"Paduan TiNi merupakan paduan ingat bentuk yang dicirikan oleh adanya transformasi fasa reversibel. Dalam penelitian ini dilakukan pengamatan karakteristik presipitat TiNi3 sebagai akibat perlakuan panas penuaan pada paduan Ti-50.04%at.Ni, dengan tujuan untuk dapat mempelajari perilaku presipitat TiNi^ dan pengaruhnya terhadap temperatur transformasi fasa. Pengamatan struktur presipitat dilakukan dengan menggunakan metoda mikroskop elektron transmisi TEM dan temperatur transformasi diamati dengan menggunakan metoda resistivitas \istrik four point probe. Hasil pengamatan menunjukan bahwa presipitat TiNii tumbuh membesar mengikuti penambalian waktu penuaan dengan orientasi pertumbuhannya adalah ....- Pertumbuhan presipitat tersebut tidak menimbulkan perubahan yang signifikan terhadap temperatur transformasi.

---

TiNi alloy represents the shape memory alloy which is characterized by reversible phase transformation. In this investigation observation of characteristic TiNi? precipitation of a Ti-50.04%at.Ni alloy affected of aging treatment was carried out. The research was intended to study the influence of TiNi3 precipitate against the phase transformation temperature. The structure precipitate was observed by transmission electron microscope (TEM) and the transformation temperatures measured by four-point probe electrical resistant method. Experimental results showed that TiNi:, precipitates grow up with aging time increased- The orientation of precipitate growth relatively to matrix was found lying on ..... This precipitate growth did not significantly affect the transformation temperature."

"Penelitian presipitasi pada paduan logam ingat bentuk (shape memory alloy) TiNi dan pengaruhnya terhadap temperatur transformasi, telah banyak dilakukan. Hasilnya antara lain menyatakan bahwa terbentuknya presipitat T13Ni4 dapat mengakibatkan paduan ingat bentuk TiNi peka terhadap perubahan temperatur laku panas, tetapi apabila presipitat tumbuh hingga mencapai fasa kesetimbangan, yaitu presipitat TiNi3, paduan ingat bentuk tidak menunjukan adanya fasa antara saat terjadi transformasi.Dalam penelitian ini, telah dilakukan penelitian pengaruh proses penuaan terhadap presipitasi dan temperatur transformasi ingat bentuk paduan Ti-50.04%at. Ni, dengan tujuan untuk mengetahui karakteristik presipitat dan temperatur paduan Ti-50,04%at.Ni yang dituakan pada tempertaur 550 °C selama 1, 2, 5, 10, 20 dan 30 jam, pengamatan dilakukan menggunakan beberapa metoda yaitu mikroskop optik, mikroskop elektron transmisi (Transmission Electron Microscope - TEM) dan metoda tahanan listrik four probe.Hasil penelitian menunjukan bahwa paduan Ti-50.04%at.Ni, akibat laku panas penuaan berfasa martensit dengan orientasi pelat yang acak. Presipitat yang terbentuk adalah TiNi3 yang tumbuh pada orientasi tertentu, yaitu sesuai dengan hubungan [2021]TmNi3 // [020]Matriks, sedangkan temperatur transformasi tidak menunjukan perubahan yang berarti sebagai akibat perlakuan penuaan.

---

Examination of precipitate of TiNi shape memory alloy on temperature transformation has been done by many scientists. They observed that Ti3Ni4 precipitate can affect the transformation temperature of the alloy by heat treatment. If precipitate grows into stability phase, i.e. TiNi3 phase, shape memory alloy failed to show intermediate phase. In this research work aging process on precipitation and transformation temperature of Ti-50.04%at.Ni shape memory alloy were carried out.

The aim was study the characteristics of precipitate and transformation temperature of Ti-50.04 %at.Ni alloy which were aged at 550 °C for 1, 2, 5, 10, 20 and 30 hours. The testing method use optical microscope, Transmission Electron Microscope (TEM) and four-probe electric resistance.

Experimental results show that Ti-50.04%at.Ni alloy, which were effected by aging treatment have martensite phase. This martensitic is arranged by fine-laths with random orientation. Type of precipitates observed is TiNi3 and they grow through fixed orientation, i.e. [2021]TiNi3 11 [020]Matrix. Furthermore in this study, the transformation temperature were not significantly affected by aging treatment."

