Irena Khatrin
"Zeolit NaY berbasis mineral alam berhasil disintesis dari zeolit alam Bayat Klaten dan kaolin Bangka sebagai sumber alumina dan silikanya. Zeolit NaY disintesis setelah material sintesisnya: zeolit alam Bayat Klaten dan kaolin Bangka di pretreatment terlebih dahulu dengan perlakuan : aktivasi, purifikasi, fragmentasi untuk zeolit alam Bayat, dan ekstraksi silika dari kaolin Bangka. Kemudian zeolit NaY disintesis menggunakan material hasil pretreatment menggunakan teknik seeding dan metode hidrotermal dengan rasio molar dan variasi waktu kristalisasi satu hari dan dua hari. Berdasarkan pola XRD diperoleh zeolit NaY berbasis bahan alam yang menunjukkan puncak khas zeolit NaY pada 2θ = 6,3o ; 15,6o ; dan 24,9o dengan rasio Si/Al sebesar 4,1. Kemudian zeolit NaY berbasis bahan alam dimodifikasi menjadi bentuk H+ menggunakan metode pertukaran kation untuk memperbanyak situs asam dan meningkatkan kemampuan katalitiknya sebagai katalis perengkahan n-heksadekana. Zeolit HY hasil modifikasi zeolit NaY kemudian diaplikasikan sebagai katalis perengkahan n-heksadekana. Dengan hasil konversi, yield, dan selektivitas produk gasolin berturut-turut sebesar 59,80%, 59,80%, dan 98,53%. Berdasarkan hasil ini, dapat disimpulkan bahwa zeolit HY berbasis mineral alam memiliki kemampuan selektivitas yang hampir serupa dan dapat dibandingkan dengan zeolit HY sintetik.

NaY zeolite based on natural minerals was successfully synthesized from Klaten Bayat natural zeolite and Bangka kaolin as a source of alumina and silica. NaY zeolite is synthesized after its synthesis material: Klaten's natural Baye zeolite and Bangka kaolin are pretreated with treatment: activation, purification, fragmentation for Bayat natural zeolite, and silica extraction from Bangka kaolin. Then NaY zeolite was synthesized using pretreatment material using seeding technique and hydrothermal method with molar ratio and variation of crystallization time of one day and two days. Based on the XRD pattern obtained by natural NaY zeolite which shows the typical peak of NaY zeolite at 2θ = 6.3o; 15.6o; and 24.9 o with a Si / Al ratio of 4.1. Then zeolite NaY based on natural ingredients was modified to form H + using cation exchange method to increase the acidic site and increase its catalytic ability as a catalyst for n-hexadecane cracking. Zeolite HY modified from zYolite NaY was then applied as a catalyst for n-hexadecane cracking. With the results of conversion, yield, and selectivity of gasoline products respectively 59.80%, 59.80%, and 98.53%. Based on these results, it can be concluded that natural mineral-based HY zeolites have almost similar selectivity and can be compared with synthetic HY zeolites."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2019
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Galih Senja Adetya Melaningtyas
"Sintesis zeolit NaY dari zeolit alam Bayat dilakukan melalui proses aktivasi, purifikasi, dealuminasi dan fragmentasi. Aktivasi dan purifikasi bertujuan untuk menghilangkan pengotor-pengotor pada zeolit. Proses dealuminasi dilakukan untuk mengurangi alumina yang terdapat di dalam struktur zeolit. Fragmentasi dilakukan berdasarkan metode Submolten Salt System dengan perbandingan zeolit alam Bayat dan NaOH adalah 2:1. Zeolit alam Bayat digunakan sebagai sumber silika dan alumina dengan NaAlO2 sebagai sumber alumina tambahan. Penelitian ini menggunakan zeolit alam Bayat karena harganya yang lebih terjangkau dan lebih ramah lingkungan dibandingkan dengan bahan sintetik. Sintesis zeolit NaY dilakukan dengan metode hidrotermal dan teknik seeding dengan komposisi seed gel 5 of Al : 6,25 Na2O: Al2O3 : 10 SiO2 : 180 H2O rasio molar dengan variasi pH 11, 12 dan 13. Didapatkan luas permukaan masing-masing zeolit sebesar 100,1744 m2/g, 142,8409 m2/g dan 22,4591 m2/g dengan ukuran pori masing ndash;masing sebesar 5,2 nm; 5,2 nm dan 35,5 nm. Hal ini didukung dengan data pola difraksi pada XRD yang menunjukan adanya kemiripan dengan pola XRD zeolit NaY sintetis dan juga data FTIR yang menunjukan adanya puncak penyusun unit pembangun sekunder puncak double 4 dan 6 ring khas faujasit pada bilangan gelombang 600-500 cm-1. Tahap selanjutnya adalah memodifikasi zeolit NaY yang telah disintesis menjadi zeolit HY dengan metode tukar kation untuk meningkatkan kadar keasaman dan kestabilannya sehingga dapat digunakan sebagai katalis perengkahan n-heksadekana. Hasil reaksi perengkahan menunjukan bahwa zeolit HY pH 12 memiliki nilai konversi dan yield gasolin paling tinggi dibandingkan dengan zeolit HY pH 11 dan HY pH 13 yaitu sebesar 25,945 . Bila ditinjau berdasarkan bahan baku pembuatannya, HY yang dimodifikasi dari zeolit alam Bayat memiliki kemampuan konversi, yield dan selektivitas terhadap gasolin yang lebih rendah jika dibandingkan dengan HY kaolin dan HY dari bahan sintetis.

