"Pada penelitian ini dikembangkan material unggul berupa hidrogel mikrosfer komposit γ-PGA/Alg/AgNP yang diaplikasikan sebagai pembalut luka sehingga dapat menyeimbangkan kelembaban jaringan luka dan membantu dalam proses hemostasis tubuh karena sifatnya yang hidrofilik dan memiliki struktur berupa jejaring tiga dimensi. Dilakukan pengujian waktu pembekuan darah untuk mengetahui kemampuan hidrogel dalam membantu proses hemostasis tubuh. Dilakukan pengujian aktivitas antibakteri terhadap bakteri gram positif (Staphylococcus aureus) dan gram negatif (Escherichia coli). Karakterisasi diamati dengan menggunakan instrumentasi spektrofotometer UV-Vis, FT-IR, XRD, SEM-EDS dan TEM. Pengujian kapasitas swelling maksimum untuk hidrogel mikrosfer komposit γ-PGA/Alg terbaik dengan rasio massa (2:8) didapatkan hasil sebesar 261,6 (g/g) dan hidrogel γ-PGA/Alg/AgNP dengan rasio massa (1:4) didapatkan sebesar 80,8 (g/g). Hidrogel γ-PGA/Alg memiliki nilai kapasitas swelling maksimum lebih tinggi dibandingkan dengan hidrogel γ-PGA/Alg/AgNP. Selanjutnya dilakukan variasi medium perendaman, hidrogel γ-PGA/Alg/AgNP dalam media perendaman larutan asam (HCl) memiliki kapasitas swelling maksimum lebih tinggi dibandingkan dalam aquades dan larutan basa (NaOH). Pengujian release ion Ag+ pada hidrogel γ-PGA/Alg/AgNP rasio massa (1:4) menunjukkan kesesuiaian nilai maksimum tertinggi dengan pengujian kapasitas swelling-nya yakni sebesar 5,46 %. dan untuk kapasitas loading sebesar 80,15 (ppm/gr). Kinetika swelling γ-PGA/Alg dan γ-PGA/Alg/AgNP mengikuti orde pseudo pertama dengan parameter lajunya masing-masing sebesar 6,06 menit dan 44,64 menit. Pengujian waktu pembekuan darah atau CBT (clotting blood time) menunjukkan bahwa hidrogel γ-PGA/Alg/AgNP memiliki kemampuan hemostasis atau penggumpalan darah tercepat yakni selama 98,7 sekon. Hasil pengujian aktivitas antibakteri, berdasarkan literatut jurnal diketahui bahwa S.aureus lebih resisten dibandingkan E.coli.

---

In this research developed material in the form of γ-PGA/Alg/AgNP composite microsphere hydrogel which was applied as a wound dressing so that it can balance the wound tissue moisture because it is hydrophilic and has a three dimensional network structure. Clotting blood time was tasted to determine the ability of hydrogel to assist the body's hemostasis. Antibacterial activity test was done to against gram positive bacteria (Staphylococcus aureus) and gram negative (Escherichia coli). Hydrogel was characterized by spectrophotometer UV-Vis, FT-IR, XRD, SEM-EDS and TEM. Testing the maximum swelling capacity for the γ-PGA/Alg composite microscope hydrogel with the best mass ratio (2:8) results of 261.6 (g/g) and γ-PGA/Alg/AgNP hydrogel with mass ratio (1:4) obtained at 80.8 (g/g). γ-PGA/Alg hydrogels have a higher maximum swelling capacity than dibandingkan γ-PGA/Alg/AgNP hydrogels. Furthermore, the variation of immersion medium, γ-PGA/Alg/AgNP hydrogel in acid solution (HCl) immersion media has a maximum swelling capacity higher than in aquades and base solutions (NaOH). The release of Ag+ ions on the γ-PGA/Alg/AgNP hydrogel mass ratio (1:4) showed the highest maximum value of conformity with the swelling capacity test which was 5.46%. and for loading capacity of 80.15 (ppm/gr). Swelling kinetics of γ-PGA/Alg and γ-PGA/Alg/AgNP follow the first pseudo order with the speed parameters of 6.06 minutes and 44.64 minutes, respectively. Tests of blood clotting time or CBT (clotting blood time) showed that the γ-PGA/Alg/AgNP hydrogel has the ability to hemostasis or the fastest blood clotting during 98.7 seconds. The results of antibacterial activity testing, based on the journal literatut, it is known that S. aureus is more resistant than E.coli."

