Abstrak :
Preparasi elektroda boron-doped diamond (BDD) termodifikasi platina (Pt) berhasil dilakukan menggunakan teknik wet seeding yang diikut oleh elektrodeposisi. Pt yang terdeposisi pada permukaan BDD dikarakterisasi menggunakan Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) yang menunjukkan %Pt pada permukaan BDD sebesar 1.54 %. Elektroda ini digunakan untuk sensor As³⁺ dan As⁵⁺ menggunakan teknik Anodic Stripping Voltammetry (ASV). Hasil deteksi As³⁺ yang diperoleh pada kondisi optimum pada potensial deposisi -500 mV, waktu deposisi 150 detik dan laju deteksi 200 mV/s menunjukkan bahwa linieritas tinggi (R² = 0.9797) pada rentang konsentrasi 0 sampai 100 ppb dengan limit deteksi (LOD) sebesar 16.50 ppb, sementara hasil deteksi As⁵⁺ dengan pre-treatment menggunakan NaBH4 0.1 M pada kondisi optimum yang sama menunjukkan linieritas yang tinggi (R² = 0.9903) pada rentang konsentrasi 0 sampai 100 ppb memiliki linearitas yang tinggi dengan LOD sebesar 8.19 ppb.

---

Boron-doped diamond electrode modified by platinum was successfully prepared using wet seeding technique followed by electrodeposition. Pt deposited on the surface of BDD characterized using Scanning Electron Microscopy-Energy Dispersive Spectroscopy (SEM-EDS) which shows %Pt on BDD surface are 1.54%.These modified electrode are used for As³⁺ and As⁵⁺ sensors using the Anodic Stripping Voltammetry (ASV) technique. As³⁺ and As⁵⁺ detection results obtained using the same deposition potential of -500 mV, deposition time of 150 s and detection rate of 200 mV/s, with addition of 0.1 M NaBH₄ for As⁵⁺ solution, shows that the calibration in the concentration range 0 to 100 ppb has high linearity (R² = 0.9797 and 0.9903, respectively) with LOD at 16.50 and 8.19 ppb, respectively.

Abstrak :
Anodisasi merupakan salah satu metode pelapisan permukaan yang lazim dipakai khususnya dalam industry otomotif. Lapisan pasif permukaan alumina yang terbentuk tidak hanya tahan terhadap korosi, namun juga mempunyai karakteristik yang unik lainnya. Seperti pada nilai kekerasan dan kemungkinan terbentuknya pori pada permukaan. Nilai lebih dari properties ? properties unik yang dimiliki aluminum ini menyebabkan banyaknya penelitian di bidang aluminum. Pori yang terbentuk di permukaan aluminum dipengaruhi oleh beberapa variabel kerja, antara lain tegangan kerja, temperatur larutan, jenis larutan dan waktu anodisasi. Dengan melakukan perampingan pada proses preparasi serta penyederhanaan sampel uji diharapkan ditemukan suatu batas bawah dalam upaya sintesa pembentukan nano yang tentunya jika berhasil akan memperluas area pengenalan nanoteknologi di masyarakat. Parameter uji dengan variabel tetap pada konsentrasi larutan fosfat dan waktu anodisasi serta variasi pada tegangan dan temperatur dilakukan untuk mengetahui perilaku benda uji dan karakter permukaan Al tersebut. Penggunaan tegangan sebesar 70V pada temperature 22_.

Abstrak :
Pengembangan teknologi proses anodisasi diharapkan dapat memberikan nilai tambah khususnya pada pemanfaatan penggunaan proses anodisasi, penggunaan alumunium foil pada proses anodisasi diharapkan memberikan informasi lebih dalam proses dalam pembentukan lapisan oksida dan pembentukan pori pada permukaan anodisasi. Tujuan dalam penelitian ini untuk mengetahui pengaruh temperatur dan tegangan dalam pembentukan oksida dalam asam fosfat dan asam oksalat, proses anodisasi menggunakan alumunium foil. Alumunium foil yang dianodisasikan dengan perubahan temperature 4°C, 22°C dan 40°C dengan variasi tegangan 10V, 40V,70V,90V dan 120V yang diaduk dengan menggunakan stirrer 200 rpm. Hasil yang diperoleh dalam penelitian ini belum memberikan hasil yang significan pada proses pembentukan pori dan ketebalan oksida, indikasi pembentukan pori diperoleh pada rentang temperature 22°C dan 40°C dengan variasi tegagan 40V, 70V dan 90V. ......Anodisasi technology development process is expected to provide added value particularly in the use of anodisasi process, the use of aluminum foil in the process anodisasi expected to provide more information in the process in the formation of oxide layer on the surface of the anodisasi. The purposed this research to determine the influence of temperature and voltage in the formation of oxide in phosphoric acid and acid oksalat, anodization process using aluminum foil. Aluminum foil with the changes that anodization temperature 4°C, 22°C and 40°C with variations in voltage 10V, 40V, 70V, 90V and 120V are stirred using a stirrer with a 200 rpm. Result of this reseace not yet give significant result for porous formation and thickness oxide layer, but indication porous formation with temperature 22°C and 40°C with range of voltage 40 V,70V and 90V

