Hasil Pencarian  ::  Simpan CSV :: Kembali

"

Lapisan paduan NiCoFeCr telah berhasil disintesis menggunakan metode elektrodeposisi dengan penambahan zat aditif Na-sakarin dalam pengaruh arus deposisi sebesar-25mA selama lima menit pada suhu ruang. Pengaruh komposisi Kromium (Cr) sebesar 0 hingga 39,78at% Cr terhadap struktur, morfologi, dan sifat magnetik lapisan paduan NiCoFeCr telah diteliti. Berdasarkan hasil X-Ray Diffractometer (XRD), peningkatan komposisi Cr tidak mengubah struktur kristal FCC dan space group Fm-3m. Hasil karakterisasi Scanning Electron Microscopy (SEM) menunjukkan terbentuknya microvoids dan microcracks yang diindikasikan oleh evolusi gelembung gas hidrogen ketika komposisi Cr bertambah. Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) menunjukkan sifat feromagnetik berdasarkan hasil Vibrating Sample Magnetometer (VSM). Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) mengalami penurunan saturasi magnetisasi (Ms) sebesar 159,85 emu/g hingga 4,20 emu/g dan mengalami peningkatan koersivitas (Hc) sebesar 51,84 Oe hingga 257,73 Oe. Peningkatan komposisi Cr menyebabkan saturasi magnetisasi (Ms) menurun dan koersivitas (Hc) meningkat.

 

---

NiCoFeCr film alloys were synthesized using the electrodeposition method by adding Na-saccharin additives under the deposition current of -25mA for five minutes at room temperature. The effect of chromium (Cr) addition with composition 0 to 39.78at%  on the structure, morphology, and magnetic properties were investigated. From the X-Ray Diffractometer (XRD) results, the increase in Cr composition does not change the FCC crystal structure and Fm-3m space group. The result of the Scanning Electron Microscopy (SEM) observation reveals a formation of microvoids and microcracks indicated by the evolution of hydrogen gas bubbles when the Cr composition is increased. The NiCoFeCr (0 to 39.78at% Cr) film alloys exhibit ferromagnetic properties based on the results of the Vibrating Sample Magnetometer (VSM). The saturation magnetization (Ms) and coercivity (Hc) of NiCoFeCr (0 to 39.78at% Cr) varied between 159.85 emu/g to 4.20 emu/g and 51.84 Oe to 257.73 Oe, respectively. The decrease in saturation magnetization (Ms) and the increase in coercivity (Hc) values are due to an increase in Cr composition.

"

"Material lapisan Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) disintesis dengan metode elektrodeposisi pada substrat ITO-PET. Struktur kristal, fasa material, sifat magnetik dan perubahan resistivitas akibat pengaruh komposisi Ni80CoxFe20-x diteliti melalui karakterisasi X-Ray Diffractometer (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS)-Mapping, Vibrating Sample Magnetometer (VSM), dan metode Four-Point Probe pada Cryogenic Magnetometer (Oxford Teslatron Instrument). Hasil XRD menunjukkan struktur kristal FCC dengan space group Fm3m. Komposisi dari seluruh sampel mencapai komposisi target (dengan toleransi ±5) dan homogenitas yang baik melalui karakterisasi EDS-Mapping dan SEM. Hasil VSM menunjukkan seluruh sampel merupakan material soft feromagnetik pada suhu ruang. Seluruh sampel berhasil menghasilkan lapisan dengan saturasi magnetisasi >80 emu/gram dan nilai koersivitas <250 Oe. Kelima sampel memiliki rentang saturasi magnetisasi dari 90,387-159,792 emu/g dan koersivitas dari 95,84-191,33 Oe di mana saturasi magnetisasi tertinggi terjadi pada komposisi Ni80Co10Fe10 sedangkan koersivitas terendah terjadi pada komposisi Ni80Co15Fe5. Pengujian nilai resistivitas listrik terhadap perubahan temperatur (5-300 K) menunjukkan bahwa seluruh sampel bersifat konduktor dikarenakan nilai resistivitasnya meningkat seiring dengan meningkatnya temperatur. Hasil penelitian ini menunjukkan bahwa komposisi suatu material memengaruhi sifat magnetik dan nilai resistivitasnya. Komposisi lapisan Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) yang memiliki fasa tunggal, lapisan yang homogen, komposisi yang mencapai target, bersifat soft magnetic dengan koersivitas rendah (<250 Oe) dan saturasi magnetisasi yang tinggi (>80 emu/gram) serta perubahan resistivitas yang kecil terhadap temperatur adalah x = 15, yaitu Ni80Co15Fe5.

