"Penelitian ini membahas mengenai karakteristik dari lapisan ganda TiO2/ZnO yang disintesis dengan metode spin coating dan hidrotermal di atas substrat kaca FTO pada aplikasi sel surya perovskite. Nanostruktur ZnO disintesis melalui proses hidrotermal di atas kaca konduktif fluorine-doped tin oxide (FTO) pada temperatur 90°C selama 3 jam dengan ketebalan lapisan 3 layer. Sementara itu nanostruktur TiO2 disintesis dengan menggunakan metode spin coating dengan variasi konsentrasi TiO2 0.3 M, 0.6 M, dan 0.9 M yang kemudian di annealing diatas hot plate dengan temperatur 450oC selama 1 jam. Fasa yang terbentuk dari proses sintesis TiO2 adalah fasa anatase sementara fasa yang terbentuk dari proses sintesis ZnO adalah zincite. Pengaruh dari variasi konsentrasi TiO2 yang digunakan, dikarakterisasi menggunakan difraksi sinar-X (XRD), sementara morfologi dari nano rosette yang dihasilkan diamati dengan field emission scanning electron microscope (FE-SEM). Pada konsentrasi TiO2 0.3 M didapatkan nilai efisiensi sebesar 0.02%, untuk konsentrasi 0.6 M sebesar 0.003%, dan konsentrasi 0.9 M sebesar 0.004%. Nilai efisiensi tertinggi didapatkan pada variasi konsentrasi 0.3 M, hal ini dikarenakan pengaruh ukuran kristalit yang dihasilkan. Semakin kecil ukuran kristalit dari nanostruktur yang dihasilkan, maka nilai efisiensi dari sel surya perovskite akan menghasilkan nilai efisiensi yang semakin tinggi.

---

This study discusses the characteristics of the TiO2 / ZnO double layer synthesized by the spin coating and hydrothermal method on FTO glass substrates for perovskite solar cell applications. ZnO nanostructures were synthesized through hydrothermal process on fluorine-doped tin oxide (FTO) conductive glass at a temperature of 90°C for 3 hours with 3 layers thickness. Meanwhile, TiO2 nanostructures are synthesized using the spin coating method with variations in the concentration of 0.3 M, 0.6 M, and 0.9 M TiO2 which is then annealed on a hot plate with a temperature of 450oC for 1 hour. The phase formed from the synthesis process of TiO2 is the anatase phase while the phase formed from the synthesis process of ZnO is zincite. The effect of variations in the concentration of TiO2 was characterized using X-ray diffraction (XRD), while the morphology of the nanostructure produced was observed with a field emission scanning electron microscope field (FE-SEM). At the concentration of 0.3 M TiO2 the efficiency value is 0.02%, for concentrations of 0.6 M is 0.003%, and a concentration of 0.9 M at 0.004%. The highest efficiency value was obtained at a variation of the concentration of 0.3 M, this is due to the influence of the size of the crystallite produced. The smaller the size of the crystallite from the nanostructure produced, the efficiency value of perovskite solar cells will result in higher efficiency values."

"Sel Surya Perovskite (PSC) adalah generasi keempat dari sel surya yang mengandung senyawa berstruktur perovskite. Senyawa ini umumnya merupakan gabungan dari senyawa organic-anorganik dari Timbal (Pb) yang berperan sebagai lapisan aktif penyerap cahaya. PSC memiliki sifat fotovoltaik yang sangat baik seperti penyerapan cahaya yang sangat baik dan mobilitas carrier yang tinggi. Namun, efisiensi dari PSC dan juga kualitas dari lapisan perovskite yang terbentuk menjadi keterbatasan utama dari sel surya ini. Dengan menambahkan oksida grafena tereduksi (rGO), diharapkan rekombinasi muatan pada batas butir yang ada dapat berkurang dan dapat meningkatkan efisiensi dengan signifikan. Selain itu substitusi parsial dari lapisan perovskite PbI2 dengan ZnCl2 juga diketahui dapat meningkatkan perpindahan elektron dari sel surya, yang menghasilkan efisiensi PSC yang lebih tinggi. PSC ini pada umumnya diproduksi pada lingkungan yang inert, namun pada penelitian ini, penggunaan rGO sebagai penstabil pada lapisan kompak ZnO nanorod akan diproduksi pada lingkungan ambien. Pengaruh dari penambahan rGO sebagai penstabil ini berhasil meningkatkan efisiensi dari sel surya hingga lebih dari 2x lipat.

