"Latar Belakang: Resin komposit merupakan bahan restorasi yang telah dikembangkan komposisinya sehingga memiliki sifat estetika, fisik, dan mekanik yang lebih baik dan diharapkan dapat mengatasi masalah yang disebabkan oleh material restorasi lainnya. Resin komposit PALFIQUE® Universal Flow dari Tokuyama Dental merupakan resin komposit yang telah dikembangkan partikel filler-nya dan diklaim memiliki kemampuan pemolesan yang tinggi serta estetika yang sempurna. Salah satu sifat permukaan restorasi resin komposit, surface gloss, memegang peranan penting terhadap estetika restorasi. Surface gloss dipengaruhi oleh berbagai faktor intrinsik dan ekstrinsik dan diantara faktor ekstrinsik yaitu sistem pemolesan. Tujuan: Menganalisis pengaruh sistem pemolesan terhadap surface gloss resin komposit supra-nano PALFIQUE® Universal Flow tipe Super Low dan Medium. Metode: Empat puluh delapan spesimen resin komposit supranano PALFIQUE® Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dibuat untuk penelitian ini. Spesimen dibagi menjadi 6 kelompok berdasarkan tipe resin komposit (Super Low dan Medium) dan sistem pemolesan (Sof-LexTM Spiral, Sof- LexTM XT Polishing Discs, Tanpa Pemolesan). Penyinaran resin komposit dilakukan dengan light curing unit iradiansi 1050 mW/cm2 selama 12 detik. Setiap spesimen dilakukan pengujian surface gloss dengan glossmeter sebanyak tiga kali. Data dianalisis menggunakan uji statistik One-Way ANOVA dan Independent Sample T-Test. Hasil: Nilai surface gloss semua kelompok berada pada rentang 76–96 GU. Surface gloss tertinggi dimiliki oleh kelompok tanpa pemolesan. Sistem pemolesan Sof-LexTM XT Polishing Discs menghasilkan surface gloss lebih tinggi dibandingkan Sof-LexTM Spiral dengan perbedaan yang signifikan (p<0,05). Surface gloss resin komposit tipe Super Low lebih tinggi dibandingkan tipe Medium dengan perbedaan yang signifikan (p<0,01). Kesimpulan: Surface gloss turut dipengaruhi oleh tipe resin komposit dan sistem pemolesan.

---

Background: Composite resin is a restorative material with composition that has been developed so that it has better aesthetic, physical, and mechanical properties and is expected to overcome problems caused by other restorative materials. PALFIQUE® Universal Flow composite resin from Tokuyama Dental is a composite resin with developed filler particles and is claimed to have high polishing ability and perfect aesthetics. One of the surface properties of composite resin restorations, surface gloss, plays an important role in the aesthetics of the restoration. Surface gloss is influenced by various intrinsic and extrinsic factors and among the extrinsic factors is the polishing system. Objectives: The aim of this study was to analyze the influence of different polishing systems on surface gloss of Super Low and Medium PALFIQUE® Universal Flow composite resin. Materials and Methods: Forty-eight specimens of PALFIQUE® Universal Flow supra-nano composite resin in cylindrical shape (diameter of 6 mm and height 2 mm) were used in this study. The specimens were divided into six groups by type (Super Low and Medium) and by polishing systems (Sof-LexTM Spiral, Sof-LexTM XT Polishing Discs, mylar strip). Specimens were polymerized with light curing unit for 12 seconds with light irradiance of 1050 mW/cm2. Each specimen was tested for surface gloss with a glossmeter three times. Data then were analyzed with One-Way ANOVA and Independent Sample T-Test. Results: Surface gloss value of all groups were above the clinically acceptable threshold (76–96 GU). Highest surface gloss value was shown on the mylar strip group. Higher surface gloss values were produced by Sof-LexTM XT Polishing Discs compared to Sof-LexTM Spiral, statistically significant (p<0,05). Surface gloss values were significantly higher on type Super Low compared to Medium (p<0,01). Conclusion: In this study, surface gloss value was influenced both by the type of composite resin and differences in polishing systems."