"Luka merupakan suatu kerusakan integritas kulit yang dapat terjadi ketika kulit terpapar suhu atau pH tertentu, zat kimia, ataupun gesekan. Setiap luka tentunya dapat beresiko infeksi atau peradangan apabila tidak diberi perawatan dengan baik dan benar, terlebih jika pemilihan material pembalut luka yang digunakan tidak sesuai dengan karakteristik luka. Pada penelitian ini dikembangkan material unggul berupa hidrogel nanokomposit yang diharapkan dapat diaplikasikan sebagai pembalut luka yang dapat menyeimbangkan kelembaban jaringan luka karena sifatnya yang hidrofilik dan memiliki struktur berupa jejaring tiga dimensi. Hidrogel nanokomposit disintesis dari biopolimer natrium alginat NaAlg dan polivinilalkohol PVA dengan metode pencangkokan grafting menggunakan akrilamida AAm dan N,N rsquo;-metilen-bis-akrilamida MBA sebagai agen pengikat silangnya cross-linker . Matriks jejaring dalam hidrogel nanokomposit NaAlg-PVA-g-AAm dimanfaatkan sebagai nanoreaktor untuk pembentukan nanopartikel perak AgNP menggunakan metode post-loading sehingga akan didapatkan material pembalut luka yang juga memiliki aktivitas antibakteri disamping dapat menjaga keseimbangan kelembaban luka. Karakterisasi hasil sintesis dilakukan dengan menggunakan instrumentasi FTIR, SEM, TEM, XRD dan AAS. Dilakukan variasi ukuran natrium alginat dan rasio Alg/PVA dalam proses polimerisasi dan didapatkan hasil terbaik yaitu hidrogel dengan ukuran alginat nano dan rasio Alg/PVA 3:1 kode. Hn 3 . Material hidrogel tanpa modifikasi Hn 3 memiliki kapasitas swelling maksimum sebesar 45,7260 g/g dan loading ion Ag 153,67 ppm/g. Kemudian dilakukan variasi konsentrasi prekursor AgNO3 pada material hidrogel Hn 3 dan diketahui bahwa Hn 3 dengan konsentrasi AgNO3 62,5 ppm kode. HNKn 3/62,5 memiliki hasil terbaik yang cukup untuk menghambat aktivitas antibakteri. Uji aktivitas antibakteri dilakukan secara in-vitro terhadap bakteri uji Staphylococcus aureus dan Escherichia coli. Diketahui bahwa S. aureus lebih resisten dibandingkan E. coli dengan nilai konsentrasi hambat minimum masing-masing secara berturut-turut sebesar 62,5 ppm dan 31,25 ppm. Didapatkan hasil untuk HNKn 3/62,5 yaitu kapasitas swelling maksimumnya 56,9407 g/g, loading ion Ag sebesar 54,2509 ppm/g dan kapasitas release maksimumnya sebesar 1,485 ppm/g. Studi kinetika swelling dilakukan terhadap material Hn 3 dan HNKn 3/62,5 menggunakan metode diferensial. Kinetika Hn 3 mengikuti orde pseudo dua dengan parameter laju swelling sebesar 80 menit. Sedangkan HNKn 3/62,5 mengikuti orde pseudo satu dengan parameter laju swelling 151,52 menit.

---

Wounds is a skin damage that occur when the skin is exposed to temperature, pH, chemicals, or friction. Wounds can be risk of infection or inflammation if wound dressing selection that used does not match with wound characteristics. This research will developed a hydrogel nanocomposite material which is expected to be applied as a wound dressing that can balancing moisture on wound tissue because it has hydrophilic properties and three dimensional network pores. Hydrogel nanocomposite will be synthesized from sodium alginate and polyvinylalcohol with grafting method used acrylamide as a monomer and N,N rsquo methylenbisacrylamide as a crosslinker. Hydrogel matrix will be used as nanoreactor to forming silver nanoparticles AgNP rsquo s with post loaded method. So, we can get a wound dressing material with antibacterial activities beside it can balancing moisture on wound tissue. Hydrogel nanocomposite was characterized by FTIR, SEM, TEM, XRD and AAS. Sodium alginate size and Alg PVA ratio in polymerization process were variated and the best material is hydrogel with nano sodium alginate and Alg PVA 3 1 ratio Code. Hn 3 . Hydrogel without modification Hn 3 has maximum swelling capacity 45,7260 g g and Ag ion loading 153,67 ppm g. Precursors AgNO3 concentration were variated on Hn 3 and it is known that 62,5 ppm Code. HNKn 3 62,5 has a best result with maximum swelling capacity 56,9407 g g Ag ion loading 54,2509 ppm g maximum release capacity 1,485 ppm g and it has antibacterial activities. Antibacterial activities test was done to against Staphylococcus aureus and Escherichia coli with minimum inhibitory concentration is 62,5 ppm and 31,25 ppm. Swelling kinetic studies for Hn 3 and HNKn 3 62,5 was done by diferential method. Hn 3 follows pseudo second order rate law with swelling rate parameter 80 minutes. HNKn 3 62,5 follows pseudo first order rate law with swelling rate parameter 151,52 minutes."