---

Perovskite solar cell (PSC) is a fourth-generation solar cell containing perovskite structured compound, mainly from organic-anorganic hybrid of lead. This perovskite acts as an active layer that collects the light from the solar. PSC has a very good photovoltaic properties such good light absorption and high carrier mobility. However, the overall efficiency of PSC and the quality of the perovskite layer formed are the primary limitation of this solar cell. Reduced graphene oxide (rGO) is expected to to increase the efficiency of the solar cell. By adding rGO to the solar cell, charge recombination in grain boundaries can be reduced and thus increase the efficiency. Substituting the perovskite layer from lead iiodide (PbI2) to zinc chloride (ZnCl2) is one of the way to increase the electron transport from the solar cell, which means a higher overall efficiency from the PSC. The PSC is normally manufactured under inert environment, but in this research the addition of rGO to zinc oxide (ZnO) nanorods was integrated under ambient environment. The addition of rGO as a stabilizer successfully increases the solar cell efficiency by more than two folds.

"

"Karakteristik dari lapisan nanokomposit TiO2/rGO sebagai lapisan kompak sel surya perovskite telah diamati. Lapisan ini berhasil dideposisikan di atas substrat kaca konduktif fluorine-doped tin oxide (FTO) dengan variasi konsentrasi TiO2 sebesar 0,3125 M, 0,625 M, dan 0,9375 M dan variasi persen volume rGO dalam pelarut 0,4% vol., 0,5% vol., dan 0,6% vol. rGO. Proses kalsinasi untuk setiap variasi konsentrasi TiO2 nanopartikel dilakukan pada temperatur 450°C selama 90 menit dan hal yang sama dilakukan untuk kalsinasi lapisan nanokomposit TiO2/rGO. Lapisan perovskte yang digunakan pada penelitian ini menggunakan campuran antara metil amunium iodida (MAI), PbCl2 dan ZnCl2 yang dilarutkan dalam DMSO. Pengaruh dari konsentrasi TiO2 nanopartikel dan persen volume rGO diamati dengan field emission scanning electron microscope (FE-SEM) untuk melihat morfologi dan ukuruan butir, sedangkan sifat kristalinitas dan fasa yang terbentuk diamati menggunakan difraksi sinar-X (XRD). Pengujian terhadap efisiensi juga dilakukan menggunakan I-V analyzer. Morfologi butir menunjukkan bahwa setiap kenaikan konsentrasi TiO2 membuat densitas TiO2 semakin tinggi dan persebaran butir lebih merata pada semua area. Fasa yang terbentuk menunjukkan adanya fasa anatase dan rutile yang merupakan fasa utama dalam TiO2 P25 Degussa. Untuk morfologi nanokomposit TiO2/rGO, terlihat bahwa pada persen volume 0,4% persebaran rGO terlihat namun sangat tipis dan kurang merata pada seluruh bagian, pada 0,5% vol. rGO terlihat bahwa persebaran rGO pada celah antarpartikel TiO2 terdistribusi merata, dan pada 0,6% vol. rGO terlrihat bahwa rGO menutupi sebagian besar lapisan TiO2. Hasil pengujian efisiensi yang didapatkan menunjukkan bahwa hasil efisiensi terbesar didapatkan pada konsentrasi 0,3125 M dan 0,5% vol. rGO dengan efisiensi sekitar 3,4216%.

---

Characteristics of TiO2/rGO nanocomposite layers as compact layers of perovskite solar cells have been observed. This layer was successfully deposited on a fluorine-doped tin oxide (FTO) conductive glass substrate with variations in TiO2 concentrations of 0.3125 M, 0.625 M, and 0.9375 M and variations in volume percent of rGO in solvents 0,4 vol%, 0,5 vol%, and 0.6 vol%. rGO. The calcination process for each variation of TiO2 nanoparticle concentration was carried out at a temperature of 450°C for 90 minutes and the same was done for the calcination of the TiO2/rGO nanocomposite layer. The perovskte layer used in this study uses a mixture of methyl amunium iodide (MAI), PbCl2 and ZnCl2 which are dissolved in DMSO. The effect of TiO2 nanoparticle concentration and rGO volume percent was observed by emission scanning electron microscope field (FE-SEM) to see the morphology and grain size, while the crystallinity and formed phases were observed using X-ray diffraction (XRD).