"Salah satu material yang sering digunakan pada industri transportasi adalah aluminium seri 6xxx. Paduan aluminium seri 6xxx mengandung silikon dan magnesium dengan proporsi yang dibutuhkan untuk membentuk magnesium silisida sehingga membuatnya dapat diberikan perlakuan panas. Penambahan Ti pada paduan aluminium seri 6xxx diharapkan dapat berkontribusi dalam meningkatkan kekuatan dari paduan aluminium melalui penguatan batas butir dengan memperkecil ukuran butir. Penelitian ini mempelajari pengaruh penambahan Ti dan temperatur pencanaian panas saat laku pelarutan pada paduan Al-1,35Mg-0,77Si-0,04Ti (% berat). Sampel dibuat menggunakan pengecoran metode squeeze casting, dilanjutkan dengan homogenisasi pada temperatur 400 °C selama 4 jam. Selanjutnya, sampel diberi perlakuan T5 yaitu pencanaian panas saat laku pelarutan dengan persen reduksi 25% diikuti oleh penuaan buatan pada temperatur 180 °C selama 0-200 jam. Temperatur laku pelarutan divariasikan 450 °C, 525 °C, dan 590 °C selama 1 jam. Sebagai variabel kontrol adalah sampel yang diberi perlakuan T6 yaitu laku pelarutan pada temperatur 590 °C selama 1 jam diikuti oleh penuaan buatan selama 0 – 200 jam. Karakterisasi yang dilakukan adalah pengujian komposisi kimia, pengujian kekerasan, pengamatan metalografi menggunakan mikroskop optik dan Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS), dan pengujian X-ray Diffraction (XRD). Hasil penelitian menunjukkan bahwa penambahan Ti sebesar 0,04 % berat mengubah morfologi butir dari dendritik menjadi equiaxed, namun tidak cukup untuk menurunkan ukuran butir sehingga terjadi penurunan kekerasan. Homogenisasi tidak memberikan efek signifikan pada nilai kekerasan paduan. Perlakuan T5 memberikan penguatan yang lebih baik dibandingkan T6, ditemukan nilai kekerasan setelah pencelupan cepat pada temperatur laku pelarutan 590 °C adalah 49,2 HRE pada T6, dan 54,6 HRE pada T5. Peningkatan temperatur pencanaian panas saat laku pelarutan meningkatkan pelarutan fasa kedua, mempromosikan peristiwa rekristalisasi dinamis, dan memicu respons penuaan yang lebih baik. Puncak kekerasan perlakuan T5 pada temperatur 450, 525, dan 590 °C masing-masing adalah 41,4 HRE, 78,8 HRE, dan 28 HRB. Fasa kedua yang terbentuk di dalam paduan adalah Mg5Si6, Mg9Si5, dan Mg2Si.

---

One material that is often used in the transportation industry is 6xxx series aluminium. The 6xxx series aluminium alloys contain silicon and magnesium in the required proportions to form magnesium silicide, making them amenable to heat treatment. The addition of Ti to 6xxx series aluminium alloys is expected to contribute to improving the strength of aluminium alloys through grain boundary strengthening by reducing grain size. This research studied the effect of Ti addition and hot rolling during solution treatment temperature on Al-1.35Mg-0.77Si-0.04Ti alloy (wt%). Samples were prepared using the squeeze casting method, followed by homogenisation at 400°C for 4 hours. Subsequently, the samples were treated with T5 temper, which is hot rolling during solution treatment with a reduction percentage of 25 percent followed by artificial ageing at 180°C for 0-200 hours. The solution treatment temperatures were varied to 450 °C, 525 °C, and 590 °C for 1 hour. As a control variable, the samples were treated with T6, i.e. solution treatment at 590 °C for 1 hour followed by artificial ageing for 0-200 hours. The characterisation carried out was chemical composition testing, hardness testing, metallographic observation using optical microscope and Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS), and X-ray Diffraction (XRD) testing. The results showed that the addition of Ti at 0.04 wt% changed the grain morphology from dendritic to equiaxed, but not enough to decrease the grain size resulting in a decrease in hardness. Homogenisation had no significant effect on the hardness value of the alloy. T5 treatment provided better reinforcement than T6, where it was found that the hardness values after quenching at a solution treatment temperature of 590 °C were 49.2 HRE in T6, and 54.6 HRE in T5. Increasing the hot rolling temperature during solution treatment enhances the dissolution of the second phase, promotes dynamic recrystallisation events, and triggers a better ageing response. The peak aged hardness of the T5 treatment at 450, 525, and 590 °C were 41.4 HRB, 78.8 HRB, and 28 HRB, respectively. The second phases that was formed in the alloy are Mg5Si6, Mg9Si5, and Mg2Si."

"Paduan Nitinol adalah salah satu paduan yang paling banyak digunakan untuk pemakaian paduan ingat bentuk karena mempunyai sifat mekanik sangat baik dan efek ingat bentuk yang stabil. Telah dilakukan penelitian pengaruh laku panas terhadap struktur mikro dan karaktristik sifat ingat bentuk paduan Nitinol. Paduan Nitinol dengan komposisi Ti-50,04% at.Ni sebagai paduan ingat bentuk diberikan perlakuan pelarutan pada 1000°C selama 1 jam dan dicelupkan kedalam air kemudian dilakukan proses penuaan pada temperatur 500°C, 550°C, 600°C, 650°C dan 700°C selama 10 jam. Struktur mikro diteliti dengan menggunakan Mikroskop Optik (MO) dan Scanning Electron Microscopy (SEM). Temperatur transformasi ditentukan dengan pengukuran resistansi dan sifat mekanik yaitu kekerasan diukur dengan metoda Vickers. Hasil pengamatan menunjukkan bahwa fasa martensit yang terbentuk tersusun oleh pelat-pelat Iamelar yang cenderung menjadi besar sedangkan kekerasan menurun pada penuaan 600°C ---700°C. Temperatur transformasi martensit menunjukkan kenaikan sekitar 4 °C setelah penuaan pada 500°C selama 10 jam. Akan tetapi penuaan dari 500°C - 700 °C tidak menunjukkan perubahan yang berarti terhadap ukuran butir dan temperatur transformasi.