"Latar Belakang: Karies atau gigi berlubang merupakan masalah gigi dan mulut yang sering terjadi pada manusia. Cara untuk menangani masalah tersebut yaitu dengan membuat restorasi. Bahan restorasi yang dapat digunakan untuk menangani karies adalah resin komposit. Salah satu resin komposit jenis supra-nano flowable yang beredar dipasaran Indonesia adalah Palfique Universal Flow (Tokuyama Corporation, Japan). Resin komposit supra-nano Palfique Universal Flow dapat digunakan sebagai restorasi direk untuk gigi anterior maupun posterior. Pada rongga mulut, saat dilakukannya curing, kecil kemungkinan light curing dapat berkontak langsung dengan permukaan restorasi terutama pada gigi posterior. Sejauh ini belum ada penelitian mengenai pengaruh jarak penyinaran terhadap diametral tensile strength pada resin komposit supra-nano Palfique Universal Flow. Tujuan: Menganalisis pengaruh jarak penyinaran terhadap diametral tensile strength dari resin komposit supra-nano Palfique Universal Flow tipe super low dan medium. Metode: Resin komposit yang digunakan adalah jenis supra-nano Palfique Universal Flow tipe super low dan medium. Spesimen resin komposit untuk menguji diametral tensile strength berbentuk silinder berdiameter 6 mm dan ketebalan 3 mm. Jumlah specimen berjumlah 36 dibagi masing-masing menjadi 3 kelompok pada tipe super low dan medium dengan jarak penyinaran 0, 3, dan 6 mm menggunakan light curing unit LED, dengan iradiansi 1050 W/cm2, durasi 10 detik. Nilai diametral tensile strength diuji dengan alat Universal Testing Machine. Data dianalisis dengan uji statistik One Way Anova dan uji Independent Sample T-test. Hasil: Nilai diametral tensile strength pada tipe super low (jarak penyinaran 0, 3, dan 6 mm secara berurutan) 46,47 ± 3,49 MPa, 43,78 ± 3,36 MPa, dan 40,00 ± 3,17 MPa. Nilai diametral tensile strength pada tipe medium (jarak penyinaran 0, 3, dan 6 mm secara berurutan) 49,19 ± 2,95 MPa, 45,64 ± 3,62 MPa, dan 43,36 ± 3,54 MPa. Nilai diametral tensile strength pada jarak 0 dan 6 mm pada tipe super low maupun medium memiliki perbedaan yang bermakna secara statistik (p<0,05). Nilai diametral tensile strength tipe medium lebih besar dibandingkan dengan tipe super low pada setiap kelompok jarak penyinaran tapi tidak memiliki perbedaan yang bermakna (p≥0,05). Kesimpulan: Semakin jauh jarak penyinaran pada resin komposit supra-nano Palfique Universal Flow tipe super low dan medium, maka nilai diametral tensile strength semakin rendah. Nilai diametral tensile strength resin komposit supra-nano Palfique Universal Flow tipe medium yang di-curing pada jarak penyinaran 0, 3, dan 6 mm lebih besar dibandingkan dengan tipe super low.

