"ABSTRAKFriction Stir Spot Welding merupakan pengelasan pada solid state welding yangmampu mencegah terjadinya kerusakan pada plat tipis, karena prosesnya tidakmemerlukan temperatur yang tinggi. Two Stage Refilled Friction Stir Spot Welding( TFSSW ) adalah pengelasan tahap kedua yang berfungsi untuk mengisi lubangyang terbentuk pada pengelasan Single Stage FSSW. Penilitan ini mencari pengaruhposisi pengelasan chain straight dan zig zag terhadap kekuatan tekuk dan geserproduk struktur ringan corrugated core sandwich panels pada masing masing jenispengelasan Single Stage FSSW dan Two Stage FSSW. Material yang digunakanyaitu Plat Alumunium AA 1100 dengan ketebalan 0.43 mm. Pengelasanmenggunakan pin diameter 2-4 mm ( pin-shoulder ) pada pengelasan tahappertama, dan pin flat 6 mm pada pengelasan tahap kedua. Diperoleh bahwaPengelasan Two Stage FSSW menghasilkan kekuatan tekuk dan kekuatan geseryang lebih baik dibanding pengelasan Single Stage FSSW. Variasi posisi pengelasanzig zag memiliki kekuatan tekuk yang lebih baik dibanding posisi pengelasan chainstraight. Kekuatan geser pada kedua variasi posisi pengelasan relatif sama.Pengujian tekuk dan pengujian geser menggunakan standar ASTM C393 danASTM C273."

"

Resistance spot welding adalah proses pengelasan lembaran logam dengan paduan pemanasan joule dan tekanan menggunakan elektroda las. Micro resistance spot welding adalah pengelasan spot welding dengan skala micro, yang digunakan untuk proses pengelasan pelat tipis. Pada penelitian ini, fokus utama tertuju pada pencarian pengaruh posisi pengelasan chain straight dan zig zag terhadap kekuatan tekuk dan geser pada produk struktur ringan corrugated core sandwich panels. Produk tersebut menggunakan material Aluminium AA100 dalam bentuk pelat dengan ketebalan 0.43mm. Proses pengelasan mRSW pada penelitian ini menggunakan diameter elektroda truncated core 4mm dan 6mm yang digerakkan oleh pneumatic piston. Lalu dilakukan pengujian destruktif pada produk dengan standar ASTM C393 untuk pengujian tekuk dan ASTM C273 untuk pengujian geser. Pengujian tekuk menunjukkan bahwa pengelasan menggunakan diameter elektroda 6mm dengan posisi pengelasan zig-zag menghasilkan produk struktur ringan corrugated core honeycomb sandwich panels yang paling baik dibandingkan dengan diameter elektroda 4mm dan posisi pengelasan chain-straight sedangkan pada pengujian tarik, hasil diameter 6mm dengan posisi pengelasan zig-zag juga menunjukkan hasil yang lebih baik namun tidak signifikan.

 

---

Resistance spot welding is a sheet material welding process which use the heat generated by the resistance from the current transferred by copper electrodes through the material. Micro resistance spot welding is a micro scaled welding process, mainly used to join thin plates. In this research, the main focus is to find the effects of welding position (chain-straight and zig-zag) to the shear strength and bending strength of the corrugated core honeycomb sandwich lightweight panels. The product consists of AA1100 Aluminum 0.43mm thick plates. The welding process uses the truncated core 4mm and 6mm in diameters copper electrodes powered by pneumatic pistons. The ASTM C273 and ASTM C393 are used for the shear and bending test respectively. The bending tests show that the welding with 6mm electrodes and zig-zag welding position creates the better strength products than it is with 4mm electrodes and chain-straight welding position. Meanwhile, in the shear tests, the 6mm electrode and zig-zag position had a slightly better results.

