatit. Setiap tikus dioperasi sesuai dengan tindakannya, kelompok perlakuan diberi perlakuan sekretom yang sesuai dan hidroksiapatit dan kemudian kalus yang terbentuk diperiksa 2 minggu kemudian. Pemeriksaan luaran menggunakan histopatologi, berupa histomorfometri (area penulangan, fibrosis dan kartilago) dan pulasan immunohistokimia Bone Morphonegetic Protein (BMP)-2, dan pemeriksaan Enzyme Linked Immunoabsorbent Assay (ELISA) protein Indian Hedgehog (Ihh). Hasil: Kelompok yang mendapatkan sekretom asal SPM jaringan lemak memiliki area penulangan terbanyak, sedangkan kedua kelompok kontrol terendah (p<0,001), kelompok sekretom asal SPM sumsum tulang memiliki area kartilago terbanyak (p=0,134), dan kedua kelompok kontrol memiliki area fibrosa terbanyak (p=0,198). Skor BMP-2 tertinggi tampak pada kelompok sekretom asal SPM adiposa dan paling rendah pada kelompok kontrol (p<0.001). Kadar protein Ihh secara bermakna paling tinggi pada kelompok sekretom asal SPM sumsum tulang, dan paling rendah pada kelompok kontrol (p<0.001) Kesimpulan: Sekretom memiliki kemampuan osteogenitas, dengan sekretom asal SPM jaringan adiposa yang memiliki kemampuan penulangan tertinggi pada tikus dengan defek tulang kritis, dibandingkan dengan kelompok sekretom lainnya dan kelompok yang tanpa diberikan tindakan ......Introduction: The management of bone defects with regenerative therapy using a secretome, for example, is promising and potentially may outweigh the shortcoming of autologous bone graft therapy such as donor morbidity. However, not many studies have compared the differences in the capabilities of bone growth from secretome derived from umbilical cord, adipose and bone marrow stem cell. Methods: This research is an experimental animal study using 63 rats. A total of 63 rats were divided into 5 major groups (umbilical cord, adipose, bone marrow stem cell secretomes, control without treatment, and control with hydroxyapatite). Each mice was treated accordingly and the harvesting was done after 2 weeks. All samples were examined histopathologically using histomorphometry (ossification, fibrosis, and cartilage area) and Bone Morphogenetic Protein (BMP)-2 immunohistochemistry staining and Enzyme Linked Immunoabsorbent Assay (ELISA) Indian Hedgehog (Ihh) protein Results: The percentage of ossification area was significantly highest in the adipose stem cell secretome group, and the lowest in both control group (p<0.001). The highest percentage of cartilage area was seen in the bone marrow stem cell secretome group (p=0.134) and the highest percentage of fibrous area was seen in both control group (p=0.198). The highest BMP-2 score was seen in the adipose stem cell secretome group and the lowest was in the control group (p<0.001). Level of Ihh protein was significantly highest in the bone marrow stem cell group group and lowest in the control group (p<0.001) Conclusion: Secretome had osteogenic inducing ability, with adipose stem cell-derived secretomes having the highest bone density in mice with critical bone defects, compared to the other secretome groups and the control group.

Abstrak :
ABSTRAK
Manufaktur adalah suatu kegiatan pengolahan bahan baku menjadi produk setengah jadi atau produk jadi. Selain proses manufaktur di dalam perindustrian adalah perancangan produk, seleksi material, distribusi material yang dibutuhkan untuk menciptakan suatu produk. Suatu produk yang dihasilkan dari suatu sistem manufaktur, mempunyai suatu indeks kompleksitas produk yang menggambarkan bahwa produk tersebut dibuat dengan tingkat kompleksitas tertentu. Metode terpilih dalam aplikasi implant miniplate adalah metode kuantitatif dengan gabungan pendekatan analitis, karena dianggap sesuai dan didasarkan pada rincian analisis desain produk, fiturnya, yang disesuaikan dengan proses manufaktur pada kasus terkait, bukan hanya mengandalkan data masa lalu atau pengetahuan tentang seorang estimator. Implant miniplate tergolong baru dan merupakan produk yang pertama dibuat maka metode kualitatif tidak sesuai dengan aplikasi yang dipilih. Indeks kompleksitas proses dari proses manufaktur implant miniplate adalah 101,9 Estimasi biaya proses dari proses manufaktur implant miniplate dengan menggunakan gabungan teknik analitis adalah Rp 139.150,9 Indeks kompleksitas proses dan biaya dari proses manufaktur implant miniplate pada tahap awal desain dapat dilakukan dengan bantuan software Siemens Nx 8 sebagai panduan penentuan waktu dengan parameter yang sama.