Abstrak :
Deteksi 5 ion logam berat secara simultan ( Zn2+, Cd2+, Pb2+, Cu2+, dan Hg2+) dilakukan dengan menggunakan metode anodic stripping voltammetry. Elektroda boron-doped diamond digunakan sebagai elektroda kerja, platina sebagai elektroda pendukung, dan Ag/AgCl sebagai elektroda pembanding. Elektrolit yang digunakan adalah 0,1 M HCl. Kondisi optimum diperoleh pada potensial deposisi -1,3V, waktu deposisi 45 detik, scan rate 0,25 V/s. Batas deteksi untuk logam Zn, Cd, Pb, Cu dan Hg masing-masing sebesar 7,42 ppm, 1,48 ppm, 1,48 ppm, 0,74 ppm, dan 0,42 ppm. Kedapatan ulangan yang baik ditunjukkan melalui pengukuran berulang ( 20 kali berturut-turut) dengan nilai RSD sebesar 3,77%, 3,72%, 2,72%, 2,66%, dan 2,59%. masing-masing untuk logam Zn, Cd, Pb, Cu, dan Hg.

---

Simultaneous of 5 heavy metal ions, including Zn2+, Cd2+, Pb2+, Cu2+, and Hg2+ using anodic stripping voltammetry method was examined boron-doped diamond was utilized as working electrode, whereas platinum and Ag/AgCl were used as counter and reference electrodes respectively. A solution of 0.1 M HCl was used as the electrolyte. Optimum condition was obtained at the deposition potential of -1.3 V, deposition time of 45 seconds,and scan rate of 0.25 mV/s. Limits of detection of 7.42 ppm, 1.48 ppm, 1.48 ppm, 0.74 ppm and 0.42 ppm could be achieved for Zn, Cd, Pb, Cu, and Hg ions, respectively. Good reproducibility was shown with RSD values of 3.77%, 3.72%, 2.72%, 2.66%, and 2.59%, respectively for Zn, Cd, Pb, Cu, and Hg ions (n=20).