---

Background: Tooth decay or dental caries is a common oral health issue in humans. One way to address this problem is by creating restorations. Composite resin is a restoration material commonly used to treat dental caries. One of the types of supra-nano flowable composite resins available in the Indonesian market is Palfique Universal Flow (Tokuyama Corporation, Japan). Supra-nano composite resin Palfique Universal Flow can be used for direct restorations in both anterior and posterior teeth. During the curing process in the oral cavity, there is a small chance that light curing can directly contact the restoration surface, especially in posterior teeth. So far, there has been no research on the influence of light curing distance on the diametral tensile strength of supra-nano composite resin Palfique Universal Flow. Objective: To analyze the effect of light curing distance on the diametral tensile strength of supra-nano composite resin Palfique Universal Flow in super low and medium types. Methods: The composite resin used was supra-nano Palfique Universal Flow in super low and medium types. Specimens for testing diametral tensile strength were cylindrical with a diameter of 6 mm and a thickness of 3 mm. There were 36 specimens, divided into 3 groups for each super low and medium types, with curing distances of 0, 3, and 6 mm using a LED light curing unit, with irradiance of 1050 W/cm2 for 10 seconds. Diametral tensile strength values were tested using a Universal Testing Machine. Data were analyzed using One-Way ANOVA and Independent Sample T-test. Results: Diametral tensile strength values for super low type (at curing distances of 0, 3, and 6 mm, respectively) were 46.47 ± 3.49 MPa, 43.78 ± 3.36 MPa, and 40.00 ± 3.17 MPa. Diametral tensile strength values for medium type (at curing distances of 0, 3, and 6 mm, respectively) were 49.19 ± 2.95 MPa, 45.64 ± 3.62 MPa, and 43.36 ± 3.54 MPa. There were statistically significant differences in diametral tensile strength values between 0 mm and 6 mm curing distances for both super low and medium types (p<0.05). The diametral tensile strength of the medium type was greater than that of the super low type in each curing distance group, but the difference was not statistically significant (p≥0.05). Conclusion: The farther the light curing distance in supra-nano composite resin Palfique Universal Flow super low and medium types, the lower the diametral tensile strength values. The diametral tensile strength values of supra-nano composite resin Palfique Universal Flow medium type cured at 0, 3, and 6 mm distances were greater than those of the super low type."

"Latar Belakang: Palfique Universal Flow® merupakan resin komposit flowable yang digunakan untuk merestorasi gigi anterior dan posterior. Untuk dapat beredar di pasaran, material restorasi harus memenuhi karakteristik standar, salah satunya adalah kekuatan fleksural. Material restorasi akan terpapar oleh lingkungan mulut yang kondisi pH-nya selalu berubah sehingga dapat berdampak pada kekuatan fleksuralnya. Tujuan: Menganalisis pengaruh perendaman resin komposit supra-nano Palfique Universal Flow® tipe medium pada berbagai pH saliva buatan terhadap kekuatan fleksural. Metode: Sejumlah dua puluh empat spesimen resin komposit supra-nano Palfique Universal Flow® tipe medium dengan dimensi 25 x 2,8 x 2 mm dikelompokkan menjadi empat, yaitu kelompok tanpa perlakuan, perendaman di saliva buatan pH 3, pH 5,5, dan pH 7. Setelah direndam selama 7 hari, kekuatan fleksural diukur menggunakan Universal Testing Machine. Data dianalisis menggunakan uji Kruskal Wallis, Mann-Whitney, dan Independent T-Test. Hasil: Nilai kekuatan fleksural pada kelompok tanpa perlakuan merupakan yang tertinggi dan semakin rendah pada perendaman di dalam saliva buatan pH 7; 5,5; dan 3 secara berturut-turut dengan perbedaan signifikan (p≤0,05). Nilai antar kelompok berbeda signifikan pada seluruh kelompok (p≤0,05), kecuali pada pH 3 dengan pH 5,5 dan pH 5,5 dengan pH 7 (p>0,05). Kesimpulan: Saliva buatan yang asam menyebabkan nilai kekuatan fleksural resin komposit supra-nano Palfique Universal Flow® tipe medium menjadi lebih rendah.

---

Background: Palfique Universal Flow® is a flowable composite resin that used for restoring both anterior and posterior teeth. To be marketed, restorative materials must meet standard characteristics, one of which is flexural strength. Restorative materials are exposed to the oral environment, where pH conditions continuously change, potentially affecting their flexural strength. Objective: To analyze the effect of immersion medium-type supra-nano composite resin Palfique Universal Flow®in artificial saliva at various pH levels on the flexural strength. Methods: Twenty-four specimens of medium-type supra-nano composite resin Palfique Universal Flow®, with dimensions of 25 x 2.8 x 2 mm, divided into four groups: untreated, immersion in artificial saliva with pH 3, pH 5.5, and pH 7. After a 7-days immersion, the flexural strength was measured using a Universal Testing Machine. The data were analyzed using Kruskal-Wallis, Mann-Whitney, and Independent T-Test. Results: The flexural strength values in the untreated group were the highest, decreasing within immersion in artificial saliva at pH 7, 5.5, and 3 with significant differences observed (p≤0.05). Significant differences were noted between groups in all cases (p≤0.05), except between pH 3 and pH 5.5, as well as between pH 5.5 and pH 7 (p>0.05). Conclusion: Artificial saliva with acidic pH levels leads to lower flexural strength values of the medium-type supra-nano composite resin Palfique Universal Flow®.

