"Perovskite tipe oksida jenis lanthanum orthoferrite (LaFeO3) telah menjadi salah satu kandidat jenis terbaru untuk material elektroda dikarenakan memiliki good activation property dan high electrochemical capacity. Beberapa penelitian sistematis tentang modifikasi LaFeO3 dengan melakukan substitusi menggunakan kation valensi yang lebih rendah seperti Zn2+ dan Ca2+ telah dilaporkan dan menunjukkan dampak yang baik pada physicochemical properties yang potensial untuk dapat diaplikasikan di bidang fotokatalitik. Pada penelitian ini, material perovskite LaFe1-xMgxO3 dengan x = 0.0, 0.1, 0.2 dan 0.3 telah berhasil disintesis menggunakan metode sol-gel. Proses sintesis material menghasilkan sampel dalam bentuk powder (bubuk) dan bulk (pellet). Uji karakterisasi yang telah dilakukan adalah XRD, XRF, FTIR, Raman, UV-VIS, SEM-EDX, BET, PSA, dan RLC Meter. Hasil uji karakterisasi XRD menunjukkan sampel yang single phase, struktur Orthorhombic dan space group Pnma. Terjadi peningkatan nilai bond-length dan bond-angle sebagai akibat dari substitusi Mg di situs Fe yang dikonfirmasi juga oleh hasil uji FTIR dan pergeseran mode pada Raman shift. Hasil uji XRF menunjukkan stoikiometri pada material yang sedikit berbeda dengan perhitungan, hal ini dikarenakan karena keterbatasan XRF untuk mendeteksi light element. Namun diperoleh komposisi stoikiometri yang lebih presisi dengan menggunakan uji EDX. Hasil uji SEM menunjukkan bahwa penambahan jumlah Mg menyebabkan rata-rata ukuran grain menurun, data ini konsisten dengan hasil yang diperoleh XRD. Hasil uji PSA menunjukkan nilai particle size rata-rata yang tidak beraturan, distribusi nilai particle size merata dan terdistribusi normal, sedangkan uji BET menunjukkan keberagaman nilai surface area yang dikonfirmasi juga karena adanya perbedaan komposisi elemen pada sampel powder yang dikonfirmasi dengan hasil uji XRF. Hasil uji UV-Vis menunjukkan data nilai band gap energy yang menurun seiring dengan peningkatan doping magnesium berkorelasi dengan peningkatan nilai bond-length pada XRD. Hasil uji dengan RLC meter menunjukkan diameter semi-sirkular menurun seiring peningkatan temperatur, mengindikasikan material ini bersifat semikonduktor serta adanya peningkatan konduktivitas pada sampel dan penurunan nilai resistansi berkorespondensi dengan energy aktivasi pada grain dan grain size hasil uji SEM.

---

Perovskite type-oxide lanthanum orthoferrite (LaFeO3) has become a new type of electrode material because has good activation property and high electrochemical capacity. A few systematic works about modifying LaFeO3 by substitute with lower valent-cation such as Zn2+ and Mg2+ has been reported before and showed a great impact on the physicochemical properties which potential to be applied as photocatalytic application. In this research, LaFe1-xMgxO3 (x = 0.0, 0.1, 0.2, 0.3) material has been synthesized using sol-gel method. The synthesis process resulting in two forms of the sample; powder and bulk. The characterization tests have done with XRD, XRF, FTIR, UV-Vis, SEM-EDX, BET, PSA and RLC meter. XRD characterization test was confirmed single phase with the orthorhombic crystal structure and Pnma space group for all samples. The increament of bond-length and bond-angle as a result of Mg-substitution in Fe-site confirmed by FTIR test and shift mode in Raman. XRF characterization test was displayed the stoichiometry a little bit different from the calculation, it can be happened because of the limitation of XRF to detecting the light element. But, the precise composition was getting from EDX characterization test. SEM characterization test shows that Mg-substitution resulting in the decreament of average grain size, this data was consistent with the XRD result. PSA characterization test observed inhomogenous of average particle size value, the particle size distribution normally, the BET characterization test shows the various value of surface area which confirmed by XRF results. UV-Vis characterization test displays band gap energy decrease with the increasing number of Magnesium correlating with increasing value of bond-length confirmed by XRD. RLC meter characterization test perform the decrement of semicircle diameter with increasing of temperature which indicating this material was a semiconductor and there is an enhancement of conductivity and the decrement of resistance value corresponding with activation energy on grain and grain size SEM result tests.