Abstrak :
Proses anodisasi pada aluminium menghasilkan struktur fenomenal berupa oksida logam yang terkenal dengan istilah Anodic Aluminum Oxide (AAO). AAO sangat diperlukan untuk meningkatkan daya adhesi pada proses pelapisan selanjutnya baik pada aluminium dan paduannya maupun komposit aluminium. Hal tersebut terjadi akibat adanya ikatan saling kunci antara lapisan oksida hasil anodisasi (AAO) dengan pelapis berikutnya. Morfologi pori pada AAO dapat dengan mudah dimodifikasi melalui perubahan parameter anodisasi. Namun, sayangnya penelitian-penelitian sebelumnya belum menyediakan informasi apapun mengenai pengontrolan diameter pori. Sedangkan seperti yang kita ketahui bahwa perbedaan aplikasi yang diinginkan membutuhkan diameter pori yang berbeda pula. Oleh karena itu guna mendapatkan diameter pori dengan ukuran tertentu maka pemilihan parameter proses anodisasi yang tepat sangatlah penting. Untuk memenuhi kebutuhan tersebut, dalam penelitian ini akan dihasilkan persamaan empiris yang dapat memprediksi ukuran diameter dan densitas pori AAO yang terbentuk hasil anodisasi dengan berbagai parameter tertentu agar dapat digunakan dalam aplikasi yang sesuai. Tujuan utama penelitian ini adalah pengembangan persamaan empiris yang menggambarkan hubungan konsentrasi oksalat, tegangan dan waktu anodisasi terhadap diameter pori. Namun penelitian ini juga menganalisis mekanisme pembentukan, karakteristik, dan ketahanan korosi lapisan terintegrasi pada Al7075/SiC. Serta menganalisis pengaruh konsentrasi, temperatur, dan resistivitas larutan elektrolit, dan tegangan anodisasi terhadap diameter dan densitas pori AAO pada aluminium foil. Proses anodisasi Al7075/SiC dilakukan dalam larutan asam sulfat 16% H2SO4 dengan rapat arus 15, 20, 25 mA/cm2 pada 25, 0, -25oC selama 30 menit. Selanjutnya dilakukan proses sealing dalam larutan CeCl3.6H2O + H2O2 pada temperatur ruang dengan pH 9 selama 30 menit. Proses anodisasi pada aluminium foil dilakukan dalam larutan 3 M H2SO4 + 0,5 M; 0,7 M; dan 0,9 M H2C2O4, dan 0,3; 0,5; 0,7 M H2C2O4 selama 40-60 menit. Proses anodisasi dilakukan pada tegangan konstan 35, 40, dan 45 V untuk larutan asam oksalat dan 15 V untuk larutan campuran. Pengamatan dan evaluasi morfologi lapisan pori hasil anodisasi dilakukan menggunakan alat FE-SEM (Field Emission Scanning Electron Microscope), ketahanan korosi material diinvestigasi menggunakan pengujian polarisasi dan EIS, sedangkan analisa kualitatif terhadap morfologi pori (diameter dan densitas) pada AAO menggunakan perangkat lunak ImagePro. Pengembangan persamaan empiris menggunakan metode derajat terkecil dan permukaan respon. Proses terintegrasi yang diaplikasikan pada komposit Al7075/SiC pada temperatur anodisasi 0 oC menghasilkan terbentuknya deposit bulat kaya cerium dengan diameter 64 nm ( 3 nm) yang menutupi seluruh permukaan lapisan oksida dan rongga secara efektif. Proteksi terintegrasi anodisasi dan pelapisan cerium meningkatkan ketahanan korosi hingga 4 order perbesaran dibandingkan tanpa perlindungan akibat terjadinya ikatan saling kunci antara kedua lapisan tersebut. Peningkatan konsentrasi larutan elektrolit asam oksalat, temperatur, tegangan dan waktu celup anodisasi dalam larutan 0,3; 0,5; dan 0,7 M mengakibatkan peningkatan diameter pori permukaan pada AAO. Sedangkan, penambahan asam sulfat dalam asam oksalat menghasilkan pori dengan morfologi diameter pori yang jauh lebih halus dan densitas pori yang jauh lebih besar. Secara umum, densitas pori hanya tergantung pada diameter pori hasil anodisasi, dimana peningkatan diameter pori menghasilkan densitas pori yang semakin menurun. Persamaan empiris hubungan antara tiga faktor anodisasi (konsentrasi asam oksalat, tegangan, dan waktu anodisasi) dengan diameter pori hasil dari penelitian ini adalah : Dp = 0,140625 MVt + 0,33125 MV ? 523542 Mt + 35,64583 M ? 0,04006 Vt + 0,685764 V +1,792431 t ? 42,5053 (derajat terkecil) dan Dp = 33,3 ? 236,3 M ? 1,453 V + 0,3942 t + 7,60 MV (metode derajat satu) ......Anodizing process in aluminum produces a phenomenal structure in form of metal oxide which is known as Anodic Aluminum Oxide (AAO). AAOis a very useful morfology to improve the adhesion properties for further coating in aluminum alloy and composite aluminum. This phenomenon is related to the presence of interlock bond between AAO and the next layer. The AAO morphology can be modified simply by varying anodizing parameters. Therefore, selecting appropriate parameters plays an important role in order to obtain the desired pore size. Unfortunately, the preliminary studies did not provide any information on controlling the pore size and density (through increasing/decreasing the concentration of sulfuric acids, voltage, and duration of anodizing to determine pore diameter and density). For that purpose, in this research some empirical models were built to predict the pore size produced by anodizing process in various parameters. The grand design if this research aims to develop empirical equations which predict the relationship between oxalic acid concentration, anodizing voltage and time to the pore diameter. However, this research also aims to analyze the formation mechanism and of the integrated layer on Al7075/SiC, as well as the enhancement of corrosion resistance resulted from the integrated layer. Moreover, the influence of various anodizing parameters, i.e. resistivity, concentration, temperature, and type of electrolyte on pore characteristics of AAOis also conducted in this study. Anodizing process of Al7075/SiC was conducted in 16% H2SO4 solution in current densities 15, 20, 25 mA/cm2 at25, 0, -25oC for 30 minutes. Subsequently, cerium sealing process was carried out in CeCl3.6H2O+H2O2 at room temperature and pH 9 for 30 minutes. Anodizing of aluminum foil were carried out in 0,3; 0,5; 0,7M H2C2O4 solution and a mixture solution of 0.5M, 0.7M, and 0.9M H2C2O4 and 3M H2SO4 for 40-60 minutes. Anodizing processes were performed under potentiostatic conditions with constant potentials of 35, 40, and 45V for oxalic solution and 15 V for a mixture solution. Morphology of AAO layer observations were performed using field emission scanning electron microscopy (FE-SEM) FEI Inspect F50, while the corrosion resistance of materials were investigated by means of polarization and EIS, and qualitative analysis of pore characteristics (pore diameters and densities) accomplised by ImagePro software. The development of empirical equations using least square and response surface methods Integrated protection by conducting anodization at 0oC prior to cerium sealing in Al7075/SiC leads tothe formation of cerium spherical deposit in the diameter of 64 nm ( 3nm) which effectively covered most of the surface of oxide film as well as cavity. Moreover, this integrated protection enhanced four orders magnification of corrosion resistance than that of bare composite due to interlock bonding between the layers. The increasing of electrolyte concentration and temperature, as well as voltage and duration of anodizing in 0.3; 0.5; dan 0.7 M oxalic acid leads to the increasing of pore diameter in AAO surface. While, the addition of sulfuric acid in oxalic acid provides much smaller pore diameters and higher pore densities at lower voltages than single electrolyte of oxalic acid. In general, pore density is only dependent on pore diameter, which decreases with the increases of pore diameter. The empirical equations built in this research are : Dp = 0,140625 MVt + 0,33125 MV ? 523542 Mt + 35,64583 M ? 0,04006 Vt + 0,685764 V +1,792431 t ? 42,5053 (least square) and Dp = 33,3 ? 236,3 M ? 1,453 V + 0,3942 t + 7,60 MV (first order model)