 

"

"ABSTRAKPengelasan aluminium terutama pada pelat tipis merupakan hal sulit, dikarenakan tidak dapat menahan panas akibat pengelasan. Teknologi friction stir spot welding yang merupakan solid state welding sehingga dapat mengatasi kerusakan, karena tidak memerlukan temperatur yang tinggi. Lalu teknologi ini diaplikasikan pada pembuatan produk struktur ringan longitudinal square honeycomb corrugated core sandwich panels. Pada penelitian ini mencari pengaruh besar diameter pin dan posisi pengelasan lurus dan zig-zag terhadap kekuatan produk struktur ringan ini. Diperoleh bahwa besar diameter pin berbanding lurus dengan kekuatan produk ini dan jika dilakukan uji tekuk, titik lasan merupakan daerah yang lebih lemah dibandingkan daerah bukan titik lasan.

---

ABSTRACTWeld aluminum material especially on thin plate is difficult because it cannot withstand the heat due to welding. Friction stir spot welding which is a solid state welding can overcome this damage because it does not require high temperatures. Then this technology is applied to the manufacture of lightweight structures square longitudinally corrugated honeycomb core sandwich panel product. This study is to determine how the pin diameter and welding position at straight and zig zag position to the strength of the product. Obtained, that diameter of the pin directly proportional to the strength of these product and in bending test, weld spot is an area that is weaker than the other area."

"Teknologi Friction Stir Welding (FSW) sangat cocok untuk diterapkan pada dunia industri untuk menanggulangi kelemahan dari proses pengelasan konvensional. Informasi pengembangan serta aplikasi FSW begitu diminati oleh dunia industri. Pada skripsi ini juga akan menyajikan hasil penelitian terkait teknologi FSW. Skripsi ini menyajikan hasil penelitian pengujian gerakan sumbu prototipe mesin micro Friction Stir Welding (mFSW) dan pengaruh dimensi sel longitudinal square honeycomb corrugated core sandwich panels terhadap kekuatan struktur dan kekuatan las. Struktur ringan longitudinal square honeycomb corrugated core sandwich panels ini terdiri dari 2 bagian utama yaitu face dan core. Penyambungan face dan core struktur ringan ini menggunakan metode micro Friction Stir Spot Welding (mFSSW) dengan tool HSS ; diameter pin 2,5 mm dan diameter shoulder 4 mm. Bahan yang digunakan untuk membuat struktur ringan ini adalah aluminium A1100 dengan ketebalan 0,4 mm. Nilai kekuatan spesimen didapatkan dari pengujian bending dan pengujian geser. Pengujian bending menggunakan 3-point bending standar ASTM C393 dan pengujian geser menggunakan standar ASTM C273. Hasil pengujian prototipe mesin mFSW menunjukkan bahwa performa gerakan sumbu mesin tersebut telah memenuhi spesifikasi yang diinginkan (ketelitian di bawah 100 mikron). Hasil pengujian bending dan geser menerangkan bahwa dimensi sel corrugated core begitu berpengaruh terhadap kekuatan struktur ringan sandwich panels tersebut.

---

Friction Stir Welding ( FSW ) technology is so suitable to be applied in the industrial company to overcome the disadvantages of conventional welding processes. Information as well as the development of FSW applications so attractive. This bachelor thesis will also present the results of research related of FSW technologies. This bachelor thesis presents the testing results of the micro Friction Stir Welding (mFSW) prototype machine axis movement and the effect of cell dimensions longitudinal square honeycomb corrugated core sandwich panels to the structural strength and strength of the welded area. Lightweight structure longitudinal square honeycomb corrugated core sandwich panels consist of two main parts : that is face and core structure. Joining process for face and core using micro Friction Stir Spot Welding (mFSSW) method with the HSS pin diameter 2.5 mm and shoulder diameter 4 mm. The materials used to make lightweight structures are aluminum A1100 with a thickness of 0.4 mm. Ultimate strength values obtained from bending and shear testing. Bending test using 3-point bending ASTM C393 standard and shear strength test using ASTM C273 standard. The test results showed that the prototype machine mFSW axis motion engine performance is good enough. Bending and shear test results explained that the core corrugated cell dimensions so affected the strength of the light structural sandwich panels."