---

ABSTRACT
Manufacturing is an activity of processing raw materials into semi finished or finished products. In addition to manufacturing processes within the industry are product design, material selection, material distribution needed to create a product. A product produced from a manufacturing system, has an index of product complexity that illustrates that the product is made with a certain degree of complexity. The preferred method in miniplate implant application is a quantitative method with a combined analytical approach, as it is considered appropriate and based on the details of the product design analysis, its features, tailored to the manufacturing process in the related case, rather than relying only on past data or the knowledge of an estimator. Miniplate implants are new and are the first product created then the qualitative method does not match the selected application. The process complexity index of the miniplate implant manufacturing process is 101.9 The estimated process cost of the miniplate implant manufacturing process using a combined analytical technique is Rp 139.150.9 The process and process complexity index of the miniplate implant manufacturing process in the early stages of the design can be done with the help of Siemens software Nx 8 as a timing guide with the same parameters.

Abstrak :
Reduksi secara tertutup dan fiksasi internal menggunakan miniplate dan screw titanium masih merupakan modalitas terapi yang terbaik untuk fraktur tulang wajah yang displaced dengan gangguan fungsi dan deformitas secara penampilan. Namun, implan maksilofasial yang beredar di Indonesia masih sangat mahal. Untuk itu diperkenalkan miniplate dan screw buatan lokal (UniFIX®) yang lebih murah dan memiliki kualitas yang sama dengan miniplate dan screw yang diimpor. Dilakukan studi eksperimental cross over dengan menggunakan enam belas model tengkorak dari bahan polyurethane yang dipasang implan UniFIX® dan implan impor pada bagian rima orbita inferior oleh pengguna. Dilakukan pencatatan terhadap waktu untuk menyelesaikan pemasangan miniplate dan screw. Setiap pengguna diberikan kuesioner evaluasi terhadap kemudahan penggunaan miniplate dan screw dalam hal kenyamanan saat penggunaan, kecocokan screw dengan screwdriver, pembengkokan plate, dan self-tapping dari screw. Setelah itu, dilakukan penilaian oleh konsultan ahli kraniofasial terhadap stabilitas dan adaptabilitas dari miniplate dan screw yang telah dipasang. Hasil penelitian menunjukkan bahwa miniplate dan screw UniFIX® tidak inferior jika dibandingkan dengan miniplate dan screw impor dalam hal kemudahan penggunaan. Meskipun demikian, karakteristik self-tapping screw UniFIX® dapat ditingkatkan untuk mendapatkan kualitas yang lebih baik. ......Open reduction and internal fixation using miniplate and screw is still the best treatment of displaced facial fracture with functional impairment and cosmetic deformity. However, imported miniplate and screw currently widely used are highly costly. Therefore, a locally-made miniplate and screw (UniFIX®) which is cost-efficient and has the same quality with the imported brand is introduced. This study aims to evaluate the usability of UniFIX® miniplate and screw in comparison with the imported miniplate and screw. Cross over experimental study was conducted with sixteen polyurethane anatomical skull models. Both UniFIX® and imported miniplate and screw were placed on the infraorbital rims by users. Time to complete the placement was recorded. Each user received questionnaire to evaluate the usability of miniplate and screw in terms of operator s comfort, screw fit to screwdriver, plate bending, and self-tapping of the screw. Subsequently, two craniofacial consultants were given scoring sheet to evaluate the stability and the adaptability of each miniplate and screw. The results showed that the usability of UniFIX® miniplate and screw was not inferior compared to the imported brand. Nevertheless, the self-tapping feature of locally-made screw may be improved to produce better quality.