---

Films of Ni80CoxFe20-x (x = 0, 5, 10, 15, and 20) was synthesized by electrodeposition method on ITO-PET substrate. The crystal structure, material phase, magnetic properties and change of resistivity as a result of composition changes on Ni80CoxFe20-x was characterized by X-Ray Diffractometer (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS)-Mapping, Vibrating Sample Magnetometer (VSM), and Four-Point Probe Method using Cryogenic Magnetometer (Oxford Teslatron Instrument). XRD results show FCC crystal structure with the Fm3m space group. The composition of all samples was successfully close to the target composition (with ±5 tolerance) and even homogeneity through EDS-Mapping and SEM. VSM results show that all samples are soft ferromagnetic in room temperature. All samples successfully achieve saturation of magnetization >80 emu/gram and coercivities <250 Oe. All samples resulted with saturation of magnetization ranging from 90,387-159,792 emu/g and coercivity ranging from 95,84-191,33 Oe where the highest saturation of magnetization was found at the composition of Ni80Co10Fe10 while the lowest coercivity was found at the composition of Ni80Co15Fe5. Characterization of resistivity values under the influence of temperature change (5-300 K) shows that all samples are conductors because of the increase of resistivity values when temperature is increased. The result of this experiment shows that the composition of a material affects the magnetic properties and resistivity value. The composition of Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) films that has a single phase, uniform film, composition that reaches the target, is soft magnetic with low coercevities (<250 Oe) and high saturation of magnetization (>80 emu/gram), and low resistivity value change under the influence of increased temperature is x = 15, that is Ni80Co15Fe5."

"Telah dilakukan penelitian sifat listrik, sifat magnet, dan efek magnetoresistan bahan perovskite manganites La0,67Sr0,33Mn1-XNixO3. Sampel dibuat dengan metode sol gel. Hasil karakterisasi XRD menunjukkan bahwa sampel sudah memiliki fase tunggal dengan struktur rhombohedral dan space group R-3c. Pemberian doping Ni tidak mengubah struktur kristal namun menurunkan nilai parameter kisi kristal. Karakterisasi SEM-EDX menunjukkan bahwa unsur Ni sudah masuk ke dalam sampel dan adanya perubahan morfologi sampel ketika doping Ni divariasikan. Data resistivitas sebagai fungsi temperatur menunjukkan bahwa doping Ni meningkatkan besar resistivitas bahan dan menggeser temperatur transisi metal-isolator ke temperatur yang lebih rendah. Efek magnetoresistan yang diberikan menunjukkan adanya peningkatan persen magnetoresistan saat doping Ni dinaikkan. Sedangkan kurva histerisis yang dihasilkan menunjukkan bahwa pemberian doping Ni menurunkan sifat kemagnetan bahan yang ditunjukkan oleh penurunan magnetisasi bahan.

---

The electrical properties, magnetic properties, and magnetoresistance effect of perovskite manganites La0,67Sr0,33Mn1-XNixO3 material have been studied. Samples were synthesized by using sol gel method. The result of XRD characterization showed that samples were single phase with Rhombohedral structure and R-3c space group. Ni doped did not change crystal structure but decreased lattice parameter. SEM-EDX characterization showed that Ni was included in the samples as a doping and the morphology of samples changed with various Ni doped.

Resistivity as temperature function showed that Ni doped increased the resistivity and decreased the metal-insulator transition temperature. Magnetoresistance effect of samples relatively enhanced with increased of Ni doping. While the hysteresis curve from VSM characterization showed that Ni doped decreased magnetic properties of samples."