"ABSTRAKTeknologi pengelasan friction stir spot welding FSSW merupakan pengelasan pada solid state welding sehingga dapat mengatasi kerusakan, karena tidak memerlukan temperatur yang tinggi. Two-stage refilled friction stir spot welding TFSSW merupakan pengelasan tahap kedua untuk pengisian lubang yang terbentuk pada pengelasan FSSW. Penelitian ini mencari pengaruh besar diameter pin dan dwell time tahap kedua terhadap kekuatan geser pengelasan. Material yang digunakan yaitu Alumunium Al 1100 dengan ketebalan 0,4 mm dan kecepatan spindle 33.000 rpm. Parameter yang digunakan pada penelitian ini yaitu variasi diameter pin 2 mm, 2.5 mm, dan 3 mm dan variasi dwell time tahap kedua 4 detik, 6 detik, dan 8 detik . Analisis makro dilakukan terhadap hasil pengelasan di setiap variabel.

---

ABSTRACTFriction stir spot welding technology is a solid state welding that can overcome damages caused by high temperatures. Two stage refilled friction stir spot welding TFSSW is a second step to refill keyhole that formed after conventional FSSW process. This study is to analyze the effect of tool diameter and second stage dwell time on TFSSW to the shear strength of welds. Alumunium material Al 1100 with thickness 0,4 mm was used and spindle speed was at 33.000 rpm. Parameters used in this study were the variable of tool diameter 2 mm, 2.5 mm, and 3 mm and variable of second stage dwell time 4 seconds, 6 seconds, and 8 seconds . Analysis of macro structure was studied on variation of welds."

"Friction Stir Welding FSW merupakan teknik yang relatif baru dalam pengelasan logam. FSW menawarkan beberapa keunggulan jika dibandingkan dengan pengelasan konvensional, terutama pada pengelasan aluminium dimana didapatkan kualitas hasil pengelasan yang lebih baik dan juga rendah distorsi. Tujuan dari penelitian ini adalah untuk mengetahui efek dari diameter pahat dan kedalaman tusuk pahat terhadap lebar diameter sambungan dan sifat mekanik hasil lasan pada penyambungan plat tipis aluminium AA1100 dengan menggunakan teknik pengelasan Micro Friction Stir Spot Welding MFSSW. Dalam penelitian ini, digunakan pahat berupa pahat permukaan datar tanpa shoulder-pin berbahan material HSS. Aluminium AA1100 dengan ketebalan 0.42 mm digunakan sebagai benda kerja uji pengelasan. Parameter yang divariasikan dalam penelitian ini adalah lebar diameter pahat 2 mm, 4 mm, dan 6 mm, dan kedalaman tusuk 300 mikron, 400 mikron, dan 500 mikron. Dimana variasi dari parameter-parameter ini akan mempengaruhi sifat mekanik dari lasan sebagai responnya yaitu beban geser. Response Surface Methods RSM digunakan untuk menganalisis pengaruh parameter-parameter tersebut terhadap beban geser dari lasan. Uji makro dilakukan untuk mengetahui profil dan lebar diameter sambungan. Hasil patahan uji geser juga dianalisis untuk mengetahui jenis patahannya, serta hasil uji makro membantu untuk meprediksi patahan. Dari hasil percobaan dan analisis diketahui bahwa diameter pahat dan kedalaman tusuk berbanding lurus terhadap beban puncak atau gaya geser maksimum. Dari hasil uji makro, diketahui bahwa variasi lebar diameter pahat berpengaruh terhadap bentuk atau profil lasan dan juga lebar diameter sambungan, yang mana hal ini berpengaruh terhadap gaya geser maksimum lasan. Sementara itu, kedalaman tusuk pahat berpengaruh terhadap struktur sambungan dimana semakin besar kedalaman tusuknya, strukturnya semakin kuat dan dapat dilihat dari kekuatannya yang lebih besar, serta memiliki cacat retak yang lebih kecil.

