Abstrak :
Perlakuan panas dilakukan untuk membebaskan tegangan pada baja tahan karat dua fasa SAF 2205 hasil pengerjaan dingin. Perlakuan panas dilakukan pada temperatur 350°C, 450°C, 550°C dengan waktu tahan 10 dan 40 menit. Pengujian korosi erosi pada sampel hasil perlakuan panas dengan menggunakan metode slurry pot dalam larutan HCL 0.3 M dan pasir silika (SiO2) dengan mekanisme tumbukan partikel padat dalam kondisi asam dengan pH 0.85. Hasil pengujian menunjukkan bahwa perlakuan panas yang dilakukan pada baja tahan karat dua fasa SAF 2205 menurunkan tingkat ketahanan korosi erosi pada permukaan logam. ......Heat treatment was conducted for stress relieving in duplex stainless steel SAF 2205 as cold worked. The annealing was conducted in temperature of 350°C, 450°C, 550°C with holding time 10 and 40 minutes. Erosion-corrosion testing was conducted on the heat treated samples with slurry pot method in chloride acid 0.3 M solution and silica sand (SiO2) with solid particles impingement mechanism in acid condition with pH 0.85. The results showed that heat treatment can reduce the resistance of erosion-corrosion on the surface of duplex stainless steel SAF 2205.

Abstrak :
Material baja tahan karat dua fasa SAF 2205 pipa kelas 65 diberikan pengerjaan berupa cold pilgering sehingga mengalami peningkatan kekuatan dan masuk kelas 140. Pada aplikasinya diperlukan pipa dengan spesifikasi kelas 110 atau 125 yang memiliki elongasi lebih tinggi tapi kekuatan yang lebih rendah. Pemberian perlakuan pelunakan pada suhu 350˚C, 450˚C, dan 550˚C dengan waktu tahan 10 dan 20 menit diberikan untuk menghasilkan penurunan kekuatan dan peningkatan elongasi pada material. Penurunan kekuatan dan peningkatan elongasi yang paling optimal terjadi pada suhu 550˚C dengan waktu tahan 10 menit. ......Seamless tube of duplex stainless steel SAF 2205 grade 65 were given cold pilgering treatmentthat increases strength and theirgrade to 140. Some applications requiringseamless tube with specification of grade 110 and 125 that have higher ductility but lower strength. Heat treatment at temperature 350˚C, 450˚C, and 550˚C with holding time 10 and 20 minutes resulted decreasing of yield strength and increasing of elongation of material. Decreasing of yield strength and increasing of elongation reach optimum number at temperature 550˚C with holding time 20 minute.