"Pada penelitian ini, telah berhasil dilakukan sintesis hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO dengan pembentukan ZnO secara in situ di dalam matriks hidrogel dengan metode hidrotermal. Karakteristik hidrogel diamati dengan FTIR, SEM, TEM, EDX, XRD, AAS serta kapasitas swelling-nya. Hidrogel NaAlg-PVA-g-AAm dengan kapasitas swelling terbaik disintesis didapatkan dengan menambahkan PVA dan alginat dengan perbandingan massa sebesar 0,6:3. Hidrogel nanokomposit setelah dimodifikasi dengan ZnO memiliki kapasitas swelling yang lebih tinggi dibandingkan hidrogel yang belum dimodifikasi. Didapatkan hasil untuk hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO yaitu kapasitas swelling maksimumnya 215,5278 g/g, loading ion Zn2 sebesar 285,82 ppm dan kapasitas release 3maksimumnya sebesar 0,9832 ppm. Kinetika swelling hidrogel NaAlg-PVA-g-AAm mengikuti orde pseudo-pertama dengan parameter laju swelling sebesar 350 menit. Sedangkan kinetika swelling hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO mengikuti orde pseudo-kedua dengan parameter laju swelling sebesar 487,5 menit. Dari hasil uji aktivitas antibakteri yang dilakukan secara in-vitro, diketahui S.aureus lebih resisten dibandingakan P. aeruginosa dengan persen inhibisi S. aureus yang lebih besar pada konsentrasi hambat minimum yang sama yaitu 31,25 ppm.

---

In this research, NaAlg PVA g AAm nanocomposite hydrogel had been successfully modified by ZnO nanoparticles in the hydrogel matrix by hydrothermal method. Characteristics of hydrogels were observed with FTIR, SEM, TEM, EDX, XRD, AAS and through their swelling capacities. The NaAlg PVA g AAm hydrogel with the best swelling capacity was synthesized by adding PVA and alginate with a mass ratio of 0.6 3. Obtained results for NaAlg PVA g AAm nanocomposite hydrogel modified ZnO nanoparticles had the maximum swelling capacity of 215.52 g g, Zn2 ion loading of 285.82 ppm and its maximum release capacity of 0.98 ppm, while the maximum swelling capacity for a NaAlg PVA g AAm nanocomposite hydrogel was 73.26 g g. Kinetics swelling of NaAlg PVA g AAm hydrogel followed the first pseudo order with a swelling rate parameter of 350 minutes, whereas kinetics swelling of NaAlg PVA g AAm nanocomposite hydrogel modified ZnO nanoparticles followed the second pseudo order with swelling rate parameter of 487.5 minutes. From in vitro antibacterial activity test, S.aureus was known to be more resistant than P. aeruginosa with a greater inhibition percentage of S. aureus at the same minimum inhibitory concentration of 31.25 ppm."

"Hidrogel adalah pembalut luka modern yang dapat menangani eksudat luka sekaligus mempertahankan kelembaban yang optimal. Hidrogel yang hanya mengandung satu polimer memiliki kekuatan mekanik, elastisitas, dan stabilitas yang rendah. Oleh sebab itu, penggabungan dua jenis polimer dalam pembuatan hidrogel banyak diterapkan dalam aplikasi biomedik saat ini. Penelitian ini bertujuan untuk mengarakterisasi dan membandingkan hidrogel yang dibentuk dari polimer kitosan dan gelatin yang ditaut silang menggunakan glutaraldehid dan genipin untuk pembalut luka. Kedua hidrogel dibuat menggunakan metode yang sama yaitu menggunakan agen penaut silang kimia. Morfologi, identifikasi gugus fungsi, pola difraksi sinar-X, stabilitas termal, sifat mekanik, kemampuan mengembang, dan evaporasi air dari hidrogel diuji. Hasil karakterisasi dari kedua hidrogel serupa karena glutaraldehid dan genipin memiliki mekanisme taut silang yang serupa terhadap polimer kitosan dan gelatin. Kemampuan mengembang metode taut silang glutaraldehid (63,07%) lebih tinggi daripada genipin (58,25%). Hasil uji sifat mekanik metode taut silang glutaraldehid lebih rendah yaitu 0,0061 MPa (mengembang) dan 0,0517 MPa (kering) dibandingkan genipin yaitu 0,0087 MPa (mengembang) dan 0,1187 MPa (kering). Laju evaporasi air metode taut silang glutaraldehid lebih tinggi (27,21%) daripada genipin (24,85%). Berdasarkan hasil karakterisasi dan evaluasi, hidrogel yang ditaut silang dengan genipin dapat menggantikan hidrogel ditaut silang glutaraldehid sebagai pembalut luka.

