"Peningkatan kekerasan pada material baja karbon dapat dilakukan dengan perlakuan panas quenching, pada baja karbon menengah hanya sedikit waktu yang diizinkan untuk mencapai fasa martensit sehingga medium quench dengan konduktivitas termal tinggi dibutuhkan. Multi wall carbon nanotube (MWCNT) memiliki konduktivitas termal yang sangat tinggi dikarakterisasi menggunakan Scanning Electron Microscope (SEM) dan Energy Dispersive X-Ray Spectroscopy (EDAX), lalu disintesis menjadi nanofluida dengan penambahan surfaktan Polyethylene Glycol (PEG) dan dilarutkan dalam air distilasi. Nanofluida di ultrasonikasi selama 15 menit untuk mencegah aglomerasi dan dilakukan pengujian konduktivitas termal serta zeta potensial yang bertujuan untuk mengukur kestabilan nanofluida. Variasi konsentrasi nanopartikel sebesar 0.1%, 0.3%, dan 0.5% dan untuk surfaktan sebesar 0%, 3%, 5%, dan 7%. Setelahnya, nanofluida digunakan sebagai medium quench dengan waktu pencelupan 4 menit dan sampel pada baja S45C dilakukan pengujian mikrostruktur dan kekerasan. Pada hasil didapatkan data bahwa penambahan nanopartikel tidak berpengaruh secara signifikan terhadap konduktivitas termal dan surfaktan PEG cenderung menurunkan nilai konduktivitas termal. Pada semua sampel yang telah dilakukan perlakuan panas diikuti dengan quench terbentuk martensite, tetapi nilai konduktivitas termal juga tidak berbanding lurus dengan kemampuan medium quench untuk meningkatkan kekerasan. Konsentrasi MWCNT 0,3% dengan surfaktan 0% menunjukan nilai konduktivitas tertinggi, sedangkan untuk hasil kekerasan tertinggi dicapai oleh media quench air.

---

Hardening on carbon steel material can be achieved with heat treatment quenching, for medium carbon steel only a little time is allowed to attain martensite phase therefore high thermal conductivity quench medium is needed. Multi wall carbon nanotube (MWCNT) has very high thermal conductivity was characterized with Scanning Electron Microscope (SEM) and Energy Dispersive X-Ray Spectroscopy (EDAX), then it synthesized as nanofluids by adding some polyethylene glycol (PEG) surfactant and dissolved in distilled water. Nanofluids were ultrasonicated for 15 minutes to prevent agglomeration and tested for thermal conductivity also for zeta potential to measure nanofluids stability. Nanoparticle concentration varies from 0.1%, 0.3%, and 0.5% and for surfactants varies from 0.0%, 3%, 5%, and 7%. Afterward, nanofluids were used as a quench medium with immersion time of 4 minutes and for S45C steel samples were tested for its microstructure and hardness. The results show nanoparticle addition not significantly affecting the thermal conductivity and PEG as surfactant tends to decrease thermal conductivity. On all heat-treated samples followed by quench martensite phase are obtained, however thermal conductivity values are also not directly proportional to quench medium ability to increase the hardness. 0,3% MWCNT along with 0% PEG concentration give the highest thermal conductivity result, while for hardness achieved by using water quench medium."