"Telah dilakukan penelitian mengenai pengaruh doping nikel terhadap sifat penyerap gelombang mikro pada senyawa La0,67Sr0,33Mn 1-x NixO3 yang disintesis dengan Metode Sol-gel. Karakterisasi XRD menunjukkan bahwa La0,67Sr0,33Mn 1-x NixO3 memiliki fasa tunggal dengan struktur kristal rhombohedral. Dari hasil SEM-EDX terlihat bahwa ukuran partikel cenderung mengecil dan tidak ada unsur lain impuritas pada material. Pengujian dengan menggunakan Cryogenic Magnetometer menunjukan nilai resistivitas terbesar yaitu 1.49 ?m untuk x = 0,3. Hasil karakterisasi VNA menunjukan doping Ni dapat meningkatkan kemampuan penyerapan gelombang mikro. Nilai Reflection Loss terbesar yaitu -11,492 dB untuk x = 0,3<.

---

A research on the effect of nickel doping on microwave absorption properties of La0,67Sr0,33Mn1 xNixO3 had been reported. The samples were synthesized by the sol gel method. The XRD characterization shows that La0,67Sr0,33Mn 1 x NixO3 had a single phase with a rhombohedral crystal structure. SEM EDX results show that there is no other element besides main elements and particle size decrease after doping Ni. Cryogenic Magnetometer showed that the resistivity increase after incoporation of Ni, the largest resistivity is 1,49 for x 0,3. The VNA characterization showed that after doping Ni The microwave absorption properties had been significantly improved. The largest Reflection Loss value is 11.49 dB for x 0,3<."

"Barium Titanate merupakan material feroelektrik dengan konstanta dielektrik yang tinggi, sehingga berpotensi untuk diterapkan menjadi berbagai jenis alat. Namun, Barium Titanate masih mempunyai kelemahan, yaitu terjadinya dielectric loss yang akan menurunkan efisiensi kinerjanya. Pada penelitian ini, dilakukan sintesis Barium Titanate berbentuk film menggunakan metode spin coating. Preparasi dilakukan untuk menghasilkan larutan 0,2 molar, 0,3 molar dan 0,4 molar. Pelapisan dilakukan menggunakan spin coating dengan kecepatan 4000 RPM selama 40 detik untuk membuat lapisan sebanyak 2, 4 dan 6 lapis. Dari penelitian ini diketahui, jika semakin besar konsentrasi dan jumlah lapisan, maka akan semakin besar kapasitansinya, namun akan semakin cenderung terjadi crack.

---

Barium Titanate is ferroelectric materials with high dielectric constant, so that potential to be applied into many devices. However, Barium Titanate still has weakness, i.e. dielectric loss that will lowering the work's efficiency. In this study, Barium Titanate was synthesized onto film by spin coating method. The preparations were done to produce 0,2 molar, 0,3 molar and 0,4 molar solutions. The coatings were done by spin coating with 4000 RPM speed for 40 seconds to produce 2, 4 and 6 layers. This study found that increasing in concentration and number of layer resulting in increasing of capacitance, yet also increasing the tendency to be cracked."

"Pada penelitian ini, pelapisan nikel dilakukan dengan menggunakan metode elektrodeposisi di atas substrat aluminium. Proses elektrodeposisi dilakukan di dalam medium elektrolit nikel sulfat dengan penambahan medan magnet eksternal diintensitas sebesar 0, 800, 1400, dan 1800 Gauss. Banyak penelitian menunjukan adanya peningkatan sifat tahan korosi dari pelapis yang diakibatkan oleh penambahan medan magnet ini. Struktur kristal dan pengaruh medan magnet terhadap preferensi bidang pertumbuhan kristal dari sampel diamati dengan menggunakan pengukuran difraksi sinar-X/ X-ray diffraction (XRD). Polarisasi potensiodinamik linear sweap voltametry (LSV) digunakan untuk mengetahui arus dan potensial korosi yang merepresentasikan perilaku korosi dari sampel. Perubahan morfologi dan tekstur kristal diobservasi menggunakan pengamatan optik. Hasil karakterisasi sampel menunjukan kalau medan magnet membuat ukuran kristal deposit mengecil, mengurangi efek preferensi orientasi kearah bidang tertentu, dan membuat lapisan menjadi lebih halus. Laju korosi dari sampel nikel dibawah pengaruh medan magnet sebesar 0, 800, 1400, dan 1800 Gauss secara berturut-turut adalah 0,0939, 0,039, 0,032, dan 0,0055 mmpy. Peningkatan ketahanan korosi terkorelasi kuat dengan pengecilan ukuran kristal dan lapisan yang lebih halus.