Abstrak :
Magnesium merupakan jenis logam dengan biokompatibilias yang sangat baik dan sifat mekanik yang paling mendekati tulang manusia sehingga cocok untuk digunakan sebagai material implan tulang mampu luruh. Akan tetapi, magnesium memiliki dua permasalahan utama dimana kemampubentukan yang terbatas karena struktur kristal HCP dan ketahanan korosi yang kurang baik. Beberapa metode yang dapat dilakukan untuk mengatasi permasalahan ini adalah dengan penambahan unsur paduan atau dengan diberikan perlakuan termomekanik. Pada penelitian ini, logam magnesium akan diberikan unsur paduan litium (Li) sebanyak 14%wt (persen berat) dan alumunium (Al) sebanyak 1%wt (persen berat). Selain penambahan unsur paduan, paduan magnesium akan diberikan perlakuan termomekanik dimana pada penelitian ini metode yang digunakan adalah pencanaian dingin (cold rolling) dan annealing. Proses cold rolling akan dilakukan dengan tiga variasi persen reduksi sebesar 30%, 60% dan 90% dimana proses annealing dilakukan pada temperatur 300oC dengan waktu tahan satu jam dan laju pemanasan sebesar 5oC/menit. Hasil dari penelitian ini menunjukan bahwa penambahan dari unsur paduan litium (Li) dan alumunium (Al) dapat meningkatkan keuletan dari paduan LA141 karena dihasilkan fasa β-Li dan θ-MgAlLi2. Proses perlakuan panas yang dilakukan dapat menghasilkan fenomena rekristalisasi sehingga dihasilkan mikrostruktur dengan ukuran butir yang lebih seragam. Selain itu, sampel dengan 90% reduksi menghasilkan nilai kekerasan yang tertinggi dengan nilai 76,81 HV untuk sampel non-HT dan 83,58 HV setelah dilakukan perlakuan panas (HT). Berdasarkan hasil penelitian ini maka metode penguatan yang terjadi pada paduan LA141 adalah penguatan dengan bantuan presipitat dan penguatan batas butir. ......Magnesium is a metal with impressive biocompatibility and mechanical properties that are closest to the human bone, making it suitable to be used as a material for biodegradable implants. However, magnesium has two major problems limited formability due to the HCP crystal structure and poor corrosion resistance. Several methods can be used to solve this problem, including adding alloying elements or providing thermomechanical treatment. This research will use 14 wt% lithium (Li) alloy and 1 wt% aluminum (Al) alloy as alloying elements in magnesium metal. Aside from the addition of alloying elements, thermomechanical treatment can help increase the mechanical properties of magnesium alloy. In this research, the methods used are cold rolling and annealing. The cold rolling process will be carried out with three variations of percent reduction as 30%, 60%, and 90% where the annealing process is carried out at 300oC with a one-hour holding time and the heating rate is 5oC/minute. The results of this research indicate that the addition of lithium (Li) and aluminum (Al) alloy elements can increase the ductility of the LA141 alloy because it produces β-Li and θ-MgAlLi2 phases. The heat treatment process can produce a recrystallization phenomenon, resulting in a more uniform grain size (fine grain) microstructure. In addition, samples with 90% reduction produced the highest hardness values, with 76.81 HV for non-HT samples and 83.58 HV after heat treatment. Based on the results of this research, the strengthening methods that occur for LA141 are solid solution strengthening and grain boundary strengthening.