---

Nitinol is one of the most of alloys used for the shape memory applications because they have good mechanical properties and stable shape memory effect. In this investigation, the influence of heat treatment on the microstructure and characteristic of Nitinol shape memory alloy were studied.The shape memory Nitinol alloy with Ti-50.04 % at.Ni composition was solution treated at 1000°C for 1 hour and quenched in water, then aged at temperature 500°C, 550°C, 600°C, 650°C and 700°C for 10 hours, respectively.

Microstructures were investigated by using optical microscopy and Scanning Electron Microscopy (SEM). Transformation temperature were measured using resistance measurement technique, whereas the mechanical property such as hardness was measured by Vickers method. The results of observation show that martensitic phase were arranged by large lamellar plates which in addition the hardness values were found to decease within the temperature range of 600°C - 700°C of aging. The martensite transformation temperature increased about 4°C after aging process at 500°C for 10 hours. However, in the aging temperature of 500°C --700°C there were no significant change observed in the grain size and the transformation temperature."

"Aluminium adalah sebuah logam ringan dan ulet yang memiliki kegunaan terbanyak kedua di dunia industri setelah besi dan baja. Salah satu paduan aluminium yang memiliki aplikasi luas adalah Al-Mg-Si yang termasuk ke dalam seri aluminium 6xxx. Peningkatan kekuatan paduan AlMg-Si dapat dilakukan melalui perlakuan penuaan dan pengerjaan panas, dimana kedua proses tersebut dapat digabungkan sehingga menghasilkan perlakuan yang disebut perlakuan panas T5. Penelitian ini menggabungkan metode canai panas yang dilakukan saat perlakuan pelarutan kemudian diikuti dengan penuaan pada paduan Al-1,01Mg-0,58Si (% berat) yang dihasilkan lewat proses squeeze casting. Pencanaian panas dilakukan pada temperatur 400, 475, dan 550 °C dengan persen deformasi sebesar 10 %, sementara itu penuaan buatan dilakukan pada temperatur 180 °C selama 0-200 jam. Karakterisasi meliputi pengujian komposisi kimia, pengujian kekerasan, pengamatan metalografi dan SEM – EDS (Scanning Electron Microscope-Energy Dispersive Spectroscopy), serta pengujian XRD (X-Ray Diffraction). Hasil penelitian menunjukkan bahwa kenaikan temperatur pemanasan atau laku pelarutan meningkatkan pelarutan fasa kedua, mempercepat peristiwa rekristalisasi dinamis, serta memicu respons penuaan yang lebih baik. Hal ini ditunjukkan dengan fenomena yang terjadi, pada kondisi setelah pencelupan cepat, paduan Al yang diberikan pencanaian panas pada temperatur 400 dan 475 °C mengalami peristiwa pemulihan, sementara pada 550 °C sudah terjadi rekristalisasi. Selanjutnya pada kondisi setelah penuaan, paduan Al hasil pencanaian panas pada temperatur 550 °C yang diikuti penuaan pada temperatur 180 °C selama 8 jam menghasilkan kekerasan yang paling tinggi diantara perlakuan lainnya.

---

Aluminum is a light and ductile metal which has the second most uses in industrial world after iron and steel. One aluminum alloy that has wide application is Al-Mg-Si which belongs to the aluminum 6xxx series. Increasing the strength of Al-Mg-Si alloys can be done through ageing treatment and hot working, which can be combined to produce T5 heat treatment. This research combined hot rolling with solution treatment followed by ageing, which was applied on Al-1.01Mg-0.58Si (Wt. %) alloy produced through the squeeze casting process. The temperatures of hot rolling were varied to 400, 475, and 550 °C with a percent deformation of 10 %, meanwhile artificial ageing was carried out at 180 °C for 0-200 hours. The characterization included chemical composition testing, hardness testing, metallographic observation by optical microscope and SEM-EDS (Scanning Electron Microscope-Energy Dispersive Spectroscopy), as well as XRD (X-Ray Diffraction) testing. The results showed that an increased in heating or solution treatment temperature increased the dissolution of the second phase into the matrix, accelerate dynamic recrystallization event, and trigger a better ageing response. This is showed by phenomenon that occurred, on the as-quenched condition, only recovery occurred to alloy that was given hot rolling at temperature of 400 and 475 °C, while at 550 °C the recrystallization occurred. On the as-aged condition, the alloy that was given hot rolling at 550 °C followed by ageing at 180 °C for 8 hours exhibits a higher hardness than other treatments."