"The aim of this research is to see the effect of various dentin conditioners (phosphoric acid) to the bond strength between resin adhesive HNPM/TEGDMA (2 Hydroxy-3,2-Napthoxy-Propyl Methacrylate/Trietilen Glikol di Methacrylate) and dentin tissue of bovine teeth. Dentin conditioner that was used are phosphoric acid solution 10%, 25%, 35% (Group A1, A2, A3). Specimens was divided into 3 Groups, each group has 10 specimens. Bond strength test used "Universal Testing Machine". A G 5000 and SHIMADZU type. The result of this research shows average differences of bond strength of each group. Anova test there is a significant difference (8.485 and p < 0,05). Double comparison Tukey test among groups generally are significant different (p<0,05) except between A2 and A3 group. The result of the research states there are effects of various dentin conditioners to the bond strength between resin adhesive NHPM/TEGDMA and dentin tissue."

"Composite resin are restorative materials having color similar to teeth and have been widely used in dentistry. The successful application of composite resin influences the duration of the restoration in the oral cavity. The aim of this research is to describe the influence of artificial saliva contamination and the application of re-conditioning on tensile bond strength of composite resin to dentin. In the control group, the dentin were etched, bonding were applied and composite resin were restored on the dentin. In the group with artificial saliva contamination without re-conditioning, the dentin were etched, bonding were applied and then contaminated with artificial saliva, dried and then restired with composite resin. While the group with artificial saliva contamination with re-conditioning, the dentin were etched, bonding were applied and contaminated with artificial saliva, and then etched and applied bonding agent and restored composite resin.Bond strength test used “Universal testing machine, AG 5000. The results showed that highest value of tensile bond strength of composite resin to dentin was at the control group. It can be concluded that artificial saliva contamination decreased tensile bond strength while re-conditioning application increased it."

"ABSTRAK Latar belakang: Ketahanan ikatan antara resin komposit dengan dentin merupakan penentu keberhasilan restorasi resin komposit.Tujuan: Menganalisis EBA terhadap kekuatan ikat resin-dentin.Metode: 48 sampel dentin dibagi menjadi 6 kelompok. Kemudianseluruh kelompok di ukur kekuatan ikat gesernya menggunakan UTM.Data dianalisa statistik dengan uji hipotesis Kruskal Wallis yangdilanjutkan dengan uji Mann Whitney. Hasil: Median tertinggikelompok 3, sedangkan median terendah kelompok 5. Kesimpulan:Ekstrak biji anggur yang diaplikasikan sebelum etsa dapatmeningkatkan kekuatan ikat gesek namun tidak dapat menghambatbiodegradasinya.ABSTRACT Background: Resilience of resin-dentin bonding known as one ofsuccess composite resin restoration determinants. Aim: To analyze theeffect of grape seed extract on resin-dentin shear bond strength.Methods: 48 dentin sample were divided into 6 groups. Shear bondstrengths measured using UTM. Statistical analysis was done byKruskal Wallis test and Mann Whitney test. Results: The highestmedian value was highest on group 3, and the lowest was group 5.Conclusion: Grape seed extract can improve the shear bond strengthbut not have effect on reducing the biodegradation.;Background: Resilience of resin-dentin bonding known as one ofsuccess composite resin restoration determinants. Aim: To analyze theeffect of grape seed extract on resin-dentin shear bond strength.Methods: 48 dentin sample were divided into 6 groups. Shear bondstrengths measured using UTM. Statistical analysis was done byKruskal Wallis test and Mann Whitney test. Results: The highestmedian value was highest on group 3, and the lowest was group 5.Conclusion: Grape seed extract can improve the shear bond strengthbut not have effect on reducing the biodegradation."