"

"Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi.

---

Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC."

"Latar Belakang : Resin komposit menjadi salah satu jenis material restorasi yang banyak digunakan karena memiliki keunggulan dalam sifat fisik, mekanik, dan estetika. Salah satu resin komposit yang beredar di Indonesia adalah Resin Komposit Palfique Supra-Nano Universal Flow yang dikembangkan partikel filler-nya dan diklaim memiliki sifat fisik yang baik antara lain water sorption dan solubility. Penggunaan resin komposit seiring waktu akan terpapar oleh lingkungan rongga mulut akibat adanya saliva yang pH-nya bisa berubah seiring konsumsi makanan dan minuman sehingga mempengaruhi water sorption dan solubility-nya. Hingga saat ini, belum terdapat penelitian mengenai pengaruh perendaman pada berbagai pH saliva buatan terhadap water sorption dan solubility Resin Komposit Palfique Supra-nano Universal Flow. Tujuan : Menganalisis pengaruh perendaman Resin Komposit Supra-Nano Palfique Universal Flow tipe Super Low dan Medium pada berbagai pH saliva buatan terhadap water sorption dan solubility. Metode : Empat puluh delapan spesimen Resin Komposit Supra-Nano Palfique Universal Flow tipe Super Low dan Medium dengan dimensi 15 x 1 mm dibagi menjadi delapan kelompok uji berdasarkan tipe dan perendaman, yaitu pada perendaman di dalam akuades, saliva buatan pH 3, 5,5, dan 7 masing-masing selama 7 hari. Perhitungan dari nilai water sorption dan solubility dilakukan sesuai ISO 4049 : 2019. Analisis data menggunakan uji One way ANOVA dan Kruskall Wallis. Hasil : Nilai water sorption dan solubility pada kedua tipe Resin Komposit Palfique Supra-nano Universal Flow semakin tinggi pada perendaman pH yang semakin rendah. Perendaman di dalam akuades dan saliva buatan pH 3 mengalami kenaikan secara signifikan (p<0,05), dan tidak signifikan pada perendaman di dalam saliva buatan pH 3 dengan pH 5,5 dan pH 7 (p<0,05). Nilai solubility pada perendaman di dalam saliva buatan pH 3 dengan pH 5,5 mengalami kenaikan secara signifikan (p<0,05), sedangkan pada saliva buatan pH 5,5 dengan 7 tidak signifikan (p>0,05). Tipe Super Low memiliki nilai water sorption dan solubility yang lebih tinggi dibandingkan tipe Medium pada semua perendaman namun tidak signifikan (p>0,05). Kesimpulan : Terjadi peningkatan nilai water sorption dan solubility Resin Komposit Palfique Supra-nano Universal Flow setelah perendaman di dalam saliva buatan pH 3 dibandingkan pH 5,5, 7, dan akuades.