Abstrak :
Tulang tengkorak berfungsi untuk membentuk struktur kepala dan melindungi organ-organ penting di dalamnya. Keretakan tulang tengkorak dapat menyebabkan berbagai gangguan kesehatan, mental, dan bahkan kematian. Polilaktida (PLA) telah menjadi salah satu bahan implan yang paling banyak digunakan untuk keretakan tulang tengkorak. Hal ini dikarenakan PLA memiliki sifat toksisitas yang rendah, biokompatibilitas, dan biodegradabilitas, serta sifat mekanis yang baik. Salah satu turunan dari PLA adalah PLLA (poli(L-laktida)) dengan struktur semi-kristalin yang digunakan pada penelitian ini. PLLA tersebut perlu dilakukan alterasi supaya sifat mekanis dan sifat degradasi sesuai dengan aplikasi pelat fiksasi patah tulang kraniomaksilofasial. Bahan yang ditambahkan dalam matriks PLLA merupakan agar-agar dengan struktur amorf. Penelitian ini bertujuan untuk memperoleh komposisi campuran yang optimal dari variasi campuran agar-agar, yaitu 4%, 8%, dan 12%. Pencampuran menggunakan metode melt-blending yaitu mencampurkan dan mengaduk bahan dalam kondisi lelehan. Sampel dicetak dengan dimensi 80×10×4 mm sesuai standar ISO 178 untuk pengujian kekuatan tekuk polimer. Sampel dilakukan karakterisasi FTIR, TGA, DSC, three-point bending UTM. Hasil karakteriasi dengan FTIR menunjukan terdapat gugus C=O, C-H simetris dan asimetris, C-O, C-COO, serta pergeseran nomor gelombang karena pengaruh suhu yang lebih tinggi. Selain itu, karakteriasi termal TGA menunjukan bahwa campuran dengan konsentrasi agar-agar yang lebih tinggi menunjukkan degradasi yang lebih besar pada suhu campuran 180°C. Suhu yang lebih tinggi juga mempercepat degradasi agar-agar dalam campuran. Hasil DSC menunjukan bahwa semakin tinggi penambahan agar-agar dalam matriks PLLA, maka titik leleh dan %Xc dari PLLA akan semakin menurun. Hal tersebut juga berdampak dengan hasil pengujian sifat mekanis, di mana kekuatan tekuk semakin menurun seiring bertambahnya agar-agar. Nilai dari kekuatan tekuk dan regangan cenderung terus menurun dari 0,87 hingga 0,35 MPa seiring dengan bertambahnya kadar agar-agar dalam matriks PLLA baik untuk T1 (160oC) maupun T2 (180oC). ......The skull functions to form the structure of the head and protect the vital organs within it. Skull fractures can cause various health issues, mental disturbances, and even death. Polylactide (PLA) has become one of the most widely used implant materials for skull fractures due to its biocompatibility, biodegradability, low immunogenicity and toxicity, and good mechanical properties. The main material used is poly(L-lactide) (PLLA) with a semi-crystalline structure. The PLLA needs to be altered to achieve the appropriate mechanical and degradation properties for craniomaxillofacial fracture fixation plates. Agar-agar with an amorphous structure is added to the PLLA matrix. This study aims to obtain the optimal composition from the variations of agar-agar mixtures, namely 4%, 8%, and 12%. The mixing is done using the melt-blending method, which involves mixing and stirring the materials in a molten state. Samples are molded to dimensions of 80×10×4 mm according to ISO 178 standards for polymer bending strength testing. The samples are characterized using FTIR, TGA, DSC, and three-point bending UTM. The FTIR characterization results show the presence of C=O, symmetric and asymmetric C-H, C-O, C-COO groups, and shifts in wave numbers due to the influence of higher temperatures. Additionally, the TGA thermal characterization shows that mixtures with higher agar-agar concentrations exhibit greater degradation at a mixing temperature of 180°C. Higher temperatures also accelerate the degradation of agar-agar in the mixture. DSC tests indicate that the higher the addition of agar-agar in the PLLA matrix, the more the melting point and %Xc of PLLA decrease. This also impacts the mechanical properties test results, where the bending strength decreases with increasing agar-agar content. In the mechanical properties test, the values of bending strength and strain tend to continuously decrease with increasing agar-agar content in the PLLA matrix for both T1 (160oC) and T2 (180oC).