---

Hydrogels are modern wound dressings which have the ability to absorb wound exudates while providing an optimum moist environment for the wound. Hydrogels made up of just one polymer have poor mechanical properties, low elasticity, and thermal instability. Therefore, two or more different types of polymers were usually used in the fabrication of hydrogels for applications in biomedical areas. The purpose of this study is to prepare chitosan/gelatin hydrogels crosslinked with glutaraldehyde and genipin as well as to characterize and study their properties as a wound dressing. Both hydrogels were fabricated by chemical crosslinking using a crosslinker. Morphology, FT-IR analysis, X-ray diffraction, thermal stability, mechanical properties, swelling capability, and water evaporation were tested. Characterization of both hydrogels showed similar results because they have similar crosslinking mechanisms when added to chitosan and gelatin. Glutaraldehyde-crosslinked hydrogel has higher swelling capability (63.07%) than genipin (58.25%). Glutaraldehyde-crosslinked hydrogel has lower tensile strength which are 0.0061 MPa (swelling) and 0.0517 MPa (dried) than genipin which are 0.0087 MPa (swelling) and 0.1187 MPa (dried). Glutaraldehyde- crosslinked hydrogel has higher water evaporation rate (27.21%) than genipin (24.85%). Based on overall characteristics and evaluation, genipin-crosslinked hydrogel can be used to replace glutaraldehyde-crosslinked hydrogel as a wound dressing."

"Pembalut luka yang ideal tidak hanya menutupi dan melindungi area yang terdampak, tetapi juga dapat menciptakan lingkungan yang optimal di lokasi luka untuk memfasilitasi penyembuhan. Hidrogel merupakan kandidat pembalut luka yang ideal karena kemampuannya untuk menyerap air sehingga mampu menjaga lingkungan lembap di sekitar luka dan membantu menyerap eksudat dari permukaan luka. Pada penelitian ini, dibuat hidrogel menggunakan dua polimer alami, yaitu kitosan dan natrium alginat yang diketahui memiliki biokompatibilitas yang baik dan biodegradabilitas yang tinggi. Hidrogel kitosan/alginat dibuat menggunakan dua cara berbeda, yaitu dengan taut silang fisik menggunakan CaCl2 dan taut silang kimia menggunakan genipin. Untuk melihat perbedaan antara kedua hidrogel yang dibuat, dilakukan karakterisasi morfologi, struktural, pola difraksi sinar-X, dan stabilitas termal masing-masing menggunakan SEM, FTIR, XRD, dan DSC. Selain itu, juga dilakukan uji kemampuan mengembang, kecepatan evaporasi air, dan evaluasi sifat mekanis dari hidrogel. Hasil karakterisasi menunjukkan bahwa hidrogel kitosan/alginat berhasil ditaut silang dengan dua cara berbeda, serta menunjukkan kompatibilitas yang baik. Hasil evaluasi sifat mekanis menunjukkan kekuatan peregangan yang lebih rendah untuk hidrogel dengan taut silang fisik dibandingkan hidrogel dengan taut silang kimia. Nilai evaporasi air setelah 24 jam yaitu 12,12 ± 0,46% untuk hidrogel dengan taut silang fisik, dan 11,78 ± 1,33% untuk hidrogel dengan taut silang kimia. Sedangkan indeks mengembang maksimum berada pada nilai 105,71 ± 8,78% untuk hidrogel dengan taut silang fisik, dan 46,91 ± 8,49% untuk hidrogel dengan taut silang kimia. Meskipun terdapat perbedaan pada hasil karakterisasi dan evaluasi, baik hidrogel kitosan/alginat dengan taut silang fisik maupun kimia memiliki potensi sebagai pembalut luka yang baik.