---

Background : Composite resin is one type of restoration material that is widely used because it has advantages in physical, mechanical, and aesthetic properties. One of the composite resins distributed in Indonesia is Palfique Supra-nano Universal Flow Composite Resin which developed its filler particles and claimed to have good physical and mechanical properties, one of which is the physical properties of water sorption and solubility. The use of composite resins over time will be exposed to the oral environment due to the presence of saliva which pH of saliva can change with the consumption of food and drinks, that affecting the water sorption and solubility of the Composite Resin. Until now, there’s not yet research the effect of immersion at various pH artificial saliva on water sorption and solubility of Palfique Supra-nano Universal Flow Composite Resin. Objective : To analyze the effect of immersion type Super Low and Medium Palfique Supra-Nano Universal Flow Composite Resin at various pH artificial saliva on water sorption and solubilty. Methods : Forty-eight type Super Low and Medium Palfique Supra-Nano Universal Flow Composite Resin specimens with dimensions of 15 x 1 mm were divided into eight test groups based on type and immersion ; distilled water, artificial saliva pH 3, 5,5, and 7 for 7 days. Calculations of water sorption and solubility values will be made according to ISO 4049: 2019. Data analysis used One way ANOVA and Kruskall Wallis test. Results : The value of water sorption and solubility for both types (Super Low and Medium) is higher in immersion at lower pH. Immersion in distilled water and artificial saliva pH 3 in both types increased significantly (p<0.05), and in artificial saliva pH 3 with pH 5.5 and pH 7 was not significant (p<0.05). The solubility value in pH 3 immersion with pH 5.5 increased significantly (p<0.05), while at pH 5.5 and 7 it was not significant (p>0.05). The Super Low type has higher water sorption and solubility values than the Medium type in all immersions but not significant (p>0.05). Conclusion : There is an increase on water sorption and solubility of Palfique Supra-nano Universal Flow Composite Resin after immersion at artificial pH 3 compared to pH 5,5, 7, and distilled water."

"Penelitian ini bertujuan untuk mengetahui pengaruh pH saliva buatan terhadap surface gloss resin komposit Giomer Bulk-Fill. Uji surface gloss menggunakan glossmeter dengan sudut pengukuran 60 . Jumlah spesimen 63 buah terbagi dalam sembilan kelompok perlakuan yaitu perendaman dalam saliva buatan dengan pH 4,5; 5,5; dan 7 dengan waktu perendaman masing-masing 1 jam, 24 jam, dan 72 jam. Hasil analisis One-way ANOVA menunjukkan perbedaan bermakna pada setiap kelompok perlakuan. Disimpulkan bahwa dengan menurunnya pH saliva buatan dapat menurunkan nilai gloss pada permukaan resin komposit Giomer Bulk-Fill.

---

This study aims to determine the effect of artificial salivary pH to surface gloss of Giomer Bulk Fill composite resin restorative materials. The surface gloss were tested using glossmeter with measurement angle of 60 . The number of specimens are 63, divided into nine groups with immersion in artificial salivary pH of 4.5, 5.5, and 7 for 1 hour, 24 hours, and 72 hours at 37 C. Statistical analysis using One way ANOVA showed significant difference in each treatment group. This result suggested that the pH value reduction of artificial saliva can reduce the gloss value on the surface of giomer bulk fill composite resin."

"Latar belakang: Mode penyinaran pulsa merupakan alternatif dari mode penyinaran kontinu untuk mempolimerisasi resin komposit. Saat ini resin komposit nanofil dan bulkfil merupakan material restorasi yang memerlukan surface gloss yang baik untuk memenuhi kebutuhan estetik. Surface gloss dapat dipengaruhi oleh penyinaran. Tujuan: Untuk menganalisa pengaruh penyinaran mode kontinu dan pulsa terhadap surface gloss resin komposit nanofil dan bulkfil segera dan setelah satu hari. Metode: Spesimen resin komposit nanofil dan bulkfil disinar menggunakan mode kontinu atau pulsa beriradiansi 900 mW/cm2 selama 20 detik. Lalu dilakukan pengujian surface gloss segera setelah penyinaran. Kemudian spesimen disimpan selama satu hari dan dilakukan pengujian surface gloss kembali. Hasil: Surface gloss yang dihasilkan oleh mode penyinaran kontinu dan pulsa tidak bermakna secara statistik (p>0,05). Resin komposit nanofil menghasilkan surface gloss lebih rendah daripada bulkfil, berbeda bermakna (p=0,00). Segera setelah penyinaran menghasilkan surface gloss lebih tinggi daripada setelah satu hari tidak bermakna secara statistik (p>0,05). Kesimpulan: Pada penelitian ini surface gloss tidak dipengaruhi oleh mode penyinaran kontinu dan pulsa serta perbedaan waktu segera dan setelah satu hari. Namun terdapat pengaruh jenis resin komposit, nanofil menghasilkan surface gloss lebih rendah dari yang dihasilkan bulkfil.