Abstrak :
Saat ini sebagian besar produk implan yang beredar di Indonesia adalah produk impor. Kementerian Kesehatan dan Kementerian Riset,Teknologi,dan Pendidikan Tinggi mendorong produksi produk implan dalam negeri supaya bisa menjadi alternatif produk implan yang selama ini didominasi oleh produk impor. Penelitian ini bertujuan untuk mengetahui kemampuan pullout dan torsi dari screw domestik yang telah dibuat dengan mengacu kepada STM F-543 tentang metode pengetesan untuk screw tulang. Spesifikasi screw yang digunakan dalam penelitian ini adalah screw titanium berukuran M1.5 yang digunakan untuk fiksasi pada area maksilofasial. Performa pullout dicari dengan menggunakan cara eksperimen, finite elemen, dan matematikal. Performa pullout screw domestik kemudian dibandingkan dengan performa screw impor. Sedangkan untuk performa torsi hanya dilakukan dengan cara eksperimen kemudian dibandingkan dengan performa dari screw impor. Hasil yang didapatkan menunjukkan bahwa nilai pull out screw domestik adalah 10,02 N dan screw impor 11,88 N. Nilai screw domestik dibandingkan dengan hasil finite elemen menunjukkan bahwa terjadi error sebesar 10,30. Sedangkan dengan menggunakan analitikal menggunakan chapman yang dimodifikasi didapat nilai sebesar 10,12 N atau error sebesar 1 Dari nilai yang didapat menunjukkan bahwa performa pullout screw domestik lebih buruk dari screw impor. Untuk performa torsi kedua screw menunjukkan performa yang sama baiknya yaitu 0,029 Nm untuk screw domestic dan 0,028 Nm untuk screw impor. Akan tetapi screw domestik membutuhkan gaya yang lebih besar untuk dipasang karena memiliki ujung yang lebih tumpul dari screw impor. ......Currently, the most of implant products that sold at Indonesia are imported product. The Ministry of Health and the Ministry of Research, Technology and Higher Education stimulate domestic implant production as an alternative for imported products that have been dominating domestic market. This study aims to observe domestic titanium screw performance especially from torque and pull out performance based on ASTM F 532 about test method for metallic bone screw. The implant spesification that observed is screw M1.5 for maxillofacial region. Those performances are tested using experimental approach, Finite Element Analysis FEA, and mathematical approach for pull out and only experimental approach for torque test. The results of this study show that the value of pull out from domestic titanium screw UI and commmercial screw respectively are 10,02 N and 11,88 N. This result for domestic screw UI is not slightly different from result which using FEA approach with error 10,30 for pull out. In the other hands, mathematical approach using chapman modified method give error 1 for pull out. The result of this study shows that the value of pull out performance of domestic titanium screw is a little bit worse than imported commercial product. For torwque performance, domestic screw UI has value 0,029 Nm which is as good as commercial screw with value 0,028 Nm. But, domestic screw needs more force to drive the screw into test block because it has duller tip than commercial screw.