"Korosi atmosferik merupakan hasil interaksi logam dengan atmosfer di sekitarnya, yang terjadi akibat kelembaban dan oksigen di udara dan diperparah dengan adanya polutan seperti gas dan garam yang terkandung di udara. Pantai atau laut adalah daerah yang paling korosif, karena atmosfemya mengandung partikel klorida yang bersifat agresif dan mempercepat laju korosi. Salah satu metode yang efektif untuk mencegah dan mengeadalikan korosi adalah dengan proses anodisasi. Anodisasi adalah proses untuk membuat lapisan oksida tipis berpori pada permukaan logam. Lapisan tersebut memiliki sifat tahan terhadap cuaca dan lebih keras dari logam dasarnya. Dalam penelitian ini digunakan logam aluminium teknis berbentuk lembaran. Daya tahan logam aluminium terhadap kondisi cuaca berbanding lurus dengan ketebalannya. Untuk mencapai tujuan tersebut maka dilakukanlah penelitian terhadap parameter proses seperti jenis larutan, temperatur, konsentrasi dan variasi waktu. Jenis larutan yang dipakai pada penelitian ini adalah larutan asam sulfat ditambah variasi konsentrasi asam fosfat (10%, 30%, 40%, 70%, 100%). Agar diperoleh kondisi optimum untuk mendapatkan sifat-sifat lapisan yang diinginkan maka dilakukan variasi terhadap temperatur (10°C, 15°C, 20°C, 30°C) dan waktu (20-60 menit). Kondisi optimum yang diperoleh adalah sebagai berikut: konsentrasi asarn sulfat 60% + asam fosfat 40%, pH = 1, waktu 60 menit, temperatur 10°C, tegangan 20V dan rapat arus 7,4 A/dm2 dengan menghasilkan ketebalan lapisan optimum 43,8 µm dan kekerasan maksimum sebesar 154 VHN.

---

Atmospheric corrosion is the interaction between metal and the surrounding environment due to the humidity, oxygen and pollutant (chloride and sulphate particle) which is contains in the air. Marine is the most corrosive region due to the atmosphere contains chloride particle whose characteristic aggressive and accelerate corrosion rate. Anodizing is one of the most effective methods to prevent and control the corrosion rate. Anodizing is an electrolytic passivation process used to increase the thickness and density of the natural oxide layer on the surface of metal parts. Anodizing increases corrosion resistance and wear resistance. In this experiment used the sheet aluminum metal. The weather resistance of aluminum has linear relation to the thickness. In this investigation used some parameter processes like type of electrolyte, temperature, concentration and time variation. The medium which is used in this experiment is sulphate acid with added phosphate acid variation (0%, 10%, 40%, 70% and 100%). To achieve optimum condition the temperature (10°C, 15°C, 20°C, 30°C) and time variation (20-60 min) is carried out. The optimum condition of this experiment is the specimen which has hardness 154 HV and the thickness is 43,8 µm with electrolyte concentration sulphate acid 60%, phosphate acid 40%, temperature 10°C, time process 60 min, voltage 20 volt and current density 7,4 A/dm2."

"Latar Belakang: Asam hialuronat (AH) merupakan glikosaminoglikan dan salah satu komponen penting dari matriks ekstraseluler pada lingkungan biologis mikro dentin.  Pada pulpa terinflamasi, ketika lingkungan biologis mikro kondusif maka terjadi rekrutmen sel punca pulpa (human dental pulp stem cells/hDPSCs) yang akan berdiferensiasi menjadi odontoblast like cell membentuk dentin reparatif dan terdapat ekspresi dentin sialophosphoprotein (DSPP).Tujuan: Mengetahui potensi berbagai konsentrasi AH pada media kultur hDPSCs terhadap ekspresi DSPP dengan waktu observasi  7 hari dan 14 hari. Metode: hDPSCs yang didapatkan dari bahan baku tersimpan pada pasase ke-3 dan 4 yang telah mengalami serum starvation selama 24 jam, diberikan AH dengan konsentrasi 10 mg/mL , 20 mg/mL , 30 mg/mL dan  kontrol positif pada medium osteogenik. Selanjutnya dilakukan observasi waktu selama 7 hari dan 14 hari untuk melihat ekspresi DSPP dari tiap kelompok secara kuantitatif (uji ELISA) dan potensi mineralisasi secara kualitatif (uji alizarin red) pada hari ke-21. Uji statistik menggunakan one way anova. Hasil: Terdapat perbedaan potensi berbagai konsentrasi  AH (10mg/mL, 20  mg/mL, 30 mg/mL)  (p<0.05) pada media kultur hDPSCs terhadap ekspresi DSPP dengan waktu observasi 7 hari dengan konsentrasi 30 mg/mL yang paling berpotensi meningkatkan DSPP dan dikonfirmasi dengan nodul yang pekat pada uji alizarin red di hari ke-21. Kesimpulan: Asam hialuronat (AH) memiliki potensi untuk meningkatkan ekspresi DSPP, konsentrasi AH 30 mg/ml merupakan konsentrasi yang optimum bagi hDPSCs. 