---

Technology of Friction Stir Welding FSW is a relatively new technique for joining metal. In some case on Aluminum joining, FSW gives better results compared with the arc welding processes, including the quality of welds and less distortion. The purpose of this study is to analyze the diameter tools effect and insertion depth effect on Micro Friction Stir Spot Welding to the width of joints diameter and the shear load of Welds. In this case, Aluminum AA1100 with thickness of 0.42 mm was used. Tools of HSS material with Flat Surface was used.

The parameter variations used in this study were the diameter of the tools 2 mm, 4 mm, 6 mm, and the variable of plunge depth 300 m, 400 m, and 500 m. Where the variation of these parameters will affect to the mechanical properties of welds as response was the shear load. Response Surface Methods RSM was used to analyze MFSSW parameters with the shear load of welds. The fracture of the shear test results was also analyzed to determine the type of fracture, as well as the macro test to predict the fracture. Macro test also used to know the width of joint diameter.

From the result of experiment and analysis, it is shown that the width of the tools diameter and the plunge depth is directly proportional to the load of the shear test results. From macro test, it is known that the variation of tools diameter affecting on profile and width diameter of joint. Meanwhile, the insertion depth affecting on the strength of joints. "

"Friction-stir welding (FSW) is a solid-state joining process primarily used on aluminum, and is also widely used for joining dissimilar metals such as aluminum, magnesium, copper and ferrous alloys. Recently, a friction-stir processing (FSP) technique based on FSW has been used for microstructural modifications, the homogenized and refined microstructure along with the reduced porosity resulting in improved mechanical properties. Advances in friction-stir welding and processing deals with the processes involved in different metals and polymers, including their microstructural and mechanical properties, wear and corrosion behavior, heat flow, and simulation. The book is structured into ten chapters, covering applications of the technology, tool and welding design, material and heat flow, microstructural evolution, mechanical properties, corrosion behavior and wear properties. Later chapters cover mechanical alloying and FSP as a welding and casting repair technique; optimization and simulation of artificial neural networks; and FSW and FSP of polymers."

"Micro Friction Stir Spot Welding (m-FSSW) merupakan salah satu jenis solid state welding dengan menggunakan non-consumable tool ber-skala micro dengan ketebalan material <1 mm serta memanfaatkan gesekan dan axial force dalam prosesnya. Hasil dair pengelasan yaitu lap-joint pada satu titik. Pada penelitian ini dilakukan pengujian Geometri tool terhadap hasil pengelasan, sehingga didapatkan korelasi antara geometri tool, temperature, perubahan kecepatan putar, axial force, hasil uji tarik geser, dan uji micro dan macro. Pada eksperimen ini menggunakan 4 jenis tool yaitu, tool 1 (One stage shoulder 450), tool 2 (one stage shoulder 650), tool 3 (small taper), tool 4 (medium taper). Standar pengujian yang digunakan adalah ISO 14273 (Uji Tarik Geser) , ASTM E340 (Makrostruktur) , ASTM E407 (Mikrostruktur).  Pada eksperimen ini hasil uji tarik geser tertinggi yaitu 600,480 N dengan dwell time 4 detik dengan temperatur sekitar 321.5 ˚C terdapat pada tool 4 (Medium Taper). Pada hasil uji struktur makro dan mikro (crossection) terdapat daerah Stir Zone (SZ), Thermo-Mechanically Affected Zone (TMAZ), Heat Affected Zone (HAZ), Parent Metal (PM), Hook dan EXTD zone (pada tool 3 dan tool 4). Pada daerah SZ, terjadi rekristalisasi secara penuh (>220°C) sedangkan daerah TMAZ yang mengalami rekristalisasi sebagian akibat adanya panas dan mengalami perubahan sifat mekanik (120°C-250°C). dan untuk daerah HAZ atau daerah yang terpengaruhi panas namun tidak mengalami rekristalisasi (<220°C).  Pada pengujian Microstructure (crossection) menunjukkan Intermetallic Compound serta cacat yang ada dalam skala mikro dari sambungan pelat tipis AA1100 dan pelat tipis CuZn. Pada ekperimen ini terdapat pengaruh pada variasi dwell time terhadap geometry tool sehingga mempengaruhi distribusi temperatur, kecepatan putar, dan axial force yang mengakibatkan hasil kekuatan uji tarik geser meningkat dari dwell time 2s ke 4s, sedangkan mengalami penurunan pada dwell time 6s.