Abstrak :
Pelepasan ion Al dan V pada produk komersial implan medis Ti-6Al-4V dapat menyebabkan permasalahan kesehatan karena bersifat toksik. Selain itu modulus elastisitas implan medis Ti-6Al-4V relatif lebih tinggi dari modulus elastisitas tulang manusia, sehingga dapat menyebabkan fenomena stress shielding effect. Oleh sebab itu, dilakukan pergantian unsur Al dan V dengan unsur Nb dan Mo yang tidak bersifat toksik. Kemudian ditambahkan kembali unsur low cost Mn dengan variasi 2%, 4%, dan 6% untuk mensubtitusi unsur Nb dan Mo yang termasuk unsur yang relatif mahal. Unsur Nb, Mo dan Mn merupakan unsur penstabil fasa β yang memiliki nilai modulus elastisitas lebih rendah dibanding Ti-6Al-4V. Fasa β merupakan fasa yang stabil pada suhu tinggi, sehingga dilakukan perlakuan panas untuk menstabilkan fasa ini dengan homogenisasi pada 3, 6 dan 12 jam untuk mengetahui pengaruhnya. Hasil penelitian membuktikan bahwa penambahan komposisi Mn pada paduan menyebabkan penurunan efek toksisitas dengan menstabilkan pembentukan lapisan pasif pada permukaan logam. Lalu, didapatkan perolehan fraksi volume fasa β yang meningkat seiring penambahan komposisi unsur Mn sehingga didapatkan nilai modulus elastisitas yang menurun. Pada proses perlakuan panas, waktu 6 jam merupakan waktu yang optimal untuk memperoleh fasa β yang lebih homogen dengan mengeliminasi sisa fraksi volume fasa α yang ada pada paduan. Dapat disimpulkan penambahan komposisi unsur paduan Mn akan meningkatkan perolehan fasa β dan perlakuan panas perlu dilakukan untuk mendapatkan fasa β yang stabil dan homogen, sehingga didapatkan paduan yang lebih inert dengan nilai modulus elastisitas mendekati nilai modulus elastisistas tulang manusia.

---

The release of Al and V ions in commercial products of Ti-6Al-4V medical implants can cause health problems because they are toxic. In addition, the modulus of elasticity of Ti-6Al-4V medical implants is relatively higher than the modulus of elasticity of human bones, so that it can cause stress shielding effect phenomena. Therefore, al and V elements are replaced with Nb and Mo elements which are not toxic. Then the low cost Mn element was added with variations of 2%, 4%, and 6% to substitute Nb and Mo elements which included relatively expensive elements. Nb, Mo and Mn elements are β phase stabilizers which have a modulus of elasticity lower than Ti-6Al-4V. The β phase is a phase that is stable at high temperatures, so heat treatment is carried out to stabilize this phase by homogenization at 3, 6 and 12 hours to determine its effect. As a result, the addition of the Mn composition to the alloy causes a decrease in the effect of toxicity by stabilizing the formation of a passive layer on the metal surface. Then, the acquisition of β phase volume fraction obtained increases with the addition of the composition of the element Mn so that the modulus of elasticity decreases. In the heat treatment process, 6 hours is the optimal time to obtain a more homogeneous β phase by eliminating the remaining α phase volume fraction present in the alloy. It can be concluded that the addition of Mn alloy element composition will increase β phase acquisition and heat treatment needs to be done to obtain a stable and homogeneous β phase, so that more inert alloys with elastic modulus values ​​are obtained close to the human bone elastic modulus.

Abstrak :
During their service life, most biomaterials and medical implants are vulnerable to tribological damage. In addition, the environments in which they are placed are often corrosive. The combination of triobology, corrosion and the biological environment has been named ‘bio-tribocorrosion’. Understanding this complex phenomenon is critical to improving the design and service life of medical implants. This important book reviews recent key research in this area. After an introduction to the topography of bio-tribocorrosion, Part one discusses different types of tribocorrosion including fatigue-corrosion, fretting-corrosion, wear-corrosion and abrasion-corrosion. The book also discusses the prediction of wear in medical devices. Part two looks at biological effects on tribocorrosion processes, including how proteins interact with material surfaces and the evolution of surface changes due to bio-tribocorrosion resulting from biofilms and passive films. Part three reviews the issue of bio-tribocorrosion in clinical practice, including dental applications and joint replacement as well the use of coatings and test methods for bio-tribocorrosion.

Abstrak :
Commercialisation and growing potential of human ICT implants have generated debate over the ethical, legal and social aspects of the technology, its products and application. Despite stakeholders calling for greater policy and legal certainty within this area, gaps have already begun to emerge between the commercial reality of human ICT implants and the current legal frameworks designed to regulate these products. This book focuses on the latest technological developments and on the legal, social and ethical implications of the use and further application of these technologies.