"

"ABSTRAKPerovskite lanthanum bismuth orthoferrite (La_1-xBi_xFeO₃ dengan x=0.1, 0.2, 0.3, 0.4 dan 0.5) telah disintesis menggunakan metode sol-gel. Hasil pola XRD yang telah dianalisa menggunakan program Highscore Plus menunjukkan bahwa material memiliki struktur orthorhombic serta semua sampel berfase tunggal dengan Pnma space group. Nilai parameter kisi meningkat dengan meningkatnya konsentrasi doping yang sebanding dengan meningkatnya jarak ikatan dari La-O dan Fe-O. Hal tersebut dipengaruhi oleh perbedaan jari-jari atom (ionic radii) antara Bi³⁺ dan La³⁺. Hasil pengukuran XRF menunjukkan terdapat perbedaan hasil antara hasil pengukuran dan eksperimental, hal ini dapat disebabkan oleh eror pengukuran dan proses sintesis (kehilangan massa pada saat proses sintesis). Hasil pengukuran SEM menunjukkan bahwa semua sampel memiliki ukuran dan bentuk grain tidak homogen dan juga terdapat porositas pada semua sampel. Pengujian sifat listrik dilakukan dengan menggunakan metode spektroskopi impedansi dengan rentang frekuensi 1 kHz sampai 1 MHz. Temperatur yang digunakan dalam pengujian ini yaitu dari rentang 75^oC - 200^oC. Analisis impedansi menunjukkan sifat semikonduktor untuk semua sampel. Terlihat jelas adanya kontribusi grain dan grain boundary pada nyquist plot dan juga terjadi penurunan grafik semisirkular dengan menurunnya temperatur. Bode plot menunjukkan fenomenana relaksasi, waktu relaksasi bergantung pada aktivitas termal. Analisis dielektrik menunjukkan semua sampel memiliki konstanta dielektrik menurun dengan menurunnya konsentrasi doping serta nilai konstanta dielektrik memiliki orde yang besar. Sifat konduktivitas listrik memenuhi Jonshers power law. Energi bandgap menurun dengan meningkatnya konsentrasi doping.

---

ABSTRACTPerovskite lanthanum bismuth orthoferrite (La_1-xBi_xFeO₃ with x = 0.1, 0.2, 0.3, 0.4 and 0.5) has been synthesized using the sol-gel method. The results of the XRD pattern analyzed using the Highscore Plus program indicate that the material has an orthorhombic structure and all single-phase samples with the Pnma space group. The lattice parameter value increases with increasing doping concentration which is proportional to the increasing bond distance of La - O and Fe - O. It is influenced by the difference in atomic radius (ionic radii) between Bi³⁺ and La³⁺. XRF measurement results show there are differences in results between measurement and experimental results, it can be caused by measurement error and synthesis process (mass loss during the synthesis process). The results of SEM measurement indicate that all samples have a size and shape not homogeneous and also have porosity in all samples. Measurement of electrical properties is carried out using impedance spectroscopic methods with a frequency range of 1 kHz to 1 MHz. The temperature used in this test is from the range 75^oC - 200^oC. Impedance analysis shows the semiconductor properties for all samples. It is clear that there is a contribution of grain and grain boundary on nyquist plots and also a decrease in semicircular graphs with decreasing temperature value. The bode plot shows the relaxation phenomena, which is the relaxation time itself depends on thermal activity. Dielectric analysis shows that all samples have a dielectric constant decreases with decreasing doping concentration and the dielectric constant value has large order. The conductivity of electricity analyze with Jonshers power law. The band gap energy decreases with increasing doping concentration.

"

"Lanthanum Orthoferrite (LaFeO3) adalah salah satu material perovskite oxide ABO3 yang memiliki struktur ortorombik. Pada penelitian ini telah disintesis LaFeO3 yang disubstitusi dengan Zr pada situs Fe (LaFe1-xZrxO3 dengan x=0.01, 0.03 dan 0.05) yang dipreparasi menggunakan metode sol-gel. Penelitian ini bertujuan untuk mengetahui sifat struktur kristal, listrik dan optik material sebagai kandidat SOFC. Sampel yang telah dipreparasi diuji menggunakan XRD menunjukkan sampel yang single phase, struktur Orthorhombic dan space group Pbnm. Terjadi perubahan nilai bond-length dan bond-angle sebagai akibat dari substitusi Zr di situs Fe. Hal tersebut sesuai dengan hasil uji FTIR dan pergeseran mode pada Raman shift. Uji XRF menunjukkan stoichiometry pada material yang memiliki sedikit perbedaan dengan perhitungan. Selain itu, diperoleh komposisi stoikiometri yang lebih presisi dengan menggunakan uji EDX. Hasil uji SEM menunjukkan bahwa penambahan jumlah Zr menyebabkan rata-rata ukuran grain menurun yang konsisten dengan hasil dari XRD. Hasil uji UV-Vis menunjukkan data nilai band gap energy yang menurun seiring dengan peningkatan doping Zr sesuai dengan perubahan nilai bond-length pada XRD. Uji listrik pada material dilakukan dengan menggunakan metode impedance spectroscopy sebagai fungsi frekuensi (100Hz-1 MHz) dengan menggunakan RLC meter. Data IS disajikan dalam bentuk Nyquist Plot dan Bode Plot, yang digunakan untuk mengindentifikasi parameter rangkaian yang ekuivalen beserta nilainya. Hasil uji dengan RLC meter menunjukkan diameter semi-sirkular menurun seiring peningkatan temperatur, mengindikasikan material ini bersifat semikonduktor serta adanya peningkatan konduktivitas pada sampel dan penurunan nilai resistansi.