Abstrak :
Penumbuhan lapisan porous anodik aluminium oksida (PAAO) di atas substrat aluminium tubular merupakan suatu tantangan karena struktur pori tumbuh kurang teratur, kurang homogen, dan lapisannya rentan mengalami retakan. Penelitian ini bertujuan untuk meningkatkan ketahanan terhadap retakan lapisan PAAO yang ditumbuhkan di atas substrat aluminium tubular dengan penambahan etilen glikol (EG) dan pemanasan. Lapisan PAAO diperoleh melalui anodisasi aluminium dalam larutan 0,3 M asam sulfat dan oksalat pada suhu 10°C selama 4 jam. EG ditambahkan dengan variasi konsentrasi 0, 5, 10 dan15 vol%. Morfologi lapisan PAAO dikarakterisasi dengan FESEM dan struktur kristalnya dianalisis dengan XRD. Jumlah retakan berkurang dari 4,04x10-4/ µm2 menjadi 2,24x10-5/ µm2 retakan dan 2,47x10-4/µm2 menjadi 6,73x10-5/µm2 retakan dalam asam sulfat dan asam oksalat dengan penambahan 0-15 vol% EG. Rentang diameter pori sebelum dilepas dari substrat adalah 10-14 nm dan setelah dilepas dari substrat dan dietsa kimia menjadi 14-24 nm. EG berperan dalam menjaga stabilitas suhu selama anodisasi, mengurangi kerapatan arus dan meningkatkan viskositas larutan sehingga mampu mengurangi populasi dan lebar retakan. Pemanasan lapisan PAAO dari 1000-1250 oC menyebabkan perubahan fasa dari fasa amorf menjadi fasa kristal g, d, dan ὰ Al2O3. ......The growth of the porous anodic aluminum oxide (PAAO) layer on a tubular aluminum substrate is challenging because the pore structure grows less orderly, less homogeneous, and layers are prone to cracking. This study aims to improve resistance to cracking of PAAO layers grown on tubular aluminum substrates by adding ethylene glycol (EG) and heating. The PAAO layer was obtained by anodizing aluminum in a 0.3 M sulfuric and oxalic acid at 10 °C for 4 hours. The EG was added at various concentrations of 0, 5, 10, and 15 vol%. The morphology of PAAO layers was characterized by FESEM and the crystal structure was analyzed by XRD. The population of cracks decreased from 4.04x10-4/µm2 to 2.24x10-5/µm2 and 2.47x10-4/µm2 to 6.73x10-5/µm2 cracks in sulfuric and oxalic acid by addition EG 0-15 vol%. The pore diameter range before being removed from the substrate was 10-14 nm and after being removed from the substrate and chemically etched it was 14-24 nm. EG plays a role in maintaining temperature stability during anodization, reducing current, and increasing viscosity of solution to reduce population and width of the crack. Heating PAAO layer from 1000-1250 oC causes the phase change from amorphous to crystalline g-, d-, and ὰ-Al2O3.