Testing of efficiency is also done using an I-V analyzer. Grain morphology showed that every increase in TiO2 concentration made the TiO2 density higher and grain distribution more evenly distributed in all areas. The phase formed shows the presence of anatase and rutile phases which are the main phases in Degussa P25 TiO2. For the morphology of TiO2/rGO nanocomposite, it is seen that in the volume percent of 0.4% the distribution of rGO is visible but very thin and less evenly distributed in all parts, at 0.5 vol%. rGO shows that the distribution of rGO in the interparticle gap of TiO2 is evenly distributed, and at 0.6 vol%. rGO is concerned that rGO covers most layers of TiO2. The efficiency test results obtained show that the greatest efficiency results were obtained at concentrations of 0.3125 M and 0.5 vol%. rGO with efficiency of around 3.4216%."

"ZnO nanorod telah berhasil disintesis menggunakan prekursor HMTA dan seng nitrat tetrahidrat melalui metode chemical bath deposition (CBD) yang sebelumnya telah melalui proses pembibitan dengan menggunakan larutan natrium hidroksida (NaOH) dan seng asetat dihidrat (Zn(CH₃COOH)₂.2H₂O). Perlakuan yang diberikan adalah variasi konsentrasi larutan CBD, yaitu 0,025 M; 0,0375M; 0,05M; dan 0,075M dan variasi durasi waktu proses CBD, yaitu 2 jam, 3 jam, 4 jam, dan 6 jam dengan tujuan untuk menganalisa pengaruh kedua hal tersebut terhadap hasil mikrostruktur ZnO, diameter ZnO nanorod, serta kristalinitas yang terbentuk. Hasil yang didapatkan kemudian diaplikasikan untuk fabrikasi sel surya berbasis perovskite dengan melihat performa efisiensi konversi (η) dari PSC yang telah difabrikasi. Metode karakterisasi material yang digunakan adalah X-ray Diffraction (XRD), dan Scanning Electron Microscope (SEM). Pengujian performa dar PSC yang telah difabrikasi menggunakan Semiconductor Parameter Analyzer dengan menganalisis kurva arus dan tegangan (I-V). Hasil penelitan menunjukkan bahwa dengan naiknya konsentrasi prekursor yang digunakan, maka akan terjadi kenaikan diameter ukuran butir ZnO nanorod, kristalinitas serta intensitas difraksi ZnO yang dihasilkan. Seiring naiknya durasi waktu proses hidrotermal pada kondisi konsentrasi yang sama juga menunjukkan adanya peningkatan diameter ZnO nanorod yang dihasilkan, peningkatan panjang dari Zno nanorod serta kenaikan kristalinitas dari ZnO. Efisiensi PCE yang paling optimal didapatkan pada kondisi sampel dengan konsentrasi prekursor 0,0375 M dan dengan durasi 3 jam, efisiensi yang didapatkan sebesar 0,027%.

---

The characteristics of ZnO grown via chemical bath deposition on an FTO glass substrate at different reaction time and precursors concentration has been examined. The seed of ZnO was firstly spin coated at 500 rpm for 5 seconds onto an FTO glass substrate and then at 3000 rpm for another 30 seconds. The coated substrate was then heated at 90 °C to remove the solvent. The growth of ZnO was performed via chemical bath deposition at various precursors concentration and reaction time. The morphology of the obtained ZnO nanorods were characterized using field-emission electron microscope (FE-SEM) equipped with energy dispersive X-ray spectroscopy (EDX) to reveal the morphology and elemental composition of the nanorod, whereas X-ray diffraction (XRD) was used to examine the crystal structure.

The results showed that the ZnO products have nanorod structure and sizes for each concentration. The results of this morphology were supported by the results from XRD. XRD patterns revealed that the formation of nanostructure of ZnO has been obtained at reaction time of 2 hour. The performance test of a fabricated PSC using the Semiconductor Parameter Analyzer by analyzing the current and voltage curves (I-V).

The results show that with the increase in the concentration of the precursors used, there will be an increasing the diameter of the ZnO nanorod grain size, the crystallinity and intensity of the ZnO nanorod. As the duration of the hydrothermal process increases in the same concentration conditions also shows an increasing of ZnO nanorod diameter, an increase in the length of Zno nanorod and an increase in the crystallinity of ZnO. The highest PCE efficiency was obtained in the condition of the sample with precursor concentration of 0.0375 M and with a duration of 3 hours., The efficiency obtained was 0.027%."