---

Lanthanum Orthoferrite (LaFeO3) is one of ABO3 perovskite oxide material which has orthorhombic structure. In this study, LaFeO3 substituted Zr at the Fe site (LaFe1-xZrxO3 with x = 0.01, 0.03 and 0.05) prepared using the sol-gel method. This study aims to determine the crystal structure, electrical properties and optical properties of materials. Sample was characterized with XRD showed single phase samples, Orthorhombic structures and Pbnm space groups. Changes in bond-length and bond-angle values occur as a result of Zr substitution at the Fe site. This is consistent with the results of FTIR and the shift mode on the Raman shift. XRF characterization shows stoichiometry on material that has a slight difference with the calculation. In addition, a more precise stoichiometric composition was obtained using EDX. SEM results show that increasing of Zr causes the average grain size decrease which is consistent with the results of XRD. UV-Vis results show that the band gap energy value decreases with the increase in Zr doping according to changes in the bond-length value in XRD. RLC meters show the semi-circular diameter decreases with increasing temperature, indicating this material is semiconductor as well as an increase in conductivity in the sample and a decrease in the resistance value corresponding to the activation energy in the grain and grain size SEM results. Electrical tests on the material are carried out using the impedance spectroscopy method as a function of frequency (100Hz-1 MHz) using the RLC meter. IS data are presented in the form of Nyquist Plots and Bode Plots, which are used to identify equivalent circuit parameters and their values."

"Substitusi atom Zinc pada site-Fe material LaFeO3 (LaFe1-xZnxO3 dengan x= 0.0, 0.03, 0.05, dan 0.07) telah dilakukan dengan metode sintesis sol-gel. Sifat struktur material perovskite LaFe1-xZnxO3 dikarakterisasi menggunakan XRD, XRF, SEM dan EDS. Hasil analisis dari XRD untuk material LaFe1-xZnxO3 menunjukkan material memiliki struktur Orthorhombic dengan space group Pbnm. Dari hasil rietveld bahwa parameter kisi, volum, densitas serta parameter geometrikal material mengalami perubahan setelah subtitusi Zinc. Hasil SEM menunjukkan bahwa ukuran grain terlihat semakin menurun dan terjadi aglomerasi. XRF dan EDS mengkonfirmasi adanya unsur La, Zn, Fe dan O pada material perovskite LaFe1-xZnxO3. Sifat optik dikarakterisasi dengan menggunakan FTIR, Raman spectroscopy dan UV-Vis. FTIR mengkonfirmasi adanya stretching vibration La-O, Fe/Zn-O dan bending vibration Fe/Zn-O-Fe/Zn sedangkan pada hasil Raman spectroscopy diperoleh pembentukan material LaFeO3 serta energi aktivasi pada material dilihat dari modes yang terbentuk. Hasil karakterisasi UV-Vis menunjukkan penurunan nilai energi band gap dengan rentang 2.14-2.05 eV. Sifat listrik material diuji menggunakan RLC-meter dengan metode Impedance Spectroscopy (IS) pada rentang temperatur 30°C-200°C, dimana, diperoleh peningkatan konduktivitas akibat terjadinya penurunan resistivitas pada sampel bulk.