Synthesis of NaY zeolite from Bayat Natural Zeolite was prepared through activation, purification, dealumination and fragmentation process. The activation and purification process are to remove some impurities. Dealumination process is done to leach some alumina from zeolite structures. Fragmentation process refers to Submolten Salt System methods with the ratio of Bayat natural zeolite and NaOH is 2 1. Bayat natural zeolite is used as silica and alumina sources with NaAlO2 as an additional source of alumina. This research uses Bayat natural zeolite because the price is more affordable and more environmentally friendly compared with synthetic materials. The NaY zeolite was synthesized with hydrothermal methods and seeding technique with the composition of seed gel 5 of Al 6.25 Na2O Al2O3 10 SiO2 180 H2O molar ratio with pH variation of 11, 12 and 13. The respective surface area of NaY zeolite pH 11, 12 and 13 as synthesized was 100,1744 m2 g, 142,8409 m2 g dan 22,4591 m2 g with the pore size of 5,25 nm 5,25 nm and 35,5 nm. This is supported by XRD diffraction pattern data which shows similarity with XRD pattern of synthetic NaY zeolite as well as FTIR data showing the peak of the construction of the secondary peak builder unit of 4 and 6 distinct faujasite rings in the wave number 600 500 cm 1. The next step is to modify the NaY zeolite that has been synthesized into HY zeolite by cation exchange method to increase the acidity level so that it can be used as a n hexadecane cracking catalyst. The next step is to modify the NaY zolite as synthesized into HY zeolite by cation exchange method to increase the acidity level so it can be used as cracking catalyst of n hexadecane. The result of the cracking reaction indicates that the HY zeolite pH 12 has the highest conversion value and highest yield of gasoline compared with the HY zeolite pH 11 and HY pH 13 which is 25,945 . Then reviewed on the basis of the raw material of manufacture, modified HY of the Bayat natural zeolite has a lower conversion ability, yield and selectivity to gasoline compared with HY kaolin and HY of synthetic materials."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Sabrina Ayu Paramadini
"Sintesis ZSM-5 mikropori dan hirarki telah dilakukan dengan menggunakan zeolit ??alam Bayat sebagai sumber silika dan alumina. Pada zeolit ??alam dilakukan proses aktivasi, purifikasi, dealuminasi, dan fragmentasi terlebih dahulu untuk menghilangkan pengotor yang terdapat dalam zeolit alam. Sintesis ZSM-5 dilakukan dengan menggunakan metode single template dengan menambahkan TPAOH tetrapropilamonium hidroksida merupakan substrat organik sebagai pengarah struktur mikropori. Selanjutnya, sintesis ZSM-5 hirarki menggunakan metode double templated dengan penambahan TPAOH dan PDDAM poli akrilamida-co-diallyldimethylammonium chloride sebagai pengarah struktur mesopori. Zeolit ??yang disintesis kemudian dikarakterisasi dengan berbagai metode seperti FTIR, XRD, SEM-EDX dan BET. Hasil karakterisasi XRD menunjukan bahwa ZSM-5 hasil sintesis memiliki puncak khas 2? 7-10? dan 22-25?. Hasil analisa SEM menunjukan ZSM-5 hasil sintesis berbentuk heksagonal yang merupakan ciri khas kristal ZSM-5. Rasio mol Si/Al hasil sintesis ZSM-5 mikropori dan ZSM-5 hirarki berturut-turut adalah 32,34 dan 43,53. Hasil analisa BET menunjukan ZSM-5 mikropori memiliki rerata diameter pori sebesar 2,0213 nm dan ZSM-5 hirarki memilki rerata diameter pori sebesar 2,3837. Kemudian, hasil sintesis ZSM-5 dimodifikasi menjadi H/ZSM-5 untuk menghasilkan zeolit yang lebih stabil dalam lingkungan termal atau hidrotermal. H/ZSM-5 mikropori dan hirarki diuji aktivitasnya sebagai katalis dalam reaksi perengkahan senyawa n-heksadekana sebagai senyawa model. H/ZSM-5 hirarki memiliki konversi yang paling tinggi yaitu sebesar 84,73 serta memiliki persentase yield dan selektivitas produk gasolin paling tinggi berturut-turut yaitu sebesar 83,13 dan 98,11.

