"Ceramic Laminate Veneer (CLV) merupakan alternatif perawatan yang sering dipilihpada kasus yang menuntut nilai estetik tinggi. Berdasarkan bahannya, ceramic litium disilikat (LiDi) banyak dipilih bagi restorasi CLV. Pada pemasangannya, CLV umumnya menggunakan semen resin light-cure dan dual-cure. Namun, terdapat beberapa laporan perubahan warna pada CLV pasca pemasangan. Fenomena ini dapat dipengaruhi oleh kestabilan warna semen resin sebagai faktor internal. Penelitian-penelitian terdahulu telah membandingkan kestabilan warna semen resin light-cure dan dual-cure pada restorasi CLV. Meskipun begitu, terdapat keragaman hasil penelitian oleh karena penggunaansistem semen resin yang berbeda pada tiap penelitian sehingga menyulitkan identifikasi dan rekomendasi semen resin dengan kestabilan warna yang lebih baik.Tujuan : Mengkaji penelitian-penelitian yang mengevaluasi kestabilan warna semenresin light-cure dan dual-cure pada CLV berbahan LiDi yang diukur secara kuantitatif menggunakan spektrofotometer.Metode : Pencarian studi dilakukan pada delapan database (PubMed, Ebsco, ProQuest,Scopus, Sciencedirect, Wiley, SpringerLink, dan Embase) dengan waktu publikasi November 2017-November 2022 dan dalam bahasa inggris. Berdasarkan kriteriakelayakan, studi berbahan LiDi yang mengukur kestabilan warna semen resin light-cure dan dual-cure secara kuantitatif menggunakan spektrofotometer dan dinyatakan dalam ΔE (nilai perubahan warna) akan diinklusikan.Hasil : Total 1937 studi di seleksi dengan 791 studi duplikat dan 1135 studi yang tidak memenuhi kriteria kelayakan di eksklusikan. Penyaringan studi berdasarkan pembacaan menyeluruh menghasilkan nilai kappa 0.85, 0.85, dan 1.00 antara seluruh peneliti.Sebanyak 11 studi yang memenuhi kriteria inklusi dilakukan kajian. Total 8 dari 11 studi inklusi melaporkan nilai perubahan warna (ΔE) yang lebih rendah pada kelompok dualcure dibandingkan kelompok light-cure.Kesimpulan : Semen resin dual-cure menunjukan kestabilan warna yang cenderunglebih baik dibandingkan semen resin light-cure.

---

Ceramic Laminate Veneer (CLV) is an alternative treatment which often chosen in high aesthetic demand cases. Based on the material, lithium disilicate ceramic (LiDi) is widely used for CLV. Light-cure and dual-cure resin cement is often used in CLV cementation. However, there are several reports of CLV discoloration in the long term. This phenomenon can be influenced by the color stability of resin cement as the internal factor. Previous studies have compared the color stability of light-cured and dual-cure resin cements on CLV restorations with varying results due to various resin cement system and making it difficult to identify and to recommend resin cements with better color stability.

Objective: To review studies that evaluate the color stability of light-cure and dual-cure resin cements in lithium disilicate laminate veneer by quantitative measurement using a spectrophotometer.

Method: An electronic search (PubMed, Ebsco, ProQuest, Scopus, Sciencedirect, Wiley, SpringerLink, dan Embase) with time limit November 2017 – November 2022 and published in english was conducted. Studies that evaluate the color stability of light-cure and dual-cure semen cement on CLV with LiDi material using a spectrophotometer and stated in ?E (color change value) will be included.

Result: A total of 1937 studies were selected, with duplication of 791 and 1135 studies being excluded based on the eligibility criteria. The kappa values representing the intra-examiner reliability for full text screening were 0.85, 0.85, and 1.00, respectively. Total of 11 studies which met the inclusion criteria were reviewed. 8 out of 11 included studies were reported lower ?E (color change value) in dual-cure group compared to light-cure group.

Conclusion: Dual-cure resin cement shows better color stability that light-cure resin cement."