---

Zinc substitution at Fe-site on LaFeO3 material (LaFe1-xZnxO3 with x = 0.03, 0.05, and 0.07) has been carried out by sol-gel synthesis method. The structural properties of LaFe1-xZnxO3 perovskite material were characterized using XRD, XRF, SEM, and EDS. The analysis results from XRD for LaFe1-xZnxO3 material showed that the material has an Orthorhombic structure with Pbnm space group. From the Rietveld result that lattice parameters, volume, density and also geometrical parameters happened to be distorted or changed the result of properties. SEM result shows a decreasing in grain size and with a homogenous form of spherical in each sample. XRF and EDS confirmed the presence of La, Zn, Fe and O elements in the LaFe1-xZnxO3 perovskite material. Optical properties were characterized using FTIR, Raman spectroscopy and UV-Vis. FTIR confirmed that there were stretching vibrations of Fe/Zn-O and bending vibration Fe/Zn-O-Fe/Zn while the results of Raman spectroscopy were obtained by LaFeO3 material formation and activation energy in the material seen from the formed modes. The results of UV-Vis characterization showed a decrease in the value of the bandgap energy with a range of 2.104-2.004 eV. The electrical properties of the material were tested using the RLC-meter with the Complex Impedance Spectroscopy (CIS) method with range of temperatures 30°C-200°C, where the result of increasing in conductivity and decreasing in activation energy."

"Material La_1-xPb_xFe_0.5Ti_0.5O₃ (x = 0.1, 0.2, 0.3) telah disintesis dengan menggunakan metode sol-gel. Hasil karakterisasi XRD menunjukan material memiliki struktur orthorhombik space group Pnma dan diperoleh fase tunggal untuk konsentrasi x = 0.2 dan x = 0.3 Hasil karakterisasi XRF mengkonfirmasi bahwa konsentrasi unsur-unsur penyusun material La_1-xPb_xFe_0.5Ti_0.5O₃ (x = 0.1, 0.2, 0.3) sesuai dengan perhitungan stoikiometri yang diharapkan. Hasil pengukuran SEM menunjukan distribusi ukuran grain pada permukaan sampel Bulk mengalami peningkatan seiring dengan kenaikan konsentrasi Pb. Karakterisasi sifat listrik dilakukan pada material La_1-xPb_xFe_0.5Ti_0.5O₃ dengan konsentrasi x = 0.2 dan x = 0.3. Plot Nyquist menunjukan semicircle yang semakin mengecil seiring dengan kenaikan temperatur yang menunjukan fenomena negative temperature coefficient resistance (NTCR). Konstanta dielektrik dan energi aktivasi mengalami peningkatan seiring dengan peningkatan konsentrasi Pb.

---

Material La_1-xPb_xFe_0.5Ti_0.5O₃ (x = 0.1, 0.2, 0.3) has been synthesized using the sol-gel method. XRD characterization results show that the material has an orthorhombic space group Pnma structure. The results of XRF characterization confirm that the concentration of La_1-xPb_xFe_0.5Ti_0.5O₃ material (x = 0.1, 0.2, 0.3) was in expected stoichiometric calculation. The SEM measurement results show the grain size distribution of Bulk materials increas along with the increasing Pb concentration. Characterization of electrical properties was carried out on La_1-xPb_xFe_0.5Ti_0.5O₃ material with concentrations of x = 0.2 and x = 0.3. Nyquist plots show a semicircle that decreases with increasing temperature which shows the phenomenon of negative temperature coefficient resistance (NTCR). The dielectric constant and activation energy increase with increasing Pb concentration."

"Perovskite tipe oksida jenis lanthanum orthoferrite (LaFeO3) telah menjadi salah satu kandidat jenis terbaru untuk aplikasi seperti sensor kimia, katalis, elektrolit, sel bahan bakar, biosensor, dan sensor gas. Beberapa penelitian sistematis tentang modifikasi LaFeO3 dengan melakukan substitusi yang potensial untuk dapat diaplikasikan di bidang fotokatalitik. Pada penelitian ini, material perovskite dengan telah berhasil disintesis menggunakan metode sol-gel. Proses sintesis material menghasilkan sampel dalam bentuk powder (bubuk) dan bulk (pellet). Hasil uji karakterisasi XRD menunjukkan sampel yang single phase, struktur Orthorhombic dan space group Pnma. Terjadi peningkatan nilai bond-length dan penurunan nilai bond-angle sebagai akibat dari substitusi Ti di situs Fe yang dikonfirmasi juga oleh hasil uji FTIR dan pergeseran mode pada Raman shift. Hasil uji XRF menunjukkan stoikiometri pada material yang sedikit berbeda dengan perhitungan, hal ini dikarenakan karena keterbatasan XRF untuk mendeteksi light element. Hasil uji SEM menunjukkan bahwa penambahan jumlah Ti menyebabkan rata-rata ukuran grain menurun, data ini konsisten dengan hasil yang diperoleh XRD. Sedangkan uji BET menunjukkan keberagaman nilai surface area yang dikonfirmasi juga karena adanya perbedaan komposisi elemen pada sampel powder yang dikonfirmasi dengan hasil uji XRF. Hasil uji UV-Vis menunjukkan data nilai band gap energy yang meningkat seiring dengan peningkatan doping titanium berkorelasi dengan peningkatan nilai bond-length pada XRD.