Synthesis of miroporous and hierarhical ZSM 5 has been carried out using Bayat natural zeolite as silica and alumina source. Prior being used as material for synthesis, natural zeolite was subjected to the process of activation, purification, dealumination, and fragmentation to remove impurities contained in natural zeolite. The synthesis of microporous ZSM 5 was performed using a single template method by adding TPAOH tetrapropylammonium hydroxide as an organic substrate as micropore structure directing agent. Furthermore, the synthesis of hierarchical ZSM 5 uses a double template method with the addition of TPAOH and PDDAM poly acrylamide co diallyldimethylammonium chloride as mesoporous structure directing agent. The synthesized zeolite were then characterized by various methods such as FTIR, XRD, SEM EDX and BET. The XRD characterization results show that the synthesized ZSM 5 had typical peaks of 2 7 10 and 22 25 . SEM analysis results showed ZSM 5 synthesized had hexagonal shaped which is characteristic of ZSM 5 crystals. The molar ratio of Si Al of synthesized ZSM 5 micropore and ZSM 5 hierarchies were 32.34 and 43.53, respectively. The result of BET analysis showed that ZSM 5 micropore has pore diameter mean was 2.0213 nm and ZSM 5 hierarchy has pore diameter mean was 2,3837. Then, the ZSM 5 synthesis results were modified to H ZSM 5 to increase the stability zeolite in thermal or hydrothermal environments. Microporous and hierarchical H ZSM 5 were then used as a catalytic cracking reaction catalyst using n hexadecane as a model compound. Hierarchical H ZSM 5 had the highest conversion that is equal to 84.73 and has the highest percentage of yield and selectivity of gasoline product which is 83.13 and 98.11 , respectively."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
S-Pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Tunas Alam
"ABSTRAK
Telah dilakukan studi sintesis dan karakteristik zeolit HY dengan pori hirarki menggunakan metode template dan non template sebagai katalis untuk reaksi perengkahan n-heksadekana. Hasil karakterisasi XRD menunjukkan zeolit NaY hirarki dengan metode template dan non template memiliki puncak khas pada 2 teta 6?, 10? dan 11? yang merupakan puncak karakteristik untuk zeolit NaY, walaupun untuk NaY hirarki dengan template memiliki sedikit pengotor yaitu zeolit NaP. Adsorpsi dengan nitrogen menunjukkan bahwa NaY hirarki dengan template dan non template memilki hysterical loop pada P/Po 0,7 ndash; 0,9 yang mengindikasikan adanya pori hirarki pada kedua zeolit tersebut dan hasil pengukuran BET menghasilkan luas permukaan 393,496 m2/g dan 528,82 m2/g untuk NaY hirarki dengan template dan NaY hirarki tanpa template secara berturut-turut. Zeolit NaY hirarki kemudian dimodifikasi dengan metode tukar kation sehingga menghasilkan HY berpori hirarki dan hasil karakterisasi dengan IR-DRS menunjukkan adanya penambahan keasaman pada kedua zeolit HY berpori hirarki. Uji keasaman dengan adsorpsi menggunakan ammonia yang menunjukkan adanya puncak pada bilangan gelombang 1458 cm-1 dan 1443 cm-1 untuk HY hirarki template dan HY hirarki non template dimana bilangan gelombang tersebut merupakan vibrasi NH3 bebas yang teradsorpsi. Zeolit HY berpori hirarki kemudian digunakan sebagai katalis reaksi perengkahan katalitik menggunakan n-heksadekana sebagai senyawa model dan hasil reaksi perengkahan menunjukkan zeolit HY berpori hirarki memiliki selektivitas yang tinggi untuk menghasilkan fraksi gasolin dengan selektivitas sebesar 30 dan 23 dibandingkan dengan zeolit HY mikropori yang memiliki selektivitas sebesar 25 .