"ABSTRAKSandblasting dilakukan pada permukaan restorasi veneer indirek resin kompositsebelum direkatkan pada email menggunakan resin semen Multi-step danSADRC. Tujuan penelitian ini untuk mengetahui pengaruh durasi sandblastingterhadap kuat rekat geser veneer indirek resin komposit yang direkatkan padaemail. Pengujian kuat rekat geser menggunakan Universal Testing Machine,kemudian analisa patahan dengan Stereomicroscope dan Scanning ElectronMicroscope. Hasil penelitian menunjukkan bahwa grup resin semen Multi-stepmenghasilkan kuat rekat geser yang lebih tinggi dan berbeda bermaknadibandingkan grup SADRC. Durasi sandblasting yang berbeda, tidak memberikanperbedaan nilai kuat rekat yang bermakna baik pada grup resin semen Multi-stepmaupun SADRC.

---

BSTRACTSandblasting was performed on the surface of indirect composite resin veneer(VIRK) restorations before bonding to enamel using Multi-step resin cement andSADRC. The purpose of this study was to determine the effect of sandblastingduration on Shear Bond Strength (SBS) of VIRK bonded to enamel. Shear BondStrength test was done using Universal Testing Machine, failure analysis wasevaluated using Stereomicroscope and Scanning Electron Microscope. The resultsshowed that VIRK cemented with Multi-step produces higher SBS andsignificantly different than VIRK cemented with SADRC. Sandblasting durationdid not influence SBS value of VIRK cemented with Multi-step and SADRC."

"Penelitian ini bertujuan untuk menganalisis pengaruh ketebalan komposit resin serat pendek KRSP dan iradiansi terhadap kekerasan dan depth of cure DoC. Dua puluh empat spesimen KRSP berbentuk silinder berdiameter 6 mm dibagi menjadi 2 kelompok ketebalan; 4 dan 5 mm n=12. Masing-masing kelompok dibagi menjadi 2 kelompok yang dipolimerisasi dengan iradiansi berbeda; 1000 dan 1200 mW/cm2 n=6. Setiap spesimen dipolimerisasi selama 20 detik dengan jarak penyinaran 2 mm. Nilai kekerasan didapat melalui uji kekerasan Vickers dan DoC didapat dengan mengukur rasio kekerasan permukaan bawah terhadap permukaan atas. Data dianalisis menggunakan uji statistik One-Way ANOVA. Hasil penelitian menunjukkan adanya perbedaan signifikan.

---

This study aims to analyze the effect of short fibre reinforced resin composite SFRC thickness and light curing irradiance on the hardness and depth of cure DoC . Twenty four specimens of SFRC were made into cylindrical shape with a diameter of 6 mm and divided into 2 different thickness groups 4 and 5 mm n 12. Each group was divided into another 2 different groups which was cured by different irradiance 1000 and 1200 mW cm2 n 6 . Each specimen was cured for 20s with 2 mm light curing distance. The hardness was measured by Vickers hardness test and DoC was measured by calculating a hardness ratio of the bottom to the top surface of specimens. Data were analyzed statistically by One Way ANOVA tests. The result showed significant differences."

"Latar Belakang: Material restorasi yang paling berkembang pesat sampai saat ini adalah resin komposit. Resin komposit yang beredar di pasaran dan menurun klaim pabrik memiliki sifat estetika yang baik, mudah dimanipulasi, serta dapat dipakai secara universal adalah Resin Komposit Supra-Nano Palfique Universal Flow. Suatu material restorasi harus mengalami polimerisasi yang adekuat agar menghasilkan sifat fisik, kimia, mekanik, dan biologis yang optimal. Sifat kekerasan mikro dan depth of cure material dapat menjadi indikator seberapa baik polimerisasi suatu material. Pada keadaan klinis, anatomi gigi dapat menghalangi sinar untuk berada tepat di atas permukaan restorasi sehingga jarak dan durasi penyinaran memengaruhi kekerasan mikro dan depth of cure resin komposit. Tujuan: Menganalisis pengaruh jarak dan durasi penyinaran terhadap kekerasan mikro dan depth of cure Resin Komposit Supra-Nano Palfique Universal Flow. Metode: Tiga puluh spesimen Resin Komposit Supra-Nano Palfique Universal Flow berbentuk silinder berdiameter 6 mm dan tinggi 2 mm dipersiapkan untuk penelitian ini. Spesimen terbagi menjadi 6 kelompok berdasarkan jarak penyinaran (0,3, dan 6 mm) dan durasi penyinaran (10 dan 15 detik) yang disinari light curing unit dengan iradiansi 1050 mW/cm2. Uji kekerasan dilakukan pada permukaan atas spesimen, dan diuji juga kekerasan pada permukaan bawah spesimen untuk menghitung depth of cure (DoC). DoC dihitung dengan menggunakan metode bottom/top hardness ratio (%). Data dianalisis menggunakan uji statistik One-way ANOVA dan Independent Sample T-test. Hasil: Kekerasan mikro dan DoC semakin tinggi pada jarak yang semakin dekat baik pada durasi 10 maupun 15 detik. Nilai kekerasan mikro dan DoC pada durasi penyinaran 15 detik lebih tinggi dibandingkan durasi penyinaran 10 detik pada jarak yang sama secara signifikan (p<0.05). DoC > 80% hanya didapatkan pada kelompok dengan jarak penyinaran 0 mm dengan durasi penyinaran 10 dan 15 detik yaitu 81,44 ± 0,02% dan 92,64 ± 0,01% secara berurutan, serta pada kelompok dengan jarak penyinaran 3 mm dan durasi penyinaran 15 detik, yaitu 88,78 ± 0,02%. Kesimpulan: Semakin dekat jarak penyinaran dan semakin lama durasi penyinaran, maka kekerasan mikro dan DoC akan semakin tinggi.