"Sel surya merupakan divais elektronika yang dapat mengubah energi cahaya menjadi energi listrik. Saat ini Indonesia memiliki banyak hasil bumi salah satunya timah. Timah merupakan bahan dasar dalam pembuatan berbagai komponen elektronika, salah satunya electron transport layer (ETL) dari sel surya perovskite. Sel surya perovskite pada umumnya menggunakan TiO2 sebagai ETL yang memiliki work function sebesar -4,1 eV. SnO2 memiliki work function yang lebih besar, yaitu -4 eV; sehingga secara teori SnO2 dapat menggantikan TiO2. Penelitian ini menguji penggunaan timah pada sel surya perovskite sebagai ETL. Timah yang digunakan diambil dari bahan timah (II) klorida dihidrat. Timah (II) klorida dihidrat akan dilarutkan menggunakan ethanol. Struktur sel surya perovskite yang digunakan adalah FTO/SnO2/Perovskite/karbon aktif/FTO. Sel surya perovskite dalam penelitian ini tidak menggunakan hole transport layer (HTL) karena sifat dari karbon aktif yang menggunakan minyak paraffin sebagai perekat dapat berperan sebagai HTL. Penelitian pra skripsi menunjukkan ethanol merupakan pelarut yang lebih baik dari thiourea, dengan Isc = 0,0015 mA; Voc = 0,1 mV; dan FF = 0,4. Skripsi ini meneliti lebih jauh terhadap dampak konsentrasi SnO2 pada larutan prekursor dengan melakukan variasi pada jumlah timah (II) klorida dihidrat yang dicampur ke ethanol. Hasil fabrikasi menunjukkan bahwa sel surya perovskite dengan pencampuran 30 mg timah (II) klorida dihidrat dengan 1 ml ethanol menghasilkan Isc dan Voc yang paling baik, yaitu Isc = 0,19 mA dan Voc = 0,177 V; namun tidak memiliki konsistensi yang baik dan memiliki dark IV curve linear, menandakan unjuk kerja yang buruk. Sampel C yang dibuat dari pencampuran 20 mg timah (II) klorida dihidrat dengan 1 ml ethanol menunjukkan konsistensi yang baik dan dark IV cruve yang baik. Sampel C memiliki Isc = 0,033 mA; Voc = 0,026 V dan FF= 0,538.

---

Solar cell is an electronic device that convert solar energy into electrical energy. Indonesia has enormous amount of tin, that responsible for producing several amount of electrical device, electron transport layer (ETL) is one of them. Perovskite solar cell frequently uses TiO2 as an ETL that has work function -4.1 eV. SnO2 has better work function, -4 eV; that make SnO2 can become replacement for TiO2 theoritically. This research test the usage of tin on solar cell perovskite as an ETL. Tin derived from tin (II) choride dihydrate, that will be mixed with ethanol. Perovskite solar cell structure used is FTO/SnO2/Perovskite/activated carbon/FTO. In this research, perovskite solar cell did not use hole transport layer (HTL) because of the nature of activated carbon using paraffin oil as an adhesive to act as a HTL. Pra Skripsi shows the best result is obtained from SnO2 that used ethanol as precursor, with Isc = 0.0015 mA, Voc = 0.1 mV, and FF = 0.4. This research concentrate on variating the amount of tin (II) chloride dihydrate that mixed with ethanol. Perovekite solar cell with mixture of 30 mg tin (II) chloride dihydrate with 1 ml ethanol produce Isc = 0.19 mA and Voc = 0.177 V that has best Voc and Isc; but lack of concintency and has linear dark IV curves, resulting on bad performance. Sampel C obtained from 20 mg tin (II) choride dihydrate with 1 ml ethanol shows better consistency, FF and better IV curve. with Isc = 0.033 mA; Voc = 0.026 V and FF= 0.538."