ABSTRACT
The synthesis and characteristic of HY zeolit with pore hierarchy using template and non template method had been done as cracking catalyst on n hexadecane. The XRD pattern showed both the hierarchical NaY zeolit with the template and non template methods had a characteristic peak at 2 teta 6 , 10 and 11 which are the characteristic peaks for NaY zeolits although for the hierarchical NaY the template has slightly impurities NaP zeolit. Adsorption with nitrogen showed that the hierarchical NaY with templates and non templates exhibited hysterical loop on P Po 0.7 0.9 which indicated a hierarchical pore on both zeolits and BET measurements results for NaY hierarchy with template and NaY hierarchy non template has surface area 393.496 m2 g and 528.82 m2 g for NaY hierarchy with template and NaY hierarchy non template, respectively. Zeolit NaY hierarchy was then modified by cation exchange method to form hierarchical HY and characterization results with IR DRS showed the addition of acidity in both zeolit after adsorption using ammonia, which are indicated peak at 1458 cm 1 and 1443 cm 1 for hierarchical HY with template and a non template which the wave numbers for NH3 vibrations. Hierarchical HY zeolits were then used as a catalytic cracking reaction catalyst using n hexadecane as a model compound and the cracking reaction result shows a porous HY porous zeolit having high selectivity to produce a gasolin fraction with selectivity of 30 and 23 compared to a micropore HY zeolit that having selectivity by 25 ."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
T48261
UI - Tesis Membership  Universitas Indonesia Library
cover
Indah Revita Saragi
"ABSTRAK
Sintesis Zeolit NaY menggunakan sumber alam alumina dan silika memiliki banyak
tantangan. Berfokus pada pengurangan bahan sintetis, dalam penelitian ini, sintesis telah
dilakukan menggunakan kaolin alam Bangka Belitung sebagai sumber silika dan
alumina. Pre-treatment pada kaolin diperlukan melalui proses aktivasi, pemurnian, dan
kalsinasi. Selanjutnya, zeolit NaY juga disintesis menggunakan kaolin alami sebagai
sumber silika dan alumina dengan beberapa jenis benih yang dibuat dari sumber silika
yang berbeda, yaitu Ludox HS40, Na-silikat, dan NaY komersil dari Wako. Semua
material kemudian dikarakterisasi menggunakan XRD, FTIR, dan SEM-EDX. Dapat
dilihat bahwa seed dari Ludox HS40 memberikan NaY terbaik. Tapi, zeolite NaP
menjadi pengotor utama. Rasio Si/Al NaY zeolit adalah ~1.78 dengan bentuk pola
difraksi mirip dengan yang ada dalam literatur. Sehingga disimpulkan, sintesis NaY
menggunakan aluminasilika alam sebagai sumber silika dan alumina cukup berhasil.
Hasil uji perengkahan memperlihatkan jika katalis dengan material sintetik (HY
sintetik) memiliki persen konversi, yield dan selektivitas yang lebih tinggi dibandingkan
dengan katalis dengan campuran bahan alam (HY MKSE dan HY SE). Namun, setiap
katalis memiliki persen yield dan selektivitas lebih tinggi terhadap produk C5
dibandingkan dengan produk lainnya.