---

In this study, Nickel Plating was carried out using the electrodeposition method on an aluminum substrate. The electrodeposition process was carried out in a Nickel Sulfate electrolyte medium and an external magnetic field was applied with intensities of 800 Gauss, 1400 Gauss, and 1800 Gauss. Many studies have shown an increase in corrosion resistance caused by magnetic fields. The crystal structure and the influence of the magnetic field on the crystal growth field preference of the samples were observed using X-ray diffraction (XRD) measurements. Potentiodynamic polarization linear sweap voltametry (LSV) was used to determine the current and corrosion potential that represented the corrosion behavior of the sample. Changes in the morphology and texture of the crystals were also analyzed using optical observations. The magnetic field reduces the deposit crystal size and reduces the effect of orientation preference. The corrosion rates of nickel samples under the influence of magnetic fields were 0, 800, 1400 and 1800 Gauss respectively 0.0939, 0.039, 0.032 and 0.0055 mmpy. Increased corrosion resistance correlated with reduction in crystal size. The results of optical observations show that the addition of a magnetic field makes the surface of the nickel layer rougher which is also the biggest influence in increasing corrosion resistance."

"Satu seri nanopartikel TiO2 didop Ni dengan variasi konsentrasi Ni dibuat dengan metode kopresipitasi. Komposisi elemen, sifat strukFtur, dan optik dikarakterisasi menggunakan X-Ray Diffraction, Electron Dispersive X-Ray dan UV-VIS diffuse reflectance spectroscopy. Identifikasi spesies paramagnetik dilakukan menggunakan Electron Spin Resonance. Berdasarkan pola difraksi XRD, hanya fase tunggal anatase yang muncul karena radius ionik Ni2+ dan Ti4+ yang hampir sama sehingga dapat menggantikan ion-ion Ti4+ pada kristal TiO2. Ukuran kristal rata-rata menurun seiring dengan peningkatan konsentrasi Ni.Fenomena ini kemungkinan terjadi akibat kehadiran ion-ion Ni2+ yang menghambat pertumbuhan kristal. Spektrum reflektansi difus UV-VIS menunjukkan bahwa penyerapan UV bergeser ke arah panjang gelombang sinar merah dan celah pita energi menurun. Hal ini disebabkan oleh atom-atom Ni yang membentuk levellevel energi localized dibawah pita konduksi pada kristal TiO2. Studi ESR pada nanopartikel TiO2 didop Ni menunjukkan adanya kehadiran Ni+, Ti3+, dan defek oksigen pada semua sampel.

---

A series Ni doped TiO2 nanoparticles with different Ni dopant concentration were facricated by coprecipitation method. The element composition, structural, and optical properties were characterized using X-Ray Diffraction, Electron Dispersive X-Ray and UV-VIS diffuse reflectance spectroscopy. Identification of paramagnetic species are conducted using Electron Spin Resonance. Based on XRD pattern, only single phase of anatase were appeared because the almost similar ionic radius of Ni2+ to that of Ti4+ which was found to replace some portion of Ti4+ ions in TiO2 lattice. The crystallite size decreases with increasing Ni content.

This phenomena probably arisen from introducing of Ni2+ ions which decrease crystalline growth. The UV-VIS diffuse reflectance spectra showed that the UV absorption moved to a longer wavelength (red shift) and the band gap energy was decreased. It caused the doped Ni atoms formed a localized energy states below conduction band of TiO2 lattice. ESR studies of Ni doped TiO2 nanoparticles revealed the presence of Ni+, Ti3+, and oxygen defects in all samples."

"Aluminium merupakan salah satu logam yang memiliki sifat mekanik yang baik. Aplikasi aluminium pada piston dalam mesin menyebabkan aluminium mengalami gesekan sehingga dapat terjadinya keausan sebelum waktunya karena karakteristik tribologi aluminium yang kurang baik. Aluminium dapat dipadukan dan dilapisi salah satunya menggunakan kobalt yang memiliki ketahanan korosi dan ketahanan aus untuk memperbaiki kekurangan dari aluminium. Pelapisan dilakukan dengan menggunakan metode elektrodeposisi karena mudah dan hemat biaya. Penambahan medan magnet selama elektrodeposisi dapat menjadi parameter yang dapat diamati pengaruhnya. Medan magnet yang diberikan secara tegak lurus terhadap katoda dapat menyebabkan adanya aliran magnetohydrodynamic yang didasarkan pada gaya Lorentz sehingga menyebabkan adanya peningkatan pada proses elektrodeposisi. Lapisan hasil elektrodeposisi dengan pengaruh medan magnet diamati menggunakan XRD didapatkan pengaruh medan magnet pada ukuran kristal yang terbentuk. Mikrostruktur lapisan yang terbentuk diamati menggunakan mikroskop optik dengan pengaruh medan magnet menyebabkan adanya perubahan pada lapisan yang terbentuk dan pengujian sifat korosi menggunakan metode linear sweep voltammetry didapatkan hasil laju korosi yang paling efektif terdapat pada sampel yang diberikan pengaruh medan magnet.