---

Micro Friction Stir Spot Welding (m-FSSW) is a type of solid state welding using non-consumable micro-scale tools with a material thickness of <1 mm and utilizing friction and axial force in the process. The result of welding is a lap-joint at one point. In this research, tool geometry was tested on welding results, so that a correlation was obtained between tool geometry, temperature, changes in rotational speed, axial force, shear tensile test results, and micro and macro tests. In this experiment, 4 types of tools were used, namely, tool 1 (One stage shoulder 450), tool 2 (one stage shoulder 650), tool 3 (small taper), tool 4 (medium taper). The test standards used are ISO 14273 (Tensile Shear Test), ASTM E340 (Macrostructure), ASTM E407 (Microstructure). In this experiment, the highest shear tensile test result is 600,480 N with a dwell time of 4 seconds with a temperature of around 321.5 ˚C, was found on tool 4 (Medium Taper). In the macro and micro structure test results (crossection) there are Stir Zone (SZ), Thermo-Mechanically Affected Zone (TMAZ), Heat Affected Zone (HAZ), Parent Metal (PM), Hook and EXTD zones (on tool 3 and tool 4). In the SZ area, full recrystallization occurs (>220°C) while the TMAZ area experiences partial recrystallization due to heat and experiences changes in mechanical properties (120°C-250°C). and for HAZ areas or areas that are affected by heat but do not experience recrystallization (<220°C). The Microstructure (crossection) test shows the Intermetallic Compound and defects that exist on a micro scale from the joints of the AA1100 plate and the CuZn plate. In this experiment, there was an influence on variations in dwell time on the tool geometry, thus affecting the temperature distribution, rotational speed and axial force, which resulted in the shear tensile test strength results increasing from a dwell time of 2s to 4s, whereas it decreased at a dwell time of 6s."

"Micro Friction Stir Spot Welding (m-FSSW) merupakan salah satu jenis solid state welding dengan menggunakan non-consumable tool ber-skala mico thicknes material<1 mm) dan memanfaatkan gesekan serta axial force pada prosesnya. Hasil pengelasan yaitu lap-joint pada satu titik. Pada penelitian ini dilakukan pengujian Geometril tool terhadap hasil pengelasan, sehingga didapartkan korelasi antara geometri tool, temperature ,perubahan kecepaatn putar, hasil uji tarik geser dan uji hardness . Dimana semakin tinggi pin maka semakin tinggi RPM,temperature dan uji tarik (berbanding lurus) dimana ketinggian pin < plunge dept (600 µm). Namun Pada tool 4 geometri tool memiliki ketinggian pin 650 µm dan diameter 2.540 mm, sehingga membuat RPM masih di putaran tinggi ,temperatur pada suhu yang rendah dan hasil uji tarik yang belum maksimal (penetrasi hanya dilakukan di pin/Shoulder tidak menyentuk spesimen uji). Pada eksperimen ini peak temperatur tertinggi berada pada tool 3 (shoulder 450) dengan temperature 428.44˚C dengan hasil uji tarik geser yaitu 449.66 N (tertinggi). Pada pengujian tarik geser terdapat mode kegagalan diamati selama TS tes, yaitu mode PF (Pulled Out Nugget) pada seluruh hasil lasan dengan menggunakan tool 1 hingga tool 4. Hasil kekerasan pada geometri tool diketahui bahwa semakin tinggi pin maka hardnes akan semakin besar atau selaras dengan temperature yang terjadi. Namun saat temperatur berada pada suhu 400°C , material AA100 mengalami fully aneling sehingga berdampak pada penurunan hardness pada material hasil lasan (Jaehyung Cho ,2010). Pada hasil uji struktur makro (crossection) terdapat daerah Stir Zone (SZ), Thermo-Mechanically Affected Zone (TMAZ), Heat Affected Zone (HAZ),ParentMetal (PM), Hook dan EXTD zone (pada tool 1,2,3).Dimana daerah SZ (stir zone), terjadi rekristalisasi secara penuh (>350°C) sedangkan daerah TMAZ yang mengalami rekristalisasi sebagian akibat adanya panas dan mengalami perubahan sifat mekanik (250°C-350°C). dan untuk daerah HAZ atau daerah yang terpengaruhi panas namun