ABSTRACT
Synthesis of sodium Y zeolite (NaY Zeolite) using natural sources of alumina and silica
is interesting yet challenging. Focused on reducing synthetic material, in this research,
synthesis has been carried out using Bangka natural Kaolin as silica and alumina
sources. Pretreatment on kaolin was needed through the process of activation,
purification, and calcination. The purpose of activation process is to remove the polar
impurities, free oxides in the surface that cover up the pores, and release the water that
trapped in the pores of the materials. The purification was conducted using Na-acetate
buffer solution with ratio 1:3 (w/v). The calcination process was required because Si-O
and Al-O structures in Kaolin are inactive and inert. Synthesis of NaY zeolite was
conducted with the addition seed gel using hydrothermal method with 24 hours at the
temperature 100 oC for crystallization. Furthermore, NaY zeolites were also synthesized
using natural kaolin as silica and alumina sources with several types of seeds made from
different silica sources, i.e Ludox HS40, Na-silicate, and NaY zeolite from Wako . All
materials then were characterized using XRD, FTIR, and SEM-EDX. It can be seen that
seed from Ludox HS40 gives the best NaY. But, NaP zeolite becomes the main
impurities. The Si/Al ratio of NaY zeolite is ~1.78 but the shape of the crystals is
similar to that in literature. To conclude, synthesis of NaY using natural
aluminasilicates as source is considerably successful. The cracking test results show if
the catalyst with synthetic material (HY synthetic) has a higher percent conversion,
yield and selectivity compared to a catalyst with a mixture of natural materials (HY
MKSE and HY SE). However, each catalyst has a higher percent yield and selectivity
for C5 products compared to other products."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2018
T51691
UI - Tesis Membership  Universitas Indonesia Library
cover
Zahara
"Sintesis ZSM-5 berpori hirarki telah dilakukan dengan metode double template untuk meningkatkan aktivitas dan selektivitas katalitik material tersebut. Dalam proses sintesis ini, dilakukan variasi template pertama yang digunakan, yaitu TPAOH (ZSM-5h), etilendiamin (ZSM-5h_en) dan trietilen tetramin (ZSM-5h_teta). Semua sampel hasil sintesis dikarakterisasi menggunakan instrumen XRD, BET SAA, SEM, EDS dan XRF.
Hasil karakterisasi XRD menunjukkan bahwa pola difraksi sinar X ZSM-5 menunjukkan puncak yang kuat pada 2 theta 7-9 dan 22-25 yang merupakan puncak khas zeolit ZSM-5. Sedangkan pada ZSM-5h_en dan ZSM-5h_teta intensitas puncak-puncak tersebut sangat lemah yang menunjukkan bahwa zeolit ZSM-5 tidak terbentuk dengan baik.
Hasil karakterisasi dengan BET Surface Area Analyzer menunjukkan bahwa ZSM-5 hasil sintesis memiliki ukuran pori > 2 nm dan terlihat adanya hysterical loop pada pola isoterm adsorpsi desorpsi yang dihasilkan. Hal ini menunjukkan bahwa telah terbentuk mesoporositas pada material hasil sintesis. Zeolit ZSM-5 selanjutnya dimodifikasi menjadi H/ZSM-5 dengan metode tukar ion kemudian dipanaskan pada suhu 550?C. H/ZSM-5 yang dihasilkan dikarakterisasi dengan FTIR dan EDS untuk mengetahui karakter keasaman yang dihasilkan kemudian diuji coba pada reaksi perengkahan katalitik senyawa n-heksadekana.
Sebagai pembanding, dilakukan pula sintesis ZSM-5 mikropori (ZSM-5m) dan diuji aktivitas katalitiknya agar diketahui pengaruh ukuran pori terhadap hasil reaksi perengkahan katalitik. Hasil yang diperoleh menunjukkan bahwa katalis H/ZSM-5h menghasilkan persen konversi yang tinggi, yaitu sebesar 37,25% dengan persen massa yield gasolin dan selektivitas gasolin berturut-turut sebesar 17,28% dan 46,38%.

Attempt to synthesize hierarchical ZSM 5 zeolites (ZSM-5h) through double template method has been hydrothermally carried out. In order to develop the structure of microporous ZSM 5, three different templates was used TPAOH, ethylene diamine (en), or triethylene tetramine teta, followed by dimethyl dialyl ammonium chloride acrylamide copolymer as mesopore directing agent. All samples were characterized using XRD, BET Surface Area Analyzer, SEM, EDS and XRF.
XRD pattern of ZSM 5h zeolite showed specific peaks at position 2 theta of 7-9 and 22-25 that were characteristic of ZSM-5 zeolite. Otherwise, in the XRD pattern of ZSM-5h en and ZSM-5h teta zeolites the peaks were very weak, indicating that ZSM 5 zeolites were not well formed. Nitrogen adsorption of ZSM-5h exhibited hysterical loop at P Po 0.7 ndash 0.9 indicating the presence of hierarchical mesoporous in this sample.
SEM images of ZSM-5h zeolite showed hexagonal shape that was characteristic of ZSM-5 zeolite. Afterward, H/ZSM-5h zeolite was prepared through ion exchange treatment using 1 M ammonium nitrate solution, followed by calcination at 550 oC to remove all ammonia and produce H/ZSM-5h. This sample was characterized using FTIR and EDS to observe its acidity. Then, preliminary test on H/ZSM-5h zeolite as catalyst in cracking of n hexadecane will be discussed.