---

Background: The most rapidly developing restoration material to date is composite resin. The composite resin on the market and according to manufacturer claims has good aesthetic properties, is easy to manipulate and can be used universally is Palfique Universal Flow Supra-Nano Composite Resin. A material restoration must have an adequate polymerization to produce optimal physical, chemical, mechanical, and biological properties. The microhardness and depth of cure properties of a material can be an indicators of how well a material is polymerized. In clinical situations, anatomical teeth can prevent light from being directly above the surface of the restoration so that the distance and duration of light-curing affect the microhardness and depth of cure of the composite resin. Objective: To analyze the effect of light-curing distance and duration on the microhardness and depth of cure of Supra-Nano Palfique Universal Flow Composite Resin. Methods: Thirty specimens of Palfique Universal Flow Supra-Nano Composite Resin in a cylindrical shape with a diameter of 6 mm and a height of 2 mm were prepared for this study. Specimens were divided into 6 groups based on the light-curing distance (0,3, and 6 mm) and duration (10 and 15 seconds) which were exposed to a light curing unit with an irradiance of 1050 mW/cm2. The hardness test was on the top surface of the specimen, and hardness was also tested on the bottom surface of the specimen to calculate the depth of cure (DoC). DoC was calculated using the bottom/top hardness ratio (%) method. Data was analyzed statistically by One-way ANOVA and Independent Sample T-test. Results: Microhardness and DoC were higher at closer light-curing distances for both 10 and 15 seconds. Microhardness and DoC values at a light-curing duration of 15 seconds were significantly higher than at a duration of 10 seconds at the same distance (p<0.05). DoC > 80% was only obtained in the group with a light-curing distance of 0 mm with a duration of 10 and 15 seconds, that is 81.44 ± 0.02% and 92.64 ± 0.01% respectively, and 88.78 ± 0.02% in the group with a light-curing distance of 3 mm and a duration of 15 seconds. Conclusion: The closer the light-curing distance and the longer the light-curing duration, the higher the microhardness and DoC."

"Penelitian ini bertujuan untuk menganalisis pengaruh jarak penyinaran terhadap depth of cure DOC resin komposit serat sebagai substruktur. Delapan belas spesimen EverX Posterior warna A3 berbentuk silinder diameter 6 mm dan tebal 4 mm dibagi menjadi 3 kelompok jarak penyinaran 0, 2, dan 4 mm yang dipolimerisasi dengan LED Litex 695, irradiansi 800 mW/cm2, selama 20 detik. Pengukuran DOC dilakukan melalui rasio kekerasan Vickers. Analisis data dilakukan menggunakan uji ANOVA satu arah. Hasil penelitian menunjukkan DOC pada jarak penyinaran 0, 2, dan 4 mm sebesar 79 0,7, 77 0,6, dan 75 0,8. Disimpulkan terdapat perbedaan bermakna pada nilai DOC pada seluruh jarak penyinaran.