"Seiring dengan perkembangan zaman, kebutuhan energi manusia semakin meningkat dan dibutuhkan berbagai alternatif sumber energi untuk memenuhinya, salah satu teknologi yang dapat memenuhi kebutuhan tersebut adalah sel surya. Salah satu jenis dari sel surya yang sedang berkembang secara pesat adalah sel surya perovskit. Sel surya perovskit masih memiliki beberapa permasalahan, diantaranya yaitu saat muatan bergerak antara lapisan sel surya, dapat terjadi fenomena yang bernama trapped charges, dan salah satu metode untuk mengatasi permasalahan tersebut adalah penambahan TEOS sebagai lapisan pasif pada saat deposisi lapisan aktif yang dapat memperbaiki ketidaksempurnaan kontur yang menyebabkan muatan menjadi trapped. Fabrikasi TEOS dengan katalis CuO/SiO2 memberikan TEOS yang memiliki ikatan antar atom yang lebih kuat dan kualitas bahan yang lebih baik. Konsentrasi dari katalis dapat memberi dampak pada produk akhir dari reaksi kimia, dan nilai suhu saat reaksi berlangsung juga terkadang memengaruhi kebutuhan konsentrasi katalis untuk proses reaksi, sehingga nilai konsentrasi terbaik untuk fabrikasi TEOS sebagai lapisan pasif perlu dicari. Penelitian dilakukan dengan menggunakan konsentrasi katalis yang berbeda dengan nilai 0,5 mol%; 1 mol%; and 1,5 mol% dari katalis CuO/SiO2 untuk fabrikasi TEOS yang kemudian akan dideposisikan sebagai lapisan pasif sel surya. Fabrikasi dari sel surya perovskit yang menggunakan lapisan pasif yang fabrikasinya menggunakan konsentrasi katalis CuO/SiO2 sebanyak 1 mol% dengan struktur TiO2/Perovskit/Karbon memberikan hasil terbaik dengan

---

product, and the temprature in which the chemical reaction happen can sometimes have impact on the consentration of the catalyst needed, so the ideal consentration for TEOS fabrication as passive layer need to be discovered. Research is done by using different catalyst concentration of 0.5 mol%, 1 mol%, and 1.5 mol% of CuO/SiO2 catalyst for TEOS fabrication which then later deposited as the passive layer of solar cell. Solar cell fabrication with a passive layer that utilizes 1 mol% of CuO/SiO2 catalyst with TiO2/Perovskite/carbon structure yield the best result with value of Isc 21.18 A, value of Voc 0.04 mV, and fill factor of 0.243."

"Sel surya berbahan perovskite adalah sel surya generasi ketiga yang menggunakan lapisan aktif berbahan halida organik-inorganik sebagai lapisan penyerap energi matahari yang lalu akan dikonversi menjadi energi listrik. Selama 10 tahun terakhir, telah tercatat sel surya perovskite yang dikembangkan dan di uji di dalam laboratorium sudah mencapai efisiensi 22,11%. Metode trap passivation adalah metode penambahan lapisan pasif pada lapisan aktif untuk memperbaiki unjuk kerja sel surya perovskite dengan membantu meminimalisir adanya trap state pada elektron yang tereksitasi antar lapisan sel surya perovskite. Oleh karena itu, pada Skripsi ini dilakukan analisis pengaruh dari penambahan konsentrasi lapisan pasif dalam bentuk Tetra-ethyl Orthosilicate (TEOS) untuk membandingkan dengan Sampel tanpa penambahan TEOS, serta untuk meningkatkan unjuk kerja sel surya perovskite. Pada Skripsi ini, sebanyak 4 sel telah difabrikasi dengan konsentrasi TEOS sebesar 0% mol; 0,25% mol; 0,3% mol; dan 0,35% mol. Nilai konsentrasi TEOS paling optimal yang didapat pada percobaan ini adalah 0,25% mol dengan nilai rata- rata Voc sebesar 1,23 V; Isc sebesar 9,25 mA; efisiensi sebesar 3,267 % dan FF sebesar 0,506.

---

Perovskite solar cell (PSC) is a third-generation solar cell in which the active material is formed using an organic-inorganic halide. PSCs have shown rapid development over the past 10 years with an increase of efficiency up to 22.11%. Trap passivation is a method of adding a passivation layer into the active layer that can be employed to prevent charge trap state caused by the non-uniformity at the active cell interlayer surface which can further improve the performance of perovskite solar cells. Therefore, in this thesis, the researcher applied and analyzed the effect of different concentration levels of a passivation layer in a form of tetraethyl orthosilicate (TEOS); 0%; 0.25%; 0.3%; 0.35%; towards the performance of perovskite solar cells as well as a comparison to the Sample that didn’t employ the TEOS solution. In this research, a best average result is obtained with 0.25% mol of applied TEOS additive into the perovskite active layer with Voc, Isc, efficiency, and FF value of 1.23 V, 9.25 mA, 3.267% and 0.506 respectively."

