"Latar Belakang: Karies atau gigi berlubang merupakan masalah gigi dan mulut yang sering terjadi pada manusia. Cara untuk menangani masalah tersebut yaitu dengan membuat restorasi. Bahan restorasi yang dapat digunakan untuk menangani karies adalah resin komposit. Salah satu resin komposit jenis supra-nano flowable yang beredar dipasaran Indonesia adalah Palfique Universal Flow (Tokuyama Corporation, Japan). Resin komposit supra-nano Palfique Universal Flow dapat digunakan sebagai restorasi direk untuk gigi anterior maupun posterior. Pada rongga mulut, saat dilakukannya curing, kecil kemungkinan light curing dapat berkontak langsung dengan permukaan restorasi terutama pada gigi posterior. Sejauh ini belum ada penelitian mengenai pengaruh jarak penyinaran terhadap diametral tensile strength pada resin komposit supra-nano Palfique Universal Flow. Tujuan: Menganalisis pengaruh jarak penyinaran terhadap diametral tensile strength dari resin komposit supra-nano Palfique Universal Flow tipe super low dan medium. Metode: Resin komposit yang digunakan adalah jenis supra-nano Palfique Universal Flow tipe super low dan medium. Spesimen resin komposit untuk menguji diametral tensile strength berbentuk silinder berdiameter 6 mm dan ketebalan 3 mm. Jumlah specimen berjumlah 36 dibagi masing-masing menjadi 3 kelompok pada tipe super low dan medium dengan jarak penyinaran 0, 3, dan 6 mm menggunakan light curing unit LED, dengan iradiansi 1050 W/cm2, durasi 10 detik. Nilai diametral tensile strength diuji dengan alat Universal Testing Machine. Data dianalisis dengan uji statistik One Way Anova dan uji Independent Sample T-test. Hasil: Nilai diametral tensile strength pada tipe super low (jarak penyinaran 0, 3, dan 6 mm secara berurutan) 46,47 ± 3,49 MPa, 43,78 ± 3,36 MPa, dan 40,00 ± 3,17 MPa. Nilai diametral tensile strength pada tipe medium (jarak penyinaran 0, 3, dan 6 mm secara berurutan) 49,19 ± 2,95 MPa, 45,64 ± 3,62 MPa, dan 43,36 ± 3,54 MPa. Nilai diametral tensile strength pada jarak 0 dan 6 mm pada tipe super low maupun medium memiliki perbedaan yang bermakna secara statistik (p<0,05). Nilai diametral tensile strength tipe medium lebih besar dibandingkan dengan tipe super low pada setiap kelompok jarak penyinaran tapi tidak memiliki perbedaan yang bermakna (p≥0,05). Kesimpulan: Semakin jauh jarak penyinaran pada resin komposit supra-nano Palfique Universal Flow tipe super low dan medium, maka nilai diametral tensile strength semakin rendah. Nilai diametral tensile strength resin komposit supra-nano Palfique Universal Flow tipe medium yang di-curing pada jarak penyinaran 0, 3, dan 6 mm lebih besar dibandingkan dengan tipe super low.

---

Background: Tooth decay or dental caries is a common oral health issue in humans. One way to address this problem is by creating restorations. Composite resin is a restoration material commonly used to treat dental caries. One of the types of supra-nano flowable composite resins available in the Indonesian market is Palfique Universal Flow (Tokuyama Corporation, Japan). Supra-nano composite resin Palfique Universal Flow can be used for direct restorations in both anterior and posterior teeth. During the curing process in the oral cavity, there is a small chance that light curing can directly contact the restoration surface, especially in posterior teeth. So far, there has been no research on the influence of light curing distance on the diametral tensile strength of supra-nano composite resin Palfique Universal Flow. Objective: To analyze the effect of light curing distance on the diametral tensile strength of supra-nano composite resin Palfique Universal Flow in super low and medium types. Methods: The composite resin used was supra-nano Palfique Universal Flow in super low and medium types. Specimens for testing diametral tensile strength were cylindrical with a diameter of 6 mm and a thickness of 3 mm. There were 36 specimens, divided into 3 groups for each super low and medium types, with curing distances of 0, 3, and 6 mm using a LED light curing unit, with irradiance of 1050 W/cm2 for 10 seconds. Diametral tensile strength values were tested using a Universal Testing Machine. Data were analyzed using One-Way ANOVA and Independent Sample T-test. Results: Diametral tensile strength values for super low type (at curing distances of 0, 3, and 6 mm, respectively) were 46.47 ± 3.49 MPa, 43.78 ± 3.36 MPa, and 40.00 ± 3.17 MPa. Diametral tensile strength values for medium type (at curing distances of 0, 3, and 6 mm, respectively) were 49.19 ± 2.95 MPa, 45.64 ± 3.62 MPa, and 43.36 ± 3.54 MPa. There were statistically significant differences in diametral tensile strength values between 0 mm and 6 mm curing distances for both super low and medium types (p<0.05). The diametral tensile strength of the medium type was greater than that of the super low type in each curing distance group, but the difference was not statistically significant (p≥0.05). Conclusion: The farther the light curing distance in supra-nano composite resin Palfique Universal Flow super low and medium types, the lower the diametral tensile strength values. The diametral tensile strength values of supra-nano composite resin Palfique Universal Flow medium type cured at 0, 3, and 6 mm distances were greater than those of the super low type."