"Carbon Nanotube (CNT) merupakan material yang memiliki banyak keunggulan, salah satunya adalah nilai konduktivitas termal yang tinggi. Oleh karena itu, CNT sangat banyak digunakan untuk aplikasi perpindahan panas, salah satunya nanofluida. CNT adalah molekul silindris yang terdiri dari lembaran-lembaran atom karbon lapisan tunggal (graphene). CNT dapat berlapisan tunggal atau single-walled CNT (SWCNT) atau multi- walled (MWCNT). Dalam penelitian ini menggunakan MWCNT as-received yang dikarakterisasi dengan menggunakan Energy Dispersive Spectroscopy (EDS) dan Scanning Electron Microscope (SEM). Nanofluida berbasis CNT disintesis dengan menambahkan konsentrasi CNT sebesar 0,01%, 0,03%, dan 0,05% serta surfaktan Polyethylene Glycol (PEG) sebanyak 10%, 20%, dan 30% pada fluida dasar yaitu air distilasi. Penambahan surfaktan bertujuan untuk menjaga kestabilan dari nanofluida. Nanofluida kemudian dilakukan ultrasonikasi selama 15 menit untuk melarutkan dan meningkatkan stabilitas nanofluida. Nanofluida kemudian dilakukan pengujian konduktivitas termal dan zeta potensial yang kemudian dibandingkan dengan analisis literatur. Penambahan konsentrasi CNT pada nanofluida meningkatkan nilai konduktivitas termal nanofluida. Penambahan konsentrasi surfaktan PEG sebanyak 20% dan 30% menurunkan konduktivitas termal nanofluida. Penurunan nilai konduktivitas termal terjadi akibat penambahan surfaktan yang sudah melewati batas optimal. Stabilitas nanofluida diukur dengan nilai zeta potensial. Kestabilan nanofluida berbasis CNT meningkat setelah ditambahkannya surfaktan PEG.

---

Carbon Nanotube (CNT) is a material that’s known to have a high thermal conductivity value. Therefore, CNT is very widely used for heat transfer applications, one of which is to make nanofluids. CNT is a cylindrical molecule consisting layers of single layer carbon atom sheets (graphene). CNTs can be single walled (SWCNT) or multi- walled (MWCNT). In this study, MWCNT as-received was characterized by using Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscope (SEM). CNT-based nanofluids were synthesized by adding 0.01%, 0.03%, and 0.05% of CNT particles and 10%, 20%, and 30% Polyethylene Glycol (PEG) surfactants to the base fluid, distilled water. The addition of surfactants is to maintain the stability of nanofluids. The nanofluid was ultrasonicated for 15 minutes to increase its stability. The nanofluid was tested for thermal conductivity and zeta potential which were then compared with literature analysis. The addition of CNT to nanofluids increases the value of the nanofluids’ thermal conductivity. The addition of PEG surfactant concentrations by 20% and 30% decreases the thermal conductivity of nanofluids. The decrease in the value of thermal conductivity occurs due to the addition of surfactants that have passed the optimal limit. The stability of nanofluid was measured by the potential zeta value. The stability of CNT-based nanofluids increases after the addition of PEG surfactants."

"Media quench merupakan salah satu bahan penting dalam proses quenching. Bahan ini yang akan menentukan kecepatan pendinginan yang terjadi dalam proses pendinginan tersebut seperti fluida termal. Pada penelitian ini, fluida termal di sintesa dengan menggunakan partikel MWCNT dengan konsentrasi 0.1%, 0.3% dan 0,5% dan air sebagai fluida dasarnya dengan tujuan akhir terbentuknya nanofluida. Penambahan PEG surfaktan digunakan dengan konsentrasi 0%, 10%, 20%, dan 30%. Nanofluida digunakan sebagai quenchant untuk mengimersi baja karbon S45C setelah melalui proses austenisasi pada suhu 900°C. Untuk mengetahui pengaruh media quench nanofluida ini, proses karakterisasi terhadap sampel partikel MWCNT, fluida termal, dan baja S45C sebelum dan sesudah quenching dilakukan. Hasil penelitian menunjukkan partikel MWCNT yang digunakan memiliki ukuran lebih besar daripada nanopartikel pada umumnya, sehingga nanofluida tidak terbentuk. Fluida termal dengan konsentrasi MWCNT dan PEG surfaktan yang optimal memiliki nilai konduktivitas termal yang lebih tinggi daripada air atau quenchant konvensional. Walaupun penambahan surfaktan dapat meningkatkan nilai zeta potensial dari fluida termal, namun hal ini tidak memiliki tren yang jelas terhadap konduktivitas termalnya. Penambahan konsentrasi dari PEG surfaktan seringkali menurunkan nilai konduktivitas termal. Hasil dari kekerasan baja karbon S45C menunjukkan tidak ada pengaruh secara langsung dari konduktivitas termal quenchant yang digunakan terhadap kekerasan baja S45C. Karena nilai kekerasan meningkat seiring dengan bertambahnya konsentrasi PEG surfaktan pada fluida termal.