As comparison, microporous ZSM-5 zeolite ZSM 5m was synthesized and tested under the same conditions to study the effect of different pore size on its activity in catalytic cracking of n-hexadecane. The result show that conversion percent of catalytic reaction using H/ZSM-5h was 37,25 (%wt), which was higher than H/ZSM-5m. Percent of yield and selectivity of gasoline product using this material were 17,28 and 46,38 (%wt) respectively
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
T48811
UI - Tesis Membership  Universitas Indonesia Library
cover
Nur Amalina Qismina Fajrianti
"ABSTRACT
Sintesis zeolit NaY dari zeolit alam Bayat dilakukan melalui metode hidrotermal dengan teknik seeding. Sintesis dilakukan berdasarkan komposisi Al2O3: 10 SiO2: 10,3 Na2O: 180,3 H2O rasio molar . Sebelum dilakukan sintesis, zeolit alam Bayat dipreparasi melalui proses purifikasi dan depolimerisasi. Hasil XRD menunjukkan bahwa zeolit yang dihasilkan merupakan zeolit NaY yang didominasi oleh kerangka sodalite. Hasil SEM-EDX memperlihatkan morfologi zeolit NaY seperti tumpang tindih dengan rasio Si/Al sebesar 2,30. Berdasarkan penelitian, zeolit NaY hasil sintesis memiliki sisi aktif yang besar sehingga dapat berperan menjadi adsorben ion logam kadmium II dan kobalt II . Hal ini dibuktikan dengan kapasitas adsorpsi ion kadmium II rata-rata zeolit NaY hasil sintesis lebih tinggi daripada kapasitas rata-rata adsorpsi dari zeolit alam Bayat raw pada waktu optimum 120 menit, 33,46 mek/100 g untuk zeolit alam Bayat raw dan 105,60 mek/100 g untuk zeolit NaY hasil sintesis. Kapasitas adsorpsi ion kobalt II rata-rata zeolit NaY hasil sintesis juga lebih tinggi daripada kapasitas rata-rata adsorpsi dari zeolit alam Bayat raw pada waktu optimum 120 menit, 12,88 mek/100 g untuk zeolit alam Bayat raw dan 78,25 mek/100 g untuk zeolit NaY hasil sintesis. Nilai kapasitas tukar kation zeolit alam Bayat raw adalah sebesar 24,41 mek/100 gram zeolit, sedangkan nilai kapasitas tukar kation zeolit NaY hasil sintesis adalah sebesar 43,45 mek/100 gram zeolit.

ABSTRACT
NaY zeolite was hydrothermally synthesized using seeding technique. The synthesis were performed according to the following composition of Al2O3 10 SiO2 10.3 Na2O 180.3 H2O molar ratio . XRD pattern confirmed that the structure was NaY zeolite. Before synthesis, natural zeolite Bayat were prepared through purification and depolymerization. From XRD measurement, it is observed that zeolite structures are dominated by sodalite framework. SEM EDX showed that NaY crystals were intergrowth with Si Al ratio of 2.30. In this study, NaY zeolite synthesized has more active sites to adsorb cadmium II and cobalt II ions because the average adsorption capacity cadmium II ions of as synthesized NaY zeolite is higher than the average adsorption capacity of raw Bayat natural zeolite at its optimum contact time 120 minutes, 33.46 meq 100 g for raw natural zeolite Bayat and 105.60 meq 100 g for as synthesized NaY zeolite. The average adsorption capacity cobalt II ions of as synthesized NaY zeolite is also higher than the average adsorption capacity of raw Bayat natural zeolite at its optimum contact time 120 minutes, 12.88 meq 100 g for raw natural zeolite Bayat and 78.25 meq 100 g for as synthesized NaY zeolite. The cation exchange capacity of raw Bayat natural zeolite is 24.41 meq 100 gram zeolite, besides the cation exchange capacity of as synthesized NaY zeolite is 43.45 meq 100 gram zeolite. "
2016
S66142
UI - Skripsi Membership  Universitas Indonesia Library
cover
Esty Mustika Suud
"ABSTRACT
Zeolit NaY dengan bahan dasar dari Zeolit Alam Lampung ZAL telah disintesis dengan rasio molar Al2O3: 10 SiO2: 10,6 Na2O: 180,3 H2O dan rasio Si/Al 2,47. Sebelum mensintesis melalui proses hidrotermal dengan teknik seeding dilakukan aktivasi dan pemurnian terhadap ZAL. Langkah ini dilakukan untuk menghilangkan senyawa karbonat dan pengotor oksida besi dari zeolit. Selanjutnya, ZAL hasil pemurnian didepolimerisasi menggunakan NaOH untuk memecah atau memutuskan ikatan dalam kerangka zeolit. Zeolit NaY hasil sintesis dikarakterisasi menggunakan instrumen SEM-EDX, XRD, FTIR. Hasil XRD menunjukkan bahwa zeolit hasil sintesis merupakan zeolit NaY, walaupun kerangka sodalite juga teramati Hasil SEM-EDX menunjukkan morfologi dari zeolit NaY. Hasil karakterisasi FTIR menunjukkan tidak adanya vibrasi dari double-six-ring. Pada penelitian ini zeolit NaY hasil sintesis memiliki nilai kapasitas tukar kation 32,97 mek/100g lebih tinggi dibandingkan dengan ZAL raw 28,01 mek/100g . Adsorpsi ion logam kadmium II dan kobal II dilakukan pada termperatur ruang, dengan volume 25mL/0,1gram zeolit dan waktu kontak 120 menit. Hasil proses adsorpsi menunjukkan kapasitas adsorpsi zeolit NaY hasil sintesis lebih tinggi dibandingkan dengan ZAL raw.