---

Lanthanum orthoferrite (LaFeO3) type oxide perovskite has become one of the newest candidate types for applications such as chemical sensors, catalysts, electrolytes, fuel cells, biosensors, and gas sensors. Several systematic studies on the modification of LaFeO3 by making substitutions have the potential to be applied in the photocatalytic field. In this study, the perovskite material with x=0,0.05, and 0.075 has been successfully synthesized using the sol-gel method. The material synthesis process produces samples in the form of powder (powder) and bulk (pellet). The results of the XRD characterization test showed that the sample was single phase, Orthorhombic structure and Pnma space group. There was an increase in the bond-length value and a decrease in the bond-angle value as a result of Ti substitution at the Fe site which was also confirmed by the results of the FTIR test and the mode shift on the Raman shift. The results of the XRF test show that the stoichiometry of the material is slightly different from the calculation, this is due to the limitations of XRF to detect light elements. The SEM test results show that increasing the amount of Ti causes the average grain size to decrease, this data is consistent with the results obtained by XRD. While the BET test shows the diversity of surface area values ​​which are confirmed also due to differences in the composition of elements in the powder sample which is confirmed by XRF test results. The results of the UV-Vis test showed that the band gap energy value increased with the increase in titanium doping and correlated with an increase in the bond-length value on XRD. "

"ABSTRAKMaterial La0.9Sr0.1Fe1-xMoxO3 x=0.1, 0.2, 0.3 telah disintesis dengan metode sol-gel. Dari hasil karakterisasi termal menggunakan DTA-TGA dihasilkan pengaruh temperature terhadap pembentukan kristal. Analisis dekomposisi massa terhadap termal melalui kurva TGA/DTA menunjukan proses pembentukan kristal melalui empat step yaitu dehidarasi fasa air , dekomposisi fasa organik asam sitrat dan ditandai juga munculnya dua buah puncak eksotermik pada rentang suhu C sampai dengan C, dan pembentukan fasa kristal terjadi pada suhu C. Adapun dari karakterisasi X-ray Diffraction XRD material LSFMO hasil sintering ditunjukan struktur material Orthorhombic dengan space group Pnma. Adapun hasil uji X-ray Fluorescence XRF dan Energy Dispersive X-ray Spectroscopy EDS menunjukan stoikiometri pada material LSFMO mendekati hasil teori yang diinginkan dan untuk hasil Scanning Electron Microscopes SEM menunjukan grain size menurun seiring meningkatnya komposisi doping Mo. Karakterisasi listrik material LSFMO sebagai fungsi temperatur 100oC-250oC dengan frekuensi 100 Hz - 1 MHz diuji dengan metode Impedance Spectroscopy IS dengan menggunakan RLC meter. Data IS disajikan dalam bentuk Nyquist Plot dan Bode Plot, pada hasil Bode Plot menunjukan relaksasi dengan nilai energi aktivasi sebesar dan . Karena nilai dari energi aktivasi yang diperoleh yaitu , maka hal ini mengindikasikan bahwa tipe pembawa muatan pada proses relaksasi adalah p-type.

---

ABSTRACT The material La0.9Sr0.1Fe1 xMoxO3 x 0.1, 0.2, 0.3 has been synthesized by sol gel method. The result of thermal characterization using DTA TGA produced temperature effect to crystal formation. The analysis of mass decomposition of thermal through the TGA DTA curve shows the process of crystalline formation by four steps the drainage of water phase , organic phase decomposition citric acid , the appearance of two exothermic peaks in the temperature range up to C, and crystalline phase formation that occurs at temperatures C. The characterization of X ray Diffraction XRD LSFMO material of sintering showed Orthorhombic material structure with Pnma space group. The results of X ray Fluorescence XRF and Energy Dispersive X ray Spectroscopy EDS showed stoichiometry on LSFMO material approaching the desired theoretical results. The results of Scanning Electron Microscopes SEM showed the decreasing grain size as the doping composition increased. Electrical characterization of LSFMO material as a function of temperature 100oC 250oC with frequency 100 Hz 1 MHz was tested by Impedance Spectroscopy IS method using RLC meter. IS data is presented by the form of Nyquist Plot and Bode Plot. Bode Plot shows the relaxation with the energy activation value of 0.33 eV, 0.28 eV and 0.23 eV. From this experiment, The energy activation is obtained at , indicating that the type of carrier in the relaxation process is p type."