"Penelitian ini bertujuan untuk menganalisis pengaruh ketebalan komposit resin serat pendek KRSP dan waktu penyinaran terhadap kekerasan dan depth of cure DoC. Dua puluh empat spesimen KRSP EverX PosteriorTM berbentuk silinder berdiameter 6 mm, dibagi menjadi dua kelompok ketebalan: 4 dan 5 mm n=12. Setiap kelompok ketebalan disinar dengan jarak 2 mm, iradiansi 800 mW/cm2 selama 25 dan 30 detik n=6. Nilai kekerasan diukur dengan uji Vickers dan DoC didapatkan dengan menghitung rasio kekerasan permukaan atas dan bawah KRSP. Data dianalisis menggunakan uji One-way ANOVA. Disimpulkan ketebalan dan waktu penyinaran mempengaruhi kekerasan dan DoC KRSP sebagai substruktur.

---

This study aims to analyze the effect of short fibre reinforced resin composite SFRC thickness and curing time on the hardness and depth of cure DoC. Twenty four specimens of SFRC EverX PosteriorTM were made and formed into cylindrical shapes with 6 mm in diameter, divided into two different thickness groups 4 and 5 mm n 12. Each thickness group were cured with 2 mm light curing distance, irradiance 800 mW cm2 for 25 and 30 seconds n 6. The hardness was measured by Vickers test and depth of cure was obtained by calculating the hardness ratio of the bottom to the top surface. Data were analyzed statistically by One Way ANOVA tests. It was concluded that thickness and curing time has significant effect on the hardness and DoC of SFRC as substructure. "

"Tujuan penelitian ini untuk mengetahui pengaruh penggunaan sumber sinar berbeda terhadap kekuatan tarik diametral resin komposit bulk-fill. Resin komposit bulk-fill Tetric N-Ceram Bulk Fill dibuat sebanyak 20 spesimen berbentuk lempeng dengan diameter 6 mm dan tebal 3 mm. Spesimen dibagi menjadi dua kelompok yaitu kelompok yang disinari dengan sumber sinar QTH dan sumber sinar LED. Uji kekuatan tarik diametral dilakukan dengan menggunakan Universal Testing Machine. Hasil penelitian menunjukkan nilai rerata kekuatan tarik diametral resin komposit bulk-fill yang disinari sumber sinar QTH dan LED sebesar 38.62 2.34 dan 42.02 3.21. Hasil uji independent sample T menunjukkan nilai rerata pada kedua kelompok berbeda bermakna.

---

This study aimed to evaluate the effect of using different light sources on the diametral tensile strength of bulk fill resin composite. Bulk fill resin composite Tetric N Ceram Bulk Fill was used to make of 20 disc shape specimens with 6 mm in diameter and 3 mm in thickness. Specimens were divided into two groups, the two groups were polymerized with using QTH and LED light source curing unit. Diametral tensile strength test was conducted by using a Universal Testing Machine Shimadzu, Japan. The results showed that diametral tensile strength mean value of bulk fill resin composite that were cured with QTH and LED light source were 38.62 2.34 and 42.02 3.21 MPa respectively. Independent sample t test results showed that the mean value of the two groups was significantly different."

"Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi.

---

Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC."

"Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi.

---

Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC."