---

Quench media is one of the important materials in the quenching process. This material characterization can determine the cooling rate that occurs in the process like a thermal fluid. In this research, thermal fluid is synthesised by using MWCNT particles with the varies of concentration is 0.1%, 0.3%, and 0,5% and water as the base fluid with the final purpose is fabricating nanofluid solution. The addition of PEG surfactant will be in varied concentrations 0%, 10%, 20% and 30%. Nanofluid is used as quenchant to immerse S45C carbon steel after austenization process at 900°C. To examine the effect of this nanofluid as quench media, characterization process is done to MWCNT particles, thermal fluid, and S45C carbon steel before and after quenching process. The result shows MWCNT particles have larger size than nanoparticles, thus the colloid solution is not classified as nanofluid. Thermal fluid with the optimum concentration of MWCNT and PEG has higher thermal conductivity than water or conventional quenchant. Although the addition of surfactant can increase thermal fluid zeta potential, it does not have clear trends towards its thermal conductivity. The addition of PEG surfactant concentration often decreases the thermal conductivity value. Hardness testing result of the specimen indicates no direct effect of quenchant thermal conductivity towards S45C carbon steel hardness because the hardness value is increasing along with the addition of PEG surfactant concentration in nanofluid."

"Pada penelitian nanofluida yang dilakukan akhir-akhir ini molekul Carbon Nanotube (CNT) merupakan salah satu molekul nano yang sering digunakan, hal ini karena CNT memiliki nilai konduktivitas termal yang tinggi dan memiliki karakterisasi yang unggul, CNT sendiri dibagi menjadi dua jenis berlapisan tunggal atau single-walled CNT (SWCNT) dan multi-walled (MWCNT). Dalam penelitian ini menggunakan MWCNT as-received yang dikarakterisasi dengan menggunakan Energy Dispersive Spectroscopy (EDS) dan Scanning Electron Microscope (SEM). Nanofluida berbasis CNT disintesis dengan menambahkan konsentrasi CNT sebesar 0,1%, 0,3%, dan 0,5% serta surfaktan sodium dodecylbenzenesulfonate (SDBS) sebanyak 10%, 20%, dan 30% pada fluida dasar yaitu air distilasi yang kemudian didispersikan menggunakann alat ultrasonikasi selama 15 menit. Kemudian nanofluida akan dikarakterisasi nilai zeta potensial dan konduktivitas termalnya di suhu ruang (25oC). nanofluida sebanyak 100ml yang sudah dikarakterisasi kemudian akan digunakan untuk proses quenching atau perlakuan panas pada baja S45C, sebelumnya baja S45C sudah diaustenisasi di suhu 900oC. Baja S45C hasil perlakuan panas akan dikarakterisasi menggunakan mikroskop optik dan rockwell hardness C. Penambahan konsentrasi CNT tanpa surfaktan pada nanofluida menaikan konduktivitas termal nanofluida, namun penambahan surfaktan konsentrasi tinggi (10%, 20%, dan 30%) pada nanofluida menurunkan konduktivtas termal nanofluida. Nilai zeta potensial dari nanofluida meningkat seiring dengan bertambahnya konsentrasi surfaktan, zeta potensial dapat mengukur stabilitas nanofluida. Hubungan konduktivitas termal dan kekerasan baja S45C hasil perlakuan panas menggunakan nanofluida tidak dapat dihubungkan secara linier walaupun terlihat tren semakin tinggi konduktivitas termal, maka nilai kekerasan akan semakin tinggi. Hal tersebut terjadi karena proses perlakuan panas dilakukan di temperatur tinggi yang dapat mempengaruhi stabilitas nanofluida. Mikrostruktur Baja S45C hasil perlakuan panas dengan media quench dengan konsentrasi SDBS 0% hingga 10% memiliki mikrostruktur yang didominasi martensite, sedangkan untuk konsentrasi SDBS 20-30% mikrostruktur baja didominasi dengan pearlite, ferrite dan sedikit widmanstätten ferrite.