---

An ideal wound dressing covers and protects the affected area and creates an optimal environment at the wound site to facilitate wound healing. Hydrogel is an ideal wound dressing candidate because of its ability to absorb water which can help maintain a moist environment around the wound and absorb exudate from the wound surface. In this study, hydrogels were made using two natural polymers, chitosan, and sodium alginate, which are known to have good biocompatibility and high biodegradability. Chitosan/alginate hydrogels were made using two different methods: physical crosslinking using CaCl2 and chemical crosslinking using genipin. To observe the differences between the two hydrogels, morphological, structural, X-ray diffraction patterns, and thermal stability characterization was conducted using SEM, FTIR, XRD, and DSC, respectively. In addition, the swelling ability test, water evaporation rate, and the evaluation of the mechanical properties of the hydrogel were also carried out. The characterization results showed that the chitosan/alginate hydrogel was crosslinked in two different ways and showed good compatibility. The evaluation of the mechanical properties showed that the tensile strength was lower for hydrogels with physical crosslinks compared to hydrogels with chemical crosslinks. The value of water evaporation after 24 hours was 12.12 ± 0.46% for hydrogels with physical crosslinks and 11.78 ± 1.33% for hydrogels with chemical crosslinks. Meanwhile, the maximum swelling index was 105.71 ± 8.78% for hydrogels with physical crosslinks and 46.91 ± 8.49% for chemical crosslinks. Although there are differences in the results of the characterization and evaluation that have been done, both chitosan/alginate hydrogels with physical and chemical crosslinks have potential as good wound dressings."

"Penelitian ini telah berhasil disintesis hidrogel ramah lingkungan dengan struktur jejaring tiga dimensi yang bersifat hidrofilik sehingga dapat diaplikasikan sebagai pembalut luka yang dapat menyeimbangkan kelembaban jaringan luka. Hidrogel ini disintesis dari karboksimetil selulosa (CMC) dan polivinil alkohol (PVA) dengan asam sitrat (CA) sebagai agen pengikat silang. Matriks jejaring hidrogel digunakan sebagai tempat untuk pembentukan nanopartikel tembaga (CuNPs) dengan metode ex situ dan in situ sebagai antibakteri pada pembalut luka. Karakterisasi hidrogel menggunakan analisis FTIR, SEM, TEM, XRD dan AAS. Hidrogel terbaik diperoleh dari 3 gram CMC, 1 gram PVA, asam sitrat 10% dan dimodifikasi oleh CuNPs dengan metode in situ. Kapasitas swelling maksimum yang diperoleh adalah 19,59 g/g dan release ion Cu2+ maksimum yang diperoleh adalah 18,70 ppm/g. Uji aktivitas antibakteri berhasil dilakukan dengan metode dilusi terhadap bakteri Staphylococcus aureus dan bakteri Escherichia coli. Uji aktivitas antibakteri dengan metode total plate count menunjukkan bahwa Staphylacoccus aureus lebih resisten dari pada Escherichia coli yaitu 12,4 juta dan 4,9 juta Colony for Units, masing-masing.

---

This study have successfully synthesized eco-friendly hydrogels with a three-dimensional network structure that is hydrophilic so that it can be applied as a wound dressing that can balance the moisture of wound tissue. This hydrogels were synthesized from carboxymethyl cellulose (CMC) and polyvinyl alcohol (PVA) with citric acid (CA) as cross-linking agent. The network matrix hydrogels was used as a place for the formation of copper nanoparticles (CuNPs) by ex situ and in situ methods as antibacterial in wound dressing. The characterization of hydrogels used FTIR, SEM, TEM, XRD and AAS analysis. The best hydrogel were obtained from 3 grams CMC, 1 gram PVA, 10% citric acid and modified by CuNPs with in situ method. The maximum swelling capacity obtained is 19.59 g/g and the maximum Cu2+ ions release obtained is 18.70 ppm/g. Antibacterial activity test was successfully carried out by dilution method against Staphylococcus aureus bacteria and Escherichia coli bacteria. Antibacterial activity test by total plate count method shows that Staphylacoccus aureus is more resistant than Escherichia coli of 12.4 million and 4.9 million Colony for Units respectively."