"Perosvkite bimuth ferrite (BiFeO3) dengan variasi temperatur kalsinasi (500°C, 600°C dan 700°C) telah disintesis menggunakan metode sol-gel. Karakterisasi sampel dilakukan untuk mempelajari sifat struktur (XRD, XRF dan SEM-EDS), sifat optik (FTIR dan UV-Vis) dan sifat listrik (spektroskopi impedansi). Hasil analis XRD menggunakan program Fullproof menunjukkan semua sampel mempunyai struktur hexagonal dengan space group R3c. Single phase BiFeO3 terbentuk pada temperatur kalsinasi 700°C, sedangkan untuk sampel yang dikalsinasi pada temperatur 500°C dan 600°C masih terdapat fase kedua berupa Bi2Fe4O9. Hasil uji SEM menunjukkan semua sampel mempunyai ukuran grain yang tidak homogen. Analisa SEM menggunakan program ImageJ menunjukkan peunurunan ukuran grain sampel yang dikalsinasi pada suhu 500°C, 600°C dan 700°C secara berurutan adalah 2459.42, 1847.11 dan 1693.98 nm. Hasil UV-Vis menunjukkan adanya peningkatan energi gap dengan rentang 1.98 eV-2.06 eV ketika temperatur kalsi dinaikkan. Peningkatan bandgap optik dapat dihubungkan dengan penurunan nilai bond length. Pengukuran data impedansi dilakukan pada rentang frekuensi 1 kHz-1 MHz dan rentang temperatur 30°C-250°C. Nyquist plot untuk semua sampel menunjukkan dua busur setengah lingkaran yang diameternya berkurang ketika temperatur meningkat. Hal ini mengindikasikan perubahan dari sifat resistif dan kapasitif sampel dan mengindikasikan negative temperature coefficient (NTCR) yang merupakan sifat dari material semikonduktor. Nilai konstanta dielektrik pada semua sampel BiFeO3 meningkat seiring dengan meningkatnya temperatur. Hal ini mengindikasikan terjadinya peningkatan mobilitas dari charge carrier oleh temperatur (thermal energy). Plot fungsi temperatur menunjukkan terjadinya peningkatan dielektrik konstan ketika temperatur meningkat pada semua sampel. Peningkatan dielektrik konstan cukup signifikan pada frekuensi rendah dan pada temperature tinggi. Fenomena ini menunjukkan polarisasi interfacial mempunyai efek dominan pada sampel dibandingkan dengan polarisasi lainnya.

---

Bismuth ferrite (BiFeO3) with calcination temperature variation (500°C, 600°C and 700oC) has been synthesized using sol-gel method. Sample characterization has been done to studying structure properties (XRD, XRF and SEM-EDS), optical properties (FTIR and UV-Vis) and electrical properties (impedance spectroscopy). XRD analyze result using Fullproof software show all samples has hexagonal structure with R3c space group. Single phase BiFeO3 obtained at calcination temperature 700°C, while for sample calcined at 500°C and 600°C still has second phase (Bi2Fe4O9). SEM characterization show all samples has inhomogeneous grain size. SEM analyse using ImageJ software show the decreasing grain size calcined at temperature 500°C, 600°C and 700°C are 2459.42, 1847.11 and 1693.98 nm respectively. UV-Vis result show increasing gap energy around 1.98 eV-2.06 eV as calcination temperature increase. Increasing optical bandgap can be related with decreasing bond length value. Impedance measurement carried out in frequency range 1 kHz-1 MHz and temperature range 30°C-250°C. Nyquist plot for all sample show two semicircle with decreasing diameter as temperature raise. This indicate change in resistive and capacitive properties and also indicating negative temperature coefficient (NTCR) which is behaviour of semiconductor material. Dielectric constant value for all BiFeO3 sample increase as temperature increase. This indicate increasing charge carrier mobility by thermal. Temperature function plot show increasing dielectric constant as temperature increase for all sample. Significant increase in dielectric constant at low frequency region and high temperature. This phenomena show interfacial polarization has dominant effect on all samples."