---

Background: Hyaluronic acid (HA) is glycosaminoglycan and one of important factors in extracellular matrix located at dentin niche biology.  In an inflamed pulp, when niche biology is conducive, the recruitment of human dental pulp stem cells (hDPSCs) will take place and it will differentiate into odontoblast like cell that will create reparative dentin and expressing dentin sialophosphoprotein (DSPP). 

Objective: To analyze the potential of HA conditioned media in various concentration towards hDPSCs differentiation via expression of DSPP at day 7 and 14. 

Methods: hDPSCs culture were obtained from previous research (ethical approval attached) at P3 and P4. After 24 hours incubation of hDPSCs, culture media were supplemented with osteogenic media. Cells were then starved for 24 hours. hDPSCs then planted into 96 well plate and HA 10 mg/ml, 20 mg/ml, 30 mg/ml added into each particular well. DSPP expression is analysed using elisa reader at day 7 and 14 and qualitative result is analysed using alizarin red at day 21. Data was analysed using one way anova.

Result: At day 7 there is a statistically significant different potential of natural HA conditioned media in various concentration (10mg/mL, 20  mg/mL, 30 mg/mL) (p<0.05) towards hDPSCs differentiation via expression of DSPP with HA 30 mg/mL being the most potential concentration to increase DSPP expression, which can be confirmed by bold nodules presented with alizarin red at day 21. 

Conclusion: HA have the potential to increase odontoblast differentiation process via expression of DSPP, with HA 30 mg/mL being the optimum concentration for hDPSCs."

"

Latar Belakang: Perawatan karies dengan minimal intervensi, yaitu dengan membuang infected dentin, dan meninggalkan affected dentin, kemudian dilakukan remineralisasi pada affected dentin. Pada affected dentin masih terdapat ikatan silang kolagen. Remineralisasi dentin lebih kompleks karena pada karies dentin sudah tidak ada sisa kristal mineral. Untuk terjadinya remineralisasi ekstrafibrilar dan intrafibrilar pada dentin, maka dibutuhkan dentin matrix protein 1 (DMP 1)  yang merupakan protein non-kolagen. Proses polymer-induced liquid precursor (PILP) merupakan metode Guided Tissue Remineralization yang bertujuan untuk remineralisasi dentin secara intrafibrilar dan ekstrafibrilar dengan penambahan polimer sebagai analog DMP1. Salah satu material analog protein non kolagen adalah asam poliaspartik.

Tujuan: Mengevaluasi remineralisasi dentin pada permukaan demineralized dentin setelah perendaman dengan larutan remineralisasi yang mengandung asam poliaspartik sebagai analog protein non kolagen.

Metode: Empat kelompok dilakukan demineralisasi buatan. Setelah itu, tiga kelompok dilakukan perendaman dengan larutan remineralisasi yang mengandung asam poliaspartik, sedaangkan satu kelompok tidak dilakukan perendaman larutan remineralisasi asam poliaspartik. Evaluasi remineralisasi dengan Micro-CT.

Hasil: Terlihat remineralisasi pada permukaan demineralized dentin yang ditandai dengan penurunan kedalaman lesi demineralized dentin yang ditandai dengan peningkatan grey scale index setelah dilakukan perendaman dengan larutan remineralisasi asam poliaspartik. Perbandingan rerata empat kelompok menunjukkan perbedaan bermakna.

Kesimpulan: Asam poliaspartik memiliki potensi untuk meremineralisasi demineralized dentin.