"Nanopartikel perak merupakan salah satu agen antibakteri yang baik dan memiliki insiden resistensi lebih kecil, sehingga dapat digunakan sebagai alternatif untuk pengobatan luka. Hidrogel merupakan sebuah sistem yang dapat digunakan sebagai pembawa dari nanopartikel perak karena dapat menciptakan kondisi yang mendukung pemulihan luka. Penelitian ini bertujuan untuk membuat dan mengkarakterisasi pembalut luka hidrogel mengandung nanopartikel perak-kitosan (Ch-AgNPs). Ch-AgNPs disintesis dari perak nitrat (AgNO3) secara kimia dengan kitosan sebagai pereduksi dan penstabil, sementara hidrogel dibuat melalui metode freeze-thaw dengan asam sitrat sebagai agen cross-linking tambahan. Karakterisasi dilakukan terhadap Ch-AgNPs dan hidrogel PVA-kitosan dengan memerhatikan ukuran nanopartikel dan struktur dari hidrogel. Hasil penelitian menunjukkan bahwa Ch-AgNPs yang dihasilkan memiliki ukuran 164 nm dengan bentuk piramidal, sementara hidrogel mengandung Ch-AgNPs memiliki struktur berpori dan persentase swelling index 1039,223%. Tetapi H-Ag tidak mampu membentuk zona inhibisi terhadap bakteri Escherichia coli. Dapat disimpulkan, CH-AgNPs yang disintesis memenuhi kriteria sebagai nanopartikel dan pembalut luka hidrogel mengandung Ch-AgNPs (H-Ag) 0,05 mg/mL ini memiliki struktur berpori yang rapat degan kemampuan absorpsi cairan yang baik.

---

Silver nanoparticles is a good antibacterial agent and have a lower incidence of resistance, so they can be used as an alternative for wound treatment. Hydrogel is a system that can be used as a carrier for silver nanoparticles because it can create conditions that support wound healing. This research aims to create and characterise hydrogel wound dressings containing chitosan-silver nanoparticles (Ch-AgNPs). Ch-AgNPs were synthesised from silver nitrate (AgNO3) chemically by chitosan as a reducing agent and stabiliser, while hydrogels were prepared via the freeze-thaw method with citric acid as an additional cross-linking agent. Characterisation was carried out on Ch-AgNPs and PVA-chitosan hydrogel with the focus on the size of the nanoparticles and the structure of the hydrogel. The results showed that the Ch-AgNPs had a z-average of  164 nm with a pyramidal shape, while the hydrogel containing Ch-AgNPs had a porous structure and a swelling index percentage of 1039.223%. But H-Ag is unable to form an inhibition zone against Escherichia coli bacteria. It can be concluded that the synthesized CH-AgNPs meet the criteria as nanoparticles and the hydrogel wound dressing containing 0,05 mg/ mL Ch-AgNPs (H-Ag) has a tight porous structure with good absorption capabilities."

"

Madu dan propolis merupakan produk dari lebah yang memiliki banyak manfaat. Banyak penelitian telah membuktikan kedua produk ini memiliki kandungan anti-bakteri dan anti-inflamasi sehingga memiliki potensi untuk digunakan sebagai bahan aktif dalam pembalut luka. Setiap tahunnya sekitar 180.000 orang meninggal akibat luka. Kematian akibat luka biasanya disebabkan oleh infeksi dari bakteri dan tidak mendapatkan perlakuan yang tepat sehingga infeksi menjadi parah dan mengakibatkan kegagalan sistemik lainnya. Bakteri yang paling banyak ada di luka adalah Staphylococcus aureus. Bakteri ini menginisiasi infeksi pada luka terbuka. Saat ini Polyvinyl Alcohol (PVA) banyak digunakan sebagai polimer karena sifatnya yang transparan, mudah dibentuk, bio-inert, dan biokompatibel. PVA banyak digunakan dalam bentuk hidrogel sebagai pembalut luka. Hidrogel berbasis PVA memiliki performa yang baik sebagai pembalut luka, namun tidak memiliki sifat antibakteri, sehingga banyak penelitian melakukan penggabungan antara hidrogel dengan bahan aktif seperti gentamicin dan nanopartikel Ag. Penelitian ini menggabungkan PVA hidrogel dengan propolis pada beberapa komposisi (2,5%; 3,75%; 5%, 6,25%; 7,5%). Zona inhibisi terbaik adalah pada konsentrasi tertinggi, sementara untuk hasil uji sifat fisik, nilai kekuatan lipat adalah >300 untuk seluruh sampel, uji pembengkakan ada di rentang 7-12% untuk sampel dari Belitung, dan 4-6% pada sampel dari Sulawesi yang sudah memenuhi standar. Uji moisture content ada pada rentang 77-82%.