Abstrak :
Aluminium merupakan salah satu material logam yang banyak digunakan, diaplikasikan dan dikembangkan pada berbagai macam produk otomotif, contohnya piston. Piston sebagai salah satu komponen otomotif yang cukup penting pada mesin kendaraan bermotor memerlukan sifat ketahanan abrasi dan ketahanan korosi yang baik. Salah satu metode perlakuan akhir yang dapat digunakan untuk mendapatkan sifat ketahanan abrasi dan korosi yang baik adalah anodisasi. Dalam proses anodisasi ini permukaan aluminium akan diubah menjadi lapisan aluminium oksida yang amat keras dan tahan korosi. Salah satu parameter terpenting yang amat menentukan karakteristik permukaan hasil anodisasi adalah potensial. Penelitian kemudian dilakukan untuk memahami pengaruh dari besarnya potensial anodisasi terhadap kekerasan dan ketebalan dari lapisan oksida yang dihasilkan pada permukaan logam paduan aluminium silikon. Variabel yang digunakan dalam penelitian kali ini adalah variasi besarnya tegangan yaitu 9 Volt, 11 Volt, 13 Volt dan 15 Volt. Hasil penelitian kemudian menunjukkan bahwa dengan meningkatnya tegangan anodisasi (yaitu dari 9, 11, 13 dan 15 Volt) maka kekerasan lapisan oksida rata-rata yang ditunjukkan dari hasil uji kekerasan mikro akan semakin meningkat pula. Ynitudari 109 uHV pada potensial 9 Volt, 116 uHVpada potensial 11 Volt, 136 fiHV potensial 13 V, hingga 153 uHV pada potensial 15 Volt. Peningkatan juga dialami oleh ketebalan lapisan oksida rata-rata yang dihasilkan, yaitu sebesar 13 _m pada potensial anodisasi 9 Volt, 15 _m pada potensial anodisasi 11 Volt, 17 _rn pada potensial anodisasi 13 Volt, hingga 19 _m pada potensial anodisasi 15 Volt.

Abstrak :
Fabricate through-hole porous anodic aluminum oxide (AAO) template were made by a two-step anodization method of an aluminum with purity 99,98% in 0,3 M oxalic acid at 45 V with 360 minutes of second anodization time. The effect of duration time on the second anodizing step, voltage and solution of the electrolyte on the porous oxide layer and influence of the pore opening on the structural as a template were studied in detail. Then, the prepared template was used as a template for fabricated of dense array of Cu by using electrochemical deposition process performed by direct current (DC). The composition of AAO was confirmed by x-ray diffraction (XRD) analyses and for the deposition of Cu were performed by energy dispersive x-ray spectroscopy (EDS). The structural features of nanowire were calculated by scanning electron microscopy (SEM) images and compared with the imaging of AAO template as parameter.

---

Fabrikasi templet Anodic aluminium Oxide (AAO) sebagai nanopori dilakukan dengan proses anodisasi dengan metode two-step anodization menggunakan alumunium dengan kemurnian 99,98 % pada larutan asam oksalat dengan konsentrasi 0,3 M pada voltase 45 V dan waktu anodisasi kedua sebesar 360 menit. Waktu anodisasi kedua dan voltase serta arus yang digunakan menjadi faktor utama dalam pembentukan ketebalan lapisan oksida dan diameter pori yang dihasilkan. Selain itu, pengaruh konsentrasi sangat berpengaruh dalam ketebalan templet AAO. Aplikasi templet AAO ini digunakan sebagai templet deposisi logam Cu, yaitu dengan cara elektrodeposisi dengan pada arus searah (DC). Digunakan pula X-ray diffraction (XRD) untuk melihat templet AAO dan komposisi Cu pada templet dikarakterisasi dengan energy dispersive x-ray spectroscopy. Untuk melihat morfologi nanopori pada cetakan AAO, dikarakterisasi dengan scanning electron microscopy (SEM).