ABSTRACT
NaY zeolite from natural zeolite Lampung had been synthesized with molar ratio of Al2O3 10 SiO2 10,6 Na2O 180,3 H2O and Si Al ratio 2,47, prior to synthesis via hydrotermal process and seeding technique ZAL was activated and purified. The purpose of this step was to remove carbonate and iron oxide which were impurities in zeolite. The purified ZAL was then depolymerized using NaOH to break the bonds within the zeolite framework. The as synthesized NaY zeolite was characterized using SEM EDX, XRD, and FTIR. XRD diffractogram shows that the as synthesized zeolite was NaY zeolite, although sodalite framework was do observed. SEM EDX characterization shows the morphology of NaY zeolite. FTIR characterization shows that there are no vibration mode for the double six ring. In this research as synthesized NaY has higher cation exchange capacity 32, 97 meq 100g compared to the raw ZAL 28,01 meq 100g . The adsorption of heavy metal cation cadmium II and cobalt II is done at room temperature, with volume 25mL per 0,1gram zeolite and contsat time of 120 minutes. The result shows that the synthesized NaY zeolite has better adsorption capacity than ZAL raw."
2016
S66143
UI - Skripsi Membership  Universitas Indonesia Library
cover
Iska Yuni Parmanti
"Kaolin memiliki struktur yang berlapis Phylosilicate yang dapat digunakan sebagai bahan baku pembuatan zeolit, salah satunya adalah zeolit NaY. Zeolit NaY merupakan zeolit jenis faujasit dengan rasio Si/Al 2-4 dan kaolin memiliki rasio Si/Al 1. Untuk itu, kaolin lebih mudah dijadikan zeolit NaY karna perbandingan rasio yang tidak berbeda jauh. Penelitian ini, menggunakan kaolin sebagai sumber Si dan Al dengan harapan memberikan sumber Si dan Al alternatif yang lebih terjangkau harganya dari bahan sintetik. Penggunaan kaolin yang berasal dari alam tak terlepas dari adanya pengotor, untuk itu dilakukan proses purifikasi.
Pada penelitian ini digunakan pemutusan ikatan dan penghancuran struktur dengan menggunakan NaOH dengan metode Submolten Salt System dengan variasi kaolin:NaOH 1:1 dan 2:1. Sintesis zeolit dilakukan dengan metode hidrotermal dengan teknik seeding dengan menggunakan rasio mol seed gel 5 of Al : 10,67 Na2O: Al2O3 : 10 SiO2 : 180 H2O. Dan memvariasikan waktu kristalisasi 16 dan 24 jam.
Didapatkan hasil zeolit NaY dengan fragmentasi 2:1 dan variasi waktu 24 jam berhasil menjadi zeolit NaY dengan rasio Si/Al 3,8 berukuran mesopori. Hal ini didukung dengan karakterisasi XRD ,EDX dan FTIR menunjukan bahwa adanya puncak penyusun unit pembangun sekunder puncak double 4 dan 6 ring khas faujasit pada bilangan gelombang 600-500 cm-1.

Kaolin has a layered structure Phylosilicate that can be used as a raw material for synthesis of zeolites, one of which is NaY zeolite. Zeolite NaY is a faujasite zeolite with Si Al ratio of 2 4 and kaolin has Si Al ratio 1. For the reason, kaolin is more easily used as NaY zeolite because the ratio is not much different. This study, using kaolin as a source of Si and Al with hope of providing a more affordable source of Si and Al alternatives than synthetic materials. The use of kaolin that comes from nature can not be separated from the impurity, so purification process is recommended.