---

Background: Pulse is an alternative of continuous light-curing mode to polymerize composite resin. Currently, nanofill and bulk-fill are restorative materials that require good gloss surface to meet aesthetic needs. Surface gloss can be obtained by irradiation.

Aim: To analyze influence of continuous and pulse light-curing mode on surface gloss of nanofill and bulk-fill immediately after irradiation and after one day.

Method: Nanofill and bulk-fill specimens were irradiated using continuous or pulse light-curing mode with irradiance of 900 mW/cm2 for 20 seconds. Then surface gloss test is carried out immediately after irradiation. Then the specimens were water-stored for one day and then tested their surface gloss again.

Result: Surface gloss produced by continuous and pulse light-curing mode were not statistically different (p>0,05). Nanofill produced lower surface gloss than bulk-fill, statistically significant (p=0,00). Immediately after irradiation, resulting surface gloss were higher than after one day, not statistically significant (p>0,05).

Conclusion: In this experiment, surface gloss was not affected by continuous and pulse light-curing mode as well as the time difference immediately and after one day. However, there is an influence on the type of composite resin, where nanofill produced lower surface gloss than bulk-fill."

"ABSTRACTTujuan: Penelitian ini bertujuan untuk mengetahui pengaruh sistem pemolesan terhadap perubahan warna resin komposit mikrohibrida setelah perendaman dalam larutan Luwakwhite coffee. Material dan Metode Penelitian: Dalam penelitian ini digunakan empat puluh dua spesimen berdiameter 6 mm dan tebal 2 mm yang dibagi menjadi 6 kelompok dengan 2 bahan yang berbeda yaitu G-aenial PosteriorTM dan Filtek Z250TM dipoles menggunakan Sof-Lex disc SuperfineTM, PoGo, dan tidak dipoles. Spesimen di polimerisasi menggunakan LED Curing Unit dengan irradiansi 700 mW/cm2 (LED Max Hilux) selama 20 detik. Setelah dipoles, spesimen direndam dalam larutan Luwak white coffee selama 7 hari. Perubahan warna diukur menggunakan colorimeter NH310 (Shenzhen 3NH) dengan sistem warna CIE Lab. Data dianalisis menggunakan uji Statistik One-Way Anova Test. Hasil: Setelah dipoles, terdapat perbedaan yang signifikan (p<0,05) pada nilai I E1 dan nilai I a1, namun untuk nilai I L1 dan nilai I b1 tidak terdapat perbedaan yang signifikan. Setelah perendaman dalam larutan Luwakwhite coffee, terdapat perbedaan yang signifikan (p<0,05) pada nilai I E2, nilai I b2. Sedangkan, nilai I L2 hampir terdapat perbedaan yang signifikan pada seluruh kelompok, kecuali G-aenial PosteriorTM yang tidak dipoles dengan Filtek Z250TM yang tidak dipoles, Filtek Z250TM yang tidak dipoles dengan Filtek Z250TM yang dipoles menggunakan Sof-LexTM Superfine, dan G-aenial PosteriorTM yang dipoles menggunakan Sof-LexTM Superfine dengan Filtek Z250TM yang dipoles menggunakan Sof-LexTMSuperfine serta nilai I a2 hampir terdapat perbedaan yang signifikan pada seluruh kelompok, kecuali Filtek Z250TM yang tidak dipoles dengan Filtek Z250TM yang dipoles menggunakan PoGo. Kesimpulan: Sistem pemolesan yang berbeda dapat mempengaruhi nilai perubahan warna resin komposit mikrohibrida. Pemolesan menggunakan PoGo menghasilkan perubahan warna paling kecil. Filtek Z250TM memiliki perubahan warna terkecil setelah perendaman dalam larutan Luwak white coffeeselama 7 hari.