"Material perovskite LaFe_1-xMn_xO₃ (x = 0,05, 0,10, 0,15, 0,20) telah disintesis dengan menggunakan metode sol-gel. Hasil karakterisasi menggunakan X-Ray Diffraction (XRD) menunjukan struktur kristal orthohombic dengan fase tunggal untuk semua sampel. Nilai crystallite size menurun seiring dengan meningkatnya substitusi Mn, dari 79,5 nm – 58,7 nm.  Karakterisasi FTIR menunjukan adanya vibrasi bending Fe/Mn – O – Fe/Mn dan stretching Fe/Mn – O pada sampel. Hasil X-Ray Fluorescence (XRF) komposisi unsur sampel LaFe_1-xMn_xO₃ telah sesuai dengan komposisi unsur hasil perhitungan. Sifat mikrostruktur hasil karakterisasi Scanning Electron Microscopy (SEM) menunjukan permukaan sampel dengan bentuk grain homogen bulat dengan adanya porositas. Nilai grain meningkat seiring meningkatnya subtitusi Mn dan menyebabkan porositas berkurang. Karakteriasi sifat listrik material LaFe_1-xMn_xO₃ dilakukan dengan menggunakan metode spektroskopi impedansi pada rentang frekuensi 100 Hz – 1 MHz. Karakterisasi dilakukan pada temperatur kamar dan  temperatur tinggi (100^oC – 275^oC). Data hasil karakterisasi disajikan dalam grafik nyquist plot dan bode plot. Pada temperatur kamar nyquist plot menunjukan penurunan ukuran semisirkular seiring bertambahnya konsentrasi substitusi Mn. Nilai konstanta dielektrik pada suhu kamar menunjukan typical colossal dielectric constant. Nyquits plot pada temperatur tinggi menunjukan sifat negative temperatur coefficient of resistance (NTCR). Hasil fitting energi aktivasi dari slope log ( ) versus 10³/T plots menunjukan bahwa nilai energi aktivasi (Ea) grain menurun dengan meningkatnya konsentrasi subtitusi Mn. Bode plot menunjukan fenomena relaksasi yang bergantung pada temperatur. Nilai waktu relaksasi menurun seiring dengan meningkatnya temperatur menunjukan typical semiconductor behavior. Energi aktivasi (Ea) yang dihitung dari waktu relaksasi menunjukan kecenderungan yang sama dengan energi aktivasi (Ea) grain. Nilai band gap energy meningkat seiring meningkatnya konsentrasi substitusi Mn.

---

Perovskite material LaFe_1-xMn_xO₃ (x = 0.05, 0.10, 0.15, 0.20) has been synthesized using the sol-gel method. The results of characterization using X-Ray Diffraction (XRD) show a single phase orthohombic crystal structure for all samples. The crystallite size value decreases with increasing Mn substitution, from 79.5 nm - 58.7 nm. FTIR characterization shows the presence of vibrations bending Fe/Mn – O – Fe/Mn and stretching Fe/Mn – O in the sample. The results of X-Ray Fluorescence (XRF) composition of LaFe_1-xMn_xO₃ sample elements are in accordance with the composition of the calculated elements. The microstructure of the the characterization results by Scanning Electron Microscopy (SEM) shows the surface of the sample in the form of a round homogeneous grain in the presence of porosity. Grain value increases with increasing Mn substitution cause decreasing porosity. The electrical properties of LaFe_1-xMn_xO₃ material is carried out using impedance spectroscopic methods in the frequency range of 100 Hz - 1 MHz. Characterization are carried out at room temperature and high temperature (100^oC – 275^oC). Data from characterization results are presented in nyquist plot and bode plot charts. The nyquist plot at room temperature shows decreasing impedance semicircle with increasing Mn substitution. The dielectric constant at room temperature shows colossal dielectric constant behavior. The nyquist plot at high temperature shows a negative temperature coefficient of resistance (NTCR). The result of energy fitting activation of the slope log ( ) versus 10³/T plots shows that the activation energy value (Ea) grain decreases with increasing Mn substitution concentration. Bode plots show the phenomenon of relaxation which depends on temperature. The value of relaxation time decreases with increasing temperature indicating typical semiconductor behavior. The activation energy (Ea) calculated from the relaxation time shows a tendency similar to the activation energy (Ea) grain. The band gap energy value increases with increasing concentration of Mn substitution."

