Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Penelitian adsorben untuk menghasilkan udara dengan kemurnian oksigen tinggi dilakukan menggunakan zeolit alam yang diimpregnasi tembaga oksida. Zeolit alam yang digunakan berasal dari Sidomulyo, South Lampung, Indonesia. Zeolit alam ini termasuk di dalam tipe klinoptilolit, yang biasanya juga disebut Zeolit Alam Lampung ZAL. Teknik pemurnian oksigen yang digunakan adalah Pressure Swing Adsorption PSA dengan tekanan operasi 4 bar. Beberapa variabel divariasikan untuk mendapatkan metode yang paling optimal untuk menghasilkan oksigen, seperti ukuran ZAL 18-100 mesh, persen loading CuO 0-1 -wt, dan konsentrasi asam sulfat 1-3 M. ZAL dikarakterisasi dengan metode BET, SEM-EDX, XRF, XRD, dan FTIR. Oksigen yang diproduksi dianalisis menggunakan GC. Hasil menunjukkan bahwa ZAL dengan ukuran 60-100 mesh dan dipreparasi menggunakan asam sulfat 2 M mempunyai luas permukaan dan volume pori paling baik 64,374 m2/g dan 0,127 cm3/g. ZAL dengan ukuran 35-60 mesh dan dipreparasi menggunakan asam sulfat 1 M mempunyai hasil adsorpsi nitrogen yang paling optimum. Impregnasi oksida tembaga pada ZAL ditemui tidak menambah performa ZAL dalam menyerap nitrogen.

---

Investigation of an adsorbent to produce oxygen enriched air was carried out by using copper oxide CuO which is impregnated to natural zeolite. The natural zeolite used is from Sidomulyo, South Lampung, Indonesia. It is a clinoptilolite zeolite type, namely Zeolit Alam Lampung ZAL. Oxygen purification method applied is Pressure Swing Adsorption PSA technique with operating pressure of 4 bar. Several variables are varied to get the optimum method to produce the best quality of oxygen, such as size of ZAL 18 100 mesh , CuO loading percentage 0 1 wt, and the concentration of sulfuric acid 1 3 M. ZAL will be characterized using BET, SEM EDX, XRF, XRD, and FTIR methods. The oxygen produced will be analysed using GC method. The result showed that ZAL with size 60 100 mesh and prepared using sulfuric acid of 2 M has the best surface area and pore volume to be impregnated, which is 64,374 m2 g dan 0,127 cm3 g, respectively. ZAL with size 35 60 mesh and prepared using sulfuric acid of 1 M has the most optimum trend of nitrogen adsorption. The impregnation of oxide of metal on the adsorbent is found not supporting the adsorbent itself to adsorb nitrogen better.

Abstrak :
Pada penelitian ini dibuat katalis dekomposisi ozon berbasis tembaga oksida CuOx dengan penyangga karbon aktif graanular GAC yang digunakan untuk dekomposisi ozon dalam emisi gas buang industri yang menggunakan ozon. GAC digunakan sebagai penyangga yang diaktivasi terlebih dahulu menggunakan HCl dan NaOH. CuOx diimpregnasi ke permukaan GAC dengan menggunakan prekursor karbonat tembaga CuCO3 dan kemudian dikalsinasi untuk penyingkiran karbon dioksida pada suhu 30°C selama 1 jam. Ukuran karbon aktif dan persentase loading CuOx divariasikan untuk mendapatkan nilai optimum. Morfologi, komposisi, dan fasa kristal dianalisis dengan metode BET, SEM-EDX, FTIR, XRF dan XRD. Dekomposisi ozon dilakukan pada suhu ruang dan tekanan atmosfir menggunakan reaktor unggun tetap. GAC dengan ukuran 60-100 mesh dan persentase loading CuOx 2 -b menunjukkan aktivitas yang tertinggi karena konversi ozon menjadi oksigen dapat mencapai 100. Jumlah CuOx pada penyangga juga menentukan efisiensi katalis karena jumlah CuOx yang sesuai tampaknya dapat mempertahankan morfologi dan fase kristal katalis.