---

ABSTRACTObjectives: This study aims to analyze the influence of polishing systems on color change of microhybrid composite resin after immersion in Luwak white coffee solution.Material and Methods: In this study, fourty two specimens, 6 mm in diameter and 2 mm thick, were divided into six groups with different composite types, that is G-aenial PosteriorTM and Filtek Z250TM, polished with Sof-Lex disc SuperfineTM, PoGo and unpolished. The specimens are polymerized for 20 seconds using a 700 mW/cm2irradiance LED curing unit (LED Max Hilux). After polishing, the specimens are immersed in Luwak white coffee solution for 7 days. The color change is measured using a colorimeter NH310 (Shenzhen 3NH) with the CIE Lab color system. Data were analyzed using One-Way ANOVA test. Results: After polishing, there were statistically significant differences (p<0,05) between the I E1 and I a1 groups. However, statistically significant differences were not found between the I L1 and I b1 groups. After immersed in Luwak white coffee, there were statistically significant differences (p<0,05) between the I E22 and I b1 groups. Meanwhile, almost all of the I L2 groups showed a significant increase, except for G-aenial PosteriorTM unpolished with Filtek Z250TM unpolished, Filtek Z250TM unpolished with Filtek Z250TM polished using Sof-LexTMSuperfine, G-aenial PosteriorTM polished using Sof-LexTM Superfine with Filtek Z250TMpolished using Sof-LexTM Superfine and I a2 groups showed a significant increase, except Filtek Z250TM unpolished with Filtek Z250TM polished using PoGo. Conclusions:It was concluded that different polishing systems affect color change of the microhybrid composite resins. Polishing with PoGo produces the smallest color change. Filtek Z250TM was determined to have the smallest color change after immersion in Luwak white coffee for 7 days."

"Latar Belakang: Perawatan restorasi resin komposit nanofilled dan nanohybrid memerlukan prosedur pemolesan untuk mengurangi tingkat kekasaran permukaan sehingga permukaan halus dan mengkilap. Tujuan: Membandingkan kekasaran permukaan resin komposit nanofilled dan nanohybrid setelah pemolesan menggunakan teknik multiple-step. Metode: 40 spesimen resin komposit yang dibagi ke dalam 2 kelompok 20 spesimen nanofilled Filtek Z350XT A dan 20 spesimen nanohybrid Filtek Z250XT B dipersiapkan kemudian dipoles. Setelah direndam dalam saliva buatan selama 24 jam, tingkat kekasaran permukaan diukur dengan surface roughness tester. Hasil: Hasil rerata tingkat kekasaran permukaan beserta standar deviasi kelompok A adalah 0,0967 m 0,0174 sedangkan kelompok B adalah 0,1217 m 0,0244. Secara statistik p=0,05 terdapat perbedaan signifikan antara kedua kelompok. Kesimpulan: Dapat disimpulkan bahwa tingkat kekasaran permukaan resin komposit nanofilled setelah pemolesan dengan teknik multiple-step lebih baik dibandingkan dengan nanohybrid.

---

Background: Restorative treatment using nanofilled and nanohybrid composite should be finished and polished to reduce surface roughness and create smoother surface of the composite.

Objective: To compare the surface roughness nanofilled and nanohybrid composite resin after polishing using multi step technique.

Method: 40 composite resin specimens were divided into 2 groups 20 nanofilled specimens Filtek Z350XT A and 20 nanohybrid specimens Filtek Z250XT B was prepared and then polished. After immersion in artificial saliva for 24 hours, the surface roughness is measured with a surface roughness tester.

ResultL The mean surface roughness results along with standard deviation of group A is 0,0967 m 0,0174 while group B is 0,1217 m 0,0244. Statistically with p 0.05 , there are significant differences between each group.

Conclusion: Surface roughness of nanofilled composite resin after polishing with multiple step technique is better than nanohybrid."