"Lanthanum titanium oxide (La2Ti2O7) dengan rumus Umum A2B2O7, termasuk dalam tipe perovskite-like layer structure (PLS) berstruktur monoklinik dengan space group P21. Perovskite La2Ti2O7 memiliki karakteristik menarik seperti material dengan struktur berlapis yaitu berisi empat lapisan oktahedra TiO6 yang saling menempel di sudut, toksisitas rendah, stabilitas yang baik, dan ketahanan fotokimia. sehingga bisa diterapkan dalam beberapa bidang aplikasi, seperti sebagai fotokatalis, aplikasi konversi energi matahari dan dan fotodinamik medis terapi. Material La2Ti2O7 yang disubstitusi dengan Zn pada situs Ti (La2Ti2-xZnxO7 dengan x=0.0, 0.1 dan 0.2) telah berhasil disintesis menggunakan metode sol-gel. Proses sintesis material menghasilkan sampel dalam bentuk powder. Uji karakterisasi yang telah dilakukan adalah XRD, XRF, BET, FTIR, Raman, UV-VIS dan RLC-meter. Hasil XRD menunjukkan sampel yang single phase, struktur monoklinik dan space group P21. Hasil XRD juga menunjukkan pergeseran puncak hkl ke sudut yang lebih tinggi, menandakan terjadinya perubahan nilai parameter kisi, yang mengindikasihan bahwa terjadinya penurunan volume sel kisi sebagai akibat dari substitusi Zn di situs Ti, dan ukuran kristal juga menurun seiring penambahan jumlah-Zn. Hasil uji FTIR menunjukkan bahwa material yang terbentuk adalah La2Ti2O7 dan mode pada Raman shift yang juga menunjukan bahwa sampel single phase. Hasil XRD menunjukkan pergeseran puncak hkl ke sudut yang lebih tinggi yang menunjukkan indikasi tersubsitusinya Zn ke dalam material La2Ti2O7 dan hasil ini juga diperkuat dengan hasil XRF. Hasil BET menunjukkan Ukuran kristal dan ukuran pori berkurang, sedang luas permukaan dan volume pori total bahan diperbesar setelah penambahan Zn dalam nanopartikel La2Ti2O7. kurva adsorpsi-desorpsi nitrogen dari La2Ti2-xZnxO7 (x =0.0, 0.1, dan 0.2), yang menunjukkan isotherm tipe IV dengan histeresis H3, yang menunjukan material ini termasuk mesopori. Hasil uji UV-Vis menunjukkan data nilai energi band gap menurun seiring dengan peningkatan doping. Hasil uji mengunakan RLC-meter menunjukan diameter lingkaran Nyquist dan nilai resistansi semakin bertambah besar seiring bertambahnya konsentrasi Zn. Hasil uji konstanta dielektrik menunjukkan bahwa konstanta dielektrik real terhadap frekuensi mengalami penurunan mengikuti penambahan konsentrasi doping, sedangkan konstanta dielektrik imajiner terhadap frekuensi menunjukan sebaliknya meningkatnya setiap penambahan konsentrasi doping dan membentuk 1 puncak relaksasi pada frekuensi diatas 1000KHz.

---

Lanthanum titanium oxide (La2Ti2O7) with the general formula A2B2O7, belongs to the type of perovskite-like layer structure (PLS) with monoclinic structure with space group P21. Perovskite La2Ti2O7 has attractive characteristics such as a material with a layered structure that contains four layers of TiO6 octahedra attached to each other at corners, low toxicity, good stability, and photochemical resistance. so that it can be applied in several fields of application, such as photocatalysts, solar energy conversion applications, and medical and photodynamic therapy. La2Ti2O7 material which is substituted with Zn at the Ti site (La2Ti2-xZnxO7 with x=0.0, 0.1, and 0.2) has been successfully synthesized using the sol-gel method. The material synthesis process produces a sample in the form of a powder. The characterization tests that have been carried out are XRD, XRF, BET, FTIR, Raman, UV-VIS, and RLC-meter. XRD results show that the sample is a single phase, monoclinic structure, and space group P21. The XRD results also showed a shift of the hkl peak to a higher angle, indicating a change in the value of the lattice parameter, which indicated that there was a decrease in lattice cell volume as a result of Zn substitution at the Ti site, and the crystal size also decreased with the addition of Zn-amount. The FTIR test results show that the material formed is La2Ti2O7 and the Raman shift mode also shows that the sample is single phase. The XRD results show a shift of the hkl peak to a higher angle which indicates the substitution of Zn into the La2Ti2O7 material and this result is also strengthened by the XRF results. The BET results showed that the crystal size and pore size were reduced, while the surface area and total pore volume of the material were enlarged after the addition of Zn in La2Ti2O7 nanoparticles. the nitrogen adsorption-desorption curve of La2Ti2-xZnxO7 (x = 0.0, 0.1, and 0.2), which shows a type IV isotherm with H3 hysteresis, which indicates this material is mesoporous. The results of the UV-Vis test showed that the bandgap energy value decreased with the increase in doping. The test results using an RLC-meter showed the diameter of the Nyquist circle and the resistance value increased with increasing Zn concentration. The results of the dielectric constant test show that the real dielectric constant with respect to frequency decreases following the increase in doping concentration, while the imaginary dielectric constant with respect to frequency shows the opposite increasing with each additional doping concentration and forms 1 relaxation peak at frequencies above 1000KHz."