---

In this research, ozone decomposition has been synthesized based on copper oxide CuOx with granular activated carbon GAC as a support catalyst, being used as ozone decomposer in effluent gas emissions of industries that use ozone. As a support, GAC was prepared by using HCl and NaOH. CuOx was impregnated to the surface of activated carbon granulated by using copper carbonate CuCO3 as precursor and then calcined to release carbon dioxide with temperature of 30°C for 1 hour. Size of activated carbon and loading percentage of copper oxide to the support were varied to get the optimum value. The morphology, composition, and crystal phase were characterized by BET, SEM EDX, FTIR, XRF, and XRD method. Ozone decomposition was performed at room temperature and atmospheric pressure using fixed bed reactor. Activated carbon with size 60 100 mesh and 2 w loading percentage showed the highest activity which the ozone conversion to oxygen reached 100 . Amount of CuOx on the support also determine the efficiency of catalyst due to appropriate amount of CuOx probably maintain the morphology and crystal phase of the catalyst.

Abstrak :
Penentuan Kadar Glukosa menggunakan sensor Non-Enzimatik pada saat ini banyak dikembangkan, sebagai alternatif sensor glukosa non-Enzimatik dengan perangkat yang lebih praktis dan sederhana, digunakan Screen Printed Electrode (SPE) sebagai solusinya. Pada penelitian ini, digunakan oksida tembaga sebagai sensor non- Enzimatik yang terdeposit pada permukaan SPE dengan metode elektrodeposisi menggunakan larutan CuSO4 0.01 M dalam 0.1 M H2SO4. Variasi potensial dan waktu deposisi dilakukan untuk mendapatkan deposit CuSPE yang optimum. Uji deteksi glukosa dilakukan pada potensial +0.7 V vs Ag/AgCl. Deposit CuSPE dengan variasi potensial dan waktu -0.4 V selama 300 detik merupakan yang paling optimum karena mempunyai sensitifitas tertinggi sebesar 1063.452 μA mM-1 cm-2, batas deteksi terendah sebesar 0.485 x 10-3 M, dan linearitas paling baik sebesar R20.987. CuSPE optimum digunakan pada sistem alir, didapatkan laju alir optimum 25 mL/menit, konsentrasi NaOH optimum 1 M dilihat dari %RSD sebesar 1.19%. Pada variasi konsentrasi glukosa dihasilkan linearitas sebesar R2 0.982 dengan LOD sebesar 4.273 x 10-3 M. Sensor memiliki repeatabilitas yang baik dengan %RSD = 1.39% (n=10). Deteksi glukosa pada sampel darah dengan batch dan sistem alirmemiliki perbedaan jika dibandingkan dengan hasil deteksi pada glukosameter. ......Determination of glucose concentration using Non-Enzymatic sensor has been developed, as an alternative to Non-Enzymatic glucose sensors with a device that is more practical and simple to use, Screen Printed Electrode (SPE) as a solution. In this study, use of copper oxide as a non-Enzymatic sensors are deposited on the surface of the SPE by electrodeposition method using a solution of 0.01 M CuSO4 in 0.1 M H2SO4. Variations potential and deposition time taken to obtain optimum CuSPE deposit. Glucose detection test conducted on the potential +0.7 V vs Ag/AgCl. Deposit CuSPE which was deposited in -0.4 V for 300 seconds was the optimum because it has the highest sensitivity 1063.452 μ𝐴𝑚𝑀-1𝑐𝑚-2, the lowest limit of detection0.458 x 10-3M, and most excellent linearity R2= 0.987. CuSPE optimum use of the system flow, obtained the optimum flow rate of 25 mL/ min, the concentration of 1 M NaOH optimum views of% RSD for 1.19%. In the glucose concentration variations resulting linearity of R2 0.982 with LOD of 4.273 x 10-3M. The sensor has a good repeatability with% RSD = 1.39% (n=10). Detection of glucose in the blood sample using batch and flow systemhave differences when compared with the results of the detection in glukosameter.