"Sel surya perovskite merupakan sel surya yang menggunakan organic-metal halide sebagai lapisan aktif pada sel surya. Pada tahun 2009, sel surya perovskite pertama kali difabrikasi dan mencapai efisiensi sebesar 3,8% dan pada tahun 2014 sudah mencapai 19,3%. Efisiensi tertinggi yang tercatat adalah sebesar 23,3%. Dalam kurun waktu 4-5 tahun sel surya perovskite sudah menunjukkan potensinya yang besar karena sudah hampir dapat menyaingi sel surya berbahan silikon. Biaya fabrikasinya yang murah, stabilitas yang baik, dan proses fabrikasi yang mudah membuat sel surya perovskite sangat menjanjikan untuk bersaing dengan sel surya silikon. Salah satu metode fabrikasi sel surya perovskite adalah dengan menggunakan proses annealing. Proses annealing merupakan proses pemanasan subtrat sampai suhu tertentu sehingga zat pelarut mulai menguap. Penelitian tentang sel surya perovskite sudah banyak, tetapi belum ada yang membahas secara langsung pengaruh suhu annealing pada struktur sel surya perovskite yang dipakai pada penelitian ini. Oleh karena itu pada penelitian ini akan dilakukan variasi suhu annealing 110ºC, 120ºC, dan 130ºC pada proses deposisi lapisan aktif sel surya perovskite dengan tujuan mencari suhu yang paling tepat terhadap efisiensi sel surya. Hasil dari penelitian ini menyatakan bahwa pada suhu 130ºC, sel surya perovskite mencapai efisiensi tertinggi yaitu sebesar 1,91%.

---

Perovskite solar cell is a solar cell using organic-inorganic metal halide material as active layer of the solar cell. In 2009, perovskite solar cell is firstly fabricated with efficiency of 3.8% and in 2014 perovskite solar cell has achieved efficiency of 19.3%. Highest efficiency of perovskite solar cell that has been reported is 22.1%. In 4-5 years of development, perovskite solar cell has proved its high potential to become a high efficiency solar cells. Cheap fabrication, good stability and easy fabrication processes make perovskite solar cells very promising to compete with silicon solar cells. One of the fabrication method of perovskite solar cells is by using annealing process. Annealing process is the process of heating the substrate to a certain temperature so that the solvent begins to evaporate.

There have been many studies on perovskite solar cells, but no one has directly discussed the effect of annealing temperature on the structure of perovskite solar cells used on this research. Therefore in this study, annealing temperature variations of 110ºC, 120ºC, and 130ºC will be carried out in the active layer deposition process of perovskite solar cells in order to find the most optimum temperature for the solar cells efficiency. The results of this study state that at 130ºC, perovskite solar cells reach the highest efficiency of 1.91%."

"ABSTRACTSel surya perovskite kini telah mencapai efisiensi senilai 23,3% yang beranjak dari 3,8% hanya dalam jangka waktu beberapa tahun. Material utama yang digunakan pada sel surya perovskite merupakan material dengan struktur perovskite sebagai lapisan aktif dari sel tersebut, seperti contohnya, methylammonium lead halide (CH3NH3PbI3). Material perovskite CH3NH3PbI3 ini menggunakan senyawa inorganik timbal klorida (PbCl2), dimana senyawa tersebut memiliki toksisitas yang tinggi dan dapat menyebabkan gangguan kesehatan, seperti kerusakan sistem saraf, otak, kanker, dan lainnya. Berbagai penelitian telah menunjukkan secara lebih lanjut bagaimana pengaruh timbal klorida terhadap kesehatan. Namun, belum ada penelitian yang secara langsung membahas mengenai bagaimana pengaruh jumlah kandungan PbCl2 terhadap karakteristik elektris sel surya perovskite CH3NH3PbI3. Pada skripsi ini dibahas mengenai pengaruh jumlah kandungan PbCl2 terhadap karakteristik elektris sel surya perovskite CH3NH3PbI3. Pada skripsi ini pula, difabrikasikan tiga sel surya pervoskite dengan lapisan aktif perovskite yang memiliki jumlah kandungan PbCl2 yang berbeda, yaitu 120 mg, 130 mg, dan 140 mg. Dari fabrikasi yang dilakukan, diperoleh hasil bahwa peningkatan jumlah kandungan PbCl2 membuat sel surya CH3NH3PbI3 memiliki karakteristik elektris yang lebih baik. Sel dengan performa terbaik pada penelitian ini adalah sel dengan140 mg PbCl2, dengan nilai Voc = 0,879 V;