---

 

 

---

Background: Caries treatment with minimal intervention, namely by removing infected dentine, and leaving affected dentine, then remineralization of affected dentine. In the affected dentine there are still have collagen cross bonds. Dentin remineralization is more complex because there is no residual mineral crystals in dentinal caries. For extrafibrillary and intrafibrillary remineralization in dentine, dentin matrix protein 1 (DMP 1) is a non-collagen protein. The polymer-induced liquid precursor (PILP) process is a Guided Tissue Remineralization method which aims to remineralize intrafibrilar and extafibrilar dentine by adding polymers as analogous to DMP1. One of the non collagen protein analog material is polyacpartic acid.

Objective: To evaluate remineralization of dentine on the demineralized dentin surface after immersion with remineralization solutions containing polyacpartic acid as a non-collagen protein analog.

Method: Four groups carried out artificial demineralization. After that, three groups were immersed with remineralization solution containing polypartic acid, while one group was not immersed in polyacpartic acid remineralization solution. Remineralization evaluation with Micro-CT.

Results: It appears remineralization on the demineralized dentin surface which is characterized by a decrease in the depth of demineralized dentin lesions which is characterized by an increase in gray scale index after immersion with polyacpartic acid remineralization solution. The comparison of the mean of the four groups showed significant differences.

Conclusion: Polyacpartic acid has the potential to remineralize for demineralized dentine.

 

 

"

"Phosphoric acid etching has been widely used to achieve a strong andlong lasting mechanical bonding between composite resin restorationand tooth structure. The bond strength between the composite resinrestoration and the enamel of permanent teeth can be measured by theshear bond strength of the composite resin restoration. The aim of thisstudy was to evaluate the bond strength between the enamel ofpermanent teeth and the composite resin restoration by measuring theshear bond strength after different durations of etching. In total 27premolar teeth were divided into 3 groups where the enamel of thebuccal surface was etched with 37% phosphoric acid for 5″, 15″, and25″ before placing the composite resin restoration. After keeping theteeth inside an incubator for 24 hours, the shear bond strength wasmeasured using a universal testing machine Shimazu AG-5000 at acrosshead speed of 0.5 mm/min. ANOVA was used for statisticalanalysis of the results, with p<0.05 assumed to imply significance.The mean shear bond strength after etching for 5″, 15″, and 25″ was16.1 MPa, 17.3 MPa and 19.0 MPa, respectively. The results of ANOVA showed significant difference between the 3 groups. However, subsequent Tukey test showed significant difference between 5″ and 25″ of etching (p<0.05), but no significant difference between between the 5″ and 15″ groups nor between the 15″ and 25″ groups (p>0.05). Conclusion: Shear bond strength of the composite resin on the permanent teeth enamel increased with increasing etching time. Significant difference was showed between 5″ and 25″ of etching time."