Abstrak :
[ABSTRAK
Penggunaan baja tahan karat dua fasa austenitik-ferritik (Duplex) UNS32205 telah digunakan secara luas pada berbagai sektor perusahaan, khususnya industri Minyak dan Gas serta industri Petrokimia karena memiliki sifat mekanik dan ketahanan korosi yang sangat baik. Pada penelitian ini,yang diamati adalah pengaruh konsentrasi NaCl pada lingkungan kerja baja tahan karat ini, yang bertujuan mencari konsentrasi yang bersifat paling korosif, dan juga dilakukan pengamatan terhadap pengaruh perubahan Ferrite Content atau nilai rasio dari kedua fasa penyusun baja tahan karat UNS32205 yaitu Austenit dan Ferrit.Pada sampel awal yang diamati tanpa diberikan perlakuan panas apapun memiliki nilai rasio fasa 40% Austenit ? 60 Ferrit. Perubahan Ferrite Content atau perubahan rasio tersebut dilakukan dengan melakukan dua metode pemanasan sampel. Yaitu pemanasan menggunakan maffle furnace pada temperatur 11000C dan ditahan selama 20 menit, dengan hasil rasio 42% Austenit ? 58% Ferrit dan nilai ketahanan korosi paling rendah. Dan juga dilakukan pemanasan dengan cara mengambil sampel pada daerah HAZ dengan temperatur antara 4000C-12000C dan langsung quench, dengan hasil pengamatannya adalah memiliki ketahanan korosi paling tinggi karena memiliki rasio 50,3% Austenit ? 49,7% Ferrit. ABSTRACT
The use of Duplex Stainless Steel UNS32205 has been widely used in various sectors of the company, particularly the oil and Gas industry and the petrochemical industry because it has excellent mechanical properties and corrosion resistance. In this study, the effect of NaCl concentration was observed on the stainless steel working environment, which aims to find the most corrosive nature of concentrations, and also carried out observations on the influence of Ferrite Content or change the value of the ratio of the phase constituent of stainless steel UNS32205 i.e. Austenite and Ferrite. On the initial samples were observed without any heat treatment has given the value of the phase ratio 40% Austenite ? 60 Ferrite. Ferrite Content changes or changes the ratio by doing two sample heating method. I.e. the heating furnace temperature on maffle using 11000C and detained for 20 minutes, with a ratio of 42% Austenit ? 58% Ferrit and lowest corrosion resistance value. And also done warming up by taking samples at the HAZ with temperature between 4000C-12000C and direct quench, with the results of its observations is to have the highest corrosion resistance because it has a ratio of 50.3% Austenite ? 49.7% Ferrite. , The use of Duplex Stainless Steel UNS32205 has been widely used in various sectors of the company, particularly the oil and Gas industry and the petrochemical industry because it has excellent mechanical properties and corrosion resistance. In this study, the effect of NaCl concentration was observed on the stainless steel working environment, which aims to find the most corrosive nature of concentrations, and also carried out observations on the influence of Ferrite Content or change the value of the ratio of the phase constituent of stainless steel UNS32205 i.e. Austenite and Ferrite. On the initial samples were observed without any heat treatment has given the value of the phase ratio 40% Austenite – 60 Ferrite. Ferrite Content changes or changes the ratio by doing two sample heating method. I.e. the heating furnace temperature on maffle using 11000C and detained for 20 minutes, with a ratio of 42% Austenit – 58% Ferrit and lowest corrosion resistance value. And also done warming up by taking samples at the HAZ with temperature between 4000C-12000C and direct quench, with the results of its observations is to have the highest corrosion resistance because it has a ratio of 50.3% Austenite – 49.7% Ferrite. ]

Abstrak :
Penyambungan dua jenis material merupakan salah satu tantangan dalam industri manufaktur. Salah satu aplikasinya dilakukan pada penyambungan antara pipa baja tahan karat Dupleks 2205 disambungkan dengan pelat baja HY80 yang banyak dipakai bahan bakar kapal selam. Pengelasan menggunakan SMAW (Shielded Metal Arc Welding) dilakukan karena merupakan pengelasan yang paling efisien dan baik bagi baja paduan. Setelah proses pengelasan dilakukan pengujian radiografi menggunakan sinar X, pengukuran tegangan sisa dengan hamburan neutron untuk mengukur ketahanan sisa di dalam serta menggunakan hamburan sinar X untuk pengukuran tegangan sisa di permukaan, selanjutnya untuk melengkapi data dilakukan juga pengujian kekerasan material dan pengambilan gambar struktur mikro atau metalografi, serta uji tekuk untuk mengetahui kekuatan hasil lasan. Hasil pengujian menunjukkan bahwa masukan panas yang lebih tinggi selain menghasilkan ukuran butir yang lebih besar, ternyata juga menghasilkan karbida yang lebih banyak sehingga kekerasannya lebih tinggi. Tingginya nilai kekerasan akan memberikan efek terhadap nilai tegangan sisa, kekerasan yang tinggi dihasilkan dari tegangan yang bersifat kompresi, sementara tegangan sisa bersifat tarik akan menghasilkan kekerasan yang rendah.

 

---

Joining two types of material is one of the challenges in the manufacturing industry. One application is carried out on the connection between HY80 steel plates connected with Duplex 2205 stainless steel pipes which are widely used as submarine fuel. Welding using SMAW (Shielded Metal Arc Welding) is done because it is the most efficient and good welding for alloy steel. After the welding process, radiographic testing using X-rays is carried out, the residual stress measured at the surface (using X ray diffraction) and in the middle of the metal (using neutron diffraction), hardness checked, metallography, and buckling test are also done to determine the strength of weld results. The test results show that higher heat input in addition to producing larger grain sizes, it also produces more carbides so that the hardness is higher. The high value of hardness will have an effect on the value of residual stress, high hardness is produced from compressive stress, while the tensile residual stress will produce low hardness.