---

This study aims to analyze the effect of light curing distance on the depth of cure DOC of fiber reinforced composite as substructure. Eighteen specimens consist of EverX Posterior shade A3, formed into a cylindrical shape 6 mm in diameter and 4 mm thickness divided into 3 groups according to light curing distance 0, 2, and 4 mm which were polymerized with LED Litex 695, irradiance 800 mW cm2, for 20s. Meansurement of DOC was carried out by Vickers hardness ratio of specimens. Data were analyzed statistically by one way ANOVA test. The result showed the DOC at a light curing distances of 0, 2, and 4 mm was 79 0,7, 77 0,6, and 75 0,8. It was concluded that there is a significant difference in DOC among the light curing distance."

"Resin komposit Bulk-Fill merupakan material yang dapat merestorasi kavitas dengan kedalaman 4-5 mm dalam satu kali penyinaran. Polimerisasi resin komposit dipengaruhi oleh durasi penyinaran dan metode penyinaran Light Curing Unit. Polimerisasi adekuat diperlukan untuk mendapatkan kekerasan permukaan dan Depth of Cure yang optimal. Penelitian ini dilakukan untuk mengetahui kekerasan permukaan dan Depth of Cure resin komposit Bulk-Fill yang disinar menggunakan Light Curing Unit penyinaran pulsa selama 5, 10, dan 20 detik. Spesimen berjumlah 30 buah dibagi berdasarkan kelompok perlakuan yaitu kelompok durasi penyinaran (5, 10, dan 20 detik) dan penyinaran (pulsa dan kontinu). Spesimen berdiameter 6 mm dan tebal 4 mm diuji menggunakan Knoop Microhardness Tester dengan beban indentasi 50 g selama 10 detik pada 5 titik berbeda. Hasil penelitian menunjukkan peningkatan kekerasan permukaan yang disinar dengan Light Curing Unit penyinaran pulsa dan kontinu seiring pemanjangan durasi penyinaran. Terdapat perbedaan bermakna (p<0,05) pada kekerasan permukaan di kelompok durasi penyinaran. Pada nilai depth of cure dengan kedua Light Curing Unit tidak terdapat perbedaan bermakna (p>0,05). Sehingga disimpulkan, penyinaran pulsa Light Curing Unit selama 5, 10, dan 20 detik pada resin komposit Bulk-Fill mengalami peningkatan kekerasan permukaan yang signifikan dan penggunaan dua metode penyinaran sama baik pada nilai depth of cure.

---

Bulk-Fill composite resin have been introduced with the purpose of time savings. It can be placed in a 4-5 mm thickness bulks to be photo-cured in one step. Polymerization of composite resins affected by the irradiation time and mode. Adequate polymerization is needed to obtain optimal surface hardness and Depth of Cure. This study aimed to evaluate the influence of different exposure time with pulse-lighting mode on Bulk-Fill composite resin surface microhardness and Depth of Cure. Thirty specimens divided into 3 groups of exposure time (5, 10, and 20 sec) and 2 groups of irradiation mode (pulse and continuous), 6 mm in diameter and 4 mm in thick were prepared. Each specimen was measured using Knoop Microhardness Tester at each surface. The result showed that irradiation of Bulk-Fill composite resin with pulse-lighting mode curing unit for 5, 10, and 20 seconds experienced a significant increase in surface hardness. The depth of cure values shows no significant difference among different irradiation mode. It was concluded that that Bulk-Fill composite resin irradiated at longer exposure time exhibited significantly higher surface microhardness than those irradiated at shorter time. Meanwhile, there was no significant difference between two different irradiation mode for depth of cure."