---

Micro Friction Stir Spot Welding (m-FSSW) is a type of solid-state welding using a non-consumable tool with a mico scale (materialthickness < 1mm), using friction and axial force in the process. The result of welding is a lap joint at one point. This study has a correlation between tool geometry, temperature, rotational speed, tensile shear test, and hardness (Vickers) test. Where the higher the pin have higher the RPM, temperature, and tensile shear test (directly proportional) where the pin height < plunge depth (600 m). However, in tool 4 the geometry of the tool has a pin height of 650 m and a diameter of 2.54 mm so that the RPM is still at high rotation, the temperature is at a low temperature and the tensile shear results are not maximized (penetration is only at the pin/shoulder not touching the specimen). In this experiment, the highest peak temperature at tool 3 (shoulder 450) is about 428.44˚C with the results of the shear tensile test being 449.66 N (the highest). In the tensile shear test, get a failure mode, there is PF (Pulled Out Nugget) on all weld results (tools 1 to tool 4). The results of the hardness on the geometry of the tool are known that the higher pin, get the high hardness or proportional with the temperature that occurs. However, when the temperature is was at 400 °C, this material (AA100) had fully annealed and had an impact on decreasing the hardness of the welded material (Jaehyung Cho, 2010). In the macrostructure test results, there are Stir Zone (SZ), Thermo-Mechanically Affected Zone (TMAZ), Heat Affected Zone (HAZ), ParentMetal (PM), Hook, and EXTD zone (on tool 1,2,3). The SZ region (stir zone), where full recrystallization occurs (>350 °C) while the TMAZ region partially recrystallizes due to heat and changes in mechanical properties (250 °C-350 °C). and for the HAZ region or heat-affected region but not recrystallized (<250 °C)."

"Kebutuhan material dengan sifat mekanik yang baik serta berbobot ringan sudah semakin tinggi saat ini, terutama untuk aplikasi yang memerlukan performa tinggi. Komposit aluminium berpenguat Al2O3 (AMC) menawarkan keunggulan tersebut. Pada penelitian ini, fabrikasi komposit dilakukan menggunakan paduan aluminium 6061 dan penguat serbuk Al2O3 berukuran 60 μm. melalui proses stir casting. Dalam penelitian ini diketahui pengaruh penambahan kadar Al2O3 serta Mg sebagai agen pembasahan terhadap sifat mekanik komposit. Variasi kadar Al2O3 yang ditambahkan sebesar 10% dan 15% fraksi volume serta kadar Mg 8%, 10%, dan 15%. Hasil penelitian menunjukan bahwa kekuatan tarik optimal sebesar 170 Mpa diperolah pada komposit dengan kadar Al2O3 10% dan Mg 10%. Di mana kekerasan dan ketahanan aus komposit meningkat seiring penambahan kadar Al2O3 dan Mg. Demikian halnya porositas meningkat ketikat kadar Al2O3 yang ditambahkan semakin besar.

---

Demand of materials with good mechanical properties and have lightweight increased in recent years especially for high performance applications. Aluminium reinforced Al2O3 composite (AMC) provide this superiority. In this research, composite was fabricated from Aluminium Alloy 6061 and 60 μm Al2O3 reinforce particles by stir casting process. This research investigated the effect of addition Al2O3 content and Mg as wetting agent to mechanical properties of composite. The addition of Al2O3 into Al melt was 10% and 15% of volume fraction and Mg was 8%, 10%, and 15%. The result showed that the optimum tensile strength of 202 Mpa was obtained in composite with 10% volume fraction of Al2O3 and 10% Mg. Moreover, hardness and wear resistant of composite increased with the addition of Al2O3 and Mg content. Porosity also increased when greater amount of Al2O3 content was added."