---

Aluminum is a metal that has good mechanical properties. The application of aluminum to the piston in the engine causes the aluminum to experience friction so that it can prematurely wear because of the unfavorable tribological characteristics of aluminum. Aluminum can be combined and coated, one of which uses cobalt which has corrosion resistance and wear resistance to increase aluminium properties. Coating is carried out using the electrodeposition method because it is easy and cost-effective. The addition of a magnetic field during electrodeposition can be a parameter where the effect can be observed. The magnetic field applied perpendicular to the cathode can cause a magnetohydrodynamic flow based on the Lorentz force, causing an increase in the electrodeposition process. The electrodeposition result layer with the influence of a magnetic field was observed using XRD. It was obtained the effect of the magnetic field on the size of the crystals formed. The microstructure of the layer formed was observed using an optical microscope with the influence of a magnetic field causing changes in the formed layer and testing the corrosion properties using the linear sweep voltammetry method, the most effective corrosion rate results were found in samples subjected to magnetic fields."

"Pada penelitian ini dibuat lapisan tipis LaMnO3 menggunakan metode deposisi elektroforesis pada susbtrat stainless steel SS-316 ukuran 1 x 10 x 30 mm. Serbuk LaMnO3 disintesis memakai metode sol-gel dengan campuran stokiometri antara La(NO3)3.6H2O dan Mn(NO3)2.4H2O. Sebagai larutan suspensi dipakai campuran ethanol dan deionized water dengan komposisi 90 : 10 serta serbuk LaMnO3 sebesar 30 mg dalam 50 ml larutan. Dengan memberikan tegangan DC (direct current) sebesar 60 V dan waktu deposisi 15 menit, dapat menghasilkan lapisan tipis dengan permukaan yang homogen yang ditunjukkan dengan nilai root mean square (RMS) roughness sebesar 30,96 nm. Karakterisasi menggunakan X-ray diffractometer (XRD) menunjukkan bahwa sampel lapisan tipis menghasilkan fasa senyawa substrat dan LaMnO3 dengan volume sel dan ukuran kristal meningkat dengan meningkatnya temperatur anil. Hasil scanning electron microscope (SEM) memperlihatkan bahwa morfologi sampel lapisan tipis memperlihatkan ukuran grain berkisar antara 200-400 nm. Karakterisasi dengan fourier transform infra red (FTIR) memperlihatkan bahwa material memiliki pita serapan pada 580 cm-1, merupakan karakteristik absorbsi ikatan Mn-O (streaching Mn-O-Mn pada oktahedral MnO6) yang berhubungan dengan gerakan internal perubahan panjang dari batas Mn-O-Mn. Hasil karakterisasi dengan vibration sample magnetometer (VSM) menunjukkan bahwa lapisan tipis LaMnO3 memiliki sifat feromagnetik. Kurva histerisis yang dihasilkan menunjukkan bahwa kenaikan temperatur anil menyebabkan meningkatnya sifat kemagnetan bahan. Nilai magnetisasi saturasi Ms sebesar 2,377 emu/g dan koersivitas Hc sebesar 212,03 Oe dicapai ketika temperatur anil 950°C. Hasil proses deposisi selama 15, 25 dan 35 menit, didapatkan hasil bahwa lapisan tipis LaMnO3 dapat digunakan sebagai bahan penyerap gelombang mikro. Bahan ini memiliki nilai permitivitas dan permeabilitas yang relatif tinggi dengan empat puncak serapan pada range frekuensi 8 – 12 GHz. Nilai reflection loss paling besar dalam tanda negatif dicapai oleh sampel dengan waktu deposisi 15 menit serta suhu anil 900°C sebesar - 49,25 dB pada frekuensi 8,59 GHz dan bandwidth sebesar 0,86 GHz. Sampel ini memiliki impedansi (Zin=33,3-j37,3 Ω) mendekati nilai impedansi line transmisition Zo (50 Ω)