---

ABSTRACTIsc =3,3 mA, FF = 0,47 dan η = 0,88%. Perovskite solar cells has reached 23.3% from 3.8% efficiency only in a few years range. The main material that used in perovskite solar cells are materials with perovskite structure as an active layer of those cells, such as methylammonium lead halide (CH3NH3PbI3). CH3NH3PbI3 perovskite contains inorganic compound lead chloride (PbCl2), which has high toxicity that can cause health hazards, such as damage to nervous systems, brain, cancer, etc. Many researches has shown further how the influence of lead chloride on health. However, there are currently no research that directly discusses about the effect of the amount of PbCl2 content on the electrical characteristics of CH3NH3PbI3 perovskite solar cell. This research discusses the effect of the amount of lead chloride on the electrical characteristics of perovskite solar cell. Three perovskite solar cells were fabricated in this research which the active perovskite layer has varying amounts of PbCl2 content, namely 120 mg, 130 mg, and 140 mg. The results of the fabricated cells shows that the increase in the amount of PbCl2 content makes the CH3NH3PbI3 solar cells have better electrical characteristics. Cell with the best performance in this research is the cell with 140 mg amounts of PbCl2 content, with the value Voc = 0,879 V, Isc = 3,3 mA, FF=0,47, and η=0,88%."

"Sel surya merupakan komponen elektronik yang dapat mengkonversi energi cahaya menjadi energi listrik. Perkembangan sel surya sudah sampai pada generasi ketiga, generasi ini terdiri dari dye-sensitized solar cell (DSSC), organic photovoltaic (OPV), quantum dot (QD) photovoltaic, dan perovskite photovoltaic. Sel surya perovskite sendiri telah memberikan peningkatan dalam waktu yang singkat dalam efisiensi konversi energi yaitu dari 3,81% pada tahun 2009 menjadi 25,2% pada tahun 2020. Lapisan penghantar elektron TiO2 merupakan bagian yang sangat diperlukan untuk meningkatkan performa sel surya perovskite. TiO2 merupakan material yang paling banyak digunakan karena porositasnya yang tinggi, kekuatan pengoksidasi yang kuat, tidak beracun dan stabilitas jangka panjang. Aktifitas fotokatalisis TiO2 bergantung pada struktur pori, luas permukaan, ukuran kristal, dan struktur fasa yang dapat dibentuk dengan penerapan suhu kalsinasi. Perbedaan suhu kalsinasi TiO2 dengan prekursor Ti berupa Titanium trichloride akan diteliti pengaruhnya terhadap unjuk kerja dari sel surya perovskite yang dihasilkan, yaitu pada suhu 175℃, 200℃, dan 225. Hasil dari skripsi ini, unjuk kerja sel surya perovskite terbaik adalah sel surya perovskite dengan suhu kalsinasi TiO2 sebesar 175℃ dengan unjuk kerja yang dihasilkan adalah VOC sebesar 2 volt; ISC sebesar 0,98 µA; dan fill factor sebesar 0,838.<

---

Solar cells are electronic components that can convert energy of light directly into electricity. The development of solar cells has reached the third generation, this generation consists of dye-sensitized solar cells (DSSC), organic photovoltaic (OPV), quantum dot (QD) photovoltaic, and perovskite photovoltaic. Perovskite solar cells themselves have provided a short-term increase in energy conversion efficiency from 3% in 2009 to 25.2% in 2020. TiO2 electron-conducting layers are indispensable to improve the performance of perovskite solar cells. This mesoporous material has been extensively studied and widely applied due to its high porosity and large specific surface area. TiO2 is the most widely used material due to its high porosity, strong oxidizing power, non-toxicity and long-term stability. The photocatalytic activity of TiO2 depends on the pore structure, surface area, crystal size, and phase structure that can be formed by applying the calcination temperature. The difference in calcination temperature of TiO2 with Ti precursor in the form of Titanium trichloride will be investigated for its effect on the performance of the resulting perovskite solar cells at temperatures of 175℃, 200℃, and 225℃. The results of this thesis, the best perovskite solar cell performance is a perovskite solar cell with a TiO2 calcination temperature of 175℃ and the resulting performance is a VOC of 2 volts; ISC of 0.98 µA; and fill factor of 0.838."