In this study used the breaking of bond and structure destruction by using NaOH with Submolten Salt System method with kaolin NaOH variation 1 1 and 2 1. Synthesis of zeolite is done by hydrothermal method woth seeding technique using mole ratio seed gel 5 of Al 10,67 Na2O Al2O3 10 SiO2 180 H2O . And variation of crystallization time 16 and 24 hours.
The result of NaY zeolite with 2 1 fragmentation and 24 hour variation succeeded to become NaY zeolite with mesoporous Si Al ratio is 3.8. This is supported by the characterization of XRD, EDX and FTIR indicating that the top of the construction of the secondary peak builder units of double 4 and 6 ring who indicated the structure faujasite on the wave number 600 500 cm 1.
"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2017
S70099
UI - Skripsi Membership  Universitas Indonesia Library
cover
Muhamad Faisal
"ZSM-5 telah berhasil disintesis melalui metode hidrotermal dari mineral alam zeolit alam Bayat dan kaolin Bangka sebagai sumber alumina dan silika, TPAOH sebagai agen pengarah struktur MFI dan PDDA-M sebagai pengarah mesopori. ZSM-5 kemudian dimodifikasi permukaannya dengan oksida logam Fe dan Co melalui metode impregnasi basah untuk meningkatkan aktivitas katalitiknya pada reaksi oksidasi parsial metana. Modifikasi dengan oksida logam ini juga dilakukan untuk ZSM-5 sintetik sebagai pembanding dalam aktivitas katalitiknya. ZSM-5 alam dan ZSM-5 sintetik termodifikasi oksida logam dikarakterisasi dengan instrumen FTIR, XRD, SEM-EDX, surface area analyzer dan XPS untuk mengetahui pengaruh modifikasi permukaan terhadap struktur, morfologi dan aktivitas katalitiknya. Analisis komposisi unsur dari ZSM-5 alam terimpregnasi oksida Fe dan Co menunjukkan % loading Fe dan Co berturut-turut sebesar 2,37% dan 1,78%. Hasil pengujian isoterm adsorpsi menunjukkan baik ZSM-5 alam maupun ZSM-5 alam terimpregnasi oksida logam Fe dan Co memiliki kurva tipe IV H4 yang merupakan kurva ciri khas material berpori hirarki. Analisis XPS menunjukkan spesi oksida logam Fe dan Co yang menempel pada ZSM-5 berturut-turut adalah Fe2O3 dan Co3O4. Hasil uji analisis kandungan gas menggunakan GC-TCD menunjukkan berkurangnya mol metana setelah reaksi yang menandakan metana telah terkonversi menjadi metanol dan formaldehida yang terlihat dari puncak kromatogram GC-FID. Hasil analisis produk dengan GC-FID menunjukkan reaksi oksidasi parsial metana menggunakan Fe/ZSM-5 menghasilkan formaldehida dan menggunakan Co/ZSM-5 menghasilkan metanol dan formaldehida.

ZSM-5 has been successfully synthesized through hydrothermal method using Bangka Kaolin and Bayat Natural Zeolite as the precursors, TPAOH as MFI-structure directing agent; PDDA-M as mesopore directing agent. Furthermore, the surface of ZSM-5 was impregnated with metal oxide of Fe and Co to improve its catalytic performance through partial oxidation of methane reaction. As comparison, ZSM-5 synthesized from pro analysis precursors was also impregnated with metal oxide of Fe and Co and tested through the reaction. Metal oxide of Fe and Co impregnated ZSM-5 were characterized with XRD, SEM-EDS, XPS and SAA-BET instruments to see the effect of impregnation to the structure and characteristic of both materials. Analysis of the elemental composition of Fe/ and Co/ZSM-5 was 2,37% and 1,78% respectively. The N2 isotherm adsorption curve shows a type IV H4 indicates that the materials has hierarchical characteristic. XPS analysis show the Fe and Co oxide that impregnated to ZSM-5 is Fe2O3 and Co3O4. GC-TCD analysis show there is a decreases of methane mol after reaction indicates that the methane has been converted. GC-FID analysis show that the partial oxidation of methane using Fe/ZSM-5 yielded formaldehyde whereas for Co/ZSM-5 yielded methanol and formaldehyde."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2020
T54844
UI - Tesis Membership  Universitas Indonesia Library