"Pada penelitian ini dicoba pembuatan serat asam fosfet dari seratrayon yang dicangkok dengan monomer glisidil metakrilat (GMA), dan selanjutnyadifungsionalisasi dengan larutan asam fosfat. Pencangkckan dllakukanm«^nggunakan metode iradiasi awal daiam medium udara denganteknikemulsi dan atmosfer nitrogen. Hasil poncangkokan dinyatakan dalambentuk persen pencangkokan (%G). Parameter yang dipelajari adalah dosistotal Iradiasi yang berhubungan dengan kerapatan rental tercangkok, konsentrasimonomer dan waktu pencangkokan yang berhubungan dengan panjangrantal tercangkok. Fungsionaiisasi dilakukan dengan mempelajari pengaruhpersen pencangkokan dari rayon-g-PGMA yang digunakan, konsentrasilarutan asam fosfat, dan suhu (32° 0 dan 98° 0). KarakterisasI serat asamfosfat dilakukan dengan analisa spektrum FTIR dan kapasitas penukaranionnya terhadap ion logam Cu^"", selektivilasnya terhadap Ion Pb^^ dan Cu^",dan kecepatan penukaran Ion terhadap Ion logam Pb^"^ yang dipelajari padapH 6,0. Pada penelitian ini juga dipelajari pengaruh struktur rantai tercangkok dari serat asam fosfat terhadap selektlvitas penukaran ionnya.Hasil yang diperoleh menunjukkan bahwa %G cenderung menlngkatdengan bertambahnya dosis iradiasi yang digunakan, konsentrasi monomer,dan waktu reaksi. Data densitas rantal tercangkok menunjukkan semakintlnggl dosis Iradiasi maka semakin rapat jarak antar rantai tercangkok Pada dosis iradiasi yang sama, semakin tinggi konsentrasi monomer makarantai tercangkok akan semakin panjang. Reaksi fungsionalisasi memberikanhasi! persen konversi GMAtertinggi sebesar 15,9% (0,81 mmol H3PO4)dengan kapasitas adsorbs! serat asam fosfat terhadap ion Cu^'^ sebesar3,1 meq/g untuk serat asam fosfat dengan kerapatan yang sedang. Hasi! inimasih jauh iebih kecii daripada kapasitas RGP^ (6-7 mek/g). Serat asamfosfat yang disintesis menun-jukkan tingkat seiektivitas yang lebih tinggiterhadap ion logam Pb^* daripada ion oJ*. Semakin jarang jarak rar.taiPGMA yang tercangkok, maka serat akan serriakin seieldif. Percobaanfpenukaran ion menunjukkan bahwa serat m.emiliki kecepatan penukaran ionyang baik karena kesetimbangan penukarannya dapat dicapai dalam vvcuctu 5menit."

"Pertukaran ion merupakan salah satu metode yang dapatdigunakan daiam pengolahan llmbah dan pengolahan air. Penukar ion {resinatau serat) yang memiliki gugus fungsi asam fosfat (-PO4H2) telah diketahuimemiliki selektifitas yang balk dan kemampuan untuk mengadsorpsi logamlogamLantanida dan Aktinida, Pb, Ba, Zn, serta terhadap logam yangdiklasifikasikan ke daiam asam Lewis seperti Fe (ill), Zr (IV), Mo (IV), danU (IV).Penelitian ini bertujuan untuk memanfaatkan serat FPA {FibrousPhosphoric Adsorbent, yang dibuat dengan mencangkok 2-hidroksietilmetakrilat asam fosfat (HMPA, 2-hydroxyethyl methacrylate phosphoricacids) pada kain non-woven yang tersusun dari serat polietilen (PE) yangdilapisi polipropilen (PP) secara radiasi) sebagai adsorban untuk mengikat Fe(III) (Fe-FPA) dan melakukan karakterisasinya melalui penentuan kapasitaspenukaran kation terhadap Na^ dan Fe (III), serta kestabilan ikatan Fe-FPA.Metode yang digunakan untuk penentuan kapasitas adalah metode batchdan pengujian kestabilan ikatan Fe-FPA digunakan metode kolom yaituIdengan mengelusinya dengan larutan FICI pada berbagai konsentrasi.Selanjutnya serat Fe-FPA yang dihasilkan dipelajari aplikasinya sebagaipenukar anion ASO2" pada berbagai pH.Kapasitas serat FPA dengan 87,11% grafting yang ditukar denganAkation Na^ sebesar 1,0983 mek/g FPA dan untuk serat FPA dengan 153,76% grafting sebesar 1,5138 mek/g FPA. Penyerapan Fe (III) optimum pada FPA*terjadi pada pFI 2,0 dan pada konsentrasi larutan Fe(N03)3 0,025 M. JumlahFe (III) yang teradsorpsi oleh FPA pada kondlsi optimum tersebut sebanyak0,9755 mek/g FPA. Dari harga kemiringan kurva Log Kd pada berbagai pH,diketahui bahwa mekanisme adsorpsi Fe (III) pada serat merupakanImekanisme koordinasi. Fe (III) yang terdesorpsi dari serat oleh FICI 0,01 M(pH 2,0) sebesar 0,22% dari jumlah Fe.(lll) yang teradsorpsi. Anion ASO2"dapat diadsorpsi optimum pada pFI 8,0 oleh serat Fe-FPA yaitu sebanyak1,052 mek/g Fe-FPA."