"In general, the Nd-Fe-B as-cast ingot is homogenized for a long time before the hydrogenation, disproportionation, desorption and recombination (HDDR) process, to produce good magnetic properties. Since the homogenizing process is expensive, this work examined the possibility of replacing it with a water quenching process for Nd-Fe-B magnetic powder. The magnetic powders were soaked at 1100oC for 4 hours, followed by water quenching prior to HDDR. The resulting powder had magnetic properties that were almost similar to magnetic powder that was homogenized prior to HDDR. The remanence values of the water-quenched alloy and the homogenized alloy were 7.8 KG and 8.9 KG, respectively, while the coercivity values were 12.6 KOe and 10.3 KOe, respectively. In general, the magnetic properties of both samples were not much different. The microstructure of Nd2Fe14B phase combined with a very slight Nd rich phase in micro grain boundary likely caused the coercivity enhancement."

"ABSTRAKTelah dilanjutkan suatu studi teoritik dan eksperimental tentang magnet permanen Nd-Fe-B. Studi teoritik melibatkan teori klasik Stoner-Wohlfarth (S-W) dengan mengikut sertakan efek interaksi antar partikel (yang absen pada asumsi S-W). Hasil komputasi menunjukkan bahwa efek interaksi menurunkan koersifitas intrinsik magnet Nd-Fe-B. Terdapat kesesuaian secara kualitatip antara nilai komputasi dan nilai eksperimental meskipun terdapat perbedaan yang sangat besar secara kuantitatip. Baik model komputasi yang dikembangkan maupun optimasi sifat dari pengukuran eksperimental masih harus sama-sama menjalani perbaikan.Studi eksperimental melibatkan dua proses berbeda untuk memproduksi magnet permanen Nd-Fe-B yaitu masing-masing proses konvensional sintering dan proses modern meltspinnig. Pada proses konvensional telah berhasil dipertahankan fasa utama Nd2Fe14B yang merupakan fasa magnetik magnet permanen setelah melalui tahapan sintering dan aniling meskipun masih teramati adanya fasa oksida yang seharusnya dihindarkan. Magnet permanen Nd-Fe-B untuk tiga komposisi berbeda (komposisi stoildometri; komposisi kaya Nd dan komposisi yang mengandungg Dy) telah dipelajari. Ketiga jenis magnet mencapai densitas medekati 100 % nilai teoritik dengan penggunaan tekanan sebesar 121 MPa untuk menghasilkan green compact dengan densitas 77 % dan densifikasi dicapai setelah proses anil pada temperatur -- 1100 °C selama 1 - 2 jam. Studi XRD menunjukkan bahwa magnet sinter komposisi stoildometri masih mengandung fasa kedua (a-Fe) yang diduga berasal dan sistem milling sedangkan magnet sinter Nd-Fe-B kaya Nd memiliki fasa kedua fasa kaya Nd. Magnet sinter yang dihasilkan menunjukkan koersivitas yang sangat tinggi demikian sehingga medan luar 1,5 T tidak cukup tinggi untuk menginduksi magnetisasi magnet. Ini memberikan loop histeresis yang tidak dapat dievaluasi.Penelitian terhadap pita alloy Nd-Fe,Co-B material magnetik dengan teknik meltspinning menunjukkan bahwa pita alloy membentuk struktur nanokomposit sistem Nd.(Fe-Co)14BIFe-Co . Struktur nanokomposit ini memberikan ratio antara remanen dan polarisasi total > 0,5 meskipun diturunkan dari loop minor. Pengukuran temperatur transisi menyimpulkan bahwa subsitusi Co terhadap Fe pada fasa Nd2Fe14B meningkatkan Tc secara progresif dari 310 °C sampai 650 °C. Ukuran-ukuran kristal kedua fasa adalah sangat lulus (berskala manometer) sehingga memberikan efek interaksi. Namun efek interaksi tidak signifikan pada nilai Tc."

"Telah dilakukan rekayasa struktur material magnet pemanen berbasis fasa Nd2Fe14B melalui subsitusi parsial atom neodymium (Nd) dalam sel satuan dengan atom dysprosium (Dy) sehingga membentuk fasa (Nd,Dy)2Fe14B untuk meningkatkan nilai koersifitas. Rekayasa struktur untuk peningkatan nilai koersifitas dimaksud juga dilakukan melalui pengecilan ukuran partikel fasa (Nd,Dy)2Fe14B dengan memperpanjang durasi waktu penghalusan pada proses penghalusan mekanik. Ingot material dengan tiga komposi berbeda Nd20-xDyxFe14B dengan x = 1, 3, 5 at.% dipersiapkan dengan mini arc melting furnace (AMF) dan dilanjutkan dengan perlakuan anil selama 24 jam untuk homogenisasi mikrostruktur. Sampel magnet untuk masing - masing komposisi diperoleh setelah tahapan-tahapan penghalusan mekanik dengan variasi durasi waktu penghalusan 5, 10, 15 dan 20 jam. Evaluasi nilai koersifitas sampel magnet memperlihatkan peningkatan tajam terjadi karena pembentukan mikrostruktur yang terdiri dari fasa utama (Nd,Dy)2Fe14B dan fasa yang kaya Nd (Nd-rich phase) paska perlakuan panas.

