Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Low carbon steel (AISI 1005) was coated by hot-dipping into a molten Al-10% Si bath at 700 °C for 18s. After hot-dipping treatment, the coating layers consisted of Al, Si, FeAl3,τ5-Fe2Al8Si, and Fe2Al5. The bare steel and the aluminized steel were isothermally oxidized at 700 °C in ethanol combustion product at atmospheric pressure for 49 h. The aluminized steel shows good performance in high temperature oxidation because the formation of Al2O3layer on the coating surface. The growth of iron oxide nodules on the surface coating was accelerated by rapid outward diffusion of Fe-ions due to the presence of H2O-vapour generated by ethanol combustion. Thus, the oxidation rate of aluminized steel increased, resulting in a substantial mass-gain as the oxidation time increased. After longer exposure, the τ1-(Al,Si) 5Fe3 phase was completely transformed to the FeAl in the outer layer. The FeAl formed near the steel substrate was due to Fe-atoms diffusing into the Fe2Al5 layer when the time and temperature increased.

Abstrak :
Pemanfaatan Gas CO2 Hasil Pembakaran Tempurung Kelapa untuk Produksi Natrium Karbonat. Penelitian ini dilakukan untuk mempelajari pemanfaatan gas CO2 hasil pembakaran tempurung kelapa menjadi natrium karbonat (Na2CO3) dengan mereaksikan gas CO2 dengan larutan NaOH dengan konsentrasi 6.5, 7.0, 7.5 dan 8.0 M. Tujuan utama penelitian adalah mengkaji potensi metode diusulkan sebagai cara mitigasi gas CO2 yang dihasilkan dari industri arang tempurung kelapa. Padatan natrium karbonat yang dihasilkan selanjutnya dikeringkan dalam oven pada suhu 110 oC, lalu dikarakterisasi dengan FTIR, XRD, dan SEM/EDS. Analisis termal menggunakan metode DTA/TGA dilakukan untuk mempelajari karakteristik termal pembentukan Na2CO3. Hasil penelitian menunjukkan bahwa konsentrasi NaOH mempengaruhi massa natrium karbonat yang dihasilkan, hasil tertinggi sebesar 190,6 g diperoleh dari penggunaan NaOH dengan konsentrasi 7,0 M. Karakterisasi dengan FTIR menunjukkan dengan jelas pembentukan natrium karbonat, yang ditandai dengan pita serapan gugus fungsi yang berkaitan dengan natrium karbonat, yakni gugus O-H, C-O, C=O, dan CO3-2. Hasil FTIR juga menunjukkan adanya gugus fungsi C-S, yang kemungkinan besar karena adanya sulfur yang terdapat dalam tempurung kelapa secara alami. Pembentukan Na2CO3 juga didukung hasil karakterisasi dengan EDS yang menunjukkan sampel terdiri dari unsur C, Na, dan O, dan deteksi fase termonatrit (Na2CO3.H2O ) dengan XRD. Karakterisasi sampel yang disintering pada suhu 450 oC dengan XRD menunjukkan perubahan termonatrit menjadi Na2CO3 dan Na2O, yang juga didukung oleh hasil karakterisasi dengan DTA/TGA. Berdasarkan hasil yang diperoleh disimpulkan bahwa metode yang diusulkan pada penelitian ini berpotensi untuk diaplikasikan sebagai metode mitigasi gas CO2 yang dihasilkan oleh industri arang tempurung kelapa.

---

In this investigation, sodium carbonate (Na2CO3) was produced by reacting the CO2 released from coconut shell combustion with NaOH solution with molar concentrations of 6.5, 7.0, 7.5, and 8.0 M. The main purpose of the study was to assess the potential of the proposed method for mitigation of the CO2 gas released into the atmosphere by the coconut shell industry. The Na2CO3 powder produced was oven-dried at 110 oC and subsequently characterized using FTIR, XRD, and SEM/EDS techniques. Thermal analysis was also carried out using DTA/TGA to investigate the thermal mechanisms of sodium carbonate formation. The experimental results show that the concentration of NaOH influences the mass of sodium carbonate produced, with the highest mass of 190.6 g obtained using 7.0 M NaOH solution. The FTIR analyses show the existence of O-H, C-O, C=O, and CO3-2, confirming the formation of Na2CO3. The C-S functional group was also detected most likely due to the presence of the sulfur that naturally exists in the coconut shell. The formation of Na2CO3 is also supported by the presence of C, Na, and O on the EDS results and the presence of the thermonatrite (Na2CO3.H2O) phase, as seen by the XRD. The XRD analysis of the sintered sample at 450 oC indicates the transformation of thermonatrite into sodium carbonate and sodium oxide, which is in accordance with the results of DTA/TGA analysis. Based on the results obtained, it is concluded that the proposed method can be applied to mitigation of CO2 gas released by the coconut shell industry.