"Latar belakang: Light Curing Unit (LCU) LED metode pulsa iradiansi 900 mW/cm2 telah dikembangkan untuk menghasilkan suhu pada ruang pulpa lebih rendah dibandingkan metode kontinu akibat polimerisasi resin komposit Nanofill pada durasi penyinaran 20 detik. Tujuan: menganalisis pengaruh durasi dan metode penyinaran pulsa terhadap kekerasan permukaan dan Depth of Cure resin komposit Nanofill. Metode: Spesimen resin komposit Nanofill (diameter 6 mm dan tebal 2 mm) disinar dengan LCU LED metode pulsa beriradiansi 900 mW/cm2 selama 5, 10, dan 20 detik, lalu direndam di dalam 5 ml akuades (37˚C 24 jam). Setiap spesimen diuji dengan Knoop Microhardness Tester sebanyak 5 kali pada permukaan atas dan bawah dan dihitung depth of cure. Hasil: Terjadi peningkatan kekerasan permukaan yang disinar dengan LCU metode penyinaran pulsa dan kontinu selama 5 hingga 20 detik yaitu 45,9±1,6/26,4±1,6 KHN hingga 68,8±1,8/57,4±1,6 KHN, dan 46,8±1,6/28,2±1,5 KHN hingga 69,3±1,2/57,8±1,1 KHN. Terdapat perbedaan bermakna (p<0,05) pada kekerasan permukaan di kelompok durasi penyinaran dengan uji One-way Anova dan post hoc Tamhane. Pada nilai depth of cure resin komposit Nanofill yang disinar antara kedua metode penyinaran tidak terdapat perbedaan bermakna (p>0,05) secara statistik. Kesimpulan: Resin komposit Nanofill yang disinar pada durasi lebih lama menunjukkan kekerasaan permukaan atas maupun bawah lebih tinggi dibandingkan dengan durasi lebih pendek. Demikian pula, depth of cure pada durasi lebih lama menunjukkan nilai lebih tinggi. Penyinaran metode pulsa iradiansi 900 mW/cm2 dan kontinu iradiansi 900 mW/cm2 menunjukkan kekerasan permukaan dan depth of cure yang sama."

"Penelitian ini bertujuan untuk mengetahui pengaruh post-cure terhadap depth of cure DOC resin komposit serat dan membandingkan metode pengukuran DOC. Sembilan spesimen EverX Posterior warna A3 yang disinar dengan irradiansi 800-1000 mW/cm2 20 detik dibagi menjadi 3 kelompok: diukur setelah penyinaran dan setelah 24 jam post-cure dengan profil kekerasan Vickers; serta metode ISO 4049. DOC yang diukur setelah penyinaran dan setelah 24 jam post-cure 3,02 0,02 mm dan 3,93 0,03 mm; serta metode pengukuran ISO 4049 4,88 0,13 mm. Disimpulkan terdapat peningkatan bermakna DOC yang diukur setelah 24 jam post-cure, dan metode ISO 4049 menghasilkan DOC bermakna lebih tinggi dari profil kekerasan Vickers.

---

This study aims to identify the effect of post cure towards depth of cure DOC fiber reinforced composite and compare DOC measuring methods. Nine speciments of EverX Posterior shade A3 cured with light irradiation 800 1000 mW cm2 20s divided into 3 groups measured after curing and after 24 hours post cure with Vickers microhardness profile and ISO 4049 method. DOC that measured after curing and after 24 hours post cure are 3,02 0,02 mm and 3,93 0,03 mm and with ISO 4049 method 4,88 0,13 mm. It was concluded thatDOC measured after 24 hours post cure is significantly higher than immediately after curing, and ISO 4049 method produce significantly higher DOC than Vickers microhardness profile."

"Penelitian ini bertujuan untuk membandingkan kuat rekat geser dan Adhesive Remnant Index (ARI) breket metal yang direkatkan dengan dua semen resin light cure berbeda. Dua puluh gigi premolar atas manusia ditanam dalam akrilik dan dibagi menjadi dua kelompok; kelompok A: Transbond XT + breket Mini Dyna Lock, kelompok B: Enlight + breket Mini Dyna Lock. Hasil penelitian menunjukkan kuat rekat geser kelompok A adalah 12,46 ± 0,35 MPa, ARI: 1 dan 2, dan kelompok B adalah 9,69 ± 0,53 MPa, ARI: 2, (p <0,05). Disimpulkan bahwa terdapat perbedaan bermakna kuat rekat geser pada kedua kelompok dengan kegagalan ikatan bersifat kohesif.

---

The aims of this study was to compare shear bond strength (SBS) and Adhesive Remnant Index (ARI) of metal bracket bonded with two different light cured resin cements. Twenty extracted human upper premolar embedded in acrylic and divided into two groups; Group A: Transbond XT + Mini Dyna Lock brackets, group B: Enlight + Mini Dyna Lock brackets.

The results showed SBS of group A was 12.46 ± 0.35 MPa, ARI: 1 and 2, and group B was 9.69 ± 0.53 MPa , ARI: 2, (p <0.05). It was concluded that the SBS of two groups was significantly different with cohesive bond failure."