---

A change of the cell structure of the permanent magnet materials based on the Nd2Fe14B phase has been carried out through partial substitution of the neodymium (Nd) atom with the dysprosium (Dy) to form (Nd, Dy)2Fe14B phase to increase the coercivity value. The increase in coercivity has also been achieved by refining the particle size of (Nd, Dy) by mechanical milling with varying times of time. Ingot of Nd20-xDyxFe14B with x = 1, 3, 5 at.% were prepared by mini arc melting furnace (AMF) and successively followed by annealing treatment for 24 hours in a sealed quartz tube for microstructure homogenization. As annealed magnetic ingots for for each composition was then mechanically refined for the duration of grinding times 5, 10, 15 and 20 hours and compacted in a cylindrical die of 12 mm diameter for magnetic sample preparation. The value of coercivity of all magnetic samples was evaluated from the hysteresis loop. It is found that the best improvement of coercivity occurred due to microstructural formation which consisting of the main phase (Nd, Dy)2Fe14B and the Nd rich phase (Nd rich phase) after heat treatment."

"ABSTRAKKorosi adalah kerusakan material yang disebabkan oleh reaksi materi dengan lingkungannya. Dalam penelitian ini telah dilakukan analisis sifat korosi material magnet Nd-Fe-B dalam larutan HCI, NaCl dan NaOH (korosi basah.) dan pemanasan 100°C serta dalam udara terbuka -30°C (korosi kering).Preparasi sampel dilakukan dengan proses metalurgi serbuk dengan komposisi nomieial Nd15+,Fe?_xBa x = 0; x = 1; x = 3; x = 5. Laju korosi dihitung dengan metode kehilangan berat selama proses. Laju korosi yang tertinggi diamati jika material berada dalam larutan HCI kemudian diikuti oleh NaCl dan NaOH. Hasil identifikasi dengan sinar-x dan SEMIEDX menunjukkan bahwa setelah korosi terbentuk fasa BFe3, cc-Fe serta oksida dari Nd dan Fe. Disamping itu serangan korosi yang terjadi adalah korosi batas butir.

---

ABSTRACT

Corrosion is a material damage which is caused by the reaction with its environment. In this research some analysis's on the corrosion behavior of magnetic material Nd-Fe-B in HCI, NaCl and NaOH solutions (wet corrosion) and heating to 100°C and in open air -30°C (dry corrosion) have been conducted. The sample preparations were done with powder metallurgy process with the nominal composition of (Nd1 xFen.xB8), x = 0; x = 1; x =3; x =5. The corrosion study was done by evaluating the rate of corrosion with loss of the mass during the reaction method. The highest corrosion rate was in HCI solution and followed by NaCl and NaOH. The phase identification by X-ray result and SEMIEDX, showed that after the corrosion there was a phase change with the formed a-Fe, BFe3 and the oxide phase out of Nd and Fe. Besides that the other corrosion that occurred was the grain boundry corrosion."

"ABSTRAKTelah dilakukan studi sifat kemagnetan terhadap magnet isotrop dan anisotropkomposisi Nd|5Fe-nB3 yang dibuat dengan tehnik metalurgi serbuk. Pembuatan sampelmagnetik dilakukan dengan vatiasi waktu penggerusan yaitu 5 detik, I0 detik, 60 detik,300 detik, dan 600 detik dalam suasana inert dan diperoleh ukuran butir rata-rata setelahproses perlakuan panas yaitu 1,55 pm, 1,48 pm, 1,14 pm, 0,93 pm, dan 0,63 pm yangdiukur dengan metode intercept (Heyne). Proses pembuatan bakalan dengan diameter I0mm dan tekanan 31,8 MPa serta medan magnet luar 0,1 T dan 0,5 T untuk prosespenyearahan. Bakalan tersebut disinter dan dianil dalam sumana inert dalam tabungquartz dengan temperalur 1080°C dan 600°C selama masing-masing 1 jam. Pendinginansecara cepat dalam air ( water quench) setel ah sinter telah berhasil mempertahankan fasamagnetik Nd2Fe|4B sebagai fasa utama berdasarkan identifikasi data difraksi sinar-X danfoto mikro. Kemungkinan adanya fasa-fasa lain seperti fasa yang kaya akan Nd (Nd-rich), fasa yang kaya akan B (NdFe_|B.|), dan fasa oksida Nd;O;. Fasa oksida banyakterdapat untuk sampel dengan waktu peggemsan yang cukup lama yaitu 300 detik dan600 detik, sehingga sifat-sifat kemagnetan yang terukur sanga! rendah. Pengukuran sifatkemagnetan menggunakan VSM untuk sampel yang dipelajari bahwa koersivitas danremanen terbesar adalah 834 kAfm dan 0,62 T diperoleh untuk magnet isotrop denganwaktu penggerusan selama 60 detik. Koersivitas dan remanen untuk magnet anisotropadalah 633,5 kA/m dan 0,75 T diperoleh dengan waktu penggerusan selama 60 detik danmedan luar 0,5 T untuk proses penyearahan.