---

Honey and propolis are products of bees that have many benefits. Many studies have proven that these two products have anti-bacterial and anti-inflammatory properties, so they have the potential to be used as active ingredients in wound dressings. Every year about 180,000 people die from injuries. Death from wounds is usually caused by infection from bacteria and not getting proper treatment so that the infection becomes severe and results in other systemic failures. The most common bacteria in the wound is Staphylococcus aureus. These bacteria initiate infection in open wounds. Currently, Polyvinyl Alcohol (PVA) is widely used as a polymer because it is transparent, malleable, bio-inert, and biocompatible. PVA is widely used in hydrogel form as a wound dressing. PVA-based hydrogels have good performance as wound dressings, but do not have antibacterial properties, so many studies have carried out combining hydrogels with active ingredients such as gentamicin and Ag nanoparticles. This research combining PVA hydrogel with propolis in several compositions (2,5%; 3,75%; 5%; 6,25%; 7,5%). The best inhibition zone is at the highest concentration, while for the physical property test results, the folding strength value is >300 for all samples, the swelling test is in the range of 7-12% for samples from Belitung, and 4-6% for samples from Sulawesi which have been meet standards. Moisture content test is in the range of 77-82%.

 

"

"ABSTRAKTelah disintesis material polimer konduktif Polianilin (PANi) dengan menggunakanmetode polimerisasi oksidatif Anilin secara kimiawi (chemical) kemudian dilakukanpemberian doping asam protonik yang bervariasi berupa asam kuat HCl, HClO4, danH2SO4. Sampel-sampel ini kemudian dikarakterisasi dengan menggunakanspektrofotometer FTIR, Conductivity Meter, PSA (Particle Size Analyzer), dan VNA(Vector Network Analyzer) untuk mengetahui gugus fungsi, nilai konduktivitas listrik,ukuran partikel, dan daya serap gelombang mikro dengan rentang frekuensi tertentu(rentang 8-12 GHz) yang terdapat pada material tersebut. Hasil karakterisasiberdasarkan penelitian menunjukkan bahwa Polianilin (PANi) yang telah terdopingasam protonik (terprotonasi) atau telah menjadi polimer konduktif memilikikarakteristik puncak pita serapan IR pada bilangan gelombang antara 1141 cm-1 ?1177 cm-1. Ukuran partikel masing-masing bentuk Polianilin hasil penelitian telahmenjadi nanopartikel dengan rentang ukuran partikel masing-masing bentuk materialini mulai dari 4-9 nm. Polianilin yang memiliki konduktivitas listrik tertinggi yaituPolianilin dengan doping asam protonik HClO4 (PANi(HClO4)) sebesar 3,6 mS/cmdan memiliki serapan gelombang mikro terendah yaitu -6,98 dB pada frekuensi 11,34GHz. Nilai permitivitas terendah dimiliki oleh PANi(HClO4) akan tetapi dengan nilaipermitivitas yang rendah (dielectric constant negatif dan dielectric loss minimum)dan konduktivitas listrik yang tinggi, membuat serapan gelombang mikro kompositdengan PANi tersebut sebagai matriks akan meningkatkan jumlah serapan gelombangmikro dan meminimalisir gelombang mikro yang ditransmisikan. Serapan gelombangmikro material komposit tertinggi dimiliki oleh komposit dengan campuran PANirekayasa (PANi-ES) sebagai matriks dan Barrium Hexaferrite (BHF) yang telahdisonikasi selama 5 jam sebagai filler dengan perbandingan komposisi % berat PANirekayasa dan BHF 30 : 70. Material komposit tersebut adalah PANi(HClO4)/5BHFyang memiliki serapan gelombang mikro tertinggi yaitu -38,3 dB pada frekuensi12,28 GHz.