---

In this study, a thin layer of LaMnO3 was prepared using the electrophoretic deposition method on a 1 x 10 x 30 mm stainless steel SS-316 substrate. LaMnO3 powder was synthesized using the sol-gel method with a stoichiometric mixture of La(NO3)3.6H2O and Mn(NO3)2.4H2O. As a suspension solution used a mixture of ethanol and deionized water with a composition of 90 : 10 and LaMnO3 powder of 30 mg in 50 ml of solution. By providing a DC (direct current) voltage of 60 V and a deposition time of 15 minutes, it can produce a thin layer with a homogeneous surface as indicated by the root mean square (RMS) roughness value of 30.96 nm. Characterization using an X-ray diffractometer (XRD) showed that the thin layer samples produced a substrate and LaMnO3 compound phase with cell volume and crystalline size increasing with increasing annealing temperature. Scanning electron microscope (SEM) results show that the morphology of the thin layer samples shows grain sizes ranging from 200-400 nm. Characterization with Fourier transform infrared (FTIR) produces an absorption band of about 580 cm-1, which is a characteristic of Mn-O bond absorption (Streaching Mn-O-Mn on the MnO6 octahedron) which is related to the internal movement of changes in length from the Mn-O Mn boundary. The results of characterization with a vibration sample magnetometer (VSM) showed that the LaMnO3 thin layer has ferromagnetic properties. From the resulting hysteresis curve, the increase in sintering temperature increases the magnetic properties of the material. The saturation magnetization value of Ms reached 2.377 emu/g and the Hc coercivity of 212.03 Oe was achieved when the annealing temperature was 950°C. The results of the deposition process for 15, 25 and 35 minutes showed that the LaMnO3 thin layer could be used as a microwave absorbent material. This material has relatively high permittivity and permeability values ​​with four absorption peaks in the frequency range of 8 – 12 GHz. The larger the negative value of reflection loss was achieved by samples with a deposition time of 15 minutes and annealing time of 900°C of -49.25 dB at a frequency of 8.59 GHz and a bandwidth of 0.86 GHz. This sample has an impedance (Zin=33.3-j37.3Ω) close to the line transmission impedance value Zo (50Ω)."

"Nanopartikel Ni doped ZnO dengan empat variasi konsentrasi ( 3, 6, 10, dan 20 %) telah berhasil disintesa menggunakan metode kopresipitasi menggunakan reagen zinc sulfate heptahydrate (ZnSO4.7H2O) dan nickel (II) nitrate hexahydrate (N2NiO6.6H2O). Semua sampel dikarakterisasi dengan menggunakan spektroskopi EDX (Energy Dispersive X-ray spectroscopy), XRD (X-ray Diffraction), dan spektroskopi UV-Vis. Pengukuran nilai crystallite size telah dilakukan menggunakan metode Scherrer dan Williamson-Hall. Nilai crystallite size mengalami penurunan seiring dengan bertambahnya konsentrasi atom Ni pada nanopartikel ZnO. Tiga metode Williamson-Hall juga digunakan untuk menghitung nilai strain, stress, dan energy density. Nilai celah pita energi nanopartikel Ni doped ZnO cenderung berkurang dengan peningkatan persen atom Ni.

---

A series of Ni doped ZnO nanoparticles ( 3, 6, 10, and 20 %) are successfully synthesized by coprecipitation technique with zinc sulfate heptahydrate (ZnSO4.7H2O) and nickel (II) nitrate hexahydrate (N2NiO6.6H2O). The composition, structural and optical characterizations were performed by EDX (Energy Dispersive X-ray spectroscopy), XRD (X-ray Diffraction), and UV-Visible. Crystallite size were determined from X-ray peak broadening using Scherrer and Williamson-Hall. The presence of Ni tends to reduce crystallite size. A modified W-H plot has been worked out and accepted as determining not only the crystallite size but also strain, stress, and energy density. The presence of Ni tends to reduce the width of the optical gap associated with increasing of Ni dopants."