Abstrak :
Telah dilakukan substitusi parsial Gd terhadap La pada sistem superkonduktor suhu kritis tinggi La1.85Sr0.15CuO4 , momen magnet Gd diharapkan akan merusak superkonduktivitas bahan dan menurunkan L. Pengukuran Tc-nya dilakukan dengan alat susceptometer. Konsentrasi Gd dari senyawa La1.85Sr0.15CuO4 bervariasi dari x = 0 sampai dengan 0.16. Hasil pengulcuran. memperlihatkan penurunan Tc yang relatif lambat. ......Partial substitution of Gd for La had been conducted in high-Tc La1.85Sr0.15CuO4 superconductor system, Gd magnetic moment was expected to reduce superconductivity and decrease critical temperature L. Tc measurement was performed by using an ac susceptometer. Gd concentration of La1.85Sr0.15CuO4 compound was varied from x = 0 up to 0.16. The result showed that L decrease was relatively slow.