Abstrak :
Titanium adalah salah satu material yang paling populer untuk digunakan sebagai material implan karena memiliki sifat biokompatibilitas yang baik karena adanya lapisan oksida tipis di permukaannya yang secara spontan terbentuk, dimana lapisan oksida ini menyebabkan Titanium menjadi pasif sehingga tidak mengalami korosi saat diaplikasikan menjadi material implan. Namun material Titanium ini tergolong sebagai material bio-inert, sehingga masih kurang mendukung dalam pertumbuhan dan perkembangan tulang (osseointegrasi) jika dibandingkan dengan material yang tergolong sebagai bio-active. Salah satu cara untuk meningkatkan biokompatibilitas dari Titanium adalah dengan mengasarkan permukaan, karena berdasarkan studi yang telah dilakukan sel cenderung lebih dapat menempel dan berkembang pada material dengan topografi permukaan yang lebih kasar. Anodisasi adalah salah satu cara yang efektif dan mudah untuk meningkatkan kekasaran permukaan Titanium, sekaligus memproduksi lapisan warna yang dapat digunakan untuk identifikasi material implan. Sehingga pada penelitian ini akan dilakukan anodisasi pada Ti-6Al-4V untuk menghasilkan lapisan warna sekaligus mengevaluasi pengaruh parameter yang diaplikasikan terhadap kekasaran permukaan serta biokompatibilitasnya. Anodisasi dilakukan dalam elektrolit H₃PO₄ dengan konsentrasi 0.5 M dan 1 M menggunakan tegangan 30, 70, dan 120 V untuk mengevaluasi kekasaran permukaan serta efeknya dalam meningkatkan biokompatibilitas Ti-6Al-4V. Selain itu juga dihasilkan Ti-6Al-4V hasil anodisasi pada tegangan 10 hingga 90 V untuk mengetahui pengaruh tegangan terhadap warna yang dihasilkan. Hasil dari anodisasi ini dievaluasi secara makro, mikro menggunakan SEM, komposisi lapisan oksida yang dihasilkan menggunakan EDS, kekasaran permukaannya menggunakan Accretech Surfcom 2900SD3, dan ketahanan goresnya menggunakan scriber yang kemudian diamati dengan mikroskop optik. Hasil yang didapatkan menunjukan kenaikan kekasaran permukaan pada Ti-6Al-4V yang telah dianodisasi, dimana dengan meningkatnya tegangan dan konsentrasi elektrolit yang diaplikasikan maka kekasarannya juga meningkat.. Lalu hasil EDS juga menunjukan adanya inkorporasi ion Fosfor dalam lapisan oksida. Mekanisme terkait hasil yang didapatkan dan pengaruhnya terhadap biokompatibilitas akan lebih lanjut dijelaskan dalam hasil penelitian ini. ......Titanium is one of the most popular materials to be used as implant material because it has good biocompatibility due to the presence of a thin oxide layer that spontaneously forms on its surface, this oxide layer causes Titanium to become passive so it does not corrode when being applied as implant material. But Titanium is only classified as a bio-inert material and still less capable in supporting bone growth and its development (osseointegration) when compared to bio-active material. One way to improve the biocompatibility of Titanium is to roughen its surface, because based on studies that have been carried out cells tend to be more adhere and develop in materials with a more rough surface topography. Anodization is one of the effective and easy ways to increase surface roughness of Titanium, while producing a colour oxide film that can be used to identify implant material. Thus, this study will carried out anodization of Ti-6Al-4V to produce a color oxide film while evaluating the effect of parameters applied to its surface roughness and biocompatibility. Anodization was carried out in H₃PO₄ electrolytes with concentrations of 0.5 M and 1 M using voltages of 30, 70 and 120 V to evaluate surface roughness and its effect in increasing Ti-6Al-4V biocompatibility. Besides that, this study also anodized Ti-6Al-4V at 10 to 90 V to find out the effect of voltage on the color produced. The results of this investigation were evaluated by macro-image, SEM, EDS, Accretech Surfcom 2900SD3, and its scratch resistance using scriber made out of carbide. The results obtained show an increase in surface roughness in anodised Ti-6Al-4V, where as the voltage and electrolyte concentration increase, the surface roughness also increases. Then, the EDS results also show the presence of incorporation of Phosphorus ions in the oxide layer produced by anodization. The mechanism related to the results obtained and its effect on biocompatibility will be further explained in the results of this study.