---

AbstractMagnetic studies on isotropy and anisotropy magnets with composition of Nd15Fe7-,Buthat were made by Powder Metallurgy Route have been done. These magnetic sampleswere prepared by various milling times 5 sec, 10 sec, 60 sec, 300 sec, and 600 sec in inertcondition and obtained mean grain sizes after heat threatment are 1.55 um,l.48 t1m,l_l4um, 0.93 pm, and 0.63 pm which were meansured by intercept method (I-Ieyne)_ Bulkswere prepared with diameter I0 mm, pressing 31.8 MPa and also extemal magnetic fieldof 0.1 T and 0.5 T for alignment. These bulks were sintered and anealed in vacuum insilica quartz with temperatures of l08O°C and 600°C for each I hour. Water quenchingalter sintering fomied magnetic main phase Nd;Fe|.1B according to X-ray diffraction dataand micro photos. Possibility of presence of other phase are like Nd-rich, B-rich,(NdFe.iB4) and Nd2O3 phase. An oxide phase Nd;O; can be found in samples with longermilling time 300 sec and 600 sec, so magnetic properties measurement use VibratingSample Magnetometer (VSM) for samples under studied, it is found that the maximumcoercivity of 834 ltA/m and remanence of 0.62 T for isotropy magnetic sample withmilling time for 60 sec. Coercivity of 633.5 kA/m and remanence of 0.75 T ofanisotropymagnetic sample are obtained with milling time for 60 sec and external field0.5 T for alignment."

"Structural adhesives have been widely used to join metal to metal, and metal to composite in automotive and aircraft structures. However, the adhesive is susceptible to water absorption from the surrounding environment and this affects the mechanical properties of the adhesive, leading to reduction in the performance of the structure. This paper investigated the water absorption and desorption behaviour of FM 73M structural adhesive film and its effect on the tensile properties. The adhesive was immersed in deionised water at a temperature of 50oC. A gravimetric method was carried out to obtain the water uptake. Dog bone specimens were used to investigate the residual tensile strength of the adhesive. Finite element modelling was performed to model the spatial moisture distribution in the adhesive and the residual tensile strength after having absorbed water. It was found that the water absorption of FM 73M deviated from Fick's second law, however the desorption behaviour followed Fick's second law. The tensile properties of the adhesive (the tensile strength and the elastic modulus) tend to decrease with the increase of water content and they are recovered after desorption at the same temperature as the absorption. The residual tensile strength was predicted using a continuum damage approach combined with environmental degradation. Good agreement has been found between the predicted and the experimental results."

"ABSTRAKMagnet permanen berperekat mulai memegang peran yang sangat vital dalam perkembangan Industri modern sejak ditemukannya material magnet Alloy magnet logam tanah jarang berbasis fasa Nd2Fe14B. Material magnet ini memiliki produk energi maksimum yang sangat tinggi sehingga memungkinkan untuk dibuat magnet berperekat dengan energi yang dapat divariasi menurut kebutuhan. Dari hasil fabrikasi magnet permanen hibrida berperekat Nd-Fe-B dan BaO.6(Fe203) dengan teknik cetakan kompresi menunjukkan penurunan port hingga <10% dengan bertambahnya fraksi perekat. Dari hasil evaluasi terhadap sifat-sifat magnetik untuk material magnet berperekat menunjukkan bahwa remanen magnetik adalah mendekati hasil teori dengan koersivitas ?300kA.m 1 dengan produk energi maksimum 12.3 -27.5 kJ.m-3. Hasil lebih rendah 47.9% - 59.4% terhadap nilai teori.

---

ABSTRACT

Bonded permanent magnets play a vital role in modem Industries since the discovery and development of Rare earth based alloys that have magnetic phase of Nd2Fe14B. The alloy has very high maximum energy product, (BH)max that could derive bonded magnets of various energy product. In this research, fabrication of bonded remanent magnets based on hybrid materials between Nd-Fe-B and Ferrite BaO.6(Fe203) has been made by compression molding. It was observed that fraction of porosity in magnets was reduced to a value of < 10% (in volume) as bonded material was increased. Evaluation of magnetic properties for the bonded magnet shown that permanence magnetization is almost equal to the theoretical value with coercivities -300kA.m'1 and corresponding maximum energy product in the range 12.3 - 27.5 kJ.m'3. However, these result is less to 47.9% - 59.4% from the theory."