"Latar Belakang: Dalam dunia kedokteran gigi, terdapat banyak pilihan material restoratif yang dapat digunakan, salah satunya yaitu resin komposit. Seiring dengan perkembangan teknologi, para peneliti berhasil mengembangakan resin komposit baru yaitu Bulk-Fill. Sebagai contoh adalah resin komposit Giomer Bulk-Fill yang memiliki berbagai sifat seperti sifat mekanik, fisis dan biologis. Namun, belum ada penelitian pada resin komposit Giomer Bulk-Fill yang secara spesifik menguji nilai kekuatan tarik diametral yang merupakan salah satu sifat mekanik material restoratif.Tujuan Penelitian: Penelitian ini bertujuan untuk mengetahui pengaruh lama perendaman 1, 24, dan 72 jam serta perbedaan nilai pH saliva buatan 7; 5,5; dan 4,5 terhadap kekuatan tarik diametral resin komposit Giomer Bulk-Fill.Metode: Penelitian eksperimental laboratorik dengan menggunakan 90 spesimen berbentuk silindris pejal dengan diameter 6 mm dan tinggi 3 mm yang diuji menggunakan Universal Testing Machine (Shimadzu AGS-X 5kN, Japan) dan dibagi ke dalam 3 kelompok pH larutan saliva buatan yaitu 7; 5,5; dan 4,5; serta 3 kelompok lama perendaman yaitu 1, 24, dan 72 jam.Hasil: Hasil pengujian menggunakan uji One-way ANOVA menunjukkan adanya perbedaan bermakna pada spesimen-spesimen yang digunakan (p<0,05). Pada kelompok spesimen yang direndam dalam larutan saliva buatan dengan pH 7, hasil rerata kekuatan tarik diametral pada perendaman selama 1 jam adalah sebesar 36,7 ± 2,7 MPa. Kemudian mengalami penurunan setelah perendaman 24 jam dengan rerata nilai kekuatan tarik diametralnya sebesar 35,2 ± 2,2 MPa dan meningkat kembali setelah perendaman 72 jam dengan hasil rerata kekuatan tarik diametralnya sebesar 40,1 ± 3,6 MPa. Pada kelompok spesimen yang direndam dalam larutan saliva buatan dengan pH 4,5, pada perendaman selama 1 jam hasil rerata kekuatan tarik diametralnya sebesar 33,6 ± 2,4 MPa. Kemudian setelah perendaman 24 jam dan 72 jam meningkat menjadi 42,6 ± 2 MPa dan 44,2 ± 2,8 MPa. Pada kelompok spesimen yang direndam dalam larutan saliva buatan dengan pH 5,5, hasil rerata kekuatan tarik diametral setelah perendaman selama 1 jam adalah sebesar 34 ± 2,4 MPa. Namun, terjadi perbedaan jika dibandingkan dengan kelompok pH 4,5 yaitu pada kelompok dengan pH 5,5 pada lama perendaman 24 jam terjadi peningkatan yaitu sebesar 44,7 ± 2,8 MPa kemudian menurun setelah perendaman 72 jam dengan nilai rerata sebesar 39 ± 3,3 MPa.Kesimpulan: Nilai kekuatan tarik diametral resin komposit Giomer Bulk-Fill tidak dipengaruhi oleh pH saliva buatan 4,5; 5,5; dan 7 yang digunakan di dalam penelitian ini. Nilai kekuatan tarik diametral resin komposit Giomer Bulk-Fill yang direndam selama 1, 24, dan 72 jam di dalam saliva buatan dengan pH 4,5; 5,5; dan 7 secara umum mengalami peningkatan sehingga lama perendaman dalam penelitian ini mempengaruhi nilai kekuatan tarik diametral resin komposit Giomer Bulk-Fill.

---

Background: In the world of dentistry, there are many choices of restorative materials that can be used, one of them is composite resin. Along with the development of technology, the researchers succeeded in developing a new composite resin called Bulk-Fill. One example is Giomer Bulk-Fill composite resin which has various properties such as mechanical, physical and biological properties. However, there is no research on Giomer Bulk-Fill composite resin which specifically tests the value of diametral tensile strength which is one of the mechanical properties of restorative material.

Objective: This study aims to determine the effect of immersion time and the difference in pH value 7; 5,5; and 4,5 of the artificial saliva solution on the value of diametral tensile strength of Giomer Bulk-Fill composite resin.

Method: Laboratory experimental research using 90 solid cylindrical specimens with a diameter of 6 mm and a height of 3 mm which were tested using Universal Testing Machine (Shimadzu AGS-X 5kN, Japan) and were divided into 3 groups pH of artificial saliva solution (7; 5.5; and 4.5) and 3 groups of immersion periods (1, 24 and 72 hours).

Results: The test results using the One-way ANOVA test showed significant differences in the specimens used (p <0.05). In the group of specimens which were immersed in artificial saliva solution with pH 7, the results of the average diametral tensile strength at immersion for 1 hour were 36.7 ± 2.7 MPa. Then it decreased for 24 hours immersed time with a mean value of diametral tensile strength of 35.2 ± 2.2 and increased again at 72 hours immersed time with an average value of diametral tensile strength 40.1 ± 3.6 MPa. In the group of specimens which were immersed in artificial saliva solution with pH 4.5, at immersion for 1 hour the average value of diametral tensile strength was 33.6 ± 2.4 MPa. Then in 24-hour and 72-hour immersion, it increased to 42.6 ± 2 MPa and 44.2 ± 2.8 MPa. In the group of specimens immersed in artificial saliva solution with a pH of 5.5, the average value of diametral tensile strength for 1 hour was 34 ± 2.4 MPa. However, there was a difference when compared to the pH 4.5 group, which was in the group with a pH of 5.5 in the 24-hour immersion period, the value increase for 44.7 ± 2.8 MPa and then decreased for 72 hours of immersion with an average value of 39 ± 3.3 MPa.

Conclusion: The value of diametral tensile strength of Giomer Bulk-Fill composite resin is not affected by pH of artificial saliva 4.5; 5.5; and 7 that used in this study. The value of diametral tensile strength of Giomer Bulk-Fill composite resin, which is immersed for 1, 24, and 72 hours in artificial saliva with pH 4.5; 5.5 and 7 generally increased so that the immersion time in this study affected the diametral tensile strength of Giomer Bulk-Fill composite resin."