---

ABSTRACTPolyaniline (PANi) conducting polymers have been synthesized using chemicaloxidative polymerization method on Aniline then carried granting varying protonicacid doping form strong acid HCl, HClO4, and H2SO4. These samples were thencharacterized using FTIR spectrophotometer, Conductivity Meter, PSA (Particle SizeAnalyzer), and VNA (Vector Network Analyzer) to determine the functional groups,the value of the electrical conductivity, particle size, and the absorption ofmicrowaves by a certain frequency range (range 8-12 GHz) contained in thesematerials. The results of the study showed that the characterization based onPolyaniline (PANi) which has been doped protonic acid (protonated) or has becomeconducting polymers have peaks characteristic IR absorption band at wave number of1141 cm-1-1177 cm-1. The particle size of each form of Polyaniline research hasbecome nanoparticles with a particle size range of each form of this material rangingfrom 4-9 nm. Polyaniline which has the highest electrical conductivity by dopingPolyaniline protonic acid HClO4 (PANi (HClO4)) of 3,6 mS / cm and has a lowabsorption of microwaves is -6,98 dB at a frequency of 11,34 GHz. Low permittivityvalue owned by PANi (HClO4) but with a lower value of permittivity (negativedielectric constant and minimum dielectric loss) and high electrical conductivity,making the absorption of microwaves by PANi composites such as matrix willincrease the amount of microwave absorption and minimize microwave transmitted.The highest microwave absorption of composite materials owned by the compositewith a mixture of modified PANi (PANi-ES) as a matrix and Barrium Hexaferrite(BHF) which had been sonicated for 5 hours as a filler with a composition ratio wt%modified PANi and BHF 30 : 70. The composite material is PANi(HClO4) / 5BHFwhich has the highest absorption of microwaves -38,3 dB at a frequency of 12,28GHz."

"Dalam penelitian ini dilakukan pembuatan komposit semikonduktor dengan menggunakan matriks akrilik yang ditambahkan dengan dua jenis filler yakni ZnO dan serat nata de coco. Tujuan dari penelitian ini adalah untuk mendapatkan material komposit semikonduktor yang memiliki kekuatan mekanik, serta ketahanan termal yang baik. Metode yang digunakan adalah polimerisasi in situ dimana filler dan monomer matriks yang berupa resin dicampurkan kemudian ditambahkan katalis sebanyak 1% berat resin untuk mempercepat polimerisasi sehingga didapat komposit dengan filler yang terdistribusi di dalam polimer akrilik setelah didiamkan selama 12 jam. Komposit ini kemudian diukur modulus elastisitas, suhu transisi gelas, serta konduktivitas listriknya. Penambahan filler nata de coco mampu meningkatkan modulus elastisitas dan suhu transisi gelas dari akrilik. Modulus elastisitas serta suhu transisi gelas tertinggi dicapai oleh komposit akrilik/nata de coco dengan persen volume sebesar 30% yakni 2,68 GPa dan 199,47oC. Secara umum penambahan filler ZnO dan nata de coco meningkatkan konduktivitas dari komposit. Komposit yang dihasilkan dapat dinyatakan sebagai material semikonduktor karena berada pada rentang konduktivitas 10-8-103 S/cm. Komposit dengan sifat semikonduktor yang paling baik adalah komposit akrilik/ZnO dengan persen volume ZnO sebesar 30% dengan konduktivitas sebesar 2,7 x 10-7 S/cm. Komposit dengan kombinasi filler ZnO sebesar 20% dan nata de coco 10% volume memberikan modulus elastisitas serta suhu transisi gelas yang lebih tinggi dari komposit akrilik/ZnO yakni mencapai 1,79 GPa dan 175,73oC. Sementara konduktivitas dari komposit tersebut lebih tinggi dari konduktivitas akrilik/nata de coco yakni mencapai 1,9 x 10-7 S/cm.

---

Synthesis of semiconductor composite using acrylic matrix filled with ZnO and nata de coco fiber has been conducted in this research. The purpose of this research is to obtain semiconductor composite material that have a good mechanical strength and thermal resistance. In situ polymerization method is used in this research where fillers and matrix monomer are mixed and then 1%wt of catalyst is added into the mixture to make it polymerizes faster. After 12 hours, the composite with acrylic matrix and filler is ready to be characterized. Three parameters are characterized in this research such as elastic modulus, glass transition temperature, and electric conductivity of the composite. The addition of nata de coco filler can increase the elastic modulus and glass transition temperature of the acrylic. The highest elastic modulus and glass transition temperature is obtained from acrylic/nata de coco composite with 30% filler volume percentage that reach 2,68 GPa and 199,47oC.

In general the addition of ZnO and nata de coco filler can increase the conductivity of the composite. The composites that has been made in this research can be classified as semiconductor material because the conductivity is in the range of 10-8-103 S/cm. Composite that has a high semiconductor characteristic is obtained from acrylic/ZnO composite with 30% filler volume percentage that reach 2,7 x 10-7 S/cm. The composite with 20% volume of ZnO filler and 10% volume of nata de coco gives a higher elastic modulus and glass transition temperature than those in acrylic/ZnO composite that reach 1,79 GPa and 175,73oC. In addition, the conductivity of this composite is 1,9 x 10-7 S/cm which is higher than the conductivity of acrylic/nata de coco composite.;"