---

In recent nanofluid research, Carbon Nanotube (CNT) are one of the nano-molecules that are often used in studies, this is because CNT’s have a high thermal conductivity value and have superior characterization. There are two kinds of CNT, Single-walled CNT (SWCNT) and multi-walled (MWCNT). In this study, the as-received MWCNT is characterized by using Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscope (SEM). CNT-based nanofluids were synthesized by adding 0.1%, 0.3%, and 0.5% CNT and as much as 10%, 20%, and 30% surfactant sodium dodecylbenzenesulfonate (SDBS) in the base fluid, namely distilled water which was then dispersed. using ultrasonication tool for 15 minutes. Then the nanofluid will be characterized by its zeta potential value and thermal conductivity at room temperature (25oC). 100ml of nanofluid that has been characterized will then be used for the quenching process or heat treatment on S45C steel, previously S45C steel has been austenized at 900oC. Heat treated S45C steel will be characterized using an optical microscope and rockwell hardness C. The addition of CNT concentrations without surfactants in nanofluids increased the thermal conductivity of nanofluids, but the addition of high concentrations of surfactants (10%, 20%, and 30%) in nanofluids decreased the thermal conductivity of nanofluids. The zeta potential value of nanofluids increases with increasing surfactant concentration, the zeta potential can measure the stability of nanofluids. The relationship between thermal conductivity and hardness of the heat treated S45C steel cannot be linearly related, although the trend is that the higher the thermal conductivity, the higher the hardness value. This happens because the heat treatment process is carried out at high temperatures which can affect the stability of the nanofluid. The microstructure of the heat treated S45C steel with nanofluids quenchant with a concentration of 0% to 10% SDBS has a predominantly martensite microstructure, while for an SDBS 20-30% concentration the steel microstructure is dominated by pearlite, ferrite and a little widmanstätten ferrite."

"Kekerasan yang tinggi pada sebuah material dapat dicapai dengan melakukan proses perlakuan panas menggunakan media quench yang memiliki nilai konduktivitas termal yang tinggi, seperti nanofluida. Pada penelitian ini, nanofluida berbasis CNT disintesis menggunakan metode 2 tahap, yaitu dengan mendispersikan CNT dengan konsentrasi sebesar 0,1%, 0,3%, dan 0,5% ke dalam fluida dasar berupa air distilasi yang kemudian ditambahkan surfaktan Cetyl Trimethylammonium Bromide (CTAB) sebanyak 0%, 3%, 5%, dan 7% untuk meningkatkan stabilitasnya, lalu dilakukan ultrasonikasi. Nanofluida tersebut kemudian digunakan sebagai media quench pada sampel baja S45C. Proses perlakuan panas dilakukan dengan memanaskan baja hingga suhu 900ºC kemudian di quenching. Baja hasil quenching diamati mikrostrukturnya dan dihitung nilai kekerasannya. Konduktivitas termal nanofluida mengalami penurunan saat digunakan surfaktan CTAB 3%, lalu mengalami peningkatan saat digunakan surfaktan CTAB 5%, dan menurun kembali saat digunakan surfaktan CTAB 7% dengan nilai konduktivitas termal tertinggi diperoleh oleh sampel nanofluida pada konsentrasi CNT 0,3% dengan surfaktan CTAB 5%, yaitu sebesar 0,72 W/mK. Sementara nilai kekerasan tertinggi untuk baja yang di quenching dengan nanofluida adalah sebesar 39 HRC, yaitu ketika digunakan konsentrasi 0,1% CNT tanpa penambahan surfaktan.

---

High hardness of a material can be achieved by doing heat treatment using a quench medium that has a high thermal conductivity value, such as nanofluids. In this study, CNT-based nanofluids were synthesized using a 2-step method, which by dispersing CNT with concentrations of 0.1%, 0.3%, and 0.5% into the base fluid in the form of distilled water which was then added with surfactant Cetyl Trimethylammonium Bromide (CTAB) as much as 0%, 3%, 5%, and 7% to increase their stability, then ultrasonication was performed. The nanofluid was then used as a quench medium for the S45C steel sample. The heat treatment process is carried out by heating the steel to a temperature of 900ºC then quench it. The quenched steel was observed for its microstructure and the hardness was calculated. The thermal conductivity of nanofluids decreased when 3% CTAB surfactant was used, increased when 5% CTAB surfactant was used, and decreased when 7% CTAB surfactant was used with the highest thermal conductivity value obtained by nanofluid samples at 0.3% CNT concentration with 5% CTAB surfactant, which the value is 0.72 W/mK. Meanwhile, the highest hardness value for steel quenched with nanofluids was 39 HRC, when 0.1% CNT was used without the addition of surfactants."

"Quenchant dengan konduktivitas termal tinggi dapat meningkatkan lajupendinginan, sehingga didapat hasil perlakuan panas dengan sifat mekanis yang lebihbaik. Salah satu cara meningkatkan konduktivitas termal adalah dengan membuatnanofluida. Pada penelitian ini, digunakan nanopartikel berupa Multi-walled CarbonNanotubes (MWCNT) as-received. Nanofluida berbasis CNT disintesis menggunakanmetode dua tahap. CNT dengan konsentrasi sebesar 0,1%, 0,3%, dan 0,5%didispersikan pada fluida dasar berupa air distilasi. Untuk meningkatkan stabilitasnanofluida, ditambahkan surfaktan Sodium Dodecyl Benzene Sulphonate (SDBS)sebanyak 3%, 5%, dan 7% serta dilakukan ultrasonikasi selama 15 menit. Nanofluidatersebut digunakan sebagai quenchant dengan lama imersi 4 menit untuk prosesperlakuan panas baja S45C dengan temperatur austenisasi sebesar 900˚C. Hasilpenelitian menunjukkan bahwa konduktivitas termal nanofluida meningkat seiringdengan penambahan konsentrasi CNT, kecuali pada sampel tanpa penambahansurfaktan. Seiring penambahan surfaktan, konduktivitas termal meningkat hinggamencapai kadar optimum dan kemudian menurun, kecuali pada sampel denganpenambahan surfaktan sebanyak 3%. Nilai kekerasan baja S45C hasil quenching tidakdipengaruhi secara linear oleh konduktivitas termal quenchant.

---

Quenchant with high thermal conductivity could increase the cooling rate;

hence heat treatment results with better mechanical properties are obtained. One

method to increase the thermal conductivity is by creating nanofluids. In this study,

Multi-walled Carbon Nanotubes (MWCNT) as-received were used as nanoparticles.

The CNT-based nanofluids were synthesized using the two-step method. CNTs with

concentrations of 0.1%, 0.3%, and 0.5% were dispersed to the base fluid, distilled

water. To increase the stability of the nanofluids, Sodium Dodecyl Benzene Sulphonate

(SDBS) surfactants as much as 3%, 5%, and 7% were added; further, ultrasonication

was carried out for 15 minutes. The nanofluids were used as quenchants with an

immersion time of 4 minutes for the heat treatment process of S45C steel with an

austenitizing temperature of 900˚C. The results showed that the thermal conductivity of

nanofluids increased with the addition of CNT concentration, except for samples

without the addition of surfactants. On the other side, as more surfactants were added,

the thermal conductivity increased until it reached the optimum level and then

decreased, except for samples with 3% surfactant. The hardness values of quenched

S45C steels are not linearly affected by the thermal conductivity of the quenchants."

"Media pendingin dapat di tingkatkan performanya dengan menggunakan nanofluida, dengan cara menggunakan nanopartikel didalam fluida untuk meningkatkan kecepatan laju pendinginan, salah satunya dengan meningkatkan konduktivitas termal. Di dalam penelitian ini, nanopartikel yang digunakan adalah Carbon Nanotubes dengan persentase 0,1%, 0,3%, dan 0,5% yang akan disintesis menjadi nanofluida dengan metode 2 tahap, setelah itu akan ditambahkan surfaktan Cetyl Trimethylammonium Bromide (CTAB) sebesar 10%, 20%, dan 30% untuk menstabilkan nanofluida. Setelah itu nanofluida yang sudah diperoleh dilakukan proses ultrasonikasi selama 15 menit. Setelah itu dilakukan proses pendinginan cepat menggunakan baja S45C dengan nanofluida sebagai media pendingin dengan suhu austenisasi 900oC. Didapatkan hasil dari penelitian bahwa nilai dari konduktivitas termal yang didapat menurun seiring dengan penambahan surfaktan, dimana pada penelitian didapatkan konduktivitas termal tertinggi berada pada variabel dengan tanpa adanya tambahan surfaktan, kecuali di sampel dengan CNT 0,1%.  Hasil optimal dari nilai kekerasan dan juga konduktivitas termal terdapat pada variabel dengan konsentrasi CNT 0,1% dengan penambahan surfaktan CTAB sebanyak 10%. Didapatkan nilai kekerasan maksimal sebesar 23 HRC, dan nilai konduktivitas termal terbesar berada di angka 0,64 W/mK.

---

The cooling media performance can be improved by using the nanofluids, by using nanoparticles in the fluid to increase the speed of cooling rate, one of which is by increasing thermal conductivity. In this study, the nanoparticles used are Carbon Nanotubes with a percentage of 0.1%, 0.3%, and 0.5% which will be synthesized into nanofluids by a 2-stage method. After that, it will be added surfactant Cetyl Trimethylammonium Bromide (CTAB) by 10%, 20%, and 30% to stabilize nanofluids. After that nanofluids that have been obtained are processed by ultrasonication for 15 minutes. After that, a rapid cooling process is carried out using S45C steel with nanofluids as a cooling medium with an austenization temperature of 900oC. The results of the study found that the value of thermal conductivity obtained decreased along with the addition of surfactants, where in the study obtained the highest thermal conductivity was in variables with no additional surfactant, except in samples with CNT 0.1%.  The optimal result of hardness values and thermal conductivity is found in variables with a CNT concentration of 0.1% with the addition of 10% CTAB surfactants. The maximum hardness value is 23 HRC, and the largest thermal conductivity is 0.64 W/mK."

"Nanofluida memiliki nilai konduktivitas termal yang baik sehingga baik untuk digunakan sebagai media pendingin bagi perlakuan panas baja. Nanofluida pada penelitian ini akan menggunakan nanopartikel carbon nanotube dan akan ditambahkan surfafktan berupa Sodium Dodecyl Benzene Sulphonate atau SDBS untuk membantu menstabilkan nanofluida. Untuk mengkarakterisasi nanopartikel dilakukan pengujian Field-Emission Scanning Electron (FE-SEM) dan Energy Dispersive X-Ray Spectroscopy (EDS) untuk melihat bentuk struktur carbon nanotube serta mengetahui komposisi dari carbon nanotube dan didapatkan hasil berupa 100% Wt% C. Nanofluida lalu difabrikasi dengan cara menimbang serbuk carbon nanotube as-received dengan variabel konsentrasi 0,01%, 0,03%, dan 0,05% dan dimasukkan ke dalam beaker 100 mL. Variabel dari konsentrasi surfaktan SDBS yang digunakan adalah 0%, 10%, 20%, dan 30%. Dispersi dari nanopartikel lalu dilakukan dengan mencampurkan bahan-bahan berupa nanopartikel dan surfaktan serta air distilasi lalu diultrasonifikasi selama 15 menit untuk melarutkan fluida. Setelah itu dilakukan pengujian konduktivitas termal sebanyak 10 kali menggunakan alat pengukur konduktivitas termal KD2 pada masing-masing variabel lalu dirata-rata. Selain itu dilakukan juga pengujian Zeta Potensial untuk melihat nilai potensial zeta dari nanofluida yang menujukkan kestabilan dari nanofluida sendiri. Semakin stabil suatu nanofluida, semakin baik ia dalam menghantarkan atau mengkonduksi panas.

---

Nanofluids have good thermal conductivity, so they are good for use as a cooling medium for steel heat treatment. Nanofluids in this research will use carbon nanotube nanoparticles and surfafktan in the form of Sodium Dodecyl Benzene Sulphonate or SDBS will be added to help stabilize the nanofluids. To characterize nanoparticles, Field-Emission Scanning Electron (FE-SEM) and Energy Dispersive X-Ray Spectroscopy (EDS) tests were performed to see the structure of carbon nanotubes and to determine the composition of carbon nanotubes and the results were 100% Wt% C. Nanofluids then fabricated by weighing as-received carbon nanotube powder with variable concentrations of 0.01%, 0.03%, and 0.05% and put into a 100 mL beaker. Variables of SDBS surfactant concentrations used were 0%, 10%, 20%, and 30%. The dispersion of the nanoparticles is then carried out by mixing the materials in the form of nanoparticles and surfactants and distilled water and then ultrasonification for 15 minutes to dissolve the fluid. After that the thermal conductivity test was conducted 10 times using a KD2 thermal conductivity meter on each variable then averaged. Potential Zeta testing is also carried out to see the zeta potential value of the nanofluid that shows the stability of the nanofluid itself. The more stable a nanofluid is, the better it is at delivering or conducting heat."

"Peningkatan sifat mekanik material dalam rekayasa mikrostruktur memiliki salah satu proses penting yaitu pendinginan cepat. Karbon aktif berbasis tempurung kelapa sawit ditumbuk halus untuk mereduksi ukuran karbon. Setelah karbon dihaluskan, proses penggilingan dilakukan untuk kembali mereduksi ukuran partikel menjadi lebih kecil menggunakan planetary ball mill dengan kecepatan 500 rpm selama 15 jam serta ditambahkan aditif Polyvinyl Alcohol (PVA). Surfaktan yang digunakan berupa Polyethylene Glycol (PEG) memiliki tujuan untuk mengurangi aglomerasi partikel sehingga dapat meningkatkan konduktivitas termal secara optimal. Penelitian ini menggunakan variasi konsentrasi partikel karbon berbasis tempurung kelapa sawit sebesar 0,1%, 0,3%, dan 0,5% serta konsentrasi surfaktan 0%, 10%, dan 20%. Karakterisasi nanopartikel karbon tempurung kelapa sawit menggunakan Energy Dispersive Spectroscopy (EDS) dan Field-Emission Scanning Electron Microscope (FE- SEM) untuk mengamati unsur, komposisi, serta morfologi partikel. Karakterisasi nanofluida menggunakan Particle Size Analyzer (PSA), uji Konduktivitas Termal, dan Zeta Potensial untuk mengamati ukuran partikel, konduktivitas termal nanofluida, dan stabilitas dari nanofluida dari karbon berbasis tempurung kelapa sawit.

---

ABSTRACTMechanical properties enhancement in microstructure modification has one important process called quenching. Palm kernell shell ash-based active carbon was crushed in order to reduce the carbon size. After carbon was crushed, the particle went through grinding process to reduce the size furthermore using planetary ball mill at 500 rpm for 15 hours and with Polyvinyl Alcohol addition. Polyethylene Glycol used as surfactant to reduce agglomeration between particle so that the thermal conductivity can be optimally improved. This research used variation of palm kernelll shell-based carbon concentration 0.1%, 0.3%, and 0.5% and surfactant concentration 0%, 10%, and 20%. Palm kernell shell-based carbon nanoparticle was characterized by Energy Dispersive Spectroscopy (EDS) and Field-Emission Scanning Electron Microscope (FE-SEM) to observe element, composition, and particle morphology. Nanofluids was characterized using Particle Size Abalyzer (PSA), Thermal Conductivity Test, and Zeta Potential Test to observe particle size, thermal conductivity of nanofluids, and palm oil kernell-based carbon nanofluids stability."

"ABSTRAKNanopartikel digunakan untuk menghasilkan nanofluida yang mempunyai stabilitas dan dispersi yang baik sehingga menghasilkan konduktivitas termal yang maksimal. Telah dilakukan penelitian pengaruh Polyethylene Glycol (PEG) terhadap transfer panas nanofluida berbasis karbon arang tempurung kelapa dan tempurung kelapa sawit. Karbon dari arang tempurung kelapa dan tempurung kelapa sawit melalui pemrosesan tertentu menjadi partikel karbon aktif. Partikel karbon aktif ditumbuk halus dan direduksi kembali agar dapat mencapai ukuran nano dengan menggunakan alat planetary ball mill dengan metode top-down selama 15 jam dengan kecepetan putaran 500 rpm. Sintesis nanofluida dilakukan dengan mendispersikan nanopartikel karbon dari arang tempurung kelapa dan tempurung kelapa sawit ke dalam fluida air distilasi. Pada penelitian ini dikaji pengaruh penambahan PEG terhadap karakteristik nanofluida berbasis karbon dari arang tempurung kelapa dan tempurung kelapa sawit. Karakterisasi nanopartikel karbon dari arang tempurung kelapa dan tempurung kelapa sawit yang dilakukan adalah menggunakan Field-Emission Scanning Electron Microscope (FE-SEM), dan Energy Dispersive Spectroscopy (EDS) untuk mengamati komposisi dan unsur partikel, morfologi partikel dan ukuran partikel agar dapat dibandingkan. Hasil EDS menunjukan partikel karbon dari arang tempurung kelapa memiliki 60,77 wt% karbon sedangkan partikel karbon dari arang tempurung kelapa sawit mengandung 78,08 wt% karbon dan terdapat banyak unsur pengotor pada kedua nya. Karakterisasi FE-SEM menunjukan partikel karbon membentuk aglomerasi. Karakterisasi nanofluida yang dilakukan adalah pengukuran Particle Size Analyzer (PSA), zeta potensial dan konduktivitas termal. Variabel yang digunakan adalah konsentrasi partikel karbon dari arang tempurung kelapa dan tempurung kelapa sawit masing-masing adalah 0%, 0,1%, dan 0,3% lalu dengan penambahan surfaktan PEG dengan konsentrasi 0%, 10% dan 20%.

---

ABSTRACT

Nanoparticles are used to produce nanofluids which have a good stability and good dispersion resulting in maximum thermal conductivity. This research study conduct the effect of Polyethylene Glycol (PEG) on heat transfer carbon-based nanofluids based on coconut shell ash particles and palm shell ash particles. Coconut shell carbon and palm shell ash carbon through certain process to become activated carbon particles. The activated carbon particles are finely ground and reduced again to reach nano size by using a planetary ball mill with a top-down method for 15 hours with a speed of 500 rpm rotation. Synthesis of nanofluids was carried out by dispersing carbon shells and coconut shell nanoparticles into distilled water fluid. In this study the effect of PEG on the characteristics of carbon-based nanofluids based on coconut shell and palm shell ash. Characterization of carbon nanoparticles of coconut shell and palm shell is done using Field-Emission Scanning Electron Microscope (FE-SEM), and Energy Dispersive Spectroscopy (EDS) to use materials and particles, morphology and particle size to be used. The EDS results showed that the coconut shell carbon particles had 60.77% carbon while the coconut shell carbon particles contained 78.08% by weight of carbon and both contained many impurities. The FE-SEM characterization shows carbon particles to form agglomeration. The nanofluid characterization carried out was the measurement of Particle Size Analyzer (PSA), zeta potential and thermal conductivity. The variables used are the composition of carbon particles of coconut shell and oil palm shell are 0%, 0.1%, and 0.3%, then the composition of surfactant PEG with concentrations